Fatigue and Corrosion in Metals

  • Pietro Paolo¬†Milella

Table of contents

  1. Front Matter
    Pages i-xx
  2. Pietro Paolo Milella
    Pages 1-72
  3. Pietro Paolo Milella
    Pages 109-191
  4. Pietro Paolo Milella
    Pages 193-243
  5. Pietro Paolo Milella
    Pages 245-308
  6. Pietro Paolo Milella
    Pages 309-363
  7. Pietro Paolo Milella
    Pages 365-403
  8. Pietro Paolo Milella
    Pages 405-476
  9. Pietro Paolo Milella
    Pages 477-520
  10. Pietro Paolo Milella
    Pages 625-650
  11. Pietro Paolo Milella
    Pages 651-687
  12. Pietro Paolo Milella
    Pages 689-729
  13. Pietro Paolo Milella
    Pages 731-765
  14. Pietro Paolo Milella
    Pages 767-806
  15. Back Matter
    Pages 807-844

About this book


This textbook, suitable for students, researchers and engineers, gathers the experience of more than 20 years of teaching fracture mechanics, fatigue and corrosion to professional engineers and running experimental tests and verifications to solve practical problems in engineering applications. As such, it is a comprehensive blend of fundamental knowledge and technical tools to address the issues of fatigue and corrosion. The book initiates with a systematic description of fatigue from a phenomenological point of view, since the early signs of submicroscopic damage in few surface grains and continues describing, step by step, how these precursors develop to become mechanically small cracks and, eventually, macrocracks whose growth is governed by fracture mechanics. But fracture mechanics is also introduced to analyze stress corrosion and corrosion assisted fatigue in a rather advanced fashion. The author dedicates a particular attention to corrosion starting with an electrochemical treatment that mechanical engineers with a rather limited knowledge of electrochemistry will well digest without any pain. The electrochemical introduction is considered an essential requirement to the full understanding of corrosion that is essentially an electrochemical process. All stress corrosion aspects are treated, from the generalized film rupture-anodic dissolution process that is the base of any corrosion mechanism to the aggression occurring in either mechanically or thermally sensitized alloys up to the universe of hydrogen embrittlement, which is described in all its possible modes of appearance. Multiaxial fatigue and out-of-phase loading conditions are treated in a rather comprehensive manner together with damage progression and accumulation that are not linear processes. Load spectra are analyzed also in the frequency domain using the Fourier transform in a rather elegant fashion full of applications that are generally not considered at all in fatigue textbooks, yet they deserve a special place and attention. The issue of fatigue cannot be treated without a probabilistic approach unless the designer accepts the shame of one-out-of-two pieces failure. The reader is fully introduced to the most promising and advanced analytical tools that do not require a normal or lognormal distribution of the experimental data, which is the most common case in fatigue. But the probabilistic approach is also used to introduce the fundamental issue of process volume that is the base of any engineering application of fatigue, from the probability of failure to the notch effect, from the metallurgical variability and size effect to the load type effect. Fractography plays a fundamental role in the post mortem analysis of fatigue and corrosion failures since it can unveil the mystery encrypted in any failure.


Damage accumulation and progression Fractography Stress corrosion Stress/strain Fatigue life Variable amplitude loading

Authors and affiliations

  • Pietro Paolo¬†Milella
    • 1
  1. 1., Faculty of EngeneeringUniversity of Cassino, ItalyCassino (FR)Italy

Bibliographic information

  • DOI
  • Copyright Information Springer-Verlag Italia 2013
  • Publisher Name Springer, Milano
  • eBook Packages Engineering
  • Print ISBN 978-88-470-2335-2
  • Online ISBN 978-88-470-2336-9
  • Buy this book on publisher's site