Abstract
In wet bulk micromachining, the etching characteristics are orientation dependent. As a result, prolonged etching of mask openings of any geometric shape on both Si{100} and Si{110} wafers results in a structure defined by the slowest etching planes. In order to fabricate microstructures with high dimensional accuracy, it is vital to align the mask edges along the crystal directions comprising of these slowest etching planes. Thus, precise alignment of mask edges is important in micro/nano fabrication. As a result, the determination of accurate crystal directions is of utmost importance and is in fact the first step to ensure dimensionally accurate microstructures for improved performance. In this review article, we have presented a comprehensive analysis of different techniques to precisely determine the crystallographic directions. We have covered various techniques proposed in the span of more than two decades to determine the crystallographic directions on both Si{100} and Si{110} wafers. Apart from a detailed discussion of each technique along with their design and implementation, we have provided a critical analysis of the associated constraints, benefits and shortcomings. We have also summed up the critical aspects of each technique and presented in a tabular format for easy reference for readers. This review article comprises of an exhaustive discussion and is a handy reference for researchers who are new in the field of wet anisotropic etching or who want to get abreast with the techniques of determination of crystal directions.
Similar content being viewed by others
Background
Micromachining is an integral part of micro/nanofabrication for MEMS/NEMS industry [1–20]. There are two kinds of micromachining methods namely surface micromachining and bulk micromachining [17, 19]. As the name indicates, surface micromachining technique makes use of the surface of the substrate (e.g., wafer) and the micro/nanostructures are fabricated using deposited thin films on the surface. The deposited thin films are used as structural and sacrificial layers [9–18]. Bulk micromachining on the other hand selectively etches the bulk to fabricate 3-D features, suspended beams, membranes, etc. [1–16, 19, 20]. Bulk micromachining is further divided into two categories: dry and wet etching. Dry etching is mainly preformed using gas phase plasma [21–26], but focussed ion beam and laser machining are also used in some special cases [27, 28]. If the etching is performed using wet chemicals, it is termed as wet etching. Based on the etch rates in different directions, wet etching can be further sub-divided into isotropic and anisotropic etching. In isotropic etching, the etch rate is same in all directions and does not depend on the crystallographic directions, however in the case of anisotropic etching the etch rate is a function of the crystallographic orientation [9–14]. Common silicon wet isotropic etchants are mixture of HF, HNO3 and CH3COOH [29, 30], while potassium hydroxide (KOH) [2, 7, 31–43] and tetramethylammonium hydroxide (TMAH) [1, 5, 35, 44–64] etchants are most extensively used for wet anisotropic etching. There are some other alkaline solutions which have been investigated for silicon wet anisotropic etching such as ethylenediamine pyrocatechol water (EDP or EPW) [4, 35, 41, 65–67], hydrazine [31, 68, 69], ammonium hydroxide [70], and cesium hydroxide (CsOH) [71]. In wet anisotropic etching, {111} planes are the slowest etch rate planes in all types of anisotropic etchants. Therefore a stable etched profile (or prolonged etched profile) in silicon wafer is formed by {111} planes, for instance, an arbitrary shaped mask opening on Si{100} wafer leads to a square/rectangular V-groove comprising of {111} planes at the four mutually perpendicular ⟨110⟩ directions as shown in Fig. 1 [72], while on Si{110} wafer it gives a hexagonal groove type of structure comprising of {111} planes at the ⟨110⟩ and ⟨112⟩ directions as presented in Fig. 2 [73].
Role of crystallographic alignment in wet bulk micromachining
In surface micromachining, there are generally no issues of proper alignment of the mask edges/sides along crystallographic directions as the wafer/substrate is used only as a support for the fabrication of micro/nanostructures. Similarly, dry etching, which although uses the bulk material for fabrication is almost orientation independent, therefore precise alignment of the mask patterns along the crystallographic directions is also not of much importance. In the case of isotropic etching, the etched profile is orientation independent. Therefore the precise alignment of mask geometries with crystallographic directions does not attract much importance in this type of etching as well. However, on the contrary to these types of etching, anisotropic wet etching is highly orientation dependent. As a result it is of utmost significance to ensure that the mask edges are aligned precisely along the required crystallographic directions in order to fabricate dimensionally accurate microstructures. This makes the precise determination of crystallographic orientation a vital step to avoid over sizing of the structure and to obtain smooth sidewalls. The oversizing of the structures depends on the degree of the misalignment as well as the length of the structures. The importance of precise alignment in wet anisotropic etching based silicon micromachining is described by taking three examples of the most widely used structures in MEMS namely microchannel, cantilever beam and diaphragm.
Microchannels
Microchannels are extensively employed in bio-MEMS and micro-fluidics applications. The lengths of these micro-channels vary from a few microns to several millimetres [19, 74–77]. In order to fabricate a dimensionally accurate vertical micro-channel in {110} silicon wafers, the mask edges must be aligned precisely along the ⟨112⟩ directions as the stable and vertical {111} planes appear at these directions. When the mask edges are aligned precisely along the crystal direction, the channels are distinctly defined as per their dimensions. However, even a small misalignment would lead to undercutting as shown in Fig. 3. If the channels are patterned closely to each other, the undercutting due to misalignment can also lead to merging of the channels.
Similarly, long cavities formed on Si{100} wafer gets oversized due to misalignment by even a small angle. It happens due to the undercutting at misaligned mask edges as shown schematically in Fig. 4. Although there would be some undercutting even in the case of precisely aligned mask owing to the finite etch rate of {111} plane, however this undercutting is extremely less to cause any significant oversizing of the channels or cavities. The amount of undercutting (U) (measured perpendicular to the mask edge) due to misalignment by an angle δ for length l, as presented in Fig. 4, can be calculated using a simple trigonometric relation as follows:
Thus, a microchannel of length 10 mm will result in an undercut of ~18 μm even for a misalignment of 0.1°.
Cantilever beams
The diodes and transistors are considered as basic building blocks of integrated circuits (ICs). In MEMS, the shape and size of the structures are application dependent. Therefore there are no elementary building blocks which can support all designs. However, cantilevers and diaphragms are extensively used for sensing and actuation purposes in wide variety of applications including but not limited to bio-sensors, switches, temperature sensor and many others [78–99]. Thus they can be called as the fundamental structures of MEMS devices. Arrays of cantilever beams are used in various sensors and actuators for developing high performance devices such as artificial nose [84]. These arrays are fabricated either by front side etching or backside etching. In order to fabricate using front side etching, the phenomenon of convex corer undercutting is used for their release from substrate [8, 100]. Etching stops when it encounters the {111} planes at the anchoring point of the beam.
Thus precise alignment of the mask edges along crystallographic directions is necessary to obtain dimensionally accurate cantilever beams as shown in Fig. 5a. Owing to large number of beams, even a slight misalignment would result in larger underetching at the anchor points leading to additional overhang as shown in Fig. 5b. The additional overhang results in coupling of the beams and affects their dynamic characteristics. In order to fabricate high performance devices, it is necessary to avoid such coupling and align the mask patterns precisely along the ⟨110⟩ direction on Si{100}.
Diaphragm
Another important MEMS structure used in sensing devices is diaphragm. To fabricate the diaphragm, the etching is done throughout the wafer thickness (h) from the backside as shown schematically in Fig. 6. The length of the mask pattern (b) for fabricating a square diaphragm of sides l can be calculated using following formula:
where, δ is the misaligned angle. It is evident from this formula that the size of the mask edge (b) for a particular diaphragm length (l) depends on the misalignment angle δ. In order to control the dimensions of the diaphragm one need to ensure that δ should be negligible. In quantitative terms, to fabricate a square diaphragm of side l = 50 μm through a 500 μm thick Si{100} wafer, the sides of the mask opening should be around 758.04 μm. However, misalignment by half degree would make the diaphragm around 13 % more of its expected dimensions which can alter the performance of a sensor.
Owing to the importance of fabricating dimensionally accurate structures with smooth sidewalls, study of crystallographic alignment techniques is extremely vital in the field of wet anisotropic etching based bulk micromachining. Another benefit of accurately aligned mask is that it reduces the etching time necessary for obtaining smooth sidewalls. While there have been several review articles published in various areas of microfabrication including wet etching [8, 100], dry etching [21], microvalves [92], micropumps [95, 97], microfluidics [101], etc., there is no review article till date which extensively discusses various techniques to identify different crystallographic directions on silicon wafers along with their associated pros and cons. Given the importance of precise alignment as discussed above, it is very important to understand the role of alignment as well as the methodologies to ensure precise mask alignment. This paper is a comprehensive review of all the proposed pre-etched patterns published from the last two decades till date. It deals with the pros and cons of various pre-etched structures as well as which design patterns are easy to fabricate and are less involved in analysing them when it comes to determining the accurate crystallographic directions. We start with a brief discussion on the methods used for aligning the mask edges to the crystallographic directions. Subsequently, the role of different pre-etched patterns in identifying the crystal directions along with the merits of each technique is discussed.
Alignment techniques
Basic method to align the mask patterns along crystallographic directions is by using the wafer flat as the reference crystallographic direction. Generally the wafer manufacturing industries uses an optical beam to focus at etched surface and the reflected ray is used to determine the crystallographic direction (wafer flat) of the whole ingot prior to cutting it to wafers [102]. These wafer flats usually have a crystallographic misalignment ranging from 1° to 5° depending on the quality of the wafer [103]. An inaccurate wafer flat would lead to inaccuracy in aligning the mask edges along crystallographic directions leading to undesired increase in dimensions as discussed in previous section (refer Figs. 3, 4). For example, in order to fabricate a vertical walled channel on Si{110} wafer, we need to align the channel mask precisely along ⟨112⟩ direction. However, if the flat is misaligned, the mask edges will not be aligned along the ⟨112⟩ directions. This will lead to undercutting resulting in an inaccurately dimensioned (oversized) channel. This inaccuracy is undesirable for the high performance devices used today as they require extremely high precision control of dimensions. Thus the wafer flat used for aligning mask is no longer sufficient to achieve the high precision. Another method is to use X-ray diffraction, which can exactly determine the crystallographic direction, but it is highly impracticable to mount the diffraction equipment onto the mask aligner. As a result there have been other attempts to determine the crystallographic directions with high accuracy on Si{100} and Si{110} wafers which are most widely used in semiconductor laboratories and industries.
In order to determine the crystallographic directions (e.g., ⟨110⟩) on silicon wafer with high precision either cleaved-edge method or wet anisotropically pre-etched patterns are employed. These methods are described in following subsections.
Cleaved-edge alignment
Single-crystal materials have a tendency to cleave along crystallographic planes and are caused by the alignment of weaker bonds between atoms in the crystal lattice. In single crystalline silicon, a perfect cleavage takes places at the direction comprising {111} and {110} planes as the bond density for these planes is lower than other planes such as {100}. Therefore, the slip lines and other defects at the edges of silicon wafers are usually responsible for wafer breakage. In this method, the silicon wafer is cleaved to reveal {111} planes for alignment, for instance, cleaved edges on {110} wafer are aligned along ⟨110⟩ and ⟨112⟩ directions as shown in Fig. 7 for the wafer whose flat is oriented along ⟨110⟩ direction. In order to fabricate the microstructures, for example long and deep channels on {110} wafer, the edges of the microchannel patterns are aligned with cleaved-edges oriented along ⟨112⟩ directions [76]. Although this method is very simple to identify the crystallographic directions, wafer is separated into pieces and the cleaved surface may not be formed by a single {111} planes instead a rugged surface is obtained as can be seen in Fig. 8a, c [76]. This leads to very poor results as can be seen in the experimental images presented in Fig. 8b [76]. Therefore, this method of alignment is undesirable owing to the uncertainty in obtaining the cleaving along the precise crystal direction. Besides, reproducibility of this method is questionable.
Pre-etched patterns
The cleaved-edge method relies on the accuracy of the wafer flat as well as the handler’s accuracy to cleave (or dice) the wafer along the scribed line. Additionally, it also depends on the accuracy of the scribed directions. Therefore, this is not an optimal method to ensure precise determination of crystallographic direction. As a result, more accurate techniques are needed for the accurate determination of crystal directions.
Researchers in the past have used anisotropic etching to fabricate patterns to determine the crystallographic direction (e.g., ⟨110⟩, ⟨100⟩) with high precision. These patterns are etched on the periphery of the wafer and therefore the usable wafer space is not affected significantly. These pre-etched patterns act as aids for the subsequent alignment of mask edges. This method of alignment has been accurate in determining the crystallographic directions precisely with an accuracy as high as 0.01°. This has helped the researchers in fabricating dimensionally accurate micro-structures for different applications. Many designs have previously been proposed which talks about the alignment techniques and its accuracy. Several pre-etched patterns have been proposed till date using various geometries [76, 102–110]. Some of them aim at determining the ⟨110⟩ direction on Si{100} and S{110} wafers [76, 102, 104–107]. At the same time, some have been aimed at determining the ⟨100⟩ direction on both types of wafer [103, 108, 109]. In the subsequent subsections, we discuss various techniques, design geometry and their accuracies in determining the crystallographic directions which have been published in the period of more than two decades. Apart from high accuracy, a good pre-etched pattern should have minimum measurement requirement, should be visually identifiable with simple equipment and should not use much of the usable wafer space. At the same time it should not only determine the crystallographic directions but also aid in alignment of the subsequent mask. We categorise the techniques based on their suitability for wafers of different orientations. Some techniques exploit the shape of etched profiles and thus can be exclusively used for one particular wafer orientation. However, some techniques have been proposed which can be used for different types of wafers. In the subsequent subsections, we discuss the details of the patterns starting with the patterns for determining directions on Si{100} followed by Si{110} wafers.
Identification of crystallographic directions on Si{100} wafer
In the fabrication of microstructures on Si{100} wafer using wet anisotropic etching, identification of ⟨110⟩ direction is of interest due to the appearance of stable {111} planes at these directions. Nevertheless, ⟨100⟩ directions are also important due to the appearance of stable {110} planes when etching is done in surfactant added etchants. These {110} planes are used as 45° micromirrors in optical MEMS applications. We start with the techniques to determine the precise ⟨110⟩ directions followed by a discussion on the techniques to determine the ⟨100⟩ directions.
In order to determine the ⟨110⟩ direction on Si{100} wafer, Ensell proposed a set of circular window feature as presented in Fig. 9 [104]. The etched pattern of circular windows results in square pyramidal structures enclosed by ⟨110⟩ directions as shown in Fig. 9b. The number of circles in the pre-etched pattern depends on the accuracy of the wafer flat (i.e., ⟨110⟩ direction). If the ⟨110⟩ direction lies within ±1° of the wafer flat, the circular patters should cover an arc of 2° on both side of the reference direction which is parallel to the wafer flat. At the same time, the diameter of the circles of the pre-etched patterns also depends on the accuracy with which the crystallographic direction needs to be identified. Although smaller circles will give better accuracy however it is difficult to investigate structures of small sizes under the mask aligner. Ensell fabricated the pre-etched pattern consisting of a series of 41 circular openings of diameter 75 μm and spaced 78.5 μm apart with an angular pitch of 0.1° on an arc of radius 45 mm. Forty-one circles require 20 circles on each side of the reference direction. Twenty circles with an angular pitch of 0.1° correspond to 2° on either side of the reference direction which is parallel to the flat. After patterning the geometry on diametrically opposite ends, etching is carried out in anisotropic etchant. Upon prolonged etching the circular openings takes the pyramidal shape as shown in Fig. 9b. The masking layer can be removed for better visualization. The misalignment of the edges of the neighbouring structures is used as a measure to determine the precise ⟨110⟩ directions. As shown in Fig. 9b, as one move towards the centre from any end, the base of the pyramid shifts to one direction. Moving down from top (Structure A), one sees that structures B is shifted (offset) by \( \Delta {\text{x}} \). The structures in B however are approximately aligned in a straight line. Moving further down to structure C, it can be seen that the base shift changes its direction. This implies that the precise ⟨110⟩ direction lies between structure A and C. If at all the shift \( \Delta {\text{x}} \) is same between A to B and B to C, then the ⟨110⟩ direction pass exactly through the central pyramid of structure B. This extent of offset is a measure of the misalignment with the ⟨110⟩ direction. The author proposed to inspect the etched patterns to find the three pyramids (structures B) with the closest alignment of edges to determine the crystal direction. After selecting the three pyramids whose edges are almost exactly aligned to each other, the central pyramid is considered to be aligned along the precise ⟨110⟩ direction. For an angular interval of \( \Delta {\emptyset } = 0.1^{{^\circ }} \), the minimum value of \( \Delta {\text{x}} \) for the given dimension of the pre-etched patterns is 0.07 μm and with every increase of 0.1° in \( \Delta {\emptyset } \), \( \Delta {\text{x}} \) increases by 0.14 μm. After finding the cavity across which the offset is minimum and changes its direction, the precise ⟨110⟩ direction can be identified based on the value of \( \Delta {\text{x}} \) of the neighbouring cavity as explained above. In order to increase the accuracy, the dimensions of the circles can be reduced in which case there would be lesser number of pyramids whose edges align precisely. This is a very simple technique both in terms of design and its implementation in finding the crystal direction. The author visually inspected the structures to determine the pyramids with almost exactly aligned edges. However, this is not the most accurate methodology as the submicron offset is not visible under the microscope. For most accurate results, the offset \( \Delta {\text{x}} \) should be measured for each structure to determine the one with minimum offset which would correspond to the precise ⟨110⟩ direction. However, this minimum offset length is of the order of submicron range which is difficult to measure on a normal mask aligner and thus it needs sophisticated equipment.
Vangbo and Backlund proposed an alignment fork as the pre-etched pattern to determine the ⟨110⟩ directions [102]. The property of symmetric undercutting across the ⟨110⟩ direction is exploited to determine the ⟨110⟩ directions. The pattern comprises of a set of three ridges tapered by small angles (\( \alpha , \beta \)) as shown schematically in Fig. 10. This set of structure is then repeated at an angular interval of 0.1˚. Using this pre-etched pattern, the ⟨110⟩ direction can be determined using two effects. The first is the tapered ridge effect. Upon etching, the dimension of the ridge will start to increase where it is narrowest and finally will lead to an oversized opening. Smaller angle of tapering ensures faster etching time to form the final undercut structure. If the ridges happen to be lying symmetrically across the ⟨110⟩ direction on the patterned wafer, then the undercut lengths of the two ridges will be same. In order to determine the ⟨110⟩ direction, the etched patterns are carefully inspected to find the pair of ridge which is symmetrically etched. This is one method to determine the precise ⟨110⟩ direction. Another method is by using the tapered groove effect. In this method, the mask pattern comprises of ridges which widen with a small angle. As etching progresses, the ridges takes the shape of grooves and the bottom plane continues to diminish and the final etched profile comprises of intersecting {111} planes. If the undercutting rate is low (i.e., near the ⟨110⟩ direction), the grooves will be narrower and more complete (i.e., the base will have a longer intersection). However, if undercutting rate is more (i.e., away from ⟨110⟩ direction) the groove will be wider with a longer length of incomplete portion of the base for the same etching time. In order to determine the correct ⟨110⟩ direction, the grooves can be inspected under a microscope to determine and compare the lengths of the incomplete portion of the formed grooves. For alignment of subsequent mask edges, a square window is added corresponding to each alignment fork. The entire set is now repeated at an angular interval of 0.1° with the centre point of rotation at the opposite side of the wafer. Additionally, a similar square is also patterned at the centre of rotation itself. Now, the subsequent mask is also added with two similar squares on each side. During subsequent alignment, one is overlapped with the square at the centre of rotation and the other is overlapped with the square corresponding to the fork where symmetric undercutting occurs. This is an easy method as the precise direction can be determined by a visual investigation of set of structures to find one with symmetric undercut. However, this can be a tedious task as the structures near the ⟨110⟩ direction can have similar undercut which may not be distinguishable. The source of error can be removed by measuring the undercut lengths to determine the symmetric undercut structures but it would require sophisticated equipment. At the same time, the varying undercut rate at different places on the wafer may also trick the human eye and give erroneous results. Similarly, determining the incomplete length of the base of the groove under a microscope will depend on the judgement of the user. This can lead to errors in determining the crystal direction.
Another method to determine the ⟨110⟩ direction on Si{100} wafer was proposed by Lai et al. where they used a series of rectangular and squared openings stacked on an arc of radius R which is greater than the diameter of the wafer [105]. These patterns were fabricated on one side of the wafer and a series of only square windows called auxiliary set on the diametrically opposite sides. These two set of patterns fabricated on opposite ends lie on an arc of concentric circles. The schematic diagram of the pre-etched patterns is shown in Fig. 11. The width of the squared geometry as well as the rectangular geometry is kept the same (W) because the vertical distance between the edges of the square and rectangular pattern after etching is a measure of the extent of misalignment. On prolonged etching, the rectangular and square openings take the shape of inverted pyramid. Depending on the degree of misalignment of the pattern edges with the ⟨110⟩ directions, the structures will become oversized. As a result, the difference in width of the rectangular and square opening (indicated by ∆y in Fig. 12) increases. Figure 12 shows the etched profile of the patterns on prolonged etching. From geometry \( \Delta {\text{y}} \) can be calculated using the following relation
At the precise ⟨110⟩ direction, δ is zero, thus the vertical distances between the edge of square and rectangular geometry (∆y) is almost zero. However, as we move away from the ⟨110⟩ direction, the vertical distance keeps on increasing and finally merges in the case of large deviation from the ⟨110⟩ direction as shown in Fig. 12. The pattern with minimum ∆y is selected and aligned with dimensionally similar pattern on the subsequent mask. The advantage of this method is that the structures far away from the precise ⟨110⟩ direction will get merged to each other, while the structures in the vicinity of ⟨110⟩ direction will remain un-merged. This will reduce the domain of investigation to find out the precise ⟨110⟩ direction. However from Eq. (3) we see that for a misalignment of 0.01°, the value of \( \Delta {\text{y}} \) is 0.18 μm when the rectangular opening is 1000 μm long and the distance (D) between rectangle and square is 16 μm. Using an optical microscope the particular structure with this minimum undercut can be located to be corresponding to the precise ⟨110⟩ direction. The next minimum undercut length for a misalignment of 0.02° is 0.35 μm. As a result it should be ensured that the microscope is capable of distinguishing between these submicron distances. However, for precise identification, these undercut lengths can be measured to determine the structure with minimum undercutting. However, measurement of such small distances firstly requires sophisticated equipment and secondly it makes the task tedious. Nevertheless, the benefit of these patterns is that it provides a longer length for aligning the mask pattern at one side of the wafer; however at the other side of the wafer the aligning length is only 16 μm. This makes the technique prone to theta error as well. At the same time etching 1000 × 15 μm opening would require a considerable time. Although, the undercut length can be increased by increasing either L or D (or both) but this is generally not preferred because first it would significantly increase the etching time and second, it would occupy more wafer space. We can however reduce the theta error by patterning the pre-etched feature on the auxiliary set as well. This would provide a longer length on diametrically opposite sides of the wafer for subsequent mask alignment and thus would reduce the error. While the etching time in this case will remain almost the same at in the previous case, but the usable space on the wafer is reduced.
In another study by Chang and Huang, a pre-etched pattern is utilized to determine the ⟨110⟩ directions on both Si{100} and Si{110} wafer [107]. Additionally they also carried out the statistical analysis to calculate the precision of determination of crystal directions. Their analysis suggested that the precision with which the crystal orientation can be determined does not solely depend on the resolution of the pre-etching mask patterns but is limited by the finite step resolution of the mask generator. As a result they optimized the dimensions and the tilt angle so as to limit the error due to finite step of the pattern generator within the design’s tolerance. However, here we discuss only the technique for precise determination of crystal direction. The proposed pre-etched pattern comprises of a series of trapezoids/ridge with the shorter sides parallel to each other and the longer sides inclined at different angles. The trapezoid with title angle of zero degree is designed to be parallel to the reference direction essentially the wafer flat (⟨110⟩ direction). The dimensions of the height and the smaller edges of the parallel sides of each trapezoid is fixed as H = 500 μm and W = 5 μm. The distance between consecutive trapezoids is also fixed as D = 17.5 μm. A symmetric set is patterned across the reference line as shown schematically in Fig. 13. Upon etching, the trapezoidal opening takes the shape of rectangular grooves (Fig. 13b). The undercutting occurs due to misalignment of mask edges and the final structure is defined by {111} planes. Due to the undercutting, the distance D reduces and finally becomes zero at a certain index T as shown in Fig. 13c. Similarly, other side of the reference direction also consists of a structure with index T′ where D becomes zero. In order to determine the misaligned angle, the following relation is used
where, Δψ is defined by ψi − ψi−1 which is 0.0125°. A positive value of ψ M implies that the crystal direction lies in the region of positive tilt angle ψ i while a negative value of ψ M implies that the crystal direction lies in the region of negative tilt angle ψ iʹ. In order to align the subsequent mask precisely along the crystal orientation, an alignment accessory pattern consisting of a series of circular opening is fabricated on an arc of radius R with centre on the opposite side of the wafer where another circle is fabricated as shown in Fig. 14. The angular pitch of the circles on the alignment accessory pattern is the same as that of the pre-etched pattern. Additional structures called dial structures are also fabricated beside each ridge to indicate the index of the structure. After etching, the pre-etched pattern takes the shape of rectangular groove and the circles on the alignment accessory pattern as well as the circle at the other end of the wafer takes the shape of square cavity. Then, the index of the ridge corresponding to T and T′ as discussed earlier are obtained using the dial structure. Subsequently, the mis-orientation angle (ψ M ) is calculated. Now, the square opening corresponding to this mis-orientation angle is selected from the alignment accessory pattern for subsequent alignment of mask. The subsequent mask which comprises of two squares: one for aligning the fabricated square on the other end of the wafer and the other for aligning the corresponding square from the alignment accessory pattern is then aligned as shown in Fig. 14. In cases where the wafer flat is perfectly aligned along the ⟨110⟩ direction, the index of T and T′ will be same. This will make the mis-orientation angle ψ M = 0. The square opening corresponding to this mis-orientation angle on the alignment accessory pattern is the one beside the 0th ridge which is essentially parallel to the wafer flat.
This method can also be used to determine ⟨110⟩ directions on Si{110} wafer. The etched geometry in case of Si{110} wafer is shown in Fig. 13d. This methodology does not require the measurement of small undercut lengths for precise determination of crystal directions. However distinguishing the target ridge from the set of etched ridge is a difficult task. At the same time the etching time increases due to long structures. Additionally it takes a lot of usable wafer space due to long length of the patterns which is itself complex in designing. Overall this methodology to determine the crystal direction is complicated as compared to several other simple methodologies which have been proposed.
The relative etch rates of silicon planes such as {100} and {110} can be altered significantly by the addition of a small amount of surfactant in high concentration TMAH (e.g. 20–25 wt%) [1, 48–50, 111–119]. In surfactant added 25 wt% TMAH, the etch rate of {110} planes is reduced to a considerably low level, while that of {100} plane remains almost unaltered. This property of surfactant added TMAH is used to fabricate 45° micromirrors which are used in optical MEMS to provide 90° out-of-plane reflection as illustrated in Fig. 15 [120–122]. In order to ensure that the reflected beam is exactly perpendicular to the incoming beam, it is vital to ensure that the mirror walls are precisely at an angle of 45˚. On Si{001} wafer, {011} plane oriented at an angle of 45˚ to the wafer surface appear at the ⟨100⟩ direction. In order to achieve smooth and exactly 45˚ sidewall, the mask edges must be precisely aligned along ⟨100⟩ direction on Si{001} surface. Earlier attempt at determining the ⟨100⟩ direction on Si{100} wafer was done by Chen et al. [108]. They exploited the phenomenon of undercutting at the contact line of the masking layer and the silicon substrate as a tool to determine the crystallographic directions. The pre-etched pattern comprises of 21 circles of 50 μm diameter fabricated on an arc of 43 mm. The angular pitch of the circles is 0.1˚. Figure 16 shows the schematic diagram of the proposed patterns. Upon etching, the circular opening starts to distort. As the etching continues further the corners of adjacent squares tends to merge with each other. The authors observed the number of such merging to determine the precise direction. In the cases where there is only one merging point, the precise ⟨100⟩ direction lies through the merged point. If the number of merged corners is even, then the precise direction passes through the center of the central square and if the number of merged structures is odd, then the ⟨100⟩ direction passes through the central merged point. In this technique, the number of merged points may depend on the etching time. This technique does not require any measurement to determine the undercut lengths and the location of the precise direction can be done by simply observing the number of merging of corners. However, this method is correct under the assumption that the undercutting is uniform for all the structures on the wafer. In practical applications, the undercutting varies for structure to structure even on the same wafer [123, 124]. As a result the reproducibility and correctness of this methodology is questionable as the number of merging can vary depending on the etch rate and can lead to error in the determination of precise crystallographic directions. At the same time, for subsequent alignment, one has to orient the wafer so as to align the mask edge to either small corner points or diagonal of the formed square. Aligning along both these is a tough task as well as prone to error owing to their small size.
Recently, Sajal et al. proposed a self-aligning technique to precisely identify the ⟨100⟩ directions on Si{100} wafer [109]. The pre-etched pattern comprises of four circles of 100 μm diameter each, fabricated with a spacing of 43.5, 44.5 and 45.5 μm. This differential spacing is incorporated in order to overcome the possibility of merging of notching due to overetching. The set of four circles is repeated at an angular interval of 0.17° on both side of the reference line which is at an angle of 45° to the wafer flat as shown in Fig. 17. The center of all the four circles lies on a straight line passing through the center of the wafer. The similar set of geometry is also patterned on diametrically opposite end of the wafer to reduce the theta error while subsequent aligning. The patterns are etched in an anisotropic etchant and the circular opening takes the shape of square V-groove with {111} sidewalls as explained in the "Background" section. The optical image of the etched pattern is shown in Fig. 18. Near the perfectly aligned ⟨100⟩ direction, the radial diagonal of all the four squares lies on a straight line and the notch of the squares align perfectly to each other. As one move away from the precise ⟨100⟩ direction, the notches starts to misalign and are no longer aligned to each other in a straight line as shown in Fig. 18. The extent of misalignment depends on the actual deviation from the precise ⟨100⟩ direction. The misalignment of the notches also changes its direction across the ⟨100⟩ direction, this also reduced the domain over which one needs to do a careful inspection to find the precise direction. As a result, with a visual inspection under a simple microscope the precise direction can be located without any need of measuring the undercut length. Thus, this is a measurement free technique to determine the crystallographic directions. The aligning of subsequent mask can be done by pre-fabricating a thin line at 45˚ to the ⟨110⟩ direction on diametrically opposite ends of the subsequent mask. This line can then be aligned along the self-aligned patterns which constitutes the ⟨100⟩ direction on both sides of the wafer. The set of four circles which provides a longer length for the subsequent alignment of mask edges ensures reduction in the theta error.
Determination of crystal directions on Si{110} wafer
On Si{110} wafer there are primarily two principal directions namely the ⟨110⟩ and ⟨112⟩ directions, which are useful owing to the appearance of slanted and vertical {111} planes at these two directions, respectively. The appearance of vertical {111} sidewalls makes Si{110} wafer indispensable to fabricate high aspect ratio microchannels and gratings using wet anisotropic etching for different applications [19, 76]. There have been a few attempts to identify the above mentioned principal directions on Si{110} wafer.
In earlier attempts to precisely identify the ⟨110⟩ direction, Ciarlo fabricated a fan like structure with rectangular openings of sides 8 μm by 3 mm with longer length parallel to the wafer flat (⟨110⟩ direction) [106]. This structure is then repeated at an angular interval of 0.1°. The obtained pattern is similar to that as shown in Fig. 11, however without the square adjacent to each rectangle. Prolonged etching leads to undercutting at the mask edges due to the misalignment of the edges with the ⟨110⟩ direction. The structure with the minimum undercut would be the least misaligned with the precise ⟨110⟩ direction. This method again deals with the disadvantage of selecting structures with small undercut lengths and increased etching time and using more wafer space etc.
In another method, James et al. used just one circle of diameter 1 mm as pre-etched pattern, which formed a hexahedron on prolonged etching [76]. The subsequent mask comprising of the structures to be fabricated also comprised of a dimensionally similar hexagon (alignment feature) which was formed after etching. The edges of the hexagon on the mask were then aligned along the edges of the hexahedron formed by wet-etching on the wafer as shown in Fig. 19. This way all the other structures to be fabricated could get aligned to the correct crystallographic direction. This method is also a very simple method to determine the ⟨110⟩ and ⟨112⟩ directions (given by the sides of the hexahedron) and it also requires less etching and processing time. However it again has the disadvantage of relying on aligning only along one side of the wafer making it prone to theta error.
Tseng and Chang attempted to determine the ⟨100⟩ directions on Si{110} wafer employing the hexagonal shape of a circular openings obtained after etching as illustrated in Fig. 20 [103]. In their technique, they fabricated circular openings of diameter 153, 74 and 35 μm with centre to centre distance of 192, 96 and 48 μm on an arc of radius 48.9 mm at 55 and −125° to the ⟨111⟩ directions. After etching, all the circular openings take the shape of hexagonal groove as explained in the "Background" section. Figures 21 and 22 show the SEM images of the fabricated structures. From the fabricated structures, that particular hexagonal structure is selected across which the direction of lateral deviation of corners changes its direction. The relative positions of the corners of the neighbouring hexagons to this hexagon is used to determine the precise ⟨100⟩ direction. Figure 20 depicts schematically the top view of the etched profile of hexagonal grooves. It can be seen that there are three possible cases of the orientation of the corners of the adjacent hexagons. One of the possible orientation is that the corners of adjacent hexagons are precisely aligned to each other and the neighbouring hexagons have corners deviated in opposite directions. In this case the precise ⟨100⟩ direction will lie perfectly in between the corners of the two aligning hexagons as presented in Fig. 20i. The second case is that the corners of hexagons on either side are deviated in opposite directions but with equal magnitude. In this case the precise ⟨100⟩ direction will pass exactly through the centre of the hexagon as illustrated in Fig. 20ii. The third case is the intermediate case where the precise ⟨100⟩ direction will pass through a point in between the two cases mentioned above depending on the magnitude of lateral deviation as shown in Fig. 20iii. Using this technique, the ⟨100⟩ directions on Si{110} wafer can be determined. This technique has the advantage of being measurement free. However for subsequent alignment, one has to orient the wafer so as to align the mask edge with respect to two corner points unlike long edges in other cases. This task becomes even more difficult when the 35 μm circles are used as reference for better accuracy where high magnification microscope is required to see the deviation. Other circles of larger diameter help in reducing the domain of investigation. However, it increases the etching time and occupies more usable space.
Recently, Sajal et al. presented an improvised measurement free technique to determine the ⟨110⟩ direction on Si{110} wafer [110]. A series of circular openings of diameter 100 μm were fabricated on four concentric arcs. Upon etching the circular openings took the shape of hexagonal grooves as shown in the optical image in Fig. 23. Near the precise ⟨110⟩ direction, the notches of all the four radial hexagons aligns to each other in a straight line while getting misaligned to each other at directions away from ⟨110⟩. The zoomed in optical images presented in Fig. 24 clearly describe the self-alignment nature of the hexagons near the precise ⟨110⟩ directions. This method is completely based on visual inspection and does not require any measurement and therefore can be employed using only an optical microscope. The large misalignment at directions away from ⟨110⟩ direction reduces the domain over which a closer inspection would be required to determine the precise ⟨110⟩ direction. This technique is simple, robust and accurate. Additionally, it provides a longer length for aligning the edges of subsequent mask patterns. This method overcomes the shortcomings of the previous method where the mask edges needed to be aligned with respect to two corners. In this technique, the pre-fabricated reference line at the wafer end on the mask can be aligned with the notches of four circles along their diagonals. This not only reduces the efforts in alignment of subsequent mask, but also reduces the associated errors.
Summary
In this review article we have discussed all the techniques available till date to identify the crystallographic directions on Si{100} and Si{110} wafers. We tabulate all the techniques for an easy reference for the readers.
Authors | Wafer orientation | Structure | Alignment technique | Property of the method |
---|---|---|---|---|
James et al. [76] | Si{100} and Si{110} | Cleaved edge | Cleave along the crystallographic direction | Space requirement This method requires scribed lines and therefore full wafer cannot be used for fabrication Measurement required No Accuracy Not accurate Requires sophisticated equipment No Remarks Accuracy depends on the skills of the handler and the precision of the scribed line |
Ensell [104] | Si{100} | Circular openings on an arc | After etching, choose structures with minimum distance between the edges of adjacent structures | Space requirement Less Measurement required Yes for better accuracy Accuracy 0.1˚ Requires sophisticated equipment Yes if measurement is needed Remarks Simple technique |
Vangbo and Backlund [102] | Si{100} and Si{110} | Alignment fork | After etching, inspect for structures with symmetric undercutting | Space requirement Less Measurement required No Accuracy 0.05˚ provided undercutting is constant Requires sophisticated equipment No Remarks Complex in design, requires visual inspection to find symmetric undercut structures, prone to error due to varying undercut rate |
Chang and Huang [107] | Si{100} and Si{110} | Tapered ridges | Look for merged structure (target ridge) to determine the misalignment | Space requirement More Measurement required No Accuracy 0.05˚ (100), 0.03˚ (110) Requires sophisticated equipment No Remarks Complex design pattern, tedious method |
Lai et al. [105] | Si{100} | Rectangular and squared openings on an arc | After etching choose pattern with minimum undercut | Space requirement More Measurement required Yes for better accuracy Accuracy Prone to theta error, can be made more accurate by patterning the same structures on auxiliary sets as well Requires sophisticated equipment Yes if measurement is needed Remarks Merging of structure occurs at directions away from ⟨110⟩. As a result the domain of inspection reduces to unmerged structures |
Chen et al. [109] | Si{100} | Circular openings on an arc | After etching the corners of the formed squares merge due to undercutting. The number of such merged corners decide the position of ⟨100⟩ direction | Space requirement Less Measurement required None Accuracy Good provided undercutting is constant Requires sophisticated equipment No Remarks Due to varying undercutting rate at different structure, this method may give inaccurate results, difficult to align subsequent mask |
Sajal et al. [110] | Si{100} | Circular openings on concentric arcs | After etching, the notches of the formed square cavities aligns at precise direction | Space requirement More Measurement required None Accuracy Good Requires sophisticated equipment No Remarks Self aligning methodology makes the crystallographic direction appear obvious, longer length for aligning subsequent mask edges reduces theta error |
Ciarlo [106] | Si{110} | Rectangular openings on an arc | After etching choose the rectangle with minimum undercutting | Space requirement More Measurement required Yes for better accuracy Accuracy Good Requires sophisticated equipment Yes if measurement is needed Remarks Simple technique, but requires longer etching time |
James et al. [76] | Si{110} | One circular opening of diameter 1 mm | Aligning of formed hexagon with a dimensionally similar hexagon on subsequent mask | Space requirement Less Measurement required None Accuracy Good Requires sophisticated equipment NO Remarks Very simple, requires very less etching time, uses less space, prone to theta error as aligning of mask patterns is done only on one side of the wafer |
Tseng and Chang [103] | Si{110} | Circular openings of various diameters on concentric arcs | Alignment of notches of adjacent hexagons | Space requirement More Measurement required None Accuracy Good, but alignment with respect to corners makes it prone to error Requires sophisticated equipment High magnification microscope to visualise corner deviation of smaller circles for better accuracy Remarks Longer etching time, alignment of subsequent mask is done with respect to corners |
Sajal et al. [110] | Si{110} | Circular openings on concentric arcs | After etching, the notches of the formed hexagons aligns precisely to each other at the precise ⟨110⟩ direction | Space requirement More Measurement required None Accuracy Good Requires sophisticated equipment No Remarks Crystal direction becomes obvious as the notches self-aligns itself at the precise direction, longer length for subsequent alignment of prefabricated line on subsequent mask |
Conclusions
This review article is aimed at aggregating at one place, the different techniques proposed till date to precisely determine the crystallographic directions on Si{100} and Si{110} wafers. Different techniques including the cleaved-edge method and the use of pre-etched patterns to determine the crystal directions are discussed. Different geometric patterns are analysed based on their applicability on either Si{100} or Si{110} wafer. The basic technique to align the mask edges along the crystal directions is to use the wafer flat as the reference. However, given the uncertainty in the determination of wafer flat, it is not enough when high dimensional accuracy is desired. As a result alternate methodologies have been developed. One of them is by fabricating structures using the wafer flat as the reference and then using the edges of the structure with minimum undercut length as the accurate crystal direction. However, measurement of such undercut lengths which are very small in some cases is a tedious task as well as requires sophisticated equipment. To overcome these shortcomings, other techniques have been proposed which do not require the measurement of any kind. One of them is to by choosing structures whose corners merge after etching, another by choosing the structure with symmetric undercut etc. While these techniques are measurement free, still it comes with an associated errors due to varying undercut rate at different places on wafers, the difficulty in determining the target structures where undercutting is symmetric, etc. More recently, self-aligning techniques have been developed which makes the crystal direction appear obvious by virtue of the self-alignment nature of the structures. These techniques overcome the shortcomings of all the previous techniques in terms of being measurement free, robustness, simplicity in implementation and reduced efforts required for identifying the direction. These techniques can be employed without using any sophisticated equipment.
References
Ashok A, Pal P (2015) Silicon micromachining in 25 wt% TMAH without and with surfactant concentrations ranging from ppb to ppm. Microsyst Technol 1–8. doi:10.1007/s00542-015-2699-9
Lee S, Park S, Cho D (1999) The surface/bulk micromachining (SBM) process: a new method for fabricating released microelectromechanical systems in single crystal silicon. J Microelectromech Syst 8:409–416
Frühauf J (2005) Shape and functional elements of the bulk silicon microtechnique: a manual of wet-etched silicon structures. Springer, Berlin
Pal P, Chandra S (2004) Bulk-micromachined structures inside anisotropically etched cavities. Smart Mater Struct 13:1424–1429
Tellier CR, Charbonnieras AR (2003) Characterization of the anisotropic chemical attack of (hhl) silicon plates in a TMAH 25 wt% solution: micromachining and adequacy of the dissolution slowness surface. Sens Actuators A Phys 105:62–75
Schnakenberg U, Benecke W, Lochel B (1990) NH4OH-based etchant for silicon micromachining. Sens Actuators A Phys 23:1031–1035
Zubel I, Kramkowska M (2009) Possibilities of extension of 3D shapes by bulk micromachining of different Si (hkl) substrates. J Micromech Microeng 15:485–493
Pal P, Sato K (2015) A comprehensive review on convex and concave corners in silicon bulk micromachining based on anisotropic wet chemical etching. Micro Nano Syst Lett 3:1–42
Gad-el-Hak M (ed) (2002) The MEMS handbook. CRC Press LLC, Boca Raton
Elwenspoek M, Jansen H (1998) Silicon micromachining. Cambridge University Press, UK
Takahata K (2013) Advances in micro/nano electromechanical systems and fabrication technologies. InTech, Rijeka
Lindroos V, Tilli M, Lehto A, Motooka T (2010) Handbook of silicon based MEMS materials and technologies. William Andrew Publishing, Norwich
Hsu TR (2003) MEMS & microsystems: design and manufacture. Tata McGraw-Hill Publishing Company Ltd, New Delhi
Madou MJ (2002) Fundamentals of microfabrication: the science of miniaturization, 2nd edn. CRC Press, Boca Raton
Varadan VK, Vinoy KJ, Gopalakrishnan S (2006) Smart material systems and MEMS: design and development methodologies. Wiley, New York
Lang W (1996) Silicon microstructuring technology. Mater Sci Eng R Rep 17:1–55
Bustillo JM, Howe RT, Muller RS (1998) Surface micromachining for microelectromechanical systems. IEEE Proc 86:1552–1574
Bhatt V, Pal P, Chandra S (2005) Feasibility study of RF sputtered ZnO film for surface micromachining. Surf Coat Technol 198:304–308
Kovacs GT, Maluf NI, Petersen KE (1998) Bulk micromachining of silicon. IEEE Proc 86:1536–1551
Petersen KE (1982) Silicon as a mechanical material. IEEE Proc 70:420–457
Jansen H, Gardeniers H, Boer MD, Elwenspoek M, Fluitman J (1996) A survey on the reactive ion etching of silicon in microtechnology. J Micromech Microeng 6:14–28
Oehrlein GS (1990) Reactive ion etching. In: Rossnagel SM, Westwood WD, Haber JJ (eds) Handbook of plasma processing technology-fundamentals, etching, deposition, and surface interactions. Noyes, Park Ridge
Coburn JW, Winters HF (1979) Plasma etching-a discussion of mechanisms. J Vaccum Sci Technol 16:391–403
Larmer F, Schilp P (1994) Method of anisotropically etching silicon. German Patent DE 4(241):045
Jiang E, Keating A, Martyniuk M, Prasad K, Faraone L, Jiang JM (2012) Characterization of low-temperature bulk micromachining of silicon using an SF6/O2 inductively coupled plasma. J Micromech Microeng 22:095005
Hynes AM, Ashraf H, Bhardwaj JK, Hopkins J, Johnston I, Shepherd JN (1999) Recent advances in silicon etching for MEMS using the ASE process. Sens Actuators A Phys 74:13–17
Teng J, Prewett PD (2005) Focused ion beam fabrication of thermally actuated bimorph cantilevers. Sens Actuators A Phys 123–124:608–613
Walker CK, Narayanan G, Knoepfle H, Capara J, Glenn J, Hungerford A, Bloomstein TM, Palmacci ST, Stern MB, Curtin JE (1997) Laser micromachining of silicon: a new technique for fabricating high quality terahertz waveguide components. In: Proceedings of 8th international symposium on space terahertz technology, Harvard University, p 358
Schwartz B, Robbins H (1976) Chemical etching of silicon. J Electrochem Soc 123(12):1903–1909
Zandi K, Arzi E, Izadi N, Mohajerzadeh S, Haji S, Abdi Y, Asl Soleimani E (2006) Study of bulk micromachining for ⟨100⟩ silicon. Eur Phys J Appl Phys 35:7–12
Lee DB (1969) Anisotropic etching of silicon. J Appl Phys 40:4569–4575
Bean KE (1978) Anisotropic etching of silicon. IEEE Trans Electron Devices 25:1185–1193
Seidel H, Csepregi L, Heuberger A, Baumgartel H (1990) Anisotropic etching of crystalline silicon in alkaline solutions I: orientation dependence and behavior of passivation layers. J Electrochem Soc 137(11):3612–3626
Sato K, Shikida M, Matsushima Y, Yamashiro T, Asaumi K, Iriye Y, Yamamoto M (1998) Characterization of orientation-dependent etching properties of single-crystal silicon: effects of KOH concentration. Sens Actuators A Phys 61:87–93
Dutta S, Imran Md, Kumar P, Pal R, Datta P, Chatterjee R (2011) Comparison of etch characteristics of KOH, TMAH and EDP for bulk micromachining of silicon (110). Microsyst Technol 17:1621–1628
Powell O, Harrison HB (2001) Anisotropic etching of 100 and 110 planes in (100) silicon. J Micromech Microeng 11:217–220
Tanaka H, Yamashita S, Abe Y, Shikida M, Sato K (2004) Fast etching of silicon with a smooth surface in high temperature ranges near the boiling point of KOH solution. Sens Actuators A Phys 114:516–520
Matsuoka M, Yoshida Y, Moronuki M (1992) Preparation of silicon thin diaphragms free from micropyramids using anisotropic etching in KOH solution. J Chem Eng 25:735–740
Baryeka I, Zubel I (1995) Silicon anisotropic etching in KOH-isopropanol etchant. Sens Actuators A Phys 48:229–238
Shikida M, Sato K, Tokoro K, Uchikawa D (2000) Differences in anisotropic etching properties of KOH and TMAH solutions. Sens Actuators A Phys 80:179–188
Backlund Y, Rosengren L (1992) New shapes in (100) Si using KOH and EDP etches. J Micromech Microeng 27:5–9
Pal P, Ashok A, Haldar S, Xing Y, Sato K (2015) Anisotropic etching in low concentration KOH: effects of surfactant concentration. Micro Nano Lett 10(4):224–228
Tanaka H, Cheng D, Shikida M, Sato K (2006) Characterization of anisotropic wet etching properties of single crystal silicon: effects of ppb-level of Cu and Pb in KOH solution. Sens Actuators A Phys 128:125–131
Tabata O, Asahi R, Funabashi H, Shimaoka K, Sugiyama S (1992) Anisotropic etching of silicon in TMAH solutions. Sens Actuators A Phys 34(1):51–57
Tang B, Shikida M, Sato K, Pal P, Amakawa H, Hida H, Fukuzawa K (2010) Study of surfactant-added TMAH for the applications in DRIE + wet etching based micromachining. J Micromech Microeng 20:065008
Mukhiya R, Bagolini A, Margesin B, Zen M, Kal S (2006) <100 > bar corner compensation for CMOS compatible anisotropic TMAH etching. J Micromech Microeng 16:2458–2462
Sato K, Shikida M, Yamashiro T, Asaumi K, Iriye Y, Yamamoto M (1999) Anisotropic etching rates of single-crystal silicon for TMAH water solution as a function of crystallographic orientation. Sens Actuators A Phys 73:131–137
Pal P, Sato K, Gosalvez MA, Tang B, Hida H, Shikida M (2010) Fabrication of novel microstructures based on orientation dependent adsorption of surfactant molecules in TMAH solution. J Micromech Microeng 21(1):015008
Pal P, Sato K (2010) Fabrication methods based on wet etching process for the realization of silicon MEMS structures with new shapes. Microsyst Technol 16(7):1165–1174
Gosalvez MA, Tang B, Pal P, Sato K, Kimura Y, Ishibashi K (2009) Orientation and concentration dependent surfactant adsorption on silicon in aqueous alkaline solutions: explaining the changes in the etch rate, roughness and undercutting for MEMS applications. J Micromech Microeng 19(12):125011
Steinsland E, Finstad T, Hanneborg A (2000) Etch rates of (100), (111), and (110) single-crystal silicon in TMAH measured in situ by laser reflectance interferometry. Sens Actuators A Phys 86:73–80
Tang B, Yao MQ, Tan G, Pal P, Sato K, Su W (2014) Smoothness control of wet etched Si{100} surfaces in TMAH + Triton. Key Eng Mater 609:536–541
Shikida M, Masuda T, Uchikawa D, Sato K (2001) Surface roughness of single-crystal silicon etched by TMAH solution. Sens Actuators A Phys 90(3):223–231
Tang B, Sato K, Zhang D, Cheng Y (2014) Fast Si (100) etching with a smooth surface near the boiling temperature in surfactant modified tetramethylammonium hydroxide solutions. Micro Nano Lett 9(9):582–584
Gosalvez MA, Pal P, Ferrando N, Hida H, Sato K (2011) Experimental procurement of the complete 3D etch rate distribution of Si in anisotropic etchants based on vertically micromachined wagon wheel samples. J Micromech Microeng 21:125007
Tang B, Pal P, Gosalvez MA, Shikida M, Sato K, Amakawa H, Itoh S (2009) Ellipsometry study of the adsorbed surfactant thickness on Si{110} and Si{100} and the effect of pre-adsorbed surfactant layer on etching characteristics in TMAH. Sens Actuators A Phys 156:334–341
Chung GS (2005) Anisotropic etching characteristics of Si in tetramethylammonium hydroxide: isopropyl alcohol: pyrazine solutions. J Korean Phys Soc 46(5):1152–1156
Choi WK, Thong JTL, Luo P, Tan CM, Chua TH, Bai Y (1998) Characterisation of pyramid formation arising from the TMAH etching of silicon. Sens Actuators A Phys 71:238–243
Resnik D, Vrtacnik D, Aljancic U, Amon S (2003) Effective roughness reduction of 100 and 311 planes in anisotropic etching of 100 silicon in 5 % TMAH. J Micromech Microeng 13:26–34
Sakaino K, Adachi S (2001) Study of Si(100) surfaces etched in TMAH solution. Sens Actuators A Phys 88:71–78
Pal P, Sato K, Gosalvez MA (2012) Etched profile control in anisotropic etching of silicon by TMAH + Triton. J Micromech Microeng 22(6):065013
Resnik D, Vrtacnik D, Aljancic U, Amon S (2000) Wet etching of silicon structures bounded by (311) sidewalls. Microelectron Eng 51:555–566
Holke A, Henderson HT (1999) Ultra-deep anisotropic etching of (110) silicon. J Micromech Microeng 9:51–57
Thong JTL, Choi WK, Chong CW (1997) TMAH etching of silicon and the interaction of etching parameters. Sens Actuators A Phys 63(3):243–249
Seidel H, Csepregi L, Heuberger A, Baumgartel H (1990) Anisotropic etching of crystalline silicon in alkaline solutions II: influence of dopants. J Electrochem Soc 137:3626–3632
Wu MP, Wu QH, Ko WH (1986) A study on deep etching of silicon using ethylenediamine-pyrocatechol-water. Sens Actuators A Phys 9:333–343
Reisman A, Berkenblit M, Chan SA, Kaufmann FB, Green DC (1979) The controlled etching of silicon in catalyzed ethylene-diamine-pyrochatechol-water solutions. J Electrochem Soc Solid-State Sci Technol 126:1406–1415
Kern W (1978) Chemical etching of silicon, germanium, gallium arsenide, and gallium phosphide. RCA Rev 39:278–307
Declercq MJ, Gerzberg L, Meindl JD (1975) Optimization of the hidrazine-water solution for anisotropic etching of silicon in integrated circuit technology. J Electrochem Soc Solid State Sci 122:545–552
Schnakenberg U, Benecke W, Lochel B (1990) NH4OH-based etchant for silicon micromachining. Sens Actuators A Phys 23:1031–1035
Clarck LD, Lund JL, Edell DJ (1988) Cesium hydroxide (CsOH): a useful etchant for micromachining silicon. In: Tech. digest, IEEE solid state sensor and actuator workshop (Hilton Head Island, SC), pp 5–8
Pal P, Singh SS (2013) A simple and robust model to explain convex corner undercutting in wet bulk micromachining. Micro Nano Syst Lett 1(1):1–6
Pal P, Singh SS (2013) A new model for the etching characteristics of corners formed by Si{111} planes on Si{110} wafer surface. Engineering 5(11):1–8
Kandlikar SG, Grande WJ (2003) Evolution of microchannel flow passages-thermohydrolic performance and fabrication technology. Heat Transf Eng 24:3–17
Koo JM, Jian L, Zhang L, Kenny T, Santiago J, Goodson K (2001) Modeling of two-phase microchannel heatsinks for VLSI chips In: 14th IEEE international conference on micro electro mechanical systems, MEMS, IEEE, Interlaken, pp 422–426
James TD, Parish G, Winchester KJ, Musca CA (2006) A crystallographic alignment method in silicon for deep, long microchannel fabrication. J Micromech Microeng 16(10):2177
Pal P, Sato K (2009) Various shapes of silicon freestanding microfluidic channels and microstructures in one step lithography. J Micromech Microeng 19(5):055003
Abedinov N, Grabiec P, Gotszalk T, Tz Ivanov, Voigt J, Rangelow IW (2001) Micromachined piezoresistive cantilever array with integrated resistive microheater for calorimetry and mass detection. J Vaccum Sci Technol A 19:2884–2888
Saya D, Belaubre P, Mathieu F, Lagrange D, Pourciel JB, Bergaud C (2005) Si-piezoresistive microcantilevers for highly integrated parallel force detection applications. Sensors Actuators A Phys 123:23–29
Lee JH, Hwang KS, Park J, Yoon KH, Yoon DS, Kim TS (2005) Immunoassay of prostate-specific antigen (PSA) using resonant frequency shift of piezoelectric nanomechanical microcantilever. Biosens Bioelectron 20:2157–2162
Battiston FM, Ramseyer JP, Lang HP, Baller MK, Gerber C, Gimzewski JK, Meyer E, Guntherodt HJ (2001) A chemical sensor based on a microfabricated cantilever array with simultaneous resonance frequency and bending readout. Sens Actuators B Chem 77:122–131
Wee KW, Kang GY, Park J, Kang JY, Yoon DS, Parkb JH, Kim TS (2005) Novel electrical detection of label-free disease marker proteins using piezoresistive self-sensing micro-cantilevers. Biosens Bioelectron 20:1932–1938
Pruitt BL, Kenny TW (2003) Piezoresistive cantileveres and measurement systems for characterizing low force electrical contacts. Sens Actuators A Phys 104:68–77
Baller MK, Lang HP, Fritz J, Gerber C, Gimzewski JK, Drechsler U, Rothuizen H, Despont M, Vettiger P, Battiston FM, Ramseyer JP (2000) A cantilever array-based artificial nose. Ultramicroscopy 82(1):1–9
Pal P, Sato K (2009) Suspended Si microstructures over controlled depth micromachined cavities for MEMS based sensing devices. Sens Lett 7:11–16
Zhang Y, Tadigadapa S (2004) Calorimetric biosensors with integrated microfluidic channels. Biosens Bioelectron 19:1733–1743
Winter W, Hohne GWH (2003) Chip-calorimeter for small samples. Thermochim Acta 403:43–53
Van Herwaarden AW, Van Duyn DC, Van Oudheusden BW, Sarro PM (1989) Integrated thermopile sensors. Sens Actuators A Phys 22:621–630
Sarro PM, van Hexwaarden AW, van der Vlist W (1994) A silicon-silicon nitride membrane fabrication process for smart thermal sensors. Sens Actuators A Phys 42(1):666–671
Wang CC, Gogoi BP, Monk DJ, Mastrangelo CH (2000) Contamination-insensitive differential capacitive pressure sensors. IEEE J Microelectromech Syst 9:538–543
Tiren J, Tenerz L, Hok B (1989) A batch-fabricated non-reverse valve with cantilever beam manufactured by micromachining of silicon. Sens Actuators 18:389–396
Oh KW, Ahn CH (2006) A review of microvalves. J Micromech Microeng 16(5):R13–R39
Bien DCS, Mitchell SJN, Gamble HS (2003) Fabrication and characterization of a micromachined passive valve. J Micromech Microeng 13:557–562
Au AK, Lai H, Utela BR, Folch A (2011) Microvalves and Micropumps for BioMEMS. Micromachines 2:179–220
Tsai NC, Sue CY (2007) Review of MEMS-based drug delivery and dosing systems. Sens Actuators A Phys 134:555–564
Nisar A, Afzulpurkar N, Mahaisavariya B, Tuantranont A (2008) MEMS-based micropumps in drug delivery and biomedical applications. Sens Actuators B Chem 130:917–942
Laser DJ, Santiago JG (2004) A review of micropumps. J Micromech Microeng 14:35–64
Woias P (2005) Micropumps-past, progress and future prospects. Sens Actuators B Chem 105:28–38
Sharma J, Krishanapura N, Das GA (2012) Fabrication of low pull-in voltage RF MEMS switches on glass substrate in recessed CPW configuration for V-band application. J Micromech Microeng 22:025001
Pal P, Sato K, Chandra S (2007) Fabrication techniques of convex corners in (100)-silicon wafer using bulk micromachining: a review. J Micromech Microeng 17:R11–R13
Gravesen P, Branebjerg J, Jensen OS (1993) Microfluidics—a review. J Mioromech Microeng 3:168–182
Vangbo M, Backlund Y (1996) Precise mask alignment to the crystallographic orientation of silicon wafers using wet anisotropic etching. J Micromech Microeng 6(2):279
Tseng FG, Chang KC (2002) Precise [100] crystal orientation determination on ⟨110⟩-oriented silicon wafers. J Micromech Microeng 13(1):47
Ensell G (1996) Alignment of mask patterns to crystal orientation. Sens Actuators A Phys 3(1):345–348
Lai JM, Chieng WH, Huang YC (1998) Precision alignment of mask etching with respect to crystal orientation. J Micromech Microeng 8(4):327
Ciarlo DR (1992) A latching accelerometer fabricated by the anisotropic etching of (110) oriented silicon wafers. J Micromech Microeng 2(1):10
Chang WH, Huang YC (2005) A new pre-etching pattern to determine ⟨110⟩ crystallographic orientation on both (100) and (110) silicon wafers. Microsyst Technol 11(2–3):117–128
Chen PH, Hsieh CM, Peng HY, Chyu MK (2000) Precise mask alignment design to crystal orientation of (100) silicon wafer using wet anisotropic etching. In: Micromachining and microfabrication international society for optics and photonics, pp 462–466
Singh SS, Veerla S, Sharma V, Pandey AK, Pal P (2016) Precise identification of ⟨100⟩ directions on Si 001 wafer using a novel self-aligning pre-etched technique. J Micromech Microeng 26(2):025012
Singh SS, Avvuru NV, Veerla S, Pandey AK, Pal P (2016) A measurement free pre-etched pattern to identify the ⟨110⟩ directions on Si{110} wafer. Microsys Technol pp 1–7. doi:10.1007/s00542-016-2984-2
Pal P, Gosalvez MA, Sato K (2010) Silicon micromachining based on surfactant-added tetramethyl ammonium hydroxide: etching mechanism and advanced application. Japan J Appl Phys 49:056702
Gosalvez MA, Pal P, Tang B, Sato K (2010) Atomistic mechanism for the macroscopic effects induced by small additions of surfactants to alkaline etching solutions. Sens Actuator A Phys 157(1):91–95
Sekimura M (1999) Anisotropic etching of surfactant-added TMAH solution. In: Proceedings 12th IEEE micro-electro-mechanical systems conference, Orlando, pp 650–655
Pal P, Sato K, Gosalvez MA, Shikida M (2007) Study of rounded concave and sharp edge convex corners undercutting in CMOS compatible anisotropic etchants. J Micromech Microeng 17:2299–2307
Resnik D, Vrtacnik D, Aljancic U, Mozek M, Amon S (2005) The role of Triton surfactant in anisotropic etching of 110 reflective planes on (100) silicon. J Micromech Microeng 15:1174–1183
Yang CR, Yang CH, Chen PY (2005) Study on anisotropic silicon etching characteristics in various surfactant-added tetramethylammonium hydroxide water solutions. J Micromech Microeng 15:202837
Sarro PM, Brida D, Vlist W, Brida S (2000) Effect of surfactant on surface quality of silicon microstructures etched in saturated TMAHW solutions. Sens Actuator A Phys 85:340–345
Pal P, Sato K, Gosalvez MA, Kimura Y, Ishibashi K, Niwano M, Hida H, Tang B, Itoh S (2009) Surfactant adsorption on single crystal silicon surfaces in TMAH solution: orientation-dependent adsorption detected by in situ infra-red spectroscopy. J Microelectromech Syst 18:1345–1356
Pal P, Sato K, Shikida M, Gosalvez MA (2009) Study of corner compensating structures and fabrication of various shapes of MEMS structures in pure and surfactant added TMAH. Sens Actuators A Phys 154:192203
Xu YW, Michael A, Kwok CY (2011) Formation of ultra-smooth 45˚ micromirror on (100) silicon with low concentration TMAH and surfactant: techniques for enlarging the truly 45˚ portion. Sens Actuators A Phys 166:16471
Rola KP, Ptasiski K, Zakrzewski A, Zubel I (2014) Silicon 45 micromirrors fabricated by etching in alkaline solutions with organic additives. Microsys Technol 20:221–226
Yagyu H, Yamaji T, Nishimura M, Sato K (2010) Forty-five degree micromirror fabrication using silicon anisotropic etching with surfactant-added tetramethylammonium hydroxide solution. Japan J Appl Phys 49:096503
Pal P, Haldar S, Singh SS, Ashok A, Xing Y, Sato K (2014) A detailed investigation and explanation to the appearance of different undercut profiles in KOH and TMAH. J Micromech Microeng 24:095026
Gosalvez MA, Li Y, Ferrando N, Pal P, Sato K, Xing Y (2016) Fluctuations during anisotropic etching: local recalibration and application to Si{110}. J Microelectromech Syst 25:1–11
Authors’ contributions
SSS and PP carried out literature search and wrote the manuscript. AKP, YX and KS reviewed/edited the manuscript. All authors read and approved the final manuscript.
Authors’ information
Sajal Sagar Singh completed his Bachelor’s degree in the Department of Mechanical and Aerospace Engineering at Indian Institute of Technology (IIT) Hyderabad, India in 2015. Currently, he is a final year Master’s student at IIT Hyderabad. His research interest lies in the field of linear and nonlinear dynamics, sensors and actuators, microfabrication techniques etc. He has published more than ten research papers in peer-reviewed international journals of high impact factor.
Prem Pal did his M.Tech in Solid State Material (SSM) in December 1999 and Ph.D. in the area of MEMS in December 2004, both from Indian Institute of Technology Delhi (IIT Delhi), India. The Foundation for Innovation and Technology Transfer (FITT), IIT Delhi awarded his thesis for “Best Industry Relevant Ph.D. Project—2005”. From July 2005 to June 2006, he worked as Postdoctoral Researcher at Yonsei Microsystems Laboratory (YML), School of Mechanical Engineering, Yonsei University Seoul, South Korea. He worked in Sato laboratory, Department of Micro-Nano Systems Engineering, Nagoya University, Nagoya, Japan: from July 2006 to March 2008 as COE Scientist and from March 2008 to March 2010 as JSPS Fellow. He joined the Department of Physics, Indian Institute of Technology Hyderabad in April 2010 as Assistant Professor. Presently, he is working as Associate Professor. He has published more than 50 papers in peer reviewed international journals of high impact factors. His research interests include MEMS technology, MEMS based sensors, Silicon Micromachining, Thin films for MEMS.
Ashok Kumar Pandey received the B.E. degree in mechanical engineering from Bhilai Institute of Technology, Durg, India, in 2001, and the M.S. and Ph.D. degrees in mechanical engineering from Indian Institute of Science, Bengaluru, India, in 2003 and 2007 respectively. He joined the Department of Mechanical and Aerospace Engineering, Indian Institute of Technology Hyderabad in July 2010. Currently, he is an Associate Professor in the same department. His research interest includes nonlinear dynamics, vehicle dynamics and micro and nanomechanics.
Yan Xing received the B.S., M.S., and Ph.D. degrees in mechanical engineering from Southeast University, Nanjing, China, in 1993, 1996, and 2001, respectively. He was with the Department of Micro-Nano Systems Engineering, Nagoya University, Nagoya, Japan from 2005 to 2007. He is currently a full Professor with the Department of Mechanical Engineering, Southeast University, Nanjing, China. He has been studying numerical simulation technologies with respect to MEMS CAD, semiconductor processes, and integrated information systems in automation.
Kazuo Sato graduated from Yokohama National University, Japan and received his BS Degree in 1970. He worked with Hitachi Co. Ltd. in a period of 1970–1994. During this period, he received his PhD degree from the University of Tokyo in 1982. He started Si-micromachining research in 1983 and published 128 international journal papers in MEMS technologies. He joined Nagoya University in 1994 as a full professor at Department of Micro Systems Engineering. He became Emeritus professor of Nagoya University in 2012, and currently is a professor at Aichi Institute of Technology, Japan. His research interests include bulk micromachining of Si and quartz, mechanical characterization of MEMS materials, and MEMS applications. He co-chaired IEEE MEMS-97 conference. He was the editor in Asia (2008–2012) and currently is an editorial board member of the Journal of Micromechanics and Microengineering. He is the founding chair of the Division of Micro/Nano Science and Engineering in the Japan Society of Mechanical Engineers (JSME), and Honorary Member of the JSME. He also is a senior member of IEEJ, and a fellow of JSPE, and a member of IEEE.
Acknowledgements
This work was supported by research grant from the Council of Scientific and Industrial Research (CSIR, Ref: 03(1320)/14/EMR-II), New Delhi, India and a Research Project BY2015070-06 Jiaungsu Povince, China. One of the authors ‘Dr. Prem Pal’ gratefully acknowledges financial support from Japan International Cooperation Agency (JICA) for visiting Sato lab (AIT Toyota) in Oct 2015 in regard to collaborative research work. Sincere thanks to Ms. Michiko Shindo (Secretory to Prof. K. Sato) for her assistance in obtaining permissions to reproduce some figures from published papers.
Competing interests
The authors declare that they have no competing interests.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Singh, S.S., Pal, P., Pandey, A.K. et al. Determination of precise crystallographic directions for mask alignment in wet bulk micromachining for MEMS. Micro and Nano Syst Lett 4, 5 (2016). https://doi.org/10.1186/s40486-016-0027-5
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s40486-016-0027-5