Abstract
In this work, we have successfully fabricated bottom gate fully transparent tin-doped zinc oxide thin film transistors (TZO TFTs) fabricated on flexible plastic substrate at low temperature by RF magnetron sputtering. The effect of O2/Ar gas flow ratio during channel deposition on the electrical properties of TZO TFTs was investigated, and we found that the O2/Ar gas flow ratio have a great influence on the electrical properties. TZO TFTs on flexible substrate has very nice electrical characteristics with a low off-state current (Ioff) of 3 pA, a high on/off current ratio of 2 × 107, a high saturation mobility (μsat) of 66.7 cm2/V•s, a steep subthreshold slope (SS) of 333 mV/decade and a threshold voltage (Vth) of 1.2 V. Root-Mean-Square (RMS) roughness of TZO thin film is about 0.52 nm. The transmittance of TZO thin film is about 98%. These results highlight that the excellent device performance can be realized in TZO film and TZO TFT can be a promising candidate for flexible displays.
Similar content being viewed by others
Explore related subjects
Find the latest articles, discoveries, and news in related topics.Introduction
The next generation of flexible displays, based on organic light-emitting diodes (OLEDs), is expected to bring excellent view ability as well as a huge spectrum of colors. Recent years, more and more studies on oxide thin film transistors (TFTs) have been reported for their widely use in driving active matrix OLEDs. Zinc oxide (ZnO) based thin films are widely used to fabricate TFTs due to their good optical and electrical properties, and good uniformity and low process temperature1,2,3,4,5,6,7,8,9,10,11,12,13,14,15,16,17,18.
Among various ZnO-based TFTs, one of the most promising materials is indium gallium zinc oxide (IGZO), which shows high electron mobility. However, IGZO thin film requires high fabricating and annealing temperature. Besides, indium element is a rare element, and the storage of In is very limited on earth. The price of indium is very high and keeping increasing. It is predicated that there will probably be a shortage of In supply in the future. Moreover, In is poisonous and harmful to human health. So novel materials for channel should be studied. The indium-free oxide-based channel materials such as zinc tin oxide (ZTO) fabricated on glass have been extensively studied3,4,5. In this letter, we choose tin-doped zinc oxide (TZO) as our experiment material. Sn is non-toxic and abundant on earth. SnO2 film is reported to possess excellent electrical characteristics. In the paper, we developed TZO TFTs on flexible substrate and studied their electrical characteristics, which were different from that on glass substrate. We turned to research the electrical performance of TZO TFTs by adjusting oxygen partial pressure (OPP) during the fabrication of the TZO film as active layer. The experiment results showed better properties of TZO TFTs than all the papers reported before3,4,5,19,20,21,22,23. The device had a low off-state current value (Ioff) of 3 pA, a high on/off current ratio of 2 × 107, a high saturation mobility (μsat) of 66.7 cm2/V•s, a subthreshold swing (SS) of 333 mV/decade, and a threshold voltage Vth of 1.2 V. These pleasing results make TZO a promising material for transparent flat panel display.
Results and Discussion
Figure 1 illustrates the transfer characteristics of the bottom-gate TZO TFTs with various O2/Ar gas pressure ratios. We analyzed the electrical characteristics of the four samples by a semiconductor parametric analyzer (Agilent 4156 C) at room temperature. Figure 1 indicates the transfer characteristics of the samples at VD = 5 V (W/L = 100 μm/50 μm). We could see that the electrical properties of the TZO TFTs are vastly improved after adding O2 during the growth of the TZO thin films but do not show large difference when the OPP increases. Table 1 shows the extracted electrical parameters of TZO TFTs. The threshold voltage (Vth) is achieved by extrapolating the linear fitting to ID1/2-VG plot under the condition VD > VG − Vth, and we can calculate the saturation mobility (μsat) through the slope of fitted line and equation (1). The subthreshold swing can be calculated by equation (2).
The mobility was extracted using transconductance method (Gm method):
Here, The capacitance per unit area COX is 2.6 × 10−8 F/cm2, which is extracted from C-V curve measured by Keithley590 C-V analyzer. VD is 5 V. The saturation mobility (μs) versus VG curve is extracted from saturation regime using transconductance (Gm) method, which is shown in Fig. 2.
We can see from Fig. 1 that the Ion and Ioff decrease with the increasing of OPP from 0% to 10%, but not obviously when the OPP keeps on increasing. This result stem from the variation of OPP which lead to the change of oxygen vacancy (Vo) including lots of electrons, which weaken the gate control and cause the poor transfer curve. With OPP increasing, the devices have better performance as Vo decreases to reinforce gate control. However, excessive oxygen contents will also deteriorate the performance owing to its large resistance from move Vo. While the OPP keeps on increasing, oxygen contents reach saturation, Vo do not decrease. So the TFT characteristic does not change so much24.
The XRD results of TZO thin film are shown in Fig. 3. The thin film was deposited by RF magnetron sputtering at RT on glass substrate. Four curves indicated different sputtering condition. There was only one peak at 2θ ≈ 34°, which mean the TZO was C-axis aligned crystalline (CAAC) oxide semiconductor25. The FWHM was measured as 0.417° (O2/Ar = 10/90) and 0.396° (O2/Ar = 0/100) respectively, which indicated the grain sizes of the film. Using the Scherer formula (D = (KΛ)/(Bcosθ)), we can get the average grain size: 20.7 nm (O2/Ar = 0/100) and 19.6 nm (O2/Ar = 10/90) respectively. This result was also confirmed by AFM surface morphology of the TZO surface (shown in Fig. 4), the extracted Root-Mean-Square (RMS) roughness of TZO thin films are shown in Table 2. We can see the TZO film (O2: Ar is 10:90) is compacter and more smoothing, the TZO thin film’s Root-Mean-Square (RMS) roughness is about 0.52 nm.
The high mobility TZO TFTs owe to optimizing process, Tin dopant concentrations, and O2/Ar gas pressure ratio. The role of oxygen during the deposition process is a key condition. Excessive oxygen may make Ion decrease, and Poor oxygen may make Ioff increase. The process of SiO2 and TZO thin films continual growth is adopted to decrease interface-state density, and enhance mobility of TZO TFTs. The high thin film quality is also a way to improve the device characteristics performances.
It is shown in Fig. 5 that the transmittance of 10%-TZO films is about 98%, and TFT fabricated shows good transparency, attesting the devices are applicable for the transparent flexible display.
In conclusion, High-performance transparent bottom gate type Tin-doped ZnO TFTs had successfully fabricated by RF Magnetron Sputtering on flexible substrate at low temperature. We had investigated the effect of O2 gas partial pressure during active channel layer deposition on the electrical properties of the device. We found growing OPP for TZO films as the channel layer did not influence the TFT characteristic much. The TZO TFTs as-fabricated exhibited excellent electrical properties, with a high Ion/Ioff of 2 × 107, a steep SS of 0.333 V/dec, a high μs of 66.7 cm2/V·s and a low Vth of 1.20 V, as the OPP was 10%. These results highlight TFTs on flexible substrates using TZO films as channel layer material can realize excellent device performance and TZO TFT can be a promising candidate for transparent flexible displays.
Methods section
In this experiment, bottom-gate type TZO TFT was fabricated by photolithography and lift-off technique. All the devices were fabricated on two-inch plastic substrates. The device structure is shown in Fig. 6. We used indium tin oxide (ITO) as gate electrode, TZO as the active layer, and ITO as S/D electrode, which were all deposited by RF sputtering. The gate insulator (SiO2) was deposited by plasma-enhanced chemical vapor deposition (PECVD). All the process temperatures are below 100 °C. Before each deposition step, the growth chamber was pre-pumped to the base vacuum pressure of 5 × 10−4 Pa. During each deposition step, the working pressure was kept at 1.0 Pa.
The fabrication procedures were as shown in Fig. 7. First, a gate electrode was patterned and a 150-nm-thick ITO film was deposited by RF sputtering on the plastic substrate, in pure Ar atmosphere at room temperature as a gate electrode. Next, a stack of 130-nm-thick gate insulator (SiO2) was fabricated on the gate electrode by PECVD at 80 °C. Third, a stack of 55-nm-thick channel layer (TZO) was sputtered at room temperature under a mixed atmosphere of Ar and O2. The RF power was kept at 70 W. The sputtering target of TZO thin film was an φ80 mm × 6 mm ceramic target with a mass ratio of ZnO:SnO2 = 97:3. Fourth, after patterning the source and drain electrode, a film of 100-nm-thick ITO was deposited using RF sputtering at room temperature and lifted to form the source and drain electrodes.
We investigate the effects of O2/Ar gas pressure ratio during channel deposition on the electrical characteristics of the TZO TFTs. There are four different samples, and their channel layers were deposited under the same total working pressure of 1.0 Pa but different O2/Ar gas pressure ratios (0:100, 10:90, 20:80, 30:70). After fabrication, the TFTs were electrically characterized by a semiconductor parameter analyzer (Agilent4156C). Crystallographic structure, and surface morphology of the TZO thin films were evaluated by x-ray diffraction (XRD) and atomic force microscopy (AFM). The transmittance of TZO with different OPPs were tested. Capacitance-voltage (C-V) characteristic was measured by Keithley590 C-V analyzer.
Additional Information
How to cite this article: Han, D. et al. Fully transparent flexible tin-doped zinc oxide thin film transistors fabricated on plastic substrate. Sci. Rep. 6, 38984; doi: 10.1038/srep38984 (2016).
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
References
Fortunato, E., Barquinha, P. & Martins, R. Oxide Semiconductor Thin-Film Transistors: A Review of Recent Advances. Adv. Mater. 24, 2945–2986 (2012).
Kenji, N. et al. Room-temperature fabrication of transparent flexible thin-film transistors using amorphous oxide semiconductors. Nature 432, 488–492 (2004).
Heineck, D. P., McFarlane, B. R. & Wager, J. F. Zinc Tin Oxide Thin-Film-Transistor Enhancement/Depletion Inverter. Ieee Electron Device Letters 30(5), 514–516 (2009).
Nayak, P. K., Pinto, J. V., Gonçalves, G., Martins, R. & Fortunato, E. Environmental, Optical, and Electrical Stability Study of Solution-Processed Zinc–Tin–Oxide Thin-Film Transistors. Journal of Display Technology 7(12), 640–643 (2011).
Parthiban, S. et al. Performances of Microcrystalline Zinc Tin Oxide Thin-Film Transistors Processed by Spray Pyrolysis. Journal of Display Technology 9(10), 825–831 (2013).
Kwon, J. Y., Lee, D. J. & Kim, K. B. Review paper: Transparent amorphous oxide semiconductor thin film transistor. Electronic Materials Letters 7, 1 (2011).
Zhang, L., Li, J., Zhang, X. W., Jiang, X. Y. & Zhang, Z. L. High performance ZnO-thin-film transistor with Ta2O5 dielectrics fabricated at room temperature. Appl. Phys. Lett. 95, 072112-1–072112-3 (2009).
Park, J. S. Improvements in the device characteristics of amorphous indium gallium zinc oxide thin-film transistors by Ar plasma treatment. Appl. Phys. Lett. 90, 262106-1–262106-3 (2007).
Lee, J. S. High-Performance a-IGZO, TFT With ZrO2 Gate Dielectric Fabricated at Room Temperature. IEEE Electron Devices Lett. 31(3), 225–227 (2012).
Park, J. Low-frequency noise in amorphous indium-gallium-zinc oxide thin-film transistors from subthreshold to saturation. Appl. Phys. Lett. 97, 122104 (2010).
Lee, K. et al. The influence of oxygen partial pressure on the performance and stability of Ge-doped InGaO thin film transistors. Ceram. Int. 40, 3215–3220 (2014).
Kang, T. et al. Revealing Al evaporation-assisted functions in solution-processed ZnO thin film transistors. J. Mater. Chem. C. 2, 10209–10216 (2014).
Kang, T. et al. Highly stable solution-processed ZnO thin film transistors prepared via a simple Al evaporation. J. Mater. Chem. C. 2, 1390–1395 (2014).
Kang, T. et al. Electrical and Structural Analyses of Solution-Processed Li-Doped ZnO Thin Film Transistors Exposed to Ambient Conditions. Appl. Phys. Express. 6, 011101 (2013).
Kim, K. et al. Low temperature and solution-processed Na-doped zinc oxide transparent thin film transistors with reliable electrical performance using methanol developing and surface engineering. J. Mater. Chem. 22, 23120–23128 (2012).
Jun, T. et al. High-performance low-temperature solution-processable ZnO thin film transistors by microwave-assisted annealing. J. Mater. Chem. 21, 1102–1108 (2011).
Park, S. et al. Aqueous zinc ammine complex for solution-processed ZnO semiconductors in thin film transistors. RSC Adv. 4, 11295–11299 (2014).
Lin, Y. et al. High-Performance ZnO Transistors Processed Via an Aqueous Carbon-Free Metal Oxide Precursor Route at Temperatures between 80–180 °C. Adv. Mater. 25, 4340–4346 (2013).
Jeong, Y. et al. Bias Stress Stability of Solution-Processed Zinc Tin Oxide Thin-Film Transistors. J. Electrochem. Soc. 156, H808–H812 (2009).
Nathan, A. et al. Amorphous oxide semiconductor TFTs for displays and imaging. Display Technology, Journal of 10(11), 917–927 (2014).
Kamiya, T., Nomura, K. & Hosono, H. Present status of amorphous In–Ga–Zn–O thin-film transistors. Science and Technology of Advanced Materials 11(4), 044305 (2010).
Song, K. et al. Solution-processable tin-doped indium oxide with a versatile patternability for transparent oxide thin film transistors. Journal of Materials Chemistry 21(38), 14646–14654 (2011).
Kim, B. S. et al. Solution-processed zinc-indium-tin oxide thin-film transistors for flat-panel displays. Applied Physics Letters 103(7), 072110 (2013).
Jung, C. H., Kim, D. J., Kang, Y. K. et al. Transparent amorphous In–Ga–Zn–O thin film as function of various gas flows for TFT applications. Thin Solid Films 517(14), 4078–4081 (2009).
Koezuka, J. et al. Development of Back-channel-etched TFT Using C-Axis Aligned Crystalline In-Ga-Zn-Oxide. SID Symposium Digest of Technical Papers. Blackwell Publishing Ltd. 44(1), 723–726 (2013).
Acknowledgements
This work is supported partly by the National Basic Research Program of China (973 program, Grant No. 2013CBA01604) and partly by the National Natural Science Foundation of China (Grant No. 61275025).
Author information
Authors and Affiliations
Contributions
D.D.H. and Y.Z. wrote the main manuscript text. Y.Y.C. and W.Y. organized the data and drew figures. The project was guided by X.Z., and Y.W. give their suggestions of the article about content and structure. All authors reviewed the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Han, D., Zhang, Y., Cong, Y. et al. Fully transparent flexible tin-doped zinc oxide thin film transistors fabricated on plastic substrate. Sci Rep 6, 38984 (2016). https://doi.org/10.1038/srep38984
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep38984
- Springer Nature Limited
This article is cited by
-
The effect of Sn on electrical performance of zinc oxide based thin film transistor
Journal of Materials Science: Materials in Electronics (2019)