Abstract
Natural muscle provides excellent motilities for animals. As the basic unit of the muscle system, the skeletal muscle fibers function as a soft linear actuator. Inspired by the muscle fibers, researchers have developed various soft active devices with linear actuation. This paper reviews several soft linear actuators, such as the dielectric elastomer, thermal responsive hydrogels, pneumatic artificial muscle, and conducting polymers. The actuation mechanisms and performances of these soft linear actuators are summarized. Based on the dielectric elastomer, we propose a design of a hybrid system with linear actuation, driven by both the electric motor and dielectric elastomer cone. The electromechanical behaviors of the dielectric elastomer cone have been investigated in both experiment and finite element analysis. This work may guide the further design of soft actuators and robots.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
1 Introduction
With the continuous development of control science, material science, and biomedicine, human’s demands for robotics and rehabilitation medical technology have been continuously growing. Robots have been widely used in the application of complex terrain environment and engineering facilities. Traditional actuating devices for robots are usually made up of hard components such as motors and hinges, which cannot adapt to complex terrain well. Some domains like rehabilitation medicine require more friendly interaction with actuators, but hard actuators are incapable of well cooperating with human muscles and skins. Some discoveries in the material provide a new way.
The development of soft artificial muscle has attracted more and more attention. Artificial muscle has the characteristics of linear actuation, large deformation, and high efficiency. It can be widely used in many fields such as robot actuators, rehabilitation training, and aerospace. In recent years, the development of smart materials has played an important role in the manufacture of artificial muscle. Smart materials refer to a kind of materials that produce functional response under external stimuli such as electricity, heat, and catalyst. As the most important function of muscle, they produce deformation and force directly or indirectly. Compared with the traditional hard actuators, soft actuators with smart materials achieve continuous deformation, high degrees of freedom, high driving efficiency, and environmental adaptability. In this paper, Sect. 2 introduces the development of smart materials for linear actuators under different excitations in recent years. Section 3 describes the system design and mechanical investigation of the hybrid linear actuator. Experimental measurement and finite element analysis have been carried out on the inhomogeneously deformed DE membranes in the hybrid actuator.
2 Artificial Muscles with Various Mechanisms
2.1 Dielectric Elastomer Linear Actuators
The dielectric elastomer (DE) actuator has become one of the most common electro-active soft actuators because of its large voltage-induced deformation, high energy density, fast response, and low cost. Its typical structure includes a hyper-elastic membrane with high dielectric constant and flexible electrodes covered on both sides of the dielectric elastomer membrane. When the driving voltage is applied through the thickness direction, the dielectric elastomer membrane will deform under the action of Maxwell force, resulting in the reduction of thickness and the expansion of the area.
Linear DE actuators have been developed for over 20 years [1, 2]. Due to the material properties of the DE membrane, the output force of extension is not practical. To better fit the nature muscle and make it more practical, researchers generally combined the DE membrane with an elastic framework to form an antagonistic system. This system could achieve the function of electrified contraction like the nature muscle. The early linear DE actuator consisted of a spring and the DE membrane. Typically, a pre-stretched DE membrane was attached to the outside of the compressed spring to maintain the pre-stretch. In this design, the linear DE actuator would elongate when voltage was applied and contract when not [3,4,5]. Particularly, Kovacs et al. [6] fabricated an arm wrestling robot with over 240 DE actuators with springs inside and figured the experimental relationship between the number of layers and the output force. Another typical linear DE actuator is the core-free DE actuator. Without any springs inside, Tryson et al. [7] extended the orientated and corrugated metal electrode covered with DE membrane in a particular direction. Lau et al. [8] replaced the inner spring with a lightweight outer structure and increased the actuating frequency up to 10 Hz. However, due to the sliding between the two rolled DE membranes, the deformation is not inhomogeneous. The inhomogeneous deformation is one of the main causes of actuating instability. Teh et al. [9] developed a cylindrical actuator, which significantly enlarged the electrically induced linear strains to 200%. Lu et al. [10] conducted the theoretical analysis of cylindrical actuator and found out how the height-to-radius ratio of the tube and loading conditions affected the actuation. There also existed some cone-like (loudspeaker-type) linear DE actuators [11,12,13] which could generate a large deformation out of the membrane plane when actuating and stay in the plane without actuating. All the above studies utilized the extension of the area of DE to fabricate actuators, the working principle of which, however, is opposite to that of nature muscles. During its actuation, the DE structure relaxes rather than contracts. To overcome this defect, some linear actuators with the feature of electrically induced contraction came up. Kovacs et al. [14] reduced the thickness of DE and stacked multiple DE layers to make an electrically contracted DE actuator. Acome et al. [15] made a self-healing electrostatic actuator by added filling liquid into the stacked structure to avoid the failure of actuator due to electric breakdown. As for microscale actuation, inspired by the McKibben’s muscle, Lee et al. [16] made a DE membrane with braided fiber on both sides of a braided fiber sleeve with a specific bias angle. Some of the linear DE actuators are shown in Fig. 1.
Some studies focused on modeling the electromechanical behavior [17,18,19,20,21,22] and electromechanical stability [23,24,25]. Despite the advantages of dielectric elastomer, there are still some challenges. A flexible and stretchable electrode which can strongly adhere to the DE membrane is necessary for avoiding inhomogeneous deformation. And better material with higher dielectric constant, breakdown voltage and tension stiffening effect is critical for improving the mechanical properties of DE [26, 27].
2.2 Thermoresponsive Linear Actuators
Thermoresponsive linear actuators are mainly divided into two types: thermal deformation and thermal response. For the former, heating always results in phase transition or thermal stress, leading to a deformation. For the latter, heating means a chemical change whose effect would depend on the environment.
A famous study conducted by Haines et al. [28] showed that when an extremely twisted nylon fiber coiling around a mandrel with the same chirality was heated, it would tend to untwist and contract along the mandrel direction by up to 49%. It could also support an incredible tension force. Further study included painting it with twisted silver for efficient heating [29] and building a control system [30]. The similar linear actuator was made up of shape memory alloys (SMAs). After shaping the SMA at high temperature, to whatever it deformed at the cooling state, the material could completely restore to its pre-deformed shape when being heated to the martensite transformation temperature. Koh et al. [31] made an SMA spring actuator and designed a crawling robot. Mosley et al. [32] designed an SMA actuator with a bundle of wires, which could generate a force of 450 N. Laurentis et al. [33] analyzed the influences of the number and diameter of SMA wires. Andrianesis et al. [34] made a robot hand system with the SMA wires. Some recent studies focused on increasing the actuation frequency by using a diamond structure [35] and the application in minimally invasive surgeries (MIS) [36].
The shape memory polymer (SMP) is another important type of smart material. The SMP can respond to various stimuli, such as electric field, pH, light, magnetic field, sonic field, solvent, ions, and so on. To recover from its temporary shape, the conventional SMP usually depends on a reversible phase and a stable polymer network. The most typical SMP is the one triggered by temperature. The thermally reversible phase fixes the temporary shape when cooled to a temperature below \({T}_{\mathrm{trans}}\) and recovers to the original shape when heated [37,38,39,40,41,42,43].
The major advantages of SMPs are that they have much larger driven strain than SMAs and are easier to achieve different shapes by adding different thermal phases. The recoverable strain of SMP can be over 800% [44] while that of SMA is generally less than 8%; SMP can be changed into more than two shapes under the strain of over 600% [45]. However, there are also some challenges: The shape change is not reversible and the recovering stress is low. Some studies focused on the liquid crystalline elastomer (LCE), a typical reversible SMP or the so-called shape changing polymer (SCP) relying on the orientation of crystalline when heated [46, 47]. Recently, Jin et al. [48] made further progress in programming the reversible LCE and made it a prototype robot. On the other hand, it is much more difficult to improve the recovering stress because the fixity would decrease under high pre-stretch or \({T}_{\mathrm{trans}}\) would be too high to achieve for practical conditions [49,50,51]. Sun et al. [52] utilized poly(methyl methacrylate) to achieve the maximum stress of 3.5 MPa at small strain; Song et al. [53] achieved 0.045 MPa at large strain (\(>90\)%) with 80/20 TPU/PLA blends. However, these are still insufficient for actuation applications. Some studies have shown a new way to achieve higher recovering stress by adding nanoparticles or SMA reinforcement. Miaudet et al. [54] significantly improved the stress to 130 MPa by fabricating an SMP with polyvinyl alcohol (PVA) and 20% CNT reinforced fibers. Zhou et al. [55] made a practical helix polymer membrane embedded with super-aligned carbon nanotubes, which could supply over 49% contraction.
The thermoresponsive hydrogel is another type of smart material to make linear actuators. Hydrogel is a hydrophilic functional polymer, which forms a three-dimensional network structure through physical or chemical crosslinking. The responsive hydrogels refer to those that can respond to changes due to the external environment. There are two main types of thermoresponsive hydrogel: one with a lower critical solution temperature (LCST) and the other with an upper critical solution temperature (UCST) [56]. The thermoresponsive hydrogel with a lower critical solution temperature exhibits hydrophilicity when the temperature is lower than its LCST and hydrophobicity when the temperature is higher than its LCST. The phase transition of the hydrogel polymer network causes a large amount of water enter the hydrogel (temperature increases, shrinkage decreases, and water absorption decreases), which changes the volume and shape of the hydrogel. The two main indicators of responsive hydrogel actuator are increasing water absorption rate [57] and actuating deformation [58]. The recent work [59] significantly improved the deformation in a particular direction by adding cofacially oriented TiNS planes in the magnetic flux, which bear the electrostatic force that could be enhanced by heating. And the strain of hydrogel in the direction orthogonal to the TiNS plane could reach 70%. The actuating time reduced to 0.5 s due to the absence of substantial water uptake and release by using a similar structure to the above, which could be heated by light [60], as shown in Fig. 2. Because of its high bioactivity and suitable actuating requirements for living creature, the application of hydrogel is mainly focused on biomedical science.
2.3 Soft Linear Actuators Driven by Ionic Diffusion
The ionic polymer–metal composite (IPMC) is an intelligent material (ionic type) for electro-deformation, which possesses the characteristics of flexible deformation, repeatability, large displacement, and low voltage. The IPMC material generally consists of the Nafion ion exchange film and the electrode. In the water-containing state, cations in polymer films can move freely, while anions cannot move in the carbon chain. When a voltage is applied at both ends of the IPMC electrode, an electric field will be generated between the electrodes. Within the electric field, the hydrated cation moves to the negative electrode, while the position of the anion remains unchanged. As a result, the negative electrode swells and positive electrode shrinks, which leads to the bending deformation of IPMC.
Due to the mechanism of actuation, the main driving mode of IPMC is bending rather than linear driving. Some special structures were thus designed to produce linear displacement. Kamamichi et al. [61] made a structure composed of two groups of IPMCs, with each group of IPMCs fixed at both ends and articulated at the junction. They did further research in the controlling system and the effect of chemical change during actuating [62, 63]. Rossiter et al. [64] attached several segments of IPMC actuator with opposite polarities to a flexible conductive polymer to produce a linear displacement and proposed a manufacturing method [65].
There were also some studies on conducting polymers which expand and shrink by electrochemical doping and dedoping. Lu et al. [66] fabricated a linear electrochemical actuator with a particular structure in hollow polyaniline fibers using solid polyaniline fibers and realized isotonic strains of 0.9% and isometric stresses of 0.9 MPa. They got the stress of 0.42–0.85 MPa generated with ionic liquid electrolytes [67]. As for polypyrrole, Hara et al. [68] reached the stress of 20.4 MPa with \(\hbox {TBACF}_{{3}}\hbox {SO}_{{3}}\) and the strain of 26% with bis(trifluoromethanesulfonyl)imide (TFSI) anion. New conducting polymers have been recently fabricated with different dopants, such as PPy doped with dodecylbenzenesulphonate (DBS) (PPy/DBS) [69], and further with phosphotungstate anions (PT) to give PPy/DBS-PT [70] and with carbide-derived carbon (CDC) to give PPy/DBS-CDC-PT [71] linear actuators. These conducting polymers have been applied in wearable devices [72] and even in tissue engineering [73], which are shown in Fig. 3.
2.4 Soft Linear Actuators Driven by Pressurized Fluidics
Pneumatic artificial muscles (PAMs) are among the most successful actuators in robotics due to their high force-to-weight ratio, controllable compliance, and simple structure. The PAM, composed of an elastomer and a braided sleeve, was invented by J.L. McKibben, so the compliant linear soft actuator has been usually called the McKibben’s artificial muscle [74, 75]. Recently, Martinez et al. [76] made a programmable pneumatic actuator with an embedded sheet and fiber. Robertson et al. [77] found that a bundle of small individual pneumatic actuators performed better than one single equivalent-volume actuator. Cui et al. [78] fabricated a PAM-driven humanoid robot hand, and applied the reinforcement learning algorithm to the PAM-driven robots. Hawkes et al. [79] reported a novel class of soft pneumatic robot that is capable of growing substantially in length. The peak rate of elongation is comparable to the rates of animal locomotion. The researchers at Tokyo Institute of Technology successfully mass-produced the McKibben. They bunched the muscles of tiny diameters together to develop characteristics of biological motion and produced a humanoid robot with muscles and skeleton as well as the clothes that serve as an auxiliary power suit. They also invented self-propelled colonoscopy and crawling robots based on McKibben [80].
PAMs could also be actuated by vacuum. Li et al. [81] came up with origami-inspired artificial muscles, which could contract over 90% of their initial lengths, generate stresses of 600 kPa, and produce peak power densities of over 2 kW/kg—all equal to, or in excess of, natural muscle. Yang et al. [82] made a linear buckling actuator with multi-chambers, which could respond within a second. Robertson et al. [83] invented vacuum-powered robots. These actuators are capable of achieving a variety of tasks, including multi-modal locomotion, object manipulation, and stiffness tuning. Some of them are shown in Fig. 4.
We summarize the strain and force data of various linear actuators introduced above and give their approximate sizes (diameters or areas) in the plane perpendicular to the direction of force (as shown in Table 1).
The inhomogeneous deformation of DE membrane possesses many advantages, such as large deformation, stackability, etc. We explored the relationship between the displacement and the output force with different ratios between the internal and external radius of fixed rings of the actuator and designed a spring–motor system to achieve the function of contraction.
2.5 Design of the Structure and Experiments
As shown in Fig. 5, we fabricated a two-layer DE actuator with a typical “sandwich” structure [84, 85], in which the outer ring A fixed the pre-tension, the inner ring B prevented crack propagation after piercing, and the VHB4910 with \(3 \times 3\) biaxial pre-stretch, shear modulus \({\mu }= 45\hbox { kPa}\), permittivity \(\varepsilon = 4.7\)\(\times ~8.854 \times 10^{-12}\hbox { F/m}\) were applied [86].
3 Linear Cone-Like DE Actuators
We carried out the finite element analysis with user-defined materials (Abaqus UMAT) [87]. Hybrid, reduced integration elements (CAX4RH) were used in the simulation, as shown in Fig. 6d, e. The failure displacement u was determined to be greater than 20 mm. The breakdown voltage at \(u=20\hbox { mm}\) was higher than 9 kV by experiment. The system was set with the maximum displacement of \(u=16\) mm and the testing voltage of \(\Phi =7\hbox { kV}\). We tested three types of actuators with different radius ratios (\(b/a=6\), 8, 10). In the tests, ring B is fixed on the lower splint of the stretcher, and ring A is fixed on the upper splint and connected with the force sensor. The measured displacement is the relative displacement between the upper splint and the lower splint, and the force is the tension obtained by the force sensor.
The experimental results are shown in Fig. 6. The solid lines are the force–displacement relationships of three actuators of different radius ratios with the voltage off, while the dashed lines are the force–displacement relationships at the voltage of 7 kV. The results show that under the same displacement load, decreasing the ratio of b / a will increase the pulling force produced by the membrane whether it is charged or not. For any given ratio of b / a, the actuating force linearly increases with the displacement u. The force reaches the highest value of 0.84 N at 7 kV and \(b/a=6\). This linear force–displacement relationship is control-friendly. We carried out the dead load actuation test to measure the force–displacement curve. With the data cutoff from 0.5 N to 2.5 N, the actuating strain decreases in inverse proportion to the load. The force–displacement relationships of three actuators with different aspect ratios were investigated. The actuator with the aspect ratio of \(b/a=8\) provides higher strain than the other two (as shown in Fig. 6c).
Besides, the displacement at failure increases with the decrease in aspect ratio. We could thus combine the cone-like linear actuators with different aspect ratios to satisfy different requirements, such as high actuating strain, high actuating force, or stable actuating condition.
3.1 System Design
Because of the extension of DE membrane when actuated, it is difficult to convert the output force into tension as the natural muscle does. Therefore, a spring–motor auxiliary actuation system is designed, as shown in Fig. 7a. When the system is under the non-working condition (State 2), ring A and ring B are in the same plane, and the membrane only keeps basic pre-stretching. While in State 2, the motor pulls the transmission line, and the tension in spring equals the tension in membrane plus the load. When under the working condition with applied voltage, the tension in membrane decreases, and the tension in spring becomes greater than the load. This voltage-induced force difference results in a linear motion until the system reaches equilibrium. To illustrate the process clearly, we tested the tension in the motor, as shown in Fig. 7b. The electromechanical output still relies on the deformation of the frame, which occurs in most bending actuators. The membrane is pre-stretched and fixed on an elastic frame that deforms, and elastic energy of distortion accumulates. When voltage is applied, the membrane expands in area and the frame recovers to its original shape. In this system, the motor stops once it gives the initially biased displacement. As a result, the DE cone-like actuator reaches State 3.
4 Conclusion
Based on the cone-shaped dielectric elastomer membrane, the hybrid driving system achieves electromechanical actuation with linear stroke. The force difference of the dielectric elastomer with alternating voltages can tune the stroke and the driving force of the whole system. Challenges still exist for the control, fabrication and power supply of the “motor–muscle” hybrid system. Control and modeling of the soft linear actuator require further investigation due to the complex behaviors of soft polymers such as viscoelasticity and electromechanical coupling. Future design of the system may include a strain sensor of flexible electronics and closed-loop feedback control to enhance the accuracy of actuators. Enhanced learning based on massive experimental data can also be induced in the modeling of the complex system [78, 88]. The fabrication methods for both soft active materials and flexible electronics should also be investigated to enhance the flexibility and endurance of the composite structure and hybrid system. The system design and operating methods for this hybrid linear actuator may guide the design of soft robots and smart flexible devices.
References
Kornbluh R, Pelrine R, Eckerle J, et al. Electrostrictive polymer artificial muscle actuators. In: Proceedings. 1998 IEEE international conference on robotics and automation (Cat. No. 98CH36146), vol 2. IEEE; 1998. p. 2147–54.
Kornbluh R, Pelrine R, Joseph J. Elastomeric dielectric artificial muscle actuators for small robots. In: Proceedings of the third IASTED international conference on robotics and manufacturing. 1995. p. 14–6.
Rajamani A, Grissom MD, Rahn CD, et al. Wound roll dielectric elastomer actuators: fabrication, analysis, and experiments. IEEE/ASME Trans Mechatron. 2008;13:117–24.
Pei Q, Pelrine R, Stanford S, et al. Electroelastomer rolls and their application for biomimetic walking robots. Synth Metals. 2003;135:129–31.
Zhang R, Kunz A, Lochmatter P, et al. Dielectric elastomer spring roll actuators for a portable force feedback device. In: Symposium on haptic interfaces for virtual environment & teleoperator systems. IEEE; 2006. p. 347–53.
Kovacs G. Arm wrestling robot driven by dielectric elastomer actuators. In: The first IEEE/RAS-EMBS international conference on biomedical robotics and biomechatronics, 2006. BioRob 2006. IEEE; 2006. p. 260–5.
Tryson M, Kiil HE, Benslimane M. Powerful tubular core free dielectric electro activate polymer (DEAP) push actuator. In: Electroactive polymer actuators and devices (EAPAD) 2009. International Society for Optics and Photonics; 2009. p. 7287–1F.
Lau GK, Lim HT, Teo JY, et al. Lightweight mechanical amplifiers for rolled dielectric elastomer actuators and their integration with bio-inspired wing flappers. Smart Mater Struct. 2014;23(2):021–5.
Teh YS, Koh SJA. Giant continuously-tunable actuation of a dielectric elastomer ring actuator. Extreme Mech Lett. 2016;9:195–203.
Lu T, Chiang Foo C, Huang J, et al. Highly deformable actuators made of dielectric elastomers clamped by rigid rings. J Appl Phys. 2014;115(18):184105.
Khanh VTV, Mathew AT, Koh SJA. Stackable configurations of artificial muscle modules that is continuously-tunable by voltage. In: Electroactive polymer actuators and devices (EAPAD) 2017. International Society for Optics and Photonics; 2017. p. 10163–2K.
Mathew AT, Koh SJA. Operational limits of a non-homogeneous dielectric elastomer transducer. Int J Smart Nano Mater. 2017;8(4):214–23.
He T, Zhao X, Suo Z. Dielectric elastomer membranes undergoing inhomogeneous deformation. J Appl Phys. 2009;106(8):083522.
Kovacs G, Düring L, Michel S, et al. Stacked dielectric elastomer actuator for tensile force transmission. Sens Actuators A Phys. 2009;155(2):299–307.
Acome E, Mitchell SK, Morrissey TG, et al. Hydraulically amplified self-healing electrostatic actuators with muscle-like performance. Science. 2018;359(6371):61–5.
Lee KH, Tawfick S. Fiber micro-architected electro-elasto-kinematic muscles. Extreme Mech Lett. 2016;8:64–9.
Suo Z. Theory of dielectric elastomers. Acta Mech Solida Sin. 2010;23(6):549–78.
Zhao X, Suo Z. Theory of dielectric elastomers capable of giant deformation of actuation. Phys Rev Lett. 2010;104(17):178302.
Lv X, Liu L, Liu Y, Leng J. Electromechanical modelling of softening behavior for dielectric elastomers. J Appl Mech. 2018;85(11):111010.
Suo Z, Zhao X, Greene WH. A nonlinear field theory of deformable dielectrics. J Mech Phys Solids. 2008;56(2):467–86.
Koh SJA, Li T, Zhou J, et al. Mechanisms of large actuation strain in dielectric elastomers. J Polym Sci Part B Polym Phys. 2011;49(7):504–15.
Lv X, Liu L, Liu Y, Leng J. Dielectric elastomer energy harvesting: maximal converted energy, viscoelastic dissipation and a wave power generator. Smart Mater Struct. 2015;24(11):115036.
Leng J, Liu L, Liu Y, Yu K, Sun S. Electromechanical stability of dielectric elastomer. Appl Phys Lett. 2007;91:061921.
Liu L, Liu Y, Luo X, Li B, Leng J. Electromechanical instability and snap-through instability of dielectric elastomers undergoing polarization saturation. Mech Mater. 2012;55:60–72.
Zhou J, Hong W, Zhao X, et al. Propagation of instability in dielectric elastomers. Int J Solids Struct. 2008;45(13):3739–50.
Plante JS, Dubowsky S. Large-scale failure modes of dielectric elastomer actuators. Int J Solids Struct. 2006;43(25–26):7727–51.
Romasanta LJ, López-Manchado MA, Verdejo R. Increasing the performance of dielectric elastomer actuators: a review from the materials perspective. Prog Polym Sci. 2015;51:188–211.
Haines CS, Márcio D Lima, Li N, et al. Artificial muscles from fishing line and sewing thread. Science. 2014;343(6173):868–72.
Mirvakili SM, Ravandi AR, Hunter IW, et al. Simple and strong: twisted silver painted nylon artificial muscle actuated by Joule heating. In: Electroactive polymer actuators and devices (EAPAD) 2014, vol 9056. International Society for Optics and Photonics; 2014. p. 90560I.
Yip MC, Niemeyer G. High-performance robotic muscles from conductive nylon sewing thread. In: 2015 IEEE international conference on robotics and automation (ICRA). IEEE; 2015. p. 2313–8.
Koh JS, Cho KJ. Omega-shaped inchworm-inspired crawling robot with large-index-and-pitch (LIP) SMA spring actuators. IEEE/ASME Trans Mechatron. 2013;18(2):419–29.
Mosley M, Mavroidis C, Pfeiffer C. Design and dynamics of a shape memory alloy wire bundle actuator. In: Proceedings of the ANS, 8th topical meeting on robotics and remote systems. 1999. p. 1–14.
De Laurentis KJ, Nikitczuk J, Fisch A, et al. Design and experimentation of shape memory alloy wire bundle actuators. In: Romansy 14. Vienna: Springer; 2002. p. 339–50.
Andrianesis K, Tzes A. Development and control of a multifunctional prosthetic hand with shape memory alloy actuators. J Intell Robot Syst. 2015;78(2):257–89.
Lee HT, Kim MS, Lee GY, et al. Shape memory alloy (SMA)-based microscale actuators with 60% deformation rate and 1.6 kHz actuation speed. Small. 2018;14(23):1801023.
Spindler C, Juhre D. Development of a shape memory alloy actuator using generative manufacturing. Int J Adv Manuf Technol. 2018;97:1–10.
Rapoport N. Physical stimuli-responsive polymeric micelles for anti-cancer drug delivery. Prog Polym Sci. 2007;32(8–9):962–90.
Schmaljohann D. Thermo-and pH-responsive polymers in drug delivery. Adv Drug Deliv Rev. 2006;58(15):1655–70.
Ionov L. Actively-moving materials based on stimuli-responsive polymers. J Mater Chem. 2010;20(17):3382–90.
Liu F, Urban MW. Recent advances and challenges in designing stimuli-responsive polymers. Prog Polym Sci. 2010;35(1–2):3–23.
Stuart MAC, Huck WTS, Genzer J, et al. Emerging applications of stimuli-responsive polymer materials. Nat Mater. 2010;9(2):101.
Roy D, Cambre JN, Sumerlin BS. Future perspectives and recent advances in stimuli-responsive materials. Prog Polym Sci. 2010;35(1–2):278–301.
Meng H, Hu J. A brief review of stimulus-active polymers responsive to thermal, light, magnetic, electric, and water/solvent stimuli. J Intell Mater Syst Struct. 2010;21(9):859–85.
Gu X, Mather PT. Entanglement-based shape memory polyurethanes: synthesis and characterization. Polymer. 2012;53(25):5924–34.
Zhao R, Zhao T, Jiang X, et al. Thermoplastic high strain multishape memory polymer: side-chain polynorbornene with columnar liquid crystalline phase. Adv Mater. 2017;29(12):1605908.
Krause S, Zander F, Bergmann G, Brandt H, Wertmer H, Finkelmann H. Nematic main-chain elastomers: coupling and orientational behavior. C R Chim. 2009;12:85–104.
Ohm C, Brehmer M, Zentel R. Liquid crystalline elastomers as actuators and sensors. Adv Mater. 2010;22:3366–87.
Jin B, Song H, Jiang R, et al. Programming a crystalline shape memory polymer network with thermo-and photo-reversible bonds toward a single-component soft robot. Sci Adv. 2018;4(1):eaao3865.
Zhao Q, Qi HJ, Xie T. Recent progress in shape memory polymer: new behavior, enabling materials, and mechanistic understanding. Prog Polym Sci. 2015;49:79–120.
Meng H, Li G. A review of stimuli-responsive shape memory polymer composites. Polymer. 2013;54(9):2199–221.
Xie T. Tunable polymer multi-shape memory effect. Nature. 2010;464(7286):267.
Sun L, Huang WM, Wang CC, et al. Optimization of the shape memory effect in shape memory polymers. J Polym Sci Part A Polym Chem. 2011;49(16):3574–81.
Song JJ, Chang HH, Naguib HE. Biocompatible shape memory polymer actuators with high force capabilities. Eur Polym J. 2015;67:186–98.
Miaudet P, Derré A, Maugey M, et al. Shape and temperature memory of nanocomposites with broadened glass transition. Science. 2007;318(5854):1294–6.
Zhou Z, Yan Q, Liu C, et al. An arm-like electrothermal actuator based on superaligned carbon nanotube/polymer composites. New Carbon Mater. 2017;32(5):411–8.
Ward MA, Georgiou TK. Thermoresponsive polymers for biomedical applications. Polymers. 2011;3(3):1215–42.
Yoshida R, Uchida K, Kaneko Y, et al. Comb-type grafted hydrogels with rapid deswelling response to temperature changes. Nature. 1995;374(6519):240–2.
Xia LW, Ju XJ, Liu JJ, et al. Responsive hydrogels with poly (N-isopropylacrylamide-co-acrylic acid) colloidal spheres as building blocks. J Colloid Interface Sci. 2010;349(1):106–13.
Kim YS, Liu M, Ishida Y, et al. Thermoresponsive actuation enabled by permittivity switching in an electrostatically anisotropic hydrogel. Nat Mater. 2015;14(10):1002.
Sun Z, Yamauchi Y, Araoka F, et al. An anisotropic hydrogel actuator enabling earthworm-like directed peristaltic crawling. Angew Chem. 2018;130(48):15998–6002.
Yamakita M, Kamamichi N, Kaneda Y, et al. Development of an artificial muscle linear actuator using ionic polymer–metal composites. Adv Robot. 2007;18(4):17.
Kamamichi N, Yamakita M, Kozuki T, et al. Doping effects on robotic systems with ionic polymer–metal composite actuators. Adv Robot. 2007;21(1–2):21.
Yamakita M, Kamamichi N, Luo ZW, et al. Robotic application of IPMC actuators with redoping capability. In: Kim KJ, Tadokoro S, editors. Electroactive polymers for robotic applications. London: Springer; 2007. p. 199–225.
Rossiter JM, Stoimenov BL, Mukai T. A linear actuator from a single ionic polymer–metal composite (IPMC) strip. In: Electroactive polymer actuators and devices (EAPAD) 2007, vol 6524. International Society for Optics and Photonics; 2007. p. 65241B.
Stoimenov BL, Rossiter JM, Mukai T. Manufacturing of ionic polymer–metal composites (IPMCs) that can actuate into complex curves. In: Electroactive polymer actuators and devices (EAPAD) 2007, vol 6524. International Society for Optics and Photonics; 2007. p. 65240T.
Lu W, Smela E, Adams P, et al. Development of solid-in-hollow electrochemical linear actuators using highly conductive polyaniline. Chem Mater. 2004;16(9):1615–21.
Lu W, Norris ID, Mattes BR. Electrochemical actuator devices based on polyaniline yarns and ionic liquid electrolytes. Aust J Chem. 2005;58(4):263–9.
Hara S, Zama T, Takashima W, et al. TFSI-doped polypyrrole actuator with 26% strain. J Mater Chem. 2004;14(10):1516–7.
Wang X, Smela E. Experimental studies of ion transport in PPy (DBS). J Phys Chem C. 2008;113(1):369–81.
Zondaka Z, Kesküla A, Tamm T, et al. Polypyrrole linear actuation tuned by phosphotungstic acid. Sens Actuators B Chem. 2017;247:742–8.
Zondaka Z, Harjo M, Khorram MS, et al. Polypyrrole/carbide-derived carbon composite in organic electrolyte: characterization as a linear actuator. React Funct Polym. 2018;131:414–9.
Zhou J, Mulle M, Zhang Y, et al. High-ampacity conductive polymer microfibers as fast response wearable heaters and electromechanical actuators. J Mater Chem C. 2016;4(6):1238–49.
Gelmi A, Cieslar-Pobuda A, de Muinck E, et al. Direct mechanical stimulation of stem cells: a beating electromechanically active scaffold for cardiac tissue engineering. Adv Healthc Mater. 2016;5(12):1471–80.
Tondu B. Modelling of the McKibben artificial muscle: a review. J Intell Mater Syst Struct. 2012;23(3):225–53.
Caldwell DG, Tsagarakis N, Medrano-Cerda GA. Bio-mimetic actuators: polymeric pseudo muscular actuators and pneumatic muscle actuators for biological emulation. Mechatronics. 2000;10(4–5):499–530.
Martinez RV, Fish CR, Chen X, et al. Elastomeric origami: programmable paper-elastomer composites as pneumatic actuators. Adv Funct Mater. 2012;22(7):1376–84.
Robertson MA, Sadeghi H, Florez JM, et al. Soft pneumatic actuator fascicles for high force and reliability. Soft Robot. 2017;4(1):23–32.
Cui Y, Matsubara T, Sugimoto K. Pneumatic artificial muscle-driven robot control using local update reinforcement learning. Adv Robot. 2017;31(8):397–412.
Hawkes EW, Blumenschein LH, Greer JD, et al. A soft robot that navigates its environment through growth. Sci Robot. 2017;2(8):eaan3028.
Suzumori Endo Lab, Tokyo Tech. https://www.youtube.com/watch?v=0ZBD2tcKOU4. Accessed 12 Mar 2019.
Li S, Vogt DM, Rus D, et al. Fluid-driven origami-inspired artificial muscles. Proc Natl Acad Sci. 2017;114(50):13132–7.
Yang D, Verma MS, So Ju-Hee, et al. Buckling pneumatic linear actuators inspired by muscle. Adv Mater Technol. 2016;1(3):1600055.
Robertson MA, Paik J. New soft robots really suck: vacuum-powered systems empower diverse capabilities. Sci Robot. 2017;2(9):eaan6357.
Pelrine RE, Kornbluh RD, Joseph JP. Electrostriction of polymer dielectrics with compliant electrodes as a means of actuation. Sens Actuators A Phys. 1998;64(1):77–85.
Pelrine R, Kornbluh R, Pei Q, et al. High-speed electrically actuated elastomers with strain greater than 100%. Science. 2000;287(5454):836–9.
Li T, Keplinger C, Baumgartner R, et al. Giant voltage-induced deformation in dielectric elastomers near the verge of snap-through instability. J Mech Phys Solids. 2013;61(2):611–28.
Zhao X, Suo Z. Method to analyze programmable deformation of dielectric elastomer layers. Appl Phys Lett. 2008;93(25):251902.
Yang T, Xiao Y, Zhang Z, et al. A soft artificial muscle driven robot with reinforcement learning. Sci Rep. 2018;8(1):14518.
Acknowledgements
This work acknowledges the supports from the following programs: National Key R&D Program of China (2017YFA0701100), National Natural Science Foundation of China (11572280, 11822207, U1613202 11321202 and 11432012), National Basic Research Program of China (Grant No. 2015CB057301), China Association for Science and Technology (Young Elite Scientist Sponsorship Program No. YESS20150004), Zhejiang Provincial Natural Science Foundation of China (R18A020004), Fund of State Key Laboratory of Fluid Power and Mechatronic Systems, Zhejiang University, and Dr. Li Dak Sum & Yip Yio Chin Fund for Stem Cell and Regenerative Medicine.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Cao, X., Zhang, M., Zhang, Z. et al. Review of Soft Linear Actuator and the Design of a Dielectric Elastomer Linear Actuator. Acta Mech. Solida Sin. 32, 566–579 (2019). https://doi.org/10.1007/s10338-019-00112-8
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10338-019-00112-8