Abstract
We established a Ca1-xBixMn1-yNiyO3 (0 ≤ xy ≤ 0.1) powder library using a combinatorial system based on the electrostatic spray deposition method. Single phase perovskite-type structures were identified in all of the powders. To measure electrical conductivity, the powder library was subjected to high-pressure (200 MPa) and heat-treated at 950°C for 1 hour in an oxygen atmosphere. As a representative example, the electrical conductivity of 5%-Bi-substituted CaMnO3-δ showed a higher value (63 S·cm-1) than an unsubstituted powder (13 S·cm-1). The improved electrical conductivity, on the other hand, was still very far from the ideal result (167 S·cm-1).
Similar content being viewed by others
References
R. B. Merrifield, J. Am. Chem. Soc., 85 (1963) 2149
J. J. Hanak et al., Physica, 55 (1971) 555
H. Koinuma et al., Jpn. J. Appl. Phys., 27 (1988) L1887
H. Koinuma et al., Nature Materials, 3(7) (2004) 429–438
X. D. Xiang et al., Science, 268 (1995) 1738
K. Fujimoto et al., Applied Surface Science, 223 (2004) 49.
K. Fujimoto et al., Measurement Science and Technology, 16 (2005) 41–45
K. Fujimoto et al., Solid State Ionics, 177 (2006) 26–39
K. Fujimoto et al., ACS Combinatorial Science, 16(2) (2014) 66–70
K. Fujimoto et al., ACS Combinatorial Science, 15 (2013) 622–625
M. Ohtaki et al., Journal of Solid State Chemistry, 120 (1995) 105–111
L. Bocher et al., Inorg. Chem., 47 (2008) 8077–8085
X.Y. Huang et al., Solid State Communications, 145 (2008) 132–136
X.H. Zhang et al., Journal of Alloys and Compounds, 634 (2015) 1–5
R. Kabir et al., Journal of Alloy and Compounds, 628 (2015) 347–351
K. Fujimoto et al., Key Engineering Materials, 617 (2014) 256–259
K.R. Poeppelmeier et al., Journal of Solid State Chemistry, 45(1) (1982) 71–9.
K.R. Poeppelmeier et al., Journal of Solid State Chemistry, 44(1) (1982) 89–98.
Author information
Authors and Affiliations
Rights and permissions
About this article
Cite this article
Fujimoto, K., Gibu, M., Yamaguchi, Y. et al. Phase relation and thermoelectric property of Ca1-xBixMn1-yNiyO3 (0 ≤ xy ≤ 0.1). MRS Advances 1, 1941–1946 (2016). https://doi.org/10.1557/adv.2016.173
Published:
Issue Date:
DOI: https://doi.org/10.1557/adv.2016.173