Abstract
Modifying the metal surface is one solution to the industry’s growing corrosion problem. Thus, via threading approach and insertion of copolymers (CoP5-7) containing polyarylidenes through the internal cavity beta-cyclodextrin β-CD, novel pseudopolyrotaxanes copolymers (PC5-7) are developed, resulting in mild steel corrosion inhibition. Inhibitors of corrosion based on β-CD molecules adsorb strongly to metal surfaces because of their many polar groups, adsorption centers, many linkages of side chains, and benzene rings. The corrosion inhibition efficiencies IE % statistics have been revised via the Tafel polarization method and Spectroscopy based on the electrochemical impedance (EIS), with PC7 achieving the highest 99.93% in 1.0 M H2SO4; they are mixed-type inhibitors. The chemical composition of the resulting PCs is determined with Fourier transform infrared spectroscopy (FTIR), Scanning electron microscopy (SEM) is utilized to examine the morphological structure of the produced polymers, and X-ray diffraction is employed to identify crystallinity. Encapsulating CoP5-7 with β-CD changes the morphological structures and increases the generated PCs' crystallinity. The thermal stability of PCs is studied, indicating the presence of these CoPs within the β-CD cavities enhances their thermal stability. This research will be a stepping stone for developing high-efficiency anti-corrosion coatings and various industrial applications.
Similar content being viewed by others
Explore related subjects
Find the latest articles, discoveries, and news in related topics.Introduction
The delocalization of π bonds in conducting polymers (CPs) relies on the disorder of their chains and generates charge carriers to transfer their nature to be a metal [1]. They have broad and significant applications in different fields and problems, including the corrosion problem. This trouble is considered serious and can extremely produce loss and environmental hazards. CPs can reduce corrosion by keeping the metal passive through different mechanisms [2, 3]. Their use as inhibitors has some limitations because of their poor adhesion, sponginess, and irreversibility of charge consumption. The direction toward modification of CPs is continued and in progress by different techniques from nano to composites [4, 5].
Overcoming the corrosion of several kinds of steel is the fundamental issue facing the industrial sectors. By adding corrosion inhibitors, steel is effectively protected against corrosion during acid pickling to remove mill scale from metallic surfaces. It is possible to use several conventional corrosion materials as inhibitors. However, using this kind of inhibitor raises concerns about environmental safety. The majority of organic corrosion inhibitors are made via numerous phases of reactions with traditional heating, hazardous and expensive chemicals, solvents, and catalysts. The classic organic corrosion inhibitors also have fewer adsorption sites in their molecular architectures, which results in inadequate metal surface coverage. Additionally, they only partially dissolve in polar electrolytes. Therefore, only at increasing concentrations do these chemicals start to work [6].
Many efforts have recently been undertaken to discover novel natural and biodegradable compounds that can be corrosion inhibitors but don’t hurt people or the environment. The fact that polysaccharides have active sites interacting with metal ions makes them potential green and natural inhibitors [7].
Macrocyclic materials are large planar systems, and their derivatives, such as crown ethers, phthalocyanines, porphyrin rings, calixarenes, and cyclodextrins, are among the substances most commonly used as effective corrosion inhibitors [8].
One of these strategies is the use of cyclodextrins (CDs) to modify the solubility or form an insulated molecular wire through polyrotaxane formation (PRs) by preventing their oxidation by losing their delocalization [9,10,11]. CDs are a type of cyclic oligosaccharide made up of 6 to 8 glucopyranose units, designated by the letters α‚ β- and γ CD. They have a unique structure with an internal surface resembling a cavity with hydrophobic characteristics. They could contain various organic and polymeric compounds or complexes that can form inclusions with organic molecules in an aqueous medium [12]. CD inner diameters are − 0.47, − 0.60, and − 0.75 nm, with a cavity depth of 0.79 nm. CDs are essential in the improvement of supramolecular chemistry and have important uses in material science, such as rigid polymers [13, 14], therapeutic science [15, 16], and cosmetics [17]. The dominant driving forces for creating supramolecular structures are the hydrophobic interaction and the hydrogen bonding in the crystal structure and the hydrous solutions [18, 19]. Cyclodextrin, the most common kind, comprises seven units of glucopyranose and two types of hydroxyl groups, secondary and primary groups, resulting in a macromolecule with twenty-one hydroxyl groups in total [20].
Supramolecular (host–guest) systems based on polymer β-cyclodextrin (CD) are used to develop new materials with desirable properties for green corrosion inhibitors. These materials have a high inhibitory efficiency while being durable, inexpensive, eco-friendly, and user-friendly. In contrast to other interlocked compounds made up of polymer chains and macrocyclic molecules, polyrotaxanes (PRs) have intramolecular mobility characterized by rotation and sliding of the rings along the chains [21]. Supramolecular complexes based on CD derivatives like octadecyl amine [22, 23], organic compounds [24,25,26], and also CD modified with graphene produce effective corrosion Inhibitors [27]. There are a few considerations about conducting polymer and Cyclodextrin using CDs as a template molecule, dopant, or conformation converter [28,29,30,31].
The main goal of this investigation is to create and innovate new types of corrosion inhibitors that rely on β-CD macromolecules by modifying the corrosion inhibition of conducting copolymers that have already been produced, adding β-CD rings, and then analyzing the results to see how this inclusion affects the characteristics of the conducting copolymers and the corrosion efficiency.
Experimental
Materials
β-cyclodextrin (β-CD) (Merck company, Germany), dimethylformamide (DMF) (Aldrich, Milwaukee, Wisconsin, USA) without additional purification, cyclopentanone, cyclohexanone, and cycloheptanone (Merck) were employed without crystallization, terephthaldehyde (Alfa Aesar) was utilized without further purification, sulfuric acid (H2SO4) was used as an acid medium (purchased from PROLABO), all chemical compounds were used as obtained.
Synthesis of copolymers (CoPs5-7)
The copolymerization of terephthaldehyde with various cycloalkanones (cyclopentanone, cyclohexanone, and cycloheptanone) was previously reported [32,33,34,35,36,37]. The synthesis of copolymers is shown in (Scheme 1) as a synthetic approach (CoP5-7).
Synthesis of pseudopolyrotaxane copolymer (PC5)
The copolymer (CoP 5) (1.5 g) was dissolved in 15 mL DMF before adding to the β -CD solution (5 g, 4.40 mmol in 30 ml DMF) at 70 °C; the reaction mixture was agitated for 22 h. The precipitate was filtered off, washed with distilled water, and dried as yellow PC5 (86% product, m.p. over 300 °C).
Synthesis of pseudopolyrotaxane copolymer (PC6)
The copolymer (CoP 6) (1.0 g) was dissolved in 10 mL DMF before adding to the β-CD solution (3 g, 2.64 mmol in 20 ml DMF) at 70 °C; the reaction mixture was agitated for 18 h. The resulting precipitate was filtered out, washed with distilled water, and dried to yield the (PC6) deep yellow residue (77% yield, m.p. over 300 °C).
Synthesis of pseudopolyrotaxane copolymer (PC7)
The copolymer (CoP 7) was dissolved in 30 mL DMF and added to the β-CD solution (3.5 g, 3.08 mmol in 20 ml DMF) at 70 °C; the reaction mixture was stirred for 24 h. Until the formation of yellow precipitate. The (PC7) was filtered out and dried in a 75% yield, m.p. over 300 °C.
Preparation of the corrosive solution and test specimens:
The corroding media in electrochemical experiments was Analar grade H2SO4 and was applied as an aerated solution. The working electrode was mild steel; all analyses were performed and accomplished in Cairo at the Tabbin Institute for Metallurgical Studies. Mild steel components are 0.022% F, 0.011% Mo, 0.011% Sn, 0.17% C, 0.71% Mn, 0.022% Si,0.045% Cr, 0.010% P, 0.0017% Al, 0.072% Ni, 0.182% Cu, and 98.74% Fe. The electrode was polished with emery paper ranging from 1000 to 1400 grade, then cleaned with distilled water before degreased with acetone. After about 5 min, rinsed again with distilled water and dried using filter paper [38].
Preparation of corrosive and inhibitor solutions
All of the corrosion inhibitors in the study were made by dissolving copolymer and polyrotaxane in DMF (200 ppm). The electrochemical tests were performed by pickling a mild steel electrode for 15 min in the produced corrosion inhibitors solution, then drying and immersed in 1.0 M H2SO4 (25 mL) [39].
Measurements
Before analysis, the samples were carefully dried under a vacuum to eliminate residual solvent molecules. The chemical structures of the synthesized pseudopolyrotaxane copolymers were proved using Fourier transform infrared (FT-IR) spectroscopy. An infrared spectrometer (Jasco Model 4100—Japan) with a wavenumber range of 4000–500 cm−1 was used to analyze the functional groups in the generated pseudopolyrotaxane copolymers at room temperature. The morphological structures of the generated pseudopolyrotaxane copolymers were revealed using SEM imaging with the Jeol JSM-5400 LV instrument (SEM). A powder diffractometer (Brucker D8 Advance, Germany) with Cu K radiation source, λ = 1.5406 and 2θ in the range (5–80°) was used to measure X-ray diffraction bands at indoor temperature to study the specimen's phase and crystalline structure. The Thermal Analyzer TA Q-600 measures thermogravimetric analysis (TGA) at a 10 °C/min rate in an N2 environment.
Electrochemical measurements
All electrochemical experiments, open circuit potential (OC), linear and Tafel polarization (LP, TP) were carried out by electrochemical instrument (EG & G potentiostat/galvanostat model 273A) using a 352/252 corrosion measurement system. The steady-state potential Es.s (open circuit potential technique) were immediately evaluated after pickling the working electrode(mild steel) within the prepared solutions, followed by potentiodynamic polarization parameters (LP, TP). electrochemical impedance spectroscopy (EIS) was measured through (Corrtest CS350). The linear polarization (LP) and the Tafel polarization (TP) were determined in the range (of + 20 to − 20 mV) and (− 250 to + 250 mV) using scan rates of 0.166 and 0.4 mV/S, respectively. The rate of corrosion (CR) and the corrosion inhibition efficiency percentage (IE %) were detected using Eqs. 1 and 2 [40].
where C.R (mpy): corrosion rate (millimeters per year), Icorr: corrosion current density (μA/cm2), (Eq. Wt): equivalent weight of the metal (g/eq), A: surface area (cm2), d: density (g/cm3), and 0.13: metric and time conversion factor.
where (CR uninh, CR inh): corrosion rates without or with inhibitors, respectively.
Results and discussion
For organic compounds to work as corrosion inhibitors, they need oxygen atoms that can easily stick to the surface of the metal. This is done by forming coordination bonds between the metal and the organic compounds’ unshared electron pair. The prepared supramolecular copolymers' chemical structure has many carboxyl and hydroxyl groups. As a result, the supramolecular copolymers’ active groups can attach to the metal’s surface and prevent corrosion. In addition to pseudopolyrotaxanes, β-CD copolymers can prevent metal from corroding at both high and low temperatures. This is because they are soluble and have π-bonds. Also, these compounds are made in ways that are good for the environment and don’t cost much. So, these compounds are considered the next generation of chemicals that stop corrosion [41, 42].
FT-IR spectroscopy
The threading approach was utilized to synthesize pseudopolyrotaxane copolymers (PCs5-7). β–CD rings include the (OH) groups that raise coordination bonds with metal surfaces and decrease corrosion development accordingly. The unique cone-shaped structure of β–CD makes it acceptable to construct inclusion complexes by encapsulating the arylidene copolymers (CoP5-7) into its cavity to yield the different polyrotaxanes by the complex inclusion method. This behavior achieves and stabilizes by creating non-covalent bonds like Vander Waals forces, hydrogen bonding, and hydrophobic-hydrophobic interactions between the hydrophobic cavity and the hydrophobic moieties of conducting arylidene Copolymers chains (aliphatic cyclic chains and aromatic rings). The chemical functional group's features and vibration were examined using IR spectroscopy. (Fig. 1) compares the FTIR spectra of the prepared (CoP5-7) and the new pseudopolyrotaxane copolymers (PCs5-7). The FTIR spectrum of (CoP5) affords peaks at 2891, 3010, 1726 and 1664 \({\mathrm{cm}}^{-1}\), represent CH aliphatic, CH aromatic, C=O group, and C=C, respectively. Meanwhile, the FTIR spectrum of (PC5) shows bands at 2885, 3007, 1734, and 1669 cm−1 due to CH aliphatic, CH aromatic, C=O group, and C=C, respectively. The broadband in the (PC5) spectrum at \(\sim\) 3393 cm−1 attributes to stretching vibrations of (OH) groups intermolecular hydrogen bonding in β–CD rings also, between the carbonyl group in (PC5). The FTIR spectrum of (PC5) indicates some spectral variations like energy shifting towards the lower wavenumber for (CH aliphatic and CH aromatic) and their intensity increase. In contrast, the bands for (C=O and C=C) were shifted toward high frequencies with less intensity. In the FT-IR spectrum (CoP6), the peaks for its active groups appear at 2843, 3012, 1743, and 1674 cm−1 due to CH aliphatic, CH aromatic, C=O group, and C=C, respectively. In addition, the bands for (PC6) appeared at 2854, 3018, 1736, and 1671, respectively, with increasing and decreasing intensity; this result is due to the overlapping between carbonyl groups with OH groups. Also, the hydrogen bond interaction between the carbonyl groups of the guest molecule and the (OH) groups of the β-CD ring causes the displacement of the C=C and carbonyl groups to higher wavenumbers and boosts their intensity [37, 43,44,45,46]. Due to the inclusion of (CoP6) inside the hydrophobic cavity of β-CD, the distinctive absorption band due to (OH) groups of (PC6) became sharper than pure β-CD [47]. Interactions between the ether linkage inside the cavity and the benzene rings are also hydrophobic-hydrophobic (CoP6) [48].
FT-IR spectra of the obtained (PC7) are displayed in (Fig. 1), which shows that the peak of the aliphatic CH symmetric stretching and CH aromatic of the (CoP7) were present at 2843, 3006 cm−1 and were shifted to higher frequencies. After complex inclusion, the peaks of [C=O] were moved to lower frequencies due to hydrogen bonding between OH groups of β-CD and CO groups of (CoP7). The variations of (CoP5-7) frequencies and (PC5-7) are presented in (Table 1), which describes the frequency changes of (CoP5-7) and (PC5-7) when the inclusion complex is created (PC5-7). These results could mean that (CoP5-7) and β-CD join together to make a complexation. The maximum value is raised by incorporating (CoP5-7) chains into the cyclodextrin rings' electron-rich cavity [37, 43]. Instead, hydrogen bonding between neighboring β-CD rings and Vander Waals forces between the OH groups of β-CDs and CO groups of copolymers are responsible for the attenuation of peaks.
X-RD analysis
After making inclusion complexes by putting copolymer chains into the hydrophobic cavity of cyclodextrins, the inclusion shifts the diffraction peak to smaller angles and changes the d-spacing. X-ray diffraction is an excellent and vital way to figure out how the crystal structures of copolymers (CoP5-7) and inclusion complexes are different (PCs). The X-ray patterns of the copolymers (CoP5-7) compared to (PC5-7) are shown in (Fig. 2). Copolymers (CoP5-7) have crystallinity values of 82.4, 31.8, and 59.8%, respectively. Pseudopolyrotaxane copolymers (PC5-7) have crystallinity values of 75.8, 58.8, and 70%, respectively. Planarity and structural effect are responsible for the significant rise in (CoP6,7) crystallinity and the slight decrease in (CoP5) crystallinity. The PC5 crystallinity diminishes because the monomer molecules' planarity reduces as the cyclic ketone size grows. [39]. Due to planarity, copolymer layers stack, and crystallinity rises; hence the structure of CoP5 is more crystalline than its PC5 counterpart, which decreases crystallinity and prevents stacking in contrast to other samples [49]. CoP6,7 inclusion complexes are channel types with an extended column structure, whereas CoP5 is a cage-type [50, 51].
We can extrapolate that complex formation, phase structure, and crystallite size (PC5-7) improve (CoP5-7).
SEM analysis
The structures and morphology of (CoP5-7) and (PC5-7) were observed by SEM analysis, as revealed in (Fig. 3). The copolymer (CoP5-7) possessed an amorphous and grainy structure from the previous work [39]. In contrast, the structures of (PC5-7) were changed. The morphology structure of (PC5) has a regular shape, like holes. In addition, SEM scans of the (PC6) matrix revealed a consistent, smooth, and pore-free surface. This architecture shows the integration of β-CD into the chain of copolymers; the regularity results from creating an inclusion complex. Furthermore, the surface morphology of (PC7) was presented as characteristic slides.
Thermogravimetric analysis:
The thermogram of the TGA. PC5-7 and CoP5-7 displayed a three-step weight decrease (Fig. 4). The initial loss of weight was attributable to solvent and water evaporation. In contrast, the second and third weight losses were caused by CD degradation and aromatic residue breakdown, respectively, resulting in char formation (Table 2). The inclusion of CD complexes decreases the degradation temperature and increases the decomposition rate. Furthermore, the final Td increased considerably during composite production with CD in PC7; all CoP5-7 exhibits greater degradation temperatures than their respective PC5-7 and a high char yield at 600 °C, except for PC7; it is evident that the structure of CoP5-7 and CD has a discernible effect on their thermal stability. However, PC7 was expected to have the maximum char yield among the PRCP; the existence of a cycloheptanone moiety next to the aromatic carbons improved the polarity of the monomer molecule. According to prior quantum calculations, CoP7 has a greater dipole moment of 2.6 in the trans conformer than CoP5 and CoP6, which have dipole moments of 1.4 and 0.1, respectively, demonstrating its greater polarity and more bonding between CD than the other CoP5,6 [39]. Due to the hydrogen bond between CD and the guest molecule, the degradation temperature generally rises as polarity increases, hence thermal stability [52]. These data provide additional proof of the development of PC5–7.
Electrochemical examinations
Open circuit potential estimations
The open-circuit technique is the relationship between time (t) and potential (E) in the absence of counter electrodes to stabilize the potential of electrochemical cells. (Fig. 5) describes all inhibitors or blanked solutions' steady-state potential (Es.s). It leads to incorporating an oxide film of mild steel electrodes surface. A blank solution’s steady-state potential (Es.s) altered significantly positively relative to its immersion potential (Eim.). These changes are attributable to the modified copolymers (PC5–7) adsorbed on active surface sites.
Polarization measurements
Previous research has shown that steric parameters, electron density, active groups, metal type, and organic-metal connections affect the mechanism by which organic molecules bind to a metallic surface. Physical contact is the initial step in this phenomenon [53, 54]. Donor–acceptor interactions between unoccupied electron pairs of heteroatoms or electrons of multiple bonds and between vacant d orbitals of metals lead to the chemical adsorption of organic compounds. As shown in (Fig. 5), the inhibitory mechanism of PC5-7 on the mild steel surface primarily involves the -CO- groups and conjugated electrons of PCs molecules, which serve as anodic adsorption sites. Anodic adsorption centers block cathodic reactions that result in the evolution of hydrogen. The hydroxyl -OH groups of β-CD served as the physical adsorption centers because they donate more electrons. Electrostatic repulsion between the -OH groups on the metal surface and the corrosion inhibitors caused a reaction. The rate of anodic disintegration decreased dramatically [55,56,57].
Tafel polarisation (TP) provides a visual representation of the method by which corrosion inhibition occurs as a relation between Log I (μA/ cm2) and potential E. (mv). The potentiodynamic polarization of studied corrosion inhibitors (PC5-7) in 1.0 M H2SO4 compared with reviewed (CoP5-7) [39] is displayed in (Fig. 5). The parameters of electrochemical polarization measurements are shown in (Table 3), corrosion current density (Icorr), rate of corrosion (CR), and effectiveness in preventing corrosion (IE%). The inhibition efficiencies (IE %) of reviewed (CoP5-7) depend on the chemical composition and the chain length that they are increased by increasing the molecular weight from CoP5 to CoP7 (85.2–87.8%), respectively [39]. Introducing β-Cyclodextrin to the chain of (CoP5-7) by the threading method that is mentioned above yields excellent corrosion inhibitors (PC5-7) with IE % (99.88–99.93). The remarkable efficacy of inhibition of modified (PC5-7) was enhanced by the addition of β-cyclodextrin to the chain of (CoP5-7), which is characterized by a large bulky polymer, hydrophobic cavities, mild steel has a thin layer of Fe2O3 on its surface, and modified inhibitors hold to it very well. Indicating the increased adsorption of particular PCs on mild steel, the degree of surface coverage measure (θ = IE%/100) was the most helpful in explaining the enhanced corrosion prevention [58]. The surface coverage increased from PC5 to 7 due to the steady rise in polarity of CoP5-7 that altered the interaction between them and β-CD, resulting in molecules with high insulation and complexation that is responsible for their increasing inhibiting PCs from 5 to 7, which covered a vast metal surface area [59]. The distinction between the corrosion potential of the blank solution and the solution containing inhibitors less than 85 mv leads to the classification of the inhibitors as mixed inhibitors [60].
Correlated impedance profiles can give insight into surface properties and reaction kinetics, making EIS a crucial pre-method in corrosion investigations [61]. (Figure. 6) shows the Nyquist of mild steel in 1.0 M H2SO4 with and without several different polymer samples. As can be seen in (Fig. 6), All of the existing polymeric additives exhibited wider capacitive loops compared to the blank medium, and the protection power exhibited more significant increases with the enhanced, modified polymer, indicating that the polymer layer on the steel interface became denser, leading to the strengthening of MS inhibition. This showed that MS surface inhibition had been enhanced due to increased polymer covering of the metal. Meanwhile, the capacitive loops in all the Nyquist profiles were remarkably similar, proving that the corrosion mechanism was unaffected by the polymer additions. The frequency dispersion also caused incomplete Nyquist profiles, the metal interface's roughness, and heterogeneous nature, adsorbed polymer additives on the MS substrate, and their combined effect [62, 63].
(Figure 7) displays the surface SEM pictures of mild steel before and after being submerged in a 1 M H2SO4 solution without and with (PCs 6,7). (Fig. 7a, b) shows that the extensive dissolution of mild steel in H2SO4 solution has severely damaged the metal surface, as seen by the numerous breaks and voids that have developed all over the steel. In contrast, the mild steel corroded less when PC was added to the environment (Fig. 7c, d). The mild steel surface has been treated with inhibitors by adsorption., improving the surface's facial structure and offering a remarkable level of corrosion protection by slowing down metal dissolution. The organic layer in the SEM pictures supports the findings of the electrochemical tests covered in the earlier sections [63].
Natural and synthetic polymers are added to β-cyclodextrin (β-CD) corrosion inhibitors to improve their efficacy by forming simple ether bonds between them and externally active hydroxyl functional groups. Based on the data in (Table 4), the results demonstrate that forming O-C bonds is responsible for most β-CD modifications. Whether in an acidic or basic environment, the polymers can impede the activity of various metals, making them an intriguing guest for the β-CD host. More stability is achieved in host–guest (supramolecular) systems based on polymer β-CDs because of the contacts, H bonds, and noncovalent interactions between the host and guest. (Table 4) shows PC5-7 and other inhibitors' corrosion inhibitory capacity (CD). As was demonstrated, the achieved inhibition efficiency in this study was much higher than that seen in the literature [64,65,66,67,68,69,70]. This result demonstrates the PCs' promising capability of inhibiting mild steel.
Conclusion
This study is about making and using green, long-lasting anti-corrosion agents derived from β-CD compounds to protect mild steel from corrosion. The research and development of β-CD-based compounds as corrosion inhibitors are crucial for making the next generation of corrosion-resistant materials. This paper describes a simple and effective approach for manufacturing novel pseudopolyrotaxane copolymers (PC5-7) by threading β-CD through the chain (CoP5-7). Tafel polarization and electrochemical impedance spectroscopy (EIS) have been used to estimate anti-corrosion effectiveness IE%; PC7 has the highest inhibitor, at 99.93% in 1.0 M H2SO4; these inhibitors are mixed-type. FT-IR spectroscopy analysis was employed to establish the chemical structures of the produced polymers. The morphology of the CoPs and PCs was studied using SEM. Compared to the prepared (CoP5-7), the SEM images demonstrate distinct morphological shapes for the prepared (PC5-7). According to X-RD, the addition of complex formation between β-CD and the (CoP5-7) increased the crystallinity of the resultant PCs. TGA studies of their thermal stabilities reveal the production of PCs with higher and modified thermal stability in PC7 due to the increased connection between β-CD and CoP7. The corrosion inhibition of PC5-7 is investigated and found to be suitable for usage as mixed-type inhibitors, with increased mild steel inhibition reaching its highest value in PC7.
Availability of data and materials
All data generated or analyzed during this study are included in this published article.
References
Le T-H, Kim Y, Yoon H. Electrical and electrochemical properties of conducting polymers. Polymers. 2017;9(4):150.
Gašparac R, Martin CR. Investigations of the mechanism of corrosion inhibition by polyaniline polyaniline-coated stainless steel in sulfuric acid solution. J Electrochem Soc. 2001;148(4):B138.
Kinlen PJ, Menon V, Ding Y. A mechanistic investigation of polyaniline corrosion protection using the scanning reference electrode technique. J Electrochem Soc. 1999;146(10):3690–5.
Eftekhari A. Nanostructured conductive polymers. Hoboken: John Wiley & Sons; 2011.
Bhandari H, SA Kumar, S Dhawan. Conducting polymer nanocomposites for anticorrosive and antistatic applications. Nanocomposites: New Trends and Developments, 2012: p. 73–96. https://doi.org/10.5772/50470.
Verma C, et al. Corrosion inhibition potential of chitosan based schiff bases: design, performance and applications. Int J Biol Macromol. 2021;184:135–43.
Ashassi-Sorkhabi H, Kazempour A. Chitosan, its derivatives and composites with superior potentials for the corrosion protection of steel alloys: a comprehensive review. Carbohyd Polym. 2020;237:116110.
Berdimurodov E, et al. Green β-cyclodextrin-based corrosion inhibitors: recent developments, innovations and future opportunities. Carbohyd Polym. 2022;292:119719.
Anderson S, et al. An approach to insulated molecular wires: synthesis of water-soluble conjugated rotaxanes. J Chem Soc Perkin Trans 1. 1998. https://doi.org/10.1039/a802680g.
Taylor PN, et al. Insulated molecular wires: synthesis of conjugated polyrotaxanes by suzuki coupling in water. Angew Chem Int Ed. 2000;39(19):3456–60.
Belosludov RV, et al. Theoretical study on inclusion complex of polyaniline covered by cyclodextrins for molecular device. Jpn J Appl Phys. 2002;41(4):2739–41.
Saenger W. Structure aspects of cyclodextrin inclusion compounds. Dordrecht: Springer; 1982.
Ito K. Novel entropic elasticity of polymeric materials: why is slide-ring gel so soft? Polym J. 2012;44(1):38–41.
Yasumoto A, et al. Highly responsive hydrogel prepared using poly(N-isopropylacrylamide)-grafted polyrotaxane as a building block designed by reversible deactivation radical polymerization and click chemistry. Macromolecules. 2017;50(1):364–74.
Pontikis CC, et al. Cyclodextrin alleviates neuronal storage of cholesterol in niemann-pick C disease without evidence of detectable blood–brain barrier permeability. J Inherit Metab Dis. 2013;36(3):491–8.
Davidson CD, et al. Efficacy and ototoxicity of different cyclodextrins in niemann-pick C disease. Ann Clin Transl Neurol. 2016;3(5):366–80.
Mori T, et al. Solubilization of ultraviolet absorbers by cyclodextrin and their potential application in cosmetics. J Incl Phenom Macrocycl Chem. 2019;93(1):91–6.
Schneider H-J, et al. NMR studies of cyclodextrins and cyclodextrin complexes. Chem Rev. 1998;98(5):1755–86.
Bekiroglu S, Kenne L, Sandström C. 1H NMR studies of maltose, maltoheptaose, α-, β-, and γ-cyclodextrins, and complexes in aqueous solutions with hydroxy protons as structural probes. J Org Chem. 2003;68(5):1671–8.
Majdecki M, et al. Monosubstituted hydrazone β-cyclodextrin derivatives for pH-sensitive complex formation with aromatic drugs. J Incl Phenom Macrocycl Chem. 2019;93(1):77–83.
Kato K, et al. Synthesis of graft polyrotaxane by simultaneous capping of backbone and grafting from rings of pseudo-polyrotaxane. Beilstein J Org Chem. 2014;10(1):2573–9.
Fan B, et al. Characterization of a supramolecular complex based on octadecylamine and β-cyclodextrin and its corrosion inhibition properties in condensate water. Corros Sci. 2014;83:75–85.
Fan B, et al. Preparation of supramolecular corrosion inhibitor based on hydroxypropyl-β-cyclodextrin/octadecylamine and its anti-corrosion properties in the simulated condensate water. Anti-Corrosion Methods Mater. 2014;61(2):104–11.
Liu Y, et al. β-cyclodextrin modified natural chitosan as a green inhibitor for carbon steel in acid solutions. Ind Eng Chem Res. 2015;54(21):5664–72.
Dehghani A, Bahlakeh G, Ramezanzadeh B. Beta-cyclodextrin-zinc acetylacetonate (β-CD@ZnA) inclusion complex formation as a sustainable/smart nanocarrier of corrosion inhibitors for a water-based siliconized composite film: integrated experimental analysis and fundamental computational electronic/atomic-scale simulation. Compos B Eng. 2020;197:108152.
Dehghani A, et al. Benzimidazole loaded β-cyclodextrin as a novel anti-corrosion system; coupled experimental/computational assessments. J Colloid Interface Sci. 2021;603:716–27.
Haruna K, et al. Cyclodextrin-based functionalized graphene oxide as an effective corrosion inhibitor for carbon steel in acidic environment. Prog Org Coat. 2019;128:157–67.
Park S-M, Lee J-Y, Choi S-J. Growth and characterization of nanosized structures of conducting polymers. Synth Met. 2001;121(1–3):1297–8.
Choi S-J, Park S-M. Electrochemical growth of nanosized conducting polymer wires on gold using molecular templates. Adv Mater. 2000;12(20):1547–9.
Yoshida K-I, et al. Inclusion complex formation of cyclodextrin and polyaniline. Langmuir. 1999;15(4):910–3.
Subramanian E, et al. Influence ofβ-cyclodextrin as an encapsule and as an inclusion complex dopant on conducting polyaniline. Bull Mater Sci. 2005;28(1):55–61.
Aly KI, et al. Novel conducting polymeric nanocomposites embedded with nanoclay: synthesis, photoluminescence, and corrosion protection performance. Polym J. 2019;51(1):77.
Aly KI, Wahdan MH, Hussein MA. New polymer syntheses, part 43: novel polyamides-based diarylidenecyclopentanone: synthesis, characterization, and corrosion inhibition behavior. J Appl Polym Sci. 2009;112(1):513–23.
Aly KI, et al. New polymer syntheses, part 44: synthesis, characterization, and corrosion inhibition behavior of new polyurea derivatives based on diaryl ether in the polymers backbone. J Appl Polym Sci. 2009;112(2):620–8.
Aly KI. New polymer syntheses part: 54 novel conducting polymers and copolymers based on 4-Teriary butyl-cyclohexanone moiety in the main chain. J Appl Polym Sci. 2012;123(6):3390–401.
Aly K, et al. New polymer syntheses part: 55# novel conducting arylidene polymers and copolymers based on methyl-cyclohexanone moiety. J Res Updates Polym Sci. 2014;3(2):97–107.
Aly K, Hussein M. Synthesis, characterization and corrosion inhibitive properties of new thiazole based polyamides containing diarylidenecyclohexanone moiety. Chin J Polym Sci. 2015;33(1):1–13.
Mahross MH, et al. Synthesis, characterization and corrosion inhibition of N′-phenylbenzohydrazide derivative metal complexes: experimental and quantum chemical studies. Z Phys Chem. 2019;233(7):949–72.
Aly KI, et al. Conducting copolymers nanocomposite coatings with aggregation-controlled luminescence and efficient corrosion inhibition properties. Prog Org Coat. 2019;135:525–35.
Shams El Din AM, Paul NJ. Oxide film thickening on some molybdenum-containing stainless steels used in desalination plants. Desalination. 1988;69(3):251–60.
Dehghani A, Bahlakeh G, Ramezanzadeh B. Construction of a sustainable/controlled-release nano-container of non-toxic corrosion inhibitors for the water-based siliconized film: Estimating the host-guest interactions/desorption of inclusion complexes of cerium acetylacetonate (CeA) with beta-cyclodextrin (β-CD) via detailed electronic/atomic-scale computer modeling and experimental methods. J Hazard Mater. 2020;399:123046.
Dewangan Y, et al. N-hydroxypyrazine-2-carboxamide as a new and green corrosion inhibitor for mild steel in acidic medium: experimental, surface morphological and theoretical approach. J Adhes Sci Technol. 2022;36(23–24):2644–64.
Dardeer HM, Toghan A. A novel route for the synthesis of pseudopolyrotaxane containing γ-cyclodextrin based on environmental waste recycling. J Mol Struct. 2021;1227:129707.
Radwan MF, et al. Novel crystalline and thermally stable chitosan-chromone based polymers: synthesis and characterization. J Mol Struct. 2021;1241:130625.
Dardeer HM, Hassan MA. Synthesis of [2] rotaxanes derived from host-gust interaction. Int J Chem. 2015;7(1):161–7.
Dardeer H. Formation of new inclusion complexes depend on cyclodextrin. Chem J. 2015;5(1):14–9.
Dardeer HM. Synthesis, characterization of novel rotaxanes depend on cyclodextrins. J Incl Phenom Macrocycl Chem. 2018;91(1):105–14.
Dardeer HM. Synthesis and characterization of original [2] rotaxanes including cyclodextrin. SN Appl Sci. 2019;1(4):363.
Fomina MV, et al. Structure-property relationships of dibenzylidenecyclohexanones. ACS Omega. 2022;7(12):10087–99.
Rusa CC, et al. Inclusion compound formation with a new columnar cyclodextrin host. Langmuir. 2002;18(25):10016–23.
Harada A, Kamachi M. Complex formation between poly(ethylene glycol) and α-cyclodextrin. Macromolecules. 1990;23(10):2821–3.
Trotta F, Zanetti M, Camino G. Thermal degradation of cyclodextrins. Polym Degrad Stab. 2000;69(3):373–9.
Sedik A, et al. Dardagan fruit extract as eco-friendly corrosion inhibitor for mild steel in 1 M HCl: electrochemical and surface morphological studies. J Taiwan Inst Chem Eng. 2020;107:189–200.
Wang C, Zou C, Cao Y. Electrochemical and isothermal adsorption studies on corrosion inhibition performance of β-cyclodextrin grafted polyacrylamide for X80 steel in oil and gas production. J Mol Struct. 2021;1228:129737.
Shahini MH, Ramezanzadeh M, Ramezanzadeh B. Effective steel alloy surface protection from HCl attacks using nepeta pogonesperma plant stems extract. Colloids Surf A. 2022;634:127990.
Molaeipour P, Ramezanzadeh M, Ramezanzadeh B. Stachys byzantina extract: a green biocompatible molecules source for graphene skeletons generation on the carbon steel for superior corrosion mitigation. Bioelectrochemistry. 2022;143:107970.
Ramezanzadeh M, et al. Corrosion inhibition of mild steel in 1 M HCl solution by ethanolic extract of eco-friendly mangifera indica (mango) leaves: electrochemical, molecular dynamics, monte carlo and ab initio study. Appl Surf Sci. 2019;463:1058–77.
Rbaa M, et al. 8-Hydroxyquinoline based chitosan derived carbohydrate polymer as biodegradable and sustainable acid corrosion inhibitor for mild steel: experimental and computational analyses. Int J Biol Macromol. 2020;155:645–55.
Prabhu R, et al. Synthesis and corrosion resistance properties of novel conjugated polymer-Cu2Cl4L3 composites. Mater Sci Energy Technol. 2021;4:92–9.
Li, W.-h. and Q. He, S.-t. Zhang, C.-l. Pei and B.-r. Hou. Journal of Applied Electrochemistry, 2008. 38(3): p. 289-295
Ansari KR, et al. Corrosion inhibition of N80 steel in 15% HCl by pyrazolone derivatives: electrochemical, surface and quantum chemical studies. RSC Adv. 2016;6(29):24130–41.
Li X-H, et al. Inhibition by tween-85 of the corrosion of cold rolled steel in 1.0 M hydrochloric acid solution. J Appl Electrochem. 2009;39(7):1125–35.
Ramezanzadeh M, et al. Development of metal-organic framework (MOF) decorated graphene oxide nanoplatforms for anti-corrosion epoxy coatings. Carbon. 2020;161:231–51.
Zou C, et al. Cyclodextrin and methacrylic acid octyl phenols poly(ethylene oxide) ester-induced synergistic effect in a novel poly(AM-co-A-β-CD-co-AE) polymer. Starch Stärke. 2012;64(4):281–9.
Zou C, et al. Synthesis of bridged β-cyclodextrin–polyethylene glycol and evaluation of its inhibition performance in oilfield wastewater. Mater Chem Phys. 2014;147(3):521–7.
Fu L, et al. Study on corrosion and scale inhibition mechanism of polyaspartic acid grafted β-cyclodextrin. Mater Lett. 2020;264:127276.
Ma Y, et al. Molecular assembly between weak crosslinking cyclodextrin polymer and trans-cinnamaldehyde for corrosion inhibition towards mild steel in 3.5% NaCl solution: experimental and theoretical studies. Polymers. 2019;11(4):635.
Liu Y, et al. Evaluation of β-cyclodextrin–polyethylene glycol as green scale inhibitors for produced-water in shale gas well. Desalination. 2016;377:28–33.
Tang M, et al. A novel eco-friendly scale and corrosion inhibitor modified by β-cyclodextrin. Aust J Chem. 2017;70(8):933–42.
He Y, Yang Q, Xu Z. A supramolecular polymer containing β-cyclodextrin as corrosion inhibitor for carbon steel in acidic medium. Russ J Appl Chem. 2014;87(12):1936–42.
Acknowledgements
This work was supported by the Academy of Science Research & Technology (ASRT) in Egypt as part of the research Project (RESPECT_1 ID: 10019).
Funding
Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB).
Author information
Authors and Affiliations
Contributions
"HD methodology, investigation, data curation, and writing. MH corrosion application, investigation, data curation, visualization, and writing. KA conceptualization, investigation, data curation, and supervision. MS methodology, investigation, data curation, visualization, writing, and editing. All authors read and approved the final manuscript."
Corresponding authors
Ethics declarations
Ethics approval and consent to participate
Not applicable.
Consent for publication
Not applicable.
Competing interests
The authors declare that they have no Competing Financial or Non-Financial Interests.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/. The Creative Commons Public Domain Dedication waiver (http://creativecommons.org/publicdomain/zero/1.0/) applies to the data made available in this article, unless otherwise stated in a credit line to the data.
About this article
Cite this article
Dardeer, H.M., Abdel-Hakim, M., Aly, K.I. et al. Modification of conducting arylidene copolymers by formation of inclusion complexes: synthesis, characterization, and applications as highly corrosion inhibitors for mild steel. BMC Chemistry 17, 77 (2023). https://doi.org/10.1186/s13065-023-00992-5
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s13065-023-00992-5