Abstract
Titania nanotubular structure was prepared by anodizing titanium metal in the fluoride containing electrolytes and studied for hydrogen reduction using photo electrochemical cell. Potentiodynamic scan was performed before actual anodizing to optimize the anodizing conditions. The morphology of the TiO2 nanotubes was investigated by SEM and the presence of TiO2 nanotubes was confirmed. Raman spectroscopy was done to confirm the different phases present. Hydrogen generation capability was revealed by electrochemical testing in three-electrode system in dark and in visible light at 200 W power using Gamry Potentiostat. The corrosion potential of TiO2 nanotubes produced was found to be more active side in potassium hydroxide solution under visible light than in the dark condition. Cathodic polarization behavior of specimens in the presence of light showed more activity towards hydrogen generation than in dark condition. In comparison, the hydrogen generation capability of specimen anodized in 2H15 electrolyte was higher than specimens anodized in other electrolytes. Electrochemical impedance spectroscopy was used to study the charge transfer resistance of the nanotubes produced. The results showed that TiO2 nanotubular structure is a promising material for photoelectrochemical cell. Low-charge transfer resistance also depicts that it can be efficiently used to harvest solar energy.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
Nanotubular materials are of great importance due to their exceptional physical properties and potential applications. In terms of surface activity, open mesoporous structure offers highest surface area-to-volume ratio among many other nanostructured materials (Cochran et al. 2007; Lee et al. 2011). Moreover, titania nanotubes have attracted considerable attention because of their energy applications like in photo-catalysis, photo-splitting of water, gas-sensing devices, photovoltaic devices such as dye-sensitized solar cells, and photo electrochemical cells (Lee et al. 2014). Titanium metal has an excellent corrosion resistance due to its inherent tendency to form passive oxide film. The passive oxide film formed is a semiconductor with a wide bandgap (Dobrzański et al. 2016). Techniques used for the synthesis of nanostructured titania, ranging from nanotubes to nanowires and nanopores, include hydrothermal method (Kasuga et al. 1999; Nian and Teng 2006; Tsai et al. 2006; Zhang et al. 2003), sol–gel technique (Momeni and Ghayeb 2016), atomic layer deposition (Knez et al. 2007; Zazpe et al. 2016; Shin et al. 2004), and anodization (Endut et al. 2013; Macak et al. 2007; Salari et al. 2011). Anodization has received attention as it is comparatively cost-effective and represents an ideal solution for developing nanostructured TiO2 for use in the variety of fields (Bozzini et al. 2008; Ellingsen 1990).
The self-organized nanotubes or nanoporous morphology of TiO2 on titanium surface can be produced in fluoride containing electrolyte by electrochemical anodization. The configuration, dimensions, shape, and activity of the grown nanotubes are affected by the process parameters. By varying the electrolyte composition and the potential applied, the diameter of the nanotubes in the desired narrow range can be achieved (Marichy et al. 2012). The length of the nanotubes can be increased or decreased by changing the pH of the electrolyte and/or by anodizing time (Sreekantan et al. 2009; Zwilling et al. 1999; Lim et al. 2012). To grow nanotubes having specific properties, the optimization of the anodizing condition is very critical. The pre-surface condition, nature of electrolyte (aqueous/organic), voltage ramp, fluoride ion concentration, and potential are all of great concern. The qualification of process parameters by potentiodynamic polarization of CP titanium in the desired electrolyte would be beneficial for optimization. Due to the pollution caused by and the depletion of fossil fuels, harnessing solar energy to achieve hydrogen as green energy carrier may be an alternative method to resolve the energy crisis. Since photo catalytic water splitting using TiO2 as photo anode was successfully reported by Fujishima and Honda (Fujishima and Honda 1972), TiO2 has been considered as the best hopeful material for this use owing to its extraordinary photo catalytic activity, low cost, nontoxicity, and photochemical stability (Nada et al. 2005; Kitano et al. 2007; Mishra et al. 2003; Paulose et al. 2006; Yi et al. 2008).
In the present work, TiO2 nanotubes were synthesized using different electrolytes containing varying amounts of fluoride ions by keeping voltage and anodization time constant. A very novel technique in this current research was devised in order to lower the possible amounts of NH4F (expensive compared to diammonium phosphate) using (NH4)2HPO4. These reduced amounts of NH4F were proved to be beneficial in hydrogen generation and also in the application of Photo Electrochemical Cell. The morphology of synthesized nanotubes was investigated by using scanning electron microscopy. Raman spectroscopy was done to confirm the different phases of TiO2 nanotubes present. As the nanotubes were synthesized for the application in photo electrochemical cell, synthesized titania nanotubes were characterized for their electrochemical performance. Three-electrode system was employed for the testing like corrosion potential, potentiodynamic scan, and electrochemical impedance spectroscopy. A comparison of the electrochemical trends was done by testing the synthesized nanotubes in the dark and in the presence of illumination source of known intensity.
Experimental
Materials
Commercially pure titanium metal was selected as substrate material in this research work. The chemical composition of the material was determined by X-ray fluorescence (Table 1). The analytical grade chemicals, i.e., ammonium fluoride (NH4F), diammonium phosphate ((NH4)2HPO4), and ethylene glycol (C2H6O2), were used for electrochemical anodization. Ethanol and acetone were used for cleaning. All the electrolytes were prepared in deionized water. Rinsing of specimens before and after anodizing was also carried out. (Ghicov et al. 2005; Tan et al. 2012; Lim et al. 2012).
Sample preparation for anodizing
The test specimens were prepared by the following method: titanium strip of 0.8 mm thickness was used as substrate material. The samples were cut into sizes of 25 cm × 12.5 cm × 0.8 mm. After cutting, the specimens were cold mounted and ground with emery papers of 100, 120, 180, 220, 320, 400, 600, 800, 1000, 1200, 1500, 2000, and 2500 grit size. The ground specimens were degreased in acetone and rinsed with deionized water. The samples were labelled as 2H, 2H15, and 2H75. After grinding and rinsing, one side of the specimen was insulated by the mounting material to make it nonconductive.
Electrochemical anodizing
The specimens were anodized in different electrolytes. The composition of prepared electrolytes and anodizing conditions are given in Table 2.
The anodizing of the specimens was performed in a two-electrode cell system attached with a power supply (Matrix-MPS-3003L-3). Before connecting the sample to the anode, the power supply was turned on and required voltage was set by turning the voltage knob. Then, it was turned off after the voltage was set to the correct value. The working sample was made anode and graphite rod cathode. Properly clamped electrodes were immersed into electrolyte. Then, power supply was turned on and samples were anodized for required time. After anodizing, the samples were rinsed with deionized water and washed with ethanol. The specimens were then dried in the air.
The electrochemical optimization was investigated by means of potentiodynamic scans in electrolytes of different composition as given in Table 2. The specimens of titanium sheet were cut into 1.0 in × 0.5 in × 0.8 mm for electrochemical testing. The surface of the titanium was prepared before electrochemical testing. The primary objective of surface preparation was that the surface should response similar to commercially produced materials in electrochemical analysis. The working electrodes were ground with emery papers of up to 2500 grit size. The ground working electrodes were degreased in acetone, rinsed with deionized water, and then dried in air. The electrochemical study was conducted in three-electrode cell in which Ti sample was used as working electrode, graphite rod as counter/auxiliary, and standard calomel electrodes as reference electrode. The samples were electrically connected with wire. Equivalent weight and exposed surface area were calculated. The experimental parameters adjusted for optimization before anodizing for the bare specimens for Electrolytes 2H, 2H15, and 2H75 are given in Table 3.
Characterization
Anodized samples were observed at high magnification to reveal surface morphology at nanoscale by scanning electron microscope (Hitachi VP SEM S3400 N). The surface morphology of the anodized specimens was investigated by scanning electron microscope (SEM) (JSm-5600LV). The anodized specimens were investigated for the composition using energy dispersive X-ray spectroscopy (EDS).
The anodized specimens were tested in dark as well as in the presence of light for the comparison. A bulb of 200 W power was used for illumination purpose. Corrosion potential test, photodynamic polarization test, and electrochemical impedance spectroscopy (EIS) were performed in 0.5 M KOH solution.
To investigate the corrosion potential (E corr) of the anodized specimens, corrosion potential test was performed. The input parameter for the test is given in Table 4.
The anodized specimens were cathodically polarized in three-electrode cell system to measure corrosion potential (E corr), and corrosion current (I corr). Potentiodynamic polarization scan can also help us to validate the passivity of the samples in the particular environment. The initial delay for open circuit potential was 300 s and stability 0.1 mV/s. During potentiodynamic polarization, the initial potential was −0.5 V versus open circuit potential, the final potential was 2 V versus open circuit potential and scan rate of 10 mV/s.
EIS was performed to observe the charge transfer behavior in that particular electrolyte. Tests were performed in dark as well as in the presence of light in 0.5 M KOH solution to observe the performance of the synthesized TiO2 nanotubular structure. The test conditions and input values are given in Table 5.
Results and discussion
Electrochemical anodizing and optimization of anodizing conditions
Table 1 shows the chemical composition of as-received Titanium metal. The chemical composition was determined by X-ray fluorescence. The polished samples ground up to 2500 grit size were anodized in three different electrolytes as mentioned in Table 2, i.e., 2H, 2H15, and 2H75. The observed color of the anodized specimens was light grey with golden shade. The organic-based electrolytes were used for the anodization.
The potentiodynamic trends (current versus potential) of as-received samples were obtained to study the variation in current under constantly increasing potential at the rate of 10 mV/s up to potential of 6 V.
As evident in Fig. 1, the potentiodynamic scan for 2H sample shows that at low potential, there is an increase in value of current which depicts the dissolution of the oxide layer already formed on the surface of the substrate. After that the value of the current is slightly decreased which shows the formation of oxide layer. The value of current is then gradually increased to a maximum value, and after 1.5 V, value of current remained almost constant.
The low current value at higher potential suggested more dissolution rate of TiO2 than its growth and results in a nanotubular structure as confirmed by SEM analysis shown in Fig. 2. The presence of oxygen in the EDS analysis also confirms the formation of TiO2 layer (Diebold 2003; Mo and Ching 1995; Tang et al. 1994; Li et al. 2007; Yin et al. 2003; Kang 2003). The EDS spectrum of the anodized specimen in 2H is shown in Fig. 3 and elemental analysis is shown in Table 6.
In 2H15 electrolyte, the value of current reaches to 190 µA at low voltage and decrease gradually, and after that, the value of current becomes constant up to 6 V. Potentiodynamic curve of the sample is shown in Fig. 4.
SEM micrograph of the specimen has been shown in Fig. 5, after anodizing, and confirmed the formation of nanotubular structure. The EDS spectrum of 2H15 specimen is shown in Fig. 6. The weight% and atomic% composition of the anodized specimen is given in Table 7. The presence of 35.77 weight% oxygen confirmed the oxide formation after anodizing.
Potentiodynamic scan for 2H75 sample is shown in Fig. 7. As evident from the figure, the current initially decreases near zero potential and then increases to 82 µA which is then became constant up to 6 V. This shows dissolution and growth of oxide layer, respectively (Kim et al. 2003; Kolen et al. 2003; Hoyer 1996).
Anodizing results in almost uniform porous structure with a little dissolution were confirmed by SEM analysis in Fig. 8. The EDS spectrum of sample is shown in Fig. 9 which shows the presence of oxygen and confirmed the oxide formation. The EDS analysis for 2H75 is shown in Table 8.
Raman spectra
The anodized samples were characterized using Raman spectroscopy. Figure 10 shows Raman spectra of anodized samples. The spectra shows different phases of titania present having different intensities in different electrolytes. Some of the peaks were observed slightly shifted from the standard pattern, while some peaks were broadened as observed by the previous research workers (Gong et al. 2001; Ghicov et al. 2005; Bauer et al. 2006).
Electrochemical analysis
Potentiodynamic, corrosion potential, and electrochemical impedance spectroscopy analysis were examined to characterize the hydrogen reduction behavior of anodized samples in 0.5 M KOH solution in dark and in the presence of light. For illuminated characterization, the samples were irradiated by Philips Electric Fluorescent Bulb of 200 W power having 2725 Lumens intensity. The cell was placed in box to insulate it from surrounding light.
The electrochemical behavior of 2H, 2H15, and 2H75 samples was characterized by open circuit potential in 0.5 M KOH solution. The behavior of corrosion potential of 2H sample, in dark and in the presence of light, is shown in Fig. 11. The scans were obtained by exposing the surface area of 2.3 cm2 in 0.5 M KOH solution for 600 s using Gamry Potentiostat (PC14/750).
The corrosion potential of first sample is initially around −0.298 V which gradually decreases to −0.322 V when tested in the absence of any illumination. The potential of the sample, when tested in the presence of light, was around −0.431 V which remains constant for the period of 600 s and reached to −0.435 V. The testing shows that the 2H sample has more negative potential in the light than dark which shows that more energetic electrons are available for reduction of H2.
As shown in Fig. 12, the corrosion potential for 2H15 in dark is the same as for 2H, but in the presence of light, it is more negative than 2H. The corrosion potential of sample is initially around −0.325 V which gradually decreases to −0.273 V when tested in the absence of any illumination. The potential of the sample, when tested in the presence of light, was around −0.508 V which remains constant for the period of 600 s and reached to −0.525 V. This indicates rate of H2 reduction is higher.
The corrosion potential for 2H75 in KOH solution is shown in Fig. 13. The corrosion potential for 2H75 is positive both in dark and in the presence of light as compared to other two samples (2H and 2H15). This shows that H2 reduction rate is lower in case of 2H75. The corrosion potential of the first sample was initially around −0.129 V which gradually decreases to −0.124 V when tested in the absence of any illumination. The potential of the sample, when tested in the presence of light, was around −0.353 V which remains constant for the period of 600 s and reached to −0.391 V. The graph in Fig. 14 shows the trend of the corrosion potential of all the specimens in dark as well as in irradiated conditions and is in confirmation with the previous researchers (Ratner et al. 2008; Yao and Webster 2006; Marcus 2002).
The anodized samples were studied by potentiodynamic scans. The samples were cathodically polarized to see the capability of the specimen for hydrogen reduction. The potentiodynamic scan of specimen 2H is shown in Fig. 15. The specimen shows increase in the current density in the presence of light. The light promotes the reduction and, hence, the current density as a facilitating source for the voltage which imparts energy to overcome the reduction potential barrier. The value was 29.70E−06 A/cm2 in the absence of light. This value increases to 71.78E−06 A/cm2 which showed increase in the activity towards hydrogen reduction.
In case of the specimen 2H15 (the potentiodynamic scan has been shown in Fig. 16), the activity of the anodized sample was observed to be increased from 13.88E−06 A/cm2 in dark to 78.56E−06 A/cm2 in the presence of light. This specimen shows an increase in activity to split the water in the presence of light as found by the previous researchers (Taveira et al. 2006; Sul et al. 2001; Meekins 2012; Yao and Webster 2006).
The specimen 2H75 (the potentiodynamic scan has been shown in Fig. 17) showed a different behavior than the other two samples. It shows a decrease in the current density when compared its performance in dark with that in the presence of light. The value of current was 74.02E−06 A/cm2 in dark which is decreased to 9.252E−06 A/cm2 when tested in the presence of light.
The Nyquist plot [Impedance (real) vs. Impedance (imaginary)] for specimen 2H is shown in Fig. 18. The anodized specimen showed an increase in Z real component in the presence of light than in the absence of light. This depicts an increase in charge transfer resistance of the anodized sample. The value of R ct was 9.38E−05 S*s^a initially which slightly increase to 9.56E−05 S*s^a.
In case of 2H15 specimen, the value of R ct was 2.86E−04 S*s^a in dark which then decreased to a value of 1.11E−04 S*s^a. This recession in the value of R ct depicted a decrease in the charge transfer resistance which means more capability to reduce the hydrogen in the presence of light. The EIS scan is shown in Fig. 19.
The specimen 2H75 showed a decrease in the charge transfer resistance in the presence of light, as shown in Fig. 20. The value of R ct was initially 8.01E−05 S*s^a in dark which decreases to a value of 1.04E−04 S*s^a. This trend shows that the specimen anodized in 2H57 electrolyte has less charge transfer resistance and, hence, more potential to split the water when tested in the presence of light. Figure 21 summarizes EIS trends of all anodized samples in dark and in the presence of light.
Conclusions
The conditions to produce self-organized nanotubular structure on titanium were optimized by anodic potentiodynamic polarization scan. The formation of TiO2 nanotubes in fluoride-based electrolytes was found to be a complex phenomenon. It was found that both the voltage and fluoride ions concentration affect the growth of TNT’s equally. The conditions to produce self-organized nanotubular structure on titanium at 30 V and for 120 min were optimized by potentiodynamic polarization scan. It is found that the concentration of fluoride ions affects the growth of TNTs. The current research work is emphasizing the use of (NH4)2HPO4 to modify the extent of self-organization of titania nanotubes. The use of (NH4)2HPO4 also reduces the amounts of NH4F to be used in electrolyte and enhanced the capability of hydrogen generation. It is found that the concentration of fluoride ions affects the growth of TNT’s. The extent of self-organization was modified with the little addition of (NH4)2HPO4 in the electrolyte. Raman spectroscopy confirms the presence of nanotubular structure. The presence of oxygen in the EDS analysis shows the formation of oxide layer. The more negative potential in light shows increase in surface activity which depicts higher hydrogen reduction than in dark. The cathodic polarization trend showed increase in hydrogen reduction reaction in the presence of light. The electrochemical impedance spectroscopy validated the decrease in charge transfer resistance on exposure to light. The electrochemical behavior depicting in hydrogen generation tendency trend was exceptionally lower on sample anodized in 2H solution compared to 2H15 and 2H75 solution which may be related to surface morphology obtained. Comparatively higher efficiency of hydrogen reduction at the surface of 2H15 was observed as validated by corrosion potential, potentiodynamic, and electrochemical impedance spectroscopy. It is concluded from the results that optimum conditions for the formation of nanotubular structure and its performance towards hydrogen generation were relatively higher for the specimen anodized in 2H15 electrolytes.
References
Bauer S, Kleber S, Schmuki P (2006) TiO2 nanotubes: tailoring the geometry in H3PO4/HF electrolytes. Electrochem Commun 8(8):1321–1325. doi:10.1016/j.elecom.2006.05.030
Bozzini B, Carlino P, D’Urzo L, Pepe V, Mele C, Venturo F (2008) An electrochemical impedance investigation of the behaviour of anodically oxidised titanium in human plasma and cognate fluids, relevant to dental applications. J Mater Sci 19(11):3443–3453. doi:10.1007/s10856-008-3487-1
Cochran RE, Shyue JJ, Padture NP (2007) Template-based, near-ambient synthesis of crystalline metal-oxide nanotubes, nanowires and coaxial nanotubes. Acta Mater 55:3007–3014. doi:10.1016/j.actamat.2007.01.005
Diebold U (2003) The surface science of titanium dioxide. Surf Sci Rep 48:53–229
Dobrzański LA, Szindler MM, Szindler M, Lukaszkowicz K, Drygala A, Prokopiuk vel Prokopowicz M (2016) Nanocrystalline TiO2 powder prepared by sol–gel method for dye-sensitized solar cells. Arch Metall Mater 61(2):833–836. doi:10.1515/amm-2016-0140
Ellingsen JE (1990) A study on the mechanism of protein adsorption to Tio2. Biomaterials 12:593–596
Endut Z, Hamdi M, Basirum WJ (2013) An investigation on formation and electrochemical capacitance of anodized titania nanotubes. Appl Surf Sci 280:962–966. doi:10.1016/j.apsusc.2013.05.118
Fujishima A, Honda K (1972) Electrochemical photolysis of water at a semiconductor electrode. Nature 238:37–38
Ghicov A, Tsuchiya H, Macak JM, Schmuki P (2005) Titanium oxide nanotubes prepared in phosphate electrolytes. Electrochem Commun 7(March):505–509. doi:10.1016/j.elecom.2005.03.007
Gong D, Grimes CA, Varghese OK, Wenchong H, Singh RS, Chen Z, Dickey EC (2001) Titanium oxide nanotube arrays prepared by anodic oxidation. J Mater Res 16(12):3331–3334
Hoyer P (1996) formation of a titanium dioxide nanotube array. Langmuir 12(6):1411–1413
Kang Misook (2003) Synthesis of Fe/TiO2 photocatalyst with nanometer size by solvothermal method and the effect of H2O addition on structural stability and photodecomposition of methanol. J Mol Catal A 197:173–183
Kasuga T, Hiramatsu M, Hoson A, Sekino T, Niihara K (1999) Titania nanotubes prepared by chemical processing. Adv Mater 11(15):1307–1311
Kim CS, Moon BK, Park JH, Chung ST, Son SM (2003) Synthesis of nanocrystalline TiO2 in toluene by a solvothermal route. J Cryst Growth 254:405–410. doi:10.1016/S0022-0248(03)01185-0
Kitano M, Takeuchi M, Matsuoka M, Thomas JM, Anpo M (2007) Photocatalytic water splitting using Pt-loaded visible light-responsive TiO2 thin film photocatalysts. Catal Today 120:133–138. doi:10.1016/j.cattod.2006.07.043
Knez M, Nielsch K, Niinistö L (2007) Synthesis and Surface engineering of complex nanostructures by atomic layer deposition. Adv Mater 19(21):3425–3438. doi:10.1002/adma.200700079
Kolen YV, Burukhin AA, Churagulov BR, Oleynikov NN (2003) Synthesis of nanocrystalline TiO2 powders from aqueous TiOSO4 solutions under hydrothermal conditions. Mater Lett 57:1124–1129
Lee J, Jho JY (2011) Fabrication of highly ordered and vertically oriented TiO2 nanotube arrays for ordered heterojunction polymer/inorganic hybrid solar cell. Solar Energy Mater Solar Cells 95(11):3152–3156. doi:10.1016/j.solmat.2011.06.046
Lee K, Mazare A, Schmuki P (2014) One-dimensional titanium dioxide nanomaterials: nanotubes. Chem Rev 114(19):9385–9454
Li JG, Ishigaki T, Sun X (2007) Anatase, brookite, and rutile nanocrystals via redox reactions under mild hydrothermal conditions: phase-selective synthesis and physicochemical properties. J Phys Chem C 111(13):4969–4976
Lim CL, Zainal Z, Hussein MZ, Tan W (2012) Effect of electrolyte composition in electrochemical synthesis of self-. Adv Mater Res 364:298–302. doi:10.4028/www.scientific.net/AMR.364.298
Macak JM, Tsuchiya H, Ghicov A, Yasuda K, Hahn R, Bauer S, Schmuki P (2007) TiO2 nanotubes: self-organized electrochemical formation, properties and applications. Curr Opin Solid State Mater Sci 11(1–2):3–18. doi:10.1016/j.cossms.2007.08.004
Marcus P (2002) Corrosion mechanisms in theory and practice, 2nd edn. CRC Press, Boca Raton
Marichy C, Bechelany M, Pinna N (2012) Atomic layer deposition of nanostructured materials for energy and environmental applications. Adv Mater 24(18):1017–1032. doi:10.1002/adma.201104129
Meekins BH (2012) Controlling interfacial transfer processes for improved photoelectrochemical performance. University of Notre Dame, Notre Dame
Mishra PR, Shukla PK, Singh AK, Srivastava ON (2003) Investigation and optimization of nanostructured TiO2 photoelectrode in regard to hydrogen production through photoelectrochemical process. Int J Hydrog Energy 28:1089–1094
Mo SD, Ching WY (1995) Electronic and optical properties of three phases of titanium dioxide: rutile, anatase, and brookite. Phys Rev B 51(19):23–32
Momeni MM, Ghayeb Y (2016) Fabrication, characterization and photoelectrochemical performance of chromium-sensitized titania nanotubes as efficient photoanodes for solar water splitting. J Solid State Electrochem 20(3):683–689. doi:10.1007/s10008-015-3093-3
Nada AA, Barakat MH, Hamed HA, Mohamed NR, Veziroglu TN (2005) Studies on the photocatalytic hydrogen production using suspended modified TiO2 photocatalysts. Int J HydrogEnergy 30:687–691. doi:10.1016/j.ijhydene.2004.06.007
Nian JN, Teng H (2006) Hydrothermal synthesis of single-crystalline anatase TiO2 nanorods with nanotubes as the precursor. J Phys Chem B 110(9):4193–4198
Paulose M, Mor GK, Varghese OK, Shankar K, Grimes CA (2006) Visible light photoelectrochemical and water-photoelectrolysis properties of titania nanotube arrays. J Photochem Photobiol, A 178:8–15. doi:10.1016/j.jphotochem.2005.06.013
Ratner DB, Brunette DM, Tengvall P, Textor M, Thomsen P (2008) Titanium in medicine. J Eng Med. doi:10.1243/0954411021536432
Salari M, Aboutalebi SH, Konstantinov K, Liu HK (2011) A highly ordered titania nanotube array as a supercapacitor electrode. Phys Chem Chem Phys 13:5038–5041. doi:10.1039/c0cp02054k
Shin H, Jeong DK, Lee J, Sung MM, Kim J (2004) Formation of TiO2 and ZrO2 nanotubes using atomic layer deposition with ultraprecise control of the wall thickness. Adv Mater 16(14):1197–1200. doi:10.1002/adma.200306296
Sreekantan S, Hazan R, Lockman Z (2009) Photoactivity of anatase–rutile TiO2 nanotubes formed by anodization method. Thin Solid Films 518(1):16–21. doi:10.1016/j.tsf.2009.06.002
Sul YT, Johansson CB, Jeong Y, Albrektsson T (2001) The electrochemical oxide growth behaviour on titanium in acid and alkaline electrolytes. Med Eng Phys 23:329–346
Tan AW, Pingguan-Murphy B, Ahmad R, Akbar SA (2012) Review of titania nanotubes: fabrication and cellular response. Ceram Int 38(6):4421–4435. doi:10.1016/j.ceramint.2012.03.002
Tang H, Prasad K, Sanjinès R, Schmid PE, Lévy F (1994) Ellectrical and optical properties of TiO2 anatase thin films. J Appl Phys 75(4):2042–2047. doi:10.1063/1.356306
Taveira LV, Macak JM, Sirotna K, Dick LFP, Schmuki P, Electrochem Soc J, B-b Pages et al (2006) Voltage oscillations and morphology during the galvanostatic formation of self-organized TiO2 nanotubes. J Electrochem Soc 153(4):B137–B143. doi:10.1149/1.2172566
Tsai CC, Nian JN, Teng H (2006) Mesoporous nanotube aggregates obtained from hydrothermally treating TiO2 with NaOH. Appl Surf Sci 253(4):1898–1902. doi:10.1016/j.apsusc.2006.03.035
Yao C, Webster TJ (2006) Anodization: a promising nano-modification technique of titanium implants for orthopedic applications. J Nanosci Nanotechnol 6(9):2682–2692. doi:10.1166/jnn.2006.447
Yi H, Peng T, Ke D, Ke D, Zan L, Yan C (2008) Photocatalytic H2 production from methanol aqueous solution over titania nanoparticles with mesostructures. Int J Hydrog Energy 33:672–678. doi:10.1016/j.ijhydene.2007.10.034
Yin S, Fujishiro Y, Jihuai W, Aki M, Sato T (2003) Synthesis and photocatalytic properties of fibrous titania by solvothermal reactions. J Mater Process Technol 137:45–48
Zazpe R, Knaut M, Sopha H, Hromadko L, Prikryl J, Gartnerova V, Bartha JW, Macak Jan M (2016) Atomic layer deposition for coating of high aspect ratio TiO2 nanotube layers. Langmuir 32(41):10551–10558. doi:10.1021/acs.langmuir.6b03119
Zhang D, Yoshida T, Minoura H (2003) Low-temperature fabrication of efficient porous titania photoelectrodes by hydrothermal crystallization at the solid/gas interface. Adv Mater 15(10):814–817. doi:10.1002/adma.200304561
Zwilling V, David D, Perrin MY, Aucouturier M (1999) Structure and physicochemistry of anodic oxide films on titanium and TA6V alloy. Surf Interface Anal 27(7):629–637
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Ahmad, A., Haq, E.U., Akhtar, W. et al. Synthesis and characterization of titania nanotubes by anodizing of titanium in fluoride containing electrolytes. Appl Nanosci 7, 701–710 (2017). https://doi.org/10.1007/s13204-017-0608-5
Received:
Accepted:
Published:
Issue Date: