Abstract
The effects of Li substitution on the properties of high temperature superconductor Bi17Pb0.3Sr2C2Cu3−x Li x O y were investigated. The samples were prepared by substituting Li (x=0.00–0.20) with changing ratios by a solid state reaction method. The samples were characterized by X-ray diffraction, DC electrical resistivity, AC magnetic susceptibility, and scanning electronic microscopy (SEM). The X-ray diffraction studies were done at room temperature and the lattice constants of the material were determined by indexing all the peaks observed.
This study shows that there are two coexisting phases; high-T c (2223) phase and low-T c (2212) phase. The lattice structure of the material belongs to the orthorhombic unit cell. The volume fraction was estimated from the intensities of Bi-(2223) and Bi-(2212) phases. The sample with 20 wt% of added Li showed the higher volume fraction of Bi-(2223) phase formed (81%) compared to the other samples. The DC electrical resistivity of all the samples decreased as the wt% of Li increased. Both the onset critical temperatures T c (onset) and zero electrical resistivity critical temperatures T c (R=0) of the samples were determined from the DC electrical resistivity measurements. The observed value of the onset critical T c (onset) temperature was 110 K agreeing well with the magnetic susceptibility measurements. We obtained T c onset at 112 K from AC magnetic susceptibility measurements.
Similar content being viewed by others
References
Ozturk, O., Yegen, D., Yilmazlar, M., Varilci, A., Terzioglu, C.: Physica C 451, 113–117 (2007)
Gul, I.H., Amin, F., Abbasi, A.Z., Anis-ur-Rehman, M., Maqsood, A.: Physica C 449, 139–147 (2006)
Gul, I.H., Rehman, M.A., Ali, M., Maqsood, A.: Physica C 432, 71–80 (2005)
Zhigadlo, N.D., Petrashko, V.V., Semenenko, Yu.A., Panagopoulos, C., Cooper, J.R., Salje, E.K.H.: Physica C 299, 327–337 (1998)
Gul, I.H., Anis-ur-Rehman, M., Maqsood, A.: Physica C 450, 83–87 (2006)
Salamati, H., Kameli, P.: Physica C 403, 60–66 (2004)
Sykorova, L.D., Smrckova, O., Jakes, V.: Phys. Stat. Sol. (C) 1(7), 1952–1956 (2004)
Kawai, T., Horiuchi, T., Mitsui, K., Ogura, K., Takagi, S., Kawai, S.: Physica C 161, 561 (1989)
Youssif, M.I., Bahgat, A.A., Ali, I.A.: Egypt. J. Sol. 23, 231–250 (2000)
Mihalache, V., Aldica, G., Giusca, C., Miu, L.: J. Supercond. Incorp. Nov. Magn. 14(5), 575–579 (2001)
Mihalache, V., Aldica, G., Badica, P.: Physica C 392–396, 185–188 (2003)
Mihalache, V., Aldica, G., Popa, S., Lifei, F., Miu, D.: Mater. Lett. 58, 3040–3044 (2004)
Saleh, S.A.: Physica C 444, 40–44 (2006)
Kamali, P., Salamati, H.: Physica C 403, 60–66 (2004)
Terzioglu, C., Yilmazlar, M., Ozturk, O., Yanmaz, E.: Physica C 423, 119–126 (2005)
Kamali, P., Salamati, H., Abdolhosseini, I.: Alloys Comp. J. (2007)
Kocabaş, K., Ciftcioğlu, M.: Phys. Stat. Sol. (a) 177, 539 (2000)
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Bilgili, O., Selamet, Y. & Kocabaş, K. Effects of Li Substitution in Bi-2223 Superconductors. J Supercond Nov Magn 21, 439–449 (2008). https://doi.org/10.1007/s10948-008-0374-4
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10948-008-0374-4
Keywords
- Bi-based superconductors
- Li substitution
- AC susceptibility
- Scanning electronic microscopy
- X-ray diffraction