Abstract
Layered double hydroxides (LDHs) are bimetallic hydroxides that currently attract considerable attention as co-catalysts in photoelectrochemical (PEC) systems in view of water splitting under solar light. A wide spectrum of LDHs can be easily prepared on demand by tuning their chemical composition and structural morphology. We describe here the electrochemical growth of NiFe-LDH overlayers on Cu2O electrodes and study their PEC behavior. By using the modified Cu2O/NiFe-LDH electrodes we observe a remarkable seven-fold increase of the photocurrent intensity under an applied voltage as low as −0.2 V vs Ag/AgCl. The origin of such a pronounced effect is the improved electron transfer towards the electrolyte brought by the NiFe-LDH overlayer due to an appropriate energy level alignment. Long-term photostability tests reveal that Cu2O/NiFe-LDH photocathodes show no photocurrent loss after 40 hours of operation under light at −0.2 V vs Ag/AgCl low bias condition. These improved performances make Cu2O/NiFe-LDH a suitable photocathode material for low voltage H2 production. Indeed, after 8 hours of H2 production under −0.2 V vs Ag/AgCl the PEC cell delivers a 78% faradaic efficiency. This unprecedented use of Cu2O/NiFe-LDH as an efficient photocathode opens new perspectives in view of low biasd or self-biased PEC water splitting under sunlight illumination.
Similar content being viewed by others
Introduction
The accelerated depletion of fossil fuel reserves combined with increasing demand of energy across the world has triggered a tremendous effort toward alternative energy sources and various technologies are currently being explored. Among those, photoelectrochemical (PEC) water splitting under solar light irradiation has shown their potential by the successful integration of abundant energy source and high efficient catalysts. In order to realize high efficiency PEC systems in view of water splitting, a number of photocatalysts have been investigated including the widespread TiO21,2,3, ZnO4,5,6,7, WO38,9,10,11, Fe2O312, as well as more innovative catalysts such as Cu2O13,14,15 and BiVO416.
Cu2O is a promising photocathode material due to its suitable band gap (1.9–2.2 eV) and high absorption coefficient in the visible region17,18,19,20. Its conduction band is located above the reduction potential of water, making it suitable for mediating H2 production with little or no external bias in a PEC cell. Among different methods, electrodeposition has proven to be the most convenient and reliable to prepare nanostructured Cu2O17,21. Recent studies show that the Cu2O morphology and orientation can be controlled by judiciously tuning the deposition parameters such as the electrolyte pH, temperature, applied potential and current density17,21. The morphology and crystal structure determine the material performances through their role in light absorption and charge transport.
Although Cu2O possesses an intrinsic potential as a photocathode, the reported photocurrents remain well below the theoretical values, in particular under low external biases. These poor performances arise essentially from structural defects at the semiconductor-electrolyte interface. It has been reported that at low external voltages, Cu2O does not transfer electrons efficiently towards the electrolyte due to an inappropriate band bending22. In order to improve the photocurrent of Cu2O electrodes, various approaches have been recently developed. For example Cu2O can be combined with another catalyst such as TiO223, or by depositing a protective layer on its surface such as Cu2S13,14, RuO224, or polyoxometallates25.
Layered double hydroxides (LDHs) attract a growing attention as co-catalysts due to several advantages. LDHs constitute a group of two-dimensional materials of general formula [M1−x2+Mx3+(OH)2][Ax/n]·mH2O in which a fraction of a divalent metal cation M2+ coordinated octahedrally by hydroxy groups is replaced isomorphously by a trivalent metal cation M3+ 26,27. The variety in chemical composition and structural morphology of LDH materials make them suitable for a wide range of applications as electrocatalysts28,29,30,31,32. In particular, LDHs can act as efficient photocatalysts for improving the charge separation of photogenerated electrons and holes33. Moreover, the hierarchical morphology of LDHs provides convenient charge transfer at the electrolyte interface in PEC systems. Several types of LDHs such as CoNi33, or ZnCo34, have been widely investigated to enhance PEC water splitting.
We describe here the fabrication of Cu2O/NiFe-LDH via a facile two-step electrodeposition method and the use of NiFe-LDH to enhance the performances of Cu2O photocathodes. The NiFe-LDH layers grow as nanoplatelets that are uniformly anchored onto the Cu2O surface. Our Cu2O/NiFe-LDH exhibits greatly improved photocurrent intensities particularly at low applied voltages. Moreover we demonstrate that modified Cu2O/NiFe-LDH photocathodes allow more efficient H2 production at low applied voltages. The Cu2O/NiFe-LDH photocathodes reveal to be highly stable with no degradation under low bias after 40 hours of illumination, making Cu2O/NiFe-LDH an excellent photoelectrode for low bias PEC water splitting.
Results and Discussion
Morphology of Cu2O/NiFe-LDH materials
Images recorded by field-emission scanning electron microscopy (FESEM) show that electrodeposited Cu2O consists of compact and highly homogeneous layers made of cubic particles having ~400 nm in size (Fig. 1a) and thicknesses of ~1 μm after 1,500 s of deposition time (Fig. 1b). NiFe-LDH overlayers are then grown on the Cu2O samples using different deposition times (Fig. 1b,c). After 60 seconds, the NiFe-LDH material adopts a uniform nanoflake morphology (Fig. 1d) with individual flakes of size ~5 nm (Figure S1). After 300 s it self-assembles into sponge-like structures (Fig. 1f). AFM images show that after deposition of NiFe-LDH, the surface roughness is greatly increased (Table S1 and Figure S2) and may thus increase substantially the number of photons absorbed by the photocathode. Besides, the XRD pattern of NiFe-LDH after 150 s exhibits typical (003), (006) and (104) reflection peaks, while Cu2O shows the known dominant (111) reflection (Figure S3)35,36. For NiFe-LDH (20 s) XRD does not reveal any visible peaks, while EDX images confirm the existence and uniformity of Ni and Fe elements in the Cu2O layer (Figure S4).
PEC measurement
Linear sweep voltammetry
The PEC properties of Cu2O with and without NiFe-LDH were investigated under chopped light by linear sweep voltammetry (LSV) (Fig. 2a and Figure S5a). Before deposition of NiFe-LDH the photocurrent density is 1.27 mA.cm−2 under −0.6 V vs Ag/AgCl. For deposition times shorter than 20 s the photocurrent of bare Cu2O does not improve significantly (Figure S6). After deposition of NiFe-LDH for 20 s, the photocurrent density exhibits a twofold increase to reach 2.42 mA.cm−2. An even more important relative photocurrent increase is observed in the low bias range from 0.0 V to −0.3 V vs Ag/AgCl. For example, Cu2O/NiFe-LDH (20 s) under −0.2 V vs Ag/AgCl, that is more than seven times that of bare Cu2O (−0.05 mA.cm−2, Fig. 2b). It shows that the introduction of the NiFe-LDH layer induces a more efficient separation of photogenerated charges on one side and an effective electron injection into the electrolyte on the other side. Prolonged deposition of NiFe (more than 20 s) results in less or no improvement in photocurrent (Figure S5a) due to a too strong light absorption by NiFe-LDH that reduces charge carriers generation by Cu2O.
Linear sweep voltammetry under light-chopped illumination of bare Cu2O and Cu2O/NiFe-LDH (20 s) electrodes in the voltage ranges (a) +0.1/−0.8 V and (b) −0.3/−0.05 V vs Ag/AgCl. ∆Jph denotes the photocurrent density after substraction of the dark current. At ‒0.25 V vs Ag/AgCl, the ∆Jph value for bare Cu2O is ∆Jph1 = 0.07 mA.cm−2 while for Cu2O/NiFe-LDH it is ∆Jph2 = 0.49 mA.cm−2. (c,d) Zoom-in of the photoresponse of Cu2O and Cu2O/NiFe-LDH electrodes in the −0.2/+0.1 V vs Ag/AgCl low voltage range.
Furthermore, although bare Cu2O generates a positive photocurrent when illuminated under positive low voltages (Fig. 2c), the Cu2O/NiFe-LDH electrodes generates a negative photocurrent under negative voltages (Fig. 2d and Figure S5c,d). For example, under −0.1V vs Ag/AgCl, Cu2O electrode produces a very weak positive photocurrent (< + 0.01 mA.cm−2) while Cu2O/NiFe-LDH (20 s) generates a negative photocurrent (−0.3 mA.cm−2). Note that for reversed voltages (that is negative for bare Cu2O and positive for Cu2O/NiFe-LDH) both types of electrodes do not produce any significant photocurrent. Whereas, this photocurrent reversal is another evidence of the profound modification brought by the NiFe-LDH (20 s) overlayer on the PEC behaviour of Cu2O electrodes.
The Mott-Schottky plots comparison of Cu2O photocathode with and without NiFe-LDH (20 s) reveals the greatly increased number of charge carriers that has reached the interface is induced by NiFe-LDH cocatalyst (Figure S7). This unveils the function of NiFe-LDH as an efficient cocatalyst that improves the charge separation of Cu2O photocathode. Furthermore, in order to eliminate the possibilities that this photocurrent enhancement is induced by the metal valence state changes in NiFe-LDH, we have investigated the cyclic voltammetry behaviour of NiFe-LDH (Figure S8). Results indicate that at the low bias condition (less than −0.2 V vs Ag/AgCl), there is no reduction/oxidation behaviour on NiFe-LDH. This excludes the likelihoods of metal valence state changes-induced photocurrent enhancement of Cu2O/NiFe-LDH photocathode in low bias condition. The photoresponse of pure NiFe-LDH (300 s) has also been explored (Figure S9). Results show that NiFe-LDH itself generates very limited charge carrier upon illumination. This excludes the possibilities that the photocurrent enhancement of Cu2O/NiFe-LDH photocathode is induced by the increased number of photon-generated charge carriers induced by NiFe-LDH.
Another point worth notice is that the difference in photocurrent of Cu2O photocathode and Cu2O/NiFe-LDH photocathode becomes smaller with increased bias voltage. This is because the increased high applied voltage is able to efficiently separate the majority of photon-generated charge carriers. The effects of NiFe-LDH become less pronounced. As there is no difference for the total number of charge carriers as Cu2O is the only photon absorber (Figure S9). Thus, the maximum photocurrent of both electrodes have very little difference.
Electrochemical impedance spectroscopy
Electrochemical impedance spectroscopy (EIS) provides information about the interfacial property of the synthesized photocathode, which further reveals the efficient charge separation effect and improved electron injection property brought by NiFe-LDH layer (Fig. 3). The semi-circular diameter of the measured EIS stands for the charge carrier transfer resistance (Rct) that controls the electron transfer kinetics at the electrode/electrolyte interface37. The resistance of Cu2O/NiFe-LDH in the dark is much larger than that under illumination, indicating a higher number of charge carriers at the electrode interface. (Figure S10). In addition, as compared with bare Cu2O, the radius of the semicircle of Cu2O/NiFe-LDH is smaller under all the conditions (Fig. 3a,b and Figure S11).
An interesting observation is that by increasing the applied bias from −0.02 V to −0.12 V vs Ag/AgCl, the interface resistance increases for bare Cu2O but decreases for the Cu2O/NiFe-LDH samples. This phenomenon arises from the difference between the electrode/electrolyte interfaces with either Cu2O or NiFe-LDH. Under illumination over the voltage range −0.02/−0.12 V vs Ag/AgCl, the surface of bare Cu2O is predominantly charged with holes essentially because of the blockage of the electron transfer path from Cu2O to the electrolyte (see Fig. 4a). At more negative voltages, the number of holes decreases, thus resulting in a resistance increase of bare Cu2O. This is evidenced by the larger semi-circle diameter in the EIS (Fig. 3a). In contrast, deposition of a NiFe-LDH overlayer induces an appropriate energy level alignment with respect to the electrolyte redox levels so that electrons are efficiently transported towards the surface where they reduce water into H2 (Fig. 4b and Figure S12b). Electrons become predominant and the NiFe-LDH surface is negatively charged. The number of electrons increases with increasing negative voltage, as confirmed by the smaller semi-circle diameter in Fig. 3b. This demonstrates the key role of NiFe-LDH in introducing appropriate energy levels at the interface and the subsequent higher electron injection rate into the electrolyte.
Overall, the inefficient surface charge separation efficiencies and insufficient electron transfer in the electrolyte of bare Cu2O induces an overwhelming number of photogenerated electrons in the bulk. On the contrary, after coating by NiFe-LDH, electrons are able to transfer from electrode to electrolyte under very low external bias (Fig. 4). This results in a reduced number of electrons in the Cu2O layer, driving electrons from the counter-electrode to the Cu2O photocathode. As a result, the sample with and without NiFe-LDH have different electron flow directions for a given bias (Fig. 4 and Figure S12). This superior property makes Cu2O/NiFe-LDH an excellent candidate for photocathode in low or non-bias PEC systems.
Photostability
In order to evaluate the potential of Cu2O/NiFe-LDH photocathodes for H2 production, we tested their long-term stability under illumination at low voltages. It is well-known that Cu2O suffers from poor stability under illumination. The photogenerated electrons reduce Cu2O into Cu and photogenerated holes oxidize Cu2O into CuO. When oxidized, the illuminated area rapidly turning black. Various attempts have been made to solve this problem38,39,40,41, but the stability of Cu2O under low bias is rarely mentioned because of too low photocurrents. However, in the presence of the NiFe-LDH co-catalyst, the photostability of Cu2O under low bias can be explored. Observations indicate that Cu2O instability is mostly caused by the highly negative applied voltage, under which electrons that accumulate at the photocathode reduce Cu2O into metallic copper (Figure S13). The testing conditions in the literature are usually under ~0V vs RHE17, under which environment Cu2O tends to be reduced to a most stable state – metallic Cu. Whereas, our testing condition is −0.2 V vs Ag/AgCl under pH 6.5, which fell exactly in its stable condition range. This is supported by the fact that Cu2O samples under −0.2 V vs Ag/AgCl is also surprisingly stable after 40 hours of continuous illumination (Fig. 5). The stability tests of Cu2O with and without NiFe-LDH under −0.6 V vs Ag/AgCl show that NiFe-LDH also lengthens the stability of Cu2O under relatively high voltage (Figure S14). Whereas, the purpose of this study to improve Cu2O photocathode’s performance under its stable condition (green shadowed area in Figure S13) instead of spend numerous efforts in improving its stability under extreme conditions such as under strong negative bias.
H2 production
H2 evolution tests using Cu2O/NiFe-LDH (20 s) photocathodes have been conducted in a 25% methanol solution as a sacrificial reagent under visible light irradiation according to literature42. The faradaic efficiency is calculated according to ρ = nH2/(Q/2F), where nH2 is the amount of hydrogen generated, Q is the total amount of charge passed through the cell (C) and F is the faraday constant. As shown in Fig. 6, under low bias −0.2 V vs Ag/AgCl, the initial faradaic efficiency is 61% and it increases with time up to 78% before decreasing slowly after 800 minutes of illumination. There is no significant decrease in the performance during the first 12 hours. Over the following 10 hours the efficiency slightly decreases to 59%. When a higher bias of −0.8 V vs Ag/AgCl is applied, it shows good H2 evolution in the first 40 minutes. However, after 60 minutes H2 stops evolving and a progressive decrease of the faradaic efficiency takes place to become less than 5% after 1,000 minutes of illumination.
Conclusions
The growth of an ultrathin NiFe-LDH co-catalyst on Cu2O electrodes by electrodeposition induces a remarkable seven-fold increase of the photocurrent density under low applied voltages (typically 0.49 mA.cm−2 at ‒0.25 V vs Ag/AgCl, as compared to 0.07 mA.cm−2 for bare Cu2O). Electrochemical impedance spectroscopy reveals that NiFe-LDH (20 s) considerably reduces the Cu2O surface resistance thus allowing photogenerated electrons to be efficiently transported and injected into the electrolyte. Both results are induced by the appropriate band alignment induced by NiFe-LDH. When coated with NiFe-LDH (20 s) as a co-catalyst, the Cu2O photocathodes generate negative photocurrents with an excellent stability over 40 hours of continuous visible illumination under an external bias of –0.2 V vs Ag/AgCl. In Cu2O/NiFe-LDH (20 s) photocathodes, the combination of high photocurrents and long-term stability under low voltage allow hydrogen evolution. After 8 hours of continuous illumination, Cu2O/NiFe-LDH photocathodes exhibit a 78% Faradaic efficiency under –0.2 V vs Ag/AgCl, while the efficiency drops down to only 5% under −0.8 V vs Ag/AgCl. These results demonstrate that modified Cu2O/NiFe-LDH photoelectrodes are well-adapted to low-biased or self-biased PEC systems in view of artificial photosynthesis.
Methods
Preparation of Cu2O photocathodes
Prior to the deposition, 50 nm Au was deposited on FTO glasses via e-beam deposition to ensure the conductivity and reproducibility of the samples. Electrodeposition of Cu2O was carried out in a basic solution of lactate-stabilized copper sulfate consisting in 0.2 M CuSO4 (Sigma Aldrich) and 3 M lactic acid (Fisher Scientific) solution in deionized water. Afterward, 1 M NaOH was added to adjust the solution pH to 12. The basic environment ensures that deposited Cu2O is of p-type conduction. During deposition, the temperature was kept constant at 40 °C using a hot plate. The Cu2O thin films were deposited at a constant current density of −1 mA·cm−2 vs Ag/AgCl reference electrode using a three-electrode system (galvanostatic mode, Gamry Instruments, Inc.)
Electrodeposition of the NiFe-LDH co-catalyst
Electrodeposition of NiFe-LDH is realized using Cu2O as the working electrode, together with a Pt counter-electrode and Ag/AgCl as the reference electrode. The solution for electrodeposition of NiFe-LDH consists in a mixture of 0.2 M [Ni(NO3)2∙6H2O] and 0.1 M [Fe(NO3)3∙9H2O] in 50 ml of deionized water. A constant potential of −1.0 V vs Ag/AgCl is applied during various periods of time in the range 20–300 s, leading to different morphologies. For less than 60 s, NiFe-LDH does not reveal a clear nanoflake morphology, although photocurrent is already improved as compared with bare Cu2O. A 150 s deposition time is required to obtain visible XRD peaks due to the intensity limit.
Morphological characterizations
The crystal phase of the synthesized photocathodes were studied using a Shimadzu thin film X-ray diffractometer with a Cu Ka excitation (λ = 1.54 Å). Microscopic morphologies including lattice analysis of scraped particles were obtained using field emission scanning electron microscopy (FESEM, JEOL JSM-7600F) and high resolution transmission electron microscopy (HRTEM, JEOL-2100F) operating at 200 kV.
Photoelectrochemical measurements
All PEC measurements were conducted in a 0.5 M Na2SO4 electrolyte using a three-electrode configuration with synthesized sample as the working electrodes, Pt and Ag/AgCl electrodes being used as the counter and reference electrodes, respectively. The inter-electrode spacing was ~1 cm. Photocurrents were recorded using a PCI4/300™ potentiostat equipped with PHE200™ software (Gamry Instruments, Inc.). The working electrodes were exposed to the AM 1.5 light from a solar simulator equipped with a 300 W Xe-lamp (HAL-320, Asahi Spectra Co., Ltd.). The incident light intensity was 100 mW·cm−2 and the sample illumination area 0.28 cm2. Linear sweep voltammetry (LSV) was carried out under both dark and illumination conditions with a scan rate of 5 mV·s−1 with chopped light irradiation (frequency = 0.2 Hz). Stability tests were conducted by chronoamperometry under a potential of ‒0.2 V vs Ag/AgCl in a 0.5 M Na2SO4 solution. Mott-Schottky measurements were conducted using the same equipment and configuration with Mott-Schottky mode in 0.5 M Na2SO4 electrolyte with a frequency of 300 Hz in the potential range of chemical stability. Cyclic voltammetry (CV) was carried out using the same equipment and configuration in 0.5 M Na2SO4 electrolyte at the potential window 0.3 V to −0.4 V vs Ag/AgCl with scan rate of 100 mV S−1.
Electrochemical impedance spectroscopy
Electrochemical impedance spectroscopy (EIS) was conducted using the same equipment and configuration as for the PEC measurements, which is a PCI4/300™ potentiostat equipped with EIS300™ software (Gamry Instruments, Inc.). Potentiostatic mode was applied under white light illumination (AM1.5, 100 mW·cm−2) at an applied voltage of −0.2 V vs. Ag/AgCl. AC perturbations of amplitude 5 mV were superimposed with frequency in the range 0.01–100 kHz. Equivalent circuit modeling and curve fitting were performed using the Echem Analyst™ software (Gamry Instruments, Inc.)
Hydrogen production
The amount of hydrogen generated was measured using a well-sealed glass cell (100 ml) mounted with a quartz window. The Cu2O and Cu2O/NiFe-LDH working electrodes (sample illumination area = 1 cm2) were exposed to the light of a solar simulator equipped with a 300 W Xe-lamp (HAL-320, Asahi Spectra Co., Ltd.) and the incident AM 1.5 light intensity was 100 mW·cm−2. The working electrode, Pt counter-electrode and Ag/AgCl reference electrode were suspended in a solution (pH = 7) containing 30 ml of 0.1 M Na2SO4 and 10 ml of methanol (25%). Prior to testing, the reactor was repeatedly vacuum-pumped and purged with argon to remove the residual air. Then, an external bias is applied on the working electrode and the lamp is turned on. The amount of generated H2 gas was quantitatively analyzed by a gas chromatograph (Shimadzu GC-2014; molecular sieve 5 Å, TCD detector, Ar carrier gas).
Additional Information
How to cite this article: Qi, H. et al. Cu2O Photocathode for Low Bias Photoelectrochemical Water Splitting Enabled by NiFe-Layered Double Hydroxide Co-Catalyst. Sci. Rep. 6, 30882; doi: 10.1038/srep30882 (2016).
References
Fujishima, A. & Honda, K. Electrochemical Photolysis of Water at a Semiconductor Electrode. Nature 238, 37–39 (1972).
Robel, I., Subramanian, V., Kuno, M. & Kamat, P. V. Quantum dot solar cells. Harvesting light energy with CdSe nanocrystals molecularly linked to mesoscopic TiO2 films. J Am Chem Soc 128, 2385–2393 (2006).
Stergiopoulos, T., Arabatzis, I. M., Katsaros, G. & Falaras, P. Binary polyethylene oxide/titania solid-state redox electrolyte for highly efficient nanocrystalline TiO2 photoelectrochemical cells. Nano Lett 2, 1259–1261 (2002).
Yang, X. Y. et al. Nitrogen-Doped ZnO Nanowire Arrays for Photoelectrochemical Water Splitting. Nano Lett 9, 2331–2336 (2009).
Fichou, D. et al. Extension of the Photoresponse of Semiconducting Zinc-Oxide Electrodes by 3d-Impurities Absorbing in the Visible Region of the Solar Spectrum. J Electroanal Chem 188, 167–187 (1985).
Jakani, M. et al. Photoelectrochemical Properties of Zinc-Oxide Doped with 3d Elements. J Solid State Chem 56, 269–277 (1985).
Cao, L. L., Yuan, J., Chen, M. X. & Shangguan, W. F. Photocatalytic energy storage ability of TiO2-WO3 composite prepared by wet-chemical technique. J Environ Sci-China 22, 454–459 (2010).
Wang, G. M. et al. Solar driven hydrogen releasing from urea and human urine. Energ Environ Sci 5, 8215–8219 (2012).
Qin, D. D. et al. Dense layers of vertically oriented WO3 crystals as anodes for photoelectrochemical water oxidation. Chem Commun 48, 729–731 (2012).
Qi, H. et al. Triple-layered nanostructured WO3 photoanodes with enhanced photocurrent generation and superior stability for photoelectrochemical solar energy conversion. Nanoscale 6, 13457–13462 (2014).
Liu, C. J. et al. In situ synthesis of Bi2S3 sensitized WO3 nanoplate arrays with less interfacial defects and enhanced photoelectrochemical performance. Sci Rep-Uk 6 (2016).
Cesar, I., Kay, A., Martinez, J. A. G. & Gratzel, M. Translucent thin film Fe2O3 photoanodes for efficient water splitting by sunlight: Nanostructure-directing effect of Si-doping. J Am Chem Soc 128, 4582–4583 (2006).
McShane, C. M. & Choi, K. S. Photocurrent Enhancement of n-Type Cu2O Electrodes Achieved by Controlling Dendritic Branching Growth. J Am Chem Soc 131, 2561–2569 (2009).
Minguez-Bacho, I., Courte, M., Fan, H. J. & Fichou, D. Conformal Cu2S-coated Cu2O nanostructures grown by ion exchange reaction and their photoelectrochemical properties. Nanotechnology 26, 185401–185411 (2015).
Kang, Z. et al. Electronic Structure Engineering of Cu2O Film/ZnO Nanorods Array All-Oxide p-n Heterostructure for Enhanced Photoelectrochemical Property and Self-powered Biosensing Application. Sci Rep-Uk 5 (2015).
Luo, W. J. et al. Solar hydrogen generation from seawater with a modified BiVO4 photoanode. Energ Environ Sci 4, 4046–4051 (2011).
Paracchino, A., Laporte, V., Sivula, K., Gratzel, M. & Thimsen, E. Highly active oxide photocathode for photoelectrochemical water reduction. Nat Mater 10, 456–461 (2011).
Yang, L. X. et al. High Efficient Photocatalytic Degradation of p-Nitrophenol on a Unique Cu2O/TiO2 p-n Heterojunction Network Catalyst. Environ Sci Technol 44, 7641–7646 (2010).
Wu, L. L., Tsui, L. K., Swami, N. & Zangari, G. Photoelectrochemical Stability of Electrodeposited Cu2O Films. J Phys Chem C 114, 11551–11556 (2010).
Paracchino, A., Brauer, J. C., Moser, J. E., Thimsen, E. & Graetzel, M. Synthesis and Characterization of High-Photoactivity Electrodeposited Cu2O Solar Absorber by Photoelectrochemistry and Ultrafast Spectroscopy. J Phys Chem C 116, 7341–7350 (2012).
Zhang, Z. H. & Wang, P. Highly stable copper oxide composite as an effective photocathode for water splitting via a facile electrochemical synthesis strategy. J Mater Chem 22, 2456–2464 (2012).
Wijesundera, R. P., Solar Cells - Thin-Film Technologies, L. A. Kosyachenko (Ed.), 2011, ISBN: 978-953-307-570-9.
Wang, M. Y. et al. p-n Heterojunction photoelectrodes composed of Cu2O-loaded TiO2 nanotube arrays with enhanced photoelectrochemical and photoelectrocatalytic activities. Energ Environ Sci 6, 1211–1220 (2013).
Tilley, S. D., Schreier, M., Azevedo, J., Stefik, M. & Graetzel, M. Ruthenium Oxide Hydrogen Evolution Catalysis on Composite Cuprous Oxide Water-Splitting Photocathodes. Adv Funct Mater 24, 303–311 (2014).
Zhang, Y. Z. et al. Photovoltaic performance enhancement of Cu2O photocathodes by electrostatic adsorption of polyoxometalate on Cu2O crystal faces. Rsc Adv 4, 1362–1365 (2014).
Sideris, P. J., Nielsen, U. G., Gan, Z. H. & Grey, C. P. Mg/Al ordering in layered double hydroxides revealed by multinuclear NMR spectroscopy. Science 321, 113–117 (2008).
Fan, G. L., Li, F., Evans, D. G. & Duan, X. Catalytic applications of layered double hydroxides: recent advances and perspectives. Chem Soc Rev 43, 7040–7066 (2014).
Liu, J. P., Li, Y. Y., Huang, X. T., Li, G. Y. & Li, Z. K. Layered double hydroxide nano- and microstructures grown directly on metal substrates and their calcined products for application as Li-ion battery electrodes. Adv Funct Mater 18, 1448–1458 (2008).
Lu, Z. et al. Three-dimensional NiFe layered double hydroxide film for high-efficiency oxygen evolution reaction. Chem Commun 50, 6479–6482 (2014).
Gong, M. et al. An Advanced Ni-Fe Layered Double Hydroxide Electrocatalyst for Water Oxidation. J Am Chem Soc 135, 8452–8455 (2013).
Li, X. D., Yang, W. S., Li, F., Evans, D. G. & Duan, X. Stoichiometric synthesis of pure NiFe2O4 spinel from layered double hydroxide precursors for use as the anode material in lithium-ion batteries rtyree. J Phys Chem Solids 67, 1286–1290 (2006).
Zheng, S. F. et al. An Inexpensive Co-Intercalated Layered Double Hydroxide Composite with Electron Donor-Acceptor Character for Photoelectrochemical Water Splitting. Sci Rep-Uk 5 (2015).
Shao, M. F., Ning, F. Y., Wei, M., Evans, D. G. & Duan, X. Hierarchical Nanowire Arrays Based on ZnO Core-Layered Double Hydroxide Shell for Largely Enhanced Photoelectrochemical Water Splitting. Adv Funct Mater 24, 580–586 (2014).
Xu, D., Rui, Y., Li, Y., Zhang, Q. & Wang, H. Zn-Co layered double hydroxide modified hematite photoanode for enhanced photoelectrochemical water splitting. Appl Surf Sci 358, 436–442 (2015).
Newman, S. P., Jones, W., O’Connor, P. & Stamires, D. N. Synthesis of the 3R(2) polytype of a hydrotalcite-like mineral. J Mater Chem 12, 153–155 (2002).
Hansen, H. C. B., Koch, C. B. & Taylor, R. M. Synthesis and Characterization of Cobalt(Ii)-Iron(Iii) Hydroxide Carbonate, a Layered Double Hydroxide Belonging to the Pyroaurite Group. J Solid State Chem 113, 46–53 (1994).
Zang, J. F. et al. Well-aligned cone-shaped nanostructure of polypyrrole/RuO2 and its electrochemical supercapacitor. J Phys Chem C 112, 14843–14847 (2008).
Juodkazyte, J. et al. Study on copper oxide stability in photoelectrochemical cell composed of nanostructured TiO2 and CuxO electrodes. Electrochim Acta 137, 363–371 (2014).
Paracchino, A. et al. Ultrathin films on copper(I) oxide water splitting photocathodes: a study on performance and stability. Energ Environ Sci 5, 8673–8681 (2012).
Morales-Guio, C. G. et al. Photoelectrochemical Hydrogen Production in Alkaline Solutions Using Cu2O Coated with Earth-Abundant Hydrogen Evolution Catalysts. Angew Chem Int Edit 54, 664–667 (2015).
Zhao, Y. X. et al. Hierarchical branched Cu2O nanowires with enhanced photocatalytic activity and stability for H2 production. Nanoscale 6, 195–198 (2014).
Wick, R. & Tilley, S. D. Photovoltaic and Photoelectrochemical Solar Energy Conversion with Cu2O. J Phys Chem C 119, 26243–26257 (2015).
Acknowledgements
The authors wish to thank the support from the Ministry of Education in Singapore under the AcRF Tier2 grant (MOE2014-T2-1-132) and from the National Research Foundation (NRF) Singapore through its Campus for Research Excellence and Technological Enterprise (CREATE) program.
Author information
Authors and Affiliations
Contributions
H.Q. and J.W. conceived, designed and performed the experiments. H.Q., J.W., D.F. and Z.C. analyzed the data. H.Q. and D.F. co-wrote the paper. Z.C. provides guidance and revises the manuscript. All authors discussed the results and reviewed the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Qi, H., Wolfe, J., Fichou, D. et al. Cu2O Photocathode for Low Bias Photoelectrochemical Water Splitting Enabled by NiFe-Layered Double Hydroxide Co-Catalyst. Sci Rep 6, 30882 (2016). https://doi.org/10.1038/srep30882
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep30882
- Springer Nature Limited
This article is cited by
-
Recent trends in photoelectrochemical water splitting: the role of cocatalysts
NPG Asia Materials (2022)
-
Nanocarbon-Enhanced 2D Photoelectrodes: A New Paradigm in Photoelectrochemical Water Splitting
Nano-Micro Letters (2021)
-
Modification of large area Cu2O/CuO photocathode with CuS non-noble catalyst for improved photocurrent and stability
Scientific Reports (2020)
-
Metal oxides nanoparticles via sol–gel method: a review on synthesis, characterization and applications
Journal of Materials Science: Materials in Electronics (2020)
-
Highly efficient and photostable photocathodes based on CuWO4/Cu2O nanostructured thin films
Journal of the Iranian Chemical Society (2020)