Abstract
Phase equilibria of the Cu-Cr-W and Cu-Cr-Mo systems were experimentally determined by using metallography, X-ray diffraction (XRD) and electron probe micro-analyzer (EPMA) techniques. Based on the experimental data determined by the present work, the thermodynamic assessments of the Cu-Cr-W and Cu-Cr-Mo systems were carried out by using CALPHAD method. A consistent set of the thermodynamic parameters has been obtained, which leaded to a good fit between calculated results and the experimental data in both the Cu-Cr-W and Cu-Cr-Mo systems.
Similar content being viewed by others
References
R. Muller, Arc-Melted CuCr Alloys as Contact Materials for Vacuum Interrupters, Siemens Forsch. - u. Entwickl. -Ber. Bd, 1988, 17, p 105-111
P.G. Slade, Advances in Material Development for High Power, Vacuum Interrupter Contacts, IEEE Trans. Com. Packag. Manuf. Technol., 1994, 17, p 96-106
Y. Wang and B. Ding, The Preparation and the Properties of Microcrystalline and Nanocrystalline CuCr Contact Materials, IEEE Trans. Com. Packag. Manuf. Technol., 1999, 22, p 467-472
Z.M. Zhou, Y.P. Wang, J. Gao, and M. Kolbe, Microstructure of Rapidly Solidified Cu-25wt.% Cr Alloys, Mater. Sci. Eng. A, 2005, 398, p 319-322
P. Frey, N. Klink, R. Michal, and K.E. Saeger, Metallurgical Aspects of Contact Materials for Vacuum Switching Devices, IEEE Trans. Plasma Sci., 1989, 17, p 734-740
S.H. Liang and Z.K. Fan, An Explorement on CuCrMoFe Contact Materials, Tech. Powder Metall., 1999, 17(2), p 122–124
C.P. Wang, X.J. Liu, I. Ohnuma, R. Kainuma, and K. Ishida, Formation of Immiscible Alloy Powders with Egg-Type Microstructure, Science, 2002, 297, p 990-993
C.P. Wang, X.J. Liu, I. Ohnuma, R. Kainuma, and K. Ishida, Formation of Core-Type Macroscopic Morphologies in Cu-Fe Base Alloys with Liquid Miscibility Gap, Metall. Trans. A, 2004, 35, p 1243-1253
B. Sundman, B. Jansson, and J.-O. Andersson, The Thermo-Calc Databank System, CALPHAD, 1985, 9, p 153-190
M. Hamalainen, K. Jasskelainen, R. Luoma, M. Nuotio, P. Taskinen, and O. Teppo, A Thermodynamic Analysis of the Binary Alloy Systems Cu-Cr, Cu-Nb and Cu-V, CALPHAD, 1990, 14(2), p 125-137
P. Gustafson, A Thermodynamic Evaluation of the Cr-Ni-W System, CALPHAD, 1987, 12, p 277-292
P.R. Subramanian and D.E. Laughlin, Cu-W (Copper-Tungsten), Phase Diagrams of Binary Tungsten Alloys, S.V. Nagender Naidu and P. Rama Rao, Ed., Indian Institute of Metals, Calcutta, 1991,
Y. Yu, C.P. Wang, Y.F. Li, X.J. Liu, I. Ohnuma, R. Kainuma, and K. Ishida, Experimental Investigation and Thermodynamic Calculation of the Phase Equilibria in the Cu-Mo-Ni Ternary System, Mater. Chem. Phys., 2011, 125, p 37-45
M. Hillert and C. Qiu, A Reassessment of the Fe-Cr-Mo-C System, J. Phase Equilib., 1992, 13, p 512-521
C.P. Wang, X.J. Liu, I. Ohauma, R. Kainuma, and K. Ishida, Phase Equilibria in the Cu-Fe-Mo and Cu-Fe-Nb Systems, J. Phase Equilib., 2000, 21, p 54-62
C.P. Wang, X.J. Liu, I. Ohauma, R. Kainuma, and K. Ishida, Phase Equilibria in Fe-Cu-X (X: Co, Cr, Si, V) Ternary Systems, J. Phase Equilib., 2002, 23, p 236-245
C.P. Wang, X.J. Liu, M. Jiang, I. Ohauma, R. Kainuma, and K. Ishida, Thermodynamic Database of the Phase Diagrams in Copper Base Alloy Systems, J. Phys. Chem. Solids., 2005, 66, p 256-260
Acknowledgments
This work was supported by the National Natural Science Foundation of China (Nos. 51031003 and 51171159), the Ministry of Education Foundation of China (No. 20120121130004). National Key Basic Research Program of China (973 program) (NO. 2012CB825700) is also acknowledged.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Wang, C.P., Huang, D.X., Zhu, J.J. et al. Experimental Investigation and Thermodynamic Calculation of the Phase Equilibria in the Cu-Cr-W and Cu-Cr-Mo Systems. J. Phase Equilib. Diffus. 35, 314–325 (2014). https://doi.org/10.1007/s11669-014-0311-0
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11669-014-0311-0