Continuous miniaturization of microelectronic devices has led the industry to develop interconnects on the order of a few microns for advanced superhigh-density and three-dimensional integrated circuits (3D ICs). At this scale, interconnects that conventionally consist of solder material will completely transform to intermetallic compounds (IMCs) such as Cu6Sn5. IMCs are brittle, unlike conventional solder materials that are ductile in nature; therefore, IMCs do not experience large amounts of plasticity or creep before failure. IMCs have not been fully characterized, and their mechanical and thermomechanical reliability is questioned. This study presents experimental efforts to characterize such material. Sn-based microbonds are fabricated in a controlled environment to assure complete transformation of the bonds to Cu6Sn5 IMC. Microstructural analysis including scanning electron microscopy (SEM), energy-dispersive x-ray spectroscopy (EDS), and x-ray diffraction (XRD) is utilized to determine the IMC material composition and degree of copper diffusion into the bond area. Specimens are fabricated with different bond thicknesses and in different configurations for various tests. Normal strength of the bonds is measured utilizing double cantilever beam and peeling tests. Shear tests are conducted to quantify the shear strength of the material. Four-point bending tests are conducted to measure the fracture toughness and critical energy release rate. Bonds are fabricated in different sizes, and the size effect is investigated. The shear strength, normal strength, critical energy release rate, and effect of bond size on bond strength are reported.
This is a preview of subscription content, log in via an institution to check access.
Similar content being viewed by others
References
L. Ladani, J. Razmi, and J. Bentley, Thin Solid Films 518, 4948 (2010).
M.M. Hou and T.W. Eagar, J. Electron. Packag. 114, 443 (1992).
J.C. Lin, L.W. Huang, G.Y. Jang, and S.H. Lee, Thin Solid Films 410, 212 (2002).
F. Bartels, J.W. Morris, G. Dalke, and W. Gust, J. Electron. Mater. 23, 8 (1994).
R.J. Field and S.R. Low, Physical and Mechanical Properties of Intermetallic Compounds Commonly Found in Solder Joints (National Institute of Standards and Technology, 2011). http://www.metallurgy.nist.gov/mechanical_properties/solder_paper.html.
J.O.G. Parent, D.D.L. Chung, and I.M. Bernstein, J. Mater. Sci. 23, 2564 (1988).
P. Zimprich, A. Betzwar-Kotas, G. Khatibi, B. Weiss, and H. Ipser, J. Mater. Sci. 19, 383 (2008).
L.M. Yinm, X.P. Zhang, and L.U. Chunsheng, J. Electron. Mater. 38, 2179 (2009).
E. Arzt, Acta Metall. Mater. 46, 5611 (1998).
W. Zhou, L. Liu, and P. Wu, Intermetallics 18, 922 (2010).
L. Ladani, J. Razmi, and J. Carter, U.S. patent 12/611,189. Patent application, Nov 3, 2009.
H.T. Lee, M.H. Chen, H.M. Jao, and T.L. Liao, Mater. Sci. Eng. A Struct. 358, 134 (2003).
R. Agrawal, B. Peng, E.E. Gdoutos, and H.D. Espinosa, Nano Lett. 8, 3668 (2008).
G.H. Jang, J.W. Lee, and J.G. Duh, J. Electron. Mater. 33, 1103 (2004).
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Ladani, L., Razmi, J. Mechanical Strength and Failure Characterization of Sn-Ag-Cu Intermetallic Compound Joints at the Microscale. J. Electron. Mater. 41, 573–579 (2012). https://doi.org/10.1007/s11664-011-1836-1
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11664-011-1836-1