Abstract
The amorphous polymer of polystyrene (PS) has been widely used in the selective laser sintering (SLS) process. However, PS is not suitable to make parts with thin-wall or delicate structures because of the poor mechanical properties of its SLS parts. Therefore, styrene–acrylonitrile copolymer (SAN), another kind of amorphous polymers, was investigated as an SLS material. The effects of laser energy density on the relative density, mechanical properties, and dimensional accuracy of the SLS parts were studied, and the properties of PS and SAN SLS parts were compared. The postprocessing method of infiltrating with epoxy resin was used to reinforce the green SAN SLS parts. The results show that there is little difference in the relative density between the SAN and PS SLS parts, while the flexural strength of the SAN SLS specimens is obviously higher than that of the PS SLS specimens at the same energy density. After the postprocessing, the flexural strength, flexural modulus, and impact strength of the SAN SLS specimens increase by 133%, 4394%, and 254%, respectively, and the SLS parts maintain relatively high-dimensional accuracy although slight shrinkage occurs due to epoxy resin cure. SAN can be used to fabricate SLS parts with more complex and delicate structures.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
Kumar S (2003) Selective laser sintering: a qualitative and objective approach. JOM 55:43–47
Pham DT, Dimov S, Lacan F (1999) Selective laser sintering: applications and technological capabilities. P I Mech Eng B- J Eng 213:435–449
Kruth JP, Wang X, Laoui T, Froyen L (2003) Lasers and materials in selective laser sintering. Assem Autom 23:357–371
Caulfield B, McHugh PE, Lohfeld S (2007) Dependence of mechanical properties of polyamide components on build parameters in the SLS process. J Mater Process Technol 182:477–488. doi:10.1016/j.matprotec.2006.09.007
Chung H, Das S (2006) Processing and properties of glass bead particulate-filled functionally graded nylon-11 composites produced by selective laser sintering. Mater Sci Eng A- Struct 437:226–234. doi:10.1016/j.msea.2006.07.112
Zarringhalam H, Hopkinson N, Kamperman NF, de Vlieger JJ (2006) Effects of processing on microstructure and properties of SLS nylon 12. Mater Sci Eng A- Struct 435–436:172–180. doi:10.1016/j.msea.2006.07.084
Jain KP, Pandey PM, Rao PVM (2009) Effect of delay time on part strength in selective laser sintering. Int J Adv Manuf Technol 43:117–126. doi:10.1007/s00170-008-1682-3
Beaman J, Barlow JW, Bourell DL, Crawford RH, Marcus HL, McAlea KP (1997) Solid freeform fabrication: a new direction in manufacturing. Kluwer Academic Publishers, Boston
Gibson I, Shi DP (1997) Material properties and fabrication parameters in selective laser sintering process. Rapid Prototyping J 3:129–136
Shi YS, Chen JB, Wang Y, Li ZC, Huang SH (2007) Study of the selective laser sintering of polycarbonate and post process for parts reinforcement. P I Mech Eng L- J Mat 221:37–42. doi:10.1243/14644207JMDA65
Yang JS, Shi YS, Shen QW, Yan CZ (2009) Selective laser sintering of HIPS and investment casting technology. J Mater Process Technol 209:1901–1908. doi:10.1016/j.jmatprotec.2008.04.056
Liu HJ, Fan ZT, Huang NY, Dong XP (2003) A note on rapid manufacturing process of metallic parts based on SLS plastic prototype. J Mater Process Technol 142:710–713. doi:10.1016/S0924-0136(03)00811-2
Ho HCH, Gibson I, Cheung WL (1999) Effects of energy density on morphology and properties of selective laser sintered polycarbonate. J Mater Process Technol 89–90:204–210
Ho HCH, Cheung WL, Gibson I (2003) Morphology and properties of selective laser sintered Bisphenol A polycarbonate. Ind Eng Chem Res 42:1850–1862. doi:10.1021/ie0206352
Ho HCH, Cheung WL, Gibson I (2002) Effects of graphite powder on the laser sintering behaviour of polycarbonate. Rapid Prototyping J 8:233–242. doi:10.1108/13552540210441148
Fan KM, Cheung WL, Gibson I (2005) Movement of powder bed material during the selective laser sintering of Bisphenol-A polycarbonate. Rapid prototyping J 11:188–198. doi:10.1108/13552540510612884
Shi YS, Li ZC, Sun HX, Huang SH, Zeng FD (2004) Development of a polymer alloy of polystyrene (PS) and polyamide (PA) for building functional part based on selective laser sintering (SLS). P I Mech Eng L- J Mat 218:299–306
Dotchev K, Soe S (2006) Rapid manufacturing of patterns for investment casting: improvement of quality and success rate. Rapid Prototyping J 12:156–164. doi:10.1108/13552540610670735
Zheng HZ, Zhang J, Lu SQ, Wang GC, Xu ZF (2006) Effect of core–shell composite particles on the sintering behavior and properties of nano-Al2O3/polystyrene composite prepared by SLS. Mater Lett 60:1219–1223. doi:10.1016/j.matlet.2005.11.003
Wang RJ, Wang LL, Zhao LH, Liu ZJ (2007) Influence of process parameters on part shrinkage in SLS. Int J Adv Manuf Technol 33:498–504. doi:10.1007/s00170-006-0490-x
Nelson JC (1993) Selective laser sintering: a definition of the process and an empirical sintering model. Ph.D. thesis, The University of Texas at Austin, Austin, Texas
Chung H (2005) Processing and properties of functionally graded polymer composites produced by selective laser sintering. Ph.D. thesis, The University of Michigan, Ann, Arbor.
Frenkel J (1945) Viscous flow of crystalline bodies under the action of surface tension. J Phys (USSR) 9:385–396
Sun MSM (1993) Physical modeling of the selective laser sintering process. Ph.D. thesis, The University of Texas at Austin, Austin, Texas.
Author information
Authors and Affiliations
Corresponding author
Additional information
An erratum to this article can be found at http://dx.doi.org/10.1007/s00170-010-2778-0
Rights and permissions
About this article
Cite this article
Yan, C., Shi, Y., Yang, J. et al. Investigation into the selective laser sintering of styrene–acrylonitrile copolymer and postprocessing. Int J Adv Manuf Technol 51, 973–982 (2010). https://doi.org/10.1007/s00170-010-2681-8
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s00170-010-2681-8