Abstract
PrBaCuO and YBaCuO cuprate materials were prepared from cooper, barium peroxide, and yttrium/praseodymium oxide by SHS and standard solid-state synthesis. SHS reactions were carried out using relatively large cooper particles (< 63 im) to obtain small product samples (13 mm in diameter). High ambient temperature was used to stabilize a combustion front in the ignited pellets. Explored was the effect of cooper particles size, starting density, and ambient temperature on phase evolutions in synthesized materials.
Similar content being viewed by others
References
Merzhanov, A.G., Materials from Exothermic Reactions, Arch. Combust., 1990, vol. 2, p. 570.
Chen, H.J. and Sharp, J.H., YBa2Cu3O6+x Synthesis Using Vertical Self-Propagating High-Temperature Synthesis, Physical, 1994, vol. 233, pp. 281–291.
Kuznetsov, M.V., Peresada, A.G., Morozov, Yu.G., Nersesyan, M.D., and Ponomarev, V.I., Properties of YBa2Cu3O6+x Superconductor Prepared by Self-Propagating High-Temperature Synthesis, Inorg. Mater., 1994, vol. 30, p. 94.
Merzhanov, A.G., Combustion Processes That Synthesize Materials, J. Mater. Process. Technol., 1996, vol. 56, p. 222.
Deawha, S. and Natalya, K., Peculiarities of SHS and Solid State Synthesis of ReBa2Cu3O7-x, J. Korean Inst. Electr. Electron. Mater. Eng., 2002, vol. 15, p. 275.
Liechtenstein, A.I. and Mazin, I.I., Quantitative Model for the Superconductivity Suppression in R1-xPrxBa2Cu3O7 with Different Rare Earths, Phys. Rev. Lett., 1995, vol. 74, p. 1000.
Blackstead, H.A., Observation of Superconductivity in PrBa2Cu3O7, Phys. Rev. B, 1996, vol. 54, p. 6122.
Zou, Z., Ye, J., Oka, K., and Nishihara, Y, Superconducting PrBa2Cu3Ox, Phys. Rev. Lett, 1998, vol. 80, pp. 1074–1077.
Collin, G., Alboy, P.A., Monod, P., and Ribault, M., Praseodymium Valency from Crystal Structure of Pr-Ba-Cu-O and (Y-Pr)-Ba-Cu-O Single Crystals, J. Phys. (Paris), 1990, vol. 51, p. 1163.
Luo, H.M., Lin, B.N., Lin, Y.H., Chiang, H.C., Hsu, Y.Y., Hsu, T.I., Lee, T.J., Ku, H.C., Lin, C.H., Kao, H.C.I., Shi, J.B., Ho, J.C., Chang, C.H., Hwang, S.R., and Lin, W.H., Variation of Anomalous Pr Ordering and Crystal Symmetry for the Oxygenated Pr1 +xBa2 -xCu3O7+y System, Phys. Rev. B, 2000, vol. 61, p. 14825.
Kramer, M.J., Dennis, K.W., Falzgraf, D., McCallun, R.W., Malik, S.K., and Yelon, B., Suppression of Superconductivity in R(Ba1-zRz)2Cu3O7 + δ, (R = Pr, Nd), Phys. Rev. B, 1997, vol. 56, p. 5512.
Neumeier, J.J., The Absence of Superconductivity in Praseodymium Barium(2) Copper(3) Oxide, PhD Thesis, University of California, 1990.
Chen, H.J. and Sharp, J.H., Self-Propagating High Temperature Synthesis of RBa2Cu3Oy (R=Y, Er or Yb) Superconductors, J. Mater. Sci. left, 1992, vol. 11 p. 1223.
Rupp, B., Wong, J., Holt, J.B., and Waide, P., The Solid Combustion Synthesis of Small REBa2Cu3Ox Samples (RE = Y, Er), J. Alloys Comp., 1994, vol. 209, pp. 25–33.
Lin, S.C., Dong, X., Li, R.S, Richardson, J.T., and Luss, D., SHS of YBa2Cu3O6 + x Using Large Cooper Particles, Physica C, 1993, vol. 218, pp. 130–136.
Park, M., Kramer, M.J., Dennis, K.W., and McCallum, R.W., Phase Equilibria in the Pr-Ba-Cu-O System under Varied Oxygen Partial Pressures, Physica C, 1996, vol. 259, pp. 43–53.
Author information
Authors and Affiliations
Corresponding author
Additional information
The text was sumbitted by the authors in English.
About this article
Cite this article
Sehab, N., Harat, A., Benaldjia, A. et al. Combustion Synthesis of PrBa2Cu3O7−δ and YBa2Cu3O7−δ cuprate materials. Int. J Self-Propag. High-Temp. Synth. 18, 235–240 (2009). https://doi.org/10.3103/S1061386209040025
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.3103/S1061386209040025