Abstract
The characteristics of interdiffusion between precipitation-hardened 17-4 PH grade stainless steel and nickel were studied in the temperature range of 900 °C to 1100 °C, using diffusion couples of these two materials. The diffusion coefficients of the major diffusing elements Fe, Ni, Cr, and Cu were evaluated for this multicomponent system. The diffusion paths plotted on the Fe-Ni-Cr isotherm showed a flat “S” shape, suggesting insignificant interaction among the diffusing species. The temperature dependence of the diffusion coefficients for each element was evaluated, and the activation energies for diffusion were determined. The asymmetric nature of concentration variation of the elements at the diffusion zone was observed and was explained by the difference in diffusivities of the diffusing species. The activation energy for diffusion of Ni was found to be lower than that of Fe and Cr.
Similar content being viewed by others
Notes
ARMCO grade 17-4 PH stainless steel is a trade mark of A K Steel Corporation, West Chester, OH.
INCONEL is a trademark of INCO Alloys International, Huntington, WV.
References
G.R. Kamat: Weld. J., 1988, vol. 3, pp. 44–46
G.B. Kale, A. Laik, P.S. Gawde, and K. Bhanumurthy: Proc. Int. Conf. on “Advanced Materials Proc. for Transport Sector,” Mumbai, India, 2004, ASM International, Materials Park, OH, 2004, pp. 1–22
K.C. Antony: J. Met., 1963, vol. 35, pp. 52–60
U.K. Vishwanathan, P.K.K. Nayar, R. Krishnan: Mater. Sci. Technol., 1989, vol. 5, pp. 346–49
J. Wang, H. Zou, C. Li, Y. Peng, S. Qiu, B. Shen: Nucl. Eng. Des., 2006, vol. 236, pp. 2531–36
Z. Guoge, R.S. Chandel, H.P. Seow, H.H. Hoon: J. Mater. Sci. Lett., 2001, vol. 20, pp. 1937–40
Z. Guoge, R.S. Chandel, H.P. Seow: Mater. Manuf. Processes, 2001, vol. 16, pp. 265–79
R.K. Shiue, S.K. Wu, C.H. Chan, C.S. Huang: Metall. Mater. Trans. A, 2006, vol. 37A, pp. 2207–17
M.A. Ashworth, M.H. Jacobs: Mater. Sci. Technol., 1999, vol. 15, pp. 951–56
J.L. Pouchou, F. Pichoir: Microbeam Analysis, San Francisco Press, San Francisco, CA, 1985
L. Onsager: Ann. N.Y. Acad. Sci., 1948, vol. 64, pp. 241–65
H. Fujita, L.J. Gosting: J. Am. Chem. Soc., 1956, vol. 78, pp. 1099–1106
M.A. Krishtal, P.N. Zakharov, A.P. Mokrov: Fiz. Tverd Tela, 1973, vol. 35, pp. 1332–36
M.A. Krishtal, A.P. Mokrov, V.K. Akimov, P.N. Zakharov: Fiz. Met. Metalloved., 1973, vol. 35, pp. 1234–40
F. Sauer, V. Freise: Z. Elektrochemie, 1962, vol. 66, pp. 353–63
G. Roper, D.P. Whittle: Met. Sci., 1980, vol. 14, pp. 541–49
M.A. Dayananda: Metall. Mater. Trans. A, 1996, vol. 27A, pp. 2504–09
M.A. Dayananda: Def. Diffus. Forum, 1993, vols. 95–97, pp. 521–36
M.A. Dayananda, Y.H. Sohn: Scripta Mater., 1996, vol. 35, pp. 683–88
C.N. Hsiao, C.S. Chiou, J.R. Yang: Mater. Chem. Phys., 2002, vol. 74, pp. 134–42
P. Villars, A. Prince, and H. Okamoto: Handbook of Ternary Alloy Phase Diagrams, ASM International, Materials Park, OH, 1995, vol. 7, p. 8868
G.B. Kale, K. Bhanumurthy, S.K. Khera, M.K. Asundi: Mater. Trans. JIM, 1991, vol. 11, pp. 1034–41
J.G. Duh, M.A. Dayananda: Diffus. Def. Data, 1985, vol. 39, pp. 1–50
G.B. Kale, K. Bhanumurthy, A. Laik, S.P. Garg: Trans. IIM, 2004, vol. 57, pp. 35–45
Acknowledgment
The authors thank Dr. G.K. Dey, Head, Materials Science Division, for his keen interest in this work.
Author information
Authors and Affiliations
Corresponding author
Additional information
Manuscript submitted July 13, 2007.
Rights and permissions
About this article
Cite this article
Laik, A., Gawde, P., Bhanumurthy, K. et al. Characteristics of Interdiffusion between 17-4 PH Steel and Nickel. Metall Mater Trans A 39, 733–741 (2008). https://doi.org/10.1007/s11661-007-9457-2
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11661-007-9457-2