Effect of heat treatment intensity on some conferred properties of different European softwood and hardwood species

  • Original
  • Published:
Wood Science and Technology Aims and scope Submit manuscript

Abstract

Effect of heat treatment intensity on some conferred properties like elemental composition, durability, anti-swelling efficiency (ASE) and equilibrium moisture content (EMC) of different European softwood and hardwood species subjected to mild pyrolysis at 230 °C under nitrogen for different durations has been investigated. Independently of the wood species studied, elemental composition is strongly correlated with the mass losses due to thermal degradations which are directly connected to treatment intensity (duration). In all cases, an important increase in the carbon content associated with a decrease in the oxygen content was observed. Heat-treated specimens were exposed to several brown rot fungi, and the weight losses due to fungal degradation were determined after 16 weeks, while effect of wood extractives before and after thermal treatment was investigated on mycelium growth. ASE and EMC were also evaluated. Results indicated important correlations between treatment intensity and all of the wood conferred properties like its elemental composition, durability, ASE or EMC. These results clearly indicated that chemical modifications of wood cell wall polymers are directly responsible for wood decay durability improvement, but also for its improved dimensional stability as well as its reduced capability for water adsorption. All these modifications of wood properties appeared simultaneously and progressively with the increase in treatment intensity depending on treatment duration. At the same time, effect of extractives generated during thermal treatment on Poria placenta growth indicated that these latter ones have no beneficial effect on wood durability.

This is a preview of subscription content, log in via an institution to check access.

Access this article

Log in via an institution

Price excludes VAT (USA)
Tax calculation will be finalised during checkout.

Instant access to the full article PDF.

Institutional subscriptions

Fig. 1
Fig. 2

Similar content being viewed by others

References

  • Brosse N, El Hage R, Chaouch M, Pétrissans M, Dumarçay S, Gérardin P (2010) Investigations of chemical modifications of Beech Wood Lignin during heat treatment. Polym Degrad Stab 95(9):1721–1726

    Article  CAS  Google Scholar 

  • Candelier K, Chaouch M, Dumarçay S, Pétrissans A, Pétrissans M, Gérardin P (2011) Utilization of thermodesorption coupled to GC–MS to study stability of different wood species to thermodegradation. J Anal Appl Pyrolysis 92(2):376–383

    Article  CAS  Google Scholar 

  • Chaouch M, Pétrissans M, Pétrissans A, Gérardin P (2010) Use of wood elemental composition to predict heat treatment intensity and decay resistance of different softwood and hardwood species. Polym Degrad Stab 95:2255–2259

    Article  CAS  Google Scholar 

  • Esteves BM, Pereira HM (2009) Wood modification by heat treatment: a review. Bioresources 4(1):370–404

    CAS  Google Scholar 

  • Hakkou M, Pétrissans M, Zoulalian A, Gérardin P (2005) Investigation of wood wettability changes during heat treatment on the basis of chemical analysis. Polym Degrad Stab 89(1):1–5

    Article  CAS  Google Scholar 

  • Hakkou M, Pétrissans M, Gérardin P, Zoulalian A (2006) Investigation of the reasons for fungal durability of heat-treated beech wood. Polym Degrad Stab 91:393–397

    Article  CAS  Google Scholar 

  • Kamdem D, Pizzi A, Triboulot M (2000) Heat-treated timber: potentially toxic byproducts presence and extent of wood cell wall degradation. Holz Roh Werkst 58:253–257

    Article  CAS  Google Scholar 

  • Kamdem DP, Pizzi A, Jermannaud A (2002) Durability of heat-treated wood. Holz Roh Werkst 60:1–6

    Article  CAS  Google Scholar 

  • Lekounougou S, Pétrissans M, Jacquot JP, Gelhaye E, Gérardin P (2009) Effect of heat treatment on extracellular enzymatic activities involved in beech wood degradation by Trametes versicolor. Wood Sci Technol 43:331–341

    Article  CAS  Google Scholar 

  • Mburu F, Dumarçay S, Bocquet JF, Pétrissans M, Gérardin P (2008) Effect of chemical modifications caused by heat treatment on mechanical properties of Grevillea robusta wood. Polym Degrad Stab 93(2):401–405

    Article  CAS  Google Scholar 

  • Militz H (2002) Thermal treatment of wood: European processes and their background. The International Research Group on Wood Preservation. IRG/WP 02-40241

  • Nguila Inari G, Mounguengui S, Dumarçay P, Pétrissans M, Gérardin P (2007) Evidence of char formation during heat treatment by pyrolysis. Polym Degrad Stab 92:997–1002

    Article  Google Scholar 

  • Nguila Inari G, Pétrissans M, Pétrissans A, Gérardin P (2009) Elemental composition of wood as a potential marker to evaluate heat treatment intensity. Polym Degrad Stab 94:365–368

    Article  Google Scholar 

  • Nuopponen M, Vuorinen T, Jamsa S, Viitaniemi P (2004) Thermal modifications in softwood studied by FTIR and UV resonance Raman spectroscopy. J Wood Chem Technol 24(1):13–26

    Article  CAS  Google Scholar 

  • Patzelt M, Stingl R, Teischinger A (2002) Termische Modifikation von Holz und deren Einfluß auf ausgewählte Holzeigenschaften. In: Modifiziertes Holz Eigenschaften und Märkte. Lignovisionen Band 3, pp 101–149. ISSN: 1681-2808

  • Peters J, Pfriem A, Horbens M, Fischer S, Wagenführ A (2009) Emissions from thermally modified beech wood, their reduction by solvent extraction and fungicidal effect of the organic solvent extracts. Wood Mat Sci Eng 1(2):61–66

    Article  Google Scholar 

  • Prins MJ, Ptasinski KJ, Janssen FJJG (2006) Torrefaction of wood. Part 2. Analysis of products. J Anal Appl Pyrolysis 77:35–40

    Article  CAS  Google Scholar 

  • Reppelin V, Govin A, Rolland M, Guyonnet R (2010) Modelling anhydrous weight loss of wood chips during torrefaction in a pilot kiln. Biomass Energy 34:602–609

    Article  Google Scholar 

  • Sivonen H, Maunu SL, Sundholm F, Jämsä S, Viitaniemi P (2002) Magnetic resonance studies of thermally modified wood. Holzforschung 56:648–654

    Article  CAS  Google Scholar 

  • Sjöström E (ed) (1981) Wood polysaccharides, Chap. 3. In: Wood chemistry. Fundamentals and applications. Academic Press, Inc. (Harcourt Brace Jovanovitch Publishers), Orlando, Florida, pp 49–67

  • Šušteršic Ž, Mohareb A, Chaouch M, Pétrissans M, Petrič M, Gérardin P (2010) Prediction of the decay resistance of heat treated wood on the basis of its elemental composition. Polym Degrad Stab 95:94–97

    Article  Google Scholar 

  • Tjeerdsma B, Militz H (2005) Chemical changes in hydrothermal treated wood: FTIR analysis of combined hydrothermal and dry heat treated wood. Holz Roh Werkst 63:102–111

    Article  CAS  Google Scholar 

  • Tjeerdsma B, Boonstra M, Pizzi A, Tekely P, Militz H (1998) Characterization of thermally modified wood: molecular reasons for wood performance improvement. Holz Roh Werkst 56(3):149–153

    Article  CAS  Google Scholar 

  • Weiland JJ, Guyonnet R (2003) Study of chemical modifications and fungi degradation of thermally modified wood using DRIFT spectroscopy. Holz Roh Werkst 61:216–220

    CAS  Google Scholar 

  • Welzbacher C, Brischke C, Rapp A (2007) Influence of treatment temperature and duration on selected biological, mechanical, physical and optical properties of thermally modified timber. Wood Mat Sci Eng 2(2):66–76

    Article  Google Scholar 

  • Zaman A, Alen R, Kotilainen R (1984) Heat behavior of Pinus sylvestris and Betula pendula at 200–230°C. Wood Fiber Sci 32(2):138–143

    Google Scholar 

Download references

Acknowledgments

The authors gratefully acknowledge the financial support of the CPER 2007-2013 “Structuration du Pôle de Compétitivité Fibres Grand’Est” (Competitiveness Fibre Cluster).

Author information

Authors and Affiliations

  1. Laboratoire d’Etudes et de Recherches sur le Matériau Bois, EA 4370, Faculté des Sciences et Technologies, Université de Lorraine, BP 70239, 54506, Vandoeuvre-lès-Nancy, France

    Mounir Chaouch, Stéphane Dumarçay, Anélie Pétrissans, Mathieu Pétrissans & Philippe Gérardin

Authors
  1. Mounir Chaouch
    View author publications

    You can also search for this author in PubMed Google Scholar

  2. Stéphane Dumarçay
    View author publications

    You can also search for this author in PubMed Google Scholar

  3. Anélie Pétrissans
    View author publications

    You can also search for this author in PubMed Google Scholar

  4. Mathieu Pétrissans
    View author publications

    You can also search for this author in PubMed Google Scholar

  5. Philippe Gérardin
    View author publications

    You can also search for this author in PubMed Google Scholar

Corresponding author

Correspondence to Philippe Gérardin.

Rights and permissions

Reprints and permissions

About this article

Cite this article

Chaouch, M., Dumarçay, S., Pétrissans, A. et al. Effect of heat treatment intensity on some conferred properties of different European softwood and hardwood species. Wood Sci Technol 47, 663–673 (2013). https://doi.org/10.1007/s00226-013-0533-z

Download citation

  • Received:

  • Published:

  • Issue Date:

  • DOI: https://doi.org/10.1007/s00226-013-0533-z

Keywords

Search

Navigation