Abstract
The magnetocaloric effect (MCE) of Ni0.4Cu0.2Zn0.4Fe2-xDyxO4 (x = 0.02, 0.03, and 0.04) nanoferrites is simulated using a phenomenological model. The analysis indicates that the MCE of Ni0.4Cu0.2Zn0.4Fe2-xDyxO4 nanoferrites is strongly influenced by Dy content in both conventional and inverse MCE. For conventional MCE, the full-width at half-maximum (\(\delta {\text{T}}_{{{\text{FWHM}}}}\)) has significant values, ranging between 200 K and 258 K for Ni0.4Cu0.2Zn0.4Fe2-xDyxO4 nanoferrites. However, for inverse MCE, \(\delta {\text{T}}_{{{\text{FWHM}}}}\) ranges between 25 and 55 K. The MCE of the Ni0.4Cu0.2Zn0.4Fe2-xDyxO4 system covers an extensive temperature range and is a particularly interesting prospect for nitrogen and hydrogen liquefaction.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
The magnetocaloric effect (MCE) is a magneto-thermodynamic phenomenon that arises in the absorption or generation of heat by such magnetically ordered material when the applied magnetic field (Hexe) is changed.1,2,3,4,5 Because of the advantages of magnetic refrigeration (MR) including environmental safety, higher efficiency, and the ability to be implemented in a wide range of temperatures, it has become an appealing replacement for traditional refrigeration systems.6,7,8,9,10,11 Many decades have been spent studying a broad range of materials that demonstrate acceptable magnetocaloric (MC) characteristics at ambient or even low temperatures.9,12,13,14,15,16,17,18 MR could be used for gas liquefaction, specifically helium, nitrogen, and hydrogen liquefaction, as well as for research activities and low-temperature space applications.19 MR reflects the concept of applying MCE to MC material at temperatures near that of a magnetic phase transition.14,15,16,17,18,19 An initial response of adiabatic demagnetization occurs in traditional MCE as a cooling action in MC material, which is carried out with the abrupt removal of the Hexe.20,21,22,23,24 However, adiabatic magnetization can cool MC materials that experience a sudden increase in the Hexe, which is called an inverse MCE.4 This inverse MCE is seen in antiferromagnetic (AFM) materials over the AFM transition temperature range.
Magnetic nanoparticles (MNPs) are an excellent replacement for bulk MCE materials due to the ease of assembly in the form of thin film and other desirable features, including their influence over the ∆SM throughout the superparamagnetic–blocking transition.24 Theoretically, decreasing the particle size to nearer the single magnetic domain enhances ∆SM by many orders of magnitude when contrasted with ∆SM in bulk materials.24 Furthermore, the high surface area of nano-materials would enhance the exchange of heat with the surroundings, and it would be possible to modify the exchange of heat between MNPs and the surroundings by carefully designing core structures. Furthermore, different MNP sizes have the potential to achieve a broader range of cooling.25,26
The Ni-Cu-Zn ferrite is a soft ferrite with high \(T_{MPT}\), large electrical resistivity and extreme permeability in the radio-frequency range. Ni-Cu-Zn ferrites are used primarily as transformer cores, inductors, recording heads, and deflection yokes.27,28 Optimizing NiCuZn ferrites by modifying the portions of metal ions in the formula or doping with new metals has recently been investigated. When the ferric ion was partially replaced with RE ions (Gd3+ Eu3+, Sm3+, and Pr3+), a distortion in the crystal structure of the Ni0.4Cu0.2Zn0.4 ferrite was noted, as was an improvement in its magnetic properties.29
Almessiere et al. used the sol-gel method to prepare Ni0.4Cu0.2Zn0.4Fe2-xDyxO4 (x ≤ 0.04) nanoferrites, which showed superparamagnetic behaviour and broadly second-order FM–paramagnetic phase transitions for all samples, along with an AFM–paramagnetic phase transition at extremely low temperatures.30 We were thus highly motivated to investigate the MCE of Ni0.4Cu0.2Zn0.4Fe2-xDyxO4 nanoferrites in this work, based on this useful point. In this research, a phenomenological model (PM) is used to investigate the thermomagnetic properties of Ni0.4Cu0.2Zn0.4Fe2-xDyxO4 nanoferrites using simulated magnetization temperature curves, resulting in ∆SM, heat capacity change (\(\Delta \, C_{P,H}\)), and relative cooling power (RCP).
Theoretical Considerations
The PM provides the relationship between magnetization (M) and temperature (T) as follows31,32:
where \(M_{i}\) is an initial value of magnetization at the FM–paramagnetic or AFM–paramagnetic transition, and \(M_{f}\) is a final value of this transition as shown in Fig. 1, where \(\alpha = \frac{2(\beta - \gamma )}{{M_{i} - M_{f} }}.\), \(\beta = \left( {\frac{dM}{{dT}}} \right)_{average}\) for FM or AFM phase, and \(\gamma = \left( {\frac{dM}{{dT}}} \right)_{{T = T_{MFT} }}\).
Results and Discussion
To simulate the MCE of Ni0.4Cu0.2Zn0.4Fe2-xDyxO4, PM parameters for Ni0.4Cu0.2Zn0.4Fe2-xDyxO4 were obtained directly from experimental results (magnetization vs temperature), as described in Almessiere et al.30 The magnetization versus temperature for Ni0.4Cu0.2Zn0.4Fe2-xDyxO4 nanoferrites measured at 0.01T is depicted in Fig. 2, with experimental data from Almessiere 30 expressed by symbols and simulated data expressed by dashed lines.
There appears to be reasonable agreement between the experimental and theoretical values of M(T) for Ni0.4Cu0.2Zn0.4Fe2-xDyxO4 nanoferrites, implying that PM is an appropriate model for fitting FM–paramagnetic and AFM transitions. Interestingly, it seems that, in addition to conventional MCE, an inverse MCE for Ni0.4Cu0.2Zn0.4Fe2-xDyxO4 nanoferrites is present at very low temperatures, as we will later explore.
\(\Delta S_{M}\) of Ni0.4Cu0.2Zn0.4Fe2-xDyxO4 nanoferrites under an adiabatic magnetic field shift (ΔH) of 0.01 T is formulated by
The maximum \(\Delta S_{M}\) (∆SMax) can be determined as follows:
The simulated temperature dependence of ∆SM for Ni0.4Cu0.2Zn0.4Fe2-xDyxO4 nanoferrites is depicted in Fig. 3. Importantly, the thermomagnetic behaviour of Ni0.4Cu0.2Zn0.4Fe2-xDyxO4 nanoferrites is strongly dependent on Dy content, leading to the conclusion that the thermomagnetic behaviour of Ni0.4Cu0.2Zn0.4Fe2-xDyxO4 nanoferrites is characterized as a conventional MCE over temperatures higher than 78, 62, and 39 K for doping levels x = 0.02, 0.03, and 0.04, respectively. However, the thermomagnetic behaviour of Ni0.4Cu0.2Zn0.4Fe2-xDyxO4 nanoferrites is characterized as an inverse MCE at lower temperatures. As a result, Ni0.4Cu0.2Zn0.4Fe2-xDyxO4 nanoferrites could be operated in MR that uses magnetization and demagnetization processes to exploit both positive and negative magnetic entropy variations. |∆SMax| is significantly reduced when the Dy content is high. The fact that Dy+3 ions are favoured to exist in the B sites, which can be attributed to their large ionic radii, could explain this decreasing trend. As a result of the Fe3+ replacement by Dy3+, the crystal symmetry is reduced, implying that the distance between Dy–O will be smaller than the distance between Fe–O.33 Consequently, some of the corresponding ions display aligned antiparallel moments with regard to others in these sites, causing a drop in net magnetic moments just on B sites. As Dy3+ content increases, further cations on B sites exhibit antiparallel moments. To put it another way, the decrease in |∆SM| at high content in samples is due to surface spin effects and cation distribution on various sites. Despite the fact that magnetic moments are no longer directed linearly, nonlinear spins of magnetic ions exist due to spin frustration.33 The increase in migration of Fe3+ cations from tetrahedral to octahedral sites with the goal of occupying the increasing Dy3+ ions causes the reduction drop in the |∆SM|. The increased presence of Fe3+ cations in octahedral B sites due to site preference causes an increase in spin canting and antiparallel spin coupling, reducing the |∆SM| and weak super-exchange interactions between tetrahedral and octahedral sites, lowering the magnetization.34 Furthermore, the ionic radii for various elements, and also the critical A–B super-exchange interactions between many magnetic ions, could be used to deduce the influence of Dy3+ ions on magnetic characteristics. Dy3+ ions have an ionic radius of 0.912 Å, indicating that they prefer to be found on B sites. The ionic radii that are subjected to substitution differ greatly, causing disorder in the electronic states and internal strains in the crystal structure. This has an impact on the A–B super-exchange interactions between metal sites A and B.35,36 Furthermore, variations in the drop in |∆SM| at high Dy3+ content can be explained by crystallite size variation. Indeed, as the Dy3+ content increases, the crystallite size decreases, resulting in a reduction in magnetization and, as a result, a decrease in |∆SM|.
The |∆SMax| and full-width at half-maximum (\(\delta {\text{T}}_{{{\text{FWHM}}}}\)) of the SM curve are used to account for RCP as follows.
where \(\delta {\text{T}}_{{{\text{FWHM}}}}\) can be obtained as follows:
For conventional MCE, the calculations show that \(\delta {\text{T}}_{{{\text{FWHM}}}}\) has significant values, ranging between 200 K and 258 K for Ni0.4Cu0.2Zn0.4Fe2-xDyxO4 nanoferrites under ΔH of 0.01 T. However, for inverse MCE, the range of \(\delta {\text{T}}_{{{\text{FWHM}}}}\) is between 25 K and 55 K. Furthermore, for conventional MCE, RCP is between 0.05 J/Kg and 0.08 J/Kg, whereas for inverse MCE, RCP is between 0.007 J/Kg and 0.01 J/Kg.
The characterization of curves for Ni0.4Cu0.2Zn0.4Fe2-xDyxO4 nanoferrites can be explained as follows, according to the PM model31,32:
∆CP,H versus temperature simulations for Ni0.4Cu0.2Zn0.4Fe2-xDyxO4 nanoferrites at ΔH of 0.01 T are shown in Fig. 4. Over the range of the AFM transition, the simulated \(\Delta \, C_{P,H}\) of all samples varies from a positive to a negative value. However, over the range of the FM transition, an inverse characterization is observed. Finally, Ni0.4Cu0.2Zn0.4Fe2-xDyxO4 nanoferrites are fascinating MC materials in MR, particularly between 10 and 325 K. Furthermore, they have high resistivity, small hysteresis, low loss of eddy current, and the energy loss is negligible.30 The MCE and the electrocaloric effect both contribute to the future of refrigeration technology.37,38,39,40,41,42,43,44,45,46,47,48,49,50,51,52,53,54,55,56,57,58,59,60,61,62,63,64,65,66,67
Conclusion
MCE simulations were performed on Ni0.4Cu0.2Zn0.4Fe2-xDyxO4 nanoferrites synthesized using the sol–gel method. The simulation results show that this PM is an efficient model for calculating the thermomagnetic properties of Ni0.4Cu0.2Zn0.4Fe2-xDyxO4 nanoferrites for both FM–AFM and FM–paramagnetic transitions. The thermomagnetic behaviour of Ni0.4Cu0.2Zn0.4Fe2-xDyxO4 nanoferrites demonstrates both conventional and inverse MCE. The Ni0.4Cu0.2Zn0.4Fe2-xDyxO4 nanoferrites are an interesting possibility for MR because they cover a wide temperature range, especially liquefaction of nitrogen and hydrogen, even at room temperature.
References
M. Hsini, S. Hcini and S. Zemni, J. Supercond. Nov. Magn. 31, 81 (2018).
E.M. Ahmed, O.M. Hemeda, H.R. Alamri and S.M. Elghnam, Phase Trans. 94, 835–841 (2021).
E.M. Ahmed, H.R. Alamri, S.M. Elghnam, O. Eldarawi, T.E. Tawfik, A.M. Mahmoud, S.E. Elwan, O.M. Hemeda, M.A. Hamad and G.A. Hussein, Phys Solid State (2021). https://doi.org/10.1134/S1063783421100024.
E.M. Ahmed, O.M. Hemeda, H.R. Alamri, S.M. Elghnam and M.A. Hamad, Phys. Met. Metallogr. 122, 1454–1457 (2021).
B. Alzahrani, M. Hsini, S. Hcini, M. Boudard, A. Dhahri and M.L. Bouazizi, J. Low Temp. Phys. 200, 26–39 (2020).
A.M. Ewas, Ceram. Int. 43, 7660 (2017).
R. Kumar, Mater. Today 4, 5544 (2017).
A.H. El-Sayed, J. Supercond. Nov. Magn. 32, 1447 (2019).
M.A. Hamad, Process. Appl. Ceram. 9, 11 (2015).
N. Mechi, B. Alzahrani, S. Hcini, M.L. Bouazizi and A. Dhahri, Phase Trans. 91, 559 (2018).
H.R. Alamri, S.M. Elghnam, O.M. Hemeda and M.A. Hamad, Phys. Solid State 63, 1332–1336 (2021).
E. Villa, C. Tomasi, A. Nespoli, F. Passaretti, G. Lamura and F. Canepa, J. Mater. Res. Technol. 9, 2259 (2020).
H. Xiang, Y. Xing, F. Dai, H. Wang, L. Su, L. Miao and L. Sheng-Guo, J. Adv. Ceram. 10, 385–441 (2021).
M. Jeddi, H. Gharsallah, M. Bekri, E. Dhahri and E.E.K. Hlil, J. Low Temp. Phys. 198, 135 (2020).
A.H. El-Sayed, O.M. Hemeda, M.A. Hamad and A.M. Mohamed, Eur. Phys. J. Plus. 134, 227 (2019).
A.H. El-Sayed, O.M. Hemeda, M.A. Hamad and A.M. Mohamed, J. Supercond. Nov. Magn. 33, 769–773 (2020).
M.A. Hamad, O.M. Hemeda, H.M. Alamri, A.M. Mohamed, J. Supercond. Nov. Magn. 33, 3853–3856 (2020)
A.H. El-Sayed and M.A. Hamad, Phase Trans. 92, 517 (2019).
M.A. Hamad, H.R. Alamri and M.E. Harb, J. Low Temp. Phys. 204, 57–63 (2021).
A.H. El-Sayed and M.A. Hamad, J. Supercond. Nov. Magn. 31, 4167–4171 (2018).
A.H. El-Sayed and M.A. Hamad, J. Supercond. Nov. Magn. 31, 1895 (2018).
A.H. El-Sayed and M.A. Hamad, J. Supercond. Nov. Magn. 31, 4091–4094 (2018).
M.A. Hamad, O.M. Hemeda, H.R. Alamri and A.M. Mohamed, J. Low Temp. Phys. 202, 121–127 (2021).
R.D. McMichael, R.D. Shull, L.J. Swartzendruber, L.H. Bennett and R.E. Watson, J. Magn. Magn. Mater. 111, 29 (1992).
R.D. Shull, IEEE Trans. Magn. 29, 2614 (1993).
J. Chen, H. Su, Y. Jing, Y. Li, X. Tang and Q. Lu, Ceram. Int. 47, 20638–20642 (2021).
B.R. Shaikh, B.G. Toksha, S.E. Shirsath, A. Chatterjee, S. Tonde and S.Q. Chishty, J. Magn. Magn. Mater. 537, 168229 (2021).
X. Wu, J. Xu, X. Huo, J. Chen, Q. Zhang, F. Huang and L. Li, J. Eur. Ceram. Soc. 41, 5193–5200 (2021).
H. Harzali, A. Marzouki, F. Saida, A. Megriche and A. Mgaidi, J. Magn. Magn. Mater. 460, 89–94 (2018).
M.A. Almessiere, Y. Slimani, H. Güngünes, A. Demir Korkmaz, S.V. Trukhanov, S. Guner, F. Alahmari, A.V. Trukhanov and A. Baykal, Mater. Sci. Eng. B 270, 115202 (2021).
M.A. Hamad, Phase Trans. 85, 106 (2012).
M.A. Hamad, Int. J. Thermophys. 36, 2748 (2015).
K. Kamala Bharathi, J. Arout Chelvane and G. Markandeyulu, J. Magn. Magn. Mater. 321, 3677–3680 (2009).
M.S.R. Prasad, B.B.V.S.V. Prasad, B. Rajesh, K.H. Rao and K.V. Ramesh, J. Magn. Magn. Mater. 323, 2115 (2011).
P. Samoila, L. Sacarescu, A.I. Borhan, D. Timpu, M. Grigoras, N. Lupu, M. Zaltariov and V. Harabagiu, J. Magn. Magn. Mater. 378, 92–97 (2015).
A. Sadaqat, M. Almessiere, Y. Slimani, S. Guner, M. Sertkol, H. Albetran, A. Baykal, S.E. Shirsath, B. Ozcelik and I. Ercan, Ceram. Int. 45, 22538–22546 (2019).
M.A. Hamad and H.R. Alamri, J. Low Temp. Phys. 207, 181–189 (2022).
M.A. Hamad, J. Adv. Dielect. 4, 1450026 (2014).
M.A. Hamad, J. Supercond. Nov. Magn. 28, 2525–2528 (2015).
M.A. Hamad, J. Supercond. Nov. Magn. 28, 3365 (2015).
M.A. Hamad, J. Supercond. Nov. Magn. 29, 2867–2871 (2016).
M.A. Hamad, Int. J. Thermophys. 34, 1158–1165 (2013).
M.A. Hamad, J. Supercond. Nov. Magn. 28, 3329–3333 (2015).
M.A. Hamad, J. Adv. Dielect. 3, 1350008 (2013).
M.A. Hamad, O.M. Hemeda, H.R. Alamri, M.E. Harb and A.M. Mohamed, Phys. Solid State 63, 709–713 (2021).
M.A. Hamad, J. Supercond. Nov. Magn. 27, 2569 (2014).
M.A. Hamad, J. Supercond. Nov. Magn. 29, 539–1543 (2016).
M.A. Hamad and H.R. Alamri, J. Mater. Res. Technol. 17, 2670–2674 (2022).
A.H. El-Sayed and M.A. Hamad, J. Supercond. Nov. Magn. 31, 3357 (2018).
M.A. Hamad and H.R. Alamri, J. Supercond. Nov. Magn. 35, 515–518 (2022).
E.M. Ahmed, O.M. Hemeda, H.R. Alamri et al., Magnetocaloric Effect in α’-MnB Nanoparticles. Russ. J. Phys. Chem. 96, S101–S104 (2022).
M.A. Hamad, J. Supercond. Nov. Magn. 31, 337 (2018).
M.A. Hamad, J. Supercond. Nov. Magn. 27, 223 (2014).
M.A. Hamad, Process. Appl. Ceram. 11, 225–229 (2017).
M.A. Hamad, O.M. Hemeda, H.R. Alamri and A.M. Mohamed, J. Mater. Res. Technol. 11, 1356–1361 (2021).
M.A. Hamad, J. Comput. Electron. 11, 344 (2012).
M.A. Hamad, J. Adv. Dielect. 3, 1350029 (2013).
M.A. Hamad, J. Supercond. Nov. Magn. 27, 1777 (2014).
M.A. Hamad, O.M. Hemeda, H.R. Alamri and A.M. Mohamed, Phys. Lett. A. 394, 127204 (2021).
M.A. Hamad, J. Supercond. Nov. Magn. 27, 269–272 (2014).
M.A. Hamad, Process. Appl. Ceram. 10, 33 (2016).
M.A. Hamad and H.R. Alamri, Front. Mater. 9, 832703 (2022).
M.A. Hamad, O.M. Hemeda and A.M. Mohamed, J. Supercond. Nov. Magn. 33, 2753–2757 (2020).
M.A. Hamad and H.R. Alamri, Phys. Metals Metallogr. 122, 1458–1462 (2021).
M.A. Hamad, J. Supercond. Nov. Magn. 28, 2223 (2015).
M.A. Hamad, O.M. Hemeda and A.M. Mohamed, J. Supercond. Nov. Magn. 33, 2521–2525 (2020).
M.A. Hamad, J. Supercond. Nov. Magn. 29, 1539 (2016).
Funding
Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB).
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
The authors declare that they have no conflict of interest.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Hamad, M.A., Alamri, H.R. The Inverse and Conventional Magnetocaloric Effects in Ni0.4Cu0.2Zn0.4Fe2-xDyxO4 Nanoferrites Over an Extraordinary Temperature Range. J. Electron. Mater. 51, 3359–3363 (2022). https://doi.org/10.1007/s11664-022-09633-4
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-022-09633-4