Phase equilibria in the MnSe–Ga2Se3 system were re-investigated by differential thermal analysis (DTA) and X-ray powder diffraction (XRD), and a phase diagram was constructed, somewhat differing from that presented earlier in the literature. We found that the system featured the formation of an intermediate phase (γ) with a wide (47–61 mol % Ga2Se3) homogeneity extent. Extensive (~30 mol %) Ga2Se3-base solid solutions were also found. The γ phase undergoes γ′ ↔ γ polymorphic transformation at 1183–1193 K, the temperature depending on the composition. The γ′ high-temperature phase has a minimum melting point at 1205 K and 55 mol % Ga2Se3, and it is in peritectic equilibrium with terminal solid solutions. The tetragonal lattice parameters of the γ phase containing 50 and 60 mol % Ga2Se3 were determined based on X-ray powder diffraction data. The previously indicated ternary compound Mn2Ga2Se5 was not confirmed to exist. A comparative analysis of the results against the related literature was carried out.
Similar content being viewed by others
REFERENCES
K. Hyunjung, A. P. Tiwari, E. Hwang, et al., Adv. Sci. 5, 1800068 (2018). https://doi.org/10.1002/advs.201800068
C. Xia and J. Li, J. Semicond. 37, 051001 (2016). https://doi.org/10.1088/1674-4926/37/5/051001
P. Wyżga, I. Veremchuk, M. Bobnar, et al., Z. Anorg. Allg. Chem. 646, 1091 (2020). https://doi.org/10.1002/zaac.202000014
N. Karthikeyan, G. Aravindsamy, P. Balamurugan, et al., Mater. Res. Innov. 22, 278 (2018). https://doi.org/10.1080/14328917.2017.1314882
A. Bose, R. Banerjee, and A. Narayan, Condens. Matter 2, 1 (2022). https://arxiv.org/pdf/2202.03317v2.pdf.
J. Yang, Z. Zhou, J. Fang, et al., Appl. Phys. Lett. 115, 222101 (2019). https://doi.org/10.1063/1.5126233
Y. Hwang, J. Choi, Y. Ha, et al., Curr. Appl. Phys. 20, 212 (2020). https://doi.org/10.1016/j.cap.2019.11.005
V. Sagredo, T. E. Torres, G. E. Delgado, et al., Rev. Mex. F 65, 14 (2019). www.scielo.org.mx/scielo.php?script= sci_arttext&pid=S0035-001X2019000100014.
B. Zhang, Y. Liu, H. Zhu, et al., Environ. Sci. Pollut. Res. 30, 13438 (2023). https://doi.org/10.1007/s11356-022-22929-6
S. A. Pauliukavets, I. V. Bychek, and M. P. Patapovich, Inorg. Mater: Appl. Res. 9, 207 (2018). https://doi.org/10.1134/S2075113318020223
H. Kim, X. Liu, M. Kim, et al., Chem. Mater. 33, 164 (2021). https://doi.org/10.1021/acs.chemmater.0c03146
S. V. Eremeev, M. M. Otrokov, and E. V. Chulkov, Nano Lett. 18, 6521 (2018). https://doi.org/10.1021/acs.nanolett.8b03057
M. M. Otrokov, I. I. Klimovskikh, H. Bentmann, et al., Nature 576, 416 (2019). https://doi.org/10.1038/s41586-019-1840-9
L. Haoyu, H. Yiya, G. Qixun, et al., J. Phys. D: Appl. Phys. 56, 045302 (2023). https://doi.org/10.1088/1361-6463/aca61e
I. I. Klimovskikh, M. M. Otrokov, D. Estyunin, et al., npj Quantum Mater. 5, 54 (2020). https://doi.org/10.1038/s41535-020-00255-9
D. A. Estyunin, I. I. Klimovskikh, A. M. Shikin, et al., APL Mater. 8, 021105 (2020). https://doi.org/10.1063/1.5142846
R. C. Walko, T. Zhu, A. J. Bishop, et al., Phys. E 143, 115391 (2022). https://doi.org/10.1016/j.physe.2022.115391
Y. Yonghao, W. Xintong, L. Hao, et al., Nano Lett. 20, 3271 (2020). https://doi.org/10.1021/acs.nanolett.0c00031
L. Zhou, Z. Tan, D. Yan, et al., Phys. Rev. B: Condens. Matter 102, 085114 (2020). https://doi.org/10.1103/PhysRevB.102.085114
K. F. Garrity, S. Chowdhury, and F. M. Tavazza, Phys. Rev. Mater. 5, 024207 (2021). https://doi.org/10.1103/PhysRevMaterials.5.024207
D. Ovchinnikov, X. Huang, Z. Lin, et al., Nano Lett. 21, 2544 (2021). https://doi.org/10.1021/acs.nanolett.0c05117
P. Swatek, Y. Wu, and L. L. Wang, Phys. Rev. B: Condens. Matter 101, 161109 (2020). https://doi.org/10.1103/PhysRevB.101.161109
T. Zhu, A. J. Bishop, T. Zhou, et al., Nano Lett. 21, 5083 (2021). https://doi.org/10.1021/acs.nanolett.1c00141
M. Garnica, M. Otrokov, P. C. Aguilar, et al., npj Quantum Mater. 7, 7 (2022). https://doi.org/10.1038/s41535-021-00414-6
A. Sharan, M. Sajjad, D. J. Singh, et al., Phys. Rev. Mater. 6, 094005 (2022). https://doi.org/10.1103/PhysRevMaterials.6.094005
A. V. Tarasov, T. P. Makarova, D. A. Estyunin, et al., Symmetry 15, 469 (2023). https://doi.org/10.3390/sym15020469
H. Djieutedjeu, J. S. Lopez, R. Lu, et al., J. Am. Chem. Soc. 141, 9249 (2019). https://doi.org/10.1021/jacs.9b01884
I. Levy, C. Forrester, X. Ding, et al., Sci. Rep. 13, 7381 (2023). https://doi.org/10.1038/s41598-023-34585-y
N. A. Moroz, J. S. Lopez, H. Djieutedjeu, et al., Chem. Mater. 28, 8570 (2016). https://doi.org/10.1021/acs.chemmater.6b03293
I. Levy, C. Forrester, H. Deng, et al., Cryst. Growth Des. 22, 3007 (2022). https://doi.org/10.1021/acs.cgd.1c01453
Y. Liu, Ch. Kang, E. Stavitski, et al., Phys. Rev. 97, 155202 (2018). https://doi.org/10.1103/PhysRevB.97.155202
M. B. Babanly, E. V. Chulkov, Z. S. Aliev, et al., Russ. J. Inorg. Chem. 62, 1703 (2017). https://doi.org/10.1134/S0036023617130034
M. B. Babanly, L. F. Mashadiyeva, D. M. Babanly, et al., Russ. J. Inorg. Chem. 64, 1649 (2019). https://doi.org/10.1134/S0036023619130035
S. Z. Imamaliyeva, D. M. Babanly, V. A. Qasymov, et al., Russ. J. Inorg. Chem. 66, 558 (2021). https://doi.org/10.1134/S0036023621040124
F. M. Mammadov, I. R. Amiraslanov, S. Z. Imamaliyeva, et al., J. Phase Equilib. Diffus. 40, 787 (2019). https://doi.org/10.1007/s11669-019-00768-2
F. M. Mamedov, D. M. Babanly, I. R. Amiraslanov, et al., Russ. J. Inorg. Chem. 65, 1747 (2020). https://doi.org/10.1134/S0036023620110121
F. M. Mammadov, I. R. Amiraslanov, Y. R. Aliyeva, et al., Acta Chim. Slovenica 66, 466 (2019). https://doi.org/10.17344/acsi.2019.4988
F. M. Mammadov, D. M. Babanly, I. R. Amiraslanov, et al., Russ. J. Inorg. Chem. 66, 1533 (2021). https://doi.org/10.1134/S0036023621100090
F. M. Mammadov, N. N. Niftiev, Ya. I. Jafarov, et al., Russ. J. Inorg. Chem. 67, 1623 (2022). https://doi.org/10.1134/S0036023622600769
M. P. Pardo and J. Flahaut, Mater. Res. Bull. 13, 1231 (1978). https://doi.org/10.1016/0025-5408(78)90214-3
P. K. Babaeva and P. G. Rustamov, Research in Inorganic and Physical Chemistry (Elm, Baku, 1981) [in Russian].
Phase Diagrams of Binary Metal Systems, Ed. by N. R. Lyakishev (Mashinostroenie, Moscow, 2001) [in Russian].
T. B. Massalski, Binary Alloy Phase Diagrams (ASM International, Materials Park, Ohio, 1990).
N. Kh. Abrikosov, V. F. Bankina, L. V. Poretskaya, et al., Semiconductor Chalcogenides and Alloys Based on Them (Nauka, Moscow, 1975) [in Russian].
M. Cannas, L. Garbato, LehmannA. Geddo, et al., Cryst. Res. Technol. 33, 417 (1998). https://doi.org/10.1002/(SICI)1521-4079(1998)33:3<417::AID-CRAT417>3.0.CO;2-2
Funding
This work was supported by ongoing institutional funding. No additional grants to carry out or direct this particular research were obtained.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
The authors declare that they are not aware of competing financial or other interests or personal relationships that could influence the work presented in this paper.
Additional information
Translated by O. Fedorova
Publisher’s Note.
Pleiades Publishing remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Mammadov, F.M., Agayeva, R.M., Amiraslanov, I.R. et al. Revised Phase Diagram of the MnSe–Ga2Se3 System. Russ. J. Inorg. Chem. (2024). https://doi.org/10.1134/S0036023623602611
Received:
Revised:
Accepted:
Published:
DOI: https://doi.org/10.1134/S0036023623602611