Abstract
Aspen was heat-treated at high temperature in a laboratory thermogravimetric analyzer. The high temperature wood treatment technology is new in North America and needs to be adapted to the North American species. The objective of this study is to understand how the treatment affects the mechanical properties of aspen such as hardness, modulus of elasticity and modulus of rupture, and, consequently, the quality of the product. The wood samples were heated in an inert gas environment under different operating conditions. The parameters studied are the final treatment temperature, heating rate, holding time, and the gas humidity. The weight loss and the temperature history of wood were monitored during the treatment. After the experiments, the properties of the samples were measured, and the effects of the above parameters on the properties were analyzed. The weight loss increased with increasing temperature, heating rate, holding time, and gas humidity. Increasing temperature caused an increase in MOE and a decrease in MOR. Overall hardness decreased with increasing temperature above 160 °C and it increased with increasing holding time and heating rate whereas it decreased with increasing gas humidity. Holding time and heating rate did not seem to affect MOE. Gas humidity increased MOE. MOR increased with holding time and decreased with heating rate and gas humidity.
Similar content being viewed by others
References
Militz H (2002) In: Proceedings of conference on enhancing the durability of lumber and engineered wood products, 2002, Kissimmee, Orlando, February 11–13, 2002. Forest Product Society, Madison, US
Koch P (1985) In: Mithchel PH (ed) Proceedings of North American symposium, Mississipi, November 27–28, 1985. State College, Mississipi, pp 1–38
Rietz RC, Page RH (2003) In: Air drying lumber: a guide to industry practice, agric. handb. 402. Madison, WI, US Department of Agriculture, Forest Services, Forest Product Laboratory, Books for Business
Simpson WT (1991) In: Dry kiln operator’s manual, agric. handb. 188. Madison, WI, US Department of Agriculture, Forest Services, Forest Product Laboratory
Gerhard CC (1982) Wood Fiber Sci 14:1
Wolcottm MP, Kamke FA, Dillard DA (1990) Wood Fiber Sci 22:345
Weiland JJ, Guyonnet R (2001) Récents Progrès en Génie des Procédés 15:195
Wikberg H, Maunu SL (2004) Carbohydrate Polym 58:461
Rowell R, Lange S, Davis M (2000) In: Evans PD (ed) Proceedings of 5th Pacific Rim bio-based composites symposium, Canberra, Australia, December 10–13, 2000. ACIAR Proceedings, pp 425–438
Stamm AJ, Burr HK, Kline AA (1946) Indust Eng Chem 38:630
Kelley SS, Rials TG, Glasser WG (1987) J Mater Sci 22:617
Salmen L (1984) J Mater Sci 19:3090
Stamm AJ (1964) Wood and cellulose science. The Ronald press company, New York
Stamm AJ (1956) Indust Eng Chem 48:413
Kininmonth JA (1976) New Zealand J Forest Sci 6:101
Rusche H (1973) Holz als Roh- und Werkstoff 31:273
Yildiz S, Çolakoğlu G, Yildiz ÜC, Gezer ED, Temiz A (2002) In: Proceedings of international research group on wood protection IRG/WP 02-40222, Cardiff, Wales, UK, May 2002
Viitaniemi P (2005) Fast-drying of wood. http://www.vtt.fi/rte/bss/coste15/cost%20e15%20esitelmat/viitaniemi.pdf, as on 17 October 2005
Robbins C, MORREL J (2006) Mold, housing and wood. Western Wood Product Publications, http://www.wwpa.org/pdf/TG2.pdf, as 13 March 2006
Duchez L, Herri JM, Guyonnet R (2001) In: Proceedings of 8ième Congrès francophone en Génie des Procédés, Nancy, 17 au 19 October 2001. Groupe ENSIC, pp 61–68
Weiland JJ, Guyonnet R (2003) Holz als Roh- und Werkstoff 61:216
Homan W, Tjeerdsma B, Beckers E, Joressen A (2000) In: Proceedings of congress WCTE, Whistler, Canada, 2000. CD-ROM, pp 3.5.1-1–3.5.1-8
Chaudhry B (2004) Traitement thermique sur le bois et termogravimetrie. Internal report, Department of Applied Sciences, University of Quebec at Chicoutimi, Chicoutimi, Canada, 2004
Mccabe WL, Smith JC, Harriot P (1985) In: Unit operations of chemical engineering, 4th edn. McGraw Hill Chemical Engineering Series, p 707
Acknowledgements
The authors would like to thank the administration of the University of Quebec at Chicoutimi (UQAC), especially Mr. Sylvain Tremblay, the Foundation of the University (FUQAC), the PCI Industries, especially Mr. Adam Lapointe and Mr. Denis Lapointe, and our technicians Mr. Patrice Paquette and Mr. Jacques Allaire for their support and contributions.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Kocaefe, D., Chaudhry, B., Poncsak, S. et al. Thermogravimetric study of high temperature treatment of aspen: effect of treatment parameters on weight loss and mechanical properties. J Mater Sci 42, 854–866 (2007). https://doi.org/10.1007/s10853-006-0054-3
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s10853-006-0054-3