The degradation and bulk failure of a polycrystalline interconnect line caused by vacancy electromigration along grain boundaries and vacancy-cluster nucleation at triple points in the bulk conductor are investigated within the general theory of the electromigration-induced degradation and failure of thin-film on-chip interconnect lines, presented in Part 1 [1]. The general equations are tailored to deal with vacancy electromigration, mechanical-stress generation, and void nucleation at triple points. Appropriate boundaryvalue problems are formulated, and numerical methods and procedures to solve them are developed and implemented in software. Computer simulations are performed to identify a pattern of electromigration failure at triple points. On this basis, (1) interconnect lifetime is investigated over wide ranges of variation of material, structural, geometric, and operating parameters, and (2) the current-density and temperature dependence—of the mechanical stress, vacancy concentration, and level of vacancy supersaturation at a triple point, and of void radius and time to nucleation-is examined and explained. The simulation results are found to agree well with previous experiments. This investigation could be seen as a natural continuation of our study of electromigration failures developed by multilevel-metallization systems as a result of interconnect failure near via junctions or at open ends [1]. Together they cover most mechanisms of electromigration failure suffered by metallization systems.
Similar content being viewed by others
References
Valiev, K.A., Goldstein, R.V., Zhitnikov, Yu.V., Makhviladze, T.M., and Sarychev, M.E., Nanoand Micrometer-Scale Thin-Film-Interconnection Failure Theory and Simulation and Metallization Lifetime Prediction, Part 1: A General Theory of Vacancy Transport, Mechanical-Stress Generation, and Void Nucleation under Electromigration in Relation to Multilevel-Metallization Degeneration and Failure, Mikroelektronika, 2009, vol. 38, no. 6, pp. 404–427 [Russ. Microelectron. (Engl. Transl.), vol. 38, no. 6, pp. 364–384].
Makhviladze, T.M. and Sarychev, M.E., Electromigration Failure of Thin-Film Interconnections: A Theory and Its Applications, in Tr. FTIAN, 2009, vol. 20.
Goldstein, R.V., Makhviladze, M.E., and Sarychev, M.E., Modeling Reliability and Mechanisms of Destruction of Metallization and Interconnects in Micro- and Nanoelectronic Structures, in Nanotechnology International Forum, Abstracts, Scientific and Technological Sections, Moscow, 2008, vol. 2, pp. 140–142.
Makhviladze, T.M., Sarychev, M.E., and Zhitnikov, Yu.V., A Model for Calculations of Effective Ion Charges in Microcircuit Interconnects, in Proc. Int. Conf. on IC Design and Technology (ICICDT), Grenoble, 2008, pp. G17–G20.
Makhviladze, T. and Sarychev, M., New Results of Modeling in Micro- and Nanoelectronics, in Int. Conf. on IC Micro- and Nanoelectronics (ICMNE-2007), Book of Abstracts, Moscow, 2007, p. L1–06.
Makhviladze, T. and Sarychev, M., Electromigration Theory and Its Applications to Integrated Circuit Metallization, in Int. Conf. on IC Micro- and Nanoelectronics (ICMNE-2009), Book of Abstracts, Moscow, 2009.
Hinode, K., Kondo, S., and Deguchi, O., Number of Voids Formed on a Line: Parameter for Electromigration Life-time, J. Vac. Sci. Technol., B, 1996, vol. 14, pp. 687–690.
Fukada, S., Hirasawa, M., and Suzuki, M., Electromigration Resistance Measurements of Multilayered Interconnections by Short Test Lines, Jpn. J. Appl. Phys., 1995, vol. 34, pp. 1001–1006.
Nikawa, K., Matsumoto, C., and Inoue, S., Novel Method for Defect Detection in Al Stripes by Means of Laser Beam Heating and Detection of Changes in Electrical Resistance, Jpn. J. Appl. Phys., 1995, vol. 34, pp. 2260–2265.
Sasagava, K., Hasegava, M., Saka, M., and Abe, H., Prediction of Electromigration Failure in Passivated Polycrystalline Line, J. Appl. Phys., 2002, vol. 91, no. 11, pp. 9005–9014.
Kraft, P.S. and Arzt, E., Current Density and Line Width Effects in Electromigration: A New Damage-Based Model, Acta Mater., 1998, vol. 46, no. 11, pp. 3733–3743.
Makhviladze, T.M., Sarychev, M.E., and Zhitnikov, Yu.V., Modeling of Electromigration and Void Nucleation Kinetics in Polycrystalline Metal Lines, in Proc. IPT RAS: Modeling and Simulation of Submicron Technology and Devices, 1997, vol. 13, pp. 98–114.
Makhviladze, T.M., Sarychev, M.E., Zhitnikov, Yu.V., Borucki, L., and Liu, C.-L., General Model for Mechanical Stress Evolution during Electromigration, J. Appl. Phys., 1999, vol. 86, no. 6, pp. 3068–3075.
Makhviladze, T.M., Sarychev, M.E., Zhitnikov, Yu.V., Borucki, L., and Liu, C.-L., A New, General Model for Mechanical Stress Evolution during Electromigration, Thin Solid Films, 2000, vol. 365, pp. 211–218.
Bokshtein, B.S., Diffuziya v metallakh (Diffusion in Metals), Moscow: Metallurgiya, 1978.
Russell, K.C., Nucleation of Voids in Irradiated Metals, Acta Metall., 1971, vol. 19, pp. 753–758.
Russell, K.C., The Theory of Void Nucleation in Metals, Acta Metall., 1978, vol. 26, pp. 1615–1630.
Kondo, S., Deguchi, O., and Hinode, K., Effects of Grain Size and Preferred Orientation on the Electromigration Lifetime of Al-Based Layered Metallization, J. Appl. Phys., 1995, vol. 78, pp. 6534–6538.
Marieb, T., Flinn, P., and Bravman, J.C., Observations of Electromigration Induced Void Nucleation and Growth in Polycrystalline and Near-Bamboo Passivated Al-Lines, J. Appl. Phys., 1995, vol. 78, pp. 1026–1032.
Park, J.H. and Ahn, B.T., Electromigration Model for the Prediction of Lifetime Based on the Failure Unit in Aluminum Metallization, J. Appl. Phys., 2003, vol. 93, no. 2, pp. 883–892.
Sasagava, K., Nakamura, N., Saka, M., and Abe, H., A New Approach to Calculate Atomic Flux Divergence by Electromigration, Trans. ASME, 1998, vol. 120, no. 12, pp. 360–366.
Abe, H., Sasagava, K., and Saka, M., Electromigration Failure of Metal Lines, Int. Fracture, 2006, vol. 138, no. 1, pp. 219–240.
Author information
Authors and Affiliations
Corresponding author
Additional information
Original Russian Text © K.A. Valiev, R.V. Goldstein, Yu.V. Zhitnikov, T.M. Makhviladze, M.E. Sarychev, 2010, published in Mikroelektronika, 2010, Vol. 39, No. 3, pp. 163–177.
Rights and permissions
About this article
Cite this article
Valiev, K.A., Goldstein, R.V., Zhitnikov, Y.V. et al. Nano- and micrometer-scale thin-film-interconnection failure theory and simulation and metallization lifetime prediction, Part 2: Polycrystalline-line degradation and bulk failure. Russ Microelectron 39, 145–157 (2010). https://doi.org/10.1134/S1063739710030017
Received:
Published:
Issue Date:
DOI: https://doi.org/10.1134/S1063739710030017