Reversible hydrogen embrittlement of steels as a physical phenomenon V. I. Shvachko OriginalPaper Pages: 449 - 460
Fracture mechanics approach to hydrogen assisted cracking: Analysis of theK-dominance condition J. ToribioV. Kharin OriginalPaper Pages: 461 - 476
Mechanism of reversible effect of hydrogen on mechanical properties of steel V. I. Tkachov OriginalPaper Pages: 477 - 484
Influence of hydrogen on the long-term strength of tire steels O. I. Balyts'kyi OriginalPaper Pages: 485 - 490
Prediction of the service life of pipeline elements subjected to the action of hydrogen-containing media O. E. AndreikivD. V. Rudavs'kyi OriginalPaper Pages: 491 - 498
Effect of high-temperature degradation of heat-resistant steel on the mechanical and fractographic characteristics of fatigue crack growth O. Z. StudentW. DudzińskiA. Kamińska OriginalPaper Pages: 499 - 508
Stress-corrosion-cracking behavior of heat-treated Al−Zn−Mg−Cu alloy with temperature J. OñoroC. Ranninger OriginalPaper Pages: 509 - 514
Influence of electrolytic hydrogenation on cyclic crack resistance of chromium-nickel steels V. I. Pokhmurs'kyiL. M. Bilyi OriginalPaper Pages: 515 - 520
Application of the method of microlocal parameters to problems of periodic thermoelastic composites S. J. Matysiak OriginalPaper Pages: 521 - 526
Modeling of surface microcracking caused by ultraviolet degradation in high-density polyethylene I. D. SkrypnykJ. L. Spoormaker OriginalPaper Pages: 527 - 534
Improvement of sulfide-corrosion resistance of gas-turbine blades with sufficient heat resistance by rational alloying I. V. Oryshych OriginalPaper Pages: 535 - 540
Rapid water quenching and formation of thermal fatigue cracks on the surface of a tube A. Ots OriginalPaper Pages: 541 - 551
Anisotropy of microhardness of directionally crystallized materials based on lanthanum hexaboride P. I. Loboda OriginalPaper Pages: 552 - 560
Iterative procedures for problems of nonisothermal elastoplasticity with isotropic kinematic hardening V. S. Mykhailyshyn OriginalPaper Pages: 561 - 571
Acoustic-emission investigation of the sensitivity of spring steel to hydrogen degradation V. R. Skal's'kyi Science for Production Pages: 572 - 580
Structural sensitivity of steels to corrosion-mechanical fracture under conditions of fatigue and cavitation O. T. Tsyrul'nykA. I. Bassarab Science for Production Pages: 581 - 586
A method for testing pipe steels under the conditions of sulfide stress cracking A. I. Astaf'evV. M. NarushevT. V. Tetyueva Science for Production Pages: 587 - 591
Influence of elastic inclusions on the strength and durability of backup rolls of rolling mills M. M. Stadnyk Science for Production Pages: 592 - 597
Internal adsorption of admixtures in precipitates of metals G. Sh. Yar-Mukhamedova Brief Communications Pages: 598 - 600
Modified electrolytic Cr-based composite coatings G. Sh. Yar-Mukhamedova Brief Communications Pages: 601 - 602