Abstract
Magnetic skyrmions1,2 are topologically protected spin textures that exhibit fascinating physical behaviours1,2,3,4,5,6 and large potential in highly energy-efficient spintronic device applications7,8,9,10,11,12,13. The main obstacles so far are that skyrmions have been observed in only a few exotic materials and at low temperatures1,2,3,4,6,7,8, and fast current-driven motion of individual skyrmions has not yet been achieved. Here, we report the observation of stable magnetic skyrmions at room temperature in ultrathin transition metal ferromagnets with magnetic transmission soft X-ray microscopy. We demonstrate the ability to generate stable skyrmion lattices and drive trains of individual skyrmions by short current pulses along a magnetic racetrack at speeds exceeding 100 m s−1 as required for applications. Our findings provide experimental evidence of recent predictions10,11,12,13 and open the door to room-temperature skyrmion spintronics in robust thin-film heterostructures.
Similar content being viewed by others
References
Rößler, U. K., Bogdanov, A. N. & Pfleiderer, C. Spontaneous skyrmion ground states in magnetic metals. Nature 442, 797–801 (2006).
Mühlbauer, S. et al. Skyrmion lattice in a chiral magnet. Science 323, 915–919 (2009).
Münzer, W. et al. Skyrmion lattice in the doped semiconductor Fe1−xCoxSi. Phys. Rev. B 81, 041203 (2010).
Yu, X. Z. et al. Real-space observation of a two-dimensional skyrmion crystal. Nature 465, 901–904 (2010).
Yu, X. Z. et al. Near room-temperature formation of a skyrmion crystal in thin-films of the helimagnet FeGe. Nature Mater. 10, 106–109 (2011).
Heinze, S. et al. Spontaneous atomic-scale magnetic skyrmion lattice in two dimensions. Nature Phys. 7, 713–718 (2011).
Jonietz, F. et al. Spin transfer torques in MnSi at ultralow current densities. Science 330, 1648–1651 (2010).
Schulz, T. et al. Emergent electrodynamics of skyrmions in a chiral magnet. Nature Phys. 8, 301–304 (2012).
Yu, X. Z. et al. Skyrmion flow near room temperature in an ultralow current density. Nature Commun. 3, 988 (2012).
Iwasaki, J., Mochizuki, M. & Nagaosa, N. Universal current-velocity relation of skyrmion motion in chiral magnets. Nature Commun. 4, 1463 (2013).
Fert, A., Cros, V. & Sampaio, J. Skyrmions on the track. Nature Nanotech. 8, 152–156 (2013).
Iwasaki, J., Mochizuki, M. & Nagaosa, N. Current-induced skyrmion dynamics in constricted geometries. Nature Nanotech. 8, 742–747 (2013).
Sampaio, J., Cros, V., Rohart, S., Thiaville, A. & Fert, A. Nucleation, stability and current-induced motion of isolated magnetic skyrmions in nanostructures. Nature Nanotech. 8, 839–844 (2013).
Dzyaloshinsky, I. A thermodynamic theory of ‘weak’ ferromagnetism of antiferromagnetics. J. Phys. Chem. Solids 4, 241–255 (1958).
Moriya, T. Anisotropic superexchange interaction and weak ferromagnetism. Phys. Rev. 120, 91–98 (1960).
Uchida, M., Onose, Y., Matsui, Y. & Tokura, Y. Real-space observation of helical spin order. Science 311, 359–361 (2006).
Bode, M. et al. Chiral magnetic order at surfaces driven by inversion asymmetry. Nature 447, 190–193 (2007).
Fert, A. & Levy, P. M. Role of anisotropic exchange interactions in determining the properties of spin-glasses. Phys. Rev. Lett. 44, 1538–1541 (1980).
Emori, S., Bauer, U., Ahn, S.-M., Martinez, E. & Beach, G. S. D. Current-driven dynamics of chiral ferromagnetic domain walls. Nature Mater. 12, 611–616 (2013).
Ryu, K.-S., Thomas, L., Yang, S.-H. & Parkin, S. Chiral spin torque at magnetic domain walls. Nature Nanotech. 8, 527–533 (2013).
Pizzini, S. et al. Chirality-induced asymmetric magnetic nucleation in Pt/Co/AlOx ultrathin microstructures. Phys. Rev. Lett. 113, 047203 (2014).
Emori, S. et al. Spin Hall torque magnetometry of Dzyaloshinskii domain walls. Phys. Rev. B 90, 184427 (2014).
Torrejon, J. et al. Interface control of the magnetic chirality in CoFeB/MgO heterostructures with heavy-metal underlayers. Nature Commun. 5, 4655 (2014).
Lo Conte, R. et al. Role of B diffusion in the interfacial Dzyaloshinskii–Moriya interaction in Ta/Co20Fe60B20/MgO nanowires. Phys. Rev. B 91, 014433 (2015).
Heide, M., Bihlmayer, G. & Blügel, S. Dzyaloshinskii–Moriya interaction accounting for the orientation of magnetic domains in ultrathin films: Fe/W(110). Phys. Rev. B 78, 140403 (2008).
Thiaville, A., Rohart, S., Jué, É., Cros, V. & Fert, A. Dynamics of Dzyaloshinskii domain walls in ultrathin magnetic films. Europhys. Lett. 100, 57002 (2012).
Malek, Z. & Kambersky, V. On the theory of the domain structure of thin films of magnetically uniaxial materials. Czech. J. Phys. 8, 416–421 (1958).
Woo, S., Mann, M., Tan, A. J., Caretta, L. & Beach, G. S. D. Enhanced spin–orbit torques in Pt/Co/Ta heterostructures. Appl. Phys. Lett. 105, 212404 (2014).
Jiang, W. et al. Blowing magnetic skyrmion bubbles. Science 349, 283–286 (2015).
Honda, S., Ikegawa, Y. & Kusuda, T. Magnetostatic energy and magnetization process in multilayers with perpendicular anisotropy. J. Magn. Magn. Mater. 111, 273–292 (1992).
Acknowledgements
Work at MIT was primarily supported by the US Department of Energy (DOE), Office of Science, Basic Energy Sciences (BES) under Award No. DE-SC0012371 (sample fabrication and MTXM and STXM experiments). The operation of the X-ray microscope at the Advanced Light Source was supported by the Director, Office of Science, Office of Basic Energy Sciences, Scientific User Facilities Division, of the US Department of Energy under Contract No. DE-AC02-05-CH11231. M.-Y.I. acknowledges support from the Leading Foreign Research Institute Recruitment Program (Grant No. 2012K1A4A3053565) through the National Research Foundation of Korea (NRF) funded by the Ministry of Education, Science and Technology (MEST). P.F. acknowledges support from the Director, Office of Science, Office of Basic Energy Sciences, Materials Sciences and Engineering Division, of the US Department of Energy under Contract No. DE-AC02-05-CH11231 within the Non-Equilibrium Magnetic Materials programme. G.S.D.B. acknowledges support from C-SPIN, one of the six SRC STARnet Centers, sponsored by MARCO and DARPA. M.K. and the group at Mainz acknowledge support by the DFG, the Graduate School of Excellence Materials Science in Mainz (MAINZ, GSC 266), the EU (MASPIC, ERC-2007-StG 208162; WALL, FP7-PEOPLE-2013-ITN 608031; MAGWIRE, FP7-ICT-2009-5), the MOGON (ZDV Mainz computing centre) and the Research Center of Innovative and Emerging Materials at Johannes Gutenberg University (CINEMA). B.K. is grateful for financial support by the Carl-Zeiss-Foundation. K.L. gratefully acknowledges financial support by the Graduate School of Excellence Materials Science in Mainz (MAINZ). S.W. acknowledges support from the Kwanjeong Foundation. L.C. acknowledges support by the NSF Graduate Research Fellowship Program. Measurements were carried out at the MAXYMUS endstation at Helmholtz-Zentrum Berlin. We thank HZB for the allocation of beamtime.
Author information
Authors and Affiliations
Contributions
S.W., P.F., M.K. and G.S.D.B. designed and initiated the research. S.W. and I.L. fabricated devices and S.W., I.L., L.C. and P.A. performed the film characterization. L.C. performed MOKE measurements of bubble domain expansion. S.W., M.-Y.I., L.C., M.M., K.L., I.L. and P.F. performed X-ray imaging experiments using MTXM at the Advanced Light Source in Berkeley, California. S.W., K.L., L.C., K.R., A.K., R.M.R. and M.W. conducted STXM experiments at the MAXYMUS beamline at the BESSY II synchrotron in Berlin. K.L., B.K. and M.K. performed and analysed the micromagnetic simulations. M.-A.M. provided technical input on sample design. B.K. derived the effective medium scaling laws and wrote the corresponding section in the Supplementary Information. P.A. and I.L. performed the analytical analysis of domain-spacing data. All authors participated in the discussion and interpreted results. S.W. drafted the manuscript and G.S.D.B. revised it with assistance from P.F. and M.K. All authors commented on the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Information (PDF 2364 kb)
Rights and permissions
About this article
Cite this article
Woo, S., Litzius, K., Krüger, B. et al. Observation of room-temperature magnetic skyrmions and their current-driven dynamics in ultrathin metallic ferromagnets. Nature Mater 15, 501–506 (2016). https://doi.org/10.1038/nmat4593
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1038/nmat4593
- Springer Nature Limited
This article is cited by
-
Electrically and mechanically driven rotation of polar spirals in a relaxor ferroelectric polymer
Nature Communications (2024)
-
Acoustic-driven magnetic skyrmion motion
Nature Communications (2024)
-
Dipolar skyrmions and antiskyrmions of arbitrary topological charge at room temperature
Nature Physics (2024)
-
The role of non-uniform magnetization texture for magnon–magnon coupling in an antidot lattice
Scientific Reports (2024)
-
Constructing coarse-grained skyrmion potentials from experimental data with Iterative Boltzmann Inversion
Communications Physics (2023)