Abstract
Joint solubility of PuF3 and CeF3 in melts of the molar composition 78LiF-7ThF4-15UF4 and 72.5LiF-7ThF4-20.5UF4 in the temperature range 550°-800°C was studied. Anhydrous PuF3 and CeF3 spiked with 144Ce, and also anhydrous ThF4 were synthesized. Isothermal saturation method was used for studying the solubility of pressed PuF3 and CeF3 pellets in these melts in an inert (argon) atmosphere. The dependence of the joint solubility of PuF3 and CeF3 on the melt temperature was determined.
Similar content being viewed by others
References
Ignatiev, V.V., Feynberg, O.S., Zagnitko, A.V., et al., At. Energy, 2012, vol. 112, no. 3, pp. 157–165.
Ignatiev, V., Feynberg, O., Lizin, A., et al., Ann. Nucl. Energy, 2014, vol. 64, pp. 408–420.
Renault, C., Delpech, S., Ignatiev, V., et al., Proc. Fission Safety (FISA), 2009, vol. 2, pp. 384–399.
Delpech, S., Merle-Lucotte, E., Heuer, D., et al., J. Fluorine Chem., 2009, vol. 130, no. 1, pp. 11–17.
Serp, J., Alilbert, M., Bereš, O., et al., Prog. Nucl. Energy, 2014, vol. 77, pp. 308–319.
Barton, C.J., Bredig, M.A., Gilpatrick, L.O., and Fredricksen, J.A., Inorg. Chem., 1970, vol. 9, no. 2, pp. 307–311.
Barton, C.J., J. Phys. Chem., 1960, vol. 64, pp. 306–309.
Mailen, J., Smith, F., and Ferris, L., J. Chem. Eng. Data, 1971, vol. 16, pp. 68–71.
Bamberger, C., Ross, R., and Baes, C., Report ORNL-4622, 1970, p. 91–92.
Sood, D., Nucl. Technol., 1975, vol. 27, pp. 411–416.
Ignat’ev, V.V., Merzlyakov, A.V., Subbotin, V.G., et al., At. Energy, 2006, vol. 101, no. 5, pp. 822–829.
Lizin, A.A., Tomilin, S.V., Gnevashov, O.E., et al., At. Energy, 2013, vol. 115, no. 1, pp. 11–17.
Lizin, A.A., Tomilin, S.V., Gnevashov, O.E., et al., At. Energy, 2013, vol. 115, no. 1, pp. 20–22.
Naumov, V., in United States-Russian Federation Molten Salt Reactor (MSR) and Fluoride Salt-Cooled High-Temperature Reactor (FHR) Technical Exchange Meet., Oak Ridge, Tennessee (USA): Oak Ridge National Laboratory, November 19–20, 2013.
Weaver, C.F., Thoma, R.E., Insley, H., and Friedman, H.A., Report of Oak Ridge National Laboratory ORNL-2548, 1959, pp. 119–120.
Yakovenko, A.G., Baranov, A.Yu., and Filippov, A.N., in Novye tekhnologii dlya energetiki, promyshlennosti i stroitel’stva (New Technologies for Power Engineering, Industry, and Building), Dimitrovgrad, 2002, issue 5, pp. 77–85.
Powder Diffraction File, Swarthmore, Pennsylvania (USA): Int. Center for Diffraction Data, 1999.
Volozhin, M.V., Zakirov, R.Ya., Mushnikov, P.N., et al., At. Energy, 2013, vol. 115, no. 1, pp. 18–21.
Author information
Authors and Affiliations
Corresponding author
Additional information
Original Russian Text © A.A. Lizin, S.V. Tomilin, V.V. Ignat’ev, A.G. Osipenko, M.V. Kormilitsyn, N.Yu. Nezgovorov, 2015, published in Radiokhimiya, 2015, Vol. 57, No. 1, pp. 32–37.
Rights and permissions
About this article
Cite this article
Lizin, A.A., Tomilin, S.V., Ignat’ev, V.V. et al. Joint solubility of PuF3 and CeF3 in ternary melts of lithium, thorium, and uranium fluorides. Radiochemistry 57, 36–42 (2015). https://doi.org/10.1134/S1066362215010063
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S1066362215010063