Abstract
With hybrid DFT calculations applied to periodic models of the bulk MoVNbTeO M1 catalyst, we examined how [TeO]2+ species in the hexagonal channels of this material stabilize nearby reduced metal centers. In particular, an S2(Mo) site, with adjacent [TeO]2+ moieties at both sides, is calculated to be reduced to Mo5+. The modeling study presented offers insight into how the redox behavior of V and Mo centers, a crucial aspect of the M1 catalyst for the selective partial oxidation of small hydrocarbons, may be fine-tuned via TeO moieties at various distances from the metal centers.
Graphic Abstract
TeO moieties in hexagonal channels, adjacent on either side of an S2(Mo) center, stabilize a gap state at the Mo center, facilitating its reduction to Mo5+.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
The catalytic production of short-chain olefins is typically carried out by energy-intensive steam cracking [1]. Moreover, with the advent of pure-ethane crackers, olefins, like propylene, formerly available as side products, become relatively less easily accessible, stimulating the development of alternatives routes for producing these olefins [2]. The MoVNbTeO catalyst stands out as an alternative for producing short olefins through oxidative dehydrogenation (ODH) of alkanes. This catalyst material is also promising in the production of acrylonitrile from propane [3, 4], avoiding propylene as used in the established process [5]. Two crystalline phases of the MoVNbTeO material have been reported to be important for the catalysis. The M1 phase is in charge of the activation of the alkane and the ODH, while the M2 phase has been assigned an auxiliary function [6,7,8]. Therefore, the M1 phase is the only one required if one simply aims at an ODH process.
Since the discovery of the MoVNbTeO mixed-metal oxide catalyst [3], significant effort was devoted in understanding this catalyst. Studies in this field range from synthesizing MoVNbTeO and its variants [9,10,11], characterizing the structure of these materials [12,13,14,15,16,17,18,19,20], elaborating the catalytic mechanism [21,22,23], to elucidating how the metal centers and V5+/V4+ pairs are distributed in the material [24,25,26,27,28]. It is well accepted that the V5+ species are responsible for activating the alkanes over this catalyst [21, 27, 29, 30], yet clarifying their location remains as one of the challenges. For an efficient catalyst design it is important to understand the factors that determine the presence and distribution of V5+ species. A higher concentration of V5+ has been determined in the vicinity of hexagonal pores with decreased TeO content in the MoVNbTeO M1 catalyst [28]. TeO moieties have also been discussed to take an active role during the catalysis [11, 17, 31].
In this letter, using a computational approach and model structures, we explore the local positions of Te centers in the hexagonal channels, and we examine how such centers affect the local lattice structure around neighboring metal centers and the electronic states of these sites.
In particular, we will address the effects of TeO moieties on sites 2 at the centers of the “pentameric units”, Fig. 1, that are nearby according to experimental evidence [14, 16]. According to our model calculations, reducing electrons in metal d-states are stabilized in the proximity of [TeO]2+ moieties. Overall, we are aiming at improving our understanding of the factors that affect the distributions of V4+/V5+ centers, thus hoping for enabling the synthesis of more active/selective catalyst materials for oxidation processes.
Given the complexity of the material at hand, we focus on understanding the effect of TeO positions in the hexagonal channels of a bulk model. This admittedly idealized situation allows us to deduce the basic effects of intercalated TeO. More complex situations, like the effect of a surface of MoVNbTeO, will be deferred to subsequent studies.
2 Models and Methods
We studied bulk models of the MoVNbTeO M1 oxide, for computational ease maintaining ideal three-dimensional periodicity. Here, we first present the considerations undertaken to build the bulk models and the nomenclature used throughout this work. We then describe the computational strategy; additional details may be found in the Electronic Supplementary Material (ESM, Online Resource 1).
The average stoichiometry of the MoVNbTeO M1 material as reported by Li et al. is Mo30V6Te3Nb4O115 [16]. However, the MoVNbTeO M1 catalyst has been successfully synthesized with a higher V content [18, 26]. TeO moieties partially occupy both heptagonal and hexagonal channels, although higher occupancies of Te have been reported in the hexagonal channels [14, 16]. We chose to model the M1 bulk by fixing the stoichiometry at Mo26V10Nb4Te4O116, with a monolayer unit cell of that composition [28].
Following our previous work [28, 32], we label inequivalent sites of MoVNbTeO as 1, 2, 3, …, 12, Fig. 1, shortened from the commonly accepted nomenclature S1, S2, S3, …, S12 [16]. The pentameric units, formed by sites 2(V), 4(V), and 7(Mo) in our models, have been discussed as active sites of the catalyst [21, 22]. We specify sites of the same type by adding a lower case letter, e.g., 3a, 3b, 3c, and 3d and we designate the various distributions of V4+ sites by a concatenated label that lists all reduced sites. For example, the label 1ab3abcd7abcd indicates that reducing electrons are located at all sites 1, 3, and 7, 10 electrons in total [28, 32]. These latter sites have been reported with the highest V occupancies for the MoVNbTeO catalyst used in experiments [14, 18] and we thus selected them as being occupied by V centers in all our models. The choice of 10 reducing electrons per unit cell, at centers V4+, entails that initially small polarons are formed primarily at V sites [14], reflecting the higher ionization potential of V4+ compared to that of Mo5+ [33].
In agreement with experimental observations [14, 17], we initially placed the Te centers, in the form of [TeO]2+ moieties, at all positions 12 in the hexagonal channels, HCs, Fig. 1. Each HC is formed by the sites 2, 3, 4, 5, 7, and 8, Fig. 1b. In consequence, the channels of the bulk models are filled by stacks along the c direction, i.e., “chains” of [TeO]2+ moieties oriented perpendicular to the ab plane.
As we probed the stability of the TeO chains at various positions within the four HCs α–δ, Fig. 1 (per unit cell), we found it necessary to identify various structure motifs. We refer to a generic configuration as [α,β][γ,δ], where the Greek characters are placeholders for the labels of the metal sites closest to the Te centers. The channel identifiers are grouped in pairs, bracketing one of the two pentameric units, Fig. 1b. We consider site n to be close to a Te center if two equatorial oxygen centers bonded to such a site form Te–O contacts shorter than 220 pm. For example, in the configuration [2,7][3,2], the TeO moieties in the pair α and β of HCs, bracketing the central pentameric unit, Fig. 1, are close to the sites 2a and 7b. The TeO moieties in the pair γ and δ of HCs, bracketing the other pentameric unit, are located close to sites 3a and 2b, respectively.
Unless otherwise stated, all reported energies were obtained from electronic structure calculations using the software CRYSTAL14 [34], applying the hybrid DFT approach B3LYP [35], supplemented by the dispersion corrections D2 [36]. This electronic structure method offers a sufficient correction of self-interaction artifacts [37, 38], otherwise typical of regular GGA DFT functionals [39], thus affording a suitable localization of electrons at reduced V and Mo complexes [40]. Integrations over the Brillouin zone were carried out with a 1 × 1 × 4 k-grid, following the scheme of Monkhorst–Pack [41]. Atomic charges were obtained from a Hirshfeld population analysis as implemented in the program CRYSTAL, with default parameters [42].
In the MoVNbTeO material, V (or Mo) centers are expected to exhibit electronic configurations d0, when oxidized, or d1, when reduced. For computational simplicity, we considered situations only where the spins of all reducing electrons are oriented parallel to each other (ferromagnetic spin orientation); low energy variations, < 8 kJ mol−1, resulted with antiferromagnetic spin orientations [32].
As in our previous studies on Mo–V mixed metal oxides [28, 32, 43], we used the all-electron split-valence basis sets 86-411d31G [44] and 8-411d1 [45] for V and O atoms, respectively. For Mo and Nb atoms, we chose the valence basis sets 311(d31)G [46] and 31(31d)G [47] in combination with Hay–Wadt small-core relativistic effective core potentials. For the Te atoms, we used a small-core relativistic effective core potential with the basis set m-pVDZ [48].
Projected densities of states were obtained with a 2 × 2 × 8 k-point mesh and the corresponding density-weighted average position of gap states was calculated as shown previously [32]. Prior to the CRYSTAL/B3LYP structure optimizations, we generated approximate structures using the plane-wave code VASP [49,50,51,52] and the PBE + U electronic structure method [53, 54], as described in the ESM (Online Resource 1) and elsewhere [28].
3 Results and Discussion
While the M1 phase of the MoVNbTeO bulk has on average symmetry Pba2, as determined by XRD Rietveld refinements [16]. Probing various TeO placements within the HCs may break the symmetry of the unit cell, entailing degenerate structures. Reducing the symmetry of the unit cell from Pba2 to Pc, for instance, leads to two degenerate structures related by one of the glide mirrors. In the present work, we only calculated those structures that are symmetry-inequivalent.
3.1 Locations of TeO Moieties and Their Influence on Neighboring Sites
Next, we will assess the effects of the TeO location within the HCs. First, we explore how the structure and the stability of the system varies with the position of the TeO moieties within the HCs. Then we examine the influence of these TeO moieties on the reducibility of neighboring metal sites.
With the HCs, we determined stable locations for the TeO moieties near the sites 2(Mo), 3(V), and 7(V), Fig. 2 and Table 1. These sites occur in the structure combinations [2,2], [2,3], [2,7], and [7,7] in pairs of HCs bracketing a single pentameric unit, Fig. 2. Framework views of configurations included in Table 1 are shown in Fig. S1 (Online Resource 1). We probed also other locations for the TeO moieties, e.g., near 4(Mo), 5(Mo), or 8(Mo), but these locations were either substantially less stable or, during optimization, the TeO moieties returned to locations already known. TeO moieties have been reported to prefer sitting near V (rather than Mo) octahedra in the HCs of the M2 phase of MoVNbTeO [55]; it was suggested that the displacement of Te towards V is associated with the stronger repulsion between Te and Mo centers, due to their higher charges. Note that these charges are formal only. A Hirshfeld population analysis [42] of the structure [2,2][2,2] revealed that typical charges for V5+, V4+, Mo6+, Mo5+, and Te4+ are 2.32 e, 2.18 e, 2.37 e, 2.20 e, and 2.33 e, respectively. These charges are much lower than the various formal oxidation states. The formally highest oxidation state of the three elements Mo, V, and Te are rather similar in charge, and so are the reduced states, which are roughly 0.15 e lower in charge. This difference may be a driving force to reduce interactions when two metal centers are nearby, leading to a lower Coulomb repulsion due to the reduction of the oxidation state. This aspect should be kept in mind when we will be invoking Coulomb interactions in the following.
In agreement with a previous study [28], two TeO moieties bracketing site 2(Mo), [2,2], render this Mo center reduced, at the expense of the centers 1(V), Table 1. In all other placements of TeO moiety studied, the V4+ centers remain as originally selected (see above), i.e., the polaron distribution 1ab3abcd7abcd is maintained.
All energies in Table 1 are with respect to the symmetric configuration, [2,2][2,2] with the alternate polaron distribution 2ab3abcd7abcd. We note, however, that this is not the most stable polaron distribution in which two TeO moieties bracket 2(Mo) centers, which was assessed elsewhere [28].
Inspecting Table 1, we deduce the stability trend [2,2] > [2,3], [3,2] > [2,7], [7,2] > [7,7] among the various TeO placements studied. The symmetric structure [7,7][7,7], with all TeO moieties placed next to the reduced centers 7(V), was determined as the least stable one, 66 kJ mol−1 higher in energy than the configuration [2,2][2,2]. The configurations [7,2][7,2] and [2,7][7,2], 8 kJ mol−1 more stable than [7,7][7,7], have one TeO moiety near a 7(V) center while maintaining the TeO moiety in the neighboring HC at the center 2(Mo). Placing one or two of the TeO moieties across the pentameric unit next to a site 3(V), producing configurations [2,7][3,2] and [2,3][3,2], increases the stability of the unit cell by 13 kJ mol−1 and 26 kJ mol−1, respectively, relative to [7,7][7,7].
To quantify how varying the TeO location affects the local structure of the 2(Mo) centers, we introduce the parameter δ2(n–2–n’) which measures the (absolute) difference between trans located equatorial 2(Mo)–O bonds, Table 2. In a general manner, n and n’ refer to sites 4 or 7, neighboring the oxygen atoms of these trans located bonds. When appropriate, we use both specific site labels, e.g. δ2(7a–2a–7b), indicating 7a(V) and 7b(V) as metal neighbors of the 2a(Mo)–O bonds. For reduced 2(Mo) centers, [2,2][2,2], the values δ2(4–2–4) and δ2(7–2–7) are all zero, indicating a symmetric octahedron with 2(Mo) located at the intersection of the two diagonals, Table 2.
Such a symmetric environment of a metal center in an oxide normally is taken to indicate a d1 metal center [16, 56]. In contrast, if the central metal moiety is located away from the intersection of the two diagonals, then one invokes the pseudo Jahn–Teller concept and infers an oxidized 2(Mo) center as a consequence of the metal d0 configuration [57]. The latter case is associated with larger values of δ2, in the range of 22–30 pm for one or both of the 4–2–4 or 7–2–7 diagonals, Table 2. In configuration [7,7][7,7], the local structures, as indicated by δ2 = 0 pm in all four distinct n–2–n’ diagonals, are at variance with the pseudo Jahn–Teller concept [57], given that both metal centers 2a(Mo) and 2b(Mo) are oxidized. This computational result might be a consequence of the symmetrically located TeO moieties across the pentameric unit.
Configurations [7,2][7,2] and [2,7][7,2] feature oxidized 2(Mo) centers with an asymmetric environment, in agreement with the pseudo Jahn–Teller concept [57], with δ2(4–2–4) = 23–25 pm and δ2(7–2–7) = 3–6 pm. While the 2(Mo) center is displaced towards one of the 4(Mo) on the diagonal 4–2–4, it remains close to the center of the diagonal 7–2–7. The direction of the distortion for d0 metal centers may be due to an effective repulsion between metal ions, as previously postulated [58]. The distortion of 2(Mo) directed towards one of the vertexes of the diagonal 4–2–4 is likely due to the proximity of the centers Te and 2(Mo). When the TeO moiety is located next to 2(Mo), the center 2(Mo) shifts towards the opposite edge of the octahedron, Fig. 2b. For TeO located next to 7(V), the 2(Mo) moiety is displaced towards the site 4(Mo) across the HC, Fig. 2c.
The centers 2(Mo) show strong off-center displacements in the configurations [2,3] and [3,2]. Sites 2a or 2b of [2,3][3,2] and site 2b of [2,7][2,3] feature values of δ2(4–2–4) and δ2(7–2–7) of 25–29 pm, Table 2. These 2(Mo) centers are displaced towards the HC in which the TeO is located near 3(V), Fig. 2b. Especially those equatorial 2(Mo)–O bonds are elongated where the oxygen atoms are interacting with the TeO moiety while the other 2(Mo)–O bonds are shortened, Figure S2 (Online Resource 1). Again, it appears as if an effective repulsion is at work between the Te and Mo metal ions, inducing a lattice distortion around these 2(Mo) centers. Indeed, the deviations of 2(Mo) from its central position were previously discussed as a cation–cation repulsion between site 2 and Te [59]. The asymmetric lattice distortion around site 2a(Mo) in the configuration [2,7][2,3] along one diagonal, δ2(4a–2a–4b) = 29 pm and δ2(7a–2a–7b) = 2 pm, may be rationalized in the same way as discussed above for the configurations [7,2][7,2] and [2,7][7,2].
For the material MoVOx, it was previously analyzed how the peak energies of the gap states (due to centers V4+) in the atom-projected density of states (pDOS) vary with the type of the reduced center, i.e., 1(V), 3(V), or 7(V), as well as with the number of polaron–polaron interactions [32]. The latter aspect had been inferred as consequence of lattice distortions where a MoO6 moiety is bracketed between immediately adjacent centers V4+, due the larger ionic radius of these species in comparison with V5+. We analyzed the effect of these polaron–polaron interactions on the stability of MoVNbTeO elsewhere [28].
For the MoVNbTeO material we determined that the density-weighted average energy, ε(n), of the gap states of reduced sites n is affected by the presence of the TeO moieties. In fact, ε(n) shifts by 0.3–0.4 eV to a lower energy if a TeO moiety is nearby, Table S1 (Online Resource 1). For instance, polarons with adjacent TeO moieties, 7a(V) and 7c(V) in configuration [7,2][7,2] as well as 7b(V) and 7c(V) in configuration [2,7][7,2], Fig. 1, exhibit gap states that are about 0.3–0.4 eV lower than the gap states of other polarons at 7(V) centers, Table S1 (Online Resource 1). Similar effects may be observed for the polaron 3a(V) in the configuration [2,7][3,2] as well as the polarons 3a(V) and 3d(V) in the configuration [2,3][3,2]. Polaron-induced gaps states at lower energies in the pDOS may be interpreted to indicate a more facile reduction of those V centers that have a [TeO]2+ moiety nearby.
3.2 Effect of the TeO Position on the Reducibility of Metal Centers
Thus far, we discussed how a TeO moiety enhances the reducibility of V centers in their vicinity. Even more drastic is the concerted effect of two adjacent TeO moieties on a 2(Mo) center in the configuration [2,2][2,2] which results in a reduction of the site 2(Mo) at the center of the pentameric unit. In fact, this configuration has the lowest energy among the configurations studied here, Table 1.
In the following, we explore whether and how shifting the TeO moieties within the hexagonal channels affects the oxidation state of the metal centers that form these channels. Such effects, including a relocation of the polarons there, could be due to the charge of TeO or a change in the bonding of equatorial oxygen centers of 2(Mo). Recall that, following the pseudo Jahn–Teller concept [57], reduced metal centers entail a more symmetric local environment in comparison to the analogous oxidized centers. We examined this question by carrying out two computer experiments where we shifted a TeO moiety in a step-wise fashion in the (001) within the HC, first admitting a local relaxation of centers other than TeO and subsequently fixing the geometry of all centers.
3.2.1 Scanning TeO Positions on a 2-Dimensional Grid with Partial Structure Relaxation
The hexagonal channel (HC) δ is formed by the sites 2b(Mo), 3b(V), 4c(Mo), 5b(Mo), 7d(V), and 8d(Mo), Fig. 3. For varying the positions of the TeO moiety inside the HC δ, we used a 2-dimensional grid in the (001) plane defined by the Te center in the configuration [2,2][2,2]. The grid, with a step size of 20 pm, comprised only points in the HC where the distance between the Te atom and any of the equatorial oxygen atoms is at least 180 pm. On this grid, the TeO moiety was shifted as rigid structure from its initial position. In addition, we fixed the coordinates of the two Nb centers at sites 9a and 9b, Fig. 1a, which reside farthest in the unit cell from the HC in question; this prevents a possible translation of the whole unit cell with respect to TeO. All other atoms were allowed to relax. We assessed the electronic configuration, d0 or d1, of the metal centers forming the HC by inspecting their spin densities ρ.
The reduced state, d1, of the site 2b(Mo) was maintained for more than half of the TeO grid positions, cf. black dots in Fig. 3. When the TeO moiety is close to 5b(Mo) or 8d(Mo), at ~ 370 pm from 2b(Mo), the reducing electron is shifted to one of these latter sites, Fig. 3. The electronic configuration of sites 3b(V), 4c(Mo), and 7d(V) remained unchanged for all TeO positions probed. Apparently, electrostatic interactions trigger the reduction of metal sites in the wall of the HC, at distances beyond direct bonds between a TeO moiety and an octahedron 2b(Mo). These conclusions agree with TEM results where (in the related M2 material) Te was preferentially found close to cations of smaller charge; this result was interpreted as a minimization of the cation–cation repulsion [55].
Relocating the reducing electron originating from 2b(Mo) produces a “ridge” in the potential energy surface of at least 80 kJ mol−1 above the energy minimum, Fig. S3 (Online Resource 1). The local potential energy wells near 5b(Mo) and 8d(Mo) are estimated to lie ~ 35 kJ mol−1 relative to the initial configuration [2,2][2,2], Fig. S3 (Online Resource 1). At these latter TeO locations, the polaron initially at 2b(Mo), is relocated either to 5b(Mo) or 8d(Mo), depending on the proximity of TeO, Fig. 3. As the TeO moiety was fixed at the grid points, we consider the energies shown in Fig. S3 as upper bounds of such configurations.
The configurations with the TeO moiety located close to 5b(Mo) or 8d(Mo) and the reducing electron relocated respectively, at relative energies of ~ 35 kJ mol−1 with respect to the stable conformer [2,2][2,2], may be interpreted to approximate the TeO configurations [2,5] or [2,8]. Because here we inspect only a single pentameric unit in contrast to the discussion above, we may compare these relative energies to values about half of those reported in Table 1. For example, configuration [2,3][3,2] is 40 kJ mol−1 above the Ref. [2,2][2,2], Table 1, or about 20 kJ mol−1 per TeO moiety displaced towards sites 3(V). These results suggest that the variations [7,2][7,2], [2,7][7,2], [2,7][3,2], or [2,3][3,2] are thermodynamically more accessible, with relative energies from 20 mol−1 to 33 kJ mol−1, than configurations involving the TeO configurations [2,5] or [2,8] just discussed.
The displacement of the TeO moiety causing a relocation of the polaron from 2b(Mo) to either 5b(Mo) or 8d(Mo) emphasizes that the proximity of TeO to a metal center may trigger a reduction of the latter.
3.2.2 Atomic Charges and Spin Densities When the TeO Position Varies in the Hexagonal Channel
We have just seen that the reducing electron at 2b(Mo) is relocated to other Mo sites of the HC δ when the stabilizing effect of the TeO moiety is reduced at larger distances Te–Mo. To probe details of the associated charge transfer, we resorted to a slightly more approximate model, where the TeO moiety is displaced in a rigid fashion along a linear path in the (001) plane, from its stable position near 2b(Mo) in the configuration [2,2][2,2] to a position near center 3b(V) while keeping the location of all other centers fixed, Fig. 4. We chose this linear scan to limit the computational effort.
According to this model, the reducing electron is maintained at the site 2b(Mo) (spin density ρ > 0.7 e) for TeO positions up to 90 pm away from that starting location, Fig. 4b. Beyond that distance, the spin density drops to ρ = 0.25 e, while the spin density at the center 8d(Mo) increases to ρ = 0.7 e, indicating a concomitant shift of the reducing electron. Center 3b with V4+ is unable to host yet another reducing electron.
During that scan, the Hirshfeld charges q of the metal centers Te, 2b(Mo), and 8d(Mo) exhibit trends concomitant to those of the spin densities ρ, Fig. 4c. When the TeO moiety is moved 120 pm from its initial position, the charge of 2b(Mo) increases by 0.10 e while the charge of 8d(Mo) decreases by 0.14 e, reflecting the transfer of the reducing electron. In the final position examined, the charge of 8d(Mo), 2.24 e, is lower than the charge of 2b(Mo), 2.30 e. Such a decreased charge at 8d(Mo) will lower the Te-8d(Mo) electrostatic interaction. Interestingly, the calculated charge of Te also changed quite remarkably. Starting from 2.33 e it reaches a minimum of 2.20 e at the distance Te-2b(Mo) = 380 pm; thus, in that configuration the atomic charge of this Te species is quite similar to that of Mo5+ or V4+. This may be interpreted as a (partial) reduction of Te due to the missing equatorial oxygen centers, that are now outside the local environment of Te. It has been hypothesized [17, 31] that the loss of axial oxygen from the TeO moieties within the HC, thus producing a reduced Te2+, causes a shortening of the Te-2 distance. By the same token, we expect a stronger interaction of partially reduced Te with its axial oxygen centers while increasing the equatorial Te–O distances.
Next, we inspect the energies of the gap states along the scan line, Table S2 (Online Resource 1). The values ε(2b) and ε(7d) of the gap states are shifted to higher energies as Te is displaced towards 3b(V) across the HC. In contrast, ε(3b) shifts to lower energies when Te approaches 3b(V). Only when Te is at 443 pm from 2b(Mo), or at 298 pm from 8d(Mo), a peak with d state character appears for 8d(Mo) at − 0.44 eV; its energy nearly matches that of the peak for the gap d state at 2b(Mo), − 0.51 eV, Table S2 (Online Resource 1), as is to be expected for an electron transfer [60].
The symmetric and distorted local environments of the centers 2b(Mo) and 8d(Mo) were maintained during the model calculations just discussed. Thus, their equatorial Mo–O bonds remained at their initial values, in the ranges 198–202 pm (Mo5+) and 178–208 pm (Mo6+), respectively. Thus, changes in the local metal environments are not required for changing the charge transfer between the sites 2b(Mo) and 8d(Mo) [or 5b(Mo)]. This result clearly points to a Coulomb effect of the TeO moiety, to induce the electron transfer. Our rather simple model, naively assuming all other factors to remain constant, entails a change in energy by ~ 100 kJ mol−1 as the charge q(2b) changes from 2.30 e to 2.20 e at the 2b(Mo) center 320 pm apart from Te with a charge of 2.33 e. Our model yields only a crude estimate, neglecting screening of charges as well as other interactions. Nevertheless, it provides a hint on the approximate size of this energy, despite the small change in the charge q(2b).
The redistribution of the reducing electron as consequence of relocating the TeO moiety in the hexagonal channels is especially important, given the recent experimental evidence for the irregular positioning of Te columns within the hexagonal channels [59]. As described above, the reducibility of the metal centers, i.e., their ability to form a small polaron, increases with the proximity to a TeO moiety. This may be rationalized as a stabilization due to a lowered M–[TeO] electrostatic repulsion (M = V, Mo), when the charge of M is somewhat reduced, when M carries a polaron.
4 Conclusions
We studied computationally how TeO moieties in the hexagonal channels (HCs) of the MoVNbTeO bulk material affect nearby transition metal sites, in particular in the pentameric unit. By populating sites 1, 3, and 7 with V ions and exploring various TeO placements within the HCs, we examined how these TeO moieties affect the local structure of 2(Mo) centers and induce alternative distributions of reduced metal centers.
-
Various stable positions of TeO moieties within the hexagonal channels (HCs) near the sites 2(Mo), 3(V), and 7(V) were determined to be energetically accessible by 20–33 kJ mol−1 uphill, translating to 40–66 kJ mol−1 uphill for both pentameric units per unit cell. These energy ranges characterize the manifold of stable positions of TeO within a channel, recently examined experimentally [59].
-
Especially noteworthy is the unique result of our model calculations that site 2(Mo) at the center of the active site (pentameric unit) is reduced when symmetrically bracketed between adjacent TeO moieties. One each in the neighboring HCs. Any deviation from this special configuration TeO–2(Mo)–TeO induces the oxidation of Mo at site 2. This result adds a crucial detail about the condition to finding a reduced center, Mo5+, sometimes identified at site 2(Mo) [14, 16, 61].
Displacing a [TeO]2+ moiety in a HC may relocate the reducing electrons to another metal center in the wall of the HC, to either 5(Mo) or 8(Mo). Yet, such alternative configurations are unfavorable by ~ 35 kJ mol−1 per TeO displaced, in comparison to the symmetric arrangement where both TeO moieties are closely bracketing the 2(Mo) site of a pentameric unit.
-
Previously we determined [28] that the likelihood of finding V5+ species at the sites in the wall of a HC increases if the channel holds a TeO defect. This is also important from a practical side, as decreasing the Te content leads to improved catalysts [11]. Our model study suggested that displacing the TeO moiety towards site 3, away from 2(Mo), has a similar effect on 2(Mo) than a TeO defect [28]. In both cases, 2(Mo) is oxidized and its local oxygen environment will be distorted, in agreement with the pseudo Jahn–Teller concept [57]. The propensity of Mo centers to be reduced, and thus to form “small polarons” [62], also increases near a TeO moiety. This points to a decisive role of TeO moieties at suitable positions, namely to control the ability to reduce site 2(Mo) at the center of the pentameric unit, discussed as active site [4, 21]. Facilitating the mobility of TeO moieties will therefore directly impact the oxidation state of centers in the HC. The combined occurrence of V4+ and V5+ within a pentameric unit has been discussed as crucial for an efficient oxidation catalyst [8, 21, 26], hence highlighting the importance of tuning the distribution of reducing sites via locating TeO moieties at suitable distances or even the creation of TeO defects.
Code Availability
The computer codes applied are commercially available.
References
Ren T, Patel M, Blok K (2006) Energy 31:425–451
Amghizar I, Vandewalle LA, Van Geem KM, Marin GB (2017) Engineering 3:171–178
Hatano M, Kayo A (1991) Catalytic conversion of alkanes to nitriles, and a catalyst therefor, U.S. Patent 5049692
Grasselli RK, Burrington JD, Buttrey DJ, Desanto P, Lugmair CG, Volpe AF, Weingand T (2003) Top Catal 23:5–22
Grasselli RK (1999) Catal Today 49:141–153
Holmberg J, Grasselli RK, Andersson A (2004) Appl Catal A 270:121–134
Holmberg J, Hansen S, Grasselli RK, Andersson A (2006) Top Catal 38:17–29
Grasselli RK (2014) Catal Today 238:10–27
Celaya Sanfiz A, Hansen TW, Girgsdies F, Timpe O, Rödel E, Ressler T, Trunschke A, Schlögl R (2008) Top Catal 50:19–32
Sadakane M, Yamagata K, Kodato K, Endo K, Toriumi K, Ozawa Y, Ozeki T, Nagai T, Matsui Y, Sakaguchi N, Pyrz WD, Buttrey DJ, Blom DA, Vogt T, Ueda W (2009) Angew Chem Int Ed 48:3782–3786
Melzer D, Mestl G, Wanninger K, Zhu Y, Browning ND, Sanchez-Sanchez M, Lercher JA (2019) Nat Commun 10:4012
DeSanto P, Buttrey DJ, Grasselli RK, Lugmair CG, Volpe AF, Toby BH, Vogt T (2004) Z Kristallogr Cryst Mater 219:152–165
Wagner JB, Timpe O, Hamid FA, Trunschke A, Wild U, Su DS, Widi RK, Hamid SBA, Schlögl R (2006) Top Catal 38:51–58
Murayama H, Vitry D, Ueda W, Fuchs G, Anne M, Dubois JL (2007) Appl Catal A 318:137–142
Pyrz WD, Blom DA, Vogt T, Buttrey DJ (2008) Angew Chem Int Ed 47:2788–2791
Li X, Buttrey DJ, Blom DA, Vogt T (2011) Top Catal 54:614–626
Aouine M, Epicier T (2016) Millet J-MM. ACS Catal 6:4775–4781
Epicier T, Aouine M, Nguyen TT (2017) Millet J-MM. ChemCatChem 9:3526–3533
Lwin S, Diao W, Baroi C, Gaffney A, Fushimi R (2017) Catalysts 7:109
Trunschke A, Noack J, Trojanov S, Girgsdies F, Lunkenbein T, Pfeifer V, Hävecker M, Kube P, Sprung C, Rosowski F, Schlögl R (2017) ACS Catal 7:3061–3071
Grasselli RK, Lugmair CG, Volpe AF (2011) Top Catal 54:595–604
Naumann d’Alnoncourt R, Csepei L-I, Hävecker M, Girgsdies F, Schuster ME, Schlögl R, Trunschke A (2014) J Catal 311:369–385
Cheng M-J, Goddard WA (2016) Top Catal 59:1506–1517
Naraschewski FN, Jentys A, Lercher JA (2011) Top Catal 54:639–649
Fu G, Xu X, Sautet P (2012) Angew Chem Int Ed 51:12854–12858
Nguyen TT, Deniau B, Delichere P (2014) Millet J-MM. Top Catal 57:1152–1162
Grasselli RK, Volpe AF (2014) Top Catal 57:1124–1137
Arce-Ramos JM, Genest A, Rösch N (2020) J Phys Chem C 124:18628–18638
Hävecker M, Wrabetz S, Kröhnert J, Csepei L-I, Naumann d’Alnoncourt R et al (2012) J Catal 285:48–60
Chen X, Dang D, An H, Chu B, Cheng Y (2019) J Taiwan Inst Chem E 95:103–111
Zhu Y, Sushko PV, Melzer D, Jensen E, Kovarik L, Ophus C, Sanchez-Sanchez M, Lercher JA, Browning ND (2017) J Am Chem Soc 139:12342–12345
Li W, Fjermestad T, Genest A, Rösch N (2018) Cat Sci Technol 8:2654–2660
Lide DR, in: Handbook of Chemistry and Physics, eds. Lide DR (CRC Press LLC, Boca Raton, Florida, 2003), ch. 10
Dovesi R, Orlando R, Erba A, Zicovich-Wilson CM, Civalleri B, Casassa S, Maschio L, Ferrabone M, De La Pierre M, D’Arco P, Noël Y, Causà M, Rérat M, Kirtman B (2014) Int J Quantum Chem 114:1287–1317
Becke AD (1993) J Chem Phys 98:5648–5652
Grimme S (2006) J Comput Chem 27:1787–1799
Dinda S (2017) Chiu C-c, Genest A, Rösch N. Comput Theor Chem 1101:36–45
Rugg G, Genest A, Rösch N (2018) J Phys Chem A 122:7042–7050
Hu Z, Metiu H (2011) J Phys Chem C 115:5841–5845
Chiu C-C, Vogt T, Zhao L, Genest A, Rösch N (2015) Dalton Trans 44:13778–13795
Monkhorst HJ, Pack JD (1976) Phys Rev B 13:5188–5192
Hirshfeld FL (1977) Theor Chim Acta 44:129–138
Li W-Q, Fjermestad T, Genest A, Rösch N (2019) Cat Sci Technol 9:1559–1569
Ruiz E, Llunell M, Alemany P (2003) J Solid State Chem 176:400–411
Bredow T, Jug K, Evarestov RA (2006) Phys Status Solidi B 243:R10–R12
Hay PJ, Wadt WR (1985) J Chem Phys 82:270–283
DallOlio S, Dovesi R, Resta R (1997) Phys Rev B 56:10105–10114
Heyd J, Peralta JE, Scuseria GE, Martin RL (2005) J Chem Phys 123:174101
Kresse G, Hafner J (1993) Phys Rev B 47:558–561
Kresse G, Hafner J (1994) Phys Rev B 49:14251–14269
Kresse G, Furthmüller J (1996) Comput Mater Sci 6:15–50
Kresse G, Furthmüller J (1996) Phys Rev B 54:11169–11186
Perdew JP, Burke K, Ernzerhof M (1996) Phys Rev Lett 77:3865–3868
Dudarev SL, Botton GA, Savrasov SY, Humphreys CJ, Sutton AP (1998) Phys Rev B 57:1505–1509
Buttrey DJ, Blom DA, Vogt T, in: Complex Oxides, An Introduction, eds. Vogt T, Buttrey DJ (World Scientific, Singapore, 2019), ch. 6:157-198
Lunkenbein T, Girgsdies F, Wernbacher A, Noack J, Auffermann G, Yasuhara A, Klein-Hoffmann A, Ueda W, Eichelbaum M, Trunschke A, Schlögl R, Willinger MG (2015) Angew Chem Int Ed 54:6828–6831
Bersuker IB (2013) Chem Rev 113:1351–1390
Kunz M, Brown ID (1995) J Solid State Chem 115:395–406
Lunkenbein T, Masliuk L, Plodinec M, Algara-Siller G, Jung S, Jastak M, Kube P, Trunschke A, Schlögl R (2020) Nanoscale 12:6759–6766
Atkins PW, De Paula J, in: Atkins’ Physical Chemistry (10th ed.), (Oxford University Press, Oxford, New York, 2014), ch. 21
Govindasamy A, Muthukumar K, Yu J, Xu Y, Guliants VV (2010) J Phys Chem C 114:4544–4549
Shluger AL, Stoneham AM (1993) J Phys 5:3049–3086
Melzer D, Xu P, Hartmann D, Zhu Y, Browning ND, Sanchez-Sanchez M, Lercher JA (2016) Angew Chem Int Ed 55:8873–8877
Funding
Open Access funding provided by TU Wien (TUW). This work was supported by Grant No. 1527700033 of the A*STAR Science and Engineering Research Council. The computational work profited enormously from a generous allotment of resources provided by the A*STAR Computational Resources Center and the National Supercomputing Centre Singapore.
Author information
Authors and Affiliations
Contributions
JMA-R: Carried out calculations and the initial analysis, wrote the initial draft, carried out the illustrations. GR: Carried out calculations and contributed to the analysis. AG: Supervised the study and the analysis, revised the manuscript. NR: Designed the project, supervised the study and the analysis, and revised the manuscript.
Corresponding authors
Ethics declarations
Conflict of interest
The authors declare that they have no conflict of interest.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Below is the link to the electronic supplementary material.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Arce-Ramos, J.M., Rugg, G., Genest, A. et al. Probing the Positions of TeO Moieties in the Channels of the MoVNbTeO M1 Catalyst: A Density Functional Theory Model Study. Catal Lett 151, 2884–2893 (2021). https://doi.org/10.1007/s10562-021-03538-3
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10562-021-03538-3