Abstract
In this work, vanadium pentoxide (V2O5) nanoparticles-filled electrospun polyvinylpyrrolidone (PVP) nanofibers were investigated systematically at various nanofiller weight percentages (8 and 10 wt%) and input intensities to reveal the effective optical limiting feature in the visible spectrum. XRD analysis demonstrated the purity of the produced V2O5 nanoparticles. According to SEM findings, V2O5 nanoparticles were effectively integrated into the PVP nanofibers. Two distinct absorption bands were observed at around 400 and 217 nm. These bands were related to PVP and V2O5 nanoparticles in linear absorption measurements, respectively. Moreover, an increased Urbach energy value was obtained with an increase in V2O5 nanofiller content within PVP. Open-aperture Z-scan measurements were taken at 532 nm considering the band gap energy of the V2O5 nanofillers in PVP composite nanofibers. In 8 wt% V2O5 nanofilled PVP nanofibers, one-photon absorption (OPA) was the main nonlinear absorption (NA) mechanism, and the defect states of the V2O5 nanoparticles had no contribution to NA. On the other hand, sequential two-photon absorption was the main NA mechanism, and the defect states of the nanoparticles caused more efficient NA behavior in 10 wt% V2O5 nanofilled PVP nanofibers. The effective optical limiting behavior was obtained for this composite nanofiber with lower limiting threshold as 1.49 × 10–5 J/cm2. The V2O5 nanofilled PVP nanofibers presented strong potential optical limiters in the visible wavelength region. This was attributed to their high linear transmittance at low input intensities and their robust NA behavior at higher input intensities.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Introduction
High-level requirements for an ideal optical limiter include broadband optical limiting capability across the whole visible spectrum as well as broadband temporal capability from the sub-nanosecond to continuous regimes [1]. The development of the perfect broadband optical limiting materials has undergone a great deal of effort. These efforts are based on a variety of phenomena, such as saturable absorption, multiphoton absorption, nonlinear scattering, and nonlinear absorption. The material with high nonlinearity has many applications, including optical switches, optical limiters, lithium batteries, smart windows, and gas sensors [2,3,4,5,6]. Vanadium oxides are transition metal oxides (TMOs) with oxidation states of + 2 to + 5. Due to high oxygen-to-vanadium (O/V) ratio, vanadium pentoxide (V2O5) is the most stable phase and exhibits a phase transition at 257 °C [7, 8]. It has been the most studied vanadium oxide phase, due to its unique transition behavior from semiconductor to metal, with a wide optical band gap, improved thermal and chemical stability with excellent thermoelectric features [9,10,11]. Nevertheless, bulk V2O5 faces limitations due to its low vanadium dissolution issues, electrical conductivity, and slow reaction kinetics [12, 13]. The use of V2O5 has been demonstrated widely in gas sensors [14, 15], catalysis [16], electrochromic [17, 18], optoelectronic applications [19, 20], and solar cells [21, 22].
Nanoparticles can be incorporated into polymeric matrices to create nanofibers, ultimately enhancing their properties and introducing novel functionalities [23]. This allows modification of their physical, chemical, electrical, or optical characteristics. For example, metal oxide nanoparticles enhance tensile strength, while metal nanoparticles facilitate electrical conductivity within the nanofiber structure. Furthermore, to add optical functionalities, nanoparticles with particular optical properties can be included into nanofibers which are suited for use in light-emitting devices, sensors, and photonics.
It has been demonstrated that two-photon absorption causes substantial optical limiting (OL) in a number of semiconductors, including ZnSe, CdS, PbS, and ZnO, as well as in various organic materials [24,25,26,27,28,29]. However, few studies exist on the OL behavior of V2O5. Parida et al. examined optical limiting features of V2O5 nanoflowers based on three-photon absorption [30]. It was reported that the optical limiting behavior of V2O5 nanoflowers resulted from an effective three-photon absorption mechanism. Poonam et al. examined the OL response of the V2O5:MoO3 thin films [31]. Nonlinear absorption was reported to be enhanced with increasing thickness in the MoO3-doped sample. Saravanakannan et al. investigated the nonlinear absorption (NA) and OL behavior of the fluorine-doped V2O5 nanoparticles [32]. It was reported that the exhibited nonlinear absorption was due to genuine two-photon absorption process. OL response of the V2O5 thin films was also investigated by our group [33]. We observed defect-assisted nonlinear absorption behavior in V2O5 thin films and found that annealing at 450 °C enhances both the nonlinear absorption and optical limiting behavior.
In the literature, the nonlinear optical properties of the nanocomposite films have been extensively investigated [34,35,36,37,38,39] due to the combination of unique properties of nanoparticles and advantages of polymers. Beside these, there are few studies related with the nonlinear optical properties of the composite nanofibers. Pramod et al. reported the nonlinear optical character of electrospun benzil-poly(methyl methacrylate) (PMMA) nanofibers [40]. They reported that the nanofibers showed saturable absorption behavior at low input intensity and nonlinear absorption at higher input intensities. Yogeswari et al. examined the OL behavior of potassium dihydrogen phosphate (KDP)–polyethylene oxide (PEO) electrospun nanofibers [41]. They revealed that the excited-state absorption process played a dominant role in the observed nonlinearity and two-photon absorption was responsible for the observed OL performance. On the other hand, there is no study examining the linear optical features, charge transfer mechanisms, and OL features with limiting thresholds of the V2O5 nanoparticles-filled PVP composite nanofibers to the best of our knowledge. Nanoparticles have an exceedingly high surface-to-volume ratio owing to their small dimensions. This property increases the light–matter interactions compared to the bulk materials. Besides, nanofibers have high aspect ratio (length-to-diameter ratio), and this property supports increased light–matter interaction like in nanoparticles. The combined system (nanofibers filled with nanoparticles) should have higher light–matter interactions than either material. High light–matter interactions are possible due to the nanofibrous structure of electrospun mats, which significantly influences the materials' nonlinear optical properties. Therefore, in this work, V2O5 nanoparticles synthesized by the hydrothermal method were used as nanofillers in PVP nanofibers. Wide band gap of PVP enabled the use of these composite nanofibers in a wide spectral range. Open-aperture (OA) Z-scan measurements were taken at 532 nm under diverse input intensities considering band gap energies of the composite nanofibers and their defect states created by V2O5 nanoparticles. Linear optical features, charge transfer mechanisms, and OL features with limiting thresholds of the PVP/V2O5 composite nanofibers were reported for the first time.
Materials and methods
Materials
Ammonium metavanadate (NH4VO3), ethanol (CH3CH2OH), and nitric acid (HNO3) (65.0%) were purchased from Sigma-Aldrich. The polymer used is a polyvinylpyrrolidone (PVP) supplied from ACROS Organics. N–N dimethylformamide (DMF—ISOLAB, purity ≥ 99.0%) was used as solvent.
Synthesis of V2O5 nanoparticles and production of V2O5 composite nanofibers
V2O5 powders were produced through hydrothermal synthesis, as reported by Mu et al. [42]. For the precursor solution, 0.819 g of NH4VO3 was dissolved in 70 ml of ethanol with the help of nitric acid (2–3 ml). Nitric acid was used to adjust the precursor solution’s pH to about 3–4. The obtained precursor solution was vigorously stirred for half an hour. Subsequently, the solution was transferred to a Teflon-lined autoclave for reaction in an oven at 180 °C for 24 h. The obtained particles were then washed with water and ethanol several times before drying at 80 °C for 10 h. Lastly, the obtained powder was annealed at 500 °C for 1 h.
A schematic for the fabrication procedure of the nanofibers is provided in Fig. 1. A 20 wt% PVP in DMF solution was prepared with constant stirring at ambient temperature. Afterward, PVP solutions containing 8 and 10 wt% (% of PVP) of V2O5 nanoparticles were prepared. The nanoparticles were dispersed in polymer solutions through ultrasonication by a BANDELIN GM 2200 ultrasonic homogenizer. Then, electrospinning was performed at ambient temperature. The tip-to-collector distance of 15 cm, high voltage of 17.5 kV, and the flow velocity of 0.25 ml/h were found to be the ideal processing parameters. The nanofibers were electrospun onto fused silica substrates to take optical measurements. The obtained composite nanofibers were labeled as PVP/V2O5–8 and PVP/V2O5–10 for 8 and 10 wt% of V2O5 nanoparticles-filled PVP nanofibers, respectively.
Characterizations
The crystal structure of the powders was identified by Rigaku D/Max-2000 diffractometer with Cu K radiation operating at 40 kV from 10° to 90° at a scan rate of 0.5°/min, and FEI Nova Nano FEG-SEM model scanning electron microscope (SEM) was used to examine the morphology of the powders. The surface chemistry and oxidation state of the elements in the powders were examined using X-ray photoelectron spectroscopy (XPS) and Raman spectroscopy. A monochromatic Al Kα X-ray source (15 kV, 400 W) and a SPECS PHOIBOS hemispherical analyzer were used to perform the XPS investigations. As a benchmark, the nominal binding energy (B.E.) of the C1s signal, which is 284.68 eV, was chosen. With a 532-nm Nd:YAG laser as the excitation source, Raman spectra were recorded using a BRUKER FRA 106/S spectrometer. Using a Malvern Nano ZS, photon correlation spectroscopy was used to measure the average particle size of the nanoparticles dispersed in water. SEM images and EDS maps of the nanofibers were captured with a HITACHI SU5000 field emission scanning electron microscope (SEM) equipped with an Oxford X-MaxN 80 energy-dispersive X-ray spectroscopy (EDS). All nanofibers were sputter coated with gold (Au) prior to analysis. Aluminum tape was used instead of carbon tape for SEM–EDS sample preparation to improve the contrast during analysis; 100 nanofibers were used to estimate their average diameters using ImageJ software (NIH—USA). The composite nanofibers thicknesses were measured by a spectroscopic ellipsometer (Woollam M-2000V) at three angles of incidence (65, 70, and 75°). The thicknesses of the composite nanofiber mats were found as 1.3 µm. Shimadzu UV-1800 model UV–Vis spectrophotometer was used to reveal the linear optical absorption feature-related band gaps of the composite nanofibers. To observe the possible defect states constructed emission, photoluminescence measurements were taken by PerkinElmer LS55 spectrophotometer. Q-switched Nd:YAG (Quantel Brilliant) laser (4-ns pulse duration, 10-Hz repetition rate) at 532 nm was used to observe the nonlinear absorption (NA) behavior of the composite nanofibers with OA Z-scan measurements. The obtained results were evaluated for their optical limiting features.
Results and discussion
Morphological and structural properties of V2O5 nanopowders
The morphology of the V2O5 nanopowders was investigated by SEM analysis, and a representative micrograph is provided in Fig. 2a. The SEM image primarily showed aggregated irregular-shaped nanoparticles. All nanoparticles were dispersed in water to determine their average particle size using photon correlation spectroscopy. The d (0.5) and d (0.9) values were found to be around 235 and 432 nm, respectively. The XRD pattern of the synthesized V2O5 nanopowders is provided in Fig. 2b. The diffraction pattern was indexed to JCPDS #41–1426 with major diffraction peaks at 15.41°, 20.32°, 21.74°, 26.10°, 31.01°, 32.43°, 34.39°, 47.31°, and 51.23° corresponding to lattice planes of (200), (001), (101), (110), (301), (011), (310), (600), and (020), respectively. This indicated a pure orthorhombic phase of V2O5 [42,43,44,45]. No impurity peaks were obtained, proving the purity of the synthesized V2O5 nanopowders.
XPS spectra for V2p core levels and O1s are provided in Fig. 2c and d, respectively. According to Silversmit et al. [46], V2p3/2 signals appeared at 517.2, 515.8, 515.3, 513.7, 512.4 eV for the V5+, V4+, V3+, V2+, V0 states, respectively. In Fig. 2c, it is evident that apart from the major O1s signal at 529.9 eV, there are three distinct V2p XPS signals detected at 524.6, 517.1, and 515.7 eV. These signals can be ascribed to the V5+2p1/2, V5+2p3/2, and V4+2p3/2 states, respectively, in great harmony with the literature [17, 33, 46,47,48]. This confirmed that the predominant oxidation state of vanadium ions was + 5. It is also important to highlight that the binding energy (B.E.) position between the V5+2p3/2 and O1s signals has a value of Δ = 12.8 eV. Moreover, there is a spin–orbit splitting difference of Δ = 7.5 eV between the V5+2p1/2 and V5+2p3/2 signals. These findings strongly supported the conclusion that the vanadium oxidation state of + 5 is the dominant phase, consistent with previous studies [17, 46, 47]. On the other hand, the most intense signal at 529.9 eV in the O1s spectrum indicated the existence of a V–O bond [49,50,51], provided in Fig. 2d. O1s signals at 531.0 and 532.4 eV can be assigned to chemisorbed hydroxyl (OH) species [52, 53] and C=O/C–O(H) [17, 53, 54] residual organic oxygenates on the surface, respectively (Fig. 2d).
Raman spectroscopy was utilized to further characterize the structure of V2O5 powder. Figure 2e reveals V2O5 powder with Raman features located at around 145, 195, 283, 303, 405, 481, 525, 701, and 995 cm−1. Commercial V2O5 powder and thin film peak positions were discovered to be in excellent concurrence with those described in the literature [17, 55,56,57,58]. The vanadyl mode associated with the stretching of V–O brought on by unshared oxygen was responsible for the high-frequency Raman peak at 995 cm−1 [17, 50, 59]. The structural quality of the V2O5 nanoparticles was proved by the presence of this peak. Peaks located at 525 and 701 cm−1 were assigned to the stretching vibrations, and those at 303 and 481 cm−1 were related to bending vibrations of the V–O–V bridging bonds [17, 60, 61]. Peaks at 283 and 406 cm−1 were attributed to V=O bond bending vibration [62, 63]. On the other hand, the lattice vibrations of O–V–O atoms were represented by the Raman peaks at 145 and 197 cm−1 in the low-frequency zone [52, 64]. The layered structure of V2O5 was directly related to these two peaks [45]. The peak at about 144 cm−1 was a rigid, layer-like mode. When the growth temperature was above 300 °C, the presence of this peak was indicative of the layer-like structure of V2O5 films [65].
Morphological analysis of PVP/V2O5 composite nanofibers
The SEM micrographs shown in Fig. 3 show that uniform and cylindrical nanofibers were produced in each case. Moreover, the diameters of the composite nanofibers were found to be thinner than the unfilled (PVP) ones (Table 1). This trend was also noted in the literature [66], associating the reduction in nanofiber diameter with increased surface charge of the polymer jet. The presence of nanoparticles that are more conductive than the polymer induces strong elongational forces that are applied on the jet, and therefore thinner nanofibers are formed [66,67,68]. Nevertheless, no definitive conclusions can be drawn regarding the impact-increased nanofiller content, as the average diameters of PVP/V2O5–8 and PVP/V2O5–10 nanofibers exhibited a certain degree of similarity. To get better observation of the nanoparticles in PVP nanofibers, higher-resolution images are also provided as insets for composite nanofibers. The V2O5 nanoparticles were well incorporated into the PVP matrix of the nanofibers as shown in Fig. 3. The nanoparticles were clearly visible in the inset micrographs. These results are also confirmed by EDS maps provided in Fig. 4. As expected, vanadium (V) is particularly localized on the nanoparticles entrapped in the nanofibers. The primary elements, carbon (C), oxygen (O), and nitrogen (N), which were the constituents of PVP, were found to be concentrated on the nanofibers. Presence of gold (Au) was due to the sputter coating of the nanofibers. The presence of aluminum (Al) was due to the use of Al tape.
Linear optical analysis of PVP/V2O5 composite nanofibers
The linear optical absorption spectra of the composite nanofibers are provided in Fig. 5a. As shown in this figure, two absorption peaks were observed at wavelengths of 400 nm and 217 nm. The observed broad absorption at about 400 nm was attributed to the absorption of V2O5 nanoparticles in nanofiber mats. On the other hand, the narrow intense absorption peaks observed at 217 nm were attributed to the PVP matrix. The determined absorption behaviors also indicated that the increasing concentration of V2O5 nanoparticles in the composite nanofibers led to a decrease in absorption behavior, despite having nearly identical thickness.
A crucial parameter that influences the NA behavior of the composite nanofibers was their band gap. Therefore, they were determined by (αhν)2 versus hν graphs known as Tauc plots [33], presented in Fig. 5b and c. The band gaps were calculated and provided in these figures. Band gap values of 5.11 and 5.33 eV were obtained using the absorption spectra of PVP. These values were highly consistent with those reported in the literature for PVP [69,70,71,72]. The small variation between the band gaps of the composite nanofibers can be due to the differences between their thicknesses. Moreover, the band gap values of PVP/V2O5–8 and PVP/V2O5–10 composite nanofibers were found to be 2.26 and 2.52 eV, respectively. These values were found to be compatible with the literature [73,74,75]. Urbach energy of the materials was the second important parameter to explain NA mechanisms. By identifying the efficient NA mechanisms, the design of effective optical limiters can be achieved. The expression of the Urbach energy of the materials revealed using their linear absorption results is given below.
where EU is the Urbach energy, α is the absorption coefficient, and α0 is a constant. The Urbach energies of the composite nanofibers are determined from inverse slope of the linear region in lnα versus hν graph which is provided in Fig. 5d. The Urbach energies were determined as 1.63 and 1.91 eV for PVP/V2O5–8 and PVP/V2O5–10 composite nanofibers, respectively. This result indicated that the increasing concentration of the V2O5 nanoparticles in the PVP nanofibers led to an increase in defect states within the band gap of the composite nanofibers. The large Urbach energy reached for the studied composite nanofibers also demonstrated that the defect states were distributed to the deep energy region inside the band gap.
The photoluminescence spectra of the PVP/V2O5 composite nanofibers given in Fig. 6 are obtained under an excitation wavelength of 300 nm. Both PVP/V2O5–8 and PVP/V2O5–10 composite nanofibers had emission signals at 447, 484, 545, and 568 nm. The energy of the 447- and 484-nm peaks corresponded to the absorption band edge of the polymer. Therefore, these emission signals occurred during the transition of electrons from the defect states of the polymer to the valence band. On the other hand, the energies of 545 and 568 nm are corresponded to the absorption band edge of the V2O5 nanoparticles. Therefore, these emission signals originated during the transition of electrons from defect states to the valence band of the V2O5 nanoparticles. Besides, it was seen that the fluorescence intensity of these defect states was reduced with increase in the concentration of V2O5 nanoparticles in the polymer.
Nonlinear absorption and optical limiting analysis of PVP/V2O5 composite nanofibers
Nonlinear absorption behaviors of the PVP/V2O5 composite nanofibers were investigated by OA Z-scan measurements at 532 nm with 4-ns pulsed laser. The linear transmittance of the PVP/V2O5–8 and PVP/V2O5–10 composite nanofibers was 44% and 61%, respectively. These experiments were performed at pulse energies of 0.5, 1, and 1.5 µJ. The obtained experimental data with theoretical fits are presented in Fig. 7. It was clearly seen that all of the composite nanofibers presented a NA behavior. As seen in Fig. 7a, the NA increased with an increase in input intensity. On the other hand, the NA decreased with increasing input intensity as can be seen in Fig. 7b. This observation was attributed to filling of the defect states by one-photon absorption (OPA). As reported in the above section, these composite nanofibers have more defect states. Absorption from valence band to these defect states and/or absorption from these defect states to upper excited states would contribute to NA. Therefore, a theoretical fit model [Eq. (2)] considering the contribution of OPA, two-photon absorption (TPA), and free carrier absorption (FCA) to NA was used the determine the NA parameters such as nonlinear absorption coefficient (βeff) and saturable intensity threshold (ISAT) values. These parameters are more important for the optical limiting behavior of the materials. In this model, the first term represents the OPA and its saturation, the second term corresponds to the two-photon absorption (TPA) and its saturation, and the third term deals with free carrier absorption (FCA) and its saturation.
ΔN(I) is the generated photocarrier density, and \(\beta_{{{\text{eff}}}}\) is the effective NA coefficient given as
where α is the linear absorption coefficient, ℏω is the photon energy, β is the TPA coefficient, \({\uptau }_{0}\) is the pulse duration, and \({ }\sigma_{0 }\) is the FCA cross section. The following expression can be obtained by substituting Eqs. (3) and (4) in Eq. (2). The beam waist at the focus and Rayleigh length of the composite nanofibers are 25 µm and 0.36 cm, respectively.
Fitting details can be found in the literature [76]. The obtained fitting results are listed in Table 2. The βeff value of the PVP/V2O5–8 composite nanofibers increased from 8.32 × 10–6 to 2.99 × 10–5 m/W with an increase in the input intensity. Similarly, the βeff value increased from 8.27 × 10–6 to 3.58 × 10–5 m/W with an increase in the input intensity. As it can be clearly seen in Table 2, the βeff value increased with the V2O5 nanofiller amount in the nanofibers. Similarly, ISAT values of both composite nanofibers increased with the input intensity, and the higher value was obtained for the PVP/V2O5–10 composite nanofibers. These results could be described with possible NA mechanism of composite nanofibers. Taking into account the energy band gap values and Urbach energies of V2O5 nanoparticles and PVP, the OPA excites an electron from the valence band to the conduction band of V2O5 nanoparticles. There is no contribution that comes to NA from the defect states of V2O5 nanoparticles for PVP/V2O5–8 composite nanofibers. These electrons in the conduction band of V2O5 nanoparticles could be excited to the defect states of PVP via excited-state absorption (ESA) considering the energy band gap value of PVP/V2O5–8 composite nanofibers, and then, they could be excited to the conduction band of PVP with multiphoton absorption. On the other hand, for PVP/V2O5–10 composite nanofibers, the OPA was enough to excite an electron from the valence band to the defect states of V2O5 nanoparticles. Some of these electrons could have lost a part of their energy and cooled down to lower excited states, and they could be excited to the defect states of the PVP via ESA. The OPA + ESA process is known as the sequential two-photon absorption (TPA). For this NA mechanism, the βeff value decreases or increases depending on the input intensity. The plot of βeff with respect to input intensity presented in Fig. 7c shows this NA mechanism. A dramatic rise in βeff was observed with increasing input intensity. In PVP/V2O5–10 composite nanofibers, an electron in defect states of PVP could be excited to the conduction band of PVP by the absorption of another photon (multiphoton absorption). Considering all of these NA mechanisms, the reason of the obtained stronger NA for PVP/V2O5–10 composite nanofibers was the contribution of sequential TPA which was assisted by defect states of V2O5 nanoparticles. In our previous report [33], the NA coefficient values of the as-deposited and annealed V2O5 thin films were found in the range of 3.85 × 10–7 and 1.02 × 10–6 cm/W. The present composite nanofibers exhibit a 100 times higher NA coefficient values. It is well-known that NA behavior of the materials is very sensitive to production method, morphology, band gap value, amount and distribution of the defect states, and possible NA mechanisms. In the case of composite nanofibers, the defect levels of PVP also contributed to possible NA mechanisms. Increasing defect levels and thus NA mechanisms induced larger NA behavior in PVP/V2O5 composite nanofibers.
In order to reveal TPA coefficient values of the composite nanofibers, the OA Z-scan curves were fitted to TPA procedure introduced by Sheik-Bahae et al. [24]. The TPA coefficient is found from fitting of OA Z-scan data into Eq. (4).
where m is an integer, q0 (z) is βI0Leff, β is the TPA coefficient, and the effective thickness is \(L_{{{\text{eff}}}} = \frac{{1 - e^{{ - \alpha_{0} L}} }}{{\alpha_{0} }}\) with the sample thickness L, and αo is the linear absorption coefficient. Figure 8 indicates the OA Z-scan curves of the composite nanofibers with their theoretical fits at various input intensities. The TPA coefficient values of PVP/V2O5–8 composite nanofibers were found as 2.64 × 10–7, 0.94 × 10–7, and 0.51 × 10–7 m/W for 6.36, 12.73, and 22.57 MW/cm2 input intensities, respectively. Besides, the TPA coefficient values of PVP/V2O5–10 composite nanofibers were found as 2.93 × 10–7, 1.63 × 10–7, and 1.13 × 10–7 m/W for 6.36, 12.73, and 22.57 MW/cm2 input intensities, respectively. These results indicated that the increased V2O5 nanofiller in PVP nanofibers caused greater TPA coefficient. As compared the TPA coefficient values with NA coefficient values, it was clear seen that the absorption depends on the defect states that contribute to NA and cause stronger NA behavior in the composite nanofibers. Saravanakannan et al. reported the TPA coefficient value of the V2O5 nanoparticles in solution to be 3.19 × 10–10 m/W [32]. This result was smaller than that of our samples’ TPA coefficient values. This difference can be attributed to contribution of defects to TPA. The results of similar studies are listed in Table 3. At the same excitation condition, the NA coefficient values of the PVP/V2O5 composite nanofibers are higher than that of listed results in Table 3. Considering nanoparticles having high surface-to-volume ratio and nanofibers having high aspect ratio (length to diameter ratio), combined nanoparticles-filled nanofibers led to increased light–matter interaction, which resulted in the strengthening of NA. It is clear that these properties will be different for different morphologies, which were strongly affected by the electrospinning process and material parameters such as solution concentration, polymer density, high voltage applied, solvent, and molecular weight of the polymer. George et al. attributed the effective nonlinear absorption and optical limiting threshold to the enhanced light–matter interactions in nanofibrous morphologies [77]. Therefore, this result can be also attributed to a higher light–matter interaction in PVP/V2O5 composite nanofibers.
An ideal OL has high transparency in the open state, which allows for IR imaging, and high transparency in the limited state, which prevents damage from high-intensity light [78,79,80,81]. Stronger NA, nonlinear scattering, and nonlinear refraction features cause stronger optical limiting features of the materials under high input intensity. The optical liming curves of the composite nanofibers at 22.57 MW/cm2 input intensity are presented in Fig. 9. The obtained values are listed in Table 2. The value of optical limiting threshold (OLT) was obtained to be 2.16 × 10–5 J/cm2, and it was found to decrease to 1.49 × 10–5 J/cm2 with increasing the content of V2O5 nanofillers in polymer. This phenomenon was due to the stronger NA behavior of 10 wt% V2O5 nanoparticles-filled nanofibers when compared to 8 wt% V2O5 nanoparticles-filled ones. It is clear that the composite nanofiber mats produced in this study showed better optical limiting performance, with a lowest limiting threshold values at 532 nm compared to benchmark materials [82,83,84]. To assess the optical limiting performance of the examined nanofibers, a comparison is made with relevant studies in Table 3 from the existing literature. It is observed that the optical limiting behavior of the PVP/V2O5 composite nanofibers surpasses that of the studies listed. These findings demonstrated that the V2O5 nanofilled PVP composite nanofibers were promising for the fabrication of optical limiters for protecting vulnerable photodetectors and human eyes from hazardous pulsed laser radiation.
Conclusions
In this paper, V2O5 nanoparticles synthesized by hydrothermal method were used as nanofillers in electrospun PVP nanofibers. XRD analysis proved the purity of the synthesized V2O5 nanopowder. SEM results showed that V2O5 nanoparticles were well incorporated into the PVP nanofibers. Linear absorption results revealed two absorption bands at around 400 and 217 nm which were related with the PVP and V2O5 nanoparticles, respectively. The results also revealed that the increasing nanofiller content increased the Urbach energy from 1.63 to 1.91 eV in the composite nanofibers. The OA Z-scan experiments were performed at 532 nm to reveal the defect states effect on the NA behavior of the composite nanofibers. It was revealed that the βeff value increased from 2.99 × 10–5 to 3.58 × 10–5 m/W with the increase in V2O5 nanoparticle content at the same input intensity. The reason of this observation was ascribed to the possible occurring of NA mechanisms. In PVP/V2O5–8 composite nanofibers, the main NA mechanism was the OPA, and there was no contribution of the defect states of V2O5 nanoparticles. On the other hand, sequential TPA was the main NA mechanism in PVP/V2O5–10 composite nanofibers. In the present composite nanofibers, the defect states of the V2O5 nanoparticles, especially, induced the higher NA behavior. The lower optical limiting threshold was obtained for PVP nanofibers with the highest V2O5 nanoparticle content as 1.49 × 10–5 J/cm2. The combination of high linear transmittance at low input intensity and robust NA behavior at high input intensity renders PVP/V2O5–10 composite nanofibers as exceptionally promising candidates for optical limiters in the visible wavelength region.
Data availability
The data that support the findings of this study are available upon reasonable request from the authors.
References
Izard N, Ménard C, Riehl D, Doris E, Mioskowski C, Anglaret E (2004) Combination of carbon nanotubes and two-photon absorbers for broadband optical limiting. Chem Phys Lett 391:124–128
Wang W, Luo Y, Zhang D, Luo F (2006) Dynamic optical limiting experiments on vanadium dioxide and vanadium pentoxide thin films irradiated by a laser beam. Appl Opt 45:3378–3381
Raja S, Bheeman D, Rajamani R, Bellan C (2016) Structural and optical properties of vacuum evaporated V2O5 thin films. Optik 127:461–464
Abbasi M, Rozati S, Irani R, Beke S (2015) Synthesis and gas sensing behavior of nanostructured V2O5 thin films prepared by spray pyrolysis. Mater Sci Semicond Process 29:132–138
Panagopoulou M, Vernardou D, Koudoumas E, Katsarakis N, Tsoukalas D, Raptis YS (2017) Tunable properties of Mg-doped V2O5 thin films for energy applications: Li-ion batteries and electrochromics. J Phys Chem C 121:70–79
Jerominek H, Picard F, Vincent D (1993) Vanadium oxide films for optical switching and detection. Opt Eng 32:2092–2099
Ureña-Begara F, Crunteanu A, Raskin J-P (2017) Raman and XPS characterization of vanadium oxide thin films with temperature. Appl Surf Sci 403:717–727
Nadkarni G, Shirodkar V (1983) Experiment and theory for switching in Al/V2O5/Al devices. Thin Solid Films 105:115–129
Moshfegh A, Ignatiev A (1991) Formation and characterization of thin film vanadium oxides: Auger electron spectroscopy, X-ray photoelectron spectroscopy, X-ray diffraction, scanning electron microscopy, and optical reflectance studies. Thin Solid Films 198:251–268
Luo Z, Wu Z, Xu X, Du M, Wang T, Jiang Y (2010) Impact of substrate temperature on the microstructure, electrical and optical properties of sputtered nanoparticle V2O5 thin films. Vacuum 85:145–150
Beke S (2011) A review of the growth of V2O5 films from 1885 to 2010. Thin Solid Films 519:1761–1771
Liu Y, Jia C, Wan Z, Weng X, Xie J, Deng L (2015) Electrochemical and electrochromic properties of novel nanoporous NiO/V2O5 hybrid film. Sol Energy Mater Sol Cells 132:467–475
Kim A, Kalita G, Kim JH, Patel R (2021) Recent development in vanadium pentoxide and carbon hybrid active materials for energy storage devices. Nanomaterials 11:3213
Raj AD, Pazhanivel T, Kumar PS, Mangalaraj D, Nataraj D, Ponpandian N (2010) Self assembled V2O5 nanorods for gas sensors. Curr Appl Phys 10:531–537
Alrammouz R, Lazerges M, Pironon J, Taher IB, Randi A, Halfaya Y, Gautier S (2021) V2O5 gas sensors: a review. Sens Actuators A 332:113179
Yan Z, Shan W, Shi X, He G, Lian Z, Yu Y, Shan Y, Liu J, He H (2020) The way to enhance the thermal stability of V2O5-based catalysts for NH3-SCR. Catal Today 355:408–414
Tutel Y, Durukan MB, Koc S, Koylan S, Cakmak H, Kocak Y, Hekmat F, Ozensoy E, Ozbay E, Udum YA (2021) Multichromic vanadium pentoxide thin films through ultrasonic spray deposition. J Electrochem Soc 168:106511
Zhang Z, Xie W, Li J, Zhang H, Wang Q, Zhang C, Xu G, Gao J, Rogachev A, Cao H (2022) In situ Raman observation of dynamically structural transformation induced by electrochemical lithium intercalation and deintercalation from multi-electrochromic V2O5 thin films. Adv Mater Interfaces 9:2200883
Altowyan AS, Hakami J, Algarni H, Shkir M (2023) Enhancing the optoelectronic properties of V2O5 thin films through Tb doping for photodetector applications. J Alloys Compd 960:170911
Akl AA (2010) Thermal annealing effect on the crystallization and optical dispersion of sprayed V2O5 thin films. J Phys Chem Solids 71:223–229
Raj R, Gupta H, Purohit L (2022) Performance of V2O5 hole selective layer in CdS/CdTe heterostructure solar cell. J Alloy Compd 907:164408
Cao W, Zhang J, Lin K, Li J, Dong Y, Xia D, Fan R, Yang Y (2022) Suppressing glass-transition and lithium-ions migration in hole transport layer by V2O5 decorated graphite carbon nitride nanosheets for thermally stable perovskite solar cells. Solar RRL 6:2200310
Khdary NH, Almuarqab BT, El Enany G (2023) Nanoparticle-embedded polymers and their applications: a review. Membranes 13:537
Sheik-Bahae M, Said AA, Wei T-H, Hagan DJ, Van Stryland EW (1990) Sensitive measurement of optical nonlinearities using a single beam. IEEE J Quantum Electron 26:760–769
Banfi G, Degiorgio V, Ricard D (1998) Nonlinear optical properties of semiconductor nanocrystals. Adv Phys 47:447–510
Sandeep S, Philip R, Satheeshkumar R, Kumar V (2006) Sol–gel synthesis and nonlinear optical transmission in Zn (1–x) Mg (x) O (x ⩽ 0.2) thin films. Appl Phys Lett 89:063102
Banin U, Lee C, Guzelian A, Kadavanich A, Alivisatos A, Jaskolski W, Bryant G, Efros AL, Rosen M (1998) Size-dependent electronic level structure of InAs nanocrystal quantum dots: test of multiband effective mass theory. J Chem Phys 109:2306–2309
Bawendi M, Wilson W, Rothberg L, Carroll P, Jedju TM, Steigerwald M, Brus L (1990) Electronic structure and photoexcited-carrier dynamics in nanometer-size CdSe clusters. Phys Rev Lett 65:1623
Kavan L, Grätzel M, Gilbert S, Klemenz C, Scheel H (1996) Electrochemical and photoelectrochemical investigation of single-crystal anatase. J Am Chem Soc 118:6716–6723
Parida MR, Vijayan C, Rout CS, Sandeep CS, Philip R, Deshmukh P (2011) Room temperature ferromagnetism and optical limiting in V2O5 nanoflowers synthesized by a novel method. J Phys Chem C 115:112–117
Poonam D, Mohan S, Bhan K, Yadav M (2022) Barala, Z-scan measurements and optical limiting response of V2O5: MoO3 thin films. Braz J Phys 52:194
Saravanakannan V, Ganesh T, Babeela C, SabariGirisun T, Kalaivani T (2022) A new insight characterization analysis and two photon absorption behaviour of pure and doped vanadium oxide. Mater Sci Eng, B 284:115916
Pepe Y, Tutel Y, Yildiz EA, Karatay A, Unalan HE, Elmali A (2021) Thermally induced phase transition and defect-assisted nonlinear absorption and optical limiting in nanorod morphology V2O5 Thin Films. Adv Eng Mater 23:2100468
Anandalli MH, Bhajantri R, Maidur SR, Patil PS (2020) Fluorescence and third-order nonlinear optical properties of thermally stable CBPEA dye-doped PMMA/ZnO nanocomposites. J Mater Sci: Mater Electron 31:10531–10547
Tekin S, Karatay A, Donar YO, Bilge S, Yildiz EA, Sınağ A, Elmali A (2021) Tuning the linear and nonlinear optical absorption properties of ZnS/hydrochar nanocomposites by concentration of nanoparticles. Opt Mater 113:110849
Pepe Y, Cevik E, Tutel Y, Karatay A, Unalan HE, Elmali A (2023) Promoting the optical limiting behavior in poly (methyl methacrylate)/α-MnO2 nanocomposite films through modulation of in-gap states by metal doping. Mater Chem Phys 309:128452
Suresh B, Ramachandran S, Shanmugam G (2023) Effect of Cerium dopant on third-order nonlinear optical properties of CdS/PEG self-standing nanocomposite films. Opt Mater 135:113299
Paul S, Balasubramanian K (2021) Charge transfer induced excitons and nonlinear optical properties of ZnO/PEDOT: PSS nanocomposite films. Spectrochim Acta Part A Mol Biomol Spectrosc 245:118901
Heidari B, Salmani S, Sasani Ghamsari M, Ahmadi M, Majles-Ara MH (2020) Ag/PVP nanocomposite thin film with giant optical nonlinearity. Opt Quantum Electron 52:1–18
Pramod A, Yogeswari C, Singh AK, Girisun TS, Manattayil JK, Raghunathan V, Nagalakshmi R (2024) Nonlinear optical characterisation of electrospun Benzil-PMMA nanofibers. Opt Laser Technol 168:109898
Yogeswari C, Sabari Girisun T, Nagalakshmi R (2021) Excited-state absorption assisted optical limiting action of potassium dihydrogen phosphate (KDP)–polyethylene oxide (PEO) electrospun nanofibers. J Electron Mater 50:4619–4632
Mu J, Wang J, Hao J, Cao P, Zhao S, Zeng W, Miao B, Xu S (2015) Hydrothermal synthesis and electrochemical properties of V2O5 nanomaterials with different dimensions. Ceram Int 41:12626–12632
Zhang Y (2017) Synthesis and characterization of hollow VO microspheres for supercapacitor electrode with pseudocapacitance. Mater Sci-Pol 35:188–196
Cao P, Gui X, Navale ST, Han S, Xu W, Fang M, Liu X, Zeng Y, Liu W, Zhu D (2020) Design of flower-like V2O5 hierarchical nanostructures by hydrothermal strategy for the selective and sensitive detection of xylene. J Alloy Compd 815:152378
Sun X, Gao R, Wu Y, Zhang X, Cheng X, Gao S, Xu Y, Huo L (2023) Novel in-situ deposited V2O5 nanorods array film sensor with enhanced gas sensing performance to n-butylamine. Chem Eng J 459:141505
Silversmit G, Depla D, Poelman H, Marin GB, De Gryse R (2004) Determination of the V2p XPS binding energies for different vanadium oxidation states (V5+ to V0+). J Electron Spectrosc Relat Phenom 135:167–175
Pei G, Xiang J, Zhong D, Li G, Lv X (2021) Isothermal reduction of V2O5 powder using H2 as oxygen carrier: thermodynamic evaluation, reaction sequence, and kinetic analysis. Powder Technol 378:785–794
Jain A, Manippady SR, Tang R, Nishihara H, Sobczak K, Matejka V, Michalska M (2022) Vanadium oxide nanorods as an electrode material for solid state supercapacitor. Sci Rep 12:21024
Williamson G, Smallman R III (1956) Dislocation densities in some annealed and cold-worked metals from measurements on the X-ray debye-scherrer spectrum. Phil Mag 1:34–46
Baddour-Hadjean R, Pereira-Ramos J, Navone C, Smirnov M (2008) Raman microspectrometry study of electrochemical lithium intercalation into sputtered crystalline V2O5 thin films. Chem Mater 20:1916–1923
Strunk J, Bañares MA, Wachs IE (2017) Vibrational spectroscopy of oxide overlayers. Top Catal 60:1577–1617
Mounasamy V, Mani GK, Ponnusamy D, Tsuchiya K, Reshma P, Prasad AK, Madanagurusamy S (2020) Investigation on CH4 sensing characteristics of hierarchical V2O5 nanoflowers operated at relatively low temperature using chemiresistive approach. Anal Chim Acta 1106:148–160
Nguyen HTT, Jung D, Park C-Y, Kang DJ (2015) Synthesis of single-crystalline sodium vanadate nanowires based on chemical solution deposition method. Mater Chem Phys 165:19–24
Lazauskas A, Marcinauskas L, Andrulevicius M (2020) Modification of graphene oxide/V2O5· n H2O nanocomposite films via direct laser irradiation. ACS Appl Mater Interfaces 12:18877–18884
Vernardou D, Spanakis E, Katsarakis N, Koudoumas E (2014) Electrodeposition of V2O5 using ammonium metavanadate at room room temperature. Adv Matter Lett 5:569–572
Vernardou D, Paterakis P, Drosos H, Spanakis E, Povey I, Pemble M, Koudoumas E, Katsarakis N (2011) A study of the electrochemical performance of vanadium oxide thin films grown by atmospheric pressure chemical vapour deposition. Sol Energy Mater Sol Cells 95:2842–2847
Ramana C, Hussain O, Naidu BS, Reddy P (1997) Spectroscopic characterization of electron-beam evaporated V2O5 thin films. Thin Solid Films 305:219–226
Lee S-H, Cheong HM, Seong MJ, Liu P, Tracy CE, Mascarenhas A, Pitts JR, Deb SK (2003) Raman spectroscopic studies of amorphous vanadium oxide thin films. Solid State Ionics 165:111–116
George A, Yang Q (2023) Gas sensing performance of Tungsten doped V2O5 nanorod thin-films deposited by hot filament CVD combined with DC sputtering. Sens Actuators B Chem 394:134371
Abd-Alghafour N, Ahmed NM, Hassan Z, Almessiere MA (2018) Hydrothermal synthesis and structural properties of V2O5 nanoflowers at low temperatures. J Phys Conf Ser IOP Pub 1083:012036
Sabna M, Jayaram P (2023) Reformed dielectric features in single phase orthorhombic nickel vanadate complex oxides and the significance of the lattice dynamics in the optoelectrical features. J Phys Chem Solids 180:111428
Basu R, Prasad AK, Dhara S, Das A (2016) Role of vanadyl oxygen in understanding metallic behavior of V2O5 (001) nanorods. J Phys Chem C 120:26539–26543
Julien C, Nazri G, Bergström O (1997) Raman scattering studies of microcrystalline V6O13. Phys Status Solidi B 201:319–326
Wachs IE, Jehng J-M, Hardcastle FD (1989) The interaction of V2O5 and Nb2O5 with oxide surfaces. Solid State Ionics 32:904–910
Beattie I, Gilson T (1969) Oxide phonon spectra. J Chem Soc A Inorg Phys Theor. https://doi.org/10.1039/J19690002322
Huang S, Zhou L, Li M-C, Wu Q, Kojima Y, Zhou D (2016) Preparation and properties of electrospun poly (vinyl pyrrolidone)/cellulose nanocrystal/silver nanoparticle composite fibers. Materials 9:523
Pepe Y, Akkoyun S, Bozkurt B, Karatay A, Ates A, Elmali A (2023) Investigation of the wavelength dependent nonlinear absorption mechanisms of polyvinylpyrrolidone and cadmium selenide hybrid nanofibers. Opt Laser Technol 164:109497
Akkoyun Ş (2021) Electrospun polyvinylpyrrolidone/graphite composite nanofiber mats: effect of the filler on the morphology and wettability. Niğde Ömer Halisdemir Üniversitesi Mühendislik Bilimleri Dergisi 10:840–846
Mergen ÖB, Arda E, Kara S, Pekcan Ö (2019) Effects of GNP addition on optical properties and band gap energies of PMMA films. Polym Compos 40:1862–1869
Hussien MS, Mohammed M, Yahia I (2020) Multifunctional applications of graphene-doped PMMA nanocomposite membranes for environmental photocatalytic. J Inorg Organomet Polym Mater 30:2708–2719
Al-Ammar K, Hashim A, Husaien M (2013) Synthesis and study of optical properties of (PMMA-CrCl2) composites. Chem Mater Eng 1:85–87
Arif S, Saleemi F, Rafique MS, Naab F, Toader O, Mahmood A, Aziz U (2016) Effect of silver ion-induced disorder on morphological, chemical and optical properties of poly (methyl methacrylate). Nucl Instrum Methods Phys Res Sect B 387:86–95
Schneider K (2020) Optical properties and electronic structure of V2O5, V2O3 and VO2. J Mater Sci Mater Electron 31:10478–10488
Chan Y-L, Pung S-Y, Sreekantan S (2014) Synthesis of V2O5 nanoflakes on PET fiber as visible-light-driven photocatalysts for degradation of RhB dye. J Catal 2014:370696
Mrigal A, Addou M, El Jouad M, Khannyra S (2017) Electrochemical performance of the V2O5 and VO2 thin films synthesized by spray pyrolysis technique. J Mater Environ Sci 8:3598–3607
Yüksek M, Kürüm U, Yaglioglu HG, Elmali A, Ateş A (2010) Nonlinear and saturable absorption characteristics of amorphous InSe thin films. J Appl Phys 107:033115
Li H, Chen X, Lu W, Wang J, Xu Y, Guo Y (2021) Application of electrospinning in antibacterial field. Nanomaterials 11:1822
Gadhwal R, Kaushik P, Devi A (2023) A review on 1D photonic crystal based reflective optical limiters. Crit Rev Solid State Mater Sci 48:93–111
Shi Y, Sang P, Yin G, Gao R, Liang X, Brzozowski R, Odom T, Eswara P, Zheng Y, Li X (2020) Aggregation-induced emissive and circularly polarized homogeneous sulfono-γ-AApeptide foldamers. Advanced optical materials 8:1902122
Bugaychuk S, Iljin A, Telbiz G, Zhulai D, Leonenko E, Romanovska N, Gridyakina A, Bordyuh A, Kravchuk M, Polishchuk A (2018) Nonlinear all-optical light valves fabricated on mesoscopic Ti-, Si-substrates. J Mol Liq 267:34–37
Zhang Y, Sui N, Kang Z, Meng X, Yuan L, Li X, Zhang H-Z, Zhang J, Wang Y (2022) Scanning the optoelectronic properties of Cs4CuxAg2–2xSb2Cl12 double perovskite nanocrystals: the role of Cu2+ content. J Mater Chem C 10:5526–5533
Zhu S, Zhang Q, Pan Q, Hu J, Liu R, Song G, Zhu H (2022) High performance Pt (II) complex and its hybridized carbon quantum dots: synthesis and the synergistic enhanced optical limiting property. Appl Surf Sci 584:152567
Chen Y, Bai T, Dong N, Fan F, Zhang S, Zhuang X, Sun J, Zhang B, Zhang X, Wang J (2016) Graphene and its derivatives for laser protection. Prog Mater Sci 84:118–157
Loh KP, Zhang H, Chen WZ, Ji W (2006) Templated deposition of MoS2 nanotubules using single source precursor and studies of their optical limiting properties. J Phys Chem B 110:1235–1239
Funding
Open access funding provided by the Scientific and Technological Research Council of Türkiye (TÜBİTAK).
Author information
Authors and Affiliations
Contributions
YP and YT helped in visualization, investigation, data curation, writing—original draft, and writing—review and editing. SA and HEU participated in conceptualization, methodology, resources, and writing—review and editing. NA was involved in resources and investigation. EÇ participated in resources, data curation, and investigation. AK helped in supervision, conceptualization, methodology, and writing—review and editing. AE participated in conceptualization, methodology, and writing—review and editing.
Corresponding authors
Ethics declarations
Conflict of interest
The authors declare that they have no conflict of interest.
Ethical approval
Not applicable.
Additional information
Handling Editor: Christopher Blanford.
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Pepe, Y., Tutel, Y., Akkoyun, S. et al. Visible-light optical limiting of vanadia–polyvinylpyrrolidone nanofibers. J Mater Sci 59, 4102–4117 (2024). https://doi.org/10.1007/s10853-024-09502-x
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-024-09502-x