Transient Liquid Phase Bonding of 2205 Duplex Stainless Steel Using a Ni-P Interlayer

  • Published:
Journal of Materials Engineering and Performance Aims and scope Submit manuscript

Abstract

Transient liquid phase (TLP) bonding was successfully applied to join 2205DSS using a Ni-P interlayer. Microstructural studies revealed that isothermal solidification (IS) progressed via formation of γ-Fe solid solution from the base metal (BM)/bonding zone (BZ) interface toward the BZ centerline. Cooling the TLP bonding assembly before completion of the IS resulted in non-isothermal solidification (athermal solidification: AS) of the residual liquid (L) along the BZ centerline. Microstructural studies revealed that the AS took place via L → γ-Fe + M3P eutectic transformation. FESEM/EDS and XRD analyses indicated that M3P was a complex (Fe,Ni,X)3P phosphide that X contained Cr and Mo elements. Formation of the phosphide constituents increased significantly the microhardness of BZ centerline (up to 510 ± 5HV) and resulted in sharp decrease of shear strength of the TLP-bonded specimen (180 MPa). Completion of the IS caused uniform microhardness profile across the BZ (~ 240 ± 5HV) and significant enhancement of shear strength of the TLP-bonded specimen (~ 380 MPa). Furthermore, pitting corrosion resistance of the TLP-bonded specimen increased significantly after completion of the IS, i.e., the weight loss of TLP-bonded specimen decreased to 0.39 mg/mm2 that was close to that of the as-received BM (0.23 mg/mm2).

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2
Fig. 3
Fig. 4
Fig. 5
Fig. 6
Fig. 7
Fig. 8
Fig. 9
Fig. 10
Fig. 11
Fig. 12
Fig. 13
Fig. 14
Fig. 15
Fig. 16
Fig. 17
Fig. 18
Fig. 19
Fig. 20
Fig. 21

Similar content being viewed by others

References

  1. J. Lv, W. Guo, and T. Liang, The Effect of Pre-Deformation on Corrosion Resistance of the Passive Film Formed on 2205 Duplex Stainless Steel, J. Alloys Compd., 2016, 686, p 176–183

    Article  CAS  Google Scholar 

  2. Z. Zhang, H. Zhao, H. Zhang, Z. Yu, J. Hu, L. He, and J. Li, Effect of Isothermal Aging on the Pitting Corrosion Resistance of UNS S82441 Duplex Stainless Steel Based on Electrochemical Detection, Corros. Sci., 2015, 93, p 120–125

    Article  CAS  Google Scholar 

  3. J. Verma and R.V. Taiwade, Effect of Welding Processes and Conditions on the Microstructure, Mechanical Properties and Corrosion Resistance of Duplex Stainless Steel Weldments, A Review, J. Manuf. Process., 2017, 25, p 134–152

    Article  Google Scholar 

  4. M. Mosallaee, A. Ekrami, K. Ohsasa, and K. Matsuura, Solute Redistribution During Transient Liquid Phase Bonding of IN738LC With BNi-3 Interlayer, Mater. Sci. Technol., 2008, 24, p 449–456

    Article  CAS  Google Scholar 

  5. M. Mosallaee, A. Ekrami, K. Ohsasa, and K. Matsuura, Microstructural Evolution in the Transient-Liquid-Phase Bonding Area of IN-738LC/BNi-3/IN-738LC, Metall. Mater. A, 2008, 39(10), p 2389–2402

    Article  Google Scholar 

  6. X. Yuan, M.B. Kim, and C.Y. Kang, Characterization of Transient-Liquid-Phase-Bonded Joints in a Duplex Stainless Steel with a Ni-Cr-B Insert Alloy, Mater. Charact., 2009, 60, p 1289–1297

    Article  CAS  Google Scholar 

  7. X. Yuan, C.Y. Kang, and M.B. Kim, Microstructure and XRD Analysis of Brazing Joint for Duplex Stainless Steel Using a Ni-Si-B Filler Metal, Mater. Charact., 2009, 60, p 923–931

    Article  CAS  Google Scholar 

  8. X. Yuan, M.B. Kim, Y.H. Cho, and C.Y. Kang, Microstructures, Mechanical and Chemical Properties of TLP-Bonded Joints in a Duplex Stainless Steel with Amorphous Ni-Based Insert Alloys, Metall. Mater. Trans. A, 2012, 43, p 1989–2001

    Article  CAS  Google Scholar 

  9. B. Rhee, S. Roh, and D. Kim, Transient Liquid Phase Bonding of Nitrogen Containing Duplex Stainless Steel UNS S31803 Using Ni-Cr-Fe-Si-B Insert Metal, Mater. Trans., 2003, 44, p 1014–1023

    Article  CAS  Google Scholar 

  10. T. Khan, M. Kabir, and R. Bulpett, Effect of Transient Liquid-Phase Bonding Variables on the Properties of a Micro-Duplex Stainless Steel, Mater. Sci. Eng. A, 2004, 372, p 290–295

    Article  Google Scholar 

  11. L. Jeffus, Welding: Principles and Applications, Cengage Learning, Boston, 2011

    Google Scholar 

  12. F. Jalilian, M. Jahazi, and R. Drew, Microstructure Evolution During Transient Liquid Phase Bonding of Alloy 617, Metallogr. Microstruct. Anal., 2013, 2, p 170–182

    Article  CAS  Google Scholar 

  13. M. Kapoor, O.N. Dogan, C.S. Carney, R.V. Saranam, P. Mcneff, and B.K. Paul, Transient Liquid Phase Bonding of H230-Ni-Based Alloy Using Ni-P Interlayer: Microstructure and Mechanical Properties, Metall. Mater. Trans. A, 2017, 48(7), p 3343–3356

    Article  CAS  Google Scholar 

  14. Y. Yang, Z. Wang, H. Tan, J. Hong, Y. Jianga, L. Jiang, and J. Li, Effect of a Brief Post-Weld Heat Treatment on the Microstructure Evolution and Pitting Corrosion of Laser Beam Welded UNS S31803 Duplex Stainless Steel, Corros. Sci., 2012, 65, p 472–480

    Article  CAS  Google Scholar 

  15. A. international, ASTM G48-11, Standard Test Methodes for Pitting and Crevice Corrosion Resistance of Stainless Steels and Related Alloys by Use of Ferric Chloride Solution, ASTM, West Conshohocken, 2015

    Google Scholar 

  16. H.-J. Kim, S.-H. Jeon, S.-T. Kim, and Y.-S. Park, Influence of the Shielding Gas Composition on the Passive Film and Erosion Corrosion of Tube-to-Tube Sheet Welds of Hyper Duplex Stainless Steel, Corros. Sci., 2015, 91, p 140–150

    Article  CAS  Google Scholar 

  17. M. Islam, N. Sato, and Y. Tomota, Effects of Process Parameters on Ferrite Grain Size of Commercially Pure Iron, J. Sci. Res., 2011, 3, p 311–319

    Article  CAS  Google Scholar 

  18. T. Padron, T.I. Khan, and M.J. Kabir, Modelling the Transient Liquid Phase Bonding Behaviour of a Duplex Stainless Steel Using Copper Interlayers, Mater. Sci. Eng. A, 2004, 385, p 220–228

    Article  Google Scholar 

  19. Y.W. Yen, J.W. Su, and D.P. Huang, Phase Equilibria of the Fe-Cr-Ni Ternary Systems and Interfacial Reactions in Fe-Cr Alloys with Ni Substrate, J. Alloys Compd., 2008, 457, p 270–278

    Article  CAS  Google Scholar 

  20. N. Llorca-Isern, H. López-Luque, and I. López-Jiménez, Maria Victoria Biezma, Identification of Sigma and Chi Phases in Duplex Stainless Steels, Mater. Charact., 2016, 112, p 20–29

    Article  CAS  Google Scholar 

  21. T. Vigraman, R. Narayanasamy, and D. Ravindran, Microstructure and Mechanical Property Evaluation of Diffusion-Bonded Joints, Mater. Des., 2012, 35, p 156–169

    Article  CAS  Google Scholar 

  22. S. Esmailzadeha, M. Aliofkhazraeia, and H. Sarlak, Sarlak, Interpretation of Cyclic Potentiodynamic Polarization Test Results for Study of Corrosion Behavior of Metals: A Review, Prot. Met. Phys. Chem. Surf., 2018, 54(5), p 976–989

    Article  Google Scholar 

Download references

Author information

Authors and Affiliations

  1. Department of Mining and Metallurgy, Yazd University, P.O. Box: 89195-741, Yazd, Iran

    Afshin Babanejhad & Masoud Mosallaee

Authors
  1. Afshin Babanejhad
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Masoud Mosallaee
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Masoud Mosallaee.

Additional information

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Rights and permissions

Reprints and permissions

About this article

Check for updates. Verify currency and authenticity via CrossMark

Cite this article

Babanejhad, A., Mosallaee, M. Transient Liquid Phase Bonding of 2205 Duplex Stainless Steel Using a Ni-P Interlayer. J. of Materi Eng and Perform 29, 2355–2367 (2020). https://doi.org/10.1007/s11665-020-04758-1

Download citation

  • Received:

  • Revised:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s11665-020-04758-1

Keywords

Search

Navigation