Abstract
A series of poly(arylene ether)s with pendant cyclohexyl units had been prepared by solution polycondensation of 4,4′-cyclohexane-1,1′-diyldiphenol (CHDP) and 4,4′-difluorobenzophenone (DFBP) (or 4,4′-difluorodiphenylsulfone (DFDPS)). The inherent viscosities of obtained poly(arylene ether)s were in the range of 0.49–0.97 dLg−1. They were found to have high glass transition temperatures (Tg) of 158–208 °C, and good thermal stability with 5% weight-loss temperature (T5%) of 442–484 °C. The tensile test and dynamic mechanical analysis results indicate the good mechanical properties of poly(arylene ether)s. Their Young’s Mdoulus were found to be 2.2–2.3 GPa, tensile strengths were 81.0–97.7 MPa, storage mdoulus were over 1.5 GPa even near glass transition temperature. The complex viscosities of the resultant polymers melt maintained a narrow range of 308–313 Pas at 260 °C or 2700–4600 Pas at 340 °C during the testing time. That indicates the resultant resins have good melt flowability and stability. In addition, these poly(arylene ether)s were found to have good solubility in various solvents such as CHCl3, THF, NMP, DMAc, DMI, etc., and have good optical transmittance (>80%) at 450 nm. It suggests that the obtained poly(arylene ether)s not only can be processed by melt method, but also can be applied with solution method easily, and can be applied to tough and transparent films.
Similar content being viewed by others
References
Labadie JW, Hedrick JL, Ueda M (1996) Poly(aryl ether) synthesis. ACS Symp Ser 624:210–225
Rose JB (1997) Preparation and properties of poly(arylene ether sulphones). Polymer 15:456–465
Attwood TE, Dawson PC, Freeman JL, Hoy LRJ, Rose JB, Staniland PA (1981) Synthesis and properties of polyaryletherketones. Polymer 22:1096–1103
Shukla D, Negi YS, Uppadhyaya JS, Kumar V (2012) Synthesis and modification of poly(ether ether ketone) and their properties: a review. Polym Rev 52:189–228
Dhara MG, Banerjee S (2010) Fluorinated high-performance polymers: poly(arylene ether)s and aromatic polyimides containing trifluoromethyl groups. Prog Polym Sci 35:1022–1077
Miyatake K, Chikashige Y, Higuchi E, Watanabe M (2007) Tuned polymer electrolyte membranes based on aromatic polyethers for fuel cell applications. J Am Chem Soc 129:3879–3887
Burgal JDS, Peeva LG, Kumbharkar S, Livingston A (2015) Organic solvent resistant poly(ether-ether-ketone) nanofiltration membranes. J Membr Sci 479:105–116
Song Y, Wang JY, Li GH, Sun QM, Jian XG, Teng J, Zhang HB (2008) Synthesis, characterization and optical properties of fluorinated poly(aryl ether)s containing phthalazinone moieties. Polymer 49:4995–5001
Zhao Z, AH W, Luan SJ, Zhang CY (2015) Preparation and characterization of a positively charged nanofiltration membrane based on poly(arylene ether sulfone) with tertiary amine groups. J Polym Res 22:168
Pei XL, Zhai WT, Zheng WG (2015) Preparation of poly(aryl ether ketone ketone)–silica composite aerogel for thermal insulation application. J Sol-Gel Sci Technol 76:98–109
Xia JQ, Zhang J, Liao GX, Jian XG (2007) Copolymerization and blending of poly(phthalazinone ether ketone)s to improve their melt processability. J Appl Polym Sci 103:2575–2580
Zhang G, Zhou YX, Kong Y, Li ZM, Long SY, Yang J (2014) Semiaromatic polyamides containing ether and different numbers of methylene (2-10) units: synthesis and properties. RSC Adv 4:63006–63015
Wang YZ, Lin CH, Chan BW, Hsieh KH (2004) Synthesis and properties of thio-containing poly(ether ether ketone)s. Polym Int 53:320–325
Wang Y, Wang PP, Xu Q, Yan T, Cai MZ (2014) Synthesis and properties of novel copolymers of poly(ether ketone biphenyl ketone ether ketone ketone) and poly(ether ketone sulfone amide). J Polym Res 21:533
Liu YJ, Jian XG, Liu SJ, Zhang J (1999) Sythesis and characterization of poly(ether ketone ketone) contain the phthalazinone moiety. Acta Polym Sin 1:37–41
Zhou H, Bucio E, Venumbaka SR, Fitch JW, Cassidy P (2006) New spirodilactam polymers. Polymer 47:6927–6930
Gao N, Zhang SB, JP X (2012) Phenolphthalein-based Cardo poly(arylene ether sulfone): preparation and application to separation membranes. J Appl Polym Sci 128:1–12
Sheng SR, Ge WW, Huang ZZ, Liu XL, Song CS (2009) Synthesis and characterization of novel soluble cardo poly(arylene ether ketone)s containing xanthene structures. J Appl Polym Sci 114:570–576
Kawasaki S, Yamada M, Kobori K, Jin FZ, Kondo Y, Hayashi H, Suzuki Y, Takata T (2007) Synthesis and chemical, physical, and optical properties of 9,9-Diarylfluorene-based poly(ether−ether−ketone). Macromolecules 40:5284–5289
Honkhambe PN, Pasale SK, Bhairamadgi NS, Kumbhar KP, Salunkhe MM, Wadgaonkar PP (2010) Poly(ether ether ketone)s and poly(ether ether ketone ketone)s containing Cardo Decahydronaphthalene groups: synthesis and characterization. J Appl Polym Sci 122:1607–1613
Zhang G, Zhou YX, Li Y, Wang XJ, Long SR, Yang J (2015) Investigation of the synthesis and properties of isophorone and ether units based semi-aromatic polyamides. RSC Adv 5:49958–49967
Huang ZZ, LM Y, Sheng SR, Ge WW, Liu LX, Song CS (2008) Synthesis and characterization of novel soluble poly(ether ketone sulfone)s with pendant polychloro groups. J Appl Polym Sci 108:1049–1054
Cai MZ, Zhu MH, YK Y (2009) Synthesis and characterization of poly(ether ketone ether ketone ketone)/poly(ether ether ketone ketone) copolymers containing naphthalene and pendant cyano groups. J Appl Polym Sci 112:3225–3231
Zhu XJ, Yan T, Xu Q, Cai MZ (2016) Synthesis and characterization of novel poly(aryl ether ketone)s containing biphenylene moieties and pendant cyano groups. J Polym Res 23:24
Zhao XY, Wang CY, Zhang K, Zhou Z, Zhu MF (2010) Soluble poly (aryl ether)s containing naphthalene pendant group: synthesis, characterization and electrospinning. Colloid Polym Sci 288:907–914
Wu T, Liu PQ, Shi MW, Lu J, Ye GD, JJ X (2011) Novel copoly(ether ether ketone)s with pendant phenyl groups: synthesis and characterization[J]. Polym Int 60:1318–1323
Risse W, Sogah DY (1990) Synthesis of soluble high molecular weight poly(aryl ether ketones) containing bulky substituents. Macromolecules 23:4029–4033
Lin C, Lei Y, Feng J, Wang CY, Li JL, Xu Z (2007) Novel heterocyclic poly(arylene ether ketone)s: synthesis and polymerization of 4-(4′-hydroxyaryl)(2H)phthalazin-1-ones with methyl groups. J Polym Sci Polym Chem 45:1525–1535
Yildiz E, Inan TY, Yildirim H, Kuyulu A, Gungor A (2007) Thermal and mechanical properties of poly(arylene ether ketone)s having pendant tertiary butyl groups. J Polym Res 14:61–66
Sayyed MM, Maldar NN (2010) Novel poly(arylene-ether-ether-ketone)s containing preformed imide unit and pendant long chain alkyl group. Mater Sci Eng B 168:164–170
Riley DJ, Gungor A, Srinivasan SA, Sankarapandian M, Tchatchoua C, Muggli MW, Ward TC, Mcgrath JE (1997) Synthesis and characterization of flame resistant poly(arylene ether)s. Polym Egn Sci 37:1501–1511
Acknowledgments
This work was supported by research grants from the Natural Science Foundation of China (21274094, 21304060) and Outstanding Young Scholars Fund of Sichuan University (2015SCU04A25).
Author information
Authors and Affiliations
Corresponding authors
Rights and permissions
About this article
Cite this article
Lu, J., Yan, G., Zhang, G. et al. Synthesis and property investigation of poly(arylene ether)s with pendant cyclohexyl units. J Polym Res 24, 152 (2017). https://doi.org/10.1007/s10965-017-1317-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s10965-017-1317-1