Abstract
Shrinking the device dimension has long been the pursuit of the semiconductor industry to increase the device density and operation speed. In the application of thin film transistors (TFTs), all-organic TFT arrays made by all-solution process are desired for low cost and flexible electronics. One of the greatest challenges is how to achieve ultrashort channel through a cost-effective method. In our study, ultrashort-channel devices are demonstrated by direct inkjet printing conducting polymer as source/drain and gate electrodes without any complicated substrate’s pre-patterning process. By modifying the substrate’s wettability, the conducting polymer’s contact line is pinned during drying process which makes the channel length well-controlled. An organic TFT array of 200 devices with 2 μm channel length is fabricated on flexible substrate through all-solution process. The simple and scalable process to fabricate high resolution organic transistor array offers a low cost approach in the development of flexible and wearable electronics.
Similar content being viewed by others
Explore related subjects
Find the latest articles, discoveries, and news in related topics.Introduction
Organic thin-film transistors (OTFTs) have attracted great attention for a wide range of applications, such as flexible displays1,2, sensors3, radio frequency identification tags4, low-cost memories5, and microprocessors6, due to their unique properties of excellent mechanical flexibility and process advantages of being compatible with high throughput and low-budget printing processes7. Over the years, significant efforts have been made to develop high carrier mobility, chemically and physically stable organic semiconductor materials with the reported device performance of OTFTs already better than that of amorphous silicon devices8,9,10,11. However, the fabrication of OTFT devices generally requires thermal evaporation through masks to deposit metal electrodes and the semiconducting layer in vacuum1,2,3,4,5,6,7,8,9,10,11,12,13,14. The process is known to be costly and difficult to scale up. To fully exploit the potentials of organic materials in the applications of low cost and flexible electronics, all-organic TFTs made by all-solution process are desired15.
Various techniques have been developed to fabricate all-organic TFTs. Conventional photolithography, which is the standard technique in inorganic semiconductor industry, has been explored for patterning polymer electrodes in bottom contact OTFTs. For example, Halik et al. fabricated all-organic pentacene TFTs on flexible polymeric substrates with photolithography-patterned PEDOT:PSS contacts16. A similar photo-induced patterning approach, named photochemical patterning, was developed by Gelinck et al. They demonstrated fully-solution-processed and all-polymer integrated circuits with conductive polyaniline electrodes defined by photochemical conversion through a shadow mask17. Although photolithography is a mature process and capable of high resolution patterning, its application in patterning OTFTs is rather limited due to degradation of organic semiconductors upon exposure of the etching chemicals.
Screen printing, which is suitable for large scale production and much cheaper than photolithography, has been exploited in OTFTs much earlier than photolithography. Garnier et al. demonstrated the first all-organic TFTs back in 1994 of which the source, drain and gate electrodes were all screen-printed from a graphite based ink, while the small molecular semiconductor was thermally evaporated18. Most recently, Hyun et al. adopted a photolithography-patterned silicon sheet as the stencil to improve the resolution of screen printing19. All-solution processed, electrolyte gated transistors were fabricated with screen-printed graphene source and drain (S/D), and an aerosol-jet printed poly(3,4-ethylenedioxythiophene) polystyrene sulfonate (PEDOT:PSS) gate. However, the obtained channel length of 90 μm is not narrow enough to meet the demand for large drive current and high switching speed.
Microcontact printing, which transfers patterns from stamps, can achieve a resolution as high as that of photolithography while retaining low cost. Parashkov et al. employed the process to pattern an electron-transfer blocking layer on a gold plate to realize selective electro-polymerization of PEDOT:PSS S/D20. The electrodes were then transferred onto a polyimide substrate where pentacene and polyvinyl alcohol (PVA) were deposited as the semiconductor and dielectric layer. The PEDOT:PSS gate was screen printed. The final channel length is as small as 10 μm. However, the costly metal deposition in vacuum for preparing the electro-polymerization template was required to deposit the electrodes.
Another simple and cost-effective patterning technique is inkjet printing. The advantages of its fully additive feature, flexibility in pattern design, and low material consumption, make inkjet printing an attractive deposition technique in OTFT fabrication. The patterning resolution of inkjet printing, however, is generally tens of micrometers owing to the difficulty in controlling the droplet size and ink-spreading on substrates. To overcome the resolution limitation, Sirringhaus et al. demonstrated an approach by depositing the functional ink onto a substrate containing a predefined surface-energy pattern that was able to split the deposited ink droplets to form a narrow gap15,21. Sub-micrometer channel length was achieved by inkjet printing PEDOT:PSS ink. The process requires photolithography or electron-beam lithography to prepare the hydrophobic strips. To further exploit the direct-writing capability by inkjet printing, the authors developed a lithography-free nanopatterning technique in which a self-assembled surface layer induced the dewetting of PEDOT:PSS resulting in sub-micrometer size channels22. However, the additional surface layer sometimes causes defects at electrode contacts, and the dewetting process is time consuming.
All aforementioned techniques require multi-step procedures to pattern organic electrodes in order to achieve the narrow channel length. In our contribution, we develop a direct-writing technique to pattern organic electrodes with high resolution by inkjet printing. All-organic and all-solution processed TFT arrays were fabricated on a flexible substrate. By modifying the surface wettability of the polyethylene terephthalate (PET) surface with PVA, a channel length around 2 μm defined by PEDOT:PSS electrodes was achieved. To the best of our knowledge, this is the highest resolution ever reported for directly inkjet-printed electrodes without any complicated substrate pre-patterning process. A 10 by 20 OTFT array were fabricated across a 3 cm × 3 cm flexible substrate showing good uniformity and high yield. Our study demonstrates that by carefully controlling ink spreading on substrates, high resolution OTFTs are achievable by direct inkjet printing.
Results
To fabricate OTFTs on a flexible substrate, a 200 μm thick PET foil first went through 20 mins oxygen-plasma treatment to increase the surface energy. PVA in deionized water (20 mg/mL) was spin-coated onto PET film to form a 50 nm buffer layer to modify the PET surface. On top of the PVA surface modification layer, S/D electrodes were fabricated by line printing conducting polymer PEDOT:PSS23. The organic semiconductor layer was deposited by spin-coating poly [3,6-bis(40-dodecyl[2,20]bithiophenyl-5-yl)-2,5-bis(2-hexyldecyl)-2,5-dihydropyrrolo[3,4-c]pyrrole-1,4-dione] (PDQT) in chloroform (6 mg/mL). The thickness of the active layer is about 60 nm. On top of the active layer, a 500 nm film of polymethylmethacrylate (PMMA) was spin-coated from its n-butyl acetate solution (50 mg/mL) as the gate dielectric layer. An additional ultrathin polyethylene glycol (PEO) layer was spin-coated from a 5 mg/mL solution in methanol to modify the PMMA surface to enhance its wettability for the subsequent PEDOT:PSS gate printing, which was laid perpendicular to the S/D lines. The top-gate OTFT structure is schematically illustrated in Fig. 1. All the processes are solution-based, and all the processes are carried out in air at room temperature.
Reducing the channel length to achieve high device integration density, high operation speed and low power consumption is critical in OTFT development. Grau et al. reported gravure-printed OTFTs with 5 μm channel length24. Yoshimura et al. achieved 4 μm channel length by inkjet printing silver inks25. Fukuda et al., taking advantage of the high-resolution off-set printing and the their customized silver ink, reached a submicrometer channel length of 0.6 μm26. However, the studies to achieve narrow channel length all used metal inks. Though direct inkjet-printing conducting polymers (mainly PEDOT:PSS) as S/D electrodes in OTFT devices without pre-patterning substrate has been demonstrated27, the typical channel length is between 20 to 50 μm owing to the ink spreading on substrates and droplet positioning error15. To overcome the problem, we propose here that by modifying the surface energy of the substrate with a hydrophilic and dissolvable layer, namely, the PVA buffer layer, accurate PEDOT:PSS patterns of short channels becomes possible due to the contact line pinning effect and excellent film morphology.
To obtain ultrashort channel, the S/D electrodes’ patterning process is crucial. During the inkjet printing process, upon striking the substrate, the PEDOT:PSS droplet spreads first as driven by the kinetic energy. Afterwards, it shrinks because of the surface tension, and finally dries to form a stable shape28. After inkjet printing PEDOT:PSS in the polar solvent (water) on a non-polar PET surface, due to the high contact angle of 107°, the consecutively printed PEDOT:PSS droplets can’t form a continuous line. Instead, isolated islands were formed, as demonstrated in Fig. 2a. To increase the hydrophilicity of the substrate, PVA was spin-coated to modify the PET surface. The atomic force microscopy (AFM) image in Fig. 2b shows the PVA has a very smooth surface with a root mean square (RMS) roughness of about 1.2 nm. On PVA, the contact angle of PEDOT:PSS was reduced to 38°. As the result, a uniform electrode line was formed by the consecutively printed PEDOT:PSS droplets as shown in Fig. 2a. The three-dimensional picture from the white light interference microscope shows a relative smooth surface of the PEDOT:PSS line free of the coffee ring (Fig. 2c). It is determined by the cross-section profile that the line width is about 106 μm, and the line thickness is about 100 nm.
(a) The contact angle of PEDOT:PSS on PET surface is 107°. Line printing on the substrate results in isolated islands due to the small solid surface energy. After PVA modification, PEDOT:PSS contact angle becomes 38°. A continuous line is formed by line printing PEDOT:PSS. (b) The AFM picture shows the smooth PVA-modified PET surface. (c) The three-dimensional white light interference microscopic picture and the cross-sectional profile of the printed PEODT:PSS line on PVA-modified PET. (d) Sequential picture of PEDOT:PSS drying process on PVA-modified PET. tf is the total drying time.
A common practice to increase the substrate surface energy is UV/ozone or oxygen plasma treatment29,30. However, the wettability provided by the treatments is not stable in air31,32. With PVA film, the hydrophilic layer guarantees the uniform coating of the PEDOT:PSS electrode array across a large area during the printing process without any wettability deterioration.
Moreover, the PVA layer can pin the contact line during PEDOT:PSS film formation. Figure 2d shows the drying process of the PEDOT:PSS droplets on PVA/PET substrate. The total drying time tf was 600 s. The contact line (as denoted by the dash lines) was strongly pinned due to the dissolution of PVA underneath the PEDOT:PSS droplet, and the contact line did not withdraw during the whole drying process as shown at t = 60 s, 180 s, 240 s, 420 s , 540 s, and 600 s, respectively. In our early work, PEDOT:PSS was inkjet printed on an oxygen-plasma treated PMMA surface33. The contact line withdrew during PEDOT:PSS solvent evaporation due to insufficient interfacial adhesion. The minimum channel length of 20 μm was determined by the receding radius of the droplet. In the current study, with surface modification of the hydrophilic PVA, precise control of the line gap and line width can be realized owing to the pinned contact line34. As the result, an ultrashort channel was achieved by direct inkjet printing through careful calculation and adjustment of the printing parameters without any complicated substrate pre-patterning process.
The stable line width through inkjet printing can be estimated by the following equation (1):35
![](http://media.springernature.com/lw217/springer-static/image/art%3A10.1038%2Fsrep29055/MediaObjects/41598_2016_Article_BFsrep29055_Equ1_HTML.gif)
where d0 is the droplet diameter in air, θ is the contact angle of the droplet on the substrate, and p is the distance between the consecutive droplets’ landing positions. It’s clear that for a given printer cartridge with the fixed d0 and θ, p is the only parameter which can be optimized. To obtain fine lines with smooth edges, p can neither be too small nor too large36. The optimized p for PEDOT:PSS jetted from a 30 μm nozzle, is around 50 μm, which resulted in a line width of about 106 μm without coffee ring (Fig. 2c). Thus, by carefully adjusting the line-center distance between two PEDOT:PSS electrodes, the printed channel length can be determined.
By setting the printing line-center distance at 118 μm after taking into account the line width and the substrate positioning accuracy, a 2 μm channel length was successfully achieved. To test the printing uniformity, 200 structures were fabricated on a 3 cm × 3 cm PET substrate with 2 μm channel length and 970 μm channel width. The microscopic pictures and AFM topography of the printed channels are shown in Fig. 3. The inset of Fig. 3a shows that the all-solution processed OTFTs are flexible and transparent. The channel length distribution in Fig. 3e shows the direct inkjet printing is reliable and repeatable (2.0 μm in average with 0.5 μm standard deviation). No shortening of the S/D electrodes was detected confirming the high yield of the device array fabrication.
(a) The printed PEDOT:PSS array (10 × 20) on the flexible PET substrate with 2 μm channel length. Inset: Picture of the array on the 3 cm × 3 cm substrate, bended with bending radius of about 5 mm. (b) The zoom-in picture of the array. (c) Picture of a single channel. (d) AFM picture of the PEDOT:PSS lines with a gap of about 2 μm. (e) The channel-length distribution of the 200 channels.
The typical transfer characteristics of the 2 μm channel OTFT device is shown in Fig. 4a. The maximum hole mobility is (0.64 ± 0.27) × 10−3cm2/V · s, ON/OFF ratio is (0.92 ± 0.48) × 103, and turn-on voltage is 1.94 ± 0.32 V. The statistics is calculated from a total of 96 devices. For comparison, OTFTs with thermal-evaporated Au S/D electrodes and a channel length of 70 μm (W/L = 4) were fabricated. As shown in Fig. 4b, the devices exhibit a mobility of 0.55 cm2/V·s, an ON/OFF ratio of 3.26 × 104, and a turn-on voltage at −5.5 V. A previous study on non-annealed PDQT devices using a bottom-gate top-contact structure with evaporated Au electrodes reported a mobility of 0.89 cm2/V·s, an ON/OFF ratio of 107, and a threshold voltage of −2.6 V37. The performances of the Au devices indicate that the poor performance of the 2-μm-channel all-organic devices is not due to the semiconducting or the dielectric layer, but the printed PEDOT:PSS electrodes and their interface to the semiconducting layer. It is observed that while the OFF current of 2-μm-channel devices remains at the same level as the Au device, the ON current is about an order of magnitude smaller, which directly reduces the ON/OFF ratio to about 103. It is also noticed that the slope of the square root of drain current quickly decreases as the gate voltage increases. Therefore, it is speculated that the poor performance may be the result of the relatively large contact resistance at the printed electrodes.
(a) Transfer characteristics of the devices with printed PEDOT:PSS electrodes. The channel width is fixed at 970 μm, and channel lengths are 2 μm, 10 μm, 20 μm and 30 μm, respectively. (b) Transfer characteristic of the device with evaporated Au S/D electrodes. W/L = 280 μm/70 μm. (c) The dependence of mobility and ON/OFF ratio on the cannel length. (d) The channel resistance of devices with different channel lengths (normalized to the channel width). The intercept at the y axis indicates the contact resistance.
To confirm it, all-solution processed, all-organic TFTs with channel lengths of 30 μm, 20 μm and 10 μm were fabricated. The channel width was kept at 970 μm. Transfer characteristics are presented in Fig. 4a,c gives the statistical distribution of the mobility and ON/OFF ratio for the devices with different channel length. The statistics are calculated from a total of 46, 93, and 61 devices, for 30 μm, 20 μm, and 10 μm channel length, respectively. The device performances are summarized in Table 1. The mobility shows a decreasing trend as the channel length shortens (Fig. 4c), which is consistent with the effect of large contact resistance in TFTs38. By further plotting the channel resistance (normalized to the channel width) as a function of channel length in Fig. 4d (at the gate voltage of −5 V), a contact resistance of about 15.0 MΩ · cm is identified. The value is about two to three orders of magnitude larger than typical solution-processed OTFTs39. Such large contact resistance will limit the drain current at high gate voltages. As a result, calculating mobility from typical equations will lead to much smaller values38. The origin of the large contact resistance could come from the relatively large injection barrier from PEDOT:PSS electrodes to the semiconducting PDQT, as well as the large bulk resistance of intrinsic PEDOT:PSS15. Further device optimization by, for example, inserting an injection layer between PEDOT:PSS electrodes and the PQDT layer, or raising the conductivity of PEDOT:PSS, will improve the device performance40,41.
In summary, all-organic and all-solution processed OTFT array is fabricated on flexible substrate PET. The source, drain and gate electrodes are deposited by inkjet printing conducting polymer PEDOT:PSS. By modifying the PET substrate with water-dissolvable PVA, the contact line of PEDOT:PSS is pinned during the drying process resulting in well-defined edges. The pinning effect subsequently enables precise control of the printed channel length. Ultrashort channel of 2 μm is successfully realized without any complicated substrate’s pre-patterning process. No short circuiting was found by printing a large array with 200 electrode pairs. Due to the large contact resistance, the printed devices show inferior performances to those with evaporated metal electrodes. By further reducing the linewidth of the printed patterns as well as optimizing the device performance, application of all-printed, high resolution TFTs in flexible displays, sensor chips, and radio-frequency identification tags will become practical.
Methods
Materials
All the chemicals and materials were purchased and used as received unless otherwise noted. PEDOT:PSS Clevios PH 500 was purchased from Heraeus Deutschland GmbH & Co. KG. PVA (98–99% hydrolyzed) was purchased from Alfa Aesar. To make PVA solution (20 mg/mL) in deionized water, the solution was heated to 90 °C for 5 hours. PDQT (molecular weight >30,000) was purchased from Lumtec Corp. PMMA, PEO, and all the solvents were purchased from Aldrich, Inc. All the solutions were filtered through a 0.45 μm filter before use.
Device Fabrication and Characterization
PEDOT:PSS printing was carried out on an inkjet printer (Jetlab II) from Microfab Technologies, Inc. The printer head’s orifice diameter is 30 μm. Film thickness and surface morphologies were obtained from a Dektak 150 surface profiler (Veeco Instruments, Inc.). The three-dimensional white light interference microscopy pictures were recorded by Veeco Instruments’ NT 9300 surface profiler. The optical microscopic images were taken with a Nikon Eclipse E600 POL with a DXM1200F digital camera. The transistor characteristics of the devices were measured using an Agilent 4155C semiconductor parameter analyzer connected to a Cascade manual probe station.
Additional Information
How to cite this article: Xu, W. et al. Flexible All-organic, All-solution Processed Thin Film Transistor Array with Ultrashort Channel. Sci. Rep. 6, 29055; doi: 10.1038/srep29055 (2016).
References
Park, C. B. et al. Flexible electrophoretic display driven by solution-processed organic TFT with highly stable bending feature. Org. Electron. 15, 3538–3545 (2014).
Steudel, S. et al. Design and realization of a flexible QQVGA AMOLED display with organic TFTs. Org. Electron. 13, 1729–1735 (2012).
Lin, P. & Yan, F. Organic Thin-Film Transistors for Chemical and Biological Sensing. Adv. Mater. 24, 34–51 (2012).
Rotzoll, R. et al. Radio frequency rectifiers based on organic thin-film transistors. Appl. Phys. Lett. 88, 123502 (2006).
Ouyang, J., Chu, C.-W., Szmanda, C. R., Ma, L. & Yang, Y. Programmable polymer thin film and non-volatile memory device. Nat Mater 3, 918–922 (2004).
Myny, K. et al. A thin-film microprocessor with inkjet print-programmable memory. Sci. Rep. 4, 7398 (2014).
Li, J. et al. A stable solution-processed polymer semiconductor with record high-mobility for printed transistors. Sci. Rep. 2, 754 (2012).
Tsao, H. N. et al. Ultrahigh Mobility in Polymer Field-Effect Transistors by Design. J. Am. Chem. Soc. 133, 2605–2612 (2011).
Chen, H. et al. Highly π-Extended Copolymers with Diketopyrrolopyrrole Moieties for High-Performance Field-Effect Transistors. Adv. Mater. 24, 4618–4622 (2012).
Lei, T., Dou, J.-H. & Pei, J. Influence of Alkyl Chain Branching Positions on the Hole Mobilities of Polymer Thin-Film Transistors. Adv. Mater. 24, 6457–6461 (2012).
Zhang, W., Liu, Y. & Yu, G. Heteroatom Substituted Organic/Polymeric Semiconductors and their Applications in Field-Effect Transistors. Adv. Mater. 26, 6898–6904 (2014).
Zhang, W., Liu, Y. & Yu, G. Heteroatom Substituted Organic/Polymeric Semiconductors and their Applications in Field-Effect Transistors. Adv. Mater. 26, 6898–6904 (2014).
Liu, D. et al. Self-Assembled Monolayers of Cyclohexyl-Terminated Phosphonic Acids as a General Dielectric Surface for High-Performance Organic Thin-Film Transistors. Adv. Mater. 26, 7190–7196 (2014).
Tan, L. et al. A Densely and Uniformly Packed Organic Semiconductor Based on Annelated β-Trithiophenes for High-Performance Thin Film Transistors. Adv. Funct. Mater. 19, 272–276 (2009).
Sirringhaus, H. et al. High-Resolution Inkjet Printing of All-Polymer Transistor Circuits. Science. 290, 2123–2126 (2000).
Halik, M. et al. Polymer Gate Dielectrics and Conducting-Polymer Contactsfor High-Performance Organic Thin-Film Transistors. Adv. Mater. 14, 1717–1722 (2002).
Gelinck, G. H., Geuns, T. C. T. & de Leeuw, D. M. High-performance all-polymer integrated circuits. Appl. Phys. Lett. 77, 1487 (2000).
Garnier, F., Hajlaoui, R., Yassar, A. & Srivastava, P. All-Polymer Field-Effect Transistor Realized by Printing Techniques. Science. 265, 1684–1686 (1994).
Hyun, W. J., Secor, E. B., Hersam, M. C., Frisbie, C. D. & Francis, L. F. High-Resolution Patterning of Graphene by Screen Printing with a Silicon Stencil for Highly Flexible Printed Electronics. Adv. Mater. 27, 109–115 (2014).
Parashkov, R., Becker, E., Riedl, T., Johannes, H.-H. & Kowalsky, W. Microcontact Printing as a Versatile Tool for Patterning Organic Field-Effect Transistors. Adv. Mater. 17, 1523–1527 (2005).
Wang, J. Z., Zheng, Z. H., Li, H. W., Huck, W. T. S. & Sirringhaus, H. Dewetting of conducting polymer inkjet droplets on patterned surfaces. Nat. Mater. 3, 171–176 (2004).
Sele, C. W., von Werne, T., Friend, R. H. & Sirringhaus, H. Lithography-Free, Self-Aligned Inkjet Printing with Sub-Hundred-Nanometer Resolution. Adv. Mater. 17, 997–1001 (2005).
Liu, H. et al. Line printing solution-processable small molecules with uniform surface profile via ink-jet printer. J. Colloid Interface Sci. 465, 106–111 (2016).
Grau, G. & Subramanian, V. Fully High-Speed Gravure Printed, Low-Variability, High-Performance Organic Polymer Transistors with Sub-5 V Operation. Adv. Electron. Mater. 2, 1500328 (2016).
Yoshimura, Y., Takeda, Y., Fukuda, K., Kumaki, D. & Tokito, S. High-speed operation in printed organic inverter circuits with short channel length. Org. Electron. 15, 2696–2701 (2014).
Fukuda, K. et al. Reverse-Offset Printing Optimized for Scalable Organic Thin-Film Transistors with Submicrometer Channel Lengths. Adv. Electron. Mater. 1, 1500145 (2015).
Basiricò, L., Cosseddu, P., Fraboni, B. & Bonfiglio, A. Inkjet printing of transparent, flexible, organic transistors. Thin Solid Films 520, 1291–1294 (2011).
Fukai, J. et al. Effects of droplet size and solute concentration on drying process of polymer solution droplets deposited on homogeneous surfaces. Int. J. Heat Mass Transf. 49, 3561–3567 (2006).
Fukuda, K. et al. Fully-printed high-performance organic thin-film transistors and circuitry on one-micron-thick polymer films. Nat Commun 5, 4147 (2014).
Liston, E. M. Plasma Treatment for Improved Bonding: A Review. J. Adhes. 30, 199–218 (1989).
You, Z. Z., Dong, J. Y. & Fang, S. Du . Surface modification of indium-tin-oxide anode by oxygen plasma for organic electroluminescent devices. Phys. status solidi 201, 3221–3227 (2004).
Jokinen, V., Suvanto, P. & Franssila, S. Oxygen and nitrogen plasma hydrophilization and hydrophobic recovery of polymers. Biomicrofluidics 6, 16501–16510 (2012).
Liu, N. et al. High-performance, all-solution-processed organic nanowire transistor arrays with inkjet-printing patterned electrodes. Langmuir 27, 14710–5 (2011).
Kajiya, T., Monteux, C., Narita, T., Lequeux, F. & Doi, M. Contact-Line Recession Leaving a Macroscopic Polymer Film in the Drying Droplets of Water−Poly(N,N-dimethylacrylamide) (PDMA) Solution. Langmuir 25, 6934–6939 (2009).
Stringer, J. & Derby, B. Formation and Stability of Lines Produced by Inkjet Printing. Langmuir 26, 10365–10372 (2010).
Soltman, D. & Subramanian, V. Inkjet-Printed Line Morphologies and Temperature Control of the Coffee Ring Effect. Langmuir 24, 2224–2231 (2008).
Li, Y. et al. Annealing-Free High-Mobility Diketopyrrolopyrrole−Quaterthiophene Copolymer for Solution-Processed Organic Thin Film Transistors. J. Am. Chem. Soc. 133, 2198–2204 (2011).
Sirringhaus, H. 25th Anniversary Article: Organic Field-Effect Transistors: The Path Beyond Amorphous Silicon. Adv. Mater. 26, 1319–1335 (2014).
Bao, Z. & Locklin, J. Organic field-effect transistors. (CRC press, 2007).
Liu, C., Xu, Y. & Noh, Y.-Y. Contact engineering in organic field-effect transistors. Mater. Today 18, 79–96 (2015).
Kim, N. et al. Highly Conductive PEDOT:PSS Nanofibrils Induced by Solution-Processed Crystallization. Adv. Mater. 26, 2268–2272 (2014).
Acknowledgements
The authors are deeply grateful to the Ministry of Science and Technology (973 Program 2015CB655000), and National Nature Science Foundation of China (51373057, 51573056), and Science and Technology Planning Project of Guangdong Province, China (2014B090916001) for their financial supports.
Author information
Authors and Affiliations
Contributions
J.W., J.P. and W.X. designed the research; W.X. and Z.H. carried out the experiments; W.X., Z.H. and L.L. analyzed the data; H.L., L.L. and Y.C. provided valuable discussion and suggestion; W.X., Z.H. and J.W. wrote the paper.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Xu, W., Hu, Z., Liu, H. et al. Flexible All-organic, All-solution Processed Thin Film Transistor Array with Ultrashort Channel. Sci Rep 6, 29055 (2016). https://doi.org/10.1038/srep29055
Received: