Abstract
High specific surface area three-dimensional pine tree-like hierarchical TiO2 nanotube array films loaded with Ag nanoparticles were successfully prepared by one-step hydrothermal reaction combining with simple and feasible magnetron sputtering. The composite Ag/TiO2-branched nanotube arrays show outstanding photocatalytic property, which is attributed to the boost of plasmonic enhancement carrier generation and separation, higher specific surface area, higher organic pollutant absorption, faster charge transport, and superior light-harvesting efficiency for efficient charge collection. The work provides a cost-effective and flexible pathway to develop high-performance photocatalyst or optoelectronic devices.
Avoid common mistakes on your manuscript.
Background
In spite of nearly half a century investigations, since Fujishima and Honda discovered the photocatalytic water splitting on TiO2 electrodes in 1972 [1], TiO2 still remains to be intensively investigated as semiconductor photocatalyst owing to its important applications in phtocatalysis [2,3,4,5,6,7], photoelectrochemical water splitting [8,9,10,11,12], solar cell [13,14,15,16], and sensors [17, 18], because of its excellent chemical stability, abundance, and low cost. However, the photocatalytic activities of TiO2 are restricted by its low photocatalytic sensitivity in the UV region and rapid recombination of photogenerated electron and hole pairs [19]. Much effort has been dedicated to enhance the photocatalytic efficiency of TiO2 in the aspect of morphology, surface area, and surface defects. Zero-dimensional (D) TiO2 particles fabricated with randomly organized provides a large specific surface area for absorbing sufficient dye molecules. However, it has high charge recombination because of the large grain boundary of nanoparticles (NPs) [20, 21]. Then, well-aligned one-dimensional nanostructure such as nanowires, nanorods, and nanotubes were fabricated to improve charge transport due to a direct transport pathway for photogenerated electrons [22,23,24]. Nevertheless, the drawback of the low surface-to-volume ratio of one-dimensional nanostructure results to a low photocatalytic activity. Recently, researchers have been enthusiastically dedicated to develop three-dimensional nanostructures such as nanoflowers and nanotrees for application in photocatalysis [25,26,27,28]. Compared with zero-dimensional NPs and one-dimensional nanowires, the three-dimensional nanostructure offers the advantage of a large surface area that increases dye loading. Additionally, the three-dimensional morphology could offer long optical paths for efficient light absorption and abundant active sites for electrochemical reactions, providing efficient transport pathway for rapid charge transport that leads to improving electron collection and electron-hole separation.
TiO2 decorated with noble metal (Au, Ag, Pt, etc.) NPs named plasmonic photocatalysis is another promising method for enhancing the photocatalytic activity of TiO2 owing to the localized surface plasmon resonance (LSPR) effect of metal NPs [29,30,31,32,33]. The band gap of TiO2 is about 3.2 eV, and Ag NPs show a very strong LSPR absorption in the near-UV region [34, 35]. So, Ag is an optimal choice due to the Ag NPs’ LSPR position close to the exciton absorption of TiO2; on the other hand, silver is most suitable for industrial applications owing to its easy preparation and low cost. Moreover, the Ag NPs decorated on the surface of TiO2 could act as an electron trap center to effectively prevent electron-hole recombination and enhance the photocatalytic activity.
Herein, we report a high-performance plasmonic photocatalyst three-dimensional pine tree-like hierarchical TiO2 nanotube array films loaded with Ag NPs fabricated by a simple two-step process. The composite Ag/TiO2-branched nanotube arrays show outstanding photocatalytic property, which is attributed to the boost of plasmonic-enhanced carrier generation and separation, higher specific surface area, higher organic pollutant absorption, faster charge transport, and superior light-harvesting efficiency for efficient charge collection. Figure 1 illustrates the formation procedure and proposed photocatalytic mechanism of three-dimensional pine tree-like hierarchical TiO2 nanotube array films loaded with Ag NPs. Compared with our previous work, the photocatalytic activity of three-dimensional pine tree-like hierarchical TiO2 nanotube array films loaded with Ag NPs was further enhanced.
Results and Discussion
The microstructural and morphology detail of the prepared three-dimensional pine tree-like hierarchical TiO2 nanotube arrays is shown in Fig. 2a. The cross-sectional SEM images show that the prepared three-dimensional pine tree-like hierarchical TiO2 nanotube arrays composing of a vertically oriented nanotube trunk with a length of approximately 5 μm grafted with large amounts of short branches with lengths of about 300 nm were directly grown on FTO substrate by a simple one-step hydrothermal method. As shown in Fig. 2b the SEM image and magnified image (the inset) of three-dimensional pine tree-like hierarchical TiO2 nanotube arrays, the three-dimensional TiO2 nanotube arrays were fully covered and arranged homogeneously on the FTO glasses with large-scale and uniform growth and large amounts of short nanorod branches. The magnified image shows the diameter of the branch at approximately 50 nm. This hierarchical architecture with large specific surface area can enhance the absorption of dye molecules and effectively improve charge transport by a direct transport path thereby may be improving the photocatalytic activity of the TiO2. The phase purity and structure of the three-dimensional pine tree-like hierarchical TiO2 nanotube arrays were analyzed using XRD as shown in Fig. 2c. It can be found that diffraction peaks appeared at 25.4° and 48°, which can be attributed to the (101) and (200) orientations of the anatase TiO2 (JCPDS No.21-1272) [36]. No characteristic peak of any impurity is probed, which demonstrates that the sample fabricated by this method has high phase purity. Raman scattering as a local probe is very sensitive to microstructures and crystallinity of materials. Figure 2d shows the Raman scattering spectra of three-dimensional pine tree-like hierarchical TiO2 nanotube arrays. The founded Raman bands at 145, 399, 516, and 640 cm−1 can be separately indexed to the Eg, B1g, A1g, or B1g and Eg, which are consistent with the anatase phase of TiO2 and without any signal of a brookite or rutile phase [37, 38]. This result is consistent with the XRD. All the results show that the three-dimensional pine tree-like hierarchical anatase TiO2 nanotube array films were successfully fabricated.
The typical SEM views of Ag NPs with deposition time of 10, 20, 30, and 40 s are shown in Fig. 3a–d, and the inset one is the corresponding magnified image. It can be observed that Ag NPs are uniformly coated on the branches of TiO2. The mean diameter of Ag NPs is approximately13, 25, 35, and 45 nm in sample Ag(10s)/TiO2, Ag(20s)/TiO2, Ag(30s)/TiO2, and Ag(40s)/TiO2, respectively. It is obvious that the diameter of Ag NPs increases with the increase of silver deposition time. So, Ag NPs deposited uniformly on three-dimensional pine tree-like hierarchical TiO2 nanotube arrays by a simple magnetron sputtering system were fabricated. It is well know that the LSPR effect of Ag NPs can form a strong local electronic field. Moreover, Ag NPs here were decorated uniformly on the branches of TiO2, so the near-field dipolar interactions between adjacent particles [39] were very strong. Therefore, it may form a stronger local electronic field in the hierarchical structure. So, Ag NPs deposited on three-dimensional pine tree-like hierarchical TiO2 nanotube arrays are expected with higher performance.
To further demonstrate the successful fabrication of Ag NPs deposited on three-dimensional pine tree-like hierarchical TiO2 nanotube arrays, the elemental chemical status and compositions of Ag(30s)/TiO2 were analyzed by XPS. Figure 4a shows the XPS spectrum of Ti 2p. It can be observed that two peaks at binding energies of 464.3 and 458.5 eV can be attributed to Ti 2p3/2 and Ti 2p1/2, respectively. The result demonstrates the state of Ti4+ in the anatase TiO2 [40]. The O 1s peaks at binding energy of 529.8 eV are attributed to the typical signal of Ti-O-Ti as shown in Fig. 4b [41]. The Ag 3d XPS spectrum shown in Fig. 4c consists of two peaks at 368.1 and 374.1 eV with a distance of approximately 6.0 eV. These binding energies are consistent with Ag 3d5/2 and Ag 3d3/2, confirming that Ag NPs primarily exist in the metallic form in the Ag/TiO2 composite [42].
The technique to characterize the plasmonic response absorption of Ag NPs is to investigate the UV-vis absorption spectrum. At Ag LSPR frequency, Ag NPs exhibit strong absorption. Figure 5 displays the absorption spectra of TiO2 and Ag NPs deposited on the branches of TiO2 with different deposited times. The absorption edge nearby 400 nm belongs to the optical band gap absorption of TiO2 [43]. The increased absorption peak at around 425 nm belongs to the SPR of Ag NPs. It also shows that absorption peak increases with the increase of Ag NPs on the surface of TiO2. It can be observed that the position of Ag NPs SPR is close to the exciton absorption of TiO2. Hence, it is beneficial for the energy coupling of the TiO2 plasmonic photocatalyst.
The phototcatalytic activity of TiO2 array films, Ag(10s)/TiO2, Ag(20s)/TiO2, Ag(30s)/TiO2, and Ag(40s)/TiO2 composite systems with an area about 6 cm2 was evaluated by degradation of the rhodamine B (RhB) solution under UV and visible irradiation, and the temperature was maintained at 18 °C in the process of photocatalytic reaction (Table 1). And the RhB solution was also measured under the same experimental conditions. The irradiation time interval is 30 min. As shown in Fig. 6a, the concentration of RhB is decreased upon the irradiation time. The RhB decolorization rate for the three-dimensional pine tree-like hierarchical TiO2 nanotube can only approach 55% after 2-h UV-vis light irradiation. However, it is found that the photocatalytic efficiency of the Ag/TiO2 composite films increases significantly than the pure TiO2. The Ag(30s)/TiO2 shows the highest photocatalytic performance that degraded 98% of RhB after the UV-vis light irradiation for 1 h. The degradation of Ag(20s)/TiO2 is 96% after 1.5-h UV-vis light irradiation. The degradation of Ag(10s)/TiO2 is 98%, and the degradation of Ag(40s)/TiO2 is 84% after 2-h UV-vis light irradiation. Moreover, the photocatalytic reaction of semiconductor materials can be accounted for by Langmuir-Hinshelwood (L-H) model, The L-H model equation is as below [44]:
where A 0/A represents the ratio of concentration of the dye at adsorption-desorption equilibrium and after irradiation for time t. And the k is the apparent first-order reaction rate constant (min−1). The k value of TiO2 and Ag/TiO2 composite structure with different Ag deposition times are shown in Table 2. The k value of pure TiO2 is 9 × 10−3 min−1, and the Ag(30s)/TiO2 shows that the largest k value is about 6 × 10−2 min−1. The k value of Ag(30s)/TiO2 is nearly seven times than that of pure TiO2, and the k value of other samples is 3.7 × 10−2 min−1(Ag(20s)/TiO2), 3.5 × 10−2 min−1(Ag(10s)/TiO2), and 1.5 × 10−2 min−1 (Ag(40s)/TiO2). The enhancement of the photocatalytic efficiency is significant for all Ag deposited samples than the pure TiO2, and the photocatalytic efficiency of Ag/TiO2 is increased with the increase of Ag deposition time, but with further increase of the deposition time to 40 s, the sample shows lower photocatalytic efficiency than other samples. Therefore, the optimum Ag deposition time is 30 s in the research.
The stability of the photocatalyst is very important for practical applications. Therefore, the stability of Ag(30s)/TiO2 has been further evaluated by recycling the photocatalyst for RhB degradation as shown in Fig. 6b. It can be seen that the degradation rate of RhB solution is more than 90% after 4 cycles with duration of 60 min per cycle, which is to say that the photocatalytic efficiency of Ag(30s)/TiO2 does not exhibit obvious loss after several recycles. The result shows that the Ag/TiO2 composite has high stability during the photocatalytic degradation of RhB.
On the basis of the experiment results, the outstanding photocatalytic performance of Ag/TiO2 may be explained as follows:
-
(1)
Large specific surface area and fast charge transport.
Three-dimensional pine tree-like hierarchical TiO2 nanotube arrays composing of a vertically oriented nanotube trunks and grafted with large amounts of short branches that have a large surface and enhance the absorption of dye molecules. Moreover, the photo-induced electrons directly transport through the nanotube [45], and the nanotube provides efficient transport pathway for rapid charge transport that leads to improving the electron collection and the electron-hole separation. Therefore, the photocatalytic activity of TiO2 could be increased.
-
(2)
LSPR-mediated local field enhancement.
It is well known that the LSPR effect of Ag NPs can induce a strong local electric field. Moreover, here, a large number of Ag NPs are uniformly located on the branches of TiO2, so near-field dipolar interactions between adjacent particles were very strong. Therefore, the LSPR of Ag NPs can enhance the local field near the surface of NPs as well as the giant field enhancement between adjacent particles [39, 46, 47]. Hence, there may be induced strong local electric field in the structure. The strong local electric field can increase the light capturing, and therefore boosts the generation of electron-hole pairs in Ag/TiO2 composite, and hence improves the performance of photocatalysis. The typical Raman spectra of TiO2, Ag(10s)/TiO2, Ag(20s)/TiO2, Ag(30s)/TiO2, and Ag(40s)/TiO2 are shown in Fig. 7. It can be observed that the Raman intensity of Ag/TiO2 composites increases compared to that of pure TiO2. The Raman scattering intensity increased with the increase of Ag deposition time and then decreased when the deposition time reaches 40 s, and the sample of Ag(30s)/TiO2 shows the strongest Raman intensity. As is well known that Raman scattering intensity is proportional to the square of the intensity of a local field [47], Raman peak intensity enhancement is due to LSPR-mediated large near-field enhancement. The scattering and absorption cross-sections are separately proportional to R6 and R3 when the size of NPs is much smaller than the wavelength of light. As a result, for small particles (about <30 nm), the optical response dominates by absorption. Moreover, the absorption increases with the increased size of Ag NPs, it implies that the local electrical field induced by LSPR will increase with the increase of NP size. Therefore, the Ag(30s)/TiO2 shows high enhancement factors of Raman scattering. However, the optical response dominates by scattering for larger particles [48, 49], so, the local field induced by LSPR of the Ag NPs of Ag(40s)/TiO2 is weaker than that of other samples. On the other hand, due to the light scatter increase for Ag(40s)/TiO2, the optical path increases, so the absorption of light can also increase. Therefore the Ag(40s)/TiO2 also shows much higher photocatalytic performance than that of pure TiO2. Based on our experiment results and literature, the boost generation of the electron-hole pairs due to the effect of LSPR is the critical factor to enhance the photocatalytic activity of TiO2.
-
3)
The electron transfer from Ag to TiO2.
Figure 1c illustrates the possible charge transfer process in Ag/TiO2 system. When TiO2 is irradiated by light with energy higher than its band gap, valence electron is excited into the conduction band and hole still in the valence. Valence holes accumulated to the surface and induced the surface hydroxyl radical · OH [50], then oxidated the decomposition of RhB. However, the generated electrons would transfer from the TiO2 to Ag NPs because the work function of TiO2 (4.2 eV [51]) is lower than that of Ag (4.52 to 4.74 eV [52]), and Ag NPs act as electron trap which effectively facilitate the separation of photogenerated carriers, thus improves the transfer efficiency of electron and hole pairs [53, 54]. The electrons on Ag NPs will be transferred to the absorbed oxygen and form superoxide, the formed superoxide is responsible for the reduction of organic RhB [55]. Thus, the Ag/TiO2 structure can efficiently prevent the recombination of electron and hole, therefore improves the photocatalytic efficiency of TiO2.
Conclusions
In summary, the high-performance plasmonic photocatalyst three-dimensional pine tree-like hierarchical TiO2 nanotube array films loaded with Ag NPs were fabricated by a simple two-step process. A large number of uniform Ag NPs dispersed in the pin tree-like hierachical TiO2, which effectively improved the light harvest, boosted the generation of electron and hole pairs, and notably improved the separation, transport, and electron-hole pairs with large specific surface area, significantly improved the photocatalytic performance under UV-visible light irradiation (seven times than pure TiO2). Therefore, this research supplies an effective synthetic strategy for noble metal NP-modified three-dimensional hierarchical TiO2, which will be of great significance for promising applications in the fields of environment and energy for high-efficiency light-energy conversion.
Methods
Synthesis of Three-Dimensional Pine Tree-Like Hierarchical TiO2 Nanotube Array Films
Three-dimensional tree-like TiO2nanotube arrays were synthesized using a hydrothermal method. The details of the synthetic procedure were described by Roh et al. [56]. Briefly, 0.73 g of potassium titanium oxide oxalate dehydrates (PTO) was dissolved in 7-ml deionized water, and then, the mixed solution was added to 33-ml diethylene glycol (DEG) and stirred well. Fluorine-doped tin oxide (FTO) transparent conductive glass substrates were washed by isopropanol, chloroform, and deionized water successively. And then, a cleaned FTO was placed in a teflon-lined stainless steel autoclave filled with mixed solutions. The hydrothermal reactions temperature is 200 °C, and the reaction time is 11 h. After the reaction, the as-synthesized samples were washed with water more than once. After that, the as-prepared samples were annealed in air at 500 °C for 1 h to remove the residuary organic substance.
Preparation of Ag/TiO2 Composites
Ag NPs were deposited on three-dimensional pine tree-like hierarchical TiO2 nanotube array films by a magnetron sputtering system. The deposition rate of Ag is about 20 nm min−1, and deposition time is 10, 20, 30, and 40 s, then obtained Ag NP-decorated three-dimensional pine tree-like hierarchical TiO2 nanotube array films were named as Ag(10s)/TiO2, Ag(20s)/TiO2, Ag(30s)/TiO2, and Ag(40s)/TiO2.
Characterization
The morphology and microstructure of the sample was examined by SEM (S4800, Hitachi) operated at an acceleration voltage of 5 kV. The crystallinity and phase constitutions of all samples were analyzed with X-ray diffraction (XRD) (D8 Germany, Bruker Axs). The elemental chemical status and compositions were analyzed with X-ray photoelectron spectroscopy (XPS) using Mg Ka1, 2 (1253.6 eV) excitation. The Raman scattering spectra were analyzed by a micro-Raman system (LabRAM HR800, HORIBA JobinYvon, Paris, France). Ar laser (532.0 nm) is the excitation source, and laser power was kept at 2.5 mW. The UV-vis absorption spectra of all samples were determined by UV-visible dual-beam spectrophotometer (Shimadzu UV 2550).
Photocatalytic Activity Measurement
The photocatalytic activity of the prepared sample with an area of about 6 cm2 was evaluated by decolorization of 10-ml rhodamine B (RhB) solution with the concentration of 10 mg/L. Mercury lamplight as a UV and visible light source (spectral distribution and relative intensity of the mercury lamp in Table 1). The temperature was maintained at 18 °C in the process of photocatalytic reaction by equipping with a water circulation facility. Before irradiation, all samples were put into 10-ml RhB solution for 30 min in darkness in order to establish an adsorption/desorption equilibrium of RhB molecules on the surface of the photocatalysts. The degradation of RhB solution was determined by using an UV-vis spectrophotometer (Shimadzu UV 2550) at 554.0 nm. The time interval is 30 min, and the total reaction time was 2 h. As a comparison, the RhB solution was also measured under the same experimental conditions.
Abbreviations
- D:
-
Dimensional
- DEG:
-
Diethylene glycol
- FTO:
-
Fluorine-doped tin oxide
- LSPR:
-
Localized surface plasmon resonance
- NPs:
-
Nanoparticles
- PTO:
-
Potassium titanium oxide oxalate dehydrates
- RhB:
-
Rhodamine B
- SEM:
-
Scanning electron microscopy
- XPS:
-
X-ray photoelectron spectroscopy
- XRD:
-
X-ray diffraction
References
Fujishima A, Honda K (1972) Electrochemical photolysis of water at a semiconductor electrode. Nature 238:37–38
Liu HY, Joo JB, Dahl M, Fu LS, Zeng ZZ, Yin YD (2015) Crystallinity control of TiO2 hollow shells through resin-protected calcination for enhanced photocatalytic activity. Energy Environ Sci 8:286–296
Tan LL, Ong WJ, Chai SP, Yong ST, Mohamed AR (2014) Self-assembly of nitrogen-doped TiO2 with exposed {001} facets on a graphene scaffold as photo-active hybrid nanostructures for reduction of carbon dioxide to methane. Nano Res 7:1528–1547
Hossain MA, Park J, Ahn JY, Park C, Kim Y, Kim SH, Lee D (2015) Investigation of TiO2 nanotubes/nanoparticles stacking sequences to improve power conversion efficiency of dye-sensitized solar cells. Electrochim Acta 173:665–671
Li H, Yu H, Quan X, Chen S, Zhao H (2015) Improved photocatalytic performance of heterojunction by controlling the contact facet: high electron transfer capacity between TiO2 and the {110} facet of BiVO4caused by suitable energy band alignment. Adv Funct Mater 25:3074–3080
Bai S, Wang L, Chen X, Du J, Xiong Y (2015) Chemically exfoliated metallic MoS2 nanosheets: a promising supporting co-catalyst for enhancing the photocatalytic performance of TiO2 nanocrystals. Nano Res 8:175–183
Xiao FX, Hung SF, Miao J, Wang HY, Yang H, Liu B (2015) Metal-cluster-decorated TiO2 nanotube arrays: a composite heterostructure toward versatile photocatalytic and photoelectrochemical applications. Small 11(5):554–567
Liu N, Schneider C, Freitag D, Hartmann M, Venkatesan U, Mîller J, Spiecker E, Schmuki P (2014) Black TiO2 nanotubes: cocatalyst-free open-circuit hydrogen generation. Nano Lett 14:3309–3313
Zhou X, Liu N, Schmuki P (2014) Ar+-ion bombardment of TiO2 nanotubes creates co-catalytic effect for photocatalytic open circuit hydrogen evolution. Electrochem Commun 49:60–64
Asahi R, Morikawa T, Irie H, Ohwaki T (2014) Nitrogen-doped titanium dioxide as visible-light-sensitive photocatalyst: designs, developments, and prospects. Chem Rev 114:9824–9852
Zhou X, Häublein V, Liu N, Nguyen NT (2016) TiO2 nanotubes: nitrogen-ion implantation at low dose provides noble-metal-free photocatalytic H2-evolution activity. Angew Chem Int Ed 55:3763–3767
Priebe JB, Radni KJ, Lennox AJJ, Pohl M, Karnahl M, Hollmann D, Grabow K, Bentrup U, Junge H, Beller M, Brîckner A (2015) Solar hydrogen production by plasmonic Au–TiO2 catalysts: impact of synthesis protocol and TiO2 phase on charge transfer efficiency and H2 evolution rates. ACS Catal 5:2137–2148
Liao JY, Lei BX, Chen HY, Kuang DB, Su CY (2012) Oriented hierarchical single crystalline anatase TiO2 nanowire arrays on Ti-foil substrate for efficient flexible dye-sensitized solar cells. Energy Environ Sci 5:5750–5757
Giordano F, Abate A, Baena JPC, Saliba M et al (2016) Enhanced electronic properties in mesoporous TiO2 via lithium doping for high-efficiency perovskite solar cells. Nat Commun 7:10379
Wang H, Wang B, Yu J, Hu Y, Xia C, Zhang J, Liu R (2014) Significant enhancement of power coversion efficiency for dye sensitized solar cell using 1D/3D network nanostructures as photoanodes. Sci Rep 5(9305):1–9
Li Z, Ding Y, Mo L, Hu L, Wu J, Dai S (2015) Fine tuning of nanocrystal and pore sizes of TiO2 submicrospheres toward high performance dye-sensitized solar cells. ACS Appl Mater Interfaces 7:22277–22283
Wang C, Yin L, Zhang L, Qi Y, Lun N, Liu N (2010) Large scale synthesis and gas-sensing properties of anatase TiO2 three-dimensional hierarchical nanostructures. Langmuir 26:12841–12848
Lou Z, Li F, Deng J, Wang LL (2013) Branch-like hierarchical heterostructure (α-Fe2O3/TiO2): a novel sensing material for trimethylamine gas sensor. ACS Appl Mater Interface 5(23):12310–12316
Yang G, Xiao T, Sloan J, Li G, Yan Z (2011) Low-temperature synthesis of visible-light active fluorine/sulfur co-doped mesoporous TiO2 microspheres. Chem Eur J 17:1096
Bisquert J, Cahen D, Hodes G, RuhleS ZA (2004) Physical chemical principles of photovoltaic conversion with nanoparticulate, mesoporous dye-sensitized solar cells. J Phys Chem B 108:8106–8118
Zhu K, Neale NR, Miedaner A, Frank AJ (2007) Enhanced charge-collection efficiencies and light scattering in dye-sensitized solar cells using oriented TiO2 nanotubes arrays. Nano Lett 7:69–74
Baker DR, Kamat PV (2009) Photosensitization of TiO2 nanostructures with CdS quantum dots: particulate versus tubular support architectures. Adv Funct Mater 19:805–811
Jiu J, Isoda S, Wang F, Adachi M (2006) Dye-sensitized solar cells based on a single-crystalline TiO2 nanorod film. J Phys Chem B 110:2087–2092
Wang J, Lin Z (2008) Freestanding TiO2 nanotube arrays with ultrahigh aspect ratio via electrochemical anodization. Chem Mater 20:1257–1261
Joshi RK, Schneider JJ (2012) Assembly of one dimensional inorganic nanostructures into functional 2D and 3D architectures. Synthesis, arrangement and functionality. ChemSocRev 41:5285–5312
Chen Q, Chen C, Ji H, Ma W, Zhao J (2013) Surfactant-additive-free synthesis of 3D anatase TiO2 hierarchical architectures with enhanced photocatalytic activity. RSC Adv 3:17559
Liu J, Yang SL, Wu W, Tian QY, Cui SY, Dai ZG, Ren F, Xiao XH, Jiang CZ (2015) 3D Flowerlike α-Fe2O3@TiO2core − shell nanostructures: general synthesis and enhanced photocatalytic performance. ACS Sustainable Chem Eng 3:2975–2984
Pathak P, Gupta S, Grosulak K, Imahori H, Subramanian V (2015) Nature-inspired tree-like TiO2 architecture: a 3D platform for the assembly of CdS and reduced graphene oxide for photoelectrochemical processes. J Phys Chem C 119:7543–7553
Jiang TT, Jia CC, Zhang LC, He SR, Sang YH, Li HD, Li YQ, Xu XH, Liu H (2015) Gold and gold-palladium alloy nanoparticles on heterostructured TiO2 nanobelts as plasmonic photocatalysts for benzyl alcohol oxidation. Nanoscale 7:209–217
Awazu K, Fujimaki M, Rockstuhl C, Tominaga J, Murakami H, Ohki Y, Yoshida N, Watanabe T (2008) A plasmonic photocatalyst consisting of silver nanoparticles embedded in titanium dioxide. J Am Chem Soc 130:1676–1680
Kumar MK, Krishnamoorthy S, Tan LK, Chiam SY, Tripathy S, Gao H (2011) Field effects in plasmonic photocatalyst by precise SiO2 thickness control using atomic layer deposition. ACS Catal 1:300–308
Zhang XG, Wang B, Wang XZ, Xiao XX, Dai ZG, Wu W, Zheng JF, Ren F, Jiang CZ (2015) Preparation of M@ BiFeO3nanocomposites (M = Ag, Au) bowl arrays with enhanced visible light photocatalytic activity. J Am Ceram Soc 98:2255–2263
Pu YC, Wang G, Chang KD, Ling Y, Lin YK, Fitzmorris BC, Liu CM, Lu X, Tong Y, Zhang JZ, Hsu YJ, Li Y (2013) Au nanostructure-decorated TiO2 nanowires exhibiting photoactivity across entire UV-visible region for photoelectrochemical water splitting. Nano Lett 13:3817–3823
Kerker M (1985) The optics of colloidal silver: something old and something new. J Colloid Interface Sci 105:297–314
Sun L, Li J, Wang CL, Li SF, Lai YK, Chen HB, Lin CJ (2009) Ultra sound aided photochemical synthesis of Ag loaded TiO2 nanotube arrays to enhance photocatalytic activity. J Hazard Mater 171:1045–1050
Fan Z, Meng F, Zhang M, Wu Z, Sun Z, Li A (2016) Solvothermal synthesis of hierarchical TiO2 nanostructures with tunable morphology and enhanced photocatalytic activity. Appl Surf Sci 360:298–305
Zhang WF, He YL, Zhang MS, Yin Z, Chen Q (2000) Raman scattering study on anatase TiO2 nanocrystals. J Phys D Appl Phys 33:912–916
Samara GA, Peercy PS (1973) Pressure and temperature dependence of the static dielectric constants and Raman spectra of TiO2 (Rutile). Phys Rev B 7:1131–1148
Biteen JS, Lewis NS, Atwater HA (2006) Spectral tuning of plasmon-enhanced silicon quantum dot luminescence. Appl Phys Lett 88(131109):1–3
Price NJ, Reitz JB, Madix RJ, Solomon EJA (1999) A synchrotron XPS study of the vanadia–titania system as a model for monolayer oxide catalysts. J Electron Spectrosc Relat Phenom 257:98–99
Yu J, Yu H, Cheng B, Zhou H, Zhao J (2006) Enhanced photocatalyticactivity of TiO2 power (P25) by hydrothermal treatment. J Mol Catal A Chem 253:112–118
Yang LB, Jiang X, Ruan WD, Yang XJ, Zhao B, Xu WQ, Lombardi JR (2009) Charge-transfer-induced surface-enhanced raman scattering on Ag-TiO2 nanocomposites. J Phys Chem C 113:16226
Linsebigler AL, Lu GQ, Yates JT Jr (1995) Photocatalysis on TiO2 surfaces: principles, mechanisms, and selected results. Chem Rev 95:735–758
Al-Ekabi H, Serpone N (1988) Kinetics studies in heterogeneous photocatalysis. I. Photocatalytic degradation of chlorinated phenols in aerated aqueous solutions over titania supported on a glass. J Phys Chem 92:5726–5731
Choi J, Kang G, Park T (2015) A competitive electron transport mechanism in hierarchical homogeneous hybrid structures composed of TiO2nanoparticles and nanotubes. Chem Mater 27:1359–1366
Xie K, Sun L, Wang C, Lai Y, Wang M, Chen H, Lin C (2010) Photoelectrocatalytic properties of Ag nanoparticles loaded TiO2 nanotube arrays prepared by pulse current deposition. Electrochim Acta 55:7211–7218
Garcia-Vidal FJ, Pendry JB (1996) Collective theory for surface enhanced Raman scattering. Phys Rev Lett 77:1163–1166
Evanoff DD Jr, Chumanov G (2005) Synthesis and optical properties of silver nanoparticles and arrays. Chem Phys Chem 6:1221–1231
Rycenga M, Cobley CM, Zeng J, Li W, Moran CH, Zhang Q, Qin D, Xia Y (2011) Controlling the synthesis and assembly of silver nanostructures for plasmonic applications. Chem Rev 111:3669–3712
Alberic RM, Jardim WF (1997) Photocatalytic destruction of VOCs in thegas-phase using titanium dioxide. Appl Catal B-Environ 14:55–68
Tan TY, Yip CK, Beydoun D, Amal R (2003) Effects of nano-Ag particles loading on TiO2 photocatalytic reduction of selenate ions. Chem Eng J 95:179–186
Fang YJ, Sha J, Wang ZL, Wan YT, Xia WW, Wang YW (2011) Behind the change of the photoluminescence property of metal-coated ZnO nanowire arrays. Appl Phys Lett 98:033103
Subramanian V, Wolf EE, Kamat PV (2004) Catalysis with TiO2/gold nanocomposites. Effect of metal particle size on the Fermi level equilibration. J Am Chem Soc 126:4943
Hirakawa T, Kamat PV (2005) Charge separation and catalytic activity of Ag@ TiO2 core-shell composite clusters under UV-irradiation. J Am Chem Soc 127:3928
Miyauchi M, Nakajima A, Hashimoto K, Watanabe T (2000) A highly hydrophilic thin film under 1 μW/cm2 UV illumination. Adv Mater 12:1923–1927
Roh DK, Chi WS, Jeon H, Kim SJ, Kim JH (2014) High efficiency solid-state dye-sensitized solar cells assembled with hierarchical anatase pine tree-like TiO2 nanotubes. Adv Funct Mater 24:379–386
Acknowledgments
The authors are thankful to the NSFC (51371131, 11305056, and 61422407), Jiangsu Provincial Natural Science Foundation (BK20141217) and the Open Foundation of Hubei Collaborative Innovation Center for High-efficiency Utilization of Solar Energy (Grant Nos. HBSKFM2014013).
Funding
NSFC (51371131, 11305056, and 61422407), Jiangsu Provincial Natural Science Foundation (BK20141217) and the Open Foundation of Hubei Collaborative Innovation Center for High-efficiency Utilization of Solar Energy (Grant Nos. HBSKFM2014013).
Authors’ contributions
JX participated in the material preparation and data analysis and drafted the manuscript. ZX, WQ, XG, and DH participated in the sample characterization. XX participated in its design and coordination. All authors read and approved the final manuscript.
Competing interests
The authors declare that they have no competing interests.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Xu, J., Wang, Z., Li, W. et al. Ag Nanoparticles Located on Three-Dimensional Pine Tree-Like Hierarchical TiO2 Nanotube Array Films as High-Efficiency Plasmonic Photocatalysts. Nanoscale Res Lett 12, 54 (2017). https://doi.org/10.1186/s11671-017-1834-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-017-1834-1