Abstract
This article investigates the effect of grain size and Cr concentration on the oxidation resistance of nanocrystalline Fe-Cr alloys having varying Cr contents between 2 and 10 wt pct. The results have been compared with microcrystalline Fe-Cr alloys with 10 and 20 wt pct Cr. Pellets of nanocrystalline and microcrystalline Fe-Cr alloys were prepared by mechanical alloying followed by hot compaction and sintering, and then oxidized at 823 K (550 °C) for 150-hours. Oxidation kinetics was determined by measuring the weight gain during oxidation, and the post-oxidation characterization of the oxide scales was performed using secondary ion mass spectroscopy. The chromium content at the inner oxide scale of nanocrystalline Fe-Cr alloys (with >7 pct Cr) was found to be comparable with that of microcrystalline 20 pctCr alloy, which suggests that nanocrystalline grain size distribution can be exploited to develop highly oxidation resistant alloys with much lower amounts of expensive alloying element (Cr). A mechanistic understanding of the high temperature oxidation in nanostructured alloys has been presented and the critical amount of bulk Cr content required to form a protective chromia layer has been calculated. The paper also investigates the role of a reactive element Zr on the high temperature oxidation resistance of nanocrystalline Fe-Cr. The beneficial effect is more pronounced at low bulk Cr (2 to 4 pct) concentrations (compared to higher Cr (>7 pct) concentration), however, at low bulk Cr, insufficient Cr enrichment occurs to establish a protective chromium oxide layer.
Similar content being viewed by others
References
A. A. Karimpoor, U. Erb, K. T. Aust and G. Palumbo, Scr. Mater., 2003, vol. 49(7), pp. 651-656.
S. Cheng, E. Ma, Y. M. Wang, L. J. Kecskes, K. M. Youssef, C. C. Koch, U. P. Trociewitz and K. Han, Acta Mater., 2005, vol. 53(5), pp. 1521-1533.
C. C. Koch, K. M. Youssef, R. O. Scattergood and K. L. Murty, Adv. Eng. Mater., 2005, vol. 7(9), pp. 787-794.
K. M. Youssef, R. O. Scattergood, K. L. Murty and C. C. Koch, Appl. Phys. Lett., 2004, vol. 85(6), pp. 929-931.
J.R. Groza: in Nanostructured Materials: Processing, Properties, and Applications, C.C. Koch, ed., William Andrew Pub., Norwich, NY, 2007.
J. H. Choi, K. I. Moon, J. K. Kim, Y. M. Oh, J. H. Suh and S. J. Kim, Journal of Alloys and Compounds, 2001, vol. 315(1-2), pp. 178-186.
C. Suryanarayana, F. Froes and G. Korth, Metall (1997). Mater. Trans. A. 28, 293-302.
S. K. Vajpai, B. V. Mahesh and R. K. Dube (2009) J. Alloys Compd, 476(1-2), 311-317.
G. Korth and R. Williamson (1995) Metall. and Mater. Trans. A. 26(10), 2571-2578.
S. K. Vajpai, R. K. Dube and A. Tewari (2008) Metall. and Mater. Trans. A, 39(11), 2725-2735.
Y. Liu and W. Liu (2007) J. Alloys Compd. 440(1-2), 154-157.
K. I. Moon and K. S. Lee (1999) J. Alloys Compd, 291(1-2), 312-321.
Y. Ji, M. Kallio and T. Tiainen, Scr. Mater., 2000, vol. 42(11), pp. 1017-1023.
B. V. Mahesh, R. K. Singh Raman and C. C. Koch, J. Mater. Sci., 2012, vol. 47(22), pp. 7735-7743.
B. V. Mahesh, R. K. Singh Raman, R. O. Scattergood and C. C. Koch, Mater. Sci. Eng. A, 2013, vol. 574, pp. 235-242.
A. U. Seybolt, Journal of the Electrochemical Society, 1960, vol. 107(3), pp. 147-156.
K. Ledjeff, A. Rahmel and M. Schorr, Oxid. Met., 1981, vol. 15, pp. 485-493.
S. Horibe and T. Nakayama, Corros. Sci., 1975, vol. 15, pp. 589.
T. Nakayama and S. Horibe, J. Jap. Inst. Met., 1973, vol. 37, pp. 1313.
K. Sasa and T. Nakayama, Corros. Sci., 1977, vol. 17, pp. 783.
C. S. Giggins and F. S. Pettit, Metall. Trans., 1969, vol. 245, pp. 2509.
M. D. Merz, Metall. Trans. A, 1979, vol. 10, pp. 71.
S. N. Basu and G. J. Yurek, Oxid. Met., 1991, vol. 36, pp. 28.
R. K. Singh Raman and R. K. Gupta, Corros. Sci., 2009, vol. 51(2), pp. 316-321.
R. K. Singh Raman, R. K. Gupta and C. C. Koch, Phil. Mag. A, 2010, vol. 90(23), pp. 3233 - 3260.
R.K. Singh Raman and P. Singh: in Nanocrystalline Structure for Oxidation Resistance at Moderate Temperatures, V.S. Saji and R. Cook, eds., Woodhead Publishing, Cambridge, U.K., 2011, pp. 129–45.
P. Kofstad, High Temperature Corrosion. Vol. 6. 1988: Elsevier Applied Science and Publishers Ltd, New York.
A. Rahmel, G. C. Wood, P. Kofstad and D. L. Douglass, Oxid. Met., 1985, vol. 23, pp. 253-337.
G. C. Wood, Corros. Sci., 1962, vol. 2(3), pp. 173-196.
J. Antill and K. Peakall, J. Iron and Steel Inst., 1967, vol. 205, pp. 1136.
A. Funkenbusch, J. Smegill and N. Bornstein, Metall. Trans. A, 1985, vol. 16, pp. 1164-1166.
C. S. Giggins, B. Kear, F. S. Pettit and J. K. Tien, Metall. Trans., 1975, vol. 5, pp. 1685.
J. K. Tien and F. S. Pettit, Metall. Trans., 1972, vol. 3, pp. 1587.
C. E. Lowell, D. L. Deadmore and J. D. Whittenberger, Oxid. Met., 1982, vol. 17, pp. 205-212.
T. N. Rhys-Jones, H. J. Grabke and H. Kudielka (1987) Mater. and Corros. 38(2), 65-72.
J. Stringer, A. Hed, G. Wallwork and B. Wilcox, Corros. Sci., 1972, vol. 32(4), pp. 511-516.
D. P. Whittle, M. E. El-Dahshan and J. Stringer, Corros. Sci., 1977, vol. 177(11), pp. 879-891.
F. A. Golightly, F. H. Stott and G. C. Wood, Oxid. Met., 1976, vol. 10, pp. 163-187.
B.A. Pint: Met. Ceram. Div., 2010, vol. 18(8), pp. 2159–68.
V. Kochubey: Effect of Ti, Hf and Zr Additions and Impurity Elements on the Oxidation Limited Lifetime of Thick and Thin-Walled FeCrAlY Components Ruhr-Universitat, Bochum, 2005.
D. P. Whittle and J. Stringer (1980) Phil. Trans. of the R. Soc. Lond. A. 295, 309-329.
C. Anghel: in Materials Science and Engineering, KTH, Stockholm, Sweden, 2004.
Z. B. Wang, N. R. Tao, W. P. Tong, J. Lu and K. Lu, Acta Mater., 2003, vol. 51(14), pp. 4319-4329.
K. Kuroda, P. A. Labun, G. Welsch and T. E. Mitchell, Oxid. Met., 1983, vol. 19, pp. 117-127.
G. E. Rhead, Trans. Faraday Soc., 1965, vol. 61, pp. 797.
C. Wagner, J. Electrochem. Soc., 1952, vol. 369, pp. 103.
C. Wagner, Z. Elektrochem., 1959, vol. 63, pp. 772.
J. H. Swisher and E. T. Turkdogan, Trans. AIME, 1967, vol. 239, pp. 426.
R. Braun and M. Feller-Kniepmeier: Phys. Status Solid. A, 1985, vol. 90 (2), pp. 553–61.
R.K. Gupta, N. Birbillis, and J. Zhang: Oxidation Resistance of Nanocrystalline Alloys, InTech, 2012. ISBN: 978-953-51-0467-4.
A. W. Bowen and G. Leak, Metall. Trans., 1970, vol. 1, pp. 1695.
I. Kaur, W. Gust and L. Kozma, Handbook of grain and interphase boundary diffusion data. 1989, Stuttgart: Ziegler Press.
Author information
Authors and Affiliations
Corresponding author
Additional information
Manuscript submitted February 4, 2014.
Rights and permissions
About this article
Cite this article
Mahesh, B.V., Singh Raman, R.K. & Koch, C.C. Resistance of Nanostructured Fe-Cr Alloys to Oxidative Degradation: Role of Zr and Cr Contents. Metall Mater Trans A 46, 1814–1824 (2015). https://doi.org/10.1007/s11661-015-2765-z
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11661-015-2765-z