Abstract
Background
Among the polyhydroxyalkanoate (PHA), poly[(R)-3-hydroxybutyrate-co-(R)-3-hydroxyhexanoate] [P(3HB-co-3HHx)] is reported to closely resemble polypropylene and low-density polyethylene. Studies have shown that PHA synthase (PhaC) from mangrove soil (PhaCBP-M-CPF4) is an efficient PhaC for P(3HB-co-3HHx) production and N-termini of PhaCs influence its substrate specificity, dimerization, granule morphology, and molecular weights of PHA produced. This study aims to further improve PhaCBP-M-CPF4 through N-terminal truncation.
Results
The N-terminal truncated mutants of PhaCBP-M-CPF4 were constructed based on the information of the predicted secondary and tertiary structures using PSIPRED server and AlphaFold2 program, respectively. The N-terminal truncated PhaCBP-M-CPF4 mutants were evaluated in C. necator mutant PHB−4 based on the cell dry weight, PHA content, 3HHx molar composition, molecular weights, and granule morphology of the PHA granules. The results showed that most transformants harbouring the N-terminal truncated PhaCBP-M-CPF4 showed a reduction in PHA content and cell dry weight except for PhaCBP-M-CPF4 G8. PhaCBP-M-CPF4 G8 and A27 showed an improved weight-average molecular weight (Mw) of PHA produced due to lower expression of the truncated PhaCBP-M-CPF4. Transformants harbouring PhaCBP-M-CPF4 G8, A27, and T74 showed a reduction in the number of granules. PhaCBP-M-CPF4 G8 produced higher Mw PHA in mostly single larger PHA granules with comparable production as the full-length PhaCBP-M-CPF4.
Conclusion
This research showed that N-terminal truncation had effects on PHA accumulation, substrate specificity, Mw, and granule morphology. This study also showed that N-terminal truncation of the amino acids that did not adopt any secondary structure can be an alternative to improve PhaCs for the production of PHA with higher Mw in mostly single larger granules.
Similar content being viewed by others
Background
Polyhydroxyalkanoate (PHA) is one of the bioplastics that are capable of replacing the current commercial petroleum-based plastic in certain applications with the advantage of being biodegradable at the same time [1, 2]. PHAs usually accumulate in the cytoplasm of most bacteria and archaea under the condition where there is an excess amount of carbon and limited nutrients like nitrogen [3]. Among the PHAs, poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) [P(3HB-co-3HHx)] is known to have properties similar to low-density polyethylene (LDPE) and polypropylene (PP) [2]. The properties of the P(3HB-co-3HHx) produced vary depending on the molar composition of the 3HHx [4].
Among the genes involved in PHA biosynthesis, phaC is the most important gene because it encodes for PHA synthase (PhaC), the key enzyme in PHA biosynthesis by polymerizing the monomeric substrates [5]. PhaC determines the properties of the PHA produced as PhaCs can have different substrate specificities toward different monomers. The incorporation of different monomer compositions will affect the properties of the PHA produced [5,6,7,8,9,10]. Additionally, PhaCs play a role in determining the molecular weights of the PHA produced, as different PhaCs accumulate PHAs of different molecular weights. Molecular weights can affect the mechanical properties of the PHA produced [11,12,13,14,15,16]. Generally, it was reviewed that the higher the 3HHx molar composition, the lower the molecular weights of the P(3HB-co-3HHx) produced [4]. However, it was reported that although PhaC from Chromobacterium sp. USM2 (PhaCCs) had lower 3HHx incorporation compared to PhaC isolated from mangrove soil metagenome (PhaCBP-M-CPF4), the molecular weights of the P(3HB-co-3HHx) produced by PhaCCs was very much lower compared to that of PhaCBP-M-CPF4 [16]. This report further highlights the importance of PhaCs in determining the molecular weights of the PHA produced regardless of its monomer composition.
The criterion of an efficient PhaC for the production of P(3HB-co-3HHx) is the ability to incorporate the desired amount of 3HHx molar composition while not compromising the weight-average molecular weight (Mw). Higher Mw PHA with certain amount of 3HHx is desired as it contributes to better physical and mechanical properties like better tensile strength and extension to break [17, 18]. Having the right 3HHx molar composition is also necessary as it can lower the melting temperature of the PHA, lowering the processing temperature. However, there is just a handful of efficient PhaCs for the production of P(3HB-co-3HHx) like PhaCBP-M-CPF4, PhaC from Rhodococcus aetherivorans I24 (PhaCRa), PhaC from Aeromonas hydrophila 4AK4 (PhaCAh), PhaC from Aeromonas sp. LFM897 (PhaCAs), and PhaC from Aeromonas caviae (PhaCAc) have shown promise in this regards [8, 19,20,21,22]. Besides isolating a naturally-evolved PhaC with broad substrate preferences, protein engineering including single and multiple point mutations were employed on PhaCAc for better 3HHx incorporation and production of higher molecular weight copolymers of P(3HB-co-3HHx) [23, 24]. Apart from being able to accumulate P(3HB-co-3HHx) with desired 3HHx molar composition and high molecular weights, accumulating PHAs in single large granules is also desired as it will ease the downstream processes of PHA extraction and purification [25, 26]. Currently, metabolic engineering of PhaPs is the most common way of manipulating the number and size of PHA granules. Previous studies had shown that overexpression of phaPs can lead to the increment in number of smaller PHA granules, and expression of phaPs from various organisms in different hosts may lead to larger PHA granule and affecting the Mw of PHA produced [9, 27].
The structure of a PhaC can be divided into 2 parts: the N-terminal and the C-terminal domains. Early researches suggested that based on the multiple sequence alignment of well-reported PhaCs, the N-terminal region of a PhaC is approximately the first 100 amino acids as they are highly variable and flexible [5, 6]. Furthermore, the N-terminal region is also highly flexible as it hinders the crystallization process of protein crystals [6]. However, the crystal structure of PhaCs from Cupriavidus necator H16 (PhaCCn) and PhaCCs later suggested that the N-terminal of PhaCs may vary between different PhaCs. The N-terminal of PhaCCn and PhaCCs were suggested to be the first 200 and 174 amino acids respectively, as the PhaCs were able to crystalize and remain stable without them [28]. On the other hand, the C-terminal of PhaCs was reported to consist of the cap subdomain, substrate entrance channel, and product egress channel [6, 29,30,31,32]
To date, there are reports regarding the N-terminal of a PhaC affecting the substrate specificity and molecular weights of the PHA produced [33, 34]. Studies on chimeric PhaC of PhaCCn with various N-terminal lengths of PhaC from Pseudomonas aeruginosa (PhaCPa) were performed. As a result, chimeric PhaC of PhaCCn and PhaCPa was observed to incorporate 3HHx whereas the wild-type PhaCCn do not [35]. In addition, Lim and co-workers reported that the N-terminal of PhaC was needed for the dimer formation of PhaCs [36]. Despite decades of advancements in PhaC research, the exact functional roles of N-terminal domain of PhaC remain elusive. In this study, the N-terminal of PhaCBP-M-CPF4 will be truncated according to its predicted secondary and tertiary structure and evaluated based on its incorporation of 3HHx monomer, the molecular weights of the PHA produced, and granule morphology for a better PhaC in the production of P(3HB-co-3HHx) copolymer. Gene expression study was performed to study how N-terminal region truncation affects the molecular weights of P(3HB-co-3HHx) produced.
Methods
Bacterial strain, plasmid, and PHA biosynthesis condition
In this study, the PHA-negative mutant strain of C. necator, PHB−4 was used as the host strain for the evaluation of the N-terminal truncated PhaCBP-M-CPF4. The N-terminal truncated phaCBP-M-CPF4 mutants (G8; 8–551, A27; 27–551, T74; 74–551, and D104; 104–551) were inserted into previously modified pBBR1MCS-2 plasmid which harbours the phaC1 promoter from C. necator (Table 1) [8]. The C. necator transformants were first pre-cultured in nutrient-rich (NR) media until OD600nm reaches 4–4.5 before transferring 3% (v/v) of the preculture into 50 mL mineral medium (MM) [11, 20]. The carbon sources used in this study were 1% (v/v) of crude palm kernel oil (CPKO) or 2% (w/v) of fructose supplemented by 0.054% (w/v) of urea as the nitrogen source. Kanamycin was added during the cultivation of C. necator transformants to the final concentration of 50 µg/mL. The cultures were then shaken at 200 rpm, 30 °C for 48 h. After 48 h, the cultures were harvested. The harvested cells were then lyophilized before use for further analysis [37].
PHA synthase structure prediction
The amino acid sequence of PhaCBP-M-CPF4 (accession no. AXB72506.1) was first obtained from National Center for Biotechnology Information (NCBI) (https://www.ncbi.nlm.nih.gov/protein/1423452970). The tertiary structure and secondary structure of amino acid sequence obtained was then predicted using AlphaFold2 program (https://www.ebi.ac.uk/Tools/sss/fasta/) and PSIPRED server (http://bioinf.cs.ucl.ac.uk/psipred/), respectively.
Construction of C. necator PHB−4 mutant harbouring N-terminal truncated PhaCBP-M-CPF4
The full nucleotide sequence of PhaCBP-M-CPF4 (accession no. MF431721.1) from a plasmid in a previous study (pBBR1-CBP-M-CPF4) was used as the template for polymerase chain reaction (PCR) to amplify the N-terminal truncated mutants (G8, A27, T74, and D104) using Q5® High-Fidelity 2 × Master Mix (New England Biolabs Inc., USA). The primers designed for the amplification of the N-terminal truncated PhaCBP-M-CPF4 mutants were listed in Table 2. For all the N-terminal truncated mutants, sequence of “ATG” was added in the starting of the sequence as the start codon which codes for methionine. The PCR products of the N-terminal truncated PhaCBP-M-CPF4 mutants were then digested using FastDigest HindIII and ApaI restriction enzymes (Thermo Scientific, USA). The vector of this study, pBBR1-ProCn was also digested with similar restriction enzymes. The expression of phaCBP-M-CPF4 with its N-terminal region truncated mutants were controlled by the native phaC1 promoter of C. necator [8]. The PCR products were ligated with the digested pBBR1-ProCn using DNA Ligation Kit Ver.2.1 (Takara Bio Inc., Japan) according to the manufacturer’s protocol, and the resultant plasmids were transformed into C. necator PHB−4 via transconjugation with Escherichia coli S17-1 [40].
Analysis of the PHA produced by C. necator PHB−4
The PHA content and molar composition of the PHA produced by the C. necator PHB−4 transformants harbouring full-length PhaCBP-M-CPF4 and its N-terminal truncated mutants were determined using gas chromatography (GC) [41]. The GC was first calibrated using chloroform extracted homopolymer of P(3HB) and copolymer of P(3HB-co-11 mol% 3HHx). A total of 15 to 20 mg of lyophilized cells were weighed and subjected to methanolysis by heating them to 100 °C for 140 min in the methanolysis solution containing 15% (v/v) sulfuric acid and 85% (v/v) methanol. Caprylic acid methyl ester (CME) was used as an internal standard to calculate the PHA content in the lyophilized cells. The PHA produced were analyzed using SHIMADZU GC-2010 Plus (Shimadzu, Japan) equipped with AOC-20i Auto-injector (Shimadzu, Japan), Rtx-1 GC column (Restek, USA) and flame ionization detector with nitrogen gas as carrier gas. The injector and detector temperatures were set to 270 °C and 280 °C respectively. The column temperature was initially set at 70 °C but gradually increased to 280 °C at a rate of 10 °C/min.
The PHA accumulated in the lyophilized cells was extracted using the solvent extraction method. The lyophilized cells were weighed, and chloroform was added to a ratio of 1 g lyophilized cells: 100 mL chloroform. The mixture was stirred for 72 h at room temperature. The mixture was then filtered using filter paper to remove the cell debris and the chloroform-dissolved PHA was precipitated using chilled methanol. The weight-average molecular weight (Mw), number-average molecular weight (Mn), and polydispersity index (PDI) of the PHA accumulated were determined through gel permeation chromatography (GPC) analysis. About 1 mg of PHA was dissolved in 1 mL of HPLC-grade chloroform and injected into the Agilent Technology 1200 Series High-Performance Liquid Chromatography (HPLC) system (Agilent, USA) equipped with a refractive index detector. The columns were TSK guard column HHR-H and TSKgel GMH HR-H (Tosoh, Japan). The flow rate was set to 0.8 mL/min and the column temperature was maintained at 40 °C [42].
Total RNA extraction and quantitative PCR (qPCR)
The effect of N-terminal truncation on the PhaC expression was also analyzed using qPCR analysis. The C. necator PHB−4 harbouring the full-length of PhaCBP-M-CPF4, and its N-terminal truncated mutants were cultured in PHA biosynthesis condition as described in previously using 2% (w/v) of fructose and 0.054% (w/v) of urea as the nitrogen source. Unlike previously, the bacterial cells were harvested at 24 h [43]. The bacterial cells were washed and resuspended in 10 mL of sterilized deionized water. About 1 mL of the suspension was centrifuged to obtain its pellet. The pellet was then resuspended in 200 µL of enzymatic lysis buffer containing 20 mg/mL of lysozyme dissolved in a mixture of 20 mM Tris–Cl (pH 8.0), 2 mM sodium EDTA, and 1.2% Triton® X-100. The suspension was incubated for 1 h at 37 °C. After that, 25 µL of Proteinase K (Thermo Scientific, USA) was added and mixed by pipetting. The mixture was incubated at 56 °C for 30 min. The total RNA was separated from other cellular components using TRI REAGENT®-RNA/DNA/PROTEIN ISOLATION REAGENT and done according to the manufacturer’s protocol and further purified using RNeasy® Mini Kit according to the modified manufacturer’s protocol. The total RNA concentration was determined using BioSpectrometer® (Eppendorf, Germany) equipped with Eppendorf µCuvette G1.0 (Eppendorf, Germany). The total RNA extracted was stored at − 80 °C before use.
A total of 1000 ng of the extracted total RNA was converted to cDNA using QuantiNova™ Reverse Transcription Kit (Qiagen, Germany) according to the manufacturer’s protocol. Primer efficiency and qPCR analysis were done with QuantiNova™ SYBR Green PCR Kit (Qiagen, Germany) using CFX96™ Real-Time System (Biorad, USA) according to the manufacturer’s protocol before determining the expression of phaCBP-M-CPF4, and its N-terminal truncated mutants. The primers used for qPCR analysis were listed in Table 2. The condition of the qPCR was optimized until primer efficiency values were in the range of 90 to 110%. A total of 75 ng of cDNA was mixed with 0.7 µL of 10 µM of forward and reverse primers, 5 µL of SYBR Green PCR Master Mix, and RNase-free water was added until the total volume of 10 µL. The PCR reaction was done at 95 °C for 5 min as the initial activation step, followed by 40 cycles of denaturation of the cDNA at 95 °C for 10 s, annealing, and extension at 60 °C for 30 s. The data obtained from the qPCR were analysed using the relative quantification method where it was expressed as fold change between the phaCBP-M-CPF4 (control) and its N-terminal truncated mutants. 16S rRNA was used as an internal control. The cycle threshold (Ct) was obtained, and the relative comparison of the truncated mutants to the full-length phaCBP-M-CPF4 was analysed using the 2−ΔΔCt formula [44, 45].
mRNA secondary structure prediction
The mRNA secondary structure of the transcribed phaCBP-M-CPF4 was also determined. First, the transcription start site in the C. necator promoter from the pBBR1-ProCn was predicted using SAPPHIRE online software (https://sapphire.biw.kuleuven.be/index.php) [46]. The nucleotide sequence starting from transcription start site until the end of full-length phaCBP-M-CPF4 was converted to mRNA sequence using DNA to mRNA to Protein Converter (https://skaminsky115.github.io/nac/DNA-mRNA-Protein_Converter.html). The mRNA sequence obtained was input into RNAfold online software (http://rna.tbi.univie.ac.at/cgi-bin/RNAWebSuite/RNAfold.cgi) for predicting its secondary structure [47].
Determination of the number and diameter of granules in each bacterial cell
The change in the granule morphology of the C. necator PHB−4 transformants harbouring the full-length of PhaCBP-M-CPF4 and its N-terminal truncated mutants was also determined using transmission electron microscopy (TEM). The C. necator PHB−4 harbouring the full-length of PhaCBP-M-CPF4, G8, A27, and T74 were cultured in PHA biosynthesis condition as described previously using 2% (w/v) of fructose supplemented by 0.054% (w/v) of urea as nitrogen source and were harvested as described previously. The harvested bacterial cells were fixed with McDowell-Trump fixatives at 4 °C for at least 24 h [48]. The fixed bacterial cells were treated with 1% osmium tetroxide (OsO4) for 1 h at room temperature, followed by dehydration gradually using ethanol concentrations starting from 50%, 75%, 95%, and 100%, respectively, and finally into 100% acetone. The dehydrated bacterial cells were embedded in low-viscosity Spurr’s resin and cured at 60 °C for at least 48 h [49]. Ultrathin sections were prepared using ultramicrotome and mounted on a copper grid followed by staining using uranyl acetate and lead citrate. The samples were then viewed under Philip CM 12/STEM and JLM-2000FX11. The number of granules in each of the mutants were counted and analyzed. A pie chart showing the percentage of bacteria cells with their respective number of PHA granules per bacterial cell was plotted and the diameter of the respective PHA granules were determined based on the TEM images obtained for C. necator PHB−4 harbouring the full-length of PhaCBP-M-CPF4, G8, A27, and T74.
Phase contrast microscopy analysis
Phase contrast microscopy was used to determine the live condition of the cultured C. necator PHB−4 transformants harbouring the full-length of PhaCBP-M-CPF4 and its N-terminal truncated mutants. The transformants were cultured in PHA biosynthesis condition as described previously. About 1 mL of the bacterial culture was collected. A drop of the culture was dropped and spread gently onto a clean glass slide followed by being gently covered with a clean cover slip. The bacteria were observed using an Olympus System Microscope Model BX41 phase contrast light microscope (Olympus, Japan). Observation of the bacterial sample was done using the objective lens with the lowest magnification (10×) to the highest magnification (100×). The PHA accumulated in the bacterial cells will be seen as transparent white granules under phase contrast microscopy.
Statistical analysis
All the data obtained were noted as mean ± standard deviation. All the statistical analyses were performed using SPSS software (IBM SPSS Statistics 24). The statistical data obtained were compared using one-way analysis of variance (ANOVA) with Tukey post hoc comparison with p values < 0.05 considered as statistically significant.
Results
Generation of C. necator PHB−4 harbouring the N-terminal truncated PhaCBP-M-CPF4
To generate N-terminal truncated PhaCBP-M-CPF4, predicted tertiary and secondary structures of PhaCBP-M-CPF4 were employed and referred to design the truncation points. The tertiary N-terminal structure of PhaCBP-M-CPF4 was predicted using Alphafold2 program (Additional file 1: Fig. S1A). Due to the low pLDDT score on the first 13 amino acid residues of the predicted tertiary structure from Alphafold2 program, secondary structure from PSIPRED server was referred for the truncation point (Additional file 1: Fig. S1B). Based on the two predicted structures, a predicted secondary N-terminal structure of PhaCBP-M-CPF4 with combination of AlphaFold2 program and PSIPRED server was done (Additional file 1: Fig. S1C). Figure 1 illustrates the simplified diagram of the full-length PhaCBP-M-CPF4 and its N-terminal truncated mutants. As a result, the first seven amino acids were truncated since they did not adapt to any secondary helix structure, and it was designated as PhaCBP-M-CPF4 G8 (comprised of residues 8–551). In the second mutant, PhaCBP-M-CPF4 A27 (comprised of residues 27–551), the first 26 amino acid residues were truncated as it was extended from the adjacent pairing α2 helix based on the Alphafold2 structure (Additional file 1: Fig. S1A). In addition, secondary structure prediction from PSIPRED server (Additional file 1: Fig. S1B) indicated the α1-helix was separated into 2 distinct α-helices with a small gap at A27. Hence, A27 could be a good position for truncation to avoid structural disruption of the α1-helix. The third truncated mutant, PhaCBP-M-CPF4 T74 (comprised of residues 74–551), the N-terminal truncated mutant started from α2-helix where the first 73 amino acid residues comprised of α1-helix (Additional file 1: Fig. S1C). In the fourth N-terminal truncated mutant PhaCBP-M-CPF4 D104 (comprised of residues 104–551), the first 103 amino acids residues were truncated, which consist of α1, and α2-helices were truncated. In summary, this study evaluates the performances of the N-terminal truncated PhaCBP-M-CPF4 mutants on PHA production, PHA polymer’s properties, and PHA granule morphology.
Production and molecular weights of P(3HB) and P(3HB-co-3HHx) by full-length PhaCBP-M-CPF4 and its N-terminal truncated mutants
Table 3 showed the PHA production of the full-length PhaCBP-M-CPF4 and its N-terminal truncated mutant PhaCs using C. necator PHB−4 as bacterial host. A total of 20 g/L of fructose or 10 g/L of crude palm kernel oil (CPKO) were used as the carbon source to produce P(3HB) and P(3HB-co-3HHx), respectively. There was no significant difference in the cell dry weight (CDW) of C. necator PHB−4 transformants expressing full-length PhaCBP-M-CPF4 and G8 when fructose was used as carbon source, which were 8.3 and 8.4 g/L respectively. A similar trend was observed when CPKO was used as the carbon source which was 11.3 and 10.2 g/L respectively. There were also no significant differences in the PHA content accumulated by C. necator PHB−4 harbouring full-length PhaCBP-M-CPF4 and G8 regardless of the carbon sources used. However, as more N-terminal regions were truncated in PhaCBP-M-CPF4 A27, T74 and D104, there was a significant reduction from 4.6 to 1.8 g/L and 56.5 to 0.5 wt% in the CDW and PHA content of the C. necator PHB−4 transformants when fructose was used as carbon source. Similarly, when CPKO was used as carbon source, there was a decrease from 7.5 to 1.8 g/L and 59.7 to 10.3 wt% in CDW and PHA content from PhaCBP-M-CPF4 A27 to D104 respectively. As for the residual biomass, there were no significant differences for C. necator PHB−4 harbouring the full-length PhaCBP-M-CPF4, G8, A27, and D104 ranging between 1.8 and 2.0 g/L when fructose was used as the carbon source. When CPKO was used as the carbon source, there were no significant differences between C. necator PHB−4 harbouring the full-length PhaCBP-M-CPF4, G8, and A27, ranging between 2.5 and 3.0 g/L. The residual biomass accumulated by C. necator PHB−4 harbouring PhaCBP-M-CPF4 T74 and D104 ranged between 1.6 and 1.7 g/L when CPKO was used as carbon source. When the bacteria cells were fed with CPKO, there was a gradual decrease in the 3HHx molar composition of the P(3HB-co-3HHx) produced from 6 to 1 mol% as more N-terminal region of the PhaC was truncated.
As for the molecular weights, there was an increase in the Mw of both P(3HB) and P(3HB-co-3HHx) produced by the truncated PhaCBP-M-CPF4 G8 and A27 compared to the full-length PhaCBP-M-CPF4 (Table 3). The Mw of the PHA produced by PhaCBP-M-CPF4 G8 and A27 were 26.1 and 26.9 × 105 Da for P(3HB), and 11.2 and 14.1 × 105 Da for P(3HB-co-3HHx), respectively. For P(3HB), the Mn of the homopolymer produced ranged from 6.7 to 11.2 × 105 with the PDI ranged from 2.3 to 2.7. For P(3HB-co-3HHx), the Mn ranged from 3.7 to 5.7 × 105 while the PDI ranged from 2.0 to 2.5. The Mn, Mw, and PDI for both P(3HB) and P(3HB-co-3HHx) produced by PhaCBP-M-CPF4 D104 was not determined as the PHA accumulated was too low to be extracted for the analysis.
Gene expression of N-terminal truncated PhaCBP-M-CPF4
Primer efficiency and melt curve analysis were performed to validate the primers designed for this study (Additional file 1: Fig. S2 and 3). Based on Fig. 2, there was a clear decrease in the gene expression level of the all the N-terminal truncated phaCBP-M-CPF4 mutants compared to its full-length. Compared to the full-length phaCBP-M-CPF4, there was a drop in gene expression level of more than 80% in all the N-terminal truncated PhaCBP-M-CPF4 mutants. Gene expression level of phaCBP-M-CPF4 G8 was the highest among all the N-terminal truncated phaCBP-M-CPF4 with about 0.17. The gene expression level of phaCBP-M-CPF4 A27 and D104 were low but comparable to each other ranging from 0.0124 to 0.0162 while phaCBP-M-CPF4 T74 was the lowest with just 0.0010. These results showed that truncation of the N-terminal region of phaCBP-M-CPF4 had effects on the gene expression or concentration of its corresponding mRNA. Based on the trends in Fig. 2, it can be suggested that the more N-terminal regions were truncated, the lower the expression of the N-terminal truncated phaCBP-M-CPF4 was. The decrease in the detectable mRNA concentration may also be due to its mRNA stability. In this study, the same promoter and RBS were used for the expression of full-length phaCBP-M-CPF4 and its N-terminal truncated mutants. This showed that the missing truncated N-terminal region might be necessary for better expression and/or mRNA stability of the phaCBP-M-CPF4 gene.
Altered morphology of the PHA granules accumulated in the C. necator PHB−4 transformants
The P(3HB) granule morphology produced by the C. necator PHB−4 harbouring full-length PhaCBP-M-CPF4 and its N-terminal truncated mutants were examined using TEM. Figure 3 showed that the N-terminal of PhaCBP-M-CPF4 truncation resulted in a lesser number of PHA granules accumulated by the C. necator PHB−4 transformants. Based on pie charts shown in Fig. 3, there was an increase in the percentage of bacteria having single granules from full-length PhaCBP-M-CPF4 to G8. There was also a decrease in the percentage of bacterial cells having at least two PHA granules as more N-terminal regions of the PhaCBP-M-CPF4 were truncated from full-length PhaCBP-M-CPF4 to T74. This observation showed that there was clear evidence where the N-terminal truncation of PhaCBP-M-CPF4 affected the number of PHA granules accumulated in the bacterial mutants.
P(3HB) granule morphology of C. necator PHB−4 harbouring full-length of PhaCBP-M-CPF4 and its truncated mutants. TEM was used to view C. necator PHB−4 harbouring full-length of PhaCBP-M-CPF4, Magnification: 4000× (A), G8, Magnification: 3200× (B), A27, Magnification: 4000× (C), and T74, Magnification: 4000× (D). The pie charts representing the percentage of bacteria cell with their respective number of granules per bacterial cell were plotted. The total mean diameter of all the PHA granules were shown in the upper-right corner of TEM images. The oozing phenomenon is indicated using black circles. The TEM images shown represent the number of granules in each bacteria harbouring the full-length of PhaCBP-M-CPF4 and its truncated mutants
Besides having lesser PHA granules, based on Fig. 3, there were also an increased in the granule mean diameter of the PHA granules of from C. necator PHB−4 transformants harbouring full-length PhaCBP-M-CPF4 to A27 but decreased for C. necator PHB−4 transformants harbouring full-length PhaCBP-M-CPF4 T74. The granule mean diameter of the PHA granules increased from 0.78 (full-length PhaCBP-M-CPF4) to 1.10 µm (PhaCBP-M-CPF4 A27) but decreased to 0.93 µm (PhaCBP-M-CPF4 T74). This hinted that not only did the N-terminal region affect the number of granules formed but also the size of the PHA granules.
On the other hand, there was also an increase in the percentage of bacterial cells without any PHA accumulated as more N-terminal regions were truncated. Based on the pie chart in Fig. 3, the percentage of bacteria having no PHA granules increased from full-length PhaCBP-M-CPF4 to T74. In Fig. 3C, and D, the percentage of bacteria having no granule were even higher than the percentage of bacteria who had at least one PHA granules. The observation indicated that the N-terminal region of PhaCBP-M-CPF4 was also necessary for the production and accumulation of PHA in the bacteria. This speculation was demonstrated when 59% of C. necator PHB−4 transformants harbouring PhaCBP-M-CPF4 A27 showed no PHA accumulation, and the percentage further hiked to 89% in C. necator PHB−4 mutant harbouring PhaCBP-M-CPF4 T74.
Another interesting morphology observed from the TEM images was the fluidic nature of the PHA granules in the bacterial cells. In Fig. 3B, some of the PHA material was flowing out of or oozing from several granules (circled in black). The fluidic PHA material was not only seen flowing out of the granules but also appeared to be flowing/oozing out of the bacterial cells. Such behavior was not observed in any other samples examined in this study.
Discussion
It is preferable to have a PhaC that can synthesize P(3HB-co-3HHx) with desired 3HHx molar composition and have high Mw in a single large PHA granule. This study successfully engineered PhaC with the desired properties by truncating the N-terminal region of PhaCBP-M-CPF4. In a previous study by Lim and co-workers, N-terminal truncation of PhaC from Aquitalea pelogenes USM4 (PhaCAp) resulted in a significant decrease in the number of PHA granules as well [36, 50]. This observation provided an impetus to this study whereby a more versatile PhaC discovered from mangrove soil metagenome was subjected to further improvement.
Table 3 showed that as more α-helices were truncated in PhaCBP-M-CPF4 A27, T74 and D104 mutants, there were greater reduction in PHA content of the bacterial cells. Generally, PhaCs were reported to exist in a monomer–dimer equilibrium, with monomeric form regarded as the inactive form, and dimeric form is regarded as the active form of PhaC [51, 52]. Extensive truncation of the N-terminal region of PhaC may interfere with the dimer formation, resulting in reduced or diminished enzymatic activity of the truncated PhaCs [36]. However, truncation of the first seven amino acids in the N-terminal of PhaCBP-M-CPF4 G8 did not affect the amount of PHA accumulated. There was no significant difference in the PHA accumulated by full-length PhaCBP-M-CPF4 and G8 although N-terminal truncated PhaCs generally tend to exhibit lower in vitro activities [36, 53]. The in vivo PHA accumulation experiments extended over 48 h, which is a significantly longer duration than the 10–30 min timeframe typically for in vitro enzyme assays. As a result, the reduced activities of PhaCBP-M-CPF4 G8 were compensated by the extended accumulation duration in the in vivo experiments using C. necator PHB−4 transformant.
The 3HHx molar composition of P(3HB-co-3HHx) reduced from 6 to 1 mol% as more N-terminal regions were truncated, suggesting that the loss of N-terminal region gradually lost its substrate specificity towards 3HHx. This showed that the N-terminal region of the PhaC played an important role in determining the substrate specificity of the PhaC as reported previously. For instance, originally PhaCCn cannot incorporate any medium-chain-length-PHA (MCL-PHA) monomers into its PHA produced. On the contrary, chimeric PhaCs of PhaCCn with N-terminal region of PhaCAc and PhaCPa were reported able to incorporate MCL-PHA monomers such as 3HHx, 3-hydroxyoctanoate (3HO), and 3-hydroxydecanoate (3HD) [35, 54]. Lim and co-workers also reported similar results as N-terminal truncated PhaCAp too incorporated lesser 3HHx monomers into its PHA [36]. These observations hinted that the N-terminal of PhaCs can affect the PHA monomers incorporated in PHA.
Besides that, there was also an increase in the Mw of the P(3HB-co-3HHx) accumulated by the N-terminal truncated PhaCBP-M-CPF4 G8 and A27 compared to the full-length PhaCBP-M-CPF4 (Table 3). Previous studies had shown that the 3HHx molar composition in P(3HB-co-3HHx) can affects the Mw of the P(3HB-co-3HHx) produced [2, 4]. An increase in 3HHx molar composition will decrease the Mw of the P(3HB-co-3HHx) produced because the 3HHx monomer is a bulky monomer and the increased in the composition of 3HHx will decrease the Mw which was in agreement with the result obtained in this study [2, 55]. To confirm the finding that N-terminal truncation on PhaCs can increase the Mw of the PHA produced as observed, the Mw of P(3HB) homopolymer produced from full-length PhaCBP-M-CPF4 and its N-terminal truncated mutants were compared as there was no longer the effect of 3HHx molar composition on the Mw of the PHA produced. As a result, there was also an increase in the Mw of P(3HB) produced by the N-terminal truncated PhaCBP-M-CPF4 G8 and A27 compared to the full-length PhaCBP-M-CPF4 which further supported the finding that N-terminal truncation of PhaC can increase the Mw of PHA produced. In addition, the Mw of the PHA produced from fructose was higher compared to that from CPKO. One reason for the lower Mw of PHA produced by CPKO was probably the presence of glycerol in the culture medium. Glycerol and fatty acids are produced when CPKO is hydrolyzed by lipase. The resulting free fatty acids are used as carbon source by the bacterium for growth and PHA biosynthesis. However, glycerol is poorly used by C. necator and had been reported to act as a PHA chain transfer agent which leads to early chain termination of the PHA polymerization, resulting in lower Mw of PHA produced from CPKO compared to fructose [56].
To determine how N-terminal truncation on PhaCs can increase the Mw of the PHA produced, gene expression of the full-length PhaCBP-M-CPF4 and its N-terminal truncated mutants were verified using qPCR analysis. There were reports on the concentration or the expression of PhaCs affecting the Mw of the PHA produced [5, 15, 57]. Based on Fig. 2, there was a drop of more than 80% in the gene expression level of the N-terminal truncated PhaCBP-M-CPF4 G8 compared to the full-length of PhaCBP-M-CPF4 and followed by similarly low expression of PhaCBP-M-CPF4 A27, T74, and D104. Lower expression of the N-terminal truncated PhaC will lead to the reduction in the concentration of PhaCs available for polymerizing the PHA monomers into the PHA polymer chains [15, 57]. The decrease in concentration of available PhaCs will increase the ratio of PHA monomers to the concentration of PhaCs in the bacterial cells. The increase in the ratio of PHA monomers to the concentration of PhaCs in the bacterial cells will allow more PHA monomers to be shared among the lower concentration of PhaCs polymerizing the PHA monomers into even longer PHA polymer chains and leading to a higher Mw of the PHA produced.
In contrast, for PhaCBP-M-CPF4 T74, there was a drop in the Mw of the PHA produced despite having even lower expression. This might be due to the cumulative effect of lower activity and the unstable dimeric structure of PhaCBP-M-CPF4 T74. This was also in agreement with the low PHA content accumulated in C. necator PHB−4 harbouring PhaCBP-M-CPF4 T74 in Table 3. The truncated first 73 amino acids might have amino acid residues or segments of amino acids important for the dimerization of the PhaC [36].
The decrease in gene expression level might be due to the instability of the respective mRNAs in the bacterial cells. Based on the qPCR analysis, the N-terminal regions of the full-length phaCBP-M-CPF4 seem to provide shielding effect towards mRNA degradation. Figure 4 showed the predicted secondary transcribed mRNA structure of phaCBP-M-CPF4 starting from the predicted transcription start site. In the predicted secondary mRNA structure, there were numerous stem-loops formed by the nucleotides in the N-terminal regions indicating the participation of the N-terminal region in the formation of stem-loop structures. The stem-loop structures of the mRNA secondary structure was suggested to have the ability to stabilize the mRNA and hence, shielding the mRNA from the mRNA degradation pathways [58]. Based on Fig. 4, the nucleotides that coded for the first seven amino acids of the N-terminal formed were paired with nucleotide 801 to 809 as indicated by cyan oval. Besides that, the nucleotide truncated too formed a stem-loop structure among themselves as indicated with blue oval. Adjacent to the stem-loop structure, there were A/U rich regions which were very susceptible to mRNA degradation by RNase E [59]. The loss of the stem-loop structures probably made the A/U rich region more susceptible to mRNA degradation, leading to a major drop of more than 80% in the gene expression level. For PhaCBP-M-CPF4 A27, truncation of first 26 amino acids of the N-terminal removed nucleotides pairing with nucleotide 746 to 809 as indicated with red oval which further compromising the stability of the mRNA leading to even lower gene expression level. For PhaCBP-M-CPF4 T74 and D104, truncation points at their respective positions too compromised the ability of the mRNA to form stem-loop structures leading to very low gene expression level. Based on the predicted secondary mRNA structure, it was observed that stem-loop structures indicated in cyan, blue, and red oval played a major role in stability of the mRNA as the loss of both stem-loops heavily affected the mRNA stability as observed PhaCBP-M-CPF4 A27, T74 and D104. However, further studies are necessary to further confirm this observation.
Predicted secondary structure of transcribed mRNA for full-length phaCBP-M-CPF4. The predicted secondary structure of transcribed mRNA starts from the predicted transcription start site. The start codon was indicated using blue square. The cyan and blue oval indicated stem-loop structures formed by nucleotides which encoded for the first seven amino acids while the red oval indicated the stem-loops structures formed by the nucleotide encoded for the first 26 amino acids residues. Points of truncation for G8, A27, T74, and D104 were indicated using green, orange, brown, and purple arrows respectively
One interesting observation was that despite the 5’-untranslated region (UTR) forming many stem-loops structures as observed in Fig. 4, it did not provide sufficient shielding effect from the mRNA degradation pathways. One mRNA degradation pathway which was well-known to play a significant role in mRNA degradation in E. coli was the 5’-end-dependent mRNA degradation pathway where the degradation of the mRNA was initiated from the 5’ regions of the mRNA [60]. Previously it was reported that 5’ UTR played major role in determining the stability of mRNA in bacteria cells by shielding the mRNAs from mRNA degradation catalyzed by RNA pyrophosphohydrolase followed by RNase E or RNase J [61,62,63]. However, this was not observed in our case because the promoter and 5’ UTR of the full-length PhaCBP-M-CPF4 and all its N-terminal truncated mutants were the same and there should not be any differences in the gene expression level between the PhaCs. But based on Fig. 2, there were significant drops in the gene expression level for all N-terminal truncated mutants although they had similar promoter, 5’ UTR sequences and the only difference were the missing N-terminal regions. This hinted that the stem-loop structures formed by the missing nucleotide which code for the N-terminal of coding region might play a significant role as well in its respective mRNA stability.
On the bright side, the decrease in expression did not affect the amount of PHA accumulated in the bacterial cells for PhaCBP-M-CPF4 G8 as shown in Table 3. Initially, we hypothesized that lower expression of phaCs will lead to a lower amount of PHA accumulated in the bacterial cells but that was not the case for PhaCBP-M-CPF4 G8. This also showed that for the bacteria to accumulate a high amount of PHA, overexpression of phaCs was not necessary as it might lead to a lower Mw of the PHA produced [5]. To the best of our knowledge, to date, there are no existing reports on the modification of the N-terminal of PhaC or DNA sequence of the PhaC on the expression of the phaCs during PHA production.
The increase in Mw of the PHA produced by N-terminal modified PhaCs was also previously reported by Ye and co-workers where it was reported that deletion of 2 to 65 amino acids in the N-terminal of PhaC from P. stutzeri 1317 increased the Mw of the PHA produced because the α-helices in the N-terminal was predicted to be involved in PHA chain elongation as the PHA chain elongation and termination were easily affected by the changes in the configurational and hydrophilicity of the N-terminal region of PhaCs [33]. The increase in Mw was also reported to be associated with the changes in the secondary structure of the PhaC and the protein-to-protein interactions. Similar results were also reported by Zheng and co-workers where mutation on the N-terminal affected the interaction between PhaC-to-PhaC and other PHA-related proteins which lead to the increase in Mw of the PHA accumulated [34]. Kim and co-workers also reported that the deletion of a region at the N-terminal of PhaCs affected the ability of the N-terminal to fold at a proper orientation which could result in the activity of PhaC [53].
Another criterion of a good PhaC for production P(3HB-co-3HHx) is the ability to accumulate single large PHA granules as it will make the PHA extraction and purification process easier by using non-solvent PHA extraction methods like centrifugation, filtration, or sedimentation [25, 26]. These non-solvent PHA extraction methods were more straightforward and safer compared to solvent PHA extraction as they were non-toxic and non-flammable.
Based on Fig. 3, there were more single larger PHA granules formed for N-terminal truncated PhaCBP-M-CPF4 G8 and A27 compared to full-length PhaCBP-M-CPF4. This may be due to the interaction of the full-length PhaCBP-M-CPF4 and its N-terminal truncated mutants with other PHA-related proteins like PhaP which is known to be present on the surface of PHA granules and also reported to affect the number and size of PHA granules [9, 26, 64,65,66]. To date, the most common strategy for the formation of a single granule in the bacterial cell is by deletion of phaPs [26, 65, 66]. Previously, a similar observation was obtained through N-and C-terminal truncation of PhaCAp [36, 50]. But the stark difference in the PHA granule morphology was that even the full-length PhaCBP-M-CPF4 accumulated lesser PHA granules compared to the full-length PhaCAp. To date, there was still no knowledge regarding the origin of this PhaCBP-M-CPF4 which was isolated from mangrove soil metagenome, unlike PhaCAp where we know that it comes from A. pelogenes USM4 [8, 50].
Figure 3 also showed that besides accumulating lesser but larger PHA granules, another clear observation was the decrease in the percentage of PHA-containing bacterial cells. As more N-terminal regions of the full-length PhaCBP-M-CPF4 were truncated, there were more non-PHA-containing bacteria cells. In Fig. 3A, even with full-length PhaCBP-M-CPF4, there were a few bacteria cells in which no PHA granules were observed, but that could be due to the angle of the slide sectioned during ultramicrotome. In Fig. 3C and D, a significant increase in the percentage of bacterial cells without any PHA granules were observed from a cross-section of the bacterial cells. These observations were further confirmed using phase contrast microscopy as shown in Fig. 5. In Fig. 5A and B, the phase contrast images of C. necator PHB−4 harbouring full-length PhaCBP-M-CPF4 and G8 did not show any non-PHA-containing bacteria cells. This showed that the non-PHA-containing cells observed in Fig. 3A and B could be due to the sectioning of the part of the bacteria which did not contain PHA. On the other hand, based on Fig. 5C and D, there was an obvious decrease in the number of PHA-containing bacterial cells from C. necator PHB−4 harbouring PhaCBP-M-CPF4 A27 and T74. These observations were also in agreement with the TEM images observed in Fig. 3C and D where there were increment in the number of non-PHA-containing cells. These observations also agreed with the gene expression level data whereby there were very low expression of the N-terminal truncated mutant PhaCBP-M-CPF4 A27 and T74 in the bacteria. As mentioned previously, this might be due to the instability of the mRNA of the N-terminal truncated PhaCBP-M-CPF4 A27 and T74. Another possible reason for the absence of PHA granules in the bacterial cells was the difficulty for the N-terminal truncated PhaCBP-M-CPF4 A27 and T74 to exist in the dimer form and very low activity of the N-terminal truncated PhaC mutants due to the missing N-terminal region [36]. The lack of PHA granules can also be due to the absence of interaction between the N-terminal truncated PhaC mutants with PhaM which might act as activators for the PhaC polymerization activity [53, 67]. This showed that when bioengineering a potential strain for PHA production, the stability of the mRNAs encoding for PHA-related proteins and their interactions with one another must also be taken into consideration to prevent unnecessary non-PHA-containing bacterial cells.
An interesting phenomenon was observed in Fig. 3B. Some of the PHA material appeared to be flowing/oozing out of the PHA granules of C. necator PHB−4 harbouring PhaCBP-M-CPF4 G8. Such fluidic/mobile nature of PHA in vivo has been reported before. PHA in vivo is maintained in an amorphous and mobile state by bacteria [68]. This amorphous and mobile state is important for the function of PHA as an intracellular carbon-storage compound because the intracellular PHA depolymerase is active only towards non-crystalline PHA. The oozing out of the PHA from its granules may be due to the damage to the surface of the PHA granules during sample preparation for TEM. This observation was only made in C. necator PHB−4 harbouring PhaCBP-M-CPF4 G8 and could be due to the lesser proteins on the granule surface which led to thinner or weaker PHA granule boundaries and hence, easier for the amorphous PHA to ooze out during sample preparation for TEM.
PHA recovery strategy by secretion of intracellular HlyA-signal-peptide-tagged-PHA granule into the culture medium through type I secretion by recombinant E. coli from bacterial culture was reported [69]. Based on the observation in Fig. 3B, there is a possibility that the oozing out of PHA from the bacteria cells could be a novel method of PHA recovery from bacterial culture. Mechanical disruption can be applied to rupture the bacterial cell wall and PHA granule boundaries, allowing the PHA to ooze out into the culture medium at the end of cultivation. However, more studies are necessary to confirm this speculation.
Based on all the data discussed above, it is evident that N-terminal truncated PhaCBP-M-CPF4 G8 showed improved properties for production of P(3HB-co-3HHx). Table 3 showed that the transformant harbouring PhaCBP-M-CPF4 G8 produced a higher Mw of P(3HB-co-3HHx) compared to the transformant harbouring the full-length PhaCBP-M-CPF4 due to its lower expression without compromising the PHA accumulating ability. The production of P(3HB-co-3HHx) with higher Mw is important as it will contribute to better physical and mechanical properties. The 3HHx molar composition only dropped by 1 mol% which will not have much effect on the physical and mechanical properties of the P(3HB-co-3HHx) produced. Another improved property of the N-terminal truncated PhaCBP-M-CPF4 G8 was that it accumulated mostly single larger PHA granules compared to the full-length PhaCBP-M-CPF4. The production of single larger PHA granules is important as it will facilitate the downstream process of non-solvent PHA extraction and purification.
Conclusions
In conclusion, the N-terminal of PhaCBP-M-CPF4 affected the substrate specificity of the PhaC, molecular weights of the PHA produced, expression of PhaCs, and the granule morphology of the PHA accumulated. N-terminal truncation decreases the 3HHx molar composition of P(3HB-co-3HHx), increases the Mw of the PHA produced, decreases the number and increases the mean diameter of PHA granules accumulated in the bacteria cells. The increase in Mw was probably due to lower expression of the N-terminal truncated PhaCBP-M-CPF4 mutants. Based on the result, among the N-terminal truncated PhaCBP-M-CPF4 mutants generated, PhaCBP-M-CPF4 G8 showed improved properties of the PHA produced compared to full-length PhaCBP-M-CPF4. This study also demonstrated N-terminal truncation can be considered as an alternative approach to improve existing PhaCs in the production of higher Mw PHA in mostly single and larger PHA granules.
Availability of data and materials
All the data in this study are included in this published article and its additional files.
Abbreviations
- PHA:
-
Polyhydroxyalkanoate
- P(3HB):
-
Poly(3-hydroxybutyrate)
- P(3HB-co-3HHx):
-
Poly[(R)-3-hydroxybutyrate-co-(R)-3-hydroxyhexanoate]
- 3HB:
-
3-Hydroxybutyrate
- MCL-PHA:
-
Medium-chain-length-PHA
- 3HHx:
-
3-Hydroxyhexanoate
- 3HO:
-
3-Hydroxyoctanoate
- 3HD:
-
3-Hydroxydecanoate
- PhaC:
-
PHA synthase
- M n :
-
Number-average molecular weight
- M w :
-
Weight-average molecular weight
- PDI:
-
Polydispersity index
- LDPE:
-
Low-density polyethylene
- PP:
-
Polypropylene
- RBS:
-
Ribosome binding site
- PhaCBP-M-CPF4 :
-
PhaC isolated from mangrove soil metagenome
- PhaCC s :
-
PhaC from Chromobacterium sp. USM2
- PhaCRa :
-
PhaC from Rhodococcus aetherivorans I24
- PhaCAh :
-
PhaC from Aeromonas hydrophila 4AK4
- PhaCAc :
-
PhaC from Aeromonas caviae
- PhaCCn :
-
PhaCs from Cupriavidus necator H16
- PhaCPa :
-
PhaC from Pseudomonas aeruginosa
- PSI-BLAST:
-
Position-Specific Iterative Basic Local Alignment Search Tool
- PSIPRED:
-
PSI-blast based secondary structure prediction
- NR:
-
Nutrient-rich
- MM:
-
Mineral medium
- CPKO:
-
Crude palm kernel oil
- PCR:
-
Polymerase chain reaction
- NCBI:
-
National Center for Biotechnology Information
- GC:
-
Gas chromatography
- CME:
-
Caprylic acid methyl ester
- GPC:
-
Gas permeation chromatography
- HPLC:
-
High-performance liquid chromatography
- qPCR:
-
Quantitative polymerase chain reaction
- RNA:
-
Ribonucleic acid
- mRNA:
-
Messenger RNA
- UTR:
-
Untranslated region
- EDTA:
-
Ethylenediaminetetraacetic acid
- cDNA:
-
Complementary deoxyribonucleic acid
- Ct:
-
Cycle threshold
- TEM:
-
Transmission electron microscopy
- OsO4 :
-
Osmium tetroxide
- ANOVA:
-
Analysis of variance
- pLDDT:
-
Per-residue estimate of its confidence
- CDW:
-
Cell dry weight
References
Sudesh K, Abe H, Doi Y. Synthesis, structure and properties of polyhydroxyalkanoates: biological polyesters. Prog Polym Sci. 2000;25:1503–55.
Doi Y. Microbial polyesters. VCH New York. 1990.
Stubbe JA, Tian J. Polyhydroxyalkanoate (PHA) homeostasis: The role of the PHA synthase. Nat Prod Rep. 2003;20:445–57.
Tang HJ, Neoh SZ, Sudesh K. A review on poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) [P(3HB-co-3HHx)] and genetic modifications that affect its production. Front Bioeng Biotechnol. 2022;10:1057067.
Rehm BHA. Polyester synthases: natural catalysts for plastics. Biochem J. 2003;376:15–33.
Chek MF, Kim SY, Mori T, Arsad H, Samian MR, Sudesh K, et al. Structure of polyhydroxyalkanoate (PHA) synthase PhaC from Chromobacterium sp. USM2, producing biodegradable plastics. Sci Rep. 2017;7:1–15.
Chuah J-A, Tomizawa S, Yamada M, Tsuge T, Doi Y, Sudesh K, et al. Characterization of site-specific mutations in a short-chain-lengths/medium-chain-length polyhydroxyalkanoate synthase: In vivo and in vitro studies of enzymatic activity and substrate specificity. Appl Environ Microbiol. 2013;79:3813–21.
Foong CP, Lakshmanan M, Abe H, Taylor TD, Foong SY, Sudesh K. A novel and wide substrate specific polyhydroxyalkanoate (PHA) synthase from unculturable bacteria found in mangrove soil. J Polym Res. 2018;25:1–9.
Kawashima Y, Orita I, Nakamura S, Fukui T. Compositional regulation of poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) by replacement of granule-associated protein in Ralstonia eutropha. Microb Cell Fact. 2015;14:1–12.
Ng LM, Sudesh K. Identification of a new polyhydroxyalkanoate (PHA) producer Aquitalea sp. USM4 (JCM 19919) and characterization of its PHA synthase. J Biosci Bioeng. 2016;122:550–7.
Doi Y, Kitamura S, Abe H. Microbial synthesis and characterization of poly(3-hydroxybutyrate-co-3-hydroxyhexanoate). Macromolecules. 1995;28:4822–8.
Kichise T, Fukui T, Yoshida Y, Doi Y. Biosynthesis of polyhydroxyalkanoates (PHA) by recombinant Ralstonia eutropha and effects of PHA synthase activity on in vivo PHA biosynthesis. Int J Biol Macromol. 1999;25:69–77.
Matsumoto K, Takase K, Aoki E, Doi Y, Taguchi S. Synergistic effects of Glu130Asp substitution in the type II polyhydroxyalkanoate (PHA) synthase: enhancement of PHA production and alteration of polymer molecular weight. Biomacromol. 2005;6:99–104.
Normi YM, Hiraishi T, Taguchi S, Sudesh K, Najimudin N, Doi Y. Site-directed saturation mutagenesis at residue F420 and recombination with another beneficial mutation of Ralstonia eutropha polyhydroxyalkanoate synthase. Biotechnol Lett. 2005;27:705–12.
Sim SJ, Snell KD, Hogan SA, Stubbe JA, Rha C, Sinskey AJ. PHA synthase activity controls the molecular weight and polydispersity of polyhydroxybutyrate in vivo. Nat Biotechnol. 1997;15:63–7.
Tan HT, Chek MF, Lakshmanan M, Foong CP, Hakoshima T, Sudesh K. Evaluation of BP-M-CPF4 polyhydroxyalkanoate (PHA) synthase on the production of poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) from plant oil using Cupriavidus necator transformants. Int J Biol Macromol. 2020;159:250–7.
Asrar J, Valentin HE, Berger PA, Tran M, Padgette SR, Garbow JR. Biosynthesis and properties of poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) polymers. Biomacromol. 2002;3:1006–12.
Aoyagi Y, Doi Y, Iwata T. Mechanical properties and highly ordered structure of ultra-high-molecular-weight poly[(R)-3-hydroxybutyrate] films: effects of annealing and two-step drawing. Polym Degrad Stab. 2003;79:209–16.
Mendonça TT, Tavares RR, Cespedes LG, Sánchez-Rodriguez RJ, Schripsema J, Taciro MK, et al. Combining molecular and bioprocess techniques to produce poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) with controlled monomer composition by Burkholderia sacchari. Int J Biol Macromol. 2017;98:654–63.
Budde CF, Riedel SL, Willis LB, Rha CK, Sinskey AJ. Production of poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) from plant oil by engineered Ralstonia eutropha strains. Appl Environ Microbiol. 2011;77:2847–54.
Fukui T, Doi Y. Cloning and analysis of the poly(3-hydroxybutyrate-co-3- hydroxyhexanoate) biosynthesis genes of Aeromonas caviae. J Bacteriol. 1997;179:4821–30.
Yu LP, Yan X, Zhang X, Chen XB, Wu Q, Jiang XR, et al. Biosynthesis of functional polyhydroxyalkanoates by engineered Halomonas bluephagenesis. Metab Eng. 2020;59:119–30.
Tsuge T, Watanabe S, Shimada D, Abe H, Doi Y, Taguchi S. Combination of N149S and D171G mutations in Aeromonas caviae polyhydroxyalkanoate synthase and impact on polyhydroxyalkanoate biosynthesis. FEMS Microbiol Lett. 2007;277:217–22.
Taguchi S, Nakamura H, Hiraishi T, Yamato I, Doi Y. In vitro evolution of a polyhydroxybutyrate synthase by intragenic suppression-type mutagenesis. J Biochem. 2002;131:801–6.
Chen GQ. A microbial polyhydroxyalkanoates (PHA) based bio- and materials industry. Chem Soc Rev. 2009;38:2434–46.
Shen R, Ning ZY, Lan YX, Chen JC, Chen GQ. Manipulation of polyhydroxyalkanoate granular sizes in Halomonas bluephagenesis. Metab Eng. 2019;54:117–26.
Pötter M, Madkour MH, Mayer F, Steinbüchel A. Regulation of phasin expression and polyhydroxylkanoate (PHA) granule formation in Ralstonia eutropha H16. Microbiology. 2002;148:2413–26.
Neoh SZ, Chek MF, Tan HT, Linares-Pastén JA, Nandakumar A, Hakoshima T, et al. Polyhydroxyalkanoate synthase (PhaC): The key enzyme for biopolyester synthesis. Curr Res Biotechnol. 2022;4:87–101.
Chek MF, Kim SY, Mori T, Tan HT, Sudesh K, Hakoshima T. Asymmetric open-closed dimer mechanism of polyhydroxyalkanoate synthase PhaC. iScience. 2020;23:101084.
Kim J, Kim YJ, Choi SY, Lee SY, Kim KJ. Crystal structure of Ralstonia eutropha polyhydroxyalkanoate synthase C-terminal domain and reaction mechanisms. Biotechnol J. 2017;12:1600648.
Teh AH, Chiam NC, Furusawa G, Sudesh K. Modelling of polyhydroxyalkanoate synthase from Aquitalea sp. USM4 suggests a novel mechanism for polymer elongation. Int J Biol Macromol. 2018;119:438–45.
Wittenborn EC, Jost M, Wei Y, Stubbe JA, Drennan CL. Structure of the catalytic domain of the class I polyhydroxybutyrate synthase from Cupriavidus necator. J Biol Chem. 2016;291:25264–77.
Ye Z, Song G, Chen G, Chen J. Location of functional region at N-terminus of polyhydroxyalkanoate (PHA) synthase by N-terminal mutation and its effects on PHA synthesis. Biochem Eng J. 2008;41:67–73.
Zheng Z, Li M, Xue XJ, Tian HL, Li Z, Chen GQ. Mutation on N-terminus of polyhydroxybutyrate synthase of Ralstonia eutropha enhanced PHB accumulation. Appl Microbiol Biotechnol. 2006;72:896–905.
Wang Q, Xia Y, Chen Q, Qi Q. Incremental truncation of PHA synthases results in altered product specificity. Enzyme Microb Technol. 2012;50:293–7.
Lim H, Chuah JA, Chek MF, Tan HT, Hakoshima T, Sudesh K. Identification of regions affecting enzyme activity, substrate binding, dimer stabilization and polyhydroxyalkanoate (PHA ) granule morphology in the PHA synthase of Aquitalea sp. USM4. Int J Biol Macromol. 2021;186:414–23.
Riedel SL, Bader J, Brigham CJ, Budde CF, Yusof ZAM, Rha C, et al. Production of poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) by Ralstonia eutropha in high cell density palm oil fermentations. Biotechnol Bioeng. 2012;109:74–83.
Simon R, Priefer U, Pühler A. A broad host range mobilization system for in vivo genetic engineering: Transposon mutagenesis in Gram negative bacteria. Nature. 1983;1:417–35.
Kovach ME, Elzer PH, Hill DS, Robertson GT, Farris MA, Roop RM, et al. Four new derivatives of the broad-host-range cloning vector pBBR1MCS, carrying different antibiotic-resistance cassettes. Gene. 1995;166:175–6.
Friedrich B, Hogrefe C, Schlegel HG. Naturally occurring genetic transfer of hydrogen-oxidizing ability between strains of Alcaligenes eutrophus. J Bacteriol. 1981;147:198–205.
Braunegg G, Sonnleitner BY, Lafferty RM. A rapid gas chromatographic method for the determination of poly-β-hydroxybutyric acid in microbial biomass. Eur J Appl Microbiolgy Biotechnol. 1978;6:29–37.
Tan HT, Chek MF, Neoh SZ, Ang SL, Yoshida S, Hakoshima T, et al. Characterization of the polyhydroxyalkanoate (PHA) synthase from Ideonella sakaiensis, a bacterium that is capable of degrading and assimilating poly(ethylene terephthalate). Polym Degrad Stab. 2022;206:110160.
Alagesan S, Hanko EKR, Malys N, Ehsaan M, Winzer K, Minton NP. Functional genetic elements for controlling gene expression in Cupriavidus necator H16. Appl Environ Microbiol. 2018;84:e00878-e918.
Livak KJ, Schmittgen TD. Analysis of relative gene expression data using real-time quantitative PCR and the 2-ΔΔCT method. Methods. 2001;25:402–8.
Ang SL, Shaharuddin B, Chuah JA, Sudesh K. Electrospun poly(3-hydroxybutyrate-co-3-hydroxyhexanoate)/silk fibroin film is a promising scaffold for bone tissue engineering. Int J Biol Macromol. 2020;145:173–88.
David L, Cheah E, Cygler M, Dijkstra B, Frolow F, Sybille M, et al. The α/β hydrolase fold. Protein Eng Des Sel. 1992;5:197–211.
Samiei H, Nazarian S, Hajizade A, Kordbacheh E. In silico design, production and immunization evaluation of a recombinant bivalent fusion protein candidate vaccine against E. coli O157:H7. Int Immunopharmacol. 2023;114:109464.
McDowell EM, Trump BF. Histologic fixatives suitable for diagnostic light and electron microscopy. Arch Pathol Lab Med. 1976;100:405–14.
Spurr AR. A low-viscosity epoxy resin embedding medium for electron microscopy. J Ultrastruct Res. 1969;26:31–43.
Wan JH, Ng L-M, Neoh SZ, Kajitani R, Itoh T, Kajiwara S, et al. Complete genome sequence of Aquitalea pelogenes USM4 (JCM19919), a polyhydroxyalkanoate producer. Arch Microbiol. 2023;205:66.
Wodzinska J, Snell KD, Rhomberg A, Sinskey AJ, Biemann K, Stubbe J. Polyhydroxybutyrate synthase: evidence for covalent catalysis. J Am Chem Soc. 1996;118:6319–20.
Gerngross TU, Snell KD, Peoples OP, Sinskey AJ, Csuhai E, Masamune S, et al. Overexpression and purification of the soluble polyhydroxyalkanoate synthase from Alcaligenes eutrophus: evidence for a required posttranslational modification for catalytic activity. Biochemistry. 1994;33:9311–20.
Kim YJ, Choi SY, Kim J, Jin KS, Lee SY, Kim KJ. Structure and function of the N-terminal domain of Ralstonia eutropha polyhydroxyalkanoate synthase, and the proposed structure and mechanisms of the whole enzyme. Biotechnol J. 2017;12:1600649.
Matsumoto K, Takase K, Yamamoto Y, Doi Y, Taguchi S. Chimeric enzyme composed of polyhydroxyalkanoate (PHA) synthases from Ralstonia eutropha and Aeromonas caviae enhances production of PHAs in recombinant Escherichia coli. Biomacromol. 2009;10:682–5.
Murugan P, Gan CY, Sudesh K. Biosynthesis of P(3HB-co-3HHx) with improved molecular weights from a mixture of palm olein and fructose by Cupriavidus necator Re2058/pCB113. Int J Biol Macromol. 2017;102:1112–9.
Madden LA, Anderson AJ, Shah DT, Asrar J. Chain termination in polyhydroxyalkanoate synthesis: Involvement of exogenous hydroxy-compounds as chain transfer agents. Int J Biol Macromol. 1999;25:43–53.
Gerngross TU, Martin DP. Enzyme-catalyzed synthesis of poly[(R)-(-)-3-hydroxybutyrate]: Formation of macroscopic granules in vitro. Proc Natl Acad Sci USA. 1995;92:6279–83.
Emory SA, Bouvet P, Belasco JG. A 5’-terminal stem-loop structure can stabilize mRNA in Escherichia coli. Genes Dev. 1992;6:135–48.
Rauhut R, Klug G. mRNA degradation in bacteria. FEMS Microbiol Rev. 1999;23:353–70.
Luciano DJ, Hui MP, Deana A, Foley PL, Belasco KJ, Belasco JG. Differential control of the rate of 5’-end-dependent mrna degradation in Escherichia coli. J Bacteriol. 2012;194:6233–9.
Richards J, Liu Q, Pellegrini O, Celesnik H, Yao S, Bechhofer DH, et al. An RNA pyrophosphohydrolase triggers 5’-exonucleolytic degradation of mRNA in Bacillus subtilis. Mol Cell. 2011;43:940–9.
Deana A, Celesnik H, Belasco JG. The bacterial enzyme RppH triggers messenger RNA degradation by 5′ pyrophosphate removal. Nature. 2008;451:355–8.
Celesnik H, Deana A, Belasco JG. Initiation of RNA decay in Escherichia coli by 5′ pyrophosphate removal. Mol Cell. 2007;27:79–90.
Neumann L, Spinozzi F, Sinibaldi R, Rustichelli F, Pötter M, Steinbüchel A. Binding of the major phasin, PhaP1, from Ralstonia eutropha H16 to poly(3-hydroxybutyrate) granules. J Bacteriol. 2008;190:2911–9.
Wieczorek R, Pries A, Steinbuchel A, Mayer F. Analysis of a 24-kilodalton protein associated with the polyhydroxyalkanoic acid granules in Alcaligenes eutrophus. J Bacteriol. 1995;177:2425–35.
Cai S, Cai L, Liu H, Liu X, Han J, Zhou J, et al. Identification of the haloarchaeal phasin (PhaP) that functions in polyhydroxyalkanoate accumulation and granule formation in Haloferax mediterranei. Appl Environ Microbiol. 2012;78:1946–52.
Pfeiffer D, Jendrossek D. PhaM is the physiological activator of poly(3-hydroxybutyrate) (PHB) synthase (PhaC1) in Ralstonia eutropha. Appl Environ Microbiol. 2014;80:555–63.
Horowitz DM, Sanders JKM. Amorphous, biomimetic granules of polyhydroxybutyrate: preparation, characterization, and biological implications. J Am Chem Soc. 1994;116:2695–702.
Rahman A, Linton E, Hatch AD, Sims RC, Miller CD. Secretion of polyhydroxybutyrate in Escherichia coli using a synthetic biological engineering approach. J Biol Eng. 2013;7:1–9.
Acknowledgements
S.Z.N. acknowledges Graduate Fellowship USM (GFUSM) awarded by Universiti Sains Malaysia (USM).
Funding
This study was funded by Ministry of Higher Education, titled "Soil Analysis and Value-Addition to Oil Palm Trunk (OPT) and sap through Biotechnology" as well as Science and Technology Research Partnership for Sustainable Development (SATREPS) (Grant Number: 203/PBIOLOGI/67811001), and Zacros (Fujimori Kogyo Co. Ltd.) (Grant Number: 304/PBIOLOGI/6501281/F117) from Japan.
Author information
Authors and Affiliations
Contributions
SZN, HTT and MFC conceived the project. SZN, HTT, CT and MFC are involved in designing the experiments. SZN carried out the experiments, collected the data of the experiments, and wrote the original manuscript. SZN, HTT, and CT were involved in the analysis of the data collected. SZN, HTT, CT, MFC, and KS were involved in reviewing and editing the manuscript. PV, TH and KS supervised this study. KS provided funding for this study. All authors had read and approved the final manuscript.
Corresponding author
Ethics declarations
Ethics approval and consent to participate
Not applicable.
Consent for publication
Not applicable.
Competing interests
K.S. reports financial support provided by Zacros (Fujimori Kogyo Co. Ltd.). K.S. reports a relationship with Zacros (Fujimori Kogyo Co. Ltd.) that includes consulting or advisory. K.S. and S.Z.N. have a patent pending to Zacros (Fujimori Kogyo Co. Ltd.): Patent application No. PI2023006066.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Additional file 1: Fig. S1
: Predicted N-terminal structure of PhaCBP-M-CPF4. Predicted N-terminal structure of PhaCBP-M-CPF4 using AlphaFold2 program. The colours in the predicted structure represented the level of confidence in the prediction. The black circle indicated the predicted structure has low confidence. The lines indicated where the truncation point of the N-terminal (A). Predicted N-terminal structure of PhaCBP-M-CPF4 using PSIPRED server. The small gap in the α1 helix is indicated with an arrow (B). Predicted secondary structure of the N-terminal of PhaCBP-M-CPF4 using a combination of AlphaFold2 program and PSIPRED server. The bold alphabets indicate the structure predicted using the PSIPRED server while the unbold alphabets indicate the structure predicted using Alphafold2 program. The truncation points were indicated with black lines (C). Fig. S2: Primer efficiency for 16S rRNA (A), phaCBP-M-CPF4 (B) primers. Fig. S3: Melt curve analysis for 16S rRNA (A), phaCBP-M-CPF4 (B) primers.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/. The Creative Commons Public Domain Dedication waiver (http://creativecommons.org/publicdomain/zero/1.0/) applies to the data made available in this article, unless otherwise stated in a credit line to the data.
About this article
Cite this article
Neoh, S.Z., Tan, H.T., Trakunjae, C. et al. N-terminal truncation of PhaCBP-M-CPF4 and its effect on PHA production. Microb Cell Fact 23, 52 (2024). https://doi.org/10.1186/s12934-024-02329-w
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s12934-024-02329-w