Abstract
Resistive-type structures based on gallium-oxide films are studied. The Ga2O3 films are produced by radio-frequency magnetron-assisted sputtering of a β-Ga2O3 (99.9999%) target onto unheated sapphire substrates with preliminarily deposited platinum electrodes. The data on the structure and phase composition of the films are obtained immediately after sputtering and after annealing in argon at 900°C for 30 min. The current–voltage characteristics are recorded in the dark and upon exposure to radiation at the wavelength λ = 254 nm. It is shown that, after annealing, the photocurrent increases by an order of magnitude. The lack of sensitivity of the structures to radiation in the visible wavelength region (λ = 400 nm) is verified experimentally.
Similar content being viewed by others
REFERENCES
E. Monroy, F. Omnes, and F. Calle, Semicond. Sci. Technol. 18, 33 (2003).
Z. Y. Xu and B. M. Sadler, IEEE Commun. Mag. 46, 67 (2008).
S. Aslam, F. Yan, D. E. Pugel, D. Franz, L. Miko, F. Herrero, M. Matsumara, S. Babu, and C. M. Stahle, Proc. SPIE 5901, 59011J-1 (2005).
Z. G. Shao, D. J. Chen, H. Lu, R. Zhang, D. P. Cao, W. J. Luo, Y. D. Zheng, L. Li, and Z. H. Li, IEEE Electron. Dev. Lett. 35, 372 (2014).
A. Balducci, M. Marinelli, E. Milani, M. E. Morgada, A. Tucciarone, G. Verona-Rinati, M. Angelone, and M. Pillon, Appl. Phys. Lett. 86, 193509 (2005).
J. Yu, C. X. Shan, J. S. Liu, X. W. Zhang, B. H. Li, and D. Z. Shen, Phys. Status Solidi RRL 7, 425 (2013).
K. Balakrishnan, A. Bandoh, M. Iwaya, S. Kamiyama, H. Amano, and I. Akasaki, Jpn. J. Appl. Phys. 46, L307 (2007).
W. Yang, S. S. Hullavarad, B. Nagaraj, I. Takeuchi, R. P. Sharma, T. Venkatesan, R. D. Vispute, and H. Shen, Appl. Phys. Lett. 82, 3424 (2003).
Y. Tomm, P. Reiche, D. Klimm, and T. Fukuda, J. Cryst. Growth 220, 510 (2000).
E. Ohba, T. Kobayashi, M. Kado, and K. Hoshikawa, Jpn. J. Appl. Phys. 55, 1202BF (2016).
H. He, R. Orlando, M. A. Blanco, R. Pandey, E. Amzallag, I. Baraille, and M. Rérat, Phys. Rev. 74, 195123 (2006).
R. Suzuki, S. Nakagomi, Y. Kokubun, N. Arai, and S. Ohira, Appl. Phys. Lett. 94, 222102 (2009).
S. Nakagomi, T. Momo, S. Takahashi, and Y. Kokubun, Appl. Phys. Lett. 103, 072105 (2013).
S. Oh, Y. Jung, M. A. Mastro, J. K. Hite, C. R. Eddy, Jr., and J. Kim, Opt. Express 23, 28300 (2015).
S. I. Stepanov, V. I. Nikolaev, V. E. Bougrov, and A. E. Romanov, Rev. Adv. Mater. Sci. 44, 63 (2016).
M. J. Tadjer, M. A. Mastro, N. A. Mahadik, M. Currie, V. D. Wheeler, J. A. Freitas, Jr., J. D. Greenlee, J. K. Hite, K. D. Hobart, C. R. Eddy, Jr., and F. J. Kub, J. Electron. Mater. 45, 2031 (2016).
S. J. Pearton, J. Yang, P. H. Cary, F. Ren, J. Kim, M. J. Tadjer, and M. A. Mastro, Appl. Phys. Rev. 5, 011301 (2018).
X. Chen, F. Ren, S. Gu, and J. Ye, Photon. Res. 7, 381 (2019).
Y. Qin, S. Long, H. Dong, Q. He, G. Jian, Y. Zhang, X. Hou, P. Tan, Z. Zhang, H. Lv, Q. Liu, and M. Liu, Chin. Phys. B 28, 018501 (2019).
A. Tsymbalov and J. Petrova, J. Phys.: Conf. Ser. 124, 071004 (2018).
Funding
The study was supported by the Russian Science Foundation, project no. 16-13-06001 (Tomsk State University, Russia) and the Deutsches Elektronen-Synchrotron research center (DESY, Germany), project no. HRSF-0004.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
The authors declare that they have no conflict of interest.
Additional information
Translated by E. Smorgonskaya
Rights and permissions
About this article
Cite this article
Kalygina, V.M., Almaev, A.V., Novikov, V.A. et al. Solar-Blind UV Detectors Based on β-Ga2O3 Films. Semiconductors 54, 682–686 (2020). https://doi.org/10.1134/S1063782620060093
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S1063782620060093