Abstract
Biological agents are getting a noticeable concern as efficient eco-friendly method for nanoparticle fabrication, from which fungi considered promising agents in this field. In the current study, two fungal species (Embellisia spp. and Gymnoascus spp.) were isolated from the desert soil in Saudi Arabia and identified using 18S rRNA gene sequencing then used as bio-mediator for the fabrication of silver nanoparticles (AgNPs). Myco-synthesized AgNPs were characterized using UV–visible spectrometry, transmission electron microscopy, Fourier transform infrared spectroscopy and dynamic light scattering techniques. Their antibacterial activity against Escherichia coli, Pseudomonas aeruginosa, Staphylococcus aureus, and Klebsiella pneumoniae were investigated. In atrial to detect their possible antibacterial mechanism, Sodium dodecyl sulfate (SDS-PAGE) and TEM analysis were performed for Klebsiella pneumoniae treated by the myco-synthesized AgNPs. Detected properties of the fabricated materials indicated the ability of both tested fungal strains in successful fabrication of AgNPs having same range of mean size diameters and varied PDI. The efficiency of Embellisia spp. in providing AgNPs with higher antibacterial activity compared to Gymnoascus spp. was reported however, both indicated antibacterial efficacy. Variations in the protein profile of K. pneumoniae after treatments and ultrastructural changes were observed. Current outcomes suggested applying of fungi as direct, simple and sustainable approach in providing efficient AgNPs.
Similar content being viewed by others
Introduction
A great concern has been given to the potential uses of the metal nanoparticles (MN) that have size in the range 1–100 nm, due to their significant optical1, physical2, and chemical3 characteristics in relation to their bulk origin. Such unique properties facilitated their applications in various fields of science and technology. In the medical and food sectors, for both biosensing and microbial detection, MN could be ideal because of their biocompatibility, ability in electron transfer, and reaction catalysis4, beside other applications in diagnosis and therapy. MN could rapidly detect the microbes and tumor cells disease-related biomarkers, however, they also demonstrate capability for single-cell evaluation5.
Biomedical and biotechnological applications are the cornerstone for MN usage. Some of their important biomedical applications, but not limited to, are anti-inflammatory, antioxidant, antibacterial, antifungal, cytotoxic, drug delivery and detecting agents6,7. However, bioremediation, biodeterioration and wastewater treatment are their most known biotechnological applications8,9. Among the MN, silver nanoparticles (AgNPs) attracted a great interest due to their chemical, physical and biological characteristics10,11. AgNPs have high ability against microbes, and cancer cells12 besides, they have been used also in wound dressings, diagnostics, catalysis, biosensors and drug delivery13,14,15. Alongside the aforementioned biomedical applications, AgNPs can be applied in different biotechnology lines, such as food preservation and water filtration, in addition to spray and sanitization13,16.
With the emergence of antimicrobial resistance, the need for alternative antimicrobial agents to replace the conventional ones enhanced researchers to develop AgNPs as one of the good options for microbial mitigation. Previous studies have approved the ability of AgNPs as antimicrobial agents with significant effects against some multidrug- resistant bacteria12,17,18. The unique and wide range of AgNPs applications are the factors that led to the development of various fabrication methods for efficient and safe usage19,20,21.
Although chemical and physical methods are the best ways to develop nanoparticles with unique size and shape in a short time, however, their weakness points are the high cost and the production of hazardous by-products22,23. Therefore, the green route could be a good alternative because it is an easy, applicable, and eco-friendly approach. Such route includes using microbes and plants, beside other biomolecules as biogenic agents14,16.
Stable nanoparticles with better distributed size and morphology were noted from the biogenic approach in relation to those produced by other methods24. The molecules from biogenic agents that may cap the MN enhance their stability and dispersity25. Generally, nanoparticles produced with the aid of biological routes are harmless, environmentally benign that can be used in agriculture, medicine, biochemical detection and related fields. On this regard, the use of microbes as one approach of the biogenic synthesis is gaining great interest. From which fungi can be used for AgNPs development by extra or intracellular approaches however, the extracellular processis easier and faster than the intracellular one26. Previous studies demonstrated extracellular approach for AgNPs fabrication using fungi18,25 Employment of fungi is an important fabrication approach due to their ability to produce greater amounts of proteins in relation bacteria27 and their high intracellular metal uptake and binding capacity28. In this respect, it is expected that, fungi from extreme conditions might have unique compounds that enhance their ability to withstand harsh environments, but also could help efficiently in AgNPs production. Therefore, the current study was designed to provide new candidates in AgNPs fabrication as safe approach in providing high stable and active materials. Two fungal species (Embellisia spp. and Gymnoascus spp.) isolated from the desert soils in Saudi Arabia, not addressed before, were selected. Hence, present study represents the first report on these two species as biogenic agents in extracellular AgNPs fabrication using fungal filtrate as source of their biomolecules. Thereafter, the fabricated AgNPs were characterized using UV, DLS, TEM, SEM, and FTIR and tested against some bacterial pathogenic strains. In a trial to detect the possible antibacterial mechanism of the myco-fabricated AgNPs, treated bacteria were investigated using TEM and SDS-PAGE analysis.
Materials and methods
Materials
The laboratory experiments have been done at the faculty of science laboratory, Princess Nourah bint Abdulrahman University, Riyadh, Saudi Arabia. Where the silver nitrate, potato-dextrose agar (PDA), Czapek-Dox Agar with 1% chloramphenicol, nutrient agar and broth and Sabouraud broth (Oxoid, UK) were obtained. The soil fungi (Embellisia spp. and Gymnoascus spp.) have been isolated from Saudi Arabian desert soils. Protein profile and TEM analysis were done at king Saud university laboratory.
Isolation of fungi
Two fungal strains (Embellisia spp. and Gymnoascus spp.) were isolated from ALkharj and ALQasab respectively, Saudi Arabian desert soils. The soil was collected from 5 to 20 cm depth, then subjected to culture following the dilution plate method, as described elsewhere29. Two culture media were used: PDA and Czapek-Dox Agar with 1% chloramphenicol. The plates were incubated for 7 days at 28 °C. Pure fungal colonies were kept at 4 °C for further analysis.
Molecular identification using 18S rRNA gene.
A PCR assay for partial amplification of the fungal 18S rRNA genes was performed as described previously30 with the primers NS1 F (5′ GTAGTCATATGCTTGTCTC 3′) and NS8 R (5′ TCCGCAGGTTCACCTACGGA 3′). The PCR reaction mixture contained 2 µL of 10 × PCR Buffer, 1.6 µL of 2.5 mM dNTPs, 1.0 µL of 10 pmol/µL from each primer, 0.2 µL of KOMA Taq (2.5 U/µL), 2 µL of 20 ng/µL DNA template and HPLC-grade water to adjust the reaction volume to 20 µL. The amplification reactions were done in a Biometra thermal cycler (Analytik Jena, Jena, Germany) with the reaction conditions mentioned elsewhere31. Confirmation of successful amplification was assured by applying the PCR products to agarose gel electrophoresis. The PCR products were purified by PCR Cleanup Kit (MilliporeSigma, Burlington, MA, USA).
Sequence analysis
The purified PCR products were sent to a commercial company (Marogen Europe, Amsterdam, The Netherlands) for partial sequencing of the 18S rDNA using the same amplification primers. Sequencing at the company was performed by the BigDye Terminator v3.1 Cycle Sequencing Kit (Applied Biosystems, USA) and 3730xl DNA Analyzer automated DNA sequencing system (Applied Biosystems). The retrieved 18S rDNA sequences of the two fungal isolates were analyzed using the software Geneious Prime Version 2020.1.232. Consent sequences were produced from forward and reverse sequences. The edited sequences were compared with other sequences of related reference strains in nucleotide database of the National Center of Biotechnology Information (NCBI) of the United States using the nucleotide platform of the Basic Local Alignment Search Tool (BLASTn). The sequences were also used to construct a phylogenetic tree using the Neighbor-Joining method33 with the software MEGA X34.
Fungal culture filtrate
Separate culture flasks containing 500 mL of Sabouraud broth (Oxoid, UK) were inoculated by each fungal species isolate individually. The flasks were incubated in static incubator for 7 days at 28 °C, after which the fungal biomass was collected by filtration through Whatman filter paper No. 1 and washed with sterile distilled water to remove excess medium. The fungal biomasses were weighed, and 0.5 g were added to distilled water (10 mL) and incubated at 28 °C for 72 h. Finally, the biomass was separated from the filtrate by filtration. The aqueous filtrate containing the fungal metabolites was kept for further usage in the refrigerator at 4 °C35.
Myco-synthesis of AgNPs
For the biosynthesis of AgNPs, 1 mM AgNO3 was added to fungal aqueous filtrate at a ratio 1:1 and then boiled for 30 min. This mixture was incubated under natural sun light at 25 °C for 24 h, till a dark brown color was formed. The nanoparticles were separated by centrifugation of the mixture at 14,000 rpm for 15 min, then dried by dropping the precipitate on petri dishes at room temperature and kept for further analysis36.
Characterization of myco-synthesized AgNPs
AgNPs was re-dispersed in 1 mL of distilled water for chracterization. A UV–visible spectrophotometer (BIOCHROM Libra S60PC, England) was used in the range of 200–600 nm for measuring the absorbance of the AgNPs with the fungal aqueous filtrate was used as blank, as described before35. The morphology, average diameter and distribution were estimated by transmission electron microscopy, TEM (JEM-1011, JEOL, Tokyo, Japan) at 80 kV voltage. The pattern of the size distribution (size and poly dispersed index, PDI) and zeta potential were assessed by a dynamic light scattering (DLS) system by a Zetasizer (NANO ZSP, Malvern Instruments Ltd., SerialNumber: MAL1118778, version 7.11, Malvern, UK). For surface analysis of the synthesized NPs, a scanning electron microscope, SEM (JED-2200 series, JEOL) provided by energy-dispersive X-ray spectroscopy (EDX) was used to confirm the presence of elemental silver, as previously described37. Functional groups of fungal aqueous filtrates responsible for AgNO3 reduction were estimated with Fourier transform infrared (FT-IR) spectroscopy (SPECTRUM100, Perkin-Elmer, Wellesley, MA, USA) with a range 450–3500 cm−1, as detailed earlier38.
Investigation of the antibacterial activity of myco-synthesized AgNPs
To assess the antibacterial potential of the myco-synthesized AgNPs in vitro, four human pathogenic bacteria were tested (Escherichia coli, Pseudomonas aeruginosa Staphylococcus aureus, and Klebsiella pneumoniae). The assay was conducted by the agar well diffusion technique39. Using sterile swabs, 100 µL of 24 h. old bacterial culture with a concentration equal to 0.5 McFarland (1.5 × 108 CFU mL−1) from each of the four tested strains were streaked on a plate of nutrient agar and left to dry. Under aseptic conditions, wells of 0.8 mm in diameter were made on the agar using a sterile cork-borer. Volumes of 50 µL of myco-synthesized AgNPs were added to the wells. The fungal filtrate and 5 µg ampicillin discs were used as negative and positive controls, respectively. The plates were incubated at 37 °C for 24 h. The experiment was performed in triplicate and the growth inhibition zones were estimated in millimeters (means ± standard variation), as described previously40.
The minimum inhibitory concentration (MIC) and the minimum bactericidal concentration (MBC) were estimated using the microdilution method in nutrient broth. The bacterial cultures of the four tested strains were individually diluted to 0.5 McFarland from which a volume of 10 µL was added to nutrient broth (350 µL). The isolates were tested against the myco-fabricated AgNPs solubilized in Dimethyl sulfoxide (DMSO) at different concentrations (0.031, 0.062, 0.125 and 0.250 mg mL−1). The negative control composed of nutrient broth inoculated with bacterial inoculum. Then, the plates were incubated at 37 °C for 24 h. The MIC was determined as the lowest concentration that inhibit observable bacterial growth41 where the MBC was verified when no growth appeared when treated bacteria were sub-cultured on nutrient agar plates after incubation period42.
Protein profile pattern by SDS-PAGE analysis
The total cellular soluble proteins of K. pneumoniae were extracted before and after treatment with 1 mg mL−1 of AgNPs synthesized from each fungal strain for 24 h at 37 °C, then purified by TriFast (Peqlab, VWR company). The proteins were further fractionated by OmniPAGE Mini vertical electrophoresis unit provided with a power Pro 5 power supply (Cleaver Scientific, Warwickshire, UK) on a SERVAGel™ TG PRiME 10% (SERVA, Heidelberg, Germany)43.
Detection of ultrastructural changes in AgNPs treated bacteria
One species (K. pneumoniae) was chosen for TEM analysis (JEM-1011, JEOL, Tokyo, Japan, at 80 kV voltage) to test the possible structural changes for cells treated with AgNPs fabricated by both fungal strains and incubated for 24 h. at 37 °C. Thereafter, bacterial suspension was centrifuged at 4000 rpm for 15 min. Then, 2.5% glutaraldehyde in 100 mM phosphate buffer, pH 7.0, was added to the pellet for sample fixation for 15–30 min. This was followed by applying 1% osmium tetroxide in 100 mM phosphate buffer for 1–2 h. at 4 °C, then washed five times with distilled water. Then, En bloc stain with 2% aqueous uranyl acetate was applied for ~ 2 h at 4 °C in the dark. Dehydration was done with series of acetone (30, 50, 70, 90 and 100%). After that, the samples were infiltrated in propylene oxide, followed by embedding in fresh resin (Epon mixture) for 12–24 h. at 60–70 °C. The ultrathin sections of the samples were put on 200-mesh copper grids after double staining with 2% uranyl acetate and lead citrate, then examined under a JEOL 100 CX electron microscope operating at 80 kV, as described previously44.
Statistical analysis
All data were represented as mean and standard deviations. One-way analysis of variance (ANOVA) as well as graphs preparation were performed by Graph-bad Prism 9.1 software (Inc., La Jolla, CA, USA). ImagJ software was used for calculating the particles size and diameter from TEM images.
Results
Fungal strains isolation and identification
The 18S rRNA gene sequences analysis identified the two soil fungal isolates from Saudi Arabian desert as Embellisia spp. and Gymnoascus spp. The phylogenetic tree constructed from the two sequences together with corresponding to other strains worldwide is shown in Fig. 1. The sequences of these isolates have been deposited in the nucleotide sequence database of the GenBank of NCBI under accession numbers MN995544 for Embellisia spp. and MN995517 for Gymnoascus spp.
Phylogenetic tree of fungal isolates based on 18S rDNA constructed using the Neighbor-Joining method in MEGA X. The accession number shown at the end of the branch and their closest relatives’ sequences from the GenBank accession number shown at the tip of the branch. Ustilago maydis accession number KP322952 was an outlier. The percentage of replicate trees in which the associated taxa clustered together are shown next to the branches.
Myco-synthesis of AgNPs
The individual mixture of the aqueous filtrates from both fungal strains and the AgNO3 has been changed from colorless to a stable brown color after incubation for 24 h. Such changes indicated the reduction of silver ions to AgNPs by fungal secondary metabolites. This conversion was the first sign that Embellisia spp. and Gymnoascus spp. were capable in AgNPs fabrication from AgNO3 providing E-AgNPs and G-AgNPs, respectively.
Myco-synthesized AgNPs characterization
UV–visible spectrophotometry was used to further confirmation of the AgNPs synthesis from fungal filtrate. Strong beaks at 430 and 450 nm for E-AgNPs and G-AgNPs, respectively, were reported (Fig. 2A,B). The absorption peaks were detected in relation to the fungal filtrate (blank).
The morphology and the size diameter of the myco-synthesized E-AgNPs and G-AgNPs were observed using TEM analysis which indicates well-dispersed spherical nanoparticles of 2–20 nm size diameter (Fig. 3A,B).
TEM micrograph showing morphological characterization of myco-synthesized using Embellisia spp (E-AgNPs, (A) and Gymnoascus spp., (G-AgNPs, B) and at magnifications of 250,000 and 150,000, respectively. Bar figures indicating the particles distribution (diameter and area) that calculated using imagJ software.
Further, analysis was done by DLS, that determined an average diameter of 63.39 nm for E-AgNPs and 59.97 nm for G-AgNPs with a polydispersity index (PDI) of 0.28 and 0.40, respectively (Fig. 4).
EDX analysis confirmed the presence of the silver element in all myco-synthesized AgNPs. Strong signals at 3 keV were noted for Ag, along with carbon and oxygen peaks (Fig. 5).
The FTIR measurements were used to determine the presence of various functional groups in the fungal metabolites involved in AgNPs synthesis, capping, stabilization and consistency. The FTIR for the aqueous filtrate from Embellisia spp. showed eight peaks ranging from 3269.54 to 1633 cm−1; the peaks increased to ten for E-AgNPs ranging between 3282.16 and 1636.98 cm−1 (Fig. 6A). In Gymnoascus spp. filtrate, eleven peaks were detected ranging from 3258.51 to 1633.37 cm−1, whereas eleven peaks were detected for G-AgNPs ranging between 3319.33 and 1637.15 cm−1 (Fig. 6B).
Antibacterial activity of the myco-synthesized AgNPs
When the E-AgNPs and G-AgNPs at concentrations of 1 mg mL−1 each were tested for antimicrobial activity against four human pathogenic bacteria. The maximum activity was recorded against K. pneumoniae, with growth inhibition zones of 5 and 3.8 mm for E-AgNPs and G-AgNPs, respectively. S. aureus was also sensitive to AgNPs with growth inhibition zones of 4.8 mm for E-AgNPs and 2.5 mm for G-AgNPs (Fig. 7A,B). The lowest activity of both AgNPs was noted against E. coil and P. aeruginosa. The activity of E-AgNPs was significantly higher than G-AgNPs (p < 0.001).Significant varitaion in the bacterial response to the myco-fabricated AgNPs was noted as well as their interaction.
The MIC and MBC estimated for both myco-synthesized AgNPs by the micro-dilution method are shown in Table 1. The lowest MIC was recorded at 0.03 μg mL−1 against K. pneumoniae for both E-AgNPs and G-AgNPs, while the lowest MBC for both AgNPs types was 0.06 μg mL−1 against the same strain (Table 1).
SDS-PAGE and protein profile pattern
Since the highest activities for E-AgNPs and G-AgNPs were noted against K. pneumoniae, therefore this strain was chosen for SDS-PAGE analysis to detect the protein profiling pattern before and after AgNPs treatment. The protein pattern from treated K. pneumoniae (Fig. 8) displayed lower protein bands intensities as clear in lanes 3 and 4 compared with the untreated control (lane 2). The total number of protein bands of the control was 22 at sizes ranged from 15 to 160 kDa, whereas in E-AgNPs treated cells (lane 3) they were 16 bands with sizes ranged from 15 to 120 kDa. In lane 4, the protein from G-AgNPs treated bacteria showed only 8 bands ranging from 19 to 120 kDa.
Ultrastructural changes detected in AgNPs treated bacteria
Examination of K. pneumoniae cells by TEM analysis after treatment with the myco-synthesized AgNPs (Fig. 9) showed damaged cell wall (Fig. 9B,C) and deformation and rupture of the bacterial cell (Fig. 9D).
TEM micrographs of AgNPs-treated K. pneumoniae where untreated cells (A) show intact cell wall (yellow arrow) and a peptidoglycan layer in periplasmic space (white arrow). Cell treated with E-AgNPs (B,C) showed damage in the cell wall (blue arrow). G-AgNPs treated bacteria (D) showed cell damage (red arrow). E-AgNPs and G-AgNPs were myco-synthesized using Embellisia spp. and Gymnoascus spp., respectively. Images were taken at 80 kV and magnification of 15,000, 20,000 and 30,000×.
Discussion
It was challenging for many scientists to find out new, simplified and ecofriendly methods for obtaining efficient AgNPs. The bio-fabrications are highly recommended due to their advantages over other synthetic methods3,37. The utilization of fungi for the synthesis of AgNPs is remarkably useful in relation to other fabrication methods due to simple handling and harmless effect. Several strains of Fusarium oxysporum mediated extracellular AgNPs formation depending on reductase/electron shuttle relationship and provided NPs ranging between 20 and 50 nm45.
In the present work the fungal filtrates from Embellisia spp. and Gymnoascus spp. indicated their ability in reducing Ag ions for self-assembly of AgNPs as detected by the formation of dark brown color when both compounds were mixed. Additionally, the recorded absorbance peaks at the UV–visible spectrum corresponded to the typical band of AgNPs that attributed to surface plasmon resonance, confirming the production of AgNPs46. DLS analysis revealed that G-AgNPs particle size was smaller than that of E-AgNPs, which may reflect the diversity of fungal bioactive molecules involved in the reduction process, such as citric acid, peroxidases, homogeneous and heterogeneous proteins along with fungal enzymes, especially nitrate reductases47. Although the size variation was not that high however, PDI indicated better mono-dispersibility and homogeneity for E-AgNPs than G-AgNPs. TEM indicated spherical shape of NPs and EDX analysis confirmed the presence of the silver element in G-AgNPs and E-AgNPs at 3 keV, which is typical for the absorption of metallic silver nano-crystallites. The signal band detected by FTIR analysis at 3269.54 and 3282.16 cm−1 corresponds to N–H, C–H, and O–H stretching vibrations, indicating the presence of primary amines in the fungal proteins alkynes, and alcohols, respectively48. Intense absorption bands in FTIR at 1633.37 and 1637.15 cm−1 might be attributed to amide I due to carbonyl stretch in proteins C=O49. Similar functional group detected at both fungal filtrate and AgNPs fabricated by their aid indicating the role of fungal biomolecules in the reduction and capping processes of AgNPs. The biological molecules from the fungal extract may carry out a double function by performing the reduction process and enhancing the AgNPs stability, as they could serve as good capping agents that covered the AgNPs surface and prevented their aggregation50,51. From these biomolecules, fungal enzymes are good reducing agents25. Fungi could have electrostatic interactions between the metal ion and cell wall associated enzymes followed by subsequent enzymatic reduction of metal ions resulting in intracellular or extracellular production of NPs52.
The capability of fungal filtrates in NPs formation was previously approved for Phoma spp., Chaetomium globosum, and Chaetomium spp., which were able to reduce AgNO3 into AgNPs with varying sizes and shapes18. Also, Fusarium oxysporum and Verticillium spp. were capable of reducing Ag and gold into their nanoparticle forms depending on their extracellular proteins and secondary metabolites52.
Current findings showed potent antibacterial against the four tested human pathogenic bacteria however, the activity of E-AgNPs was higher than G-AgNPs. The reasons behind the variation in the NPs activity could be attributed to the variation in their PDI characteristics since no clear variations were noted in their size and morphology. PDI bellow 0.3 reflecting the mono dispersity and uniformity of the E-AgNPs53 that might enhance their activity compared to G-AgNPs where their PDI was 0.4. K. pneumoniae was the most sensitive tested strain, which is in accordance with previous findings by Sonbol et al.18, who observed strong antibacterial activity of three myco-synthesized AgNPs. The antibacterial activity of morphologically modified AgNPs and chitosan loaded essential oils, were reported against multidrug resistant Gram negative bacteria and biofilm forming Acinetobacter baumannii, respectively54,55.
The antibacterial ability of AgNPs could be related to the electrostatic interactions between positively charged Ag ions and the negatively charged bacterial membrane, which would lead to membrane permeability disruption and cell wall damage56,57. AgNPs could have also bound a specific group of enzymes (thiols) and affected the DNA capacity to replicate leading to cell death58. In this study, the MIC and MBC indicated low fungal based AgNPs concentrations were needed to suppress the growth of both tested Gram-negative and Gram-positive bacteria. The efficiency of mucogenic AgNPs as antibacterial agents could be associated with their ability to enhance cellular oxidative stress causing destruction of the cell components leading to cell death.
Polyacrylamide gel electrophoresis (SDS-PAGE) is a powerful technique for molecular analysis of cell proteins, especially in comparing protein patterns to detect qualitative, and quantitative changes, as well as clustering of bacterial groups59. Proteomic differences of K. pneumoniae before and after treatment with fungal-based AgNPs might indicate significant polymorphism in the protein profiles that could be attributed to degradation or even block of the pathways for biosynthesis of certain proteins. Lower protein band intensity compared with untreated control might also be attributed to oxidative stress enhanced by NPs treatment. Besides, unfolding of the protein chain resulting from the reaction of AgNPs with thiol groups of the proteins60 is expected to cause degradation of the proteins. Therefore, it might explain the reduction in the number of protein bands from 22 in untreated to 16 and 8 in the treated bacteria with E-AgNPs and G-AgNPs, respectively. Different studies reported that AgNPs may be involved in preventing protein synthesis by preventing many translation factors61,62.
Moreover, TEM imaging of K. pneumoniae treated with fungal-based AgNPs showed disruption within the cell membrane that led to damage in the outer membrane and deformation of the bacterial cell. As a result of interaction of free Ag+ with several cellular sites, such as cytoplasmic membrane, cytoplasm and nuclear matrix. So, membrane permeability increased leading to loss of certain membrane ions as K+ that impaired membrane integrity, and effects on the respiration process63,64. Other reports linked AgNPs toxicity to induce oxidative stress by motivating the development of ROS, which lead to cellular dysfunction and death65. In general, the unique characters of NPs, such as their smaller size with larger surface area, their charges enable them to easily attach and penetrate bacterial cell walls and membranes44 make them a perfect tool from biological source to control adverse antibiotic resistant human pathogens.
Conclusion
The present investigation indicated the ability of two soil fungal isolates from Saudi Arabian desert (Embellisia spp. and Gymnoascus spp.) for the biosynthesis of AgNPs. Both strains provided NPs with good physiochemical characteristics however, the PDI for E-AgNPs was low indicating higher homogeneity compared to G-AgNPs which might enhance their antibacterial activity. As an ecofriendly, safe, and cost-effective approach, both myco-synthesized AgNPs could be recommended as antibacterial agents specially against K. pneumoniae where their mode of action was reported by TEM and SDS PAGE analysis. However, further investigations are required to validate these findings by increasing the sample size of tested agents and study their antibacterial mechanisms. Overall, this study added new fungal isolates as bio mediators for nanoparticle synthesis with efficiency as antibacterial agents against some human pathogens.
Data availability
The datasets generated and/or analyzed during the current study of the two sequences were submitted to GenBank (Accession numbers MN995544.1 and MN995517.1) and are available online in the NCBI repository, persistent in the following web link: https://www.ncbi.nlm.nih.gov/nuccore/MN995544.1?report=genbank, https://www.ncbi.nlm.nih.gov/nuccore/MN995517.
References
Susarrey-Arce, A. et al. Inception and trapping of ZnO nanoparticles within desilicated mordenite and ZSM-5 zeolites. Part. Part. Syst. Charact. 27, 100–111 (2010).
Yilmaz, A. & Yilmaz, M. Bimetallic core–shell nanoparticles of gold and silver via bioinspired polydopamine layer as surface-enhanced raman spectroscopy (SERS) platform. Nanomaterials 10, 688 (2020).
Singh, J. et al. ‘Green’ synthesis of metals and their oxide nanoparticles: Applications for environmental remediation. J. Nanobiotechnol. 16, 84 (2018).
Simões, M. F., Ottoni, C. A. & Antunes, A. Biogenic metal nanoparticles: A new approach to detect life on Mars?. Life 10, 28 (2020).
Cheng, L. et al. Nanotechnology strategies for antibacterial and remineralizing composites and adhesives to tackle dental caries. Nanomedicine 10, 627–641 (2015).
Aldahasi, R. M., Shami, A. & Mohammed, A. E. Bimetallic nanoparticles and biochar produced by Adansonia Digitata shell and their effect against tomato pathogenic fungi. PeerJ 12, e17023 (2024).
Soliman, M. K. Y., Abu-Elghait, M., Salem, S. S. & Azab, M. S. Multifunctional properties of silver and gold nanoparticles synthesis by Fusarium pseudonygamai. Biomass Convers. Biorefinery 1–18 (2022).
Salem, S. S. & Fouda, A. Green synthesis of metallic nanoparticles and their prospective biotechnological applications: An overview. Biol. Trace Elem. Res. 199, 344–370 (2021).
Fouda, A., El-Din Hassan, S., Salem, S. S. & Shaheen, T. I. In-vitro cytotoxicity, antibacterial, and UV protection properties of the biosynthesized Zinc oxide nanoparticles for medical textile applications. Microb. Pathog. 125, 252–261 (2018).
Alsharif, S. M. et al. Multifunctional properties of spherical silver nanoparticles fabricated by different microbial taxa. Heliyon 6, e03943 (2020).
Nie, P., Zhao, Y. & Xu, H. Synthesis, applications, toxicity and toxicity mechanisms of silver nanoparticles: A review. Ecotoxicol. Environ. Saf. 253, 114636 (2023).
Alburae, N., Alshamrani, R. & Mohammed, A. E. Bioactive silver nanoparticles fabricated using Lasiurus scindicus and Panicum turgidum seed extracts: Anticancer and antibacterial efficiency. Sci. Rep. 14, 4162 (2024).
Burdușel, A.-C. et al. Biomedical applications of silver nanoparticles: An up-to-date overview. Nanomaterials 8, 681 (2018).
Siddiqi, K. S., Husen, A. & Rao, R. A. K. A review on biosynthesis of silver nanoparticles and their biocidal properties. J. Nanobiotechnol. 16, 1–28 (2018).
Kedi, P. B. E. et al. Eco-friendly synthesis, characterization, in vitro and in vivo anti-inflammatory activity of silver nanoparticle-mediated Selaginella myosurus aqueous extract. Int. J. Nanomed. 13, 8537–8548 (2018).
Rafique, M., Sadaf, I., Rafique, M. S. & Tahir, M. B. A review on green synthesis of silver nanoparticles and their applications. Artif. Cells Nanomed. Biotechnol. 45, 1272–1291 (2017).
Mohammed, A. E. et al. In silico prediction of Malvaviscus arboreus metabolites and green synthesis of silver nanoparticles–opportunities for safer anti-bacterial and anti-cancer precision medicine. Int. J. Nanomed. 18, 2141–2162 (2023).
Sonbol, H., Mohammed, A. E. & Korany, S. M. Soil fungi as biomediator in silver nanoparticles formation and antimicrobial efficacy. Int. J. Nanomed. 17, 2843–2863 (2022).
Al-Rajhi, A. M. H., Salem, S. S., Alharbi, A. A. & Abdelghany, T. M. Ecofriendly synthesis of silver nanoparticles using Kei-apple (Dovyalis caffra) fruit and their efficacy against cancer cells and clinical pathogenic microorganisms. Arab. J. Chem. 15, 103927 (2022).
Hassan, W. A. et al. Characterization of Amaranthus species: Ability in nanoparticles fabrication and the antimicrobial activity against human pathogenic bacteria. PeerJ 11, e16708 (2024).
Salem, S. S. A mini review on green nanotechnology and its development in biological effects. Arch. Microbiol. 205, 128 (2023).
Guilger, M. et al. Biogenic silver nanoparticles based on Trichoderma harzianum: Synthesis, characterization, toxicity evaluation and biological activity. Sci. Rep. 7, 1–13 (2017).
Jamkhande, P. G., Ghule, N. W., Bamer, A. H. & Kalaskar, M. G. Metal nanoparticles synthesis: An overview on methods of preparation, advantages and disadvantages, and applications. J. Drug Deliv. Sci. Technol. 53, 101174 (2019).
Azizi, S., Ahmad, M., Mahdavi, M. & Abdolmohammadi, S. Preparation, characterization, and antimicrobial activities of ZnO nanoparticles/cellulose nanocrystal nanocomposites. BioResources 8, (2013).
Guilger-Casagrande, M. & de Lima, R. Synthesis of silver nanoparticles mediated by fungi: A review. Front. Bioeng. Biotechnol. https://doi.org/10.3389/fbioe.2019.00287 (2019).
Priyadarshini, S., Gopinath, V., Priyadharsshini, N. M., MubarakAli, D. & Velusamy, P. Synthesis of anisotropic silver nanoparticles using novel strain, Bacillus flexus and its biomedical application. Colloids Surf. B Biointerfaces 102, 232–237 (2013).
Pantidos, N. & Horsfall, L. E. Biological synthesis of metallic nanoparticles by bacteria, fungi and plants. J. Nanomed. Nanotechnol. 5, 1 (2014).
Osorio-Echavarría, J., Osorio-Echavarría, J., Ossa-Orozco, C. P. & Gómez-Vanegas, N. A. Synthesis of silver nanoparticles using white-rot fungus Anamorphous Bjerkandera sp. R1: Influence of silver nitrate concentration and fungus growth time. Sci. Rep. 11, 3842 (2021).
Waksman, S. A. A method for counting the number of fungi in the soil. J. Bacteriol. 7, 339 (1922).
White, T. J., Bruns, T., Lee, S. & Taylor, J. Amplification and direct sequencing of fungal ribosomal RNA genes for phylogenetics. PCR Protoc. Guid. Methods Appl. 18, 315–322 (1990).
Reda Bakkar, M. et al. Rhamnolipids nano-micelles as a potential hand sanitizer. (2021). https://doi.org/10.3390/antibiotics10070751.
Kearse, M. et al. Geneious Basic: An integrated and extendable desktop software platform for the organization and analysis of sequence data. Bioinformatics 28, 1647–1649 (2012).
Saitou, N. & Masatoshi, N. The neighbor-joining method: A new method for reconstructing phylogenetic trees. Mol. Biol. Evol. 4, 406–425 (1987).
Kumar, S., Stecher, G., Li, M., Knyaz, C. & Tamura, K. MEGA X: Molecular evolutionary genetics analysis across computing platforms. Mol. Biol. Evol. 35, 1547–1549 (2018).
Madbouly, A. K., Abdel-Aziz, M. S. & Abdel-Wahhab, M. A. Biosynthesis of nanosilver using Chaetomium globosum and its application to control Fusarium wilt of tomato in the greenhouse. IET Nanobiotechnol. 11, 702–708 (2017).
Nayak, B. K., Prabhakar, V. & Nanda, A. Myco-facilitated biosynthesis of nano-silver from wasp nest fungus, Paecilomyces variotii, and its antimicrobial activity against MTCC strains. Front. Microbiol. 13, 1–12 (2022).
Paul, S., Singh, A. R. J. & Sasikumar, C. S. Green synthesis of bio-silver nanoparticles by Parmelia perlata, Ganoderma lucidum and Phellinus igniarius and their fields of application. Indian J. Res. Pharm. Biotechnol. 3, 100 (2015).
Sonbol, H. et al. Bioinspired synthesize of CuO nanoparticles using Cylindrospermum stagnale for antibacterial, anticancer and larvicidal applications. Appl. Nanosci. https://doi.org/10.1007/s13204-021-01940-2 (2021).
Sgouras, D. et al. In vitro and in vivo inhibition of Helicobacter pylori by Lactobacillus casei strain shirota. Appl. Environ. Microbiol. 70, 518–526 (2004).
Jiang, L. et al. Evaluation of diffusion and dilution methods to determine the antimicrobial activity of water-soluble chitosan derivatives. (2012). https://doi.org/10.1111/jam.12111.
Alqahtani, M. A., Al Othman, M. R., Mohammed, A. E. & Jim, O. Bio fabrication of silver nanoparticles with antibacterial and cytotoxic abilities using lichens. Sci. Rep. 10, 1–17 (2020).
Maruthupandy, M., Rajivgandhi, G., Muneeswaran, T., Song, J.-M. & Manoharan, N. Biologically synthesized zinc oxide nanoparticles as nanoantibiotics against ESBLs producing gram negative bacteria. Microb. Pathog. 121, 224–231 (2018).
Hamida, R. S., Abdelmeguid, N. E., Ali, M. A., Bin-Meferij, M. M. & Khalil, M. I. Synthesis of silver nanoparticles using a novel cyanobacteria Desertifilum sp. extract: Their antibacterial and cytotoxicity effects. Int. J. Nanomed. 15, 49 (2020).
Romero-Urbina, D. G. et al. Ultrastructural changes in methicillin-resistant Staphylococcus aureus induced by positively charged silver nanoparticles. Beilstein J. Nanotechnol. 6, 2396–2405 (2015).
Durán, N., Marcato, P. D., Alves, O. L., De Souza, G. I. H. & Esposito, E. Mechanistic aspects of biosynthesis of silver nanoparticles by several Fusarium oxysporum strains. J. Nanobiotechnol. 3, 1–7 (2005).
Wypij, M. et al. Synthesis, characterization and evaluation of antimicrobial and cytotoxic activities of biogenic silver nanoparticles synthesized from Streptomyces xinghaiensis OF1 strain. World J. Microbiol. Biotechnol. 34, 1–13 (2018).
Khandel, P. & Shahi, S. K. Mycogenic nanoparticles and their bio-prospective applications: Current status and future challenges. J. Nanostruct. Chem. 8, 369–391 (2018).
Amin, M. A. et al. The potency of fungal-fabricated selenium nanoparticles to improve the growth performance of Helianthus annuus L. and control of cutworm Agrotis ipsilon. Catalysts 11, 1551 (2021).
Khandel, P., Kumar, S. S., Kanwar, L., Kumar Yadaw, R. & Kumar Soni, D. Biochemical profiling of microbes inhibiting Silver nanoparticles using symbiotic organisms. Int. J. Nano Dimens. 9(273), 285 (2018).
Spagnoletti, F. N., Kronberg, F., Spedalieri, C., Munarriz, E. & Giacometti, R. Protein corona on biogenic silver nanoparticles provides higher stability and protects cells from toxicity in comparison to chemical nanoparticles. J. Environ. Manag. 297, 113434 (2021).
Sunkar, S. & Nachiyar, C. V. Biogenesis of antibacterial silver nanoparticles using the endophytic bacterium Bacillus cereus isolated from Garcinia xanthochymus. Asian Pac. J. Trop. Biomed. 2, 953–959 (2012).
Li, Q., Liu, F., Li, M., Chen, C. & Gadd, G. M. Nanoparticle and nanomineral production by fungi. Fungal Biol. Rev. https://doi.org/10.1016/j.fbr.2021.07.003 (2021).
Shakeel, F. et al. Nanoemulsions as vehicles for transdermal delivery of aceclofenac. Aaps Pharmscitech 8, 191–199 (2007).
Rajivgandhi, G. et al. Morphological modification of silver nanoparticles against multi-drug resistant gram–negative bacteria and cytotoxicity effect in A549 lung cancer cells through in vitro approaches. Arch. Microbiol. 205, 282 (2023).
Govindan, R. et al. Effective removal of biofilm formation in Acinetobacter baumannii using chitosan nanoparticles loaded plant essential oils. J. King Saud Univ. 34, 101845 (2022).
Nathan, C. & Cunningham-Bussel, A. Beyond oxidative stress: An immunologist’s guide to reactive oxygen species. Nat. Rev. Immunol. 13, 349–361 (2013).
Jadhav, S., Gaikwad, S., Nimse, M. & Rajbhoj, A. Copper oxide nanoparticles: Synthesis, characterization and their antibacterial activity. J. Clust. Sci. 22, 121–129 (2011).
Li, H. et al. A comparative study of the antibacterial mechanisms of silver ion and silver nanoparticles by Fourier transform infrared spectroscopy. Vib. Spectrosc. 85, 112–121 (2016).
Durrani, R. et al. Biological characterization and protein profiles of two model bacteria by SDS-PAGE and FT-IR. ARPN J. Agric. Biol. Sci. 3, (2008).
Soliman, H., Elsayed, A. & Dyaa, A. Antimicrobial activity of silver nanoparticles biosynthesised by Rhodotorula sp. strain ATL72. Egypt. J. Basic Appl. Sci. 5, 228–233 (2018).
Gogoi, S. K. et al. Green fluorescent protein-expressing Escherichia coli as a model system for investigating the antimicrobial activities of silver nanoparticles. Langmuir 22, 9322–9328 (2006).
Velusamy, P., Kumar, G. V., Jeyanthi, V., Das, J. & Pachaiappan, R. Bio-inspired green nanoparticles: Synthesis, mechanism, and antibacterial application. Toxicol. Res. 32, 95–102 (2016).
Xiu, Z.-M., Ma, J. & Alvarez, P. J. J. Differential effect of common ligands and molecular oxygen on antimicrobial activity of silver nanoparticles versus silver ions. Environ. Sci. Technol. 45, 9003–9008 (2011).
Ivask, A. et al. Toxicity mechanisms in Escherichia coli vary for silver nanoparticles and differ from ionic silver. ACS Nano 8, 374–386 (2014).
Gurunathan, S. et al. Cytotoxicity and transcriptomic analysis of silver nanoparticles in mouse embryonic fibroblast cells. Int. J. Mol. Sci. 19, 3618 (2018).
Funding
The authors extend their appreciation to the Deputyship for Research & Innovation, Ministry of Education in Saudi Arabia for funding this research work through the project number RI-44-0428.
Author information
Authors and Affiliations
Contributions
A.E.M. conceptualization, conducted the experiments, investigation, analyzed the results, writing—original draft preparation, writing—review and editing. H.S. conceptualization, conducted the experiments, investigation, analyzed the results, writing—review and editing, supervision, funding acquisition. S.M.K. conceptualization, conducted the experiments, investigation, analyzed the results, writing—review and editing. E.A.A. conducted the experiments, investigation, analyzed the results, writing—review and editing. S.S.A. investigation, analyzed the results, writing—review and editing, funding acquisition. R.M.E. Investigation, analyzed the results, writing—review and editing. All authors have read and agreed to the published version of the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Mohammed, A.E., Korany, S.M., Sonbol, H. et al. Myco-fabricated silver nanoparticle by novel soil fungi from Saudi Arabian desert and antimicrobial mechanism. Sci Rep 14, 15211 (2024). https://doi.org/10.1038/s41598-024-63117-5
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-024-63117-5
- Springer Nature Limited