Abstract
Chromium slag usually contains various heavy metals, making its safe treatment difficult. Glass-ceramic sintering has been applied to resolve this issue and emerged as an effective method for metal immobilization by incorporating heavy metals into stable crystal structures. Currently, there is limited knowledge about the reaction pathways adopted by multiple heavy metals and the co-stabilization functions of the crystal structure. To study the Cu/Cr co-stabilization mechanisms during thermal treatment, a simulated system was prepared using a mixture with a molar ratio of Al2O3:Fe2O3:Cr2O3: CuO = 1:1:1:3. The samples were sintered at temperatures 600–1300°C followed by intensive analysis of phase constitutions and microstructure development. A spinel phase (CuFexAlyCr2−x−yO4) started to generate at 700°C and the incorporation of Cu/Cr into the spinel largely complete at 900°C, although the spinel peak intensity continued increasing slightly at temperatures above 900°C. Fe2O3/Cr2O3 was more easily incorporated into the spinel at lower temperatures, while more Al2O3 was gradually incorporated into the spinel at higher temperatures. Additionally, sintered sample microstructures became more condensed and smoother with increased sintering temperature. Cu / Cr leachability substantially decreased after Cu/Cr incorporation into the spinel phase at elevated temperatures. At 600°C, the leached ratios for Cu and Cr were 6.28% and 0.65%, respectively. When sintering temperature was increased to 1300°C, the leached ratios for all metal components in the system were below 0.2%. This study proposes a sustainable method for managing Cu/Cr co-exist slag at reasonable temperatures.
Similar content being viewed by others
References
Ballesteros S, Rincón J M, Rincón-Mora B, Jordán M M (2017). Vitrification of urban soil contamination by hexavalent chromium. Journal of Geochemical Exploration, 174: 132–139
Bragg W H, Bragg W L (1913). The reflection of X-rays by crystals. Proceedings of the Royal Society of London. Series A, Containing Papers of a Mathematical and Physical Character, 88(605): 428–438
Brown M E, Gallagher P K (2011). Handbook of Thermal Analysis and Calorimetry: Recent Advances, Techniques and Applications. Amsterdam: Elsevier Science
Cerbo A A V, Ballesteros F Jr, Chen T C, Lu M C (2017). Solidification/stabilization of fly ash from city refuse incinerator facility and heavy metal sludge with cement additives. Environmental Science and Pollution Research International, 24(2): 1748–1756
Chen Q, Zhang L, Ke Y, Hills C, Kang Y (2009). Influence of carbonation on the acid neutralization capacity of cements and cement-solidified/stabilized electroplating sludge. Chemosphere, 74(6): 758–764
El-Shobaky G A, Fagal G A, Amin N H (1989). Thermal solid-solid interaction between CuO and pure Al2O3 solids. Thermochimica Acta, 141: 205–216
Fu F, Xie L, Tang B, Wang Q, Jiang S (2012). Application of a novel strategy—Advanced fenton-chemical precipitation to the treatment of strong stability chelated heavy metal containing wastewater. Chemical Engineering Journal, 189–190: 283–287
Kim J H, Kim J S, Han S H, Kang H W, Lee H G, Cheon C I (2017). Low-temperature sintering and piezoelectric properties of CuO-doped (K,Na)NbO3 ceramics. Materials Research Bulletin, 96: 121–125
Liao C, Tang Y, Liu C, Shih K, Li F (2016). Double-Barrier mechanism for chromium immobilization: A quantitative study of crystallization and leachability. Journal of Hazardous Materials, 311: 246–253
Ma G, Garbers-Craig A (2006). A review on the characteristics, formation mechanisms and treatment processes of Cr (VI)-containing pyrometallurgical wastes. Journal of the Southern African Institute of Mining and Metallurgy, 106: 753–763
Ma W, Meng F, Qiu D, Tang Y (2020). Co-stabilization of Pb/Cu/Zn by beneficial utilization of sewage sludge incineration ash: Effects of heavy metal type and content. Resources, Conservation and Recycling, 156: 104671
Mao L, Tang R, Wang Y, Guo Y, Su P, Zhang W (2018). Stabilization of electroplating sludge with iron sludge by thermal treatment via incorporating heavy metals into spinel phase. Journal of Cleaner Production, 187: 616–624
Naja G M, Volesky B (2009). Treatment of metal-bearing effluents: Removal and recovery. Heavy Metals in the Environment, 247–292
Okuno N, Ishikawa Y, Shimizu A, Yoshida M (2004). Utilization of sludge in building material. Water science and technology: A journal of the International Association on Water Pollution Research, 49: 225–232
OuYang S, Zhang Y, Chen Y, Zhao Z, Wen M, Li B, Shi Y, Zhang M, Liu S (2019). Preparation of glass-ceramics using chromium-containing stainless steel slag: Crystal structure and solidification of heavy metal chromium. Scientific Reports, 9(1): 1964–1973
Qu Y, Yang Y, Zou Z, Zeilstra C, Meijer K, Boom R (2014). Thermal decomposition behaviour of fine iron ore particles. ISIJ International, 54(10): 2196–2205
Roessler J G, Oehmig W N, Blaisi N I, Townsend T G (2014). Chemical characterization of high-temperature arc gasification slag with a focus on element release in the environment. Environmental Science & Technology, 48(14): 7781–7788
Sarıkaya Y, Ada K, Önal M (2008). A model for initial-stage sintering thermodynamics of an alumina powder. Powder Technology, 188(1): 9–12
Shih K, Tang Y (2011). Prolonged toxicity characteristic leaching procedure for nickel and copper aluminates. Journal of Environmental Monitoring, 13(4): 829–835
Shih K, Tang Y (2012). Incorporating simulated zinc ash by kaolinite- and sludge-based ceramics: Phase transformation and product leachability. Chinese Journal of Chemical Engineering, 20(3): 411–416
Stumm W, Morgan J J (2013). Aquatic Chemistry: Chemical Equilibria and Rates in Natural Waters. London: Wiley Blackwell
Tang Y, Chan S W, Shih K (2014a). Copper stabilization in beneficial use of waterworks sludge and copper-laden electroplating sludge for ceramic materials. Waste Management (New York, N.Y.), 34(6): 1085–1091
Tang Y, Chui S S Y, Shih K, Zhang L (2011). Copper stabilization via spinel formation during the sintering of simulated copper-laden sludge with aluminum-rich ceramic precursors. Environmental Science & Technology, 45(8): 3598–3604
Tang Y, Lu X, Shih K (2014b). Alumina polymorphs affect the metal immobilization effect when beneficially using copper-bearing industrial sludge for ceramics. Chemosphere, 117: 575–581
Tang Y, Shih K, Chan K (2010). Copper aluminate spinel in the stabilization and detoxification of simulated copper-laden sludge. Chemosphere, 80(4): 375–380
Tang Y, Shih K, Liu C, Liao C (2016). Cubic and tetragonal ferrite crystal structures for copper ion immobilization in an iron-rich ceramic matrix. RSC Advances, 6(34): 28579–28585
Tsuchida T, Furuichi R, Sukegawa T, Furudate M, Ishii T (1984). Thermoanalytical study on the reaction of the CuO—Al2O3(η, γ AND α) systems. Thermochimica Acta, 78(1–3): 71–80
Wu F, Tang Y, Lu X, Liu C, Lv Y, Tong H, Ning Z, Liao C, Li F (2019). Simultaneous immobilization of Zn(II) and Cr(III) in spinel crystals from beneficial utilization of waste brownfield-site soils. Clays and Clay Minerals, 67(4): 315–324
Wu P, Tang Y, Cai Z (2018). Dual role of coal fly ash in copper ion adsorption followed by thermal stabilization in a spinel solid solution. RSC Advances, 8(16): 8805–8812
Acknowledgements
This work is supported financially by the National Natural Science Foundation of China (Grant No. 21707063), the National Key R&D Program of China (Grant No. 2018YFC1902904), and the Natural Science Foundation of Guangdong Province in China (No. 2019A15150-11836). This work is also sponsored by State Environmental Protection Key Laboratory of Integrated Surface Water-Groundwater Pollution Control. The authors are sincerely grateful for the help of SUSTech Core Research Facilities.
Author information
Authors and Affiliations
Corresponding author
Additional information
Highlights
• Cu and Cr can be mostly incorporated into CuFexAlyCr2−x−yO4 with a spinel structure.
• Spinel phase is the most crucial structure for Cu and Cr co-stabilization.
• Compared to Al, Fe and Cr are easier to be incorporated into the spinel structure.
• ‘Waste-to-resource’ by thermal process at attainable temperatures can be achieved.
Electronic supplementary material
Rights and permissions
About this article
Cite this article
Meng, F., Xia, Y., Zhang, J. et al. Cu/Cr co-stabilization mechanisms in a simulated Al2O3-Fe2O3-Cr2O3-CuO waste system. Front. Environ. Sci. Eng. 15, 116 (2021). https://doi.org/10.1007/s11783-021-1408-4
Received:
Revised:
Accepted:
Published:
DOI: https://doi.org/10.1007/s11783-021-1408-4