Abstract
Manganese dioxide nanoparticles/activated carbon (MnO2/AC) composites and manganese dioxide nanoparticles (MnO2 NPs) are prepared through chemical reduction method. Morphological study shows that MnO2 NPs had cylindrical and spherical shape. The morphological study also revealed that MnO2 NPs were well dispersed on AC while neat Mn NPs present both in dispersed and in agglomerated form. The FT-IR study confirms the synthesis of MnO2 NPs. Zetasizer study presented that the Mn NPs had uniform size and below 100 nm in size and had zeta potential of − 20 mV, which represent its stability in the suspension form. The synthesized Mn/AC composite and Mn NPs were utilized as photocatalysts for the photodegradation of Congo red (CR) dye. The degradation study shows that MnO2/AC composite degraded CR dye more efficiently than MnO2 NPs under UV and normal light irradiation. The efficient degradation of dye by Mn/AC composite is due to the synergistic effect between dye adsorption on AC and rapid photodegradation by supported MnO2 NPs. The results revealed that Mn/AC composite degraded about 98.53% of CR dye within 5 min while MnO2 NPs degraded 66.57% of dye within the same irradiation time. The recycled catalyst also significantly degraded dye which verifies its sustainability. The effect of catalyst dosage and initial dye concentration was conducted. The degradation rate of dye was found drastically faster in tap water (in presence of catalyst), which might be due to the presence of various mineral ions in the tap water.
Similar content being viewed by others
References
Akpan UG, Hameed BH (2009) Parameters affecting the photocatalytic degradation of dyes using TiO2-based photocatalysts: a review. J Hazard Mater 170:520–529
Dang TD, Le TTH, Hoang TBT, Mai TT (2015) Synthesis of nanostructured manganese oxides based materials and application for supercapacitor. Adv Nat Sci Nanosci Nanotechnol 6:025011
Erdemoglu S, Aksu SK, Sayılkan F, Izgi B, Asilturk M, Sayilkan H, Frimmel F, Gucer S (2008) Photocatalytic degradation of Congo red by hydrothermally synthesized nanocrystalline TiO2 and identification of degradation products by LC–MS. J Hazard Mater 155:469–476
Feng L, Xuan Z, Zhao H, Bai Y, Guo J, Su C, Chen X (2014) MnO2 prepared by hydrothermal method and electrochemical performance as anode for lithium-ion battery. Nanoscale Res Lett 9:290–297
Ganeshan S, Ramasundari P, Elangovan A, Arivazhagan G, Vijayalakshmi R (2017) Synthesis and characterization of MnO2 nanoparticles: study of structural and optical properties. Int J Sci Res Phys Appl Sci 5:5–8
Gong K, Hu Q, Yao L, Li M, Sun D, Shao Q, Qiu B, Guo Z (2018) Ultrasonic pretreated sludge derived stable magnetic active carbon for Cr(VI) removal from wastewater. ACS Sustain Chem Eng 6:7283–7291
Hamukwaya SL, Zengying Z, Ning W, Hu L, Ahmad U, Jiaoxia Z, Tingting W, Zhanhu G (2019) Enhanced photocatalytic activity of B, N-Codoped TiO2 by a new molten nitrate process. J Nanosci Nanotechnol 19:839–949
Huang J, Cao Y, Shao Q, Peng X, Guo Z (2017) Magnetic Nanocarbon adsorbents with enhanced hexavalent chromium removal: morphology dependence of Fibrillar vs particulate structures. Ind Eng Chem Res 56:10689–10701
Huang J, Li Y, Cao Y, Peng F, Cao Y, Shao Q, Liu H, Guo Z (2018) Hexavalent chromium removal over magnetic carbon nanoadsorbents: synergistic effect of fluorine and nitrogen co-doping. J Mater Chem A 6:13062–13074
Ioannidou O, Zabaniotou A (2007) Agricultural residues as precursors for activated carbon production-a review. Renew Sust Energ Rev 11:1966–2005
Jaganyi D, Altaf M, Wekesa I (2013) Synthesis and characterization of whisker-shaped MnO2 nanostructure at room temperature. Appl Nanosci 3:329–333
Koo Y, Littlejohn G, Collins B, Shanov YYVN, Schulz M, Pai D, Sankar J (2014) Synthesis and characterization of ag-TiO2-CNT nanoparticle composites with high photocatalytic activity under artificial light. Composites Part B 57:105–111
Li Z, Wang B, Qin X, Wang Y, Liu C, Shao Q, Wang N, Zhang J, Shen C, Guo Z (2018) Superhydrophobic/Superoleophilic polycarbonate/carbon nanotubes porous monolith for selective oil adsorption from water. ACS Sustain Chem Eng 6:13747–13755. https://doi.org/10.1021/acssuschemeng.8b01637
Lin C, Hu L, Cheng C, Sun K, Guo X, Shao Q, Li J, Wang N, Guo Z (2018) Nano-TiNb2O7/carbon nanotubes composite anode for enhanced lithium-ion storage. Electrochim Acta 260:65–72
Liu S, Cai Y, Cai X, Li H, Zhang F, Mu Q, Liu Y, Wang Y (2013) Catalytic photodegradation of Congo red in aqueous solution by ln(OH)3 (ln = Nd, Sm, Eu, Gd, Tb, and Dy) nanorods. Appl Catal A Gen 453:45–53
Mamba G, Mbianda XY, Mishra AK (2015) Photocatalytic degradation of the diazo dye naphthol blue black in water using MWCNT/Gd,N,S-TiO2 nanocomposites under simulated solar light. J Environ Sci 33:219–228
Melghit K, Al-Rabaniah SS (2006) Photodegradation of Congo red under sunlight catalysed by nanorod rutile TiO2. J Photochem Photobiol A Chem 184:331–334
Mohamed A, El-Sayed R, Osman TA, Toprak MS, Muhammed M, Uheida A (2016) Composite nanofibers for highly efficient photocatalytic degradation of organic dyes from contaminated water. Environ Res 145:18–25
Padikkaparambil S, Narayanan B, Yaakob Z, Viswanathan S, Tasirin S (2013) Au/TiO2 reusable Photocatalysts for dye degradation. Int J Photoenergy 752605(2013):1–10
Pan D, Ge S, Zhang X, Mai X, Li S, Guo Z (2018a) Synthesis and photoelectrocatalytic activity of In2O3 hollow microspheres via a bio-template route using yeast templates. Dalton Trans 47:708–715
Pan D, Ge S, Zhao J, Shao Q, Guo L, Zhang X, Lin J, Xu G, Guo Z (2018b) Synthesis, characterization and photocatalytic activity of mixed-metal oxides derived from NiCoFe ternary layered double hydroxides. Dalton Trans 47:9765–9778
Pouretedal HR, Kiyani M (2014) Photodegradation of 2-nitrophenol catalyzed by CoO, CoS and CoO/CoS nanoparticles. J Iran Chem Soc 11:271–277
Reza KM, Kurny ASW, Gulshan F (2017) Parameters affecting the photocatalytic degradation of dyes using TiO2: a review. Appl Water Sci 7:1569–1578
Rout L, Rengasamy P, Ekka B, Kumar A, Dash P (2015) Supported bimetallic AgSn nanoparticle as an efficient Photocatalyst for degradation of methylene blue dye. NANO 10:1550059
Sadiq M, Khan M, Numan M, Aman R, Hussain S, Ahmad MS, Sadiq S, Zia MA, Rashid HU, Ali R (2017) Tuning of activated carbon for solvent-free oxidation of cyclohexane. J Chem 2017:1–8. https://doi.org/10.1155/2017/5732761
Saeed K, Khan I, Park SY (2015) TiO2/amidoxime-modified polyacrylonitrile nanofibers and its application for the photodegradation of methyl blue in aqueous medium. Desalin Water Treat 54:3146–3151
Saeed K, Khan I, Ahmad Z, Khan B (2018) Preparation, analyses and application of cobalt–manganese oxides/nylon 6,6 nanocomposites. Polym Bull 75:4657–4669. https://doi.org/10.1007/s00289-018-2292-3
Sangami G, Dharmaraj N (2012) UV–visible spectroscopic estimation of photodegradation of rhodamine-B dye using tin(IV) oxide nanoparticles. Spectrochim Acta A Mol Biomol Spectrosc 97:847–852
Shivaraju HP, Midhun G, Kumar KMA, Pallavi S, Pallavi N, Behzad S (2017) Degradation of selected industrial dyes using mg-doped TiO2 polyscales under natural sun light as an alternative driving energy. Appl Water Sci 7:3937–3948
Soltani RDC, Haghighat Z (2016) Visible light photocatalysis of a textile dye over ZnO nanostructures covered on natural diatomite. Turk J Chem 40:454–466
Song B, Wang T, Sun H, Shao Q, Zhao J, Song K, Hao L, Wang L, Guo Z (2017) Two-step hydrothermally synthesized carbon nanodots/WO3 photocatalysts with enhanced photocatalytic performance. Dalton Trans 46:15769–15777
Su T, Shao Q, Qin Z, Guo Z, Wu Z (2018) Role of interfaces in two-dimensional Photocatalyst for water splitting. ACS Catal 8:2253–2276
Velusamy P, Lakshmi G (2017) Enhanced photocatalytic performance of (ZnO/CeO2)-b-CD system for the effective decolorization of rhodamine B under UV light irradiation. Appl Water Sci 7:4025–4036
Wang H, Xie C, Zhang W, Cai S, Yang Z, Gui Y (2007) Comparison of dye degradation efficiency using ZnO powders with various size scales. J Hazard Mater 141:645–652
Wang C, Murugadoss V, Kong J, He Z, Mai X, Shao Q, Chen Y, Guo L, Liu C, Angaiah S, Guo Z (2018) Overview of carbon nanostructures and nanocomposites for electromagnetic wave shielding. Carbon 140:696–733
Wu ZC, Zhang Y, Tao TX, Zhang L, Fong H (2010) Silver nanoparticles on amidoxime fibers for photo-catalytic degradation of organic dyes in waste water. Appl Surf Sci 257:1092–1097
Wu T, Shao Q, Ge S, Bao L, Liu Q (2016) The facile preparation of novel magnetic zirconia composites with the aid of carboxymethyl chitosan and their efficient removal of dye. RSC Adv 6:58020–58027
Yang Z, Hao X, Chen S, Ma Z, Wang W, Wang C, Yue L, Sun H, Shao Q, Murugadoss V, Guo Z (2019) Long-term antibacterial stable reduced graphene oxide nanocomposites loaded with cuprous oxide nanoparticles. J Colloid Interface Sci 533:13–23
Zada N, Khan I, Saeed K (2017) Synthesis of multiwalled carbon nanotubes supported manganese and cobalt zinc oxides nanoparticles for the photodegradation of malachite green. Sep Sci Technol 52:1477–1485
Zhang D, Zeng F (2010) Structural, photochemical and photocatalytic properties of zirconium oxide doped TiO2 nanocrystallites. Appl Surf Sci 257:867–871
Zhang L, Qin M, Yu W, Zhang Q, Xie H, Sun Z, Shao Q, Guo X, Hao L, Zheng Y, Guo Z (2017a) Heterostructured TiO2/WO3 nanocomposites for photocatalytic degradation of toluene under visible light. J Electrochem Soc 164:H1086–H1090
Zhang L, Yu W, Han C, Guo J, Zhang Q, Xie H, Shao Q, Sun Z, Guo Z (2017b) Large scaled synthesis of Heterostructured electrospun TiO2/SnO2 nanofibers with an enhanced photocatalytic activity. J Electrochem Soc 164:H651–H656
Zhang Y, Qian L, Zhao W, Li X, Huang X, Mai X, Wang Z, Shao Q, Yan X, Guo Z (2018) Highly efficient Fe-N-C nanoparticles modified porous graphene composites for oxygen reduction reaction. J Electrochem Soc 165:H510–H516
Zhao J, Ge S, Liu L, Shao Q, Mai X, Zhao CX, Hao L, Wu T, Yu Z, Guo Z (2018a) Microwave Solvothermal fabrication of zirconia hollow microspheres with different morphologies using pollen templates and their dye adsorption removal. Ind Eng Chem Res 57:231–241
Zhao J, Ge S, Pan D, Shao Q, Lin J, Wang Z, Hu Z, Wu T, Guo Z (2018b) Solvothermal synthesis, characterization and photocatalytic property of zirconium dioxide doped titanium dioxide spinous hollow microspheres with sunflower pollen as bio-templates. J Colloid Interface Sci 529:111–121
Zhao B, Shao Q, Hao L, Zhang L, Liu Z, Zhang B, Ge S, Guo Z (2018c) Yeast-template synthesized Fe-doped cerium oxide hollow microspheres for visible photodegradation of acid orange 7. J Colloid Interface Sci 511:39–47
Zhua H, Jiang R, Xiao L, Chang Y, Guan Y, Li X, Zeng G (2009) Photocatalytic decolorization and degradation of Congo red on innovative crosslinked chitosan/nano-CdS composite catalyst under visible light irradiation. J Hazard Mater 169:933–940
Author information
Authors and Affiliations
Corresponding author
Additional information
Responsible editor: Suresh Pillai
Rights and permissions
About this article
Cite this article
Khan, I., Sadiq, M., Khan, I. et al. Manganese dioxide nanoparticles/activated carbon composite as efficient UV and visible-light photocatalyst. Environ Sci Pollut Res 26, 5140–5154 (2019). https://doi.org/10.1007/s11356-018-4055-y
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s11356-018-4055-y