Abstract
In the present study, the effect of Zn content on the microstructure and deformation behavior of the as-cast Mg–Zn–Y–Nd alloy has been investigated. The results showed that as Zn content increased, the volume fraction of secondary phases increased. Moreover, the phase transformation from W-phase to W-phase and I-phase occurred. In the as-cast state, W-phase exists as eutectic and large block form. When Zn content increases to 6 and 8% (wt%), small I-phase could precipitate around W-phase particles. Additionally, the effect of Zn content on the tensile properties and deformation behavior varies with the testing temperature. At room temperature, the tensile strength increases with Zn content, whereas the elongation increases initially and then decreases. At 250 °C, as Zn content increases, the tensile strength decreases initially and then increases slightly, whereas the elongation decreases. At 350 °C, the elongation increases with Zn content, whereas the tensile strength decreases initially and then increases slightly.
Similar content being viewed by others
References
P.F. Cheng, P. Han, C.L. Zhao, S.X. Zhang, H.L. Wu, J.H. Ni, P. Hou, Y.Z. Zhang, J.Y. Liu, H.D. Xu, S. Liu, X.N. Zhang, Biomaterials 81, 14 (2016)
C. Wang, H. Ding, B.S. Wang, K. Wang, J.J. Shi, J.F. Chen, Acta Metall. Sin. (Engl. Lett.) 30, 921 (2017)
Y.P. Wang, Y.H. He, Z.J. Zhu, Y. Jiang, J. Zhang, J.L. Niu, L. Mao, G.Y. Yuan, Bull. Sci. Technol. 32, 3111 (2012)
F. Witte, Acta Biomater. 6, 1680 (2010)
H. Hornberger, S. Virtanen, A.R. Boccaccini, Acta Biomater. 8, 2442 (2012)
S.X. Zhang, X.N. Zhang, C.L. Zhao, J.N. Li, Y. Song, C.Y. Xie, H.R. Tao, Y. Zhang, Y.H. He, Y. Jiang, Y.J. Bian, Acta Biomater. 6, 626 (2010)
H.X. Wang, S.K. Guan, X. Wang, C.X. Ren, L.G. Wang, Acta Biomater. 6, 1743 (2010)
Y. Zhang, X.F. Huang, Z.D. Ma, Y. Li, F. Guo, J.C. Yang, Y. Ma, Y. Hao, Mater. Sci. Eng. A 686, 93 (2017)
D.K. Xu, W.N. Tang, L. Liu, Y.B. Xu, E.H. Han, J. Alloys Compd. 432, 129 (2007)
F. Wang, J.B. Li, J. Liu, D. Lv, P.L. Mao, Z. Liu, Acta Metall. Sin. (Engl. Lett.) 27, 609 (2014)
J.Y. Lee, D.H. Kim, H.K. Lim, D.H. Kim, Mater. Lett. 59, 3801 (2005)
D.K. Xu, W.N. Tang, L. Liu, Y.B. Xu, E.H. Han, J. Alloys Compd. 432, 129 (2007)
J.M. Seitz, R. Eifler, C. Weber, T.H. Lenarz, H.J. Maier, M. Durisin, J. Biomed. Mater. Res. A 103, 2427 (2015)
J. Kubásek, D. Vojtěch, Trans. Nonferrous Met. Soc. China 23, 1215 (2013)
J. Liu, B. Zheng, P. Wang, X. Wang, B. Zhang, Q. Shi, T.F. Xi, M. Chen, S.K. Guan, A.C.S. Appl, Mater. Interfaces 8, 17842 (2016)
Z.Q. Zhang, X. Liu, W.Y. Hu, J.H. Li, Q.C. Le, L. Bao, Z.J. Zhu, J.Z. Cui, J. Alloys Compd. 624, 116 (2015)
D.K. Xu, E.H. Han, Y.B. Xu, Prog. Nat. Sci. Mater. Int. 26, 117 (2016)
J.B. Liu, K. Zhang, J.T. Han, X.G. Li, Y.J. Li, M.L. Ma, J.W. Yuan, G.L. Shi, M. Li, C.F. Lu, Mater. Sci. Eng. A 625, 107 (2015)
Z.P. Luo, S.Q. Zhang, Y.L. Tang, Chin. J Nonferrous Met. 3, 62 (1993)
J.W. Geng, X.Y. Teng, G.R. Zhou, J. Alloys Compd. 577, 498 (2013)
Q. Li, Q.D. Wang, Y.X. Wang, X.Q. Zeng, W.J. Ding, J. Alloys Compd. 427, 115 (2007)
D.K. Xu, E.H. Han, Prog. Nat. Sci. Mater. Int. 22, 364 (2012)
K. Yang, J.S. Zhang, X.M. Zong, W. Liu, C.X. Xu, Acta Metall. Sin. (Engl. Lett.) 30, 464 (2017)
E.L. Zhang, W.W. He, H. Du, K. Yang, Mater. Sci. Eng. A 488, 102 (2008)
Y.B. Zhang, S.R. Yu, X.Y. Zhu, Y.R. Luo, J. Non-Cryst. Solids 354, 1564 (2008)
H. Feng, H.P. Liu, H. Cao, Y. Yang, Y.C. Xu, J.Y. Guan, Mater. Sci. Eng. A 639, 1 (2015)
J. Luo, H. Yan, N. Zheng, R.S. Chen, Acta Metall. Sin. (Engl. Lett.) 29, 205 (2016)
Y.F. Zheng, X.N. Gu, F. Witte, Mater. Sci. Eng. R 77, 1 (2014)
Z.J. Li, X.N. Gu, S.Q. Lou, Y.F. Zheng, Biomaterials 29, 1329 (2007)
F. Peng, H. Li, D.H. Wang, P. Tian, Y.X. Tian, G.Y. Yuan, D.M. Xu, X.Y. Liu, A.C.S. Appl, Mater. Interf. 8, 35033 (2016)
H. Qin, Y.C. Zhao, Z.Q. An, M.Q. Cheng, Q. Wang, T. Cheng, Q.J. Wang, J.X. Wang, Y. Jiang, X.L. Zhang, G.Y. Yuan, Biomaterials 53, 211 (2015)
L.P. Xu, G.N. Yu, E.L. Zhang, F. Pan, K. Yang, J. Biomed. Mater. Res. A 83, 703 (2007)
A.F. Cipriano, A. Sallee, M. Tayoba, M.C.C. Alcaraz, A. Lin, R.G. Guan, Z.Y. Zhao, H.N. Liu, Acta Biomater. 48, 499 (2017)
X. Zhao, L.L. Shi, J. Xu, Mater. Sci. Eng. C 33, 3627 (2013)
X.Q. Zeng, Y. Zhang, C. Lu, W.J. Ding, Y.X. Wang, Y.P. Zhu, J. Alloys Compd. 395, 213 (2005)
T.J. Chen, W. Wang, D.H. Zhang, Y. Ma, Y. Hao, J. Alloys Compd. 546, 28 (2013)
B. Zberg, P.J. Uggowitzer, J.F. Löffler, Nat. Mater. 8, 887 (2009)
A. Drynda, N. Deinet, N. Braun, M. Peuster, J. Biomed. Mater. Res. A 91, 360 (2009)
Acknowledgements
This work was supported financially by the Shenzhen Technology Innovation Plan (Nos. CXZZ20140731091722497 and CXZZ20140419114548507), the Shenzhen Basic Research Project (Nos. JCYJ20150529162228734, JCYJ20160407090231002, JCYJ20150625155931806 and JCYJ20160427100211076) and The Thirteen Five National Key Research and Development Plan (No. 2016YFC1102601).
Author information
Authors and Affiliations
Corresponding author
Additional information
Available online at http://link.springer.com/journal/40195
Rights and permissions
About this article
Cite this article
Du, BN., Hu, ZY., Sheng, LY. et al. Influence of Zn Content on Microstructure and Tensile Properties of Mg–Zn–Y–Nd Alloy. Acta Metall. Sin. (Engl. Lett.) 31, 351–361 (2018). https://doi.org/10.1007/s40195-018-0713-9
Received:
Revised:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40195-018-0713-9