Abstract
We design and fabricate elastically tunable monodisperse microcapsules using microfluidics and cross-linkable polydimethylsiloxane (PDMS). The overall stiffness of the microcapsules is governed by both the thickness and cross-link ratio of the polymer shell. Flowing suspensions of microcapsules through constricted spaces leads to transient blockage of fluid flow, thus altering the flow behavior. The ability to tune microcapsule mechanical properties enables the design of elastic microcapsules that can be tailored for desired flow behavior in a broad range of applications such as oil recovery, reactor feeding, red blood cell flow and chemical targeted delivery.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Introduction
Particle flow through confined spaces is important in many industrial and biomedical applications including, enhanced oil recovery (EOR), reactor feeding, filtration, lubrication, red-blood-cell transport, and drug delivery1,2,3,4. To design particles for such applications, an understanding of the characteristics of their flow behavior through confined media is required. Generally, particles deform to squeeze through smaller geometries which results in a transient partial blockage of fluid flow, thereby limiting fluid mobility causing an increase in fluid pressure. Upon achieving a critical pressure increase that is dependent on the particle’s mechanical properties, the particle dislodges and continues to flow. This pressure increase is problematic in pneumatic feeding of reactors3, yet advantageous for EOR applications because the reduction in fluid mobility leads to flow redistribution in the porous space, resulting in increased volumes of oil recovered. Thus, it is essential to design particles with tunable mechanical properties that can be used to induce a range of fluid pressures as a means to control the flow behavior of suspensions in constricted spaces. However, designing this required range of tunability of mechanical properties into traditional particles such as emulsions and preformed polymer gels (PPG) remains challenging. In such systems, the range of fluid flow mobility achieved by controlling the particle's properties is narrow. In surfactant-stabilized emulsions, the range of interfacial tension is small and cannot be used as an effective control parameter; the dispersed phase viscosity is the only available control variable. Solid particles, such as PPGs, cannot be submitted to very large deformation to flow through constrictions smaller than their diameter and therefore are not effective as a mobility control additive. A liquid core-shelled microparticle such as a polymer microcapsule with multiple adjustable physical parameters, including shell thickness and shell elastic modulus, would provide a wide range of fluid mobility and have increased utility for a broad range of flow conditions and applications.
A microcapsule with known and tunable mechanical properties can be prepared through the use of highly-controlled synthesis techniques such as droplet microfluidics; these enable control of microcapsule size and membrane thickness through careful manipulation of fluid flow rates. In addition, microfluidics, particularly glass capillary microfluidics, affords the flexibility and choice of materials5 to impart various mechanical properties. An elastomer such as polydimethylsiloxane (PDMS) is an ideal shell material because it has high elastic deformation6,7,8,9. In addition, the mechanical properties10,11 of the PDMS can be easily tuned by changing the ratio of the two-component PDMS precursor8. Despite the potential to tune the stiffness of PDMS microparticles, this parameter remains unvaried for solid PDMS6,8,12, gas-filled5,13,14 and liquid-filled microcapsules7,9.
Single compression confinement methods5,9,15,16,17 are commonly used to determine the overall microparticle stiffness. In addition, the pressure-drop associated with microparticle blockage and passage through confined geometries is measured and correlated to the microparticle properties5,18,19,20,21,22,23. The combination of compression and constriction techniques provides a quantitative measure of the mechanical properties of the microparticles, and the effect of particle stiffness on the flow behavior through confined geometries. Such a well-characterized and elastically tunable PDMS shelled microcapsule could be used to adjust fluid mobility in complex constricted media.
In this paper, we use microfluidics to prepare batches of PDMS-shelled microcapsules. Adjusting the fluid flow rates and the cross-link ratio of the two-component PDMS precursor enables production of PDMS-shelled microparticles with tunable elastic properties. We use single particle compression tests to measure their overall stiffness and flow them through constricted capillaries, thereby evaluating their potential to control fluid mobility through confined geometries.
Results and Discussion
To produce monodisperse PDMS microcapsules, we use a double emulsion glass capillary device24, which consists of an outer square capillary, one round injection capillary, and one round collection capillary, as shown in Fig. 1. The tapered injection capillary and the unmodified round collection capillary are inserted from opposite ends into the square capillary and coaxially aligned within the square, as shown schematically in Fig. 1a. The geometry of the double emulsion glass capillary device is held constant while the fluid flow rates are independently varied and controlled through the use of syringe pumps coupled to the device by tubing. The inner water phase comprising of dyed Milli-Q® is pumped through the tapered round capillary, whereas the middle phase, PDMS, co-flows in the space between the square and the round tapered capillary. The outer fluid, a 10% PVA solution, flows in the opposite direction in the space between the square capillary and the blunt-end round capillary to flow-focus the fluids to enable microcapsule formation. A high-speed camera acquiring images at a frame rate of 1000 f/s is used to monitor and capture images of microcapsule production, as shown in Fig. 1b and supplementary video 1. We collect the microcapsules in Milli-Q® water, and rotate them for 1 week to ensure the center droplet and the outer droplet are concentric upon curing at room temperature.
To tune the stiffness of the shells, the PDMS polymer to cross-linker ratio is altered from 5:1, 10:1, 17.5:1 and 20:1. The degree of cross-linking for the pure elastomer is proportional to the elastic modulus: the high-ratio cross-linked PDMS, 5:1, is the most rigid10,11. To visually distinguish between the varied cross-linker ratios, the inner water phase is dyed blue for 5:1, yellow for 10:1, orange for 17.5:1 and red dye for 20:1. The capsules from each batch are monodisperse independent of the cross-linker ratio used in droplet fabrication, as seen in Fig. 1c–f.
We prepare microcapsules with diameter 2 R of approximately 700 µm, with no more than 1.5% deviation from the mean for each batch, and vary shell thicknesses δ by changing only the middle phase flow rate (Q m ). The flow is initially stabilized at the smallest possible Q m which renders capsules with the thinnest shell. The thickness of the surrounding middle phase increases with the flow rate Q m ; this delays microcapsule breakup and leads to thicker shells, as shown qualitatively in Fig. 2a–f. Remarkably, a simple mass balance9 (Equation 1) describes the relationship between the microcapsule thickness and the middle and inner phase flow rate ratio Q m /Q i , as shown in Fig. 2g; this enables a priori prediction of flow rates to obtain desired shell thicknesses.
Our microfluidic technique combined with the use of cross-linkable PDMS elastomer enables us to precisely tune the mechanical properties of the microcapsules. To measure the mechanical properties and to evaluate the degree to which these parameters affect the overall stiffness, we conduct single particle compression tests. For each test, an individual microcapsule is submerged in water between two parallel plates on a rheometer25. Initially, the microcapsule is axisymmetrically positioned between the two plates separated at a distance equivalent to the droplet diameter (2 R), as shown in Fig. 3a. As the top plate is incrementally lowered, the gap between the plates (2c) decreases and the capsule deforms to an oblate spheroid-shape, as shown in Fig. 3b. At each position, the normal force (F) is measured until the force reaches steady-state. Assuming constant volume26 of the compressed and uncompressed states enables calculation of the radius of the spheroid a. The stress σ and the shell surface area A are evaluated at each plate position as shown in Equations 2 and 3:
From these data, true area strain ε is calculated as shown in Equation (4), where the change in area ΔA is the difference between A and A o , the surface area of the uncompressed capsule.
We evaluate the apparent modulus as the ratio of the maximum stress to the maximum strain and plot these values as a function of thickness, as shown in Fig. 4. Here, two trends are observed: one of a higher apparent modulus for higher cross-linked ratios, and the other of a higher modulus for larger δ/R values. In the former trend, a larger stress is required to deform the higher cross-linked ratio group (5:1), whereas the lowest stresses are required to deform the more flexible shells20 due to use of the lower-modulus bulk polymer10. This behavior is expected because the elastic modulus is directly proportional to the cross-link ratio20,27. Furthermore, the second trend observed is that within each cross-linker ratio system, the overall microcapsule stiffness increases with δ, thereby suggesting the shell thickness drastically influences the overall microcapsule stiffness16,17.
To further elucidate the effect of thickness within a given cross-linker ratio5,16 we curve-fit the data, as shown in Fig. 4. The bending stiffness for a membrane/shell is proportional to the cubic thickness while the stretching is proportional to the thickness15. The top curve representing the highest cross-linked ratio fits to a cubic power, thus indicating the stress proportionality to the cubic thickness; this relationship shows the bending or flexural rigidity is the predominant contributor to the overall stiffness of the capsules prepared with the 5:1 PDMS. By contrast, the 10:1 and 17.5:1 curves are linear, hence emphasizing the importance of the stretching response for the lower cross-linked ratios. Unexpectedly, at the lowest cross-link ratio of 20:1, the shells become too fragile to withstand significant stress, consequently preventing evident data trends. The fragility of the shells with the lowest cross-linking ratio suggests there is a critical limit for which the cross-link ratio becomes more significant to the overall stiffness than does the shell thickness. Moreover, when shells are thin26,28 bending is typically loosely defined and considered negligible. Consequently, the bending to stretching regime is solely defined as a thickness dependent condition. However, the differences between the curves in Fig. 4 for the various cross-linked densities indicate shell elasticity is also an important factor in the bending to stretching transition. A similar phenomenon is observed for thin blistering films29 in which a dimensionless parameter, k, is proportional to the square root of the radius squared over the modulus. At a fixed thickness, increasing the Young’s modulus lowers k. Consequently, the transition from bending to stretching is defined for low values of k, which corresponds to a higher stiffness. Regardless of the regime of deformation, all microcapsules will bend or stretch under stress; however, with the high cross-linked ratio, the stress is primarily attributed to bending, whereas for lower cross-linked ratio capsules, the stress is governed by stretching.
We hypothesize that the stiffer microcapsules will reduce fluid mobility to a larger extent than the softer microcapsules27. To evaluate this hypothesis, we flow the microcapsules through constrictions; these are prepared by using the capillary puller. A cylindrical glass capillary (with an inner diameter of 860 µm) is pulled to generate a constriction smaller than the average microcapsule diameter (2R = 707.5 µm). The constriction diameter of approximately 400 µm enables the microcapsules to deform to ~57% of their initial diameter. By coupling a pressure transducer to the capillary flow system, the pressure changes caused by microcapsules restricting fluid flow can be monitored. For each experiment, a syringe pump drives the microcapsule and its surrounding fluid (Milli-Q® water) at a fixed volumetric flow rate through the constriction. Each capsule slowly and continuously deforms as it passes through the constriction; this behavior is characteristic of a lubrication flow between the PDMS and the glass surface. To evaluate the contribution of lubricated friction to the pressure drop, we obtain an estimate of µ f = 0.0130. Thus, the friction force contributes only to approximately 4% of the total pressure drop acting on the capsule as it flows through the constriction.
The three positions (I, II, and III) of the microcapsule as it passes through the constriction are shown in Fig. 5a; these positions are directly correlated to the measured pressure difference (ΔP) as a function of time, shown in Fig. 5b. Each microcapsule position is defined by a distinct deformation regime: pre-deformation, maximum deformation, and recovery. The pre-deformation regime occurs when the microcapsule remains spherical prior to entering the constriction, as shown in Fig. 5a,I. In the pre-deformation regime, the position of the microcapsule is associated with the low-pressure region, shown in Fig. 5b,I; this pressure difference is equivalent to that of the suspending liquid alone. By contrast, a larger pressure is required to deform the capsule and push it through the constriction, as shown in Fig. 5b,II. As a result, in the maximum deformation state, the microcapsule deforms to a dumbbell shape thereby occupying the constriction and restricting fluid flow. The pressure increases to a maximum until the advancing microcapsule ceases to block fluid flow and it recovers to its initial spherical shape. The microcapsule then exits constriction into the wider opening of the unconstricted region of the capillary; this transition is coupled to an immediate drop in pressure, seen in Fig. 5b,III.
We plot the maximum pressure difference as a function of shell thickness δ for each cross-link ratio to assess the impact of overall microcapsule stiffness on the ability of the microcapsule to change the mobility of the fluid flow, as shown in Fig. 6. As the thickness and stiffness increase, the resistance to fluid flow increases. For 5:1, the pressure increases with an approximate slope of ~5kPa (coefficient of determination = 0.998) and for the 20:1 increases with an approximate slope of 1kPa (coefficient of determination = 0.833). Moreover, the maximum pressure for the 5:1 group is six times the highest pressure from the 20:1 group because the microcapsules with high overall stiffness (more rigid) require more pressure to deform21. In addition, there is a trend of increased pressure with shell thickness, which is somewhat disrupted by an outlier in the 10:1 group. Nevertheless, at the highest thickness values for each cross-linking ratio, the pressure is largest for the high cross-linking ratio (5:1), and smallest at the low ratio (20:1), signaling the proportionality between the overall microcapsule stiffness and the ability of the microcapsule to increase fluid flow resistance. Thus, the extent of mobility control can be tuned by the elastic properties of the microcapsules suspended in a continuous phase.
Conclusion
We controllably produced monodisperse microcapsules with tunable overall stiffness determined by two factors: the PDMS cross linking ratio that defines the polymer stiffness and the shell thickness. Single microcapsule compression tests show high cross-linking ratio shells require greater stress to deform. Moreover, the deformation mode of bending or stretching is determined by both the PDMS cross-linking ratio and the shell thickness, thus indicating the significance of both parameters in the design of elastically tunable microcapsules. Furthermore, the microcapsules with the high cross-linking ratio are able to reduce fluid mobility through a constricted passage to the greatest extent, whereas lower cross-linking ratios have a smaller range of effectiveness as mobility control agents in constricted media.
The strategies presented here enable the design of elastic capsules for use in confined environments with different flow behavior requirements. Suspensions of more rigid microcapsules can be used in porous media at which a high degree of mobility reduction of the water phase is needed, whereas softer microcapsules can be used in applications in which the intensity of the mobility reduction cannot be very high.
Materials and Methods
The microcapsules are produced with the use of a double emulsion glass microcapillary device24. The device is composed of an outer square capillary (outer diameter, OD, 1.5 mm, inner diameter, ID, 1.05 mm, manufactured by Atlantic International Technology, Inc.), circular injection and collection capillaries (OD 0.58 mm, ID 1.00 mm, World Precision Instruments, Inc.), dispensing needles (type 304, McMaster-Carr) for fluid injection and a 25 mm × 75 mm glass microscope slide. The circular injection capillary is pulled with a micropipette puller (P-1000, Sutter Instrument) to a tapered opening of 40 µm and subsequently sanded to a diameter of ~150 µm. Then it was surface treated with Acquapel® to make it hydrophobic. The capillaries are coaxially aligned manually with the aid of a microscope for visualization. The fluids are injected with the use of three syringe pumps (Harvard Apparatus 11 Elite). The inner fluid is Milli-Q® (Millipore Corporation) water with food dye for visualization purposes, the middle fluid is the PDMS (Sylgard 184® from Dow Corning base and curing agent). A 10% polyvinyl alcohol (PVA) solution is used in the outer phase to increase its viscosity and to serve as a surfactant. The production of the microcapsules is monitored with a high-speed camera (Photron SA3 Fast Camera) attached to an inverted microscope (Leica DMi8). Images are acquired at 1000 fps.
The mechanical characterization is performed with a Rheometer (DHR-3, TA Instruments) using a 40 mm diameter stainless steel plate-plate geometry. Each capsule is placed in 20 µL of water (enough liquid to cover the entire capsule). The procedure consists of several steps of compression where the axial force is recorded after steady state is reached at each condition. Compression is performed only up to a predetermined deformation in order to avoid capsule rupture.
A syringe pump is used to flow a single microcapsule suspended in Mili- Q® water through a glass capillary (OD 1.5 mm, ID 0.86 mm, World Precision Instruments, Inc.) with a constriction, of inner diameter of approximately 0.40 mm. The capillary constriction is produced using a micropipette puller. For all tests, the pump is set to inject at a constant flow rate of 6 mL/h. A port, connected to a pressure transducer (Valydine) is installed to measure the pressure difference during the flow of the capsule through the constricted capillary. Pressure values are acquired on a PC by using a multiplexer slot as interface between the transducer and the computer. The inverted microscope and a high-speed camera are used to monitor and record the image of the microcapsule flowing through the capillary. For both the mechanical characterization and the microcapsule flow through a constriction, the results correspond to an average of at least three measurements.
References
Rorai, C., Touchard, A., Zhu, L. & Brandt, L. Motion of an elastic capsule in a constricted microchannel. Eur. Phys. J. E. 38, 1–13 (2015).
Wang, Y. & Dimitrakopoulos, P. Low-Reynolds-number droplet motion in a square microfluidic channel. Theor. Comput. Fluid Dyn. 26, 361–379 (2012).
Dai, J. & Grace, J. R. Blockage of constrictions by particles in fluid–solid transport. Int. J. Multiph. Flow. 36, 78–87 (2010).
Li, Y. et al. Universal behavior of hydrogels confined to narrow capillaries. Sci. Rep. 5, 17017 (2015).
Duncanson, W. J. et al. Microfluidic fabrication and micromechanics of permeable and impermeable elastomeric microbubbles. Langmuir. 31, 3489–3493 (2015).
Muñoz-Sánchez, B. N., Silva, S. F., Pinho, D., Vega, E. J. & Lima, R. Generation of micro-sized PDMS particles by a flow focusing technique for biomicrofluidics applications. Biomicrofluidics. 10, 14122 (2016).
Fu, Z. et al. Elastic silicone encapsulation of n-hexadecyl bromide by microfluidic approach as novel microencapsulated phase change materials. Thermochim. Acta. 590, 24–29 (2014).
Jiang, K., Thomas, P. C., Forry, S. P., DeVoe, D. L. & Raghavan, S. R. Microfluidic synthesis of monodisperse PDMS microbeads as discrete oxygen sensors. Soft Matter. 8, 923–926 (2012).
Vilanova, N., Rodriguez-Abreu, C., Fernaandez-Nieves, A. & Solans, C. Fabrication of novel silicone capsules with tunable mechanical properties by microfluidic techniques. ACS Appl. Mater. Interfaces. 5, 5247–5252 (2013).
Johnston, I. D., McCluskey, D. K., Tan, C. K. L. & Tracey, M. C. Mechanical characterization of bulk Sylgard 184 for microfluidics and microengineering. J. Micromechanics Microengineering. 24, 35017 (2014).
Wang, Z., Volinsky, A. A. & Gallant, N. D. Crosslinking effect on polydimethylsiloxane elastic modulus measured by custom-built compression instrument. J. Appl. Polym. Sci. 131, (2014).
Zhao, L.-B. et al. A novel method for generation of amphiphilic PDMS particles by selective modification. Microfluid. Nanofluidics 10, 453–458 (2011).
Hettiarachchi, K. & Lee, A. P. Polymer–lipid microbubbles for biosensing and the formation of porous structures. J. Colloid Interface Sci. 344, 521–527 (2010).
Agastin, S., Giang, U.-B. T., Geng, Y., DeLouise, L. A. & King, M. R. Continuously perfused microbubble array for 3D tumor spheroid model. Biomicrofluidics. 5, 24110 (2011).
Chen, P. W., Brignoli, J. & Studart, A. R. Mechanics of thick-shell microcapsules made by microfluidics. Polymer (Guildf). 55, 6837–6843 (2014).
Rachik, M., Barthes-Biesel, D., Carin, M. & Edwards-Levy, F. Identification of the elastic properties of an artificial capsule membrane with the compression test: effect of thickness. J. Colloid Interface Sci. 301, 217–226 (2006).
Neubauer, M. P., Poehlmann, M. & Fery, A. Microcapsule mechanics: From stability to function. Adv. Colloid Interface Sci. 207, 65–80 (2014).
Guillen, V. R., Romero, M. I., da Silveira Carvalho, M. & Alvarado, V. Capillary-driven mobility control in macro emulsion flow in porous media. International Journal of Multiphase Flow. 43, 62–65 (2012).
Guillen, V. R., Carvalho, M. S. & Alvarado, V. Pore scale and macroscopic displacement mechanisms in emulsion flooding. Transp. Porous Media. 94, 197–206 (2012).
Cui, J. et al. Super-Soft Hydrogel Particles with Tunable Elasticity in a Microfluidic Blood Capillary Model. Adv. Mater. 26, 7295–7299 (2014).
Li, Y., Kumacheva, E. & Ramachandran, A. The motion of a microgel in an axisymmetric constriction with a tapered entrance. Soft Matter. 9, 10391–10403 (2013).
Cobos, S., Carvalho, M. S. & Alvarado, V. Flow of oil–water emulsions through a constricted capillary. Int. J. Multiph. Flow. 35, 507–515 (2009).
Sun, H. et al. Structure governs the deformability of polymer particles in a microfluidic blood capillary model. ACS Macro Lett. 4, 1205–1209 (2015).
Utada, A. S. et al. Monodisperse double emulsions generated from a microcapillary device. Science. 308, 537–541 (2005).
Keller, M. W. & Sottos, N. R. Mechanical properties of microcapsules used in a self-healing polymer. Exp. Mech. 46, 725–733 (2006).
Bando, K., Ohba, K. & Oiso, Y. Deformation analysis of microcapsules compressed by two rigid parallel plates. J. Biorheol. 27, 18–25 (2013).
Dai, J. & Grace, J. R. Blockage of constrictions by particles in fluid–solid transport. International Journal of Multiphase Flow. 36, 78–87 (2010).
Kessler, S., Finken, R. & Seifert, U. Swinging and tumbling of elastic capsules in shear flow. J. Fluid Mech. 605, 207–226 (2008).
Wan, K.-T. & Lim, S.-C. The bending to stretching transition of a pressurized blister test. Int. J. Fract. 92, 43–47 (1998).
Kaneko, D., Oshikawa, M., Yamaguchi, T., Gong, J. P. & Doi, M. Friction coefficient between rubber and solid substrate – Effect of rubber thickness. J. of the Phys. Soc. of Japan 76(4), 043601–1 (2017).
Acknowledgements
This work was carried out in association with the ongoing Project registered as “Escoamento de dispersões complexas em meios porosos heterogêneos: análise na escala de poro e macroscópica” (PUC-Rio/BG Brasil/Shell Brasil/ANP) - Complex Dispersion Flow Through Porous Media - funded by BG Brasil/Shell Brasil under the ANP R&D levy as “Compromisso de Investimentos com Pesquisa e Desenvolvimento”. We thank Tina Lin and Thomas E. Kodger for their contributions.
Author information
Authors and Affiliations
Contributions
M.S.C. and W.J.D. planned the project and experiments. D.F.N. and W.J.D. performed the microcapsule fabrication experiments. J.A.A. and A.M. performed the mechanical characterization experiments. A.M. and M.J.B.M. performed the flow through constricted capillary experiments. All the authors contributed to the data analysis and the discussions. W.J.D. wrote the first draft of the manuscript. All the authors read and commented the final manuscript before submission.
Corresponding authors
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
do Nascimento, D.F., Avendaño, J.A., Mehl, A. et al. Flow of Tunable Elastic Microcapsules through Constrictions. Sci Rep 7, 11898 (2017). https://doi.org/10.1038/s41598-017-11950-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-017-11950-2
- Springer Nature Limited
This article is cited by
-
A curing agent for epoxy resin based on microencapsulation of 1-butylimidazole
Journal of Materials Science (2022)
-
Deformation and rupture of microcapsules flowing through constricted capillary
Scientific Reports (2021)
-
Microcapsules with controlled magnetic response
Microfluidics and Nanofluidics (2021)
-
Transport mechanism of deformable micro-gel particle through micropores with mechanical properties characterized by AFM
Scientific Reports (2019)