Durability of heat-treated wood

G. trabeum

and 46% for P. placenta. About 56% and 54% weight loss were obtained for southern pine control exposed to G. trabeum and P. placenta, respectively. The weight loss of the water and acetone extracted heat-treated sample exposed to P. placenta was 49.7% and 53.9%, respectively. Only about 11% and 14.8% weight loss was obtained for water and acetone extracted samples exposed to G. trabeum. The moisture content of the tested samples was about 70 ± 10% for the un-heated controls and 50 ± 10% for heat-treated samples. This treatment may modify the durability from non-resistant to moderate/resistant species depending on the fungus species as defined in the ASTM 2017 standard. The data from the bending test indicate that such treatment may create a 10 to 50% reduction in MOR and deflection, which will limit the use of such wood for structural purposes.

G. trabeum

11%, durch P. placenta 46%. Bei Kiefernproben waren es sogar 56% bzw. 54%. Die Gewichtsverluste von mit Wasser bzw. Aceton extrahierten und dann hitzebehandelten Proben betrugen gegenüber P. placenta 49,7 bzw. 53,9%. Die Werte gegenüber G. trabeum lagen dagegen nur bei 11% und 14,8%. Die Feuchte der geprüften hitzebehandelten Proben betrug 70 ± 10%, die der nicht erhitzten Proben 50 ± 10%. Die Hitzebehandlung könnte also die Dauerhaftigkeit von Holzproben von einer nicht widerstandfähigen zu einer mäßig widerstandsfähigen modifizieren, abhängig von der Pilzart gemäß ASTM 2017. Die Prüfung der Biegefestigkeiten ergab, daß die Hitzebehandlung einen Rückgang des MOR und der Durchbiegung um 10–50% verursachen kann, wodurch die Verwendung solcher Proben als Bauholz eingeschränkt ist.