Abstract
An electrospun poly(lactide-co-glycolide) (PLGA) membrane was prepared and used to perform the anti-adhesion of Achilles tendon. Throughout the experiments, the membrane showed an appropriate degradation rate, and the pH values of degradation media were maintained at around 7.4. Simultaneously, the excellent biocompatibility of the membrane in vitro and in vivo was confirmed by live/dead and histopathological analyses. Meanwhile, the membrane can reduce tendon adhesion significantly and promote functional recovery effectively. The encouraging results were further demonstrated by hematoxylin and eosin (H&E), and Masson’s trichrome stainings, and type I collagen immunohistochemical analysis. It was concluded that the model treated with the electrospun PLGA membrane was significantly better with respect to the adhesion prevention and tissue repair than that without treatment. Considering the results of degradation and adhesion prevention efficacy, the electrospun PLGA membrane would be a great candidate for the prevention of postoperative tendon adhesion.
Similar content being viewed by others
References
Hu, J.Z., Zhou, Y.C., Huang, L.H. and Lu, H.B., BMC Musculoskel. Dis., 2013, 14(1): 1
Sammer, D.M. and Chung, K.C., Wound Repair Regen., 2014, 22(S1): 25
Jorgensen, H.G., McLellan, S.D., Crossan, J.F. and Curtis, A.S., Cytokine, 2005, 30(4): 195
Karakurum, G., Buyukbebeci, O., Kalender, M. and Gulec, A., J. Surg. Res., 2003, 113(2): 195
Liu, S., Qin, M., Hu, C., Wu, F., Cui, W., Jin, T. and Fan, C., Biomaterials, 2013, 34(19): 4690
Hu, C., Liu, S., Zhang, Y., Li, B., Yang, H., Fan, C. and Cui, W., Acta Biomater., 2013, 9(7): 7381
Zheng, Z., Zhang, W., Sun, W., Li, X., Duan, J., Cui, J., Feng, Z. and Mansour, H.M., J. Mater. Sci., Mater. Med., 2013, 24(11): 2549
Zhou, Y., Zhang, L., Zhao, W., Wu, Y., Zhu, C. and Yang, Y., Biomaterials, 2013, 34(33): 8269
Khanna, A., Friel, M., Gougoulias, N., Longo, U.G. and Maffulli, N., Med. Bull., 2009, 90(1): 85
Zhou, X.L., Chen, S.W., Liao, G.D., Shen, Z.J., Zhang, Z.L., Sun, L., Yu, Y.J., Hu, Q.L. and Jin, X.D., World J. Gastroentero., 2007, 13(8): 1262
Way, T.D., Hsieh, S.R., Chang, C.J., Hung, T.W. and Chiu, C.H., Appl. Surf. Sci., 2010, 256(10): 3330
Seunarine, K., Meredith, D.O., Riehle, M.O., Wilkinson, C.D.W. and Gadegaard, N., Microelectron. Eng., 2009, 44(21): 5713
Sabir, M., Xu, X. and Li, L., J. Mater. Sci., 2009, 44(21): 5713
Liu, C.X., Zhang, D.R., He, Y., Zhao, X.S. and Bai, R., J. Membrane Sci., 2010, 346(1): 121
Agarwal, S., Wendorff, J.H. and Greiner, A., Adv. Mater., 2009, 21(32–33): 3343
Zhang J., Liu H., Xu, H., Ding, J.X., Zhuang, X.L., Chen, X.S., Chang, F., Xu, J.Z. and Li, Z.M., RSC Adv., 2014, 79(4): 41696
Zong, X., Li, S., Chen, E., Garlick, B., Kim, K.S., Fang, D., Chiu, J., Zimmerman, T., Brathwaite, C., Hsiao, B.S. and Chu, B., Ann. Surg., 2004, 240(5): 910
Franco, R.A., Nguyen, T.H. and Lee, B.T., J. Mater. Sci., Mater. Med., 2011, 22(10): 2207
Dinarvand, P., Hashemi, S.M., Seyedjafari, E., Shabani, I., Mohammadi-Sangcheshmeh, A., Farhadian, S. and Soleimani, M., J. Surg. Res., 2012, 172(1): E1
Virto, M.R., Elorza, B., Torrado, S., Elorza, M.D.L.A. and Frutos, G., Biomaterials, 2007, 28(5): 877
McUsic, A.C., Lamba, D.A. and Reh, T.A., Biomaterials, 2012, 33(5): 1396
Jain, R.A., Biomaterials, 2000, 21(23): 2475
Son, S.R., Franco, R.A., Bae, S.H., Min, Y.K. and Lee, B.T., J. Biomed. Mater. Res. B, 2013, 101(6): 1095
Yan, B.Z, Jian, X.D., Wei, G.X., Jie, W., Fei, C., Xiu, L. Z., Xue, S. C. and Jin, C.W., Chinese J. Polym. Sci., 2014, 32(12): 1590
Li, W.J., Laurencin, C.T., Caterson, E.J., Tuan, R.S. and Ko, F.K., J. Biomed. Mater. Res., 2002, 60(4): 61
Liu, S., Hu, C., Li, F., Li, X.J., Cui, W. and Fan, C., Tissue Eng. Part A, 2012, 19(3–4): 529
Song, Z.M., Shi, B., Ding, J.X., Zhuang X.L., Zhuang, X.N., Fu, C.F. and Chen, X.S., Sci. China Chem., 2014, In Press
Ishiyama, N., Moro, T., Ishihara, K., Ohe, T., Miura, T., Konno, T., Ohyama, T., Kimura, M., Kyomoto, M. and Nakamura, K., Biomaterials, 2010, 31(14): 4009
Jung, J.H., Ree, M. and Kim, H., Catal. Today, 2006, 115(1–4): 283
D’Souza, S., Faraj, J.A., Dorati, R. and DeLuca, P.P., AAPS Pharm. Sci. Technol., 2014, 15(3): 530
Park, T.G., Biomaterials, 1995, 16(15): 1123
Tsuji, H., Tezuka, Y. and Yamada, K., J. Polym. Sci., Part B: Polym. Phys., 2005, 43(9): 1064
Tsuji, H. and Tezuka, Y., Macromol. Biosci., 2005, 5(2): 135
Grayson, A.C., Cima, M.J. and Langer, R., Biomaterials, 2005, 26(14): 2137
Saha, S.K. and Tsuji, H., Macromol. Mater. Eng., 2006, 291(4): 357
Sun, L., Zhou, S., Wang, W., Li, X., Wang, J. and Weng, J., Colloid. Surface. A, 2009, 345(1–3): 173
Menei, P., Daniel, V., Montero-Menei, C., Brouillard, M., Pouplard-Barthelaix, A. and Benoit, J., Biomaterials, 1993, 14(6): 470
Gibbons, D., “Degradation Phenomena on Polymeric Biomaterials”, Springer, 1992, p. 97
Sun, L., Zhang, S., Zhang, J., Wang, N., Liu, W. and Wang, W., J. Mater. Chem. B, 2013, 1(32): 3932
Fang, M., Goldstein, E.L., Turner, A.S., Les, C.M., Orr, B.G., Fisher, G.J., Welch, K.B., Rothman, E.D. and Banaszak Holl, M.M., ACS Nano, 2012, 6(11): 9503
Langberg, H., Skovgaard, D., Petersen, L. J., Bülow, J. and Kjær, M., J. Physiol., 1999, 521(1): 299
Author information
Authors and Affiliations
Corresponding authors
Additional information
This work was financially supported by the National Natural Science Foundation of China (Nos. 51303174, 51321062, 51233004, 51390484, 51273196, and 51203153) and the Scientific Development Program of Jilin Province (No. 20140520050JH).
Rights and permissions
About this article
Cite this article
Song, Zm., Shi, B., Ding, Jx. et al. Prevention of postoperative tendon adhesion by biodegradable electrospun membrane of poly(lactide-co-glycolide). Chin J Polym Sci 33, 587–596 (2015). https://doi.org/10.1007/s10118-015-1611-5
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10118-015-1611-5