Abstract
Thin tensile specimens of 316L-type austenitic stainless steel were tested either at room temperature after cathodic charging or whilst undergoing cathodic charging. Throughout this study we have compared solution-annealed samples with samples given the additional sensitization treatment. The results of the tensile tests show that the room temperature yield and ultimate strengths were not much affected by sensitization, whilst significant reduction in the ductility was observed depending on the heat treatment and the method of charging. The specimens tested while undergoing cathodic charging showed 21% reduction of elongation at-fracture for the annealed specimens and 49% reduction of elongation for the sensitized specimens. The fracture surfaces of the specimens tested while cathodically charged show considerable differences between the annealed and the sensitized specimens. The sensitized specimens were predominantly intergranular, while the fracture of annealed specimens showed massive regions of microvoid coalescence producing ductile rupture. The results were correlated with the presence or absence of the martensite phases determined by means of a ferrite detector and transmission electron microscopy studies.
Similar content being viewed by others
References
M. L. Holzworth andM. R. Louthan, Jr,Corrosion 24 (1968) 110.
M. B. Whiteman andA. R. Troiano,ibid. 21 (1965) 53.
M. L. Holzworth,ibid. 25 (1969) 107.
M. L. Mehta andJ. Burke,ibid. 31 (1975) 108.
A. W. Thompson,Met. Trans. 4 (1973) 2819.
C. L. Briant,ibid. 9A (1978) 731.
Idem, ibid. 10A (1979) 181.
D. Eliezer, D. G. Chakrapani, C. J. Altstetter, andE. N. Pugh,ibid. 10A (1979) 935.
A. W. Thompson,Mater. Sci. Eng. 14 (1974) 253.
J. P. Fidelle, L. R. Allemand, C. Roux andM. Rapin, “L'hydrogene dans les Metaux”, edited by J. P. Fidelle and M. Rapin (Centre d'etudes CEA, Bruyeres-le-chatel, 1967) p. 131, in French.
J. P. Fidelle, R. Bernardi, R. Broudeur, C. Roux andM. Rapin, ASTM Publication ASTM-STP 543, (ASTM, Philadelphia, 1974) p. 221.
R. L. Cowan andC. S. Tedman, Jr,Adv. Corr. Sci. Tech. 3 (1973) 293.
E. C. Bain, R. H. Aborn andJ. J. B. Rutherford,Trans. Amer. Soc. Steel Treating 21 (1933) 481.
ASTM Standard Number E8.
M. L. Louthan, Jr, G. R. Caskey, J. A. Donovan andD. E. Rawl,Mater. Sci. Eng. 10 (1972) 357.
G. R. Caskey,Scripta Met. 11 (1977) 1077.
A. W. Thompson, “Effect of Hydrogen on Behaviour of Materials” edited by A. W. Thompson and J. M. Bernstein (TMS-AIME, New York, 1976) p. 91.
A. W. Thompson andJ. A. Brooks,Met. Trans. 6A (1975) 1431.
A. W. Thompson,ibid. 10A (1979) 731.
H. Hannien andT. Hakkarainen,ibid. 10A (1979) 1196.
D. Eliezer, D. G. Chakrapani, C. J. Altstetter andE. N. Pugh, Proceedings of the Second International Congress on Hydrogen in Metals (Pergamon Press, Oxford and New York, 1977) p. 3F5.
L. K. Zamiryakin,Sov. Mater. Sci. 7 (1971) 9.
D. A. Vaughn, D. I. Phalen, C. L. Peterson andW. K. Boyd,Corrosion 19 (1963) 3157.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Minkovitz, E., Eliezer, D. Hydrogen-assisted cracking of sensitized 316L stainless steel. J Mater Sci 16, 2507–2511 (1981). https://doi.org/10.1007/BF01113588
Received:
Accepted:
Issue Date:
DOI: https://doi.org/10.1007/BF01113588