Abstract
Novel cross-linked fluorinated acrylate latex was successfully synthesized via the semi-continuous seeded emulsion polymerization, in which methyl methacrylate (MMA) and butyl acrylate (BA) were used as the main monomers, and dodecafluoroheptyl methacrylate (DFMA) and N–N methylene bisacrylamide (MBA) were used as the fluorine monomer and the cross-linked monomer, respectively. Potassium persulfate (KPS) and mixed surfactants of sodium lauryl sulfate and alkyl alcohol polyether (EFS-470) were used as the initiator and emulsifier, respectively. The structure of resultant latex film was characterized by Fourier transform infrared spectroscopy (FTIR). The latex films were tested by thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), contact angle (CA), cross-linked degree and X-ray diffractometer (XRD). The particle size and its distribution of the latex were measured by the nanoparticle size analyzer and transmission electron microscope (TEM). The factors that have an influence on the properties of the latex and the film are investigated in detail. The stability of the resultant latex was good. The average particles of the latex and its distribution were small and uniform, respectively. In comparison with the conventional latex film, the thermal stability and hydrophobicity of the novel latex film were improved obviously.
Similar content being viewed by others
References
Guan S (2013) Coating chemistry and technology. Chemical Industry Press, Beijing
Wang XR, Yang LL, Zhang WH, Wang XL (2017) Application study of cross-linked monomer modified acrylate emulsion. Coat Ind 47:29–34
Zhang ZX, Fu GW, Chen RQ, Wang CP (2019) Study on the properties of crosslinked emulsion after acrylate. Chin Adhes 28:1–4
Zhang J, Du M (2009) Self-crosslinking reactive acrylate microgel emulsion and coating properties thereof. Synth Rubber Ind 32:109–113
Bizet B, Grau E, Cramail H, Asua JM (2021) Crosslinked isocyanate-free poly(hydroxy urethane)s: Poly(butyl methacrylate) hybrid latexes. Eur Polym J 146:1–12
Machotova J, Knotek P, Cernoskova E, Svoboda R, Zarybnicka L, Kohl M, Kalendova A (2022) Effect of fluorinated comonomer, polymerizable emulsifier, and crosslinking on water resistance of latex coatings. Coatings 12:1150–1167
Shao TT, Gong YL, Chen XL, Chen LJ (2021) Preparation and properties of novel self-crosslinking long fluorocarbon acrylate (MMA-BA-DFMA-HPMA) polymer latex with mixed surfactants. Chem Pap 75:5561–5569
Fei GQ, Wang T, Yang J, Wang HH, Yang XF (2019) Effect of soft and hard monomers on polysiloxane/acrylate composite emulsion. Chin Adhes 28:6–12
Liu ZG, Ye H, Chao Z, Zhang MY, Li WM, Zhang HX, Liu FQ, Liu WJ (2010) Seeded emulsion polymerization of butyl acrylate using a redox initiator system: kinetics and mechanism. Ind Eng Chem Res 49:7152–7158
Parsimehr H, Pazokifard S (2022) Ambient temperature cross-linkable acrylic latexes: effect of cross-link density, glass transition temperature and application temperature difference on mechanical properties. Polym Bull 79:1347–1366
Qiu XZ, Li JW, Gu JJ, Xie RY, Yan XF, Qi DM (2022) Novel self-cross-linking fluorinated polyacrylate latex films with short chain perfluoroalkyl group: surface free energy and surface reorganization. React Funct Polym 172:105185
Liu Y, Tran K, Ho K, Emsermann J, Zhang M, Silva PPD, Walker G, Lucas F, Soleimani M, Winnik MA (2022) Influence of intraparticle cross-linking on polymer diffusion in latex films prepared from secondary dispersions. Influence of intraparticle cross-linking on polymer diffusion in latex films prepared from secondary dispersions. Prog Org Coat 164:106691
Gong YL, Shao TT, Chen LJ (2020) Preparation and characterization of fluorine-containing soap: free acrylic emulsion. Pigm Resin Technol 50:41–47
Yang TT, Peng H, Cheng SY, Park IJ (2005) Surface immobilization of perfluorinated acrylate copolymers by self-crosslinking. J Fluorine Chem 126:1570–1577
Chen YJ, Zhang CC, Wang YF, Cheng SY, Chen PZ (2003) Study of self-crosslinking acrylate latex containing fluorine. J Appl Polym Sci 90:3609–3616
Zhang YL, An QF, Yu Y (2013) Synthesis of self-crosslinked fluoroacrylic resin and its application in coatings. Coat Ind 43:31–35
Du PH, Xiao XY, Zhang HP, Wan CX (2007) Preparation of self-crosslinked fluoroacrylate copolymer emulsion. Chem Ind Eng Prog 26:1456–1461
Xu W, An QF, Hao LF, Zhang M (2014) Synthesis of self-crosslinking fluorinated polyacrylate soap-free latex and its waterproofing application on cotton fabrics. Fibers and Polym 15:457–464
Chen LJ, Wu FQ (2012) Preparation and characterization of novel self cross-linking fluorinated acrylic latex. J Appl Polym Sci 123:1997–2002
Fang C, Zhu K, Zhu XB, Li ZX (2019) Preparation and characterization of self-crosslinking fluorinated polyacrylate latexes and their pressure sensitive adhesive applications. Int J Adhes Adhes 95:1–8
Tuba ÇÇ, Esin H, Ersin S (2013) Synthesis and characterization of perfluorinated acrylate–methyl methacrylate copolymers. J Appl Polym Sci 128:1450–1461
Chen LJ, Shao TT, Gong YL (2019) Synthesis and characterization of fluoro-silicone polyacrylate latex emulsified with novel green surfactants. Prog Rubber Plast Recycl Technol 35:102–114
Cao XG, Ni TT (1998) Synthesis and application of N, N-methylenebisacrylamide. Chem Ind Times 11:28–29
Silvestri D, Gagliardi M, Cristallini C, Barbani N, Giusti P (2009) Different composition poly(methyl methacrylate-co-butyl methacrylate) copolymers through seeded semi-batch emulsion polymerization. Polym Bull 63:423–439
Steward PA, Hearn J, Wilkinson MC (2000) An overview of polymer latex film formation and properties. Adv Colloid Interface Sci 86:195–267
Jiang WL (2017) Evaluating the structure of thermoplastic elastomers by the equilibrium swelling method. World Rubber Ind 44:59–62
Xin H, Shen YD, Li XR (2011) Synthesis and properties of cationic polyurethane-fluorinated acrylic hybrid latexes by emulsifier-free emulsion polymerization and the solvent-free method. Polym Bull 67:1849–1863
Li Y, Xin X, Mao X (2019) Preparation and research of acrylate latex. In: Zhao P, Ouyang Y, Xu M, Yang L, Ren Y (eds) Advances in graphic communication, printing and packaging Lecture notes in electrical engineering. Springer, Singapore
Cao TY, Liu QP, Hu JS (1997) Synthetic principle, properties and application of polymer latex. Chemical Industry Press, Beijing
Nomura M, Tobita H, Suzuki K (2005) Emulsion polymerization: kinetic and mechanistic aspects. In: Okubo M (ed) Polymer particles. Advances in polymer science. Springer, Berlin, Heidelberg
Mariz IFA, de la Cal JC, Leiza JR (2010) Control of particle size distribution for the synthesis of small particle size high solids content latexes. Polymer 51:4044–4052
Liu S, An QF, Xu W, Yuan JM, Kang LJ (2010) Synthesis of long-chain fluoroacrylate emulsion and its application in leather waterproofing. New Chem Mater 38:138–140
Machotova J, Kalendova A, Steinerova D, Macova P, Slang S, Snuparek J, Vajdak J (2021) Water-resistant latex coatings: tuning of properties by polymerizable surfactant, covalent crosslinking and nanostructured ZnO additive. Coatings 11:347–369
Zhang FH, Jing C, Yan ZY, Ge SS, Liu P, Maganti S, Xu BB, Mahmoud KH, El-Bahy ZM, Huang MN, Guo ZH (2022) Fluorinated acrylic monomer modified core-shell polyacrylate latex particles: preparation, properties and characterizations. Polymer 247:1–10
Karsu Dülgar C, Serhatlı İE (2018) Synthesis of poly(BA-co-MMA) dispersions having AA/MAA/AAm/MAAm comonomers and the comparison of their effect on adhesive performance. Polym Bull 75:877–890
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflicts of interest
The authors do not have any conflict of interests to declare and there are no financial conflicts of interest.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.
About this article
Cite this article
Li, S., Gong, Z. & Chen, L. Study on preparing novel cross-linked and fluorinated acrylate latex. Polym. Bull. (2024). https://doi.org/10.1007/s00289-024-05165-5
Received:
Revised:
Accepted:
Published:
DOI: https://doi.org/10.1007/s00289-024-05165-5