Electrospinning Synthesis of ZIF-67/PAN Fibrous Membrane with High-capacity Adsorption for Malachite Green

  • Published:
Fibers and Polymers Aims and scope Submit manuscript

Abstract

Metal-organic frameworks (MOFs) exhibit great potential for dye adsorption. However, MOF powder is difficult to remove from aqueous solution, which hinders the practical application of MOFs. Integration of MOFs on polymeric fibrous membrane provides a new strategy to reach the achievements that not only keep the adsorption ability of MOFs for dyes, but also easily remove the MOF/dye complex from water. Here, we successfully synthesize zeolitic imidazole framework-67/polyacrylonitrile (ZIF-67/PAN) fibrous membrane with ZIF-67 loading ratio of 54 % by electrospinning method. The average diameters of ZIF-67 nanoparticles and ZIF-67/PAN fibers are about 200 nm and 0.72 µm, respectively. The adsorption process of MG on ZIF-67 nanoparticles or ZIF-67/PAN fibers followed a pseudo-second-order kinetic model and fitted Langmuir isotherm. The maximum adsorption capacities of ZIF-67 nanoparticles and ZIF-67/PAN fibers are 2545 and 1305 mg·g−1, respectively. After four regeneration cycles, the ZIF-67/PAN fibers membrane still exhibit over 92 % of the original capacity of ZIF-67/PAN fibers. In addition, ZIF-67/PAN fibers also show good adsorption abilities for Congo red (849 mg·g−1) and Basic fuschin (730 mg·g−1). Therefore, ZIF-67/PAN fibers would be as a promising adsorbent for the removal of dye in industrial application because of its simple preparation method, excellent adsorption property, ease of separation and favorable reusability.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Similar content being viewed by others

References

  1. S. Nethaji, A. Sivasamy, G. Thennarasu, and S. Saravanan, J. Hazard. Mater., 181, 271 (2010).

    Article  CAS  PubMed  Google Scholar 

  2. E. S. Baeissa, J. Alloys Compd., 672, 564 (2016).

    Article  CAS  Google Scholar 

  3. D. J. Alderman and R. S. Clifton-Hadley, J. Fish. Dis., 16, 297 (1993).

    Article  CAS  Google Scholar 

  4. S. Shanmugam, P. S. Ulaganathan, K. Waminathan, S. Sadhasivam, and Y. R. Wu, Inter. Biodeter. Biodegr., 125, 258 (2017).

    Article  CAS  Google Scholar 

  5. Y. Panahian and N. Arsalani, J. Phys. Chem. A, 121, 5614 (2017).

    Article  CAS  PubMed  Google Scholar 

  6. B. H. Hameed and T. W. Lee, J. Hazard. Mater., 164, 468 (2009).

    Article  CAS  PubMed  Google Scholar 

  7. L. Jin, X. Zhao, X. Qian, and M. Dong, J. Colloid. Interf. Sci., 509, 245 (2018).

    Article  CAS  Google Scholar 

  8. N. P. Raval, P. U. Shah, and N. K. Shah, Appl. Clay. Sci., 7, 3407 (2017).

    CAS  Google Scholar 

  9. J. R. Li, J. Sculley, and H. C. Zhou, Chem. Soc. Rev., 112, 869 (2011).

    Article  CAS  Google Scholar 

  10. S. H. Huo and X. P. Yan, J. Mater. Chem., 22, 7449 (2012).

    Article  CAS  Google Scholar 

  11. X. Y. Xu, J. Zhang, X. Zhao, H. Fu, C. Chu, P. Wang, and C. C. Wang, ACS Appl. Nano Mater., 2, 418 (2019).

    Article  CAS  Google Scholar 

  12. X. Y. Xu, C. Chu, H. Fu, X. D. Du, P. Wang, W. Zheng, and C. C. Wang, Chem. Eng. J., 350, 436 (2018).

    Article  CAS  Google Scholar 

  13. J. J. Li, C. C. Wang, H. F. Fu, J. R. Cui P. Xu, J. Guo, and J. R. Li, Dalton Trans., 46, 10197 (2017).

    Article  CAS  PubMed  Google Scholar 

  14. Y. Yan, Y. Luo, J. Ma, B. Li, H. Xue, and H. Pang, Small, 14, 1801815 (2018).

    Article  CAS  Google Scholar 

  15. Y. Yan, B. Li, W. Guo, H. Pang, and H. Xue, J. Power Sources, 329, 148 (2016).

    Article  CAS  Google Scholar 

  16. Y. Yan, H. Xu, W. Guo, Q. Huang, M. Zheng, H. Pang, and H. Xue, Inorg. Chem. Front., 3, 791 (2016).

    Article  CAS  Google Scholar 

  17. Y. Yan, T. Wang, X. Li, H. Pang, and H. Xue, Inorg. Chem. Front., 4, 33 (2017).

    Article  CAS  Google Scholar 

  18. K. Gupta, D. Gupta, and O. P. Khatri, Appl. Surf. Sci., 476, 647 (2019).

    Article  CAS  Google Scholar 

  19. J. J. Li, C. C. Wang, J. Guo, J. R. Cui, P. Wang, and C. Zhao, Polyhedron, 139, 89 (2018).

    Article  CAS  Google Scholar 

  20. A. Liu, C. C. Wang, C. Z. Wang, H. F. Fu, W. Peng, Y. L. Cao, H. Y. Chu, and A. F. Du, J. Colloid. Interf. Sci., 730, 512 (2018).

    Google Scholar 

  21. Y. Yan, P. Gu, S. Zheng, M. Zheng, H. Pang, and H. Xue, J. Mater. Chem. A, 4, 19078 (2016).

    Article  CAS  Google Scholar 

  22. K. Y. A. Lin and H. A. Chang, Chemosphere, 139, 624 (2015).

    Article  CAS  PubMed  Google Scholar 

  23. K. Y. A. Lin and W. D. Lee, Appl. Surf. Sci., 361, 114 (2016).

    Article  CAS  Google Scholar 

  24. L. Fan, M. Xue, Z. Kang, H. Li, and S. Qiu, J. Mater. Chem., 22, 25272 (2012).

    Article  CAS  Google Scholar 

  25. Y. N. Wu, F. Li, H. Liu, W. Zhu, M. Teng, Y. Jiang, and G. Li, J. Mater. Chem., 22, 16971 (2012).

    Article  CAS  Google Scholar 

  26. Y. Chen, X. Li, K. Park, W. Lu, C. Wang, W. Xue, F. Yang, J. Zhou, L. Suo, T. Lin, H. Huang, J. Li, and J. B. Goodenough, Chem., 3, 152 (2017).

    Article  CAS  Google Scholar 

  27. Q. Niu, J. Guo, B. Chen, J. Nie, X. Guo, and G. Ma, Carbon, 114, 250 (2017).

    Article  CAS  Google Scholar 

  28. R. Ostermann, J. Cravillon, C. Weidmann, M. Wiebcke, and B. M. Smarsly, Chem. Commun., 47, 442 (2011).

    Article  CAS  Google Scholar 

  29. M. R. Armstrong, K. Y. Y. Arredondo, C. Y. Liu, J. E. Stevens, A. Mayhob, B. Shan, and B. Mu, Ind. Eng. Chem. Res., 54, 12386 (2015).

    Article  CAS  Google Scholar 

  30. M. Gao, L. Zeng, J. Nie, and G. Ma, RSC Adv., 6, 7078 (2016).

    Article  CAS  Google Scholar 

  31. N. D. Shooto, C. W. Dikio, D. Wankasi, L. M. Sikhwivhilu, F. M. Mtunzi, and E. D. Dikio, Nanoscale Res. Lett., 11, 414 (2016).

    Article  PubMed  PubMed Central  CAS  Google Scholar 

  32. G. Wang, H. Zhang, J. Wang, Z. Ling, and J. Qiu, Sep. Purif. Technol., 177, 257 (2017).

    Article  CAS  Google Scholar 

  33. L. E. Lange, F. O. Ochanda, S. K. Obendorf, and J. P. Hinestroza, Fiber. Polym., 15, 200 (2014).

    Article  CAS  Google Scholar 

  34. C. Liu, Y. N. Wu, C. Morlay, Y. Gu, B. Gebremariam, X. Yuan and F. Li, ACS Appl. Mater. Inter., 8, 2552 (2016).

    Article  CAS  Google Scholar 

  35. A. F. Gross, E. Sherman, and J. J. Vajo, Dalton T., 41, 5458 (2012).

    Article  CAS  Google Scholar 

  36. H. T. Kwon, H. K. Jeong, A. S. Lee, H. S. An, and J. S. Lee, J. Am. Chem. Soc., 137, 12304 (2015).

    Article  CAS  PubMed  Google Scholar 

  37. C. Wang, C. Liu, J. Li, X. Sun, J. Shen, W. Han, and L. Wang, Chem. Comm., 53, 1751 (2017).

    Article  CAS  PubMed  Google Scholar 

  38. L. N. Jin, X. Y. Qian, J. G. Wang, H. Aslan, and M. Dong, J. Colloid. Interf. Sci., 453, 270 (2015).

    Article  CAS  Google Scholar 

  39. X. X. Huang, L. G. Qiu, W. Zhang, Y. P. Yuan, X. Jiang, A. J. Xie, and J. F. Zhu, CrystEngComm, 14, 1613 (2012).

    Article  CAS  Google Scholar 

  40. S. Patel and G. Hota, Fiber. Polym., 15, 2272 (2014).

    Article  CAS  Google Scholar 

  41. Z. Li, G. Zhou, H. Dai, M. Yang, Y. Fu, Y. Ying, and Y. Li, J. Mater. Chem. A, 6, 3402 (2018).

    Article  CAS  Google Scholar 

  42. R. Xu, M. Jia, Y. Zhang, and F. Li, Micropor. Mesopor. Mat., 149, 111 (2012).

    Article  CAS  Google Scholar 

  43. X. P. Luo, S. Y. Fu, Y. M. Du, J. Z. Guo, and B. Li, Micropor. Mesopor. Mat., 237, 268 (2017).

    Article  CAS  Google Scholar 

  44. H. Liu, L. Chen, and J. Ding, Rsc. Adv., 6, 48884 (2016).

    Article  CAS  Google Scholar 

  45. R. U. A. N. Chang-Ping, A. I. Ke-Long, and L. U. Le-Hui, Chinese J. Anal. Chem., 44, 224 (2016).

    Article  Google Scholar 

  46. F. Jiang, D. M. Dinh, and Y. L. Hsieh, Carbohyd. Polym., 173, 286 (2017).

    Article  CAS  Google Scholar 

  47. H. Liu, Z. Mo, L. Li, F. Chen, Q. Wu, and L. Qi, J. Chem. Eng. Data, 62, 3036 (2017).

    Article  CAS  Google Scholar 

  48. X. Feng, T. Wu, and M. A. Carreon, J. Cryst. Growth, 455, 152 (2016).

    Article  CAS  Google Scholar 

  49. X. D. Du, C. C. Wang, J. G. Liu, X. D. Zhao, J. Zhong, Y. X. Li, J. Li, and P. Wang, J. Colloid. Interf. Sci., 506, 437 (2017).

    Article  CAS  Google Scholar 

Download references

Acknowledgements

This work was supported by the National Natural Science Foundation of China (No. 21401081) and the Senior Intellectuals Fund of Jiangsu University (No. 14JDG058).

Author information

Authors and Affiliations

  1. Institute for Advanced Materials, and School of Materials Science and Engineering, Jiangsu University, Zhenjiang, 212013, China

    Lina Jin, Jian Ye & Xinye Qian

  2. Center for DNA Nanotechnology (CDNA), Interdisciplinary Nanoscience Center (iNANO), Aarhus University, DK-8000, Aarhus, Denmark

    Yin Wang & Mingdong Dong

Authors
  1. Lina Jin
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Jian Ye
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Yin Wang
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Xinye Qian
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Mingdong Dong
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Xinye Qian.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Jin, L., Ye, J., Wang, Y. et al. Electrospinning Synthesis of ZIF-67/PAN Fibrous Membrane with High-capacity Adsorption for Malachite Green. Fibers Polym 20, 2070–2077 (2019). https://doi.org/10.1007/s12221-019-1196-7

Download citation

  • Received:

  • Revised:

  • Accepted:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s12221-019-1196-7

Keywords

Search

Navigation