Abstract
As a promising desalination technology, capacitive deionization (CDI) have shown practicality and cost-effectiveness in brackish water treatment. Developing more efficient electrode materials is the key to improving salt removal performance. This work reviewed current progress on electrode fabrication in application of CDI. Fundamental principal (e.g. EDL theory and adsorption isotherms) and process factors (e.g. pore distribution, potential, salt type and concentration) of CDI performance were presented first. It was then followed by in-depth discussion and comparison on properties and fabrication technique of different electrodes, including carbon aerogel, activated carbon, carbon nanotubes, graphene and ordered mesoporous carbon. Finally, polyaniline as conductive polymer and its potential application as CDI electrode-enhancing materials were also discussed.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Review
Introduction
The concept of capacitive deionization (CDI) was first introduced in the 1960s in the University of Oklahoma by G.W. Murphy and D.D. Caudle [1]. The first CDI system they designed was based on flew through mode in which electrode sheets were made of activated carbon powder and saline water was pumped through the charged electrode sheets. Ions were hold into the pores of the electrode sheets as a result of the static electrical force and the physical adsorption. This process was later improved by Johnson et al. [2] in the 1970s who proposed a reversible electrosorption model to regenerate the electrode by removing the electrical field of the electrode and release the ions back to a concentrate flow. Following researches included describing the process with physical theories, trying different electrode materials and designing various water flowing systems. However, the fundamental process still similar to that of Johnsons’. A typical CDI system is shown in Fig. 1.
As the ions are actually removed by the electrical adsorption and the physical adsorption effect, both the electrical double layer theory and the physical adsorption models were applied to explain the process theoretically.
Electrical Double Layers
Electrical double layer (EDL) is a basic concept in electrochemistry. When the electrode is charged and put into a solution with ions, the interface of the charged electrode and ions rich solution will be occupied with counter ions as a result of the Coulomb force, forming EDL. Diminishing the charge hence the removal of Coulomb force releases the held ions back to the solution. This taking up and release process can be used as deionization and regeneration operation in desalination. The first model for CDI based on electrical double layer was developed by Johnson and Newman [3, 4] in the 1970s. In this model, it was assumed that ion sorption in the CDI is approximated as capacitive process; kinetics of adsorption does not limit the rate and faradaic reactions are negligible. The model has been widely used to investigate the process and explain experimental results.
Interfacial properties and structures between an electronic conductor (electrode) and an aqueous electrolyte solution have been explained well by widely accepted Gouy-Chapman-Stern double layer theory [5]. According to the model of Gouy-Chapman-Stern model, the double layer can be assumed to be divided into an ‘inner’ region and a ‘diffusion’ region. The inner region is named as the Helmholtz layer where ions covered directly onto the surface of electrode, while the region further from the surface is a diffusion layer called the Gouy–Chapman layer where the distribution of electric charge is depended on the potential at the surface. Both capacitances of the two layers contribute to the total capacitance; thus, the total capacitance can be calculated like a series union of both the inner Helmholtz layer and diffuse Gouy–Chapman layer (Fig. 2). The electrical capacitance of the interface, C T , is expressed as the sum of two capacitors in series: Eq. (1).
Distribution of charge in the Gouy–Chapman–Stern mode [5]
where C M−H is the capacity of the inner double layer between the electrode surface M and the plane of closest approach for the ions H (Helmholtz layer, and C H−S is the capacity of the Gouy-Chapman layer).
In a classic parallel-plate capacitor, charge separation is electrostatic. Capacitance is in proportion directly with the area of the plates and the inverse distance of separation as shown in Eq. (2):
where C M−H is the capacitance (F); A is the area of each plate (m 2); ε r is the relative electro static permittivity (dielectric constant) of the material between the plates; ε 0 is the permittivity of free space (8.854 × 10−12 F/m) and D is the separation between the plates (m);
Gouy and Chapman developed the formation for calculating the dependence of the excess charge, q on the potential at the Helmholtz plane (Eq. 3), by treating ions as point charges and assuming an ideally polarized electrode, namely, no electron transfer through the interface and ignoring the ion adsorption associated with other interactions.
Differentiating the charge q with respect to Φ H the electrical capacity of the diffuse layer is obtained by Eq. (4):
The excess charge distribution at the interface between a charged electrode-electrolyte according to the Gouy–Chapman–Stern model is described schematically in Fig. 2.
From Eq. (1), it is shown that both the capacity of the inner Helmholtz layer, C M−H , and the capacity of the Gouy–Chapman layer, C H−S , contribute to the total capacitance. However, in practical CDI processes, C M−H is much more important for ions capacity. Equation (2) shows that the specific electrical capacities can reach high values, as a result of the extremely short distances involved in double layer capacitors, large relative electrostatic permittivity of the material between the plates and large specific surface of the electrodes. In fact, distances involved in double layer structure have been reduced to an extreme, and the permittivity of the material between the plates can hardly improve because of the aqueous environment in CDI cells. The option of increasing the specific surface area of the electrodes becomes the main solution to achieve high electrical capacity.
Biesheuvel et al. [6–8] further studied the Gouy–Chapman–Stern-based adsorption and desorption model in CDI process. They took a simplified process by neglecting the effect of concentration gradients and consider only the driving force of electric field. In calculation, they found only the Helmholtz layer capacity was a freely adjustable parameter that described the data well suggesting that the Helmholtz layer capacity was of equal importance to surface area in characterization of salt storage capacity. Also, taking the microporous structure of the electrode material into account, they tried to evaluate the influence of co-ion expulsion by defining charge efficiency as the ratio between the amount of salt molecules removed from the solution and the amount of electronic charge transferred between the electrodes. Charge efficiency was used as a factor to evaluate ion distribution within the electrical double layer. It was also used as indicator for estimation of energy efficiency [9–11].
Adsorption Model
Langmuir Isotherm
In traditional water treatment, carbon was used as adsorbent to removal impurities from water by an adsorption process without the help of driving force of electrical field. Several models have been used to describe the adsorption process, and Langmuir and Freundlich adsorption isotherms are the most commonly used ones. CDI is a similar process in which electrical force driving is used instead of driving of concentration gradient. In both cases, equilibrium happens as a result of the surface saturation of the carbon material. Adsorption models that have been used to studied carbon adsorption are also used to study CDI process. Although electrical double layer theory is the most commonly used model for CDI, Jayson et al. [12] reported the adsorption of mercury(II) acetate from aqueous solution onto an activated charcoal cloth (ACC) was Langmuir charactered. Gabelich et al. [13] used Langmuir, Freundlich and BET isotherms in their study on electrosorption of ions onto carbon aerogels to fit experimental data and found the Langmuir isotherm described the data well. Their findings suggested that for modelling purpose in CDI, monolayer adsorption could be assumed. The Langmuir adsorption isotherm is expressed as
where X per unit weight of adsorbent; C e represents equilibrium concentration of the solute.
Freundlich Isotherm
The Freundlich isotherm is an empirical mathematical description of adsorption in aqueous system, as
where x is the amount of solute adsorbed; m refers to the weight of adsorbent; C e represents equilibrium concentration of the solute; and K and n are constants depending on the system.
Li et al. [14, 15] studied the adsorption isotherm of NaCl on carbon nanotube and carbon nanofibre composite. By comparing the Langmuir and Freundlich isotherms, they found the Langmuir isotherm described the experimental data better than Freundlich isotherm. Interestingly, their following studies [16, 17] on electrosorption of carbon nanotubes and graphene showed that at low salt concentration, the electrosorption followed Freundlich isotherm, too. Explanation for this phenomenon was the adsorbed layer did not fulfil the monolayer capacity at diluted solution. At this point, the Freundlich isotherm as an empirical equation of adsorption described the data well. Ban et al. [18] on the other hand found the electrosorption of naphthalenesulfonic acid on activated carbon fits the Freundlich isotherm.
Parameters That Affect the CDI Performance
Many factors influence the adsorptive performance of the electrode material: first, the nature of the electrode material such as surface area, pore size and distribution; second, applied electrical potential and third, the solution conditions, concentration and type of ions. Gabelich et al. [19] carefully studied the effects of operational parameters including applied voltage, flow rate and pH on the system performance for the first time in a carbon aerogel-based CDI device. Obviously, all the parameters affect ion sorption and desorption process; salt removal was better at higher applied voltages (2.0 V in their study); increased sorption efficiency was obtained at slower flow rates (50 mL/min) and high pH did adversely affect desorption. Further studies addressing the determining factor for CDI found that pore distribution of the electrode material and drive potential as well as ion type and concentration influence the deionization performance significantly.
Pore Distribution
Early in Cauddle and Farmer’s work, it was found that the average pore size of the electrode material had significant effect on the ion removal performance. Yang et al. [20] conducted special work on the relationship between electrosorption behaviour and the pore size of carbon. They took the overlapping effect into the model by defining the cut-off pore size as the smallest width that contribute to the electrical double layers. The cut-off pore width for 100 ppm NaF at the voltage of 1.2 V is 0.6 nm. Any pore with a width smaller than 0.6 nm does not hold any ion. Mesosized pores can provide a smaller resistance for the ion transport pathway through the porous carbon [21] and also a high surface area for the ion adsorption [22]. When pore size is larger than 10 nm, the amount of ions adsorbed remain constant. For the regions between 0.6 and 10 nm, the electrical double layers overlap to some extent resulting in partially losing the anion capacity. Macrosized pores can serve as ion-buffering reservoirs guarantees shorter ion diffusion distance, which facilitates the rapid transportation of the ions into the interior of the bulk material [23]. Noked et al. [11] carried out experiments of ions of different dimensions adsorbed onto carbon electrodes with various porous structures. They found that the ratio between the pore size and the ion size affected the electrosorption process significantly. When the ions’ radii approached the pore dimension, the electrical double layer charging process was impeded. They also reported that the rate of double layer charging was not only depended on high capacitance. Lager pore size leads to faster adsorption rate. The author suggested that multiporous fractal-structured electrodes with mesopores being the entries of micropores could be a better choice that facilitates both high capacitance and faster adsorption. Peng et al. [24] compared the electrosorption behaviour of mesoporous carbon electrodes with various pore structures and found the electrode of 2D hexagonal space groups showed better ion removal performance for monovalent cation solutions, while 3D symmetry cubic carbon was more efficient in removal of large-sized bivalent and trivalent valent ions.
Potential
Farmer et al. [25, 26] first studied the NaCl removal with four different voltages of 0.6, 0.8, 1.0 and 1.2. They found with the increase of applying voltage the ion removal efficiency improved significantly. Similar results also found in deionization of NH4ClO4. It is easy to interpret these results from the view of EDL. Higher voltage means more free electric charge on the electrode surfaces. However, to avoid the electrical dialysis of water, the voltage applied must have an upper limit. The standard potential of the water electrolysis is 1.23 V [5], so most researchers conduct the experiment at the voltage of 1.2 V. Lee et al. [27] investigated the electrode reactions related to the applied potential by monitoring the pH value of the solution during adsorption/desorption process. It was found that pH changed correspondingly to the applied potential.
The solution pH increased at a potential of 1.0 V due to the reduction of dissolved oxygen and decreased rapidly at potentials of 1.2 V or greater due to the oxidation of chloride at the anode. The pH level of the solution was around 10 when the adsorption equilibrium was achieved while applying voltage of 0.8 and 1.0 V. When applying a potential of 1.2 V, pH increases to 10 and drops to less than 8. With 1.2 V potential, it increases to 9 and drop quickly below 4.
Salt Type and Concentration
In Johnson’s study [3] on electrosorption of activated carbon powders, it was observed that divalent ions were preferred to adsorb onto carbon surface than monovalent ions. The preferential sorption of divalent ions was attributed to chemical equilibrium in the electrical double layers. Gabelich et al. [13] later studied the effects of ion charge and size on sorption onto carbon aerogel electrode specifically. Results contrary to Jonson’s observation were found. Adsorption of single-valent ions was prior to divalent species when both ionic species were present. But capacity of divalent ions could be enhanced when both ions were divalent. The author suspected hydrated radius of ions dictated the process. Seo et al. [28] discussed this phenomena and gave an acceptable explanation. They considered the two contrary results were obtained using different electrode material. Differences in pore structure of the two materials caused the difference in adsorption properties. Smaller size of pores attributed to the selective adsorption of monovalent ions which are small in hydrated radius while larger pore size favoured divalent ions with large hydrated radius. Noked et al. [29] took further investigation on this problem. They proposed the ratio between pore size of electrode and hydrated ion size and demonstrated the ratio were of crucial effect in the electrosorption process. When the ions’ hydrated radius approached pore dimension of carbon, the EDL charging was impeded. The ionic strength which determines the effective diameter of ions was considered to be another important factor in electrosorption, as high ionic strength results in smaller hydration shells leading to easier entrance of ions. Furthermore, salt concentration was taken into consideration. The salt concentration influenced the electrosorption process in two ways. One way was by determining the resistance of the solution. Lower concentration means higher resistance hence slower kinetics. Another way was through ionic strength and effective size.
Development of Electrode Materials in CDI
Carbon Material
The first CDI system in Caudle’s [1] research was a flew through system with electrode sheets made of activated carbon powder. Then, in the 1970s, Johnson et al. [2] continued the study and developed the process as a reversible electrosorption. Several carbon materials were studied as electrode material in their work. A theoretical model based on the electrical double layer theory was first proposed. Apparently, the electrode material should be of large specific surface area to have high capacity to hold considerable quantity of ions and be physically stable during the ions taking and release procedure to avoid polluting the water flew and gain good regeneration property. At the same time, in order to complete the procedure quickly, the electrode should be of high electrical conductivity. Porous carbon due to its high surface area, good electrical conductivity as well as low cost was used as electrode in this electrochemical deionization process. Various carbon materials including activated carbon powder, carbon aerogel, carbon nanotubes and graphene for instance are studied as candidates of electrode materials for CDI.
Carbon material is a large family represents a wide range of materials that are mainly composed by element carbon. Among them, graphite and diamond are the two with crystal structures and are not property adsorption materials because of the lack of surface area. Others are normally referred to as amorphous carbon. Characterization of these amorphous carbon shows they also have microcrystalline structure. Unlike graphite in which flat layers of hexagonal carbon rings compact together to give a crystalline structure, the orientation of microcrystalline layers in amorphous carbon are different and less ordered. The random arranged disordered microcrystallites tend to crosslink with each other which result in a well-developed porous structure hence enormous internal surface [18]. These high surface porous-structured carbons are known as activated carbons and have been widely used as adsorbents for odour, colour and organic impurities for a long time because of their unique porous structure [30]. Even before CDI, carbon had already been used as adsorbent in water treatment. With the highly favourable structure, it is no coincident that carbon is considered to be the most promising electrode material in CDI.
Apart from activated carbon, there are other carbon materials structured with carbon atoms in certain patterns such as tubes (carbon nanotubes) and sheets (graphene). These structure patterns provide the materials with unique properties, such as large surface area, high electrical conductivity and good thermal conductivity. Applications of these materials in CDI will be discussed in detail later in this part.
Activated Carbon
Activated carbon powder (AC) as a strong adsorbent in industry application is mainly produced by the pyrolysis of carbonaceous source materials such as nutshells and wood at temperatures lower than 1000 °C. The raw carbon materials are first carbonized at temperatures below 800 °C and followed by the activation of carbonized product between the temperatures of 950 and 1000 °C [30]. Alternatively, the raw materials could be chemically activated by acid, strong base or salt prior to carbonization and then carbonized at lower temperature (400–700 °C) [31].
AC has been the mostly used electrode materials in CDI mainly because its low cost. It was actually the first electrode materials used for electrosorption. The history of AC as an electrode material in capacitive desalination date back to the early 1960s by Caudle and Murphy [1, 32]. Since then, AC has been the most common material for CDI electrode. Normally, a CDI electrode was fabricated by a certain ratio of carbon material, conductive additives (graphite in most case) and binders. Research works on AC in CDI include modifying the pore structure, retaining faradaic reaction determining the type and amount of binder and improving the conductive property. Zou et al. [33, 34], Lee et al. [27, 35], Choi et al. [36, 37], Chang et al. [38] and Hou et al. [39] published paper on AC electrode CDI, Zou et al. emphasized on the pore structure optimization, Lee investigated the effect of operation parameter of the system, Choi et al. worked on controlling the faradaic reaction of the electrode by using poly(vinylidene fluoride) binder, Chang et al. obtained promising AC electrode by using a novel liquid binder and Hou et al. estimated that the suitable amount of binder (PVDF in their study) was 10 %. Kim et al. [40] investigated the desalination of brackish water containing oil compound using AC electrode and found the process was reproducible adsorption and desorption characteristic. Bouhadana et al. [41, 42] studied the practical aspects of an AC-based CDI system, in which the author designed a flow-by system. By estimating the energy consuming of the system, they concluded that cost-effective production of drinking water is possible by CDI process. Avraham et al. [9, 10, 43] studied the limitations of charge efficiency of the AC electrode in CDI process, in which electrosorption behaviour of a single AC electrode and double AC electrodes and the surface oxidized AC electrode were well studied. The author concluded that it is possible to maximize the charge efficiency by applying discharge potentials (upon regeneration) higher than zero and for AC of pore-size larger than 0.58 nm, the oxygen-containing surface groups have no obvious effect in the ion adsorption/desorption process.
Recently, modifying the AC electrode was used as new strategy to obtain better desalination performance. AC electrode with deposited ion-selective membrane [44], making AC electrode with water soluble blinder [45], and compositing AC with other materials to enhance its conductivity, improve the capacity and modify its pore structure have been reported. In the case of combining AC with other materials, candidate such as ion-exchange resin [35], MnO2 [46], titania [47] and graphene [48] were used as component to improve capacitance and desalination performance of activated carbon powder. The adding to ion-exchange resin to the electrode improved the hydrophilicity of electrode, and the ion exchange site enhanced the ion removal capacity. Deionization performance of the ion-exchange resin/AC electrode was enhanced by 35 % compared to the one without ion-exchange resin. The MnO2/AC composite showed doubled ion removal amount than the AC material due to a more suitable pore size distribution and effective cation intercalation of MnO2. For titania-loaded AC, the formation rate of electrical double layer in AC electrode was improved significantly and the amount of ions removed was increased by 62.7 %, along with good regeneration performance of electrode. Graphene-containing AC showed improved ion capacity as the graphene sheets acted as spacer that prevented the aggregation of AC, providing more available surface.
Carbon Aerogel
Carbon aerogels are nanosize air-filled foams with mainly carbon as skeleton. Synthesis of carbon aerogel starts by sol-gel polymerization of resorcinol (1,3-dihydroxy benzene) with formaldehyde. Polycondensation of resorcinol and formaldehyde form highly cross-linked transparent hydrogels which are dried under supercritical condition to form the precursor called RF aerogel. Pyrolyzing the RF aerogel at relatively high temperature (600–1200 °C) in an inert atmosphere gives carbon final product aerogel. Other organic aerogels, phenol-furfural, phenol-resorcinol-formaldehyde, melamine-formaldehyde, polyurethanes, polyureas and polyvinyl chloride for instance can also be used as precursors [49, 50]. Carbon aerogels are attractive as electrode materials because of their exceptional property such as high surface area (400–1000 m2/g) and good electrical conductivity (10–100 S/cm) [51]. Also, morphology of carbon aerogels can be controlled to be films, powders or microspheres [52]. Figure 3 shows the TEM image of carbon aerogels.
TEM image of carbon aerogels [53]
In the 1990s, carbon aerogel was synthesized and became a promising candidate for energy storage and CDI electrode material. Farmer et al. [25, 26, 54–58] from Lawrence Livermore National Laboratory did a lot of work on the application of carbon aerogel in CDI. Salts such as NaCl, NaNO3, Na3PO4 · Na2SO4, NH4ClO4 and hexavalent chromium were shown to be removed from aqueous solution. Since carbon aerogel could be produced as monolithic sheets by controlling the morphology, Farmer developed electrodes with pairs of thin sheets of carbon aerogels instead of deep bed. The electrolyte flowed in a channel between anodes and cathodes so as not to create a potential drop as it did in flowing though packed beds thus avoiding entraining the electrode material into the fluid stream. Their experiments showed that after prolonged operation, the electrodes lost part of their adsorption capacity, but it is believed that reversing the electrodes could make recover most of the losses. Later in 2002, Gabelich et al. [13] conducted a thorough study on the electrosorption of ions on carbon aerogels including effect of ionic charge, radius and mass. It was found that monovalent ions with smaller hydrated radii were preferentially removed from the solutions over multivalent ions and because of the small pore size only a few percentage (14–42 m2/g) of the BET electrode surface area (400–1000 m2/g) were available for electrosorption. Fouling of aerogel surface by nature organic matter was deemed to be a problem for the effective treatment of nature water. Yang et al. [59] tried to use silica gel enforced carbon aerogel as CDI electrodes. Results of their experiments showed the adding silica improved ion capacity by up to 28 % due to increased wettability and enhanced mechanical hardness.
OMCs
Ordered mesoporous carbons (OMCs) are carbon materials with ordered uniform pore size in the range of 2–50 nm. Typical SEM images of OMC are shown in Fig. 4. Conventionally, the uniform pore structures are obtained by attaching carbon precursors onto certain templates with three-dimensional pore structures (e.g. silica and zeolite) and remove the template after carbonization. This is called hard-template method. To overcome time-consuming and costly steps of the silica etching process, a soft-templating approach was introduced by directly assembly of organic amphiphilic surfactant or block copolymers templates with the carbon precursors [60].
SEM images of OMC [61]
Zou et al. [62–64] first studied the electrosorption performance of OMC and compared with AC electrode. They found the ion removal performance of OMC was much better than AC due to its optimized pore structure. The ordered uniform structure with a peak diameter of 4.0 nm facilitated the fast entrance and release of ions onto and off the electrode surface lead to high ion removal and faster regeneration. They further modified the OMC structure by introducing nickel salts during the synthesis process. The nickel containing OMC had smaller ordered mesopores; the peak diameter shifted to 3.7 nm from the original 4.0 nm. Also, the modified OMC possessed higher surface area and exhibited higher ion capacity. Tsouris et al. [65] compared the deionization performance of self-assembled OMC with carbon aerogel and reported that OMC was a more suitable choice for CDI. The reason was attributed to the order pore size which provided more surface area to be accessed by ions. Nadakatti et al. [66] also reported the enhancement of CDI performance by adding mesoporous carbon black. It is demonstrated that the ion removal efficiency increased by 100 % after adding the mesoporous carbon black. More recently, Peng et al. [67] synthesized composites of OMC and carbon nanotube for CDI. They found that with 10 wt.% carbon nanotube combined, the composite exhibited higher ion removal efficiency. Meanwhile, reversibility and stability of the composite electrode were both improved.
CNT and Graphene
Graphene and carbon nanotube (CNT) are novel carbon materials with unique structure and extraordinary electrical properties. Graphene is one-layered graphite in which a one-atom-thick sheet is formed by carbon atoms arranged in a regular hexagonal pattern (Fig. 5b). It is a two-dimensional material in which carbon atoms are sp2-bonded in the bond length of 0.144 nm. The electron mobility of graphene can be as high as 200,000 cm2V−1s−1 [68]. This demonstrates that the electrical conductivity of graphene is excellent. More importantly, being a single-atom layer structure, the theoretical surface area of graphene is 2630 m2/g [69]. Besides, the interlayered open structure of graphene sheets favours easy ion adsorption and desorption. A single-walled carbon nanotube (SWCNT) is a rolled graphene sheet in a cylindrical shape (Fig. 5a). A tube surrounding tube structure made of two layers of graphene sheets is called double-walled carbon nanotube (DWCNT). And the one made of more than two layers of graphene sheets is called multi-walled carbon nanotube (MWCNT). Depending on the arrangement of the hexagon rings along the tubular surface, CNT can be metallic or semiconducting.
These properties of uniform structure, large surface area and good conductivity make graphene and CNT very promising for a CDI electrode. Since ions are electrically adsorbed and stored in the EDL on the electrode surface, higher electrical conductivity and larger specific surface areas mean higher ion capacity [70, 71]. Compared to other carbon materials, CNT and graphene not only possess high specific surface area but also are excellent in electrical conductivity. Good conductivity not only contributes to the ion capacity but also speeds up the ion adsorption and desorption process.
Dai et al. [72, 73] reported the use of multi-walled carbon nanotube-based electrodes in the adsorption of NaCl and confirmed the promising properties of carbon nanotubes in the CDI process. Li and co-workers [15, 74] using carbon nanotubes and carbon nanofiber composites as CDI electrode material, they compared the electrosorptive properties of SWCNTs and DWCNTs, and the results of these studies are promising with respect to the suitability of CNTs as electrode material. Zhang et al. studied the effect of CNT diameter on its performance as CDI electrode [75]. They discovered that salt removal efficiency increase with the decrease of CNT diameter due to its enhanced surface area.
Pan et al. [14, 76, 77] did a great deal of work on the application of carbon nanotubes and graphene. They studied the effects of ion charge, size and mass on electrosorption of the ions. The result showed better electrosorption capacity was obtained for the anions with smaller hydrate radius. Capacity pattern of Cl− > NO3 − > SO4 2− was found as smaller ions has easier access to the porous network. Meanwhile, the carbon nanotubes exhibited quite efficient regeneration performance due to high electrical conductivity. Wang et al. [78] prepared three-dimensional continuous carbon nanotube sponge by chemical vapour deposition and studied its capacitive deionization performance. The carbon nanotube sponge electrodes showed higher desalination capacity than that of AC, AC fibre and carbon aerogel. Composites of carbon nanotube with mesoporous carbon [67, 79], polyacrylic acid [80] and graphene [81, 82] were also used as electrode material in CDI. The mesoporous carbon/carbon nanotube composite exhibited excellent desalination behaviour with low energy consumption. Carbon nanotube/polyacrylic acid composite film showed higher ion capacity than pure CNT with good regeneration ability. Graphene/carbon nanotube composite demonstrated significant synergistic effect as the ion capacity of the composite was better that either of the component itself. It was explained that the long CNTs not only interconnect adjacent graphene sheets thus increasing conductivity of the composite but also inhibited the aggregation of individual sheets, providing more applicable surface.
Graphene as the novel material in CDI research showed good deionization performance than activated carbon powder, even with a much lower surface area. Li et al. [16, 17, 83] first reported the electrosorption behaviour of graphene synthesized by a modified Hummers method in NaCl solution. They later studied the ferric ion removal of the graphene material. Inspired by these research, Wang et al. [84, 85] conducted research on capacitive deionization performance of resol functionalized graphene, in which the resol restricted the aggregation of graphene resulting in higher ion capacity. Jia et al. [86] developed a three-step reduction of graphene oxide (GO) in which the GO was first mildly reduced by iron powder and then sulphonic functional groups were introduced to the partially reduced GO to obtain good dispersion property. The functionalized GO was finally reduced by hydrazine. In this way, the resultant graphene electrode showed high ion capacity and good regeneration performance. Wang et al. reported a modified thermal reduction method utilizing pyridine as intercalating agent to prepare graphene for CDI application [87]. Lei et al. prepared graphene nanosheets by a novel Fe-catalyzed carbonization method using glucose as carbon source [88]. More recently, graphene featuring three-dimensional structure as high performance CDI electrode using different templating methods was demonstrated due to higher surface area, pore volume and superior ion transportation pathway [89, 90]. Possibility of graphene/OMC composites as CDI electrode using core-shell and triblock-copolymer templating method was also explored [91, 92].
Other Carbon Materials
Activated carbon cloth (ACC) is another form of carbon material that has been well studied for CDI. Ryoo et al. [93, 94] carried out electrosorption experiments on ACC and silicon, aluminium and titania modified ACC. It was found that titania could be highly dispersed on ACC surface hence reduce its polar group, resulting in a reduction of physical adsorption. While electrosorption of titania modified, ACC was enhanced significantly due to increase of adsorption sites introduced by the incorporated titania atoms. Rapid desorption and good reversibility was also obtained with titania modification. Oh et al. [95] studied the influence of chemical activation of ACC on its deionization property. Myint et al. studied the CDI electrode made of nano/microsized zinc oxide/ACC composites [96], where up to 22 % salt removal efficiency was observed compared with using ACC alone.
A pair of asymmetric electrodes made of nanoporous silicon dioxide and magnesium-doped aluminium oxide was synthesized and examined for CDI application by Leonard et al. [97]. It was reported that the electrodes pair demonstrated effective removal of cations with various valences as well as decreased regeneration time. Haro et al. [98] developed carbon gel to remove ions from brackish water. Parada et al. [99] reported carbide-derived carbon for CDI and indicated that it could be a good choice as electrode material for CDI based on easy controlling of pore size. Yang et al. [100] prepared a MnO2/PSS/CNTs composite electrodes, and Liu et al. [101] studied electrosorption of polypyrrole and graphite composites. More recently, CDI performance of hollow carbon nanofibers, which was prepared by the electrospinning process of polyacrylonitrile (shell) and poly(methyl methacrylate) (core) [102], activated carbon fibre [103], and three-dimensional hierarchical porous carbon (3DHPC) [104] was also reported in the literature. Table 1 summarizes the CDI performances of different electrode materials.
Membrane CDI
Conventional CDI is energy inefficient because adsorption and desorption processes happen simultaneously at the EDL. When an electric potential is applied, counter-ions in the pore adsorb onto the electrode and co-ions are expelled from the electrodes which will seriously reduce desalination efficiency. To solve these problems, a membrane capacitive deionization (MCDI) system was introduced by Andelman et al. [105] in which ion-exchange membranes were incorporated along into the electrode fabrication. Including the membranes in the process block co-ions from leaving the electrodes and counter ions can be more fully flushed from the electrode region during ion release procedure increasing ion removal efficiency. Li et al. [106] constructed an MCDI device using carbon nanotube and nanofiber electrodes with ion-exchange membranes. They reported that the salt removal by the MCDI system was about 50 % higher than that by the CDI system. Biesheuvel et al. [107] presented a pilot-plant experimental data for salt removal in MCDI as a function of influent salt concentration and flow rate and found that the salt concentration ratio between the diluted product and the concentrated salt was as high as 25. Choi et al. [44, 108, 109] also developed their own MCDI device has the potential to be very ion-removal efficient. The data shows that salt removal efficiencies of the MCDI cell were enhanced by about 32.8–55.9 % compared to the CDI cell depending on the operating conditions; the current efficiencies were 35.5–43.1 % for the CDI cell but 83.9–91.3 % for the MCDI cell, about twice that of the CDI cell. It was evident that MCDI can increase the desalination efficiency significantly.
Polyaniline as Conducting Polymer
Polyaniline (PANI) is one of the conducting polymers that has been extensively studied due to its extraordinary electrical properties and good environmental stability [119]. Conducting polymers are mainly organic macromolecular which can be electrically conductive because of the π conjugated double bonds in the polymer back bones. Electrons in the π conjugated double bonds are delocalized and can move along the main chain as charge carrier. Electrical conductivity can also be achieved by movement of holes in occupied energy state. Conducting polymers need to be doped to be conductive or to enhance the conducting property. By doping, it is introducing conductive electrons or holes. When electrons are introduced, it is called n-type doping and p-type doping when holes are introduced.
Polyaniline was first discovered in 1842 in the study of aniline-based dye industry [120]. However, the electrical property and electrochemical property of the substance were not revealed until mid-1980s. MacDiarmid and his group conducted much research on polyaniline, demonstrated the inter conversion of its three oxidation states [121] and elaborated their IR absorption and optical absorption spectroscopy [122]. Also, 15 N NMR [123] and X-ray scattering [124] of the polymer were well studied.
Structure of PANI
PANI has a variety of forms according to its oxidation and protonation state, which exhibit different electrical conductivities and other interesting properties. The base form of PANI consists of alternating quinoid and benzenoid rings with repeat unit chain and can be divided into three states based on the oxidation state: the reduced form (leucoemeraldine), the fully oxidized form (pernigraniline) and the intermediate form (emeraldine). In the reduced form, nitrogen atoms connect entirely with the benzenoid units: in the fully oxidized version, a 1: 1 mixture of benzenoid and quinoid rings; in the emeraldine, with a 3: 1 benzenoid/quinoid ratio (Fig. 6). Treatment of this last state by soaking in acid (see Fig. 7) leads to a dramatic increase in electrical conductivity up to around 500 S/m, and the process is called proton doping [125].
a Generalized composition of PANI indicating the reduced and oxidized repeat units. b Completely reduced polymer. c Half-oxidized polymer. d Fully oxidized polymer [126]
Scheme of proton doping in PANI [127]
The physical structure of PANI was profoundly revealed along with the study of the conductivity mechanism. The structure was described as a semi-crystalline with order crystalline in the core surrounded by amorphous edge. The doped central crystalline is metallic conductivity in nature, amorphous region has disordered or fold polymer chains which are lower in conductivity and the total conductivity of PANI is restrained by the disordered area [127]. As for which, the total conductivity of PANI depends on the percentage of crystallinity molecular weight molecular arrangement and degree of doping [128]. Mechanism of conductivity was attributed to polaron structure that is formed by nitrogen radicals, which act as charge carrier holes. Except for acids polyaniline could also be n-doped by strong reductant KH or NaH [129]. More recently, carbon nanotubes were proved to be doping agent for PANI [130, 131]. The SWCNT/PANI nanocomposite processed good electrochemical activity in neutral and alkaline media. SWCNTs were considered pristine as potential dopant to preserve the electrochemical property of PANI effectively in the neutral and alkaline media.
Polymerization Mechanism and Morphology Controlling
Polymerization Mechanism
Chemical polymerization is a conventional method to produce high quality PANI in a large scale. The reaction is initiated by an oxidizing agent such as ammonium persulfate (APS) [132, 133], H2O2 [134], benzoyl peroxide [135, 136], ferric chloride [137, 138] and chloroaurate acid [139, 140]. APS is considered to be an optical choice due to its high yield.
Chemical polymerization of PANI is shown in Fig. 8. In the beginning, aniline monomers are induced into radical cations by the oxidation agent. The radical cations are recombined into a dimer according to the electrophilic substitution mechanism to start the polymerization. After this induction period, the terminal amine group of oligomer or polymer attacks para-position in monomer causing chain propagation, in which step it is assumed as an electrophilic substitution process [141].
Chemical polymerization of PANI [141]
The induction step is reaction. It is observed in experiment that adding aniline dimer accelerates the polymerization significantly [142]. Temperature is an important factor in the aniline polymerization as a low temperature is beneficial for producing high crystalline PANI [143].
Morphology Controlling in Chemical Polymerization
Parameters as type of oxidant, acid concentration, reaction temperature and stirring pattern all affect the structure of final polymer. PANI with granular [144], nanotubes/nanowire [145–147], spheres [148, 149] and nanodiscs [150] morphology has been reported depending on the experimental conditions.
The granular morphology is the most typical form of PANI prepared in acidic aqueous media (see Fig. 9a). This morphology usually forms in high acidic concentration (pH <2.5) and intense monomer concentration (>0.1 mol/L) with a strong oxidant, in which condition the polymer chains grow before the phenazine nucleates organization. So the nucleates packed in random to form globular structure instead of the more organized nanotubes [151]. Nanotubes (Fig. 9b) and nanowires of PANI can be self-assembled directly by polymerization. The methods include diluted monomer [152, 153], weak acid dopant [154–156], interfacial polymerization [157, 158] and rapid mixing [159]. In these conditions, as for the low reactant concentration or low radical cation concentration the growth rate of the backbone is low, the phenazine nucleates are able to stack in ordered cylindrical pattern, producing nanotubes and nanowires. Redox potential of the oxidant is related to the diameter of the grown nanotubes; it was found that the diameter increased with increasing oxidant redox potential [160]. Higher H+/aniline ratio result in highly ordered smooth nanotubes with similar diameter [161, 162]. Increase of acid concentration leads to the increase in average diameter of the resultant nanofiber [159].
Polyaniline with different morphology (a granular b nanotubes) [156]
The ratio of APS to aniline is of importance to the fine surface of nanofibers. Lower APS gives a longer and less branched structure with smaller average diameter [161]. Hollow or filled spherical structures are mostly obtained by emulsion polymerization. In emulsion polymerization, the reaction media composed of oil and water phase. By adding stabilizer and applying appropriate dispersing technique, one phase forms droplets and surrounded by the other phase: oil in water in direct emulsion and water in oil in inverse emulsion. Size of the droplets can be tuned through selection of stabilizer, the ratio of water to oil and the reaction temperature [163].
The two-dimensional disc or plate morphology was also synthesized in acidic aqueous solution with APS as oxidant. The nanodiscs or nanoplates were found to have similar structure in which the nanowires packed together in perpendicular directions to constitute a spiny surface [164]. At high monomer concentration, the dense structure of plat is formed. Controlling the morphology of PANI can also be achieved by seeding polymerization and template synthesis. PANI powder and nanofibres were used as seeds. Nanostructures present during the very early stages of the reaction can orchestrate bulk formation of similar nanostructures. The seeding polymerization is rapid and suitable for bulk quantities production [165]. The synthesized polyaniline nanofibers were found to be high in capacitance. Template synthesis include hard template (i.e. zeolite) and soft template (i.e. water soluble polymers [166], gels [167] and liquid crystalline polymers [168]). In hard template method, the polyaniline grows at the surface of the nanostructured template directly. In soft template, the template forms micelles or guides the polymerization through hydrogen bonding force or electrostatic force [169].
PANI as Electrode Material
The electrochemical oxidation and reduction of conducting polymers involves take up and give off ions to maintain electro-neutrality of the material. PANI has three redox peaks which results in large ion capacitance during the ion insertion process and is also attractive with good stability, easy preparation low cost and good conductivity. Since mid-1980s, MacDiarmid and his group demonstrated the inter conversion of its three oxidation states; PANI has been regarded as one of the most promising material for the preparation of rechargeable battery because of this high specific capacitance [121, 128, 170]. In order to use PANI as electrode material in electrochemical battery, intensive research was conducted since 1990s [125, 171, 172].
At first, PANI was electrically synthesized or chemically deposited onto the surface of various substrates, platinum [171, 173], Indium tin oxide [174, 175], graphite [176], etc. The modified electrode showed large redox capacitance. Realizing the porosity and internal microstructure of the electrode material plays a crucial role in ion taking rate as well as capacitance; researchers have been focused on fine structured nano-scope PANI to achieve better property. Several synthetic methods were reported to produce PANI powder [177], nanofibers [137, 146, 152, 153, 160, 178, 179], nanowires [180–184] and nanotubes [133, 147, 156, 185] to exploit high rate and large capacitance.
To optimize the performance of PANI, two approaches were useful. One is to increase specific surface and the other is to enhance electrochemical activity. By producing PANI nanowires, nanofiber and nanotubes specific surface area of PANI increased dramatically. The other is to combine PANI with other materials with high specific capacitance. PANI was combined with polypyrrole nanotubes [186] and nafion nanofibers [187]. It was also combined with electrochemical active metal oxides materials such as MnO2 [188, 189], TiO2 [190, 191], SnO2 [192] and MnWO4 [193], for instance. In the meanwhile, combining PANI with large surface materials such as silicon [194], sodium alginate [195], porous carbon, CNT and graphene also proved to be effective approach in increasing the surface area and eventually the capacitance of PANI.
PANI combined with porous carbon to increase the capacitance of carbon and improve the stability of PANI was studied by Chen et al. [196] as electrode material for supercapacitor. With PANI electrochemically deposited onto the surface of porous carbon electrode, the specific capacitance was enhanced and significant contribution of pseudo-capacitance was confirmed. Following the approach, PANI was also combined with various carbon material including porous carbon [197], activated carbon powder [198–200], hollow carbon sphere [201], carbon nanofiber [119, 202] reticulated vitreous carbon [203], calcium carbide derived carbon [204], macroporous carbon [205], mesoporous carbon [206–208] and carbon cloth [209, 210] and carbon black [211]. PANI and activated carbon powder composites were reported have improved capacitance performance compared to bare carbon electrode. PANI-deposited carbon nanofiber electrode was reported to possess high reversibility good stability as well as high specific capacitance. Carbon black acted as cores to form core-shell structures with PANI shell covered uniformly on the surface in which carbon black was considered to be a good component to improve electrical conductivity of the electrode material efficiently. Although incorporating with ordered macroporous carbon resulted in relatively lower specific surface, the PANI composite-based electrode showed high capacitance as good rate capability. The composites of PANI with reticulated vitreous carbon and calcium carbide derived carbon as well as carbon cloth also showed higher specific capacitance than the carbon substrates and good cycle stability. Mesoporous carbon and PANI composites were synthesized though in situ chemical polymerization, the resultant materials were studied and reported to have higher specific capacitance and good reversibility. Furthermore, MnO2 was introduced in the PANI/mesoporous carbon composite. The authors concluded that MnO2 nanoparticles involved in the material stabilized the interaction between quinoid ring of PANI and OMC/MnO2 particles thereby lead to enhance specific capacitance and good cycling stability.
The combination of PANI with carbon nanotubes has drawn great attention since the last decade. Composites of PANI and both SWCNT and MWCNT have been synthesized, and their properties were characterized as electrode materials for supercapacitor. The structural characterization of CNT/PANI composites showed that CNTs were linked up by PANI chains, forming a network structure with new conductive passage and higher conductivity. The strong conjugating interaction between the two components provided fast charge transfer reaction between the two [212, 213]. Capacity tests also showed the composites possessed enhanced specific capacitance. Most of the researchers adopted electrochemical method to obtain CNT/PANI composites as morphology controlling of the composites is convenient in electrochemical polymerization. Zhu et al. [214] fabricated PANI/WMCNT composites by electrochemical approach and found that the specific capacitance of the composites was significantly influenced by its morphological structure and the content of PANI. At the lower, content of PANI was glossily coated onto the tube surface, and the diameter of the composites increased with the increasing PANI content. When the content of PANI reached 76.4 %, the PANI layer became rough and further increasing of PANI content leaded to independently grown PANI nanorods. A maximum specific capacitance of 521.2 F/g when weight percent of PANI was 76.4 % was reported. In accordance, Gupa et al. [215] also reported morphology of electrochemically synthesized PANI/SWCNT composites varied with the content of PANI deposited. As the weight percent of PANI below 70–75 %, the deposited PANI wrapped onto the surface of SWCNT. Beyond the amount, PANI tended to grow independently around the surface or into the micropores. Zhang et al. [216, 217] electrochemically deposited PANI onto the surface of carbon nanotube array in which the nanotube array framework provided large surface area and superconductivity leading to extraordinary energy storage performance. The authors found morphologies of composites were of great importance in improving their performance. Introduction of PANI turned the macro/mesopores of the CNT array into smaller meso/micropores providing higher specific surface area and maintaining regular channels of the material.
In situ chemical polymerization is another well-studied choice to synthesize PANI/CNT composites [218, 219]. Choi et al. [220] chemically synthesize PANI/MWCNT composite in which the surface of MWCNT had been thickly decorated by PANI forming covalent attachment. King et al. [221] investigated the influence of carbon nanotube characteristic on the morphology and properties of the chemically synthesized nanohybrids. It was found that despite aniline monomers themselves could result in nanofibrous structures, CNTs were the dominant templates in the polymerization. However, a less ordered and thinner polyaniline coating was observed at the unoxidized CNTs due to the worse water solubility and weaker hydrogen bonding effects with aniline monomers. By comparing the effects of SWCNT and MWCNT, they found that MWCNT-containing composites was less conducting that the SWCNT-based series and composites based on oxidized CNTs were less conducting than that containing unoxidized ones. More recently, Fan et al. [222] reported chemically synthesized carpenterworm-like PANI/CNT nanocomposites in which MWCNTs were covered by interlace PANI nanoprotuberances. They ascribed the formation of the interesting morphology to the introduction of ethanol in the polymerization solution.
Microwave assisted synthesis [223], liquid-liquid interfacial polymerization [224] and a solid-sate synthesis [225] were reported to obtain PANI/CNT composites. In the former two synthetic methods, PANI coated to the surface of CNTs displaying core-shell structures. In solid state synthesis, the composite containing 16 % MWCNT was aggregated particles in morphology while the resultant containing 32 % MWCNT showed some nanofiber morphology. Combination of PANI/CNT and transition metal oxidize MnO2 was also studied to further improve the capacitance performance [226, 227].
Dong et al. [228] studied electrochemical performance of PANI/MWCNT composites in neutral aqueous solution and found that the composites showed higher specific capacitance than pure PANI. Infrared spectroscopy studies have shown that introduction of CNTs affected both the free N–H environment and quinoid units in PANI backbones indicating doping effect of CNTs [130]. Zhou et al.’s [131] study revealed that mixture of SWCNT and PANI processed good electrochemical activity in neutral and alkaline media. The authors concluded that fast electron transfer property and high stability of the mixture in neutral and alkaline media were due to effective doping of PANI by SWCNT.
More recently, due to arising of different methods of graphene preparation, the unique electrical property of graphene and promising electrochemical characteristics of PANI, combination of the two draw great attention. Studies in the field covered both the combination of graphene oxide and graphene with PANI. Methods of fabrication included in situ polymerization of aniline [229–232], filtration of the mixed dispersion [233, 234] and grafting PANI nanofibers to the edge of graphene sheets [235, 236] as well as layer-by-layer self-assemble method [237]. Further studies use functionalized graphene to composite with PANI in order to obtain higher capacitance. Li et al. [229] synthesized sandwich-like graphene/PANI composite in which PANI particles covered homogeneously on the surface of the graphene sheets at lower aniline ratio. Increasing the aniline ratio leaded to larger particle size of the deposited PANI. When the aniline ratio exceeded 12:1, fibrous PANI grew simultaneously with the sandwich composite. In situ polymerization can also produce graphene/PANI nanofiber composite in which nanofibers stick paralleled onto graphene sheets [231]. PANI was reported to anchor onto partially reduced graphene sheets and form a loose flower-like structure that extended the specific surface area of the material [238]. Polymerization of PANI in the presence of graphene oxide could result in the direct exfoliation of GO. PANI grew into layered GO causing peeling of the GO layers forming a single-layered GO/PANI nanosheet with folded edge [239]. Wu et al. [234] developed supercapacitor based on paper-like flexible graphene/PANI nanofiber composite films. The films obtained by filtrating mixed dispersions of graphene nanosheets and PANI nanofibers showing high flexibility that could be bent into large angles. By directly filtration of an in situ polymerized, a mixture of PANI and GO and a mixture of reduced GO, Yan et al. [233] obtained flexible composites paper and found that compactable small particles were formed on the GO sheets while nanorods and large particles were formed on the reduced GO substrate. The authors assumed that nanorods came from the individual PANI fibres formed in the aqueous phase, but why PANI fibres adsorbed onto graphene not GO was not explained. A comparison study on surface functionalities of GO with N and NH2 groups was carried out by Lai et al. [240]. It was found NH2-functionalized GO/PANI (NH2-GO/PANI) showed high conductive stable composite. Interestingly, an increase in capacitance was observed for NH2-GO/PANI composite. The authors suspected that the amine functional groups assisted the doping and dedoping in PANI causing the enhancement of capacitance in long cycles. Others [235, 236] tried grafting PANI nanofibers to the edge of graphene sheets through an amide-connecting system. The PANI nanofiber connected to the graphene intimately and distributed homogeneously along of graphene layers inhabiting the agglomeration of the layers. Computing of the electronic densities of the system showed that π-π conjugation was extended from graphene to PANI chains through the amide group. O=C–N group also played as electron bridge spreading the electrons along the conjugation system. The conjugation system facilitated the fast transfer of electron.
Multilayered PANI/GO films could be built up on top of silica or ITO (indium tin oxide) glass through layer-by-layer self-assemble. Specifically, the substrate was immersed alternatively into the positive-charged PANI solution and the negative-charged GO dispersion forming compact stacked bilayers, and the GO could be reduced into graphene resulting in graphene/PANI films. More importantly, the graphene/PANI films demonstrated good electrical conductivity and high volumetric capacitance even in a neutral Na2SO4 electrolyte [237].
Dong et al. [241, 242] grew 3D graphene on the substrate of nickel foams and chemically synthesized PANI onto the surface of the 3D feature obtaining porous graphene/PANI composite which exhibited high specific capacitance and good cycling stability. A controlled morphology of hierarchical PANI nanowire arrays grown on the plane of GO nanosheets was obtained by Xu et al. [182]. The authors suspected the oxygen functional groups on the plane of the GO sheets acted as anchor sites and enabled the attaching of PANI nanowires on the surface of GO. The π-π stacking force was also considered to be the beneficial factor that promoted the initial nuclei of PANI on the GO sheets. Later, Li et al. [243] synthesized oriented PANI arrays on expended graphite sheets. The morphology of the composites could be adjusted by varying the ratio of expended graphite sheets and aniline monomer. These methods demonstrated morphology engineering at the nanoscale level, producing convenient approaches for fabricating conducting polymer composite material with designed morphology.
In various GO or graphene and PANI composites, the capacitance were greatly improve by introducing PANI along with high cycling stability due to the synergistic effect between the two components (Table 2). The close contact of graphene sheets and PANI backbone allows strong conjugation interaction between the two that promotes fast charge transfer resulting in improved electrochemical properties. Also, the fast charge transfer prevents the charge accumulation of electrons produced by faradic reaction of PANI thus decelerating structure conformation of PANI during electrochemical reaction which eventually benefit to good cycling stability. Moreover, with careful engineering, PANI could modify pore structure of graphene by acting as a spacer to stop layer restack to produce favourable pores facilitating the transfer of ions within the electrolyte.Composites based on graphene/CNT/PANI were synthesized and studied as electrode material for supercapacitors. The composite showed high specific capacitance comparable to or even better than that of graphene/PANI composites [244]. More importantly, the graphene/CNT/PANI showed a super high cycling retention of 96 % after 5000 cycles [245].
Conclusions
CDI is a novel ion removal technology that uses static electrical force to drive ions to the charged electrode and stores the ions into porous structure of the electrode. Developing more efficient electrode materials is the key to improving salt removal performance. The current work reviewed up-to-date progress on electrode fabrication in application of CDI. Fundamental principal (e.g. EDL theory and adsorption isotherms) and process factors (e.g. pore distribution, potential, salt type and concentration) of CDI performance were presented first. It was then followed by in-depth discussion and comparison on properties and fabrication technique of different electrodes, including carbon aerogel, activated carbon, carbon nanotubes, graphene and ordered mesoporous carbon. Novel nanomaterials such as graphene and CNTs have been drawing increased attention in this field with their extremely high specific surface area and super electrical properties. However, research in the use of CNT and graphene as CDI electrodes is still in its infancy, and initial milestones such as large scale of synthesis and fabrication of high surface area graphene and CNT CDI electrodes have not been reached yet. Although CDI and MCDI have shown practicality and cost-effectiveness in brackish water treatment, only few semi-pilot scale demonstration of the CDI or MCDI has been performed so far and no complete pilot scale demonstration has been performed yet [270–272], not to mention demonstrations of graphene and CNT-based CDI systems. Full-scale CDI design with enhanced energy efficiency will be the focus of future endeavour in this area. Finally, it is noteworthy that PANI as conductive polymer has great potential in the CDI application as electrode-enhancing materials. It is envisaged that large-scale PANI-assisted CDI electrode fabrication can be plausible due to its low cost, mechanical flexibility and good electrical properties.
References
Caudle DD (1966) Electrochemical demineralization of water with carbon electrodes. U.S. Dept. of the Interior, Washington, p 188, Research and development progress report
Johnson AM, Venolia AW, Wilbourne RG, Newman J (1970) The electrosorb process for desalting water. U.S. Dept. of the Interior, Washington, p 516, Research and development progress report
Johnson AM, Newman J (1971) Desalting by means of porous carbon electrodes. J Electrochem Soc 118(3):510–517
Johnson AM, Venolia AW, Newman J, Wilbourne RG, Wong CM, Gillam WS (1970) Electrosorb process for desalting water, Office of Saline Water Research and Development. Progress Report No 516.
Bockris JOM, Reddy AKN, Modern Electrochemistry 2B: Electrodics in Chemistry, Engineering, Biology and Environmental Science. 2nd ed., Revised: Kluwer Academic Publishers 2000.
Biesheuvel PM (2009) Thermodynamic cycle analysis for capacitive deionization. J Colloid Interface Sci 332(1):258–264
Biesheuvel PM, van Limpt B, van der Wal A (2009) Dynamic adsorption/desorption process model for capacitive deionization. J Phys Chem C 113(14):5636–5640
Zhao R, Biesheuvel PM, Miedema H, Bruning H, van der Wal A (2010) Charge efficiency: a functional tool to probe the double-layer structure inside of porous electrodes and application in the modeling of capacitive deionization. J Phys Chem Lett 1(1):205–210
Avraham E, Bouhadana Y, Soffer A, Aurbach D (2009) Limitation of charge efficiency in capacitive deionization I: on the behavior of single activated carbon. J Electrochem Soc 156(6):95–99
Avraham E, Noked M, Bouhadana Y, Soffer A, Aurbach D (2010) Limitations of charge efficiency in capacitive deionization processes III: the behavior of surface oxidized activated carbon electrodes. Electrochim Acta 56(1):441–447
Noked M, Avraham E, Soffer A, Aurbach D (2009) The rate-determining step of electroadsorption processes into nanoporous carbon electrodes related to water desalination. J Phys Chem C 113(51):21319–21327
Jayson GG, Sangster JA, Thompson G, Wilkinson MC (1987) Adsorption and electrosorption of mercury(II) acetate onto activated charcoal cloth from aqueous solution. Carbon 25(4):523–531
Gabelich CJ, Tran TD, Suffet IHM (2002) Electrosorption of inorganic salts from aqueous solution using carbon aerogels. Environ Sci Technol 36(13):3010–3019
Li H, Pan L, Lu T, Zhan Y, Nie C, Sun Z (2011) A comparative study on electrosorptivebehavior of carbon nanotubes and graphene for capacitive deionization. J Electroanal Chem 653(1-2):40–44
Li H, Pan L, Zhang Y, Zou L, Sun C, Zhan Y (2010) Kinetics and thermodynamics study for electrosorption of NaCl onto carbon nanotubes and carbon nanofibers electrodes. Chem Phys Lett 485(1-3):161–166
Li H, Zou L, Pan L, Sun Z (2010) Using graphene nano-flakes as electrodes to remove ferric ions by capacitive deionization. Sep Purif Technol 75(1):8–14
Li H, Zou L, Pan L, Sun Z (2010) Novel graphene-like electrodes for capacitive deionization. Environ Sci Technol 44(22):8692–8697
Ban A, Schafer A, Wendt H (1998) Fundamentals of electrosorption on activated carbon for wastewater treatment of industrial effluents. J Appl Electrochem 28(3):227–236
Gabelich CJ, Green JF, Duin SJ, Suffet IH, Tran TD (1999) Capacitive deionization with carbon aerogels: the effects of operational parameters on system performance, Proc. - Water Qual. Technol. Conf. 1316-1327.
Yang K-L, Ying T-Y, Yiacoumi S, Tsouris C, Vittoratos ES (2001) Electrosorption of ions from aqueous solutions by carbon aerogel: an electrical double-layer model. Langmuir 17(6):1961–1969
Morishita T, Soneda Y, Tsumura T, Inagaki M (2006) Preparation of porous carbons from thermoplastic precursors and their performance for electric double layer capacitors. Carbon 44:2360–2367
Kim YS, Guo XF, Kim GJ (2010) Synthesis of carbon monolith with bimodal meso/macroscopic pore structure and its application in asymmetric catalysis. Catal Today 150:91–99
Rolison DR (2003) Catalytic nanoarchitectures—the importance of nothing and the unimportance of periodicity. Science 299:1698–1701
Peng Z, Zhang D, Shi L, Yan T, Yuan S, Li H (2011) Comparative electroadsorption study of mesoporous carbon electrodes with various pore structures. J Phys Chem C 115(34):17068–17076
Farmer JC, Fix DV, Mack GV, Pekala RW, Poco JF (1995) Capacitive deionization of water: an innovative new process. Proc. - 5th International Conference on Radioactive Waste Management and Environmental Remediation 1215-1220.
Farmer JC, Fix DV, Mack GV, Pekala RW, Poco JF (1996) Capacitive deionization of NH4ClO4 solutions with carbon aerogel electrodes. J Appl Electrochem 26(10):1007–1018
Lee JH, Bae WS, Choi JH (2010) Electrode reactions and adsorption/desorption performance related to the applied potential in a capacitive deionization process. Desalination 258(1-3):159–163
Seo S-J, Jeon H, Lee JK, Kim G-Y, Park D, Nojima H (2010) Investigation on removal of hardness ions by capacitive deionization (CDI) for water softening applications. Water Res 44(7):2267–2275
Noked M, Avraham E, Soffer A, Aurbach D (2010) Assessing the concentration effect on hydration radii in aqueous solutions by electroadsorption on a carbon molecular sieve electrode. J Phys Chem C 114(31):13354–13361
Bansal RC (2005) Activated carbon adsorption. Taylor & Francis/CRC Press, Boca Raton
Teng H, Yeh T-S, Hsu LY (1998) Preparation of activated carbon from bituminous coal with phosphoric acid activation. Carbon 36(9):1387–1395
Murphy GW, Cooper JL, United S, University of O (1969) Activated carbon used as electrodes in electrochemical demineralization of saline water. U.S. Dept. of the Interior, Washington, D.C
Zou L, Morris G, Qi D (2008) Using activated carbon electrode in electrosorptive deionisation of brackish water. Desalination 225(1-3):329–340
Mossad M, Zou L (2012) A study of the capacitive deionisation performance under various operational conditions. J Hazard Mater 213–214:491–497
Lee JB, Park KK, Yoon SW, Park PY, Park KI, Lee CW (2009) Desalination performance of a carbon-based composite electrode. Desalination 237(1-3):155–161
Choi JH (2010) Fabrication of a carbon electrode using activated carbon powder and application to the capacitive deionization process. Sep Purif Technol 70(3):362–366
Lim JA, Park NS, Park JS, Choi JH (2009) Fabrication and characterization of a porous carbon electrode for desalination of brackish water. Desalination 238(1-3):37–42
Chang L, Yu Y, Duan X, Liu W (2012) Capacitive deionization performance of activated carbon electrodes prepared by a novel liquid binder. Sep Sci Technol 48(2):359–365
Hou CH, Huang JF, Lin HR, Wang BY (2012) Preparation of activated carbon sheet electrode assisted electrosorption process. J Taiwan Inst Chem Eng 43(3):473–479
Kim Y-J, Hur J, Bae W, Choi JH (2010) Desalination of brackish water containing oil compound by capacitive deionization process. Desalination 253(1-3):119–123
Bouhadana Y, Avraham E, Soffer A, Aurbach D (2010) Several basic and practical aspects related to electrochemical deionization of water. AIChE J 56(3):779–789
Bouhadana Y, Ben-Tzion M, Soffer A, Aurbach D (2011) A control system for operating and investigating reactors: the demonstration of parasitic reactions in the water desalination by capacitive de-ionization. Desalination 268(1-3):253–261
Avraham E, Noked M, Bouhadana Y, Soffer A, Aurbach D (2009) Limitations of charge efficiency in capacitive deionization II. On the behavior of CDI cells comprising two activated carbon electrodes, J Electrochem Soc 156(10):157-61.
Kim J-S, Choi J-H (2010) Fabrication and characterization of a carbon electrode coated with cation-exchange polymer for the membrane capacitive deionization applications. J Membr Sci 355(1-2):85–90
Park BH, Choi JH (2010) Improvement in the capacitance of a carbon electrode prepared using water-soluble polymer binder for a capacitive deionization application. Electrochim Acta 55(8):2888–2893
Yang J, Zou L, Song H, Hao Z (2011) Development of novel MnO2/nanoporous carbon composite electrodes in capacitive deionization technology. Desalination 276(1-3):199–206
Chang LM, Duan XY, Liu W (2011) Preparation and electrosorption desalination performance of activated carbon electrode with titania. Desalination 270(1-3):285–290
Li H, Pan L, Nie C, Liu Y, Sun Z (2012) Reduced graphene oxide and activated carbon composites for capacitive deionization. J Mater Chem 22(31):15556–15561
Pekala RW, Farmer JC, Alviso CT, Tran TD, Mayer ST, Miller JM (1998) Carbon aerogels for electrochemical applications. J Non-Cryst Solids 225:74–80
Pekala RW, Mayer ST, Kaschmitter JL, Morrison RL, inventors; Method for making thin carbon foam electrodes patent WO9506002A1. (1995).
Tran TD, Lenz D, Kinoshita K, Droege M (1998) Effects of processing conditions on the physical and electrochemical properties of carbon aerogel composites. Mater Res Soc Proc 496:607-611.
Richard W. Pekala CTA (1992) Carbon aerogels and xerogels. Mater Res Soc Procs 270:3-14
Lee YJ, Jung JC, Park S, Seo JG, Baeck SH, Yoon JR (2010) Preparation and characterization of metal-doped carbon aerogel for supercapacitor. Curr Appl Phys 10(3):947–951
Farmer J, inventor Method and apparatus for capacitive deionization and electrochemical purification of waters, and regeneration of electrodes patent US5425858A. (1995).
Farmer JC, inventor Method and apparatus for capacitive deionization and electrochemical purification and regeneration of electrodes patent US5954937A. (1999).
Farmer JC, Fix DV, Mack GV, Pekala RW, Poco JF (1996) Capacitive deionization of NaCl and NaNO3 aq. solutions with carbon aerogel electrodes. J Electrochem Soc 143(1):159–169
Farmer JC, Fix DV, Mack GV, Pekala RW, Poco JF (1995) Capacitive deionization with carbon aerogel electrodes: carbonate, sulfate, and phosphate. Int SAMPE Tech Conf 27:294–304
Farmer JC, Fix DV, Pekala RW, Nielsen JK, Volpe AM, Dietrich DD (1996) The use of carbon aerogel electrodes for environmental cleanup. Prepr Pap - Am Chem Soc, Div Fuel Chem 41(1):484–487
Yang CM, Choi WH, Na B-K, Cho BW, Cho WI (2005) Capacitive deionization of NaCl solution with carbon aerogel-silica gel composite electrodes. Desalination 174(2):125–133
Tanaka S, Nishiyama N, Morphology control of ordered mesoporous carbon using organic-templating approach, progress in molecular and environmental bioengineering—from analysis and modeling to technology applications. In Progress in Molecular and Environmental Bioengineering—from Analysis and Modeling to Technology Applications; Carpi A. Ed.; InTech, 2011.
Ryoo R, Joo SH, Kruk M, Jaroniec M (2001) Ordered mesoporous carbons. Adv Mater 13(9):677–681
Li L, Zou L, Song H, Morris G (2009) Ordered mesoporous carbons synthesized by a modified sol-gel process for electrosorptive removal of sodium chloride. Carbon 47(3):775–781
Zou L, Li L, Song H, Morris G (2008) Using mesoporous carbon electrodes for brackish water desalination. Water Res 42(8-9):2340–2348
Zou L, Li L, Song H, Morris G (2010) Improving the capacitive deionisation performance by optimising pore structures of the electrodes. Water Sci Technol 61(5):1227–1233
Tsouris C, Mayes R, Kiggans J, Sharma K, Yiacoumi S, DePaoli D (2011) Mesoporous carbon for capacitive deionization of saline water. Environ Sci Technol 45(23):10243–10249
Nadakatti S, Tendulkar M, Kadam M (2011) Use of mesoporous conductive carbon black to enhance performance of activated carbon electrodes in capacitive deionization technology. Desalination 268(1-3):182–188
Peng Z, Zhang D, Shi L, Yan T (2012) High performance ordered mesoporous carbon/carbon nanotube composite electrodes for capacitive deionization. J Mater Chem 22(14):6603–6612
Choi W, Graphene : Synthesis and applications, CRC Press 2011.
Peigney A, Laurent C, Flahaut E, Bacsa RR, Rousset A (2001) Specific surface area of carbon nanotubes and bundles of carbon nanotubes. Carbon 39(4):507–514
Foo KY, Hameed BH (2009) A short review of activated carbon assisted electrosorption process: an overview, current stage and future prospects. J Hazard Mater 170(2-3):552–559
Oren Y (2008) Capacitive deionization (CDI) for desalination and water treatment—past, present and future (a review). Desalination 228:10–29
Dai K, Shi L, Fang J, Zhang D, Yu B (2005) NaCl adsorption in multi-walled carbon nanotubes. Mater Lett 59(16):1989–1992
Dai K, Shi L, Zhang D, Fang J (2006) NaCl adsorption in multi-walled carbon nanotube/active carbon combination electrode. Chem Eng Sci 61(2):428–433
Gao Y, Pan L, Li H, Zhang Y, Zhang Z, Chen Y (2009) Electrosorption behavior of cations with carbon nanotubes and carbon nanofibres composite film electrodes. Thin Solid Films 517(5):1616–1619
Zhang D, Shi L, Fang J, Dai K (2007) Influence of diameter of carbon nanotubes mounted in flow-through capacitors on removal of NaCl from salt water. J Mater Sci 42:2471–2475
Pan L, Wang X, Gao Y, Zhang Y, Chen Y, Sun Z (2009) Electrosorption of anions with carbon nanotube and nanofibre composite film electrodes. Desalination 244(1-3):139–143
Nie C, Pan L, Li H, Chen T, Lu T, Sun Z (2012) Electrophoretic deposition of carbon nanotubes film electrodes for capacitive deionization. J Electroanal Chem 666:85–88
Wang L, Wang M, Huang Z-H, Cui T, Gui X, Kang F (2011) Capacitive deionization of NaCl solutions using carbon nanotube sponge electrodes. J Mater Chem 21(45):18295–18299
Peng Z, Zhang D, Yan T, Zhang J, Shi L (2013) Three-dimensional micro/mesoporous carbon composites with carbon nanotube networks for capacitive deionization. Appl Surface Sci 282:965–973
Nie C, Pan L, Liu Y, Li H, Chen T, Lu T (2012) Electrophoretic deposition of carbon nanotube/polyacrylic acid composite film electrode for capacitive deionization. Electrochim Acta 66:106–109
Sui Z, Meng Q, Zhang X, Ma R, Cao B (2012) Green synthesis of carbon nanotube-graphene hybrid aerogels and their use as versatile agents for water purification. J Mater Chem 22(18):8767–8771
Zhang D, Yan T, Shi L, Peng Z, Wen X, Zhang J (2012) Enhanced capacitive deionization performance of graphene/carbon nanotube composites. J Mater Chem 22(29):14696–14704
Li H, Lu T, Pan L, Zhang Y, Sun Z (2009) Electrosorption behavior of graphene in NaCl solutions. J Mater Chem 19(37):6773–6779
Wang Z, Dou B, Zheng L, Zhang G, Liu Z, Hao Z (2012) Effective desalination by capacitive deionization with functional graphene nanocomposite as novel electrode material. Desalination 299:96–102
Wang Z, Yue L, Liu ZT, Liu ZH, Hao Z (2012) Functional graphene nanocomposite as an electrode for the capacitive removal of FeCl3 from water. J Mater Chem 22(28):14101–14107
Jia B, Zou L (2012) Graphene nanosheets reduced by a multi-step process as high-performance electrode material for capacitive deionisation. Carbon 50(6):2315–2321
Wang H, Zhang D, Yan T, Wen X, Shi L, Zhang J (2012) Graphene prepared via a novel pyridine–thermal strategy for capacitive deionization. J Mater Chem 22:23745–23748
Lei H, Yan T, Wang H, Shi L, Zhang J, Zhang D (2015) Graphene-like carbon nanosheets prepared by a Fe-catalyzed glucose-blowing method for capacitive deionization. J Mater Chem A 3:5934–5941
Wen X, Zhang D, Yan T, Zhang J, Shi L (2013) Three-dimensional graphene-based hierarchically porous carbon composites prepared by a dual-template strategy for capacitive deionization. J Mater Chem A 1:12334–12344
Wang H, Zhang D, Yan T, Wen X, Zhang J, Shi L, Zhong Q (2013) Three-dimensional macroporous graphene architectures as high performance electrodes for capacitive deionization. J Mater Chem A 1:11778–11789
Zhang D, Wen X, Shi L, Yan T, Zhang J (2012) Enhanced capacitive deionization of graphene/mesoporous carbon composites. Nanoscale 4:5440–5446
Wang H, Shi L, Yan T, Zhang J, Zhong Q, Zhang D (2014) Design of graphene-coated hollow mesoporous carbon spheres as high performance electrodes for capacitive deionization. J Mater Chem A 2:4739–4750
Ryoo MW, Kim JH, Seo G (2003) Role of titania incorporated on activated carbon cloth for capacitive deionization of NaCl solution. J Colloid Interface Sci 264(2):414–419
Ryoo MW, Seo G (2003) Improvement in capacitive deionization function of activated carbon cloth by titania modification. Water Res 37(7):1527–1534
Oh HJ, Lee JH, Ahn HJ, Jeong Y, Kim YJ, Chi CS (2006) Nanoporous activated carbon cloth for capacitive deionization of aqueous solution. Thin Solid Films 515(1):220–225
Myint M, Al-Harthi S, Dutta J (2014) Brackish water desalination by capacitive deionization using zinc oxide micro/nanostructures grafted on activated carbon cloth electrodes. Desalination 344:236–242
Leonard KC, Genthe JR, Sanfilippo JL, Zeltner WA, Anderson MA (2009) Synthesis and characterization of asymmetric electrochemical capacitive deionization materials using nanoporous silicon dioxide and magnesium doped aluminum oxide. Electrochim Acta 54(22):5286–5291
Haro M, Rasines G, Macias C, Ania CO (2011) Stability of a carbon gel electrode when used for the electro-assisted removal of ions from brackish water. Carbon 49(12):3723–3730
Porada S, Weinstein L, Dash R, van der Wal A, Bryjak M, Gogotsi Y (2012) Water desalination using capacitive deionization with microporous carbon electrodes. ACS Appl Mater Interfaces 4(3):1194–1199
Yang J, Zou L, Song H (2012) Preparing MnO2/PSS/CNTs composite electrodes by layer-by-layer deposition of MnO2 in the membrane capacitive deionization. Desalination 286:108–114
Liu Q, Wang Y, Zhang Y, Xu S, Wang J (2012) Effect of dopants on the adsorbing performance of polypyrrole/graphite electrodes for capacitive deionization process. Synth Met 162(7-8):655–661
El-Deen A, Barakat N, Khalild K, Kim H (2014) Hollow carbon nanofibers as an effective electrode for brackish water desalination using the capacitive deionization process. New J Chem 38:198–205
Huang Z-H, Wang M, Wang L, Kang F (2012) Relation between the charge efficiency of activated carbon fiber and its desalination performance. Langmuir 28(11):5079–5084
Wen X, Zhang D, Shi L, Yan T, Wang H, Zhang J (2012) Three-dimensional hierarchical porous carbon with a bimodal pore arrangement for capacitive deionization. J Mater Chem 22:23835–23844
M.D. Andelman, Charge barrier flow-through capacitor, Can. Patent CA 2444390 (2002).
Li H, Gao Y, Pan L, Zhang Y, Chen Y, Sun Z (2008) Electrosorptive desalination by carbon nanotubes and nanofibres electrodes and ion-exchange membranes. Water Res 42(20):4923–4928
Biesheuvel PM, van der Wal A (2010) Membrane capacitive deionization, J. Membr. Sci. 346(2):256-62
Kim YJ, Choi JH (2010) Enhanced desalination efficiency in capacitive deionization with an ion-selective membrane. Sep Purif Technol 71(1):70–75
Lee JH, Choi JH (2012) The production of ultrapure water by membrane capacitive deionization (MCDI) technology. J Membr Sci 409–410:251–256
Villar I, Roldan S, Ruiz V, Granda M, Blanco C, Menendez R (2010) Capacitive deionization of NaCl solutions with modified activated carbon electrodes. Energy Fuels 24(6):3329–3333
Chen Z, Song C, Sun X, Guo H, Zhu G (2011) Kinetic and isotherm studies on the electrosorption of NaCl from aqueous solutions by activated carbon electrodes. Desalination 267(2-3):239–243
Wang G, Pan C, Wang L, Dong Q, Yu C, Zhao Z (2012) Activated carbon nanofiber webs made by electrospinning for capacitive deionization. Electrochim Acta 69:65–70
Ying TY, Yang KL, Yiacoumi S, Tsouris C (2002) Electrosorption of ions from aqueous solutions by nanostructured carbon aerogel. J Colloid Interface Sci 250(1):18–27
Jung HH, Hwang SW, Hyun SH, Lee KH, Kim GT (2007) Capacitive deionization characteristics of nanostructured carbon aerogel electrodes synthesized via ambient drying. Desalination 216(1-3):377–385
Xu P, Drewes JE, Heil D, Wang G (2008) Treatment of brackish produced water using carbon aerogel-based capacitive deionization technology. Water Res 42(10-11):2605–2617
Wang S, Wang D, Ji L, Gong Q, Zhu Y, Liang J (2007) Equilibrium and kinetic studies on the removal of NaCl from aqueous solutions by electrosorption on carbon nanotube electrodes. Sep Purif Technol 58(1):12–16
Wang M, Huang Z-H, Wang L, Wang MX, Kang F, Hou H (2010) Electrospun ultrafine carbon fiber webs for electrochemical capacitive desalination. New J Chem 34(9):1843–1845
Wang XZ, Li MG, Chen YW, Cheng RM, Huang SM, Pan LK (2006) Electrosorption of ions from aqueous solutions with carbon nanotubes and nanofibers composite film electrode. Appl Phys Lett 89:053127
Jang J, Bae J, Choi M, Yoon SH (2005) Fabrication and characterization of polyaniline coated carbon nanofiber for supercapacitor. Carbon 43(13):2730–2736
Seize, Black aniline, Journal of Colorists and Dyists. 1842.
de Albuquerque JE, Mattoso LHC, Faria RM, Masters JG, MacDiarmid AG (2004) Study of the interconversion of polyaniline oxidation states by optical absorption spectroscopy. Synth Met 146(1):1–10
McCall RP, Roe MG, Ginder JM, Kusumoto T, Epstein AJ, Asturias GE (1989) IR absorption, photoinduced IR absorption, and photoconductivity of polyaniline. Synth Met 29(1):433–438
Richter AF, Ray A, Ramanathan KV, Manohar SK, Furst GT, Opella SJ (1989) 15 N NMR of polyaniline. Synth Met 29(1):243–249
Annis BK, Specht ED, Theophilou N, MacDiarmid AG (1991) Structural aspects of stretched emeraldine as determined by X-ray scattering. Polymer 32(7):1160–1166
Cowan DL, Priest V, Marrero TR, Slaughter DW (1990) Electrical conductivity in polyaniline. J Phys Chem Solids 51(4):307–312
MacDiarmid AG, Epstein AJ (1994) The concept of secondary doping as applied to polyaniline. Synth Met 65(2-3):103–116
MacDiarmid AG, Epstein AJ (1995) Secondary doping in polyaniline. Synth Met 69(1-3):85-92
Stafstrom S, Bredas JL, Epstein AJ, Woo HS, Tanner DB, Huang WS (1987) Polaron lattice in highly conducting polyaniline: theoretical and optical studies. Phys Rev Lett 59(13):1464–1467
Hua MY, Hwang GW, Chuang YH, Chen SA, Tsai RY (2000) Soluble n-doped polyaniline: synthesis and characterization. Macromolecules 33(17):6235–6238
Zengin H, Zhou W, Jin J, Czerw R, Smith DW, Echegoyen L (2002) Carbon nanotube doped polyaniline. J Adv Mater 14(20):1480–1483
Zhou H, Lin Y, Yu P, Su L, Mao L (2009) Doping polyaniline with pristine carbon nanotubes into electroactive nanocomposite in neutral and alkaline media. Electrochem Commun 11(5):965–968
Singh P, Singh RA (2012) Preparation and characterization of polyaniline nanostructures via a interfacial polymerization method. Synth Met 162(24):2193–2200
Bai X, Mei J, Bai Y, Mu Z (2012) Synthesis and characterization of polyaniline nanotubes doped with amino acetic acid. Appl Mech Mater (184-185):1285-1288
Gmati F, Fattoum A, Manaii A, Mohamed AB (2012) Effects of the action of hydrogen peroxide on the electrical properties of polyaniline-aluminium composites. J Phys D Appl Phys 315405/1-/9.
Palaniappan S, Sairam M (2008) Benzoyl peroxide as a novel oxidizing agent in a polyaniline dispersion: Synthesis and characterization of a pure polyaniline–poly(vinyl pyrrolidone) composite. J Appl Polym Sci 108(2):825–832
Sydulu Singu B, Srinivasan P, Pabba S (2012) Benzoyl peroxide oxidation route to nano form polyaniline salt containing dual dopants for pseudocapacitor. J Electrochem Soc 159(1):A6-A13.
Zhang Z, Deng J, Wan M (2009) Highly crystalline and thin polyaniline nanofibers oxidized by ferric chloride. Mater Chem Phys 115(1):275–279
Zhang L, Wan M, Wei Y (2006) Nanoscaled polyaniline fibers prepared by ferric chloride as an oxidant. Macromol Rapid Commun 27(5):366–371
Wang Y, Liu Z, Han B, Sun Z, Huang Y, Yang G (2004) Facile synthesis of polyaniline nanofibers using chloroaurate acid as the oxidant. Langmuir 21(3):833–836
Yang W, Liu J, Zheng R, Liu Z, Dai Y, Chen G (2008) Ionic liquid-assisted synthesis of polyaniline/gold nanocomposite and its biocatalytic application. Nanoscale Res Lett 3(11):468–472
Sapurina IY, Shishov MA (2012) Oxidative polymerization of aniline: molecular synthesis of polyaniline and the formation of supramolecular structures. In New Polymers for Special Applications; De Souza Gomes A. Ed.; InTech, 2012.
Tran HD, Wang Y, D’Arcy JM, Kaner RB (2008) Toward an understanding of the formation of conducting polymer nanofibers. ACS Nano 2(9):1841–1848
Stejskal J, Riede A, Hlavatá D, Jan P, Helmstedt M, Holler P (1998) The effect of polymerization temperature on molecular weight, crystallinity, and electrical conductivity of polyaniline. Synth Met 96(1):55–61
Stejskal J, Gilbert RG (2002) Polyaniline: preparation of a conducting polymer. Pure Appl Chem 74(5):857–867
Wei Z, Zhang Z, Wan M (2002) Formation mechanism of self-assembled polyaniline micro/nanotubes. Langmuir 18(3):917–921
Chiou N-R, Lee LJ, Epstein AJ (2007) Self-assembled polyaniline nanofibers/nanotubes. Chem Mater 19(15):3589–3591
Zhang L, Zujovic ZD, Peng H, Bowmaker GA, Kilmartin PA, Travas-Sejdic J (2008) Structural characteristics of polyaniline nanotubes synthesized from different buffer solutions. Macromolecules 41(22):8877–8884
Zhong W, Wang Y, Yan Y, Sun Y, Deng J, Yang W (2007) Fabrication of shape-controllable polyaniline micro/nanostructures on organic polymer surfaces: obtaining spherical particles, wires, and ribbons. J Phys Chem B 111(15):3918–3926
Zhu Y, Hu D, Wan MX, Jiang L, Wei Y (2007) Conducting and superhydrophobic rambutan-like hollow spheres of polyaniline. Adv Mater 19(16):2092–2096
Li G, Zhang C, Peng H (2008) Facile synthesis of self-assembled polyaniline nanodisks. Macromol Rapid Commun 29(1):63–67
Sapurina I, Stejskal J (2008) The mechanism of the oxidative polymerization of aniline and the formation of supramolecular polyaniline structures. Polym Int 57(12):1295–1325
Subramania A, Devi SL (2008) Polyaniline nanofibers by surfactant-assisted dilute polymerization for supercapacitor applications. Polym Adv Technol 19(7):725–727
Chiou NR, Epstein AJ (2005) Polyaniline nanofibers prepared by dilute polymerization. Adv Mater 17(13):1679–1683
Anilkumar P, Jayakannan M (2008) Divergent nanostructures from identical ingredients: unique amphiphilic micelle template for polyaniline nanofibers, tubes, rods, and spheres. Macromolecules 41(20):7706–7715
Zhang L, Zhang L, Wan M, Wei Y (2006) Polyaniline micro/nanofibers doped with saturation fatty acids. Synth Met 156(5-6):454–458
Konyushenko EN, Stejskal J, Šeděnková I, Trchová M, Sapurina I, Cieslar M (2006) Polyaniline nanotubes: conditions of formation. Polym Int 55(1):31–39
Huang J, Kaner RB (2003) A general chemical route to polyaniline nanofibers. J Am Chem Soc 126(3):851–855
Zhang X, Chan-Yu-King R, Jose A, Manohar SK (2004) Nanofibers of polyaniline synthesized by interfacial polymerization. Synth Met 145(1):23–29
Rezaei F, Tavandashti N, Zahedi A (2008) Morphology of polyaniline nanofibers synthesized under different conditions. Res Chem Intermed 40:1233-1247
Ding H, Wan M, Wei Y (2007) Controlling the diameter of polyaniline nanofibers by adjusting the oxidant redox potential. Adv Mater 19(3):465–469
Wu J, Tang Q, Li Q, Lin J (2008) Self-assembly growth of oriented polyaniline arrays: a morphology and structure study. Polymer 49(24):5262–5267
Ding Z, Yang D, Currier RP, Obrey SJ, Zhao Y (2009) Polyaniline morphology and detectable intermediate aggregates. Macromol Chem Phys 211(6):627–634
Bhadra S, Khastgir D, Singha NK, Lee JH (2009) Progress in preparation, processing and applications of polyaniline. Prog Polym Sci 34(8):783–810
Blinova NV, Stejskal J, Trchová M, Sapurina I, Ćirić-Marjanovićc G (2009) The oxidation of aniline with silver nitrate to polyaniline silver composites. Polymer 50(1):50–56
Zhang X, Goux WJ, Manohar SK (2004) Synthesis of polyaniline nanofibers by nanofiber seeding. J Am Chem Soc 126(14):4502–4503
Prathap MUA, Srivastava R (2011) Morphological controlled synthesis of micro-/nano-polyaniline. J Polym Res 18(6):2455–2467
Garai A, Nandi AK (2009) Tuning of different polyaniline nanostructures from a coacervate gel/sol template. Synt Met 159(7):757–760
Song G, Han J, Bo J, Guo R (2009) Synthesis of polyaniline nanostructures in different lamellar liquid crystals and application to lubrication. J Mater Sci 44(3):715–720
Deepshikha, Basu T (2011) The role of structure directing agents on chemical switching properties of nanostructured conducting polyaniline (NSPANI). Res J Chem Sci 1(6):20-9.
Quillard S, Louarn G, Lefrant S, Macdiarmid AG (1994) Vibrational analysis of polyaniline: a comparative study of leucoemeraldine, emeraldine, and pernigraniline bases. Phys Rev B 50(17):12496–12508
Mazeikiene R, Malinauskas A (1996) Electrochemical behaviour of polyaniline film polymerized by the use of a chemical oxidation step. Electrochim Acta 41(10):1587–1591
Kang ET, Neoh KG, Tan KL (1998) Polyaniline: a polymer with many interesting intrinsic redox states. Progr Polym Sci 23(2):277–324
Volfkovich YM, Sergeev AG, Zolotova TK, Afanasiev SD, Efimov ON, Krinichnaya EP (1999) Macrokinetics of polyaniline based electrode: effects of porous structure, microkinetics, diffusion, and electrical double layer. Electrochim Acta 44(10):1543–1558
Malinauskas A, Holze R (1998) An in situ spectroelectrochemical study of redox reactions at polyaniline-modified ITO electrodes. Electrochim Acta 43(18):2563–2575
Ram MK, Salerno M, Adami M, Faraci P, Nicolini C (1999) Physical properties of polyaniline films: assembled by the layer-by-layer technique. Langmuir 15(4):1252–1259
Hu CC, Chu CH (2001) Electrochemical impedance characterization of polyaniline-coated graphite electrodes for electrochemical capacitors: effects of film coverage/thickness and anions. J Electroanal Chem 503(1-2):105–116
Ryu KS, Kim KM, Park NG, Park YJ, Chang SH (2002) Symmetric redox supercapacitor with conducting polyaniline electrodes. J Power Sources 103(2):305–309
Pauliukaite R, Brett CMA, Monkman AP (2004) Polyaniline fibres as electrodes: electrochemical characterisation in acid solutions. Electrochim Acta 50(1):159–167
Mi H, Zhang X, Yang S, Ye X, Luo J (2008) Polyaniline nanofibers as the electrode material for supercapacitors. Mater Chem Phys 112(1):127–131
Cao Y, Mallouk TE (2008) Morphology of template-grown polyaniline nanowires and its effect on the electrochemical capacitance of nanowire arrays. Chem Mater 20(16):5260–5265
Wang K, Huang J, Wei Z (2010) Conducting polyaniline nanowire arrays for high performance supercapacitors. J Phys Chem C 114(17):8062–8067
Xu J, Wang K, Zu SZ, Han BH, Wei Z (2010) Hierarchical nanocomposites of polyaniline nanowire arrays on graphene oxide sheets with synergistic effect for energy storage. ACS Nano 4(9):5019–5026
Zhang L, Zhao G, Wang Y (2013) Polyaniline nanowire electrodes with high capacitance synthesized by a simple approach. Mater Sci Eng C 33(1):209–212
Zhao G-Y, Li HL (2008) Preparation of polyaniline nanowire arrayed electrodes for electrochemical supercapacitors. Microporous Mesoporous Mater 110(2-3):590–594
Qin Q, Zhang R (2013) A novel conical structure of polyaniline nanotubes synthesized on ITO-PET conducting substrate by electrochemical method. Electrochim Acta 89:726–731
Mi H, Zhang X, Ye X, Yang S (2008) Preparation and enhanced capacitance of core-shell polypyrrole/polyaniline composite electrode for supercapacitors. J Power Sources 176(1):403–409
Kim BC, Kwon JS, Ko JM, Park JH, Too CO, Wallace GG (2010) Preparation and enhanced stability of flexible supercapacitor prepared from nafion/polyaniline nanofiber. Synth Met 160(1-2):94–98
Zhang X, Ji L, Zhang S, Yang W (2007) Synthesis of a novel polyaniline-intercalated layered manganese oxide nanocomposite as electrode material for electrochemical capacitor. J Power Sources 173(2):1017–1023
Ni W, Wang D, Huang Z, Zhao J, Cui G (2010) Fabrication of nanocomposite electrode with MnO2 nanoparticles distributed in polyaniline for electrochemical capacitor. Mater Chem Phys 124(2):1151–1154
Bian C, Yu A, Wu H (2009) Fibriform polyaniline/nano-TiO2 composite as an electrode material for aqueous redox supercapacitors. Electrochem Commun 11(2):266–269
Oh M, Park S-J, Jung Y, Kim S (2012) Electrochemical properties of polyaniline composite electrodes prepared by in-situ polymerization in titanium dioxide dispersed aqueous solution. Synth Met 162(7):695–701
Li X, Chai Y, Zhang H, Wang G, Feng X (2012) Synthesis of polyaniline/tin oxide hybrid and its improved electrochemical capacitance performance. Electrochim Acta 85:9–15
Saranya S, Selvan RK, Priyadharsini N (2012) Synthesis and characterization of polyaniline/MnWO4 nanocomposites as electrodes for pseudocapacitors. Appl Surf Sci 258(11):4881–4887
Liu Q, Nayfeh MH, Yau ST (2010) Supercapacitor electrodes based on polyaniline-silicon nanoparticle composite. J Power Sources 195(12):3956–3959
Li Y, Zhao X, Xu Q, Zhang Q, Chen D (2011) Facile preparation and enhanced capacitance of the polyaniline/sodium alginate nanofiber network for supercapacitors. Langmuir 27(10):6458–6463
Chen WC, Wen TC, Teng H (2003) Polyaniline-deposited porous carbon electrode for supercapacitor. Electrochim Acta 48(6):641–649
Chen WC, Wen TC (2003) Electrochemical and capacitive properties of polyaniline-implanted porous carbon electrode for supercapacitors. J Power Sources 117(1-2):273–282
Ko JM, Song RY, Yu HJ, Yoon JW, Min BG, Kim DW (2004) Capacitive performance of the composite electrodes consisted of polyaniline and activated carbons powder in a solid-like acid gel electrolyte. Electrochim Acta 50(2-3):873–876
Wang Q, Li J, Gao F, Li W, Wu K, Wang X (2008) Activated carbon coated with polyaniline as an electrode material in supercapacitors. New Carbon Mater 23(3):275–280
Jin Z, Ren X, Qin C, Li B, Quan S, Bai X (2011) Hybrid supercapacitors based on polyaniline and activated carbon composite electrode materials. Pigm Resin Technol 20(4):235–239
Lei Z, Chen Z, Zhao XS (2010) Growth of polyaniline on hollow carbon spheres for enhancing electrocapacitance. J Phys Chem C 114(46):19867–19874
Yan X, Tai Z, Chen J, Xue Q (2011) Fabrication of carbon nanofiber-polyaniline composite flexible paper for supercapacitor. Nanoscale 3(1):212–216
Dalmolin C, Biaggio SR, Rocha-Filho RC, Bocchi N (2009) Preparation, electrochemical characterization and charge/discharge of reticulated vitreous carbon/polyaniline composite electrodes. Electrochim Acta 55(1):227–233
Zheng L, Wang Y, Wang X, Li N, An H, Chen H (2010) The preparation and performance of calcium carbide-derived carbon/polyaniline composite electrode material for supercapacitors. J Power Sources 195(6):1747–1752
Woo SW, Dokko K, Nakano H, Kanamura K (2009) Incorporation of polyaniline into macropores of three-dimensionally ordered macroporous carbon electrode for electrochemical capacitors. J Power Sources 190(2):596–600
Cai JJ, Kong LB, Zhang J, Luo YC, Kang L (2010) A novel polyaniline/mesoporous carbon nano-composite electrode for asymmetric supercapacitor. Chin Chem Lett 21(12):1509–1512
Liu WX, Liu N, Song HH, Chen XH (2011) Properties of polyaniline/ordered mesoporous carbon composites as electrodes for supercapacitors. New Carbon Mater 26(3):217–223
Dou YQ, Zhai Y, Liu H, Xia Y, Tu B, Zhao D (2011) Syntheses of polyaniline/ordered mesoporous carbon composites with interpenetrating framework and their electrochemical capacitive performance in alkaline solution. J Power Sources 196(3):1608–1614
Bian LJ, Luan F, Liu SS, Liu XX (2012) Self-doped polyaniline on functionalized carbon cloth as electroactive materials for supercapacitor. Electrochim Acta 64:17–22
Cheng Q, Tang J, Ma J, Zhang H, Shinya N, Qin LC (2011) Polyaniline-coated electro-etched carbon fiber cloth electrodes for supercapacitors. J Phys Chem C 115(47):23584–23590
Mu B, Liu P, Wang A (2013) Synthesis of polyaniline/carbon black hybrid hollow microspheres by layer-by-layer assembly used as electrode materials for supercapacitors. Electrochim Acta 88:177–183
Deng J, Ding X, Zhang W, Peng Y, Wang J, Long X (2002) Carbon nanotube-polyaniline hybrid materials. Eur Polym J 38(12):2497–2501
Zhou Y, Qin ZY, Li L, Zhang Y, Wei YL, Wang LF (2010) Polyaniline/multi-walled carbon nanotube composites with core-shell structures as supercapacitor electrode materials. Electrochim Acta 55(12):3904–3908
Zhu Z, Wang G, Sun M, Li X, Li C (2011) Fabrication and electrochemical characterization of polyaniline nanorods modified with sulfonated carbon nanotubes for supercapacitor applications. Electrochim Acta 56(3):1366–1372
Gupta V, Miura N (2006) Polyaniline/single-wall carbon nanotube (PANI/SWCNT) composites for high performance supercapacitors. Electrochim Acta 52(4):1721–1726
Zhang H, Cao G, Wang Z, Yang Y, Shi Z, Gu Z (2008) Tube-covering-tube nanostructured polyaniline/carbon nanotube array composite electrode with high capacitance and superior rate performance as well as good cycling stability. Electrochem Commun 10(7):1056–1059
Zhang H, Cao G, Wang W, Yuan K, Xu B, Zhang W (2009) Influence of microstructure on the capacitive performance of polyaniline/carbon nanotube array composite electrodes. Electrochim Acta 54(4):1153–1159
Wu F, Chen J, Li L, Zhao T, Chen R (2011) Improvement of rate and cycle performence by rapid polyaniline coating of a MWCNT/sulfur cathode. J Phys Chem C 115(49):24411–24417
Zhou Y, He B, Zhou W, Huang J, Li X, Wu B (2004) Electrochemical capacitance of well-coated single-walled carbon nanotube with polyaniline composites. Electrochim Acta 49(2):257–262
Choi HJ, Jeon IY, Kang SW, Baek JB (2011) Electrochemical activity of a polyaniline/polyaniline-grafted multiwalled carbon nanotube mixture produced by a simple suspension polymerization. Electrochim Acta 56(27):10023–10031
King RCY, Roussel F, Brun JF, Gors C (2012) Carbon nanotube-polyaniline nanohybrids: influence of the carbon nanotube characteristics on the morphological, spectroscopic, electrical and thermoelectric properties. Synth Met 162(15):1348–1356
Fan H, Zhao N, Wang H, Li X, Xu J (2013) Preparation of carpenterworm-like polyaniline/carbon nanotubes nanocomposites with enhanced electrochemical property. Mater Lett 92:157–160
Mi H, Zhang X, An S, Ye X, Yang S (2007) Microwave-assisted synthesis and electrochemical capacitance of polyaniline/multi-wall carbon nanotubes composite. Electrochem Commun 9(12):2859–2862
Rodrigues FO, Salvatierra RV, Zarbin AJG, Rocco MLM (2013) Investigation of carbon nanotube/polyaniline nanocomposite thin films produced by interfacial polymerization through electron desorption. J Mol Struct 1037:93–98
Ubul A, Jamal R, Rahman A, Awut T, Nurulla I, Abdiryim T (2011) Solid-state synthesis and characterization of polyaniline/multi-walled carbon nanotubes composite. Synth Met 161(19-20):2097–2102
Razak SIA, Ahmad AL, Zein SHS, Boccaccini AR (2009) MnO2-filled multiwalled carbon nanotube/polyaniline nanocomposites with enhanced interfacial interaction and electronic properties. Scripta Mater 61(6):592–595
Li Q, Liu J, Zou J, Chunder A, Chen Y, Zhai L (2011) Synthesis and electrochemical performance of multi-walled carbon nanotube/polyaniline/MnO2 ternary coaxial nanostructures for supercapacitors. J Power Sources 196(1):565–572
Dong B, He BL, Xu CL, Li HL (2007) Preparation and electrochemical characterization of polyaniline/multi-walled carbon nanotubes composites for supercapacitor. Mater Sci Eng B 143(1-3):7–13
Li Y, Peng H, Li G, Chen K (2012) Synthesis and electrochemical performance of sandwich-like polyaniline/graphene composite nanosheets. Eur Polym J 48(8):1406–1412
Kumar NA, Choi HJ, Shin YR, Chang DW, Dai L, Baek JB (2012) Polyaniline-grafted reduced graphene oxide for efficient electrochemical supercapacitors. ACS Nano 6(2):1715–1723
Li J, Xie H, Li Y, Liu J, Li Z (2011) Electrochemical properties of graphene nanosheets/polyaniline nanofibers composites as electrode for supercapacitors. J Power Sources 196(24):10775–10781
Murugan AV, Muraliganth T, Manthiram A (2009) Rapid, facile microwave-solvothermal synthesis of graphene nanosheets and their polyaniline nanocomposites for energy storage. Chem Mater 21(21):5004–5006
Yan X, Chen J, Yang J, Xue Q, Miele P (2010) Fabrication of free-standing, electrochemically active, and biocompatible graphene oxide/polyaniline and graphene/polyaniline hybrid papers. ACS Appl Mater Interfaces 2(9):2521–2529
Wu Q, Xu Y, Yao Z, Liu A, Shi G (2010) Supercapacitors based on flexible graphene/polyaniline nanofiber composite films. ACS Nano 4(4):1963–1970
An J, Liu J, Zhou Y, Zhao H, Ma Y, Li M (2012) Polyaniline-grafted graphene hybrid with amide groups and its use in supercapacitors. J Phys Chem C 116(37):19699–19708
Liu J, An J, Zhou Y, Ma Y, Li M, Yu M (2012) Preparation of an amide group-connected graphene/polyaniline nanofiber hybrid and its application in supercapacitors. ACS Appl Mater Interfaces 4(6):2870–2876
Sarker AK, Hong JD (2012) Layer-by-layer self-assembled multilayer films composed of graphene/polyaniline bilayers: high-energy electrode materials for supercapacitors. Langmuir 28(34):12637–12646
Gao Z, Yang W, Wang J, Wang B, Li Z, Liu Q (2013) A new partially reduced graphene oxide nanosheet/polyaniline nanowafer hybrid as supercapacitor electrode material. Energy Fuels 27(1):568–575
Chen G-L, Shau S-M, Juang T-Y, Lee R-H, Chen C-P, Suen S-Y (2011) Single-layered graphene oxide nanosheet/polyaniline hybrids fabricated through direct molecular exfoliation. Langmuir 27(23):14563–14569
Lai L, Yang H, Wang L, Teh BK, Zhong J, Chou H (2012) Preparation of supercapacitor electrodes through selection of graphene surface functionalities. ACS Nano 6(7):5941–5951
Dong X, Wang J, Wang J, Chan-Park MB, Li X, Wang L (2012) Supercapacitor electrode based on three-dimensional graphene-polyaniline hybrid. Mater Chem Phys 134(2-3):576–580
Yong YC, Dong XC, Chan-Park MB, Song H, Chen P (2012) Macroporous and monolithic anode based on polyaniline hybridized three-dimensional graphene for high-performance microbial fuel cells. ACS Nano 6(3):2394–2400
Li Y, Zhao X, Yu P, Zhang Q (2013) Oriented arrays of polyaniline nanorods grown on graphite nanosheets for an electrochemical supercapacitor. Langmuir 29(1):493–500
Lu X, Dou H, Yang S, Hao L, Zhang L, Shen L (2011) Fabrication and electrochemical capacitance of hierarchical graphene/polyaniline/carbon nanotube ternary composite film. Electrochim Acta 56(25):9224–9232
Yan J, Wei T, Fan Z, Qian W, Zhang M, Shen X (2010) Preparation of graphene nanosheet/carbon nanotube/polyaniline composite as electrode material for supercapacitors. J Power Sources 195(9):3041–3045
Gupta V, Miura N (2006) High performance electrochemical supercapacitor from electrochemically synthesized nanostructured polyaniline. Mater Lett 60(12):1466–1469
Ghenaatian HR, Mousavi MF, Kazemi SH, Shamsipur M (2009) Electrochemical investigations of self-doped polyaniline nanofibers as a new electroactive material for high performance redox supercapacitor. Synth Met 159(17-18):1717–1722
Li GR, Feng ZP, Zhong JH, Wang ZL, Tong YX (2010) Electrochemical synthesis of polyaniline nanobelts with predominant electrochemical performances. Macromolecules 43(5):2178–2183
Dhawale DS, Dubal DP, Jamadade VS, Salunkhe RR, Lokhande CD (2010) Fuzzy nanofibrous network of polyaniline electrode for supercapacitor application. Synth Met 160(5-6):519–522
Dhawale DS, Vinu A, Lokhande CD (2011) Stable nanostructured polyaniline electrode for supercapacitor application. Electrochim Acta 56(25):9482–9487
Yan Y, Cheng Q, Pavlinek V, Saha P, Li C (2012) Fabrication of polyaniline/mesoporous carbon/MnO2 ternary nanocomposites and their enhanced electrochemical performance for supercapacitors. Electrochim Acta 71:27–32
Yang M, Cheng B, Song H, Chen X (2010) Preparation and electrochemical performance of polyaniline-based carbon nanotubes as electrode material for supercapacitor. Electrochim Acta 55(23):7021–7027
Meng C, Liu C, Fan S (2009) Flexible carbon nanotube/polyaniline paper-like films and their enhanced electrochemical properties. Electrochem Commun 11(1):186–189
Meng C, Liu C, Chen L, Hu C, Fan S (2010) Highly flexible and all-solid-state paperlike polymer supercapacitors. Nano Lett 10(10):4025–4031
Mikhaylova AA, Tusseeva EK, Mayorova NA, Rychagov AY, Volfkovich YM, Krestinin AV (2011) Single-walled carbon nanotubes and their composites with polyaniline. Structure, catalytic and capacitive properties as applied to fuel cells and supercapacitors. Electrochim Acta 56(10):3656–3665
Sivakkumar SR, Kim WJ, Choi JA, MacFarlane DR, Forsyth M, Kim DW (2007) Electrochemical performance of polyaniline nanofibres and polyaniline/multi-walled carbon nanotube composite as an electrode material for aqueous redox supercapacitors. J Power Sources 171(2):1062–1068
Zhang JJ, Gu MM, Zheng TT, Zhu JJ (2009) Synthesis of gelatin-stabilized gold nanoparticles and assembly of carboxylic single-walled carbon nanotubes/au composites for cytosensing and drug uptake. Anal Chem 81(16):6641–6648
Gao B, Fu Q, Su L, Yuan C, Zhang X (2010) Preparation and electrochemical properties of polyaniline doped with benzenesulfonic functionalized multi-walled carbon nanotubes. Electrochim Acta 55(7):2311–2318
Yin Y, Liu C, Fan S (2012) Well-constructed CNT mesh/PANI nanoporous electrode and its thickness effect on the supercapacitor properties. J Phys Chem C 116(50):26185–26189
Wang H, Hao Q, Yang X, Lu L, Wang X (2010) Effect of graphene oxide on the properties of its composite with polyaniline. ACS Appl Mater Interfaces 2(3):821–828
Wang DW, Li F, Zhao J, Ren W, Chen ZG, Tan J (2009) Fabrication of graphene/polyaniline composite paper via in situ anodic electropolymerization for high-performance flexible electrode. ACS Nano 3(7):1745–1752
Zhang K, Zhang LL, Zhao XS, Wu J (2010) Graphene/polyaniline nanofiber composites as supercapacitor electrodes. Chem Mater 22(4):1392–1401
Wang H, Hao Q, Yang X, Lu L, Wang XA (2010) Nanostructured graphene/polyaniline hybrid material for supercapacitors. Nanoscale 2(10):2164–2170
Zhou G, Wang D, Li F, Zhang L, Weng Z, Cheng H (2011) The effect of carbon particle morphology on the electrochemical properties of nanocarbon/polyaniline composites in supercapacitors. New Carbon Mater 26(3):180–186
Liu S, Liu X, Li Z, Yang S, Wang J (2011) Fabrication of free-standing graphene/polyaniline nanofibers composite paper via electrostatic adsorption for electrochemical supercapacitors. New J Chem 35(2):369–374
Mao L, Zhang K, On Chan HS, Wu J (2011) Surfactant-stabilized graphene/polyaniline nanofiber composites for high performance supercapacitor electrode. J Mater Chem 22(1):80–85
Mishra AK, Ramaprabhu S (2011) Functionalized graphene-based nanocomposites for supercapacitor application. J Phys Chem C 115(29):14006–14013
Zhang J, Zhao XS (2012) Conducting polymers directly coated on reduced graphene oxide sheets as high-performance supercapacitor electrodes. J Phys Chem C 116(9):5420–5426
Zhong M, Song Y, Li Y, Ma C, Zhai X, Shi J (2012) Effect of reduced graphene oxide on the properties of an activated carbon cloth/polyaniline flexible electrode for supercapacitor application. J Power Sources 217:6–12
Zhang W, Mossad M, Zou L (2013) A study of the long-term operation of capacitive deionisation in inland brackish water desalination. Desalination 320:80–85
Mossad M, Zhang W, Zou L (2013) Using capacitive deionisation for inland brackish groundwater desalination in a remote location. Desalination 308:154–160
Zhang W, Mossad M, Yazdi J, Zou L (2016) A statistical experimental investigation on arsenic removal using a solar powered capacitive deionisation unit. Desalination Water Treat 57:3254-3260
Acknowledgements
Dr Wei Zhang would like to thank Japan Society for Promotion of Science (JSPS) for his tenured fellowship (P15712).
Author information
Authors and Affiliations
Corresponding author
Additional information
Competing Interests
The authors declare that they have no competing interests.
Authors’ Contributions
All authors contributed equally during the preparation of this manuscript. All authors read and approved the final manuscript.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Jia, B., Zhang, W. Preparation and Application of Electrodes in Capacitive Deionization (CDI): a State-of-Art Review. Nanoscale Res Lett 11, 64 (2016). https://doi.org/10.1186/s11671-016-1284-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-016-1284-1