Abstract
The thrust to develop eco-friendly procedures for the production of nanoparticles arises from the extremely recent nanotechnology research. Extracellular biosynthesis of gold nanoparticles was achieved by an easy biological procedure using Klebsiella pneumoniae as the reducing agent. After exposing the gold ions to K. pneumoniae, rapid reduction of gold ions is observed foremost to the formation of gold nanoparticles in colloidal solution. UV-vis spectrum of the aqueous medium containing gold nanoparticles showed a peak around 560 nm. The crystalline nature of the particles was confirmed from an X-ray diffractometer. Transmission electron microscopy (TEM) micrograph analysis of the gold nanoparticles indicated that they were well dispersed and ranged in sizes 35 to 65 nm. The high crystalline in the FCC phase is evidenced by bright circular spots in a selected-area electron diffraction pattern and clear lattice fringes in the high-resolution TEM image. Fourier transform infrared spectroscopy revealed possible involvement of reductive groups on the surface of nanoparticles. The method exploits a cheap and easily available biomaterial not explored so far for the synthesis of metallic nanoparticles.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Background
Currently, nanoparticles (NPs) have drawn marvelous consideration because of their valuable properties on various fields such as medical, sensor, optical, electronic, and catalytic application [1]. Green-mediated synthesis and characterization of nanoparticles have emerged as a significant division of nanotechnology in the last decade, particularly for noble metals such as gold, silver, platinum, and palladium. Moreover, the chemical or physical approaches are usually employed to synthesize metal nanoparticles because of their intrinsic advantage in producing well-defined NPs with quite controllable shapes and sizes [2]. However, the former methods involve tedious treatments, such as inert gas condensation, pyrolysis [3], laser ablation, and hydrothermal and solvothermal synthesis [4]. Sol-gel method is based on inorganic polymerization reactions. The sol-gel process includes four steps: hydrolysis, polycondensation, drying, and thermal decomposition [5]. Ambitious by the growing momentum of green nanotechnology, the synthesis of NPs utilizing biological materials could be an improved alternative to toxic chemicals and the expensive physical methods. In general, biological organisms, such as bacteria and fungi majorly referred to as microorganisms [6], plants [7], and algae [8] represent a development of an eco-friendly and cost-effective approach [9]. Using of bacteria for the biosynthesis of metal nanoparticle process is the easiest method.
Following the revolutionary study of [10] on bacteria-mediated biosynthesis of silver NPs, many efforts have been directed toward this area with the use of bacteria, such as Thermomonospora sp.[11], Lactobacillus strains[12], Shewanella algae[13], Actinobacter sp. [14], Plectonema boryanum[15], Rhodopseudomonas capsulate[16], Shewanella algae[17], Geobacter sulfurreducens[18], Morganella sp. [19], Bacillus subtilus[20], Staphylococcus aureus[21], Escherichia coli[22], and Serratia nematodiphila[6]. These bacteria were demonstrated to be responsible for the bacterial synthesis and stabilization of metal nanoparticles. One of the chief applications of nanotechnology is the use of gold nanoparticles in biomedical research like X-ray computed tomography and magnetic resonance imaging [23], cancer nanotechnology [24], drug delivery applications [25], and its optical properties for cancer diagnosis and photo thermal therapy.
Herein, an eco-friendly method for the bacteria-mediated synthesis of gold nanoparticles by the reduction of HAuCl4 ions using the broth of Klebsiella pneumoniae is reported. The bioreduction process was monitored by the UV-visible spectroscopy, and the crystalline structure was investigated by the X-ray diffraction (XRD) technique. The nanostructure and size of the synthesized gold nanoparticles were characterized by transmission electron microscopy (TEM) and Fourier transformation infrared spectroscopy (FTIR) was used to understand the biomolecules responsible for the biosynthesis.
Results and discussion
Isolation and identification
The bacterial strain is used for the synthesis of gold nanoparticles which is isolated from the saltpan soil from Tuticorin. The isolate strain MAA was morphologically and biochemically identified as K. pneumoniae that produces a red pigment. K. pneumoniae MAA was a gram-positive rod-shaped non-motile bacterium that has to be identified and maintained at the Microbial Type Culture Collection and Gene Bank (MTCC), Chandigarh.
Synthesis of gold nanoparticles
Visual identification of gold nanoparticles
The detailed study on extracellular biosynthesis of gold nanoparticle by K. pneumoniae was carried out in this work. Figure 1a shows the biomass of K. pneumoniae without the addition of HAuCl4, and Figure 1b,c exhibits the HAuCl4-treated biomass incubated at 6 to 24 h. In the biomass of K. pneumoniae, the gold nanoparticle synthesis process was completed at 24 h. The color change from yellow to dark purple indicates the formation of gold nanoparticles at 24 h incubation time. The appearance of a dark-purple color at 24 h of incubation time confirms the reduction of gold chloride into gold NPs using the K. pneumoniae culture supernatant. The pink color in the solution at 6 h indicates that the gold nanoparticle synthesis process has started. After 24 h, there was no absorbance. The color of the colloidal solution reaction turned from yellow to purple which indicated the formation of gold nanoparticles upon using K. pneumoniae observed in the UV-vis spectra and also confirmed the completion of gold nanoparticle synthesis reaction in both bacteria. The color change is dependent upon the incubation time (6 to 24 h) and the shape of the nanoparticles. Similarly, the gold nanoparticles were synthesized by P. aeruginosa[26] and R. capsulate[27]. The colloidal solutions of gold nanoparticles show a very intense color, which is absent in the bulk material as well as for individual atoms. The origin is attributed to the collective oscillation of free conduction electrons by an interacting electromagnetic field. These resonances are called surface plasmon resonances [28].
UV-vis spectra of gold nanoparticles
The production and stabilization of the reduced gold nanoparticles in the colloidal solution was monitored by UV-vis spectrophotometer analysis. UV-vis spectroscopy is one of the most important techniques to identify the formation and stability of the gold nanoparticles in aqueous solution. Gold nanoparticles are known to exhibit at maximum in the range of 400 to 700 nm. The synthesis of gold nanoparticles was monitored at different time intervals such as 6, 12, 18, 24, 36, and 48 h. The gold nanoparticles synthesized by K. pneumoniae are positioned at 560 nm (Figure 2). Initially, at 6 h, the gold nanoparticle was absorbed slowly, and the absorbance was gradually increased up to 48 h. After 48 h, there was no absorbance which indicated that the gold NP synthesis process was completed. Similarly, Skirtach et al. (2005) reported that the gold NPs were absorbed at 560 nm, and it was synthesized using P. aeruginosa. The reduction of gold ions occurs comparatively slowly, but the gold nanoparticles are found to be very stable in the colloidal suspension. The spectrum shows three bands: one in the visible region and the other two in the NIR region, which is characteristic for the formation of anisotropic nanoparticles [29, 30]. It is well known that spherical nanoparticles of Au should exhibit single-surface plasmon bands whereas anisotropic particles should exhibit two or three bands, corresponding to the quadrupole and higher multipole plasmon excitations [31, 32].
XRD spectrum of gold nanoparticle
The crystalline nature of the gold nanoparticles was confirmed from X-ray diffraction analysis. The XRD pattern clearly shows that the extracellular synthesis of gold nanoparticles formed by the reduction of gold chloride ions using K. pneumoniae. Gold nanoparticles exhibited four prominent Bragg reflections at around 38.2°, 44.7°, 64.5°, and 78.3° (Figure 3) for K. pneumoniae. The fraction between the intensity of the (200), (220), and (311) diffraction peaks is much lower, suggesting that the (111) plane is the predominant orientation. The XRD facets of the gold nanoparticle match with standard gold which was published by JCPDS (file no. 04-0784). The mean size of gold nanoparticles was calculated using the Debye-Scherer equation by determining the width of the (111) and the similar Bragg reflection [33, 34]. R. capsulata was found to have an average size of 38 nm which matched with the particle sizes obtained from TEM results discussed later.
FTIR
The FTIR measurements were carried out to identify the possible biomolecules responsible for the reduction and capping of the reduced gold nanoparticles synthesized by S. nematodiphila and K. pneumoniae. The FTIR spectra of gold nanoparticles with absorption peaks 1,716, 1,670, 1,630, 1,526, 1,389, 1,239, and 1,037 cm-1 for K. pneumoniae are seen in Figure 4. The strong peak at 1,630 cm-1 are identified as C=O stretching vibrations due to the carbonyl stretch in proteins of the respective amide I group of proteins [35, 36]. The peak at 1,526 cm-1 shows the characteristic of N-O asymmetric stretching vibrations of nitro compounds. The small band at 1,670 cm-1 arises from the -C=C stretching vibrations corresponding to the -C=O stretching vibrations due to carboxylic acids and carbonyl groups [37, 38]. The small peak at 1,239 cm-1 can be assigned to the C-N stretching vibrations of aliphatic amine groups. Gold nanoparticles can bind to proteins through free amine groups or carboxylate groups in the protein. The presence of the intense peak at C=O stretching mode indicates the presence of carboxylic groups in the material bound to gold nanoparticles [39].
TEM and SAED pattern of gold nanoparticle
TEM analysis is performed to examine the size and shape of the biosynthesized gold nanoparticles using K. pneumoniae. Interestingly, the K. pneumoniae-derived gold nanoparticles exhibit a predominantly spherical shape (Figure 5). Such different sizes of gold nanoparticles are extracellularly synthesized by the bacteria R. capsulate, [34], fungus Sclerotium rolfsii, and plant Coriandrum sativum. The spherical-shaped nanoparticles are formed at the beginning of the reaction, and after that, the spherical-shaped nanoparticles are aggregated with each other. Due to the presence of enough amount of reducing agent in the biomass, the initially synthesized gold nanoparticles are stablilized in spherical shape, similar to the shape of nanoparticles synthesized by the bacteria K. planticola[40].
The single-crystalline nature of K. pneumoniae of these nanoparticles was further confirmed by their corresponding selected-area electron diffraction (SAED) analysis for K. pneumoniae. The SAED pattern of the spherical nanoparticle showed clear lattice fringes with bright circular rings corresponding to (111), (200), (220), and (311) planes. There are three sets of spots that could be identified from this diffraction pattern as shown in Figure 6. K. pneumoniae-derived gold nanoparticles also showed strong intensity at (111) plane of gold nanoparticles. Similarly, four concentric rings are observed in the gold nanoparticles indicating their crystalline nature, as reported by [39]. TEM analysis revealed that the synthesized gold nanoparticles are stable in solution.
Conclusion
The microbe-mediated biosynthesis of gold nanoparticles is non-toxic compared to all other reported methods. Also, the method has advantages: the process is easy since it can be scaled, and it is also economically possible. Reduction and surface accretion of metals may be processed, by which bacteria keep themselves from the toxic effects of metallic ions. In the present investigation, the gold nanoparticles were synthesized using K. pneumoniae which was isolated from saltpan soil and identified by MTCC. The synthesis of gold nanoparticles was confirmed by color change of the liquid medium from yellow to intense dark purple, and it exhibited its maximum absorbance at 560 nm which played a prominent role in the reduction of gold chloride to gold nanoparticles. The X-ray diffractometer showed the crystalline nature of nanoparticles. The Fourier transform infrared spectroscopy showed that the functional groups of gold nanoparticles can bind to proteins through free amine groups or carboxylate groups in the protein. The morphology of the gold nanoparticles are found to be spherical in shape and stable in water for 3 months that can be attributed to the surface binding of stabilization materials secreted by the bacteria. Gold colloidal solution is biologically well suited and has the potential to be used in medical and pharmaceutical applications due to their homologous size distribution.
Methods
Isolation and identification of microorganism
The organism was isolated from saltpan soil, and the sample was collected from Tuticorin. The collection of samples was serially diluted, and the isolates were morphologically and microbiologically characterized as Klebsiella pneumoniae. The isolated culture was identified as Klebsiella pneumoniae (MAA) from MTCC and maintained it by a subculture process for the synthesis of gold nanoparticles.
Extracellular synthesis of gold nanoparticle
K. pneumoniae (MAA) was grown in 100 ml nutrient broth and incubated at 35°C for 24 h. The overnight culture broth was centrifuged at 6,000 rpm for 10 min. The cell-free supernatants were collected, 1 mM of gold chloride was added and mixed, and the solution was incubated at 35°C for 24 h. The spectrum of the sample was measured using a UV-visible spectrophotometer.
Characterization of gold nanoparticle
UV-vis spectrophotometer
The bioreduction of pure HAuCl4 are monitored using UV-vis spectroscopy at regular intervals. During the reduction, 0.1 ml of samples was taken and diluted several times with millipore water. After dilution, it was centrifuged at 800 rpm for 5 min. The supernatant was scanned using a UV-300 spectrophotometer (UNICAM, York Street, Cambridge, Cambridgeshire) for a UV-vis 1601 Schimodzu spectrophotometer (Kyoto, Japan), operated at a resolution of 420 nm.
X-ray diffractometer
X-ray diffraction (Bruker, Karlsruhe, Germany) is one of the important techniques for the structure characterization of the crystalline material. Prepared nanoparticles can be analyzed by this instrument using the lynx eye detector (silicon strip detector technology).
Transmission electron microscopy
Transmission electron microscopy (TEM) analysis of the sample was done using a Philips CM 200 instrument (Philips, Amsterdam, The Netherlands) operated at an accelerating voltage of 200 kV with a resolution of 0.23 nm. A drop of the solution was placed on carbon-coated copper grid and later exposed to infrared light (45 min) for solvent evaporation.
FTIR
A known weight of sample (1 mg) was taken in a mortar and pestle and ground with 2.5 mg of dry potassium bromide (KBr). The powder so obtained was filled in a 2-mm internal diameter microcup and loaded onto the FTIR set at 26°C ± 1°C. The samples were scanned in the range of 4,000 to 400 cm-1 using a Fourier transform infrared spectrometer (Thermo Nicolet Model‒6700, Waltham, MA, USA). The spectral data obtained were compared with the reference chart to identify the functional groups present in the sample.
Authors’ information
CM completed her B.Sc. in Zoology and M.Sc. Environmental Biotechnology in Sri Paramakalyani Centre for Environmental Sciences, Manonmaniam Sundaranar University, Alwarkurichi, Tirunelveli. She achieved her Ph.D. degree under the guidance of GA in the field of nanotechnology. Her research interests include synthesis of semiconductor nanomaterials and metal nanoparticles and its biomedical applications. SR completed his M.Sc. Biotechnology in Periyar University and obtained his Ph.D. degree in Nanotechnology under the guidance of GA. He published seven research articles in nanoparticle synthesis using algae. He is interested in the metallic nanoparticle synthesis using algae and algae-derived compounds and their potential applications in the biomedical field. VM obtained her M.Sc. in Environmental Biotechnology in Sri Paramakalyani Centre for Environmental Sciences, Manonmaniam Sundaranar University, Alwarkurichi, Tirunelveli. She obtained her Ph.D. degree under the guidance of GA in the field of nanotechnology. Her research interests include eco-friendly synthesis of nanoparticles and its application in the environment. KP received his B.Sc. (2005) and M.Sc. in Biotechnology (2007) from Madurai Kamaraj University and Periyar University, India, respectively. He is currently working to obtain his Ph.D. degree at Manonmaniam Sundaranar University in India. He is interested in the green and immobilized microbe-mediated synthesis process of nanoparticles and nanocomposites and their biomedical and textile industry applications. GG completed her M.Sc. in Biotechnology in Periyar University and obtained her Ph.D. degree in Nanotechnology under the guidance of GA. Her research interests include green-meditated synthesis of nanoparticles and its agricultural applications for controlling plant diseases. GA received his M.Sc. in Applied Chemistry (1992) and Ph.D. in Environmental Biotechnology (1997) from Anna University, India. He had ten years (1999 to 2008) post-doctoral experiences from the National Taiwan University in Taiwan, National Institute of Advanced Industrial Science and Technology in Japan, and National Central University in Taiwan. He has received many research awards from Indian and other country governments. He is an associate editor in five international journals. At present, he is an associate professor of the Environmental Biotechnology and the leader of Environmental Nanobiotechnology Division at Sri Paramakalyani Centre for Environmental Sciences, Manonmaniam Sundaranar University, India. His main research interest is on the biosynthesis of nanoparticles and nanomaterials, nanobiocatalyst, and environmental chemistry.
References
Mohanpuria P, Ran KN, Yadav SK: Biosynthesis of nanoparticles: technological concepts and future applications. J. Nanopart. Res. 2008, 10: 507–517. 10.1007/s11051-007-9275-x
Yuqing M, Sun K, Qiu J, Liu J: Preparation and characterization of gold nanoparticles using ascorbic acid as reducing agent in reverse micelles. J. Mater. Sci. 2009, 44: 754–758. 10.1007/s10853-008-3162-4
Rao CNR, Muller A, Cheetham AK: The Chemistry of Nanomaterials: Synthesis. Properties and Applications, Wiley VCH, Weinheim; 2004.
Moreno-Álvarez SA, Martínez-Castañón GA, Niño-Martínez N, Reyes-Macías JF, Patiño-Marín N, Loyola-Rodríguez JP, Ruiz F: Preparation and bactericide activity of gallic acid stabilized gold nanoparticles. J. Nanopart. Res. 2010, 12: 2741–2746. 10.1007/s11051-010-0060-x
Oshavsky MA, Allcock HR: Small scale system for in-vivo drug delivery. Chem. Mater. 1997, 9: 1367. 10.1021/cm960584x
Malarkodi C, Annadurai G: A novel biological approach on extracellular synthesis and characterization of semiconductor zinc sulfide nanoparticles. Appl. Nanosci. 2012. 10.1007/s13204-012-0138-0
Gnanajobitha G, Annadurai G, Kannan C: Green synthesis of silver nanoparticle using Elettaria cardamomom and assesment of its antimicrobial activity. Int. J. Pharma Sci. Res. (IJPSR) 2012, 3: 323–330.
Rajeshkumar S, Kannan C, Annadurai G: Synthesis and characterization of antimicrobial silver nanoparticles using marine brown seaweed Padina tetrastromatica . Drug Invention Today 2012, ISSN: 0975–7619.
Karthiga P, Soranam R, Annadurai G: Alpha-mangostin, the major compound from Garcinia mangostana linn. responsible for synthesis of Ag nanoparticles: its characterization and evaluation studies. Research Journal of Nanoscience and Nanotechnology 2012, 2: 46–57. 10.3923/rjnn.2012.46.57
Klaus T, Joerger R, Olsson E, Granqvist CG: Silver-based crystalline nanoparticles, microbially fabricated. Proc. Natl. Acad. Sci. U. S. A. 1999, 96: 13611–13614. 10.1073/pnas.96.24.13611
Ahmad A, Senapati S, Khan MI, Kumar R, Sastry M: Extracellular biosynthesis of monodisperse gold nanoparticles by a novel extremophilic actinomycete. Thermomonospora sp. Langmuir 2003, 19: 3550–3553. 10.1021/la026772l
Nair B, Pradeep T: Coalescence of nanoclusters and formation of submicron crystallites assisted by Lactobacillus strains. Crystal Growth and Design 2002,2(4):293–298. 10.1021/cg0255164
Konishi Y, Ohno K, Saitoh N, Nomura T, Nagamine S: Microbial synthesis of gold nanoparticles by metal reducing bacterium. Transactions of the Materials Research Society of Japan 2004, 29: 2341–2343.
Bharde A, Wani A, Shouche Y, Pattayil A, Bhagavatula L, Sastry M: Bacterial aerobic synthesis of nanocrystalline magnetite. J. Am. Chem. Soc. 2005,127(26):9326–9327. 10.1021/ja0508469
Lengke MF: Ravel, B, Fleet, ME, Wanger, G, Gordon, RA, Southam, G: Mechanisms of gold bioaccumulation by filamentous cyanobacteria from gold (III)-chloride complex. Environ. Sci. Technol. 2006,40(20):6304–6309. 10.1021/es061040r
Shiying H, Zhirui G, Zhanga Y, Zhanga S, Wanga J, Ning G: Biosynthesis of gold nanoparticles using the bacteria Rhodopseudomonas capsulate . Material Letters 2007,61(18):3984–3987. 10.1016/j.matlet.2007.01.018
Yasuhiro K, Kaori O, Norizoh S, Toshiyuki N, Shinsuke N, Hajime H, Yoshio T, Tomoya U: Bioreductive deposition of platinum nanoparticles on the bacterium Shewanella algae. J. Biotechnol. 2007, 128: 648–653. 10.1016/j.jbiotec.2006.11.014
Law N, Ansari S, Livens FR, Renshaw JC, Lloyd JR: The formation of nano-scale elemental silver particles via enzymatic reduction by Geobacter sulfurreducens . Appl. Environ. Microbiol. 2008, 74: 7090–7093. 10.1128/AEM.01069-08
Parikh RP: Singh, S, Prasad, BLV, Patole, MS, Sastry, M, Shouche. YS: Extracellular synthesis of crystalline silver nanoparticles and molecular evidence of silver resistance from Morganella sp: towards understanding biochemical synthesis mechanism. Chembiochem 2008,9(9):1415–1422.
Saifuddin N, Wong CW, Nuryasumira AA: Rapid biosynthesis of silver nanoparticles using culture supernatant of bacteria with microwave irradiation. E-Journal of Chemistry 2009, 6: 61–70. 10.1155/2009/734264
Nanda A, Saravanan M: Biosynthesis of silver nanoparticles from Staphylococcus aureus and its antimicrobial activity against MRSA and MRSE. Nanomedicine: Nanotechnology, Biology and Medicine 2009, 5: 452–456. 10.1016/j.nano.2009.01.012
Bao H, Lu Z, Cui X, Guo J, Anderson JM, Li CM: Extracellular microbial synthesis of biocompatible CdTe quantum dot. Acta Biomater. 2010,6(9):3534–3541. 10.1016/j.actbio.2010.03.030
Alric C, Taleb J, Le Duc G, Mandon C, Billotey C, Meur-Herland AL, Brochard T, Vocanson F, Janier M, Perriat P, Roux S, Tillement O: Gadolinium chelate coated gold nanoparticles as contrast agents for both X-ray computed tomography and magnetic resonance imaging. J. Am. Che. Soc. 2008, 138: 5908–5915.
Cail W, Gao T, Hong H, Sun J: Applications of gold nanoparticles in cancer nanotechnology. Nanotechnol. Sci. Appl. 2008, 1: 17–32.
Ghosh P, Han G, De M, Kim CK, Rotello VM: Gold nanoparticles in delivery applications. Adv. Drug Deliv. Rev. 2008, 60: 1307–1315. 10.1016/j.addr.2008.03.016
Husseiny MI, Abd El-Aziz M, Badr Y, Mahmoud MA: Biosynthesis of gold nanoparticles using Pseudomonas aeruginosa . Spectrochimica Acta Part A 2007, 67: 1003–1006. 10.1016/j.saa.2006.09.028
Wang H, Xu K, Liu L, Tan JP, Chen Y, Li Y, Fan W, Wei Z, Sheng J, Yang YY, Li L: The efficacy of self-assembled cationic antimicrobial peptide nanoparticles against Cryptococcus neoformans for the treatment of meningitis. Biomaterials 2010,31(10):2874–2881. 10.1016/j.biomaterials.2009.12.042
Smitha SL, Philip D, Gopchandrana KG: Green synthesis of gold nanoparticles using Cinnamomum zeylanicum leaf broth. Spectrochimica Acta Part A 2009, 74: 735–739. 10.1016/j.saa.2009.08.007
Liz LM, Tailoring M: Surface plasmons through the morphology and assembly of Metal nanoparticles. Langmuir 2006, 22: 32. 10.1021/la0513353
Skirtach AG, Dejugnat C, Braun D, Susha AS, Rogach AL, Parak WJ, Mohwald H, Sukhorukov GB: The role of metal nanoparticles in remote release of encapsulated. Nano Lett. Materials 2005, 5: 1371–1377. 10.1021/nl050693n
Murphy TK, Sau AM, Gole CJ, Orendorff J, Gao L, Gou SE, Hunyadi T: Li: Measurement of lactose crystallinity using Raman spectroscopy. J. Pharm. Biomed. 2005, 38: 186–190. 10.1016/j.jpba.2004.12.013
Xu W, Wang Y, Xu R, Liang S, Zhang G, Yin D: Synthesis and fluorescence spectrum analysis of CdS nanocrystals. J. Mat. Sci. 2007, 42: 6942–6945. 10.1007/s10853-006-1332-9
Kasthuria , Veerapandian S, Rajendiran N: Biological synthesis of silver and gold nanoparticles using apiin as reducing agent. Colloids Surf. B Biointerfaces 2009, 68: 55–60. 10.1016/j.colsurfb.2008.09.021
He S, Guo Z, Zhang Y, Zhang S, Wang J, Gu N: Biosynthesis of gold nanoparticles using the bacteria Rhodopseudomonas capsulate . Mater. Lett. 2007, 61: 3984–3987. 10.1016/j.matlet.2007.01.018
Narayanan KB, Sakthivel N: Coriander leaf mediated biosynthesis of gold nanoparticles. Mater. Lett. 2008, 62: 4588–4590. 10.1016/j.matlet.2008.08.044
Rajeshkumar S, Kannan C, Annadurai G: Green synthesis of silver nanoparticles using marine brown algae Turbinaria conoides and its antibacterial activity. J. Pharm. Bio. Sci. 2012,3(4):502–510.
Rajeshkumar S, Kannan C, Annadurai G: Synthesis and characterization of antimicrobial silver nanoparticles using marine brown seaweed Padina tetrastromatica . Drug Invention Today 2012, 4: 511–513.
Gnanajobitha G, Vanaja M, Paulkumar K, Rajeshkumar S, Malarkodi C, Annadurai G, Kannan C: Green synthesis of silver nanoparticles using Millingtonia hortensis and evaluation of their antimicrobial efficacy. International Journal of Nanomaterials and Biostructures 2013,3(1):21–25.
Philip D: Biosynthesis of Au, Ag and Au–Ag nanoparticles using edible mushroom extract. Spectrochimica Acta Part A 2009, 73: 374–381. 10.1016/j.saa.2009.02.037
Paulkumar K, Rajeshkumar S, Gnanajobitha G, Vanaja M, Malarkodi C, Annadurai G: Eco-friendly synthesis of silver chloride nanoparticles using Klebsiella planticola (MTCC 2277). International Journal of Green Chemistry and Bioprocess 2013,3(1):12–16.
Acknowledgements
CM thanks UGC, India for the financial support under the Rajiv Gandhi National Fellowship (Sanction Letter no. F. 14-2(SC)/2009 (SA-III) -09/2010) and IIT Bombay University for the TEM analyses.
Author information
Authors and Affiliations
Corresponding author
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors’ contributions
CM and SR carried out the nanoparticle synthesis. MV and KP carried out the manuscript preparation. GG carried out the antimicrobial activity. All authors read and approved the final manuscript.
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License ( https://creativecommons.org/licenses/by/2.0 ), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Malarkodi, C., Rajeshkumar, S., Vanaja, M. et al. Eco-friendly synthesis and characterization of gold nanoparticles using Klebsiella pneumoniae. J Nanostruct Chem 3, 30 (2013). https://doi.org/10.1186/2193-8865-3-30
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/2193-8865-3-30