Abstract
In the present work, we synthesized cesium superoxide (CsO2) nanoparticles by solution-processed spray pyrolysis technique. The as-synthesized CsO2 nanoparticles were characterized through Raman spectroscopy, X-ray diffraction, scanning electron microscopy and ultraviolet–visible spectroscopy. The CsO2 nanoparticle-based gas sensor is more selective towards the carbon dioxide (CO2) gas. The sensor shows good gas sensing performance for CO2 gas. Gas sensing mechanism is dominated by the adsorption and desorption process. Through this paper, we studied another dimension of gas sensing process by employing superoxide for gas sensing. The sensing mechanism for cesium superoxide is explained by newly designed “bridging oxygen-free mechanism”.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
The superoxides have been a subject of growing interest because of its extraordinary characteristics resulting from superoxide ion (O2 −) (Budanur and Khan 2014). The study of superoxide ion can facilitate understanding its role in metal–oxygen batteries. Ren et al. reported the metal–oxygen battery application of potassium superoxide nanoparticles. This study successfully confirms formation and removal of KO2 in the battery cycle test. Moreover, without any catalysts, a low discharge/charge potential gap of the order of 50 mV was observed (Ren and Wu 2013). Bryantsev et al. (2011) reported the predicting solvent stability of aprotic electrolyte Li–air batteries by the superoxide anion radical. This experimental study provides competent qualitatively screening solvent stability in Li–air batteries. Hartmann et al. (2013) reported the rechargeable room-temperature battery application of sodium superoxide. This study shows that exchange of lithium by sodium may offer an unforeseen route towards rechargeable metal–air batteries.
Inspiring from the extraordinary characteristics resulting from superoxide ion (O2 −) in superoxide, we planned to study the gas sensing application of cesium superoxide nanoparticles. A very small number and scattered reports found in the literature of material science on superoxide. Thus, through this work, we make an attempt to explore gas-sensing performance of cesium superoxide nanoparticles. As the superoxide itself contains the superoxide ion (O2 −), therefore, we developed “bridging oxygen-free mechanism” for superoxide.
The core objective behind the development of “bridging oxygen-free mechanism” for gas sensing materials are that it will result in fast sensing, selectivity and fast response and recovery time. This is due to the traditional gas sensing material-bridging oxygen forms layer between target gas molecules and sensing surface, but the superoxide-based sensing materials itself contain superoxide ion (O2 −). Generally, in resistive gas-sensing method, bridging oxygen forms layer on sensing material, through which electron transfer takes place (Alwan and Dheyab 2017). The transfers of electrons result in resistance change through which sensing response is measured (Muhsien et al. 2014). The formation of bridging oxygen layer acts as a barrier between target gas and sensing surface for rapid detection of target gas. In addition, formation of bridging oxygen layer on sensing surface increases response and recovery time of sensor. Therefore, UV light exposure is given to sensor surface to achieve baseline value of resistance (Chinh et al. 2016). This increases the operation cost and decreases the life of sensor.
Experimental
In the present work, cesium superoxide (CsO2) was prepared by solution-processed spray pyrolysis technique. For the synthesis of CsO2 nanoparticles, cesium chloride (CsCl) and hydrogen peroxide (H2O2) was used as starting chemicals. The 1 M of cesium chloride was dissolved in H2O2 under rapid magnetic stirring in distilled water of resistivity not less than 18.2 MΩ cm for 15 min. Subsequent to this step; solution was kept for probe sonication. After this step, solution was loaded in spray pyrolysis set-up of specification (Nemade and Waghuley 2014a). This solution was allowed to spray and deposit on chemically clean glass substrate maintained at temperature 100°C. The complete process was conducted in dry oxygen-rich environment under constant flow. By considering the highly reactive nature of cesium, the complete process was handled in an atmosphere of water below 0.1 ppm.
The highly conducting silver paste was used as ohmic contacts to determine the film surface resistance change measurements. The as-deposited CsO2 nanoparticles on chemically cleaned SiO2 substrate of dimensions 25 mm × 25 mm used for gas sensing action. The gas sensing performance of chemiresistor was checked in air as reference gas. The sensing response (S) is defined as \(S = |R_{\text{a}} - R_{\text{g}} |/R_{\text{a}}\), where R a is the resistance in air i.e., baseline resistance and R g represents the resistance in CO2 gas.
Results and discussion
Figure 1 shows the Raman spectrum of as-synthesized CsO2 nanoparticles at room temperature (303 K). The spectra exhibit the sharp intense peak at 1134 cm−1, which can be assigned to the stretching mode of the superoxide dumbbell. This reflects as-synthesized CsO2 nanoparticles acquire hyperoxide state. The inset of Fig. 1 shows XRD pattern of CsO2 nanoparticles, indicates the presence of a very low concentration of peroxide anions, which might result from incomplete oxidation (Bates et al. 1972). The CsO2 acquires the space group I/4mmm with lattice parameters at temperature 303 K, a = b = 4.461 Ǻ and c = 7.331 Ǻ. Generally, superoxides have the largest lattice parameters, which is consequential to larger distance between the dioxygen dumbbells and cesium. Therefore, lower cationic field experienced by the dumbbells. Thus, even in oxygen-rich reaction environment, superoxides do not merge entirely superionic state (Zumsteg et al. 1974). The average crystallite size of as-synthesized CsO2 nanoparticles was estimated using Debye–Scherrer formula (Nemade and Waghuley 2013a, 2014b), \(D = 0.89\lambda /\beta \cos \theta\), where 0.89 is Scherrer’s constant, λ is the wavelength of X-rays, θ is the Bragg diffraction angle, and β is the full width at half maximum. The average particle size of the CsO2 nanoparticles was found to be 21.39 nm.
Figure 2 represents the SEM image of as-synthesized CsO2 nanoparticles. This image substantiates the irregular shape of the nanoparticles, and most of the particles exhibit small amount of agglomeration. From the image, it is observed that the size of the nanoparticle is around 22 nm, which was in good agreement with the particle sizes (21.39 nm) calculated from the Debye–Scherrer formula.
The UV–VIS absorption spectroscopy is used to analyze the optical properties of CsO2 nanoparticles. The as-synthesized CsO2 nanoparticles exhibit excitonic absorption tail around 225 nm. The monodisperse nature of the CsO2 nanoparticle distribution reflects from sharp increase in absorbance value (Zhang et al. 2002). The optical band gap of as-synthesized CsO2 nanoparticles was determined by applying the energy-wavelength relation (Nemade and Waghuley 2013b). The optical band gap is determined by extrapolating straight line at R = 0 to the curve (αhν)2 vs. (hν) is shown in inset of Fig. 3. This extrapolation intersect energy axis at 5.3 eV. This is optical band gap of CsO2 nanoparticles. The intense absorption around the 225 nm indicates the presence of quantum confinement (Nemade and Waghuley 2013c).
The selectivity is the ability of a sensor to measure only one gas with maximum response (Morrison 1987). To check selectivity response of CsO2 nanoparticles-based sensor, we investigate sensing response towards the LPG and CO2 gas at 250 ppm at room temperature as shown in Fig. 4. Plot clearly shows that CsO2 nanoparticles exhibits higher sensing response towards the CO2 gas. Therefore, as-synthesized CsO2 nanoparticles are more selective for CO2 gas. Thus, the future study focused on CO2 gas sensing.
Figure 5 depicts the gas sensing response of CsO2 nanoparticles towards the CO2 gas at room temperature (303 K). The plot clearly shows the good dependence on the CO2 concentration. Sensing response curve has nearly linear fitting (R 2 = 0.9933) with CO2 gas concentration. The resistance of CsO2 nanoparticles increases in the presence of CO2 gas. This reflects the n-type behavior of as-synthesized CsO2 nanoparticles (Nemade and Waghuley 2013d, 2015b). The increase in resistance is also indicating the oxidizing nature of CO2 gas. The oxidizing gases have tendency to inject electron for sensing surface. This results in reduction of electron density in conduction band of sensing surface (Nemade and Waghuley 2015a). Therefore, resistance of CsO2 sensing surface is increase in the presence of CO2 gas.
Generally, gas sensing mechanism is dominated by the adsorption and desorption process through oxygen species (Fig. 6a). This is known as oxygen bridging mechanism. But in case of the materials, which itself contains superionic species such as O2 −, that is superoxide oxide, oxygen bridging mechanism laps. This may be due to adsorption of oxygen is not necessary for superoxide oxide. Therefore, it is necessary to develop mechanism for gas sensing by superoxide oxide. Through this paper, we proposed this mechanism, which is termed as “bridging oxygen-free mechanism” (Fig. 6b). According to this mechanism during the gas sensing, CO2 directly converted into the surface carbonates, without adsorption of oxygen molecules, which is generally observed in another materials.
Figure 7 shows that the operating temperature response of CsO2 nanoparticle-based sensor was studied towards the 250 ppm CO2 gas. The sensing response value increases up to 448 K. Beyond 448 K, sensing response starts to decrease. This is the operating temperature (448 K) for as-fabricated sensor. This decrease in sensing response may attribute to desorption of gas molecules. Beyond fixed temperature, the response value starts to decrease, which is assigned to desorption of adsorbed oxygen molecules from sensing surface. At higher temperature, due to increase in internal thermal vibration adsorbed oxygen is detached from the sensing surface (Nemade and Waghuley 2013e).
Figure 8 shows transient response of CsO2 nanoparticles towards 250 ppm CO2 gas at room temperature. The plot shows sensor-exhibited fast response time around 50 s and recovery time 40 s. This shows that sensors have good practical applicability. The fast response and recovery time attributed to fast interaction between target gas molecules and superoxide-based sensing material. The fast interaction between gas and sensing surface is due to absence of bridging oxygen layer as CsO2 nanoparticles itself contains superionic species such as O2 −.
Figure 9 shows the stability performance of CsO2 nanoparticles against 250 ppm CO2 gas at room temperature. The sensing curve shows nearly stable response for the entire month.
Conclusions
Stable CsO2 nanoparticles were prepared by solution-processed spray pyrolysis method. The prepared particles were characterized by various techniques to confirm structural, chemical and optical purity. The Raman spectroscopy directly shows that as-synthesized nanoparticles contain the superoxide ions. The gas sensing performance of CsO2 nanoparticles towards the CO2 gas quite fit for practical application. The operating temperature was found to be 448 K. The as-fabricated sensor shows good stability and rapid response and recovery time. The fast response and recovery time characteristic of sensor is attributed to “bridging oxygen-free mechanism”. The study towards further development of “bridging oxygen-free mechanism” is currently underway in our lab.
References
Alwan AM, Dheyab AB (2017) Room temperature CO2 gas sensors of AuNPs/mesoPSi hybrid structures. Appl Nanosci 7:335
Bates JB, Boyd GE, Brooker MH (1972) Raman spectra of O– 2 and O– 3 ions in alkali-metal superoxides and ozonides. Chem Phys Lett 16:391
Bryantsev VS, Giordani V, Walker W, Blanco M, Zecevic S, Sasaki K, Uddin J, Addison D, Chase GV (2011) Predicting solvent stability in aprotic electrolyte Li–air batteries: nucleophilic substitution by the superoxide anion radical (O2•–). J Phys Chem A 115:12399
Budanur BM, Khan FA (2014) Superoxide chemistry revisited: synthesis of tetrachloro-substituted methylenenortricyclenes. Beilstein J Org Chem 10:2531
Chinh ND, Quang ND, Lee H, Hien TT, Hieu NM, Kim D, Kim C, Kim D (2016) NO gas sensing kinetics at room temperature under UV light irradiation of In2O3 nanostructures. Sci Rep 6:35066
Hartmann P, Bender CL, Vracar M, Durr AK, Garsuch A, Janek J, Adelhelm P (2013) A rechargeable room-temperature sodium superoxide (NaO2) battery. Nat Mater 12:228
Morrison SR (1987) Selectivity in semiconductor gas sensors. Sens Actuators 12:425
Muhsien MA, Salem ET, Agool IR, Hamdan HH (2014) Gas sensing of Au/n-SnO2/p-PSi/c-Si heterojunction devices prepared by rapid thermal oxidation. Appl Nanosci 4:719
Nemade KR, Waghuley SA (2013a) Synthesis and characterization of bismuth oxide quantum dots. Adv Sci Eng Med 5:988
Nemade KR, Waghuley SA (2013b) Low temperature synthesis of semiconducting α-Al 2 O 3 quantum dots. Ceramics Int 40:6109
Nemade KR, Waghuley SA (2013c) LPG sensing application of graphene/CeO 2 quantum dots composite. AIP Conf Proc 1536:1258
Nemade KR, Waghuley SA (2013d) Carbon dioxide gas sensing application of graphene/Y2O3 quantum dots composite. Int J Modern Phys Conf Series 22:380
Nemade KR, Waghuley SA (2013e) Chemiresistive gas sensing by few-layered graphene. J Electron Mater 42:2857
Nemade KR, Waghuley SA (2014a) Synthesis of MgO nanoparticles by solvent mixed spray pyrolysis technique for optical investigation. Int J Metals 2014:389416
Nemade KR, Waghuley SA (2014b) Role of defects concentration on optical and carbon dioxide gas sensing properties of Sb 2 O 3/graphene composites. Opt Mater 36:712
Nemade KR, Waghuley SA (2015a) Comparative study of carbon dioxide sensing by Sn-doped TiO2 nanoparticles synthesized by microwave-assisted and solid-state diffusion route. Appl Nanosci 5:419
Nemade KR, Waghuley SA (2015b) Carbon dioxide gas sensing by Ag/TiO2 composites prepared by solid-state diffusion and chemical routes. J Chinese Adv Mater Soc 3:9
Ren X, Wu Y (2013) A low-overpotential potassium–oxygen battery based on potassium superoxide. J Am Chem Soc 135:2923
Zhang DH, Xue ZY, Wang QP (2002) The mechanisms of blue emission from ZnO films deposited on glass substrate by rf magnetron sputtering. J Phys D 35:2837
Zumsteg A, Ziegler M, Kanzig W, Bosch M (1974) Magnetische und kalorische Eigenschaften von Alkali-Hyperoxid-Kristallen. Phys Condens Matter 1974:267
Acknowledgements
The authors acknowledge Prof. S.K. Omanwar, Head, Department of Physics, Sant Gadge Baba Amravati University, Amravati for providing necessary facilities for the work.
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Nemade, K.R., Waghuley, S.A. Synthesis of stable cesium superoxide nanoparticles for gas sensing application by solution-processed spray pyrolysis method. Appl Nanosci 7, 753–758 (2017). https://doi.org/10.1007/s13204-017-0619-2
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13204-017-0619-2