Abstract
A series of directional solidification experiments with superalloy CMSX-4 was carried out with various surface profiles. The results obtained clearly demonstrate the influence of surface features on the occurrence of freckles. The rough surfaces exhibit less freckling tendencies than smooth surfaces. For a notch depth larger than the critical layer beneath the surface, the freckle formation can be completely suppressed. The freckle formation is not only a surface defect but can initiate the occurrence of internal equiaxed and stray grains. The results of the present study can be applied to completely prevent freckle formation and the accompanying internal grain defects by using oversize with an appropriately roughened surface.
Similar content being viewed by others
References
A.F. Giamei and B.H. Kear: Metall. Trans., 1970, vol. 1, pp. 2185–92.
S.M. Copley, A.F. Giamei, S.M. Johnson, and M.F. Hornbecker: Metall. Trans., 1970, vol. 1, pp. 2193–2204.
S. Tin and T.M. Pollock: J. Mater. Sci., 2004, vol. 39, pp. 7199–7205.
T.M. Pollock and W.H. Murphy: Metall. Mater. Trans. A, 1996, vol. 27A, pp. 1081–94.
P. Auburtin, T. Wang, S.L. Cockcroft, and A. Mitchell: Metall. Mater. Trans. B, 2000, vol. 31B, pp. 801–11.
P. Auburtin, S.L. Cockcroft, A. Mitchell, and T. Wang: Superalloy 2000, T.M. Pollock, R.D. Kissinger, R.R. Bowman, K.A. Green, M. McLean, S.L. Olson, and J.J. Schirra, eds., TMS, Warrendale, PA, 2000, pp. 255–61.
D. Ma, Q. Wu, and A. Bührig-Polaczek: Metall. Mater. Trans. B, 2012, vol. 43B, pp. 344–53.
S. Tin: Ph.D. Thesis, University of Michigan, Ann Arbor, MI, 2001, p. 26.
S.D. Felicelli, D.R. Poirior, and J.C. Heinrich: J. Cryst. Growth, 1997, vol. 177, pp. 145–61.
M.C. Schneider, J.P. Gu, C. Beckermann, and U.R. Katterner: Metall. Mater. Trans. B, 1998, vol. 29B, pp. 847–55.
C. Frueh, D.R. Poirior, and S.D. Felicelli: Mater. Sci. Eng. A, 2002, vol. 328, pp. 245–55.
M. Medina, Y. Du Terrail, F. Durand, and Y. Fautrelle: Metall. Mater. Trans. B, 2004, vol. 35B, pp. 743–53.
J. Jain, A. Kumar, and P. Dutta: J. Phys. D: Appl. Phys., 2007, vol. 40, pp. 1150–60.
R.F. Katz and M.G. Worster: J. Computat. Phys., 2008, vol. 227, pp. 9823–40.
L. Yuan and P.D. Lee: ISIJ Int., 2010, vol. 50, pp. 1814–18.
C. Beckermann, J.P. Gu, and W.J. Boettinger: Metall. Mater. Trans. A, 2000, vol. 31A, pp. 2545–52.
J.C. Ramirez and C. Beckermann: Metall. Mater. Trans. A, 2003, vol. 34A pp. 1525–35.
S.N. Tewari and R. Tiwari: Metall. Mater. Trans. A, 2003, vol. 34A, pp. 2365–76.
S.N. Tewari, R. Tiwari, and G. Magadi: Metall. Mater. Trans. A, 2004, vol. 35A, pp. 2927–34.
Q. Feng, L.J. Carroll, and T.M. Pollock: Metall. Mater. Trans. A, 2006, vol. 37A, pp. 1949–62.
T.M. Pollock, J. Dibbern, M. Tsunekane, J. Zhu, and A. Suzuki: JOM, 2010, vol. 62, pp. 58–63.
J. Valdes, P. King, and X. Liu: Metall. Mater. Trans. A, 2010, vol. 41A, pp. 2408–16.
D. Ma, B. Zhou, and A. Bührig-Polaczek: Int. Foundry Res., 2010, vol. 62, pp. 32–40.
This work was supported by the Deutsche Forschungsgemeinschaft (DFG) through Grant No. BU1072/15-1 and -2. Appreciation is extended to S. Hollad, J. Norminikat, D. Lembrecht, and E. Schaberger-Zimmerman for their assistance in the experimental work.
Author information
Authors and Affiliations
Corresponding author
Additional information
Manuscript submitted January 31, 2012.
Rights and permissions
About this article
Cite this article
Ma, D., Bührig-Polaczek, A. The Influence of Surface Roughness on Freckle Formation in Directionally Solidified Superalloy Samples. Metall Mater Trans B 43, 671–677 (2012). https://doi.org/10.1007/s11663-012-9691-x
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11663-012-9691-x