Abstract
Photoelectrochemical (PEC) water splitting is an appealing approach for “green” hydrogen generation. The natural p-type semiconductor of Cu2O is one of the most promising photocathode candidates for direct hydrogen generation. However, the Cu2O-based photocathodes still suffer severe self-photo-corrosion and fast surface electron-hole recombination issues. Herein, we propose a facile in-situ encapsulation strategy to protect Cu2O with hydrogen-substituted graphdiyne (HsGDY) and promote water reduction performance. The HsGDY encapsulated Cu2O nanowires (HsGDY@Cu2O NWs) photocathode demonstrates a high photocurrent density of −12.88 mA cm−2 at 0 V versus the reversible hydrogen electrode under 1 sun illumination, approaching to the theoretical value of Cu2O. The HsGDY@Cu2O NWs photocathode as well as presents excellent stability and contributes an impressive hydrogen generation rate of 218.2 ± 11.3 μmol h−1cm−2, which value has been further magnified to 861.1 ± 24.8 μmol h−1cm−2 under illumination of concentrated solar light. The in-situ encapsulation strategy opens an avenue for rational design photocathodes for efficient and stable PEC water reduction.
Similar content being viewed by others
Introduction
Large-scale application of hydrogen as clean fuel plays a critical and indispensable role in revolutionizing the current fossil-fuel-based energy system. Hydrogen is as well as an important chemical feedstock and building block, which has been widely utilized in petroleum refining, ammonia synthesis, and core chemicals production. In various sustainable hydrogen production routes, photoelectrochemical (PEC) water splitting is regarded as one of the promising hydrogen generation systems1,2,3, in which, the solar energy collection and water electrolysis are integrated in one device. The PEC device with p-type semiconductor as photocathodes (with electron as photo-generated minority charge) can directly generate hydrogen on the surface of photoelectrodes through converting renewable and intermittent solar energy into chemical energy and storing in chemical bonds of hydrogen4. Currently, PEC water reduction is well developed with inorganic p-type semiconductors, such as silicon5,6, metal oxides7,8, metal phosphides9, and metal sulfides10,11. Cuprous oxide (Cu2O), a natural p-type semiconductor, owns a narrow direct bandgap of 2.0 eV, high theoretical photocurrent density of −14.7 mA cm−2 and photoconversion efficiency of 18%, suitable conduction band position (0.7 V higher than the hydrogen evolution potential), and earth-abundance and low cost12,13,14,15, all of these merits distinguish it to be one of the most promising photocathode candidates for PEC hydrogen generation. Nevertheless, the practical utilization of Cu2O-based photocathode for PEC water reduction is still impeded by its intrinsic drawbacks of self-photo-corrosion in aqueous solution and fast surface electron-hole recombination16,17, which leads to severe stability and inefficiency issues respectively. To alleviate the above-mentioned limitations, a series of surface protection and modification strategies have been proposed18,19. Grätzel and his co-workers in their pioneering work has proposed a multiple-protective-layer strategy with a precision atomic layer deposition method to reach a good stability and high photocathodic current density of −7.6 mA cm−2 at potential of 0 V vs RHE (reversible hydrogen electrode) after coupling noble metal electrocatalyst of Pt nanoparticles12. Our group have also reported that the stability and PEC performance of Cu2O photocathodes have been improved by using carbon, CuO, TiO2, and Cu2S as multi-functional layers20,21,22,23. Nevertheless, there is still a big gap between the practical performance and the theoretically maximum photocurrent density on the Cu2O-based photocathodes. Therefore, the exploration of “ideal” protective and promotive layer on Cu2O photocathode is still a big challenge.
Very recently, an acetylenic carbon-rich framework of hydrogen-substituted graphdiyne (HsGDY) is proposed and synthesized by Li group and reported its excellent electronic conductivity and high stability in aqueous solution24. The HsGDY is an extended π-conjugated carbon skeleton comprised of butadiyne linkages and benzene rings. Different from graphene and graphdiyne, the HsGDY has lower atom density, larger pore size with H group in the pores, which would lead to excellent hydrogen ion mobility24. Feng and co-workers have even proposed to synthesize HsGDY, named poly(1,3,5-triethynylbenzene) (PTEB) in their paper, on flat copper foil surface and used as free-standing photocathode with a photocurrent density of 10 μA cm−225,26. Our group have also prepared the HsGDY on porous copper foam (CF) and reached a high photocurrent density of 1.03 mA cm−2 (geometric area)27. The HsGDY presents distinguishing advantages of (1) high stability in aqueous solution, (2) robustness under illumination, (3) excellent solid-state charge transfer characteristics, (4) fast hydrogen ion permeation, and (5) facile film-forming processability on copper-based substrates28,29, which endow it great potentials as “ideal” candidate to protect and promote Cu2O photocathode for efficient and stable PEC applications.
Herein, a photocathode of HsGDY encapsulated Cu2O nanowire (HsGDY@Cu2O NWs) on three-dimensional porous CF is proposed and prepared. The HsGDY is in-situ generated on the surface of Cu2O NWs through a Cu(I) ion mediated Glaser coupling reaction with 1,3,5-triethynylbenzene (TEB) as precursor. The HsGDY@Cu2O NWs photocathode demonstrates a high photocurrent density of −12.88 mA cm−2 at 0 V vs RHE, approaching to the theoretical photocurrent density of Cu2O photocathode under illumination of AM 1.5 G solar light, and a high photoconversion efficiency of 2% is achieved either. In addition, the HsGDY@Cu2O NWs photocathode presents excellent stability with only 7.5% loss of photocurrent density after 24 h PEC operation. The efficient PEC performance and high stability enable HsGDY@Cu2O NWs photocathode to reach an impressive hydrogen generation rate of 218.2 ± 11.3 μmol h−1cm−2. Furthermore, the HsGDY@Cu2O NWs photocathode has been integrated into a concentrated solar light system, and a high photocurrent density of −50.7 mA cm−2 and hydrogen generation rate of 861.1 ± 24.8 μmol h−1cm−2 are obtained under 10-sun illumination. The HsGDY presents multi-function of protective layer, electron transfer layer, and kinetically catalytic layer. The in-situ encapsulation strategy of dual-functional HsGDY layer opens up an avenue for rational design of Cu2O-based photocathodes for efficient and stable PEC water reduction.
Results
Preparation and characterization of HsGDY@Cu2O NWs
The fabrication processes of HsGDY@Cu2O NWs on CF are schematically illustrated in Fig. 1a. The CF was rationally selected as substrate of photocathode due to its highly interconnected macroporous structure that brought large surface area and fast electrolyte transfer rate, in addition, the surface metallic Cu can be easily in situ converted to Cu oxides, and the rest metallic Cu skeleton can be directly used as current collector with high electronic conductivity. The HsGDY@Cu2O NWs/CF was fabricated through three-step processes of electrochemical- anodization/annealing/Glaser-coupling. The detailed synthesis processes can be found in Method. In brief, the CF was electrochemically anodized in alkali solution to form Cu(OH)2 NWs, which then underwent an annealing process in nitrogen atmosphere and converted to Cu2O NWs, finally, the Cu2O NWs was conformally coated with microporous HsGDY layers. As presented in Fig. 1b, Glaser coupling reaction occurred with 1,3,5-triethynylbenzene (TEB) as precursor, piperidine as ligand, pyridine as solvent, and Cu(I) ion as catalyst (slightly dissolved from Cu2O in polar solvent), and the HsGDY layer was generated with giant two-dimensional network structure that comprised large organic hexatomic rings as the construction unit and alternating-distributed benzene ring and alkynyl as sub-units.
a Schematic illustration of the fabrication of HsGDY@Cu2O/CF photocathode; b Synthesis of HsGDY with Cu-mediated Glaser coupling reaction; SEM images of c Cu2O NWs and d HsGDY@Cu2O NWs; e Enlarged SEM image of HsGDY@Cu2O NWs; f TEM image of HsGDY@Cu2O NWs; g, h HRTEM images of HsGDY on the surface of Cu2O NWs; i Raman spectrum of HsGDY@Cu2O NWs, the inset is the core-level XPS of C 1s of HsGDY@Cu2O NWs; j1 HADDF-STEM image and corresponding EDX mapping images of j2 Cu, j3 O, j4 C elements, and j5 EDX line scan curves.
The micro-morphologies of Cu2O NWs and HsGDY@Cu2O NWs were characterized from scanning electron microscope (SEM) and transmission electron microscope (TEM). As depicted in Fig. 1c, the Cu2O sample showed a tapered off nanowire structure with length of several micrometers. For HsGDY@Cu2O NWs sample, as presented in Fig. 1d, e, the nanowire structures were still well maintained with much rougher and gossamer-like surface, indicated the coating of HsGDY on the surface of Cu2O NWs. The elemental compositions of HsGDY@Cu2O NWs were detected from energy dispersive X-ray spectrum (EDS) (Supplementary Fig. 1) and only Cu, O, and C elements were identified. The TEM image in Fig. 1f further revealed the conformal nanowire structure with clear HsGDY layer covered on the surface of Cu2O NWs. In addition, the high-resolution TEM (HRTEM) image in Fig. 1g uncovered stacked sheets of HsGDY. Surprisingly, some small dots with size of ~3 nm were determined to be embedded on HsGDY sheet. Closer observation as shown in Fig. 1h, clear lattice with interplanar spacing of 0.21 nm can be ascribed to (200) plane of Cu2O. The formation of Cu2O nanodots was probably due to the micro-dissociation of Cu2O NWs in polar solvents, which lead to the production of Cu(I) ions and mediated the Glaser coupling reaction, then, after the formation of HsGDY, the Cu(I) ions converted to the state of Cu2O and accumulated in HsGDY sheets.
The crystal structure of HsGDY@Cu2O NWs was revealed from X-ray diffraction (XRD) pattern (Supplementary Fig. 2), and all diffraction peaks can be ascribed to metallic Cu and Cu2O. No diffraction peak of HsGDY was detected, which implied amorphous nature of HsGDY. To further indicate the presence of HsGDY framework, Raman spectrum and x-ray photoelectron spectrum (XPS) of HsGDY@Cu2O NWs were measured and presented in Fig. 1i. For Raman analysis, the strongest peak at 2215 cm−1 can be ascribed to the typical acetylenic bond (C ≡ C) stretching vibration, and the peaks in 1500–1650 cm−1 can be assigned to the stretching vibrations of aromatic ring with a strong G-band peak located at 1580 cm−125, which suggested that the samples possessed abundant aromatic rings. Except these typical Raman peaks of HsGDY, an unusual peak at 1993 cm−1 with relative weak intensity has been observed, which can be ascribed to the formation of Cu-metalated C ≡ C stretching30. The XPS survey revealed that the HsGDY@Cu2O NWs contained only elemental copper, O, and carbon (Supplementary Fig. 3), in addition, compared with pristine Cu2O NWs, the HsGDY@Cu2O NWs presented much higher intensity of carbon element. The core-level XPS C 1 s of HsGDY@Cu2O NWs was depicted in the inset of Fig. 1i, and the deconvoluted subpeaks at 284.6 eV and 285.4 eV can be ascribed to C = C (sp2) and C ≡ C (sp), respectively30. The area ratio of sp2 and sp carbon was close to 1:1, in accordance with the structure of HsGDY, and thus provided further robust evidence for the formation of HsGDY. Except the two main subpeaks, the peak at 287.1 eV can be assigned to C–O. However, compared to binding energy of 287.5 eV of C–O bond obtained from individual HsGDY24, the negative shift of binding energy implied the potential electron transfer from Cu2O to HsGDY. To further reveal the elemental distribution on single HsGDY@Cu2O nanowire, high-angle annular dark-field scanning transmission electron microscopy (HADDF-STEM) image (Fig. 1j1) and corresponding EDS elemental mapping images were measured and revealed uniform distribution of Cu (Fig. 1j2), O (Fig. 1j3), and C (Fig. 1j4) elements on nanowire. In addition, the line scan EDS curves (Fig. 1j5) presented obvious expansion of carbon element distribution on single HsGDY@Cu2O nanowire, which further indicated encapsulation of Cu2O nanowire with HsGDY. All of the above experimental results indicated intense interaction between Cu2O and HsGDY. The unique encapsulation structure of HsGDY@Cu2O NWs portended promising charge transfer activity and excellent PEC performance can be expected.
The PEC performance of HsGDY@Cu2O NWs
The PEC water reduction performance of HsGDY@Cu2O NWs was evaluated by linear sweep voltammetry (LSV) method under illumination of simulated solar light (AM 1.5 G, 100 mW cm−2). The Glaser coupling reaction durations have been optimized to maximize the PEC performance of HsGDY@Cu2O NWs with different HsGDY thickness (Supplementary Fig. 4). As presented in Fig. 2a, both photocathodes under dark conditions did not show measurable HER activity in the potential window. While, under illumination, the optimized HsGDY@Cu2O NWs/CF photocathode showed a high photocurrent density of −12.88 mA cm−2 at 0 V vs RHE, much higher than the photocurrent density of −4.2 mA cm−2 on pristine Cu2O NWs/CF photocathode. The high photocurrent density value was closely approaching to the theorical maximum photocurrent density of Cu2O-based photocathodes12. The LSV plot of HsGDY@Cu2O NWs/CF photocathode under illumination of chopped light was also measured and presented fast light-dark current conversion with similar values (Supplementary Fig. 5). In addition, the electrochemical active surface area of HsGDY/Cu2O NWs were also estimated through Helmholtz double layer capacitance measurements31. The electrochemical active surface area can be measured to be 1.38 ± 0.63 cm2 (Supplementary Fig. 6), therefore, the intrinsic photocurrent density of HsGDY@Cu2O NWs/CF can be converted to be 9.33 ± 2.92 mA cm−2, which value indicated the efficient intrinsic PEC activity of HsGDY@Cu2O NWs. The HsGDY on pristine CF was also prepared and the corresponding PEC and optical properties have been measured (Supplementary Fig. S7). The relative low PEC performance further implied the decisive role of charge transfer of HsGDY layer.
a LSV plots of Cu2O NWs and HsGDY@Cu2O NWs in dark and under illumination of simulated solar light (AM 1.5 G, 100 mW cm−2), recorded with scan rate of 5 mV s−1 in 0.1 M Na2SO4 solution with pH = 4.9; b Photoconversion efficiency of Cu2O NWs and HsGDY@Cu2O NWs; c IPCE plots of Cu2O NWs and HsGDY@Cu2O NWs under a constant potential of 0 V vs RHE in wavelength region from 300 nm to 800 nm; d Stability measurement of HsGDY@Cu2O NWs at potential of 0 V vs RHE, the inset is the chronoamperometric curve on Cu2O NWs; e Hydrogen generation on HsGDY@Cu2O NWs/CF photocathodes at potential of 0 V vs RHE under illumination of simulated solar light (100 mW cm−2, AM 1.5 G).
The photoconversion efficiencies of Cu2O NWs and HsGDY@Cu2O NWs photocathodes were calculated using equation of η = JPmaxVPmax/Pin, where JPmax and VPmax are the current density (mW cm−2) and photovoltage (V vs RHE) at the maximum power point and Pin (mW cm−2) is the incoming light flux (100 mW cm−2)32. The plots of photoconversion efficiency vs potential vs RHE were presented in Fig. 2b, where, the Cu2O NWs exhibited an optimal conversion efficiency of 0.40% at 0.197 V, while, the HsGDY@Cu2O NWs achieved a much higher optimal conversion efficiency of 2.0% at 0.275 V.
To better elucidate the enhancement of PEC performance after HsGDY encapsulated Cu2O NWs, incident photon-to-current-conversion efficiency (IPCE) measurements were conducted on Cu2O NWs and HsGDY@Cu2O NWs. The IPCE value was estimated and calculated with following equation:33
where I is the photocurrent density (mA cm−2), Plight is the incident light irradiance (mW cm−2), and λ is the incident light wavelength (nm). As presented in Fig. 2c, both Cu2O NWs and HsGDY@Cu2O NWs showed PEC response threshold at ~650 nm, whereas, the HsGDY@Cu2O NWs exhibited considerably enhanced PEC performance in broad wavelength region from 650 nm to 320 nm. The photocurrent density under illumination of solar light can be integrated from the IPCE values and solar irradiance and the corresponding integrated photocurrent density was 12.82 mA cm−2 (Supplementary Fig. 8), which value was close to photocurrent density of 12.88 mA cm−2 under illumination of simulated solar light with AM 1.5 G filter. The insignificant variation can be ascribed to the slight difference of irradiance spectra of simulated solar light and solar light. More interestingly, the IPCE value on HsGDY@Cu2O NWs increased rapidly with decreasing wavelength in a small region between 650 nm to 570 nm, and reached the highest value of 93.3% at wavelength of 580 nm. In addition, IPCE plots on HsGDY@Cu2O NWs at different applied potentials have been recorded (Supplementary Fig. 9). The HsGDY@Cu2O NWs at applied potential of +0.4 V vs RHE presented slow IPCE increase tendency, which can be ascribed to the slow charge transfer due to the relative positive potential. While, at applied potential of −0.4 V vs RHE, the IPCE plot displayed similar increase tendency with that at 0 V vs RHE with higher IPCE values. The fast IPCE increase indicated that the coupling of HsGDY can effectively promote the charge separation on Cu2O NWs, and greatly increased the probability of photoelectrons generation. In addition, a unique multi-band shape of the IPCE curve of HsGDY@Cu2O NWs can be observed. This phenomenon may be ascribed to the photon competition between HsGDY and Cu2O, and thus presented optical absorption “filter” property at special wavelength.
Long-term PEC stability is crucial for practical applications of photoelectrodes, especially for Cu2O-based photocathodes. The PEC stability of Cu2O NWs and HsGDY@Cu2O NWs were evaluated with a steady-state chronoamperometry, and the results were presented in Fig. 2d. The photocurrent on Cu2O NWs rapidly decayed and remained 24.2% to its initial photocurrent after 1 h illumination (the inset in Fig. 2d). Nevertheless, the photocurrent on HsGDY@Cu2O NWs maintained 93.6% of its original value after continuous illumination for 80 h, and 82.5% of original photocurrent was remained after 100 h measurements. The encapsulation strategy with HsGDY indeed protected the Cu2O NWs from self-photo-corrosion. With longer stability measurements, after 120 h duration, the photocurrent decreased to ~3.5 mA cm−2, which can be ascribed to the partial broken of the HsGDY@Cu2O layer due to the violently producing hydrogen bubbles (Supplementary Fig. 10). The chemical compositions after long-term measurements were as well as characterized, and the emergence of metallic Cu species also suggested the exposure of copper foam surface after falling off the HsGDY@Cu2O NWs (Supplementary Fig. 11).
Furthermore, the practical application of PEC water reduction for hydrogen generation on HsGDY@Cu2O NWs photocathode were evaluated and presented in Fig. 2e. The hydrogen generation experiments were repeated for 4 cycles with one cycle of 6 h, and an impressive generation rate of 218.2 ± 11.3 μmol h−1 cm−2 was achieved. The Faraday efficiency for PEC hydrogen generation was also calculated to be 96.1 ± 2.3% during the entire water reduction process, which indicated that almost of the photogenerated carriers virtually participated into the process of hydrogen generation. We have electrodeposited Pt nanoparticles on the surface of HsGDY, and no further increase of the photocurrent density can be recorded (Supplementary Fig. 12), which implied that the HsGDY worked as kinetically active layer for hydrogen generation. The acetylene units (-C ≡ C-) can be well regarded as efficient active sites for PEC hydrogen generation26,34,35. Up to now, the excellent PEC performance of HsGDY@Cu2O NWs has proposed that the encapsulation strategy with HsGDY on Cu2O NWs was a very successful attempt, and to the best of our knowledge, the HsGDY@Cu2O NWs contributed the highest photocurrent density value ever reported on Cu2O materials with/without using of noble metal co-catalysts (Supplementary Fig. 13 and Supplementary Table 1). The HsGDY presented multi-function of protective layer, electron transfer layer, and kinetically catalytic layer, all of these roles contributed to the efficient PEC water reduction for hydrogen generation.
Mechanism of enhanced PEC performance on HsGDY@Cu2O NWs
To deeply reveal the mechanism of significantly enhanced PEC performance on HsGDY@Cu2O NWs, a series of experiments and calculation were conducted. The optical absorption property of Cu2O NWs and HsGDY@Cu2O NWs were measured and the UV-Vis-NIR diffuse reflection spectra were presented in Fig. 3a. Both samples showed similar absorption threshold at ~640 nm, but the HsGDY@Cu2O NWs depicted higher absorbance in the range of 300–500 nm. The band gap values of these two materials were also estimated from the corresponding Tauc plots. As shown in Fig. 3b, both samples presented the same band gap value of 1.98 eV. Although the encapsulation Cu2O NWs with HsGDY did not change the band gap, the absorbance was increased in a wide spectral range, which was beneficial to the improvement of PEC performance. In addition, the fluorescence emission spectra of Cu2O NWs and HsGDY@Cu2O NWs have been recorded and presented in Fig. 3c. The Cu2O NWs showed few sharp and intensive emission fluorescence peaks, while, after encapsulation with HsGDY, the fluorescence emission has been severely quenched, which helped to gain more insights into the potential charge carrier transfer between HsGDY and Cu2O NWs.
a Optical absorption spectra of Cu2O NWs and HsGDY@Cu2O NWs; b Tauc plots of Cu2O NWs and HsGDY@Cu2O NWs; c Fluorescence spectra of Cu2O NWs and HsGDY@Cu2O NWs; d DFT calculation of difference charge density on the interface of HsGDY and Cu2O; Core-level XPS of e Cu 2p and f O 1 s of Cu2O NWs and HsGDY@Cu2O NWs; g valence band XPS of Cu2O NWs and HsGDY@Cu2O NWs; h Mott-Schottky plots of Cu2O NWs and HsGDY@Cu2O NWs; i Band energy structure diagrams of Cu2O NWs and HsGDY@Cu2O NWs.
The potential electron transfer direction between Cu2O NWs and HsGDY has been predicted by density functional theory (DFT) calculations. All calculations were performed using CP2K quantum chemistry software package with Perdew–Burke–Ernzerhof (PBE) parametrization of generalized gradient approximation to describe the exchange-correlation part in Hamiltonian36. The HsGDY@Cu2O NWs heterostructures were constructed by matching the layer HsGDY on the Cu2O (200) surface based on the experimental results. As shown in Fig. 3d, clear spatial charge redistributions on the interface of HsGDY and Cu2O was depicted, and based on the Mulliken population analysis, each Cu2O donated 0.23 electron to adsorbed HsGDY. The DFT calculation results indicated that photo-generated electrons in Cu2O can be expected to efficiently transfer to HsGDY, and thus facilitated the charge separation.
To further verify the charge transfer and chemical states of Cu and O atoms, core-level XPS of Cu 2p and O 1s in pristine Cu2O and in HsGDY@Cu2O were measured and are presented in Fig. 3e, f respectively. For Cu2O NWs, the binding energy of at 932.3 eV and 952.2 eV can be ascribed to Cu(I) 2p3/2 and Cu(I) 2p1/2, and the broad and weak peaks at 933.7 eV and 953.5 eV as well as the satellite peaks at 944.4 eV and 962.9 eV indicated the existence of small amount of CuO on the surface of Cu2O due to the inevitable oxidation in air37. For HsGDY@Cu2O NWs, the binding energy of Cu(I) 2p3/2 and Cu(I) 2p1/2 positively shifted to 933.0 and 952.7 eV, which implied the decrease of electron cloud density on Cu atoms due to the charge transfer from Cu2O to HsGDY. In addition, the core-level O 1 s of Cu2O presented two peaks at the binding energies of 530.2 eV and 531.3 eV, which can be attributed to the oxygen in Cu2O lattice and oxygen associated with an oxygen vacancy environment38. After encapsulated by HsGDY, the strong peak at 531.7 eV indicated the formation of Cu–O–H structure39, which implied that the dominated connection between the hydrogen in HsGDY and the oxygen in Cu2O. Except the oxygen in lattice, the weak peak in 533.4 eV can be ascribed to the formation of C–O bond40. Therefore, the XPS results further validated the prediction about efficient charge transfer from Cu2O to HsGDY from the DFT calculation.
For efficient water reduction on photocathode, except the virtues of proper bandgap and fast charge transfer, the suitable band positions are as well as essential. The valence band-XPS (VB-XPS) measurements were conducted on Cu2O NWs and HsGDY@Cu2O NWs and are presented in Fig. 3g. The Cu2O NWs and HsGDY@Cu2O NWs showed distances from VB edge level of 0.12 eV and 0.45 eV corresponding to their Fermi level (Ef) respectively. In addition, Mott−Schottky (M-S) plots were also recorded to determine the flat band potentials, which would reflect the differences between Ef and water-reduction potential. As presented in Fig. 3h, the flat band potentials on Cu2O NWs and HsGDY@Cu2O NWs were determined to be 0.45 V and 0.49 V respectively. Finally, based on the band gap values from Fig. 3b and the results from VB-XPS (Fig. 3g) and M-S plots (Fig. 3h), the band energy structure diagrams of Cu2O NWs and HsGDY@Cu2O NWs were illustrated in Fig. 3i, where the enlarged distance between Ef and VB in HsGDY@Cu2O further revealed higher electron density than that in Cu2O. This result can be ascribed to the π-electron delocalization and effective electron transfer from Cu2O to HsGDY, and the corresponding results of lower electronic resistance have as well as been obtained from electrochemical impedance spectra (Supplementary Fig. 14).
PEC water reduction under concentrated solar light
The PEC water reduction under illumination with high light intensity is a facile and promising way to accelerate hydrogen generation rate in limited time41,42. The HsGDY@Cu2O NWs based photocathode was integrated into a concentrated solar light system (Fig. 4a), established through a simple Fresnel lens, and a high photocurrent density of −50.7 mA cm−2 at 0 V vs RHE was obtained under 10-sun illumination (Fig. 4b). The Fresnel lens was comprised with cheap plastics, which was beneficial for its large-scale application in low-cost. Long-term PEC stability on HsGDY@Cu2O NWs were evaluated with a steady-state chronoamperometry under illumination of 10-sun, and the results were presented in Fig. 4c. The high photocurrent density did not show significantly decay after 12 h test. The fast hydrogen generation was also recorded for practical application of PEC water reduction under 10-sun illumination (Fig. 4d), and the hydrogen generation rate reached 861.1 ± 24.8 μmol h−1 cm−2.
a Schematic illustration of PEC water reduction device with concentrated solar light illumination; b LSV plot of HsGDY@Cu2O NWs under illumination of 10-sun (AM 1.5 G, 1000 mW cm−2), recorded with scan rate of 5 mV s−1 in 0.1 M Na2SO4 solution with pH = 4.9; c Long-term PEC stability test on HsGDY@Cu2O NWs photocathodes under illumination of 10-sun; d Hydrogen generation on HsGDY@Cu2O NWs/CF photocathode at potential of 0 V vs RHE under illumination of 10-sun.
Discussion
In summary, an encapsulation strategy was proposed to prepare HsGDY@Cu2O NWs photocathode. The HsGDY was selected with dual-functions of protection and charge transfer layer. The rational designed HsGDY@Cu2O NWs photocathode demonstrated a high photocurrent density and high stability with impressive hydrogen generation rate of 218.2 ± 11.3 μmol h−1cm−2. To further increase the hydrogen generation rate in limited time, the HsGDY@Cu2O NWs photocathode was integrated into a concentrated solar light system, and obtained a high photocurrent density of −50.7 mA cm−2 and hydrogen generation rate of 861.1 ± 24.8 μmol h−1cm−2. Our study presented a straightforward approach for achieving highly efficient and stable Cu2O NWs-based photocathode. We believe the encapsulation strategy will open an avenue of rational designing efficient photoelectrodes for PEC water splitting.
Methods
Chemicals and materials
A 1-mm-thick copper foam supplied by Suzhou Taili New Energy Materials Co., Ltd. (China), was cut into pieces of 50 × 10 mm2. Pyridine (99.5%), methanol (99.9%), dichloromethane (AR), sodium hydroxide, potassium dihydrogen phosphate, and sodium sulfate were purchased from Macklin Chemical and used as received. Piperidine (99.5 %) was bought from SCR Chemical. TEB (97%) was supplied from Sigma Chemical. All aqueous solutions were prepared using deionized (DI) water with a resistivity of 18.2 MΩ·cm.
Preparation of HsGDY@Cu2O NWs/CF photocathode
The HsGDY coated Cu2O NWs supported on a CF (HsGDY@Cu2O NWs/CF) photocathode was fabricated by three-step of electrochemical anodization, annealing, and the Glaser coupling reaction. The CF was anodized in an alkaline solution (3 M NaOH) for 30 min with anodic current density of 45 mA cm−2 to form Cu(OH)2 NWs/CF, following which the color of the CF changed from red orange with metallic luster to sky blue. The as-anodized nanowire was annealed in a tube furnace at 550 °C for 4 h under nitrogen atmosphere, where the Cu(OH)2 NWs/CF were converted into Cu2O NWs/CF and the color of the Cu2O NWs changed to brick red. Finally, the top layer of Cu2O was coved with HsGDY through a Glaser coupling reaction with TEB (5 mg, 0.033 mmol) as precursor. The piperidine (10 μL, 0.1 mmol) were added to a reaction tube with 10 mL pyridine as a solvent. Remarkably, the reaction tube is filled with oxygen. Cu2O NWs/CF was immersed in the reaction mixture and then the tube was sealed and heated in an oil bath pan to 60 °C for different durations. After reaction, the samples were immediately washed sequentially with pyridine, dichloromethane, and methanol. At last, the samples were blow-dried by dry nitrogen jet and the surface of the Cu2O NWs was covered with a golden yellow film. The HsGDY on copper foam has also prepared with the same method. The Pt/HsGDY@Cu2O NWs were also prepared through electrochemical deposition of platinum nanoparticles from a solution of 1 mM H2PtCl6 in deionized water at −0.1 V versus Ag/AgCl for 15 min.
Materials characterizations
The morphologies of samples were characterized by scanning electron microscopy (SEM, S4800, Hitachi), and transmission electron microscopy (TEM, JEOLJEM 2100). The crystalline structure and chemical structure of the samples were analyzed by X-ray diffraction (XRD) (Bruker D8 Discover diffractometer, using Cu Kα radiation (1.540598 Å)) and DXR Raman Microscope (ThermoFisher Scientific) with excitation of 532 nm laser. The X-ray photoelectron spectroscopy (XPS) was carried out to reveal hybridization of elements, collected by an Axis Ultra instrument (Kratos Analytical) under ultrahigh vacuum (<10−8 torr) and using a monochromatic Al Kα X-ray source, with binding energies referenced to the C 1s binding energy of 284.8 eV. The diffuse reflectance UV-vis adsorption spectra were recorded on a spectrophotometer (Shimadzu, UV 3600), with the reference of BaSO4 powder. Photoluminescence (PL) emission spectra were measured using a photoluminescence spectrometer (FLS980, Edinburgh Instruments Ltd.) from 300 to 750 nm under an excitation wavelength of 260 nm. The electrochemical characterizations of electrochemical impedance spectra (EIS) and capacity were measured by a PGSTAT 302 N Autolab Potentiostat/Galvanostat (Metrohm) equipped with an excitation signal of 10 mV amplitude, and the Mott-Schottky measurement was performed at fixed frequency of 1 kHz.
Photoelectrochemical measurements
All the PEC measurements were employed with CHI 660E electrochemical working station (Chenhua Instrument Co., Ltd., Shanghai), in a three-electrode system: the reference electrode was Ag/AgCl with saturated KCl solution, the counter electrode was a platinum foil, and the working electrode was the HsGDY@Cu2O NWs/CF photocathode. The supporting electrolyte was a 0.1 M Na2SO4 solution with pH to 4.9. The potential relation between reference electrode (Ag/AgCl with saturated KCl solution) and reversible hydrogen electrode (RHE) was calculated through the following equation:
while \({{{\rm{E}}}}{^{\circ} _{{{{\rm{Ag}}}}/{{{\rm{AgCl}}}}}}=0.1976\,{{{\rm{V}}}}\,{{{\rm{at}}}}\,25^{\circ} {{{\rm{C}}}}\).
Linear scanning voltammetry (LSV) was conducted with a slow scan rate of 5 mV s−1. The intensity of the light source was regulated with a Si diode (Model 818, Newport) to simulate AM 1.5 illumination (100 mW cm−2). The stability measurements of the photocathode were detected under 0 V vs RHE. The hydrogen generation reaction was performed under 0 V vs RHE in a gas-closed system equipped with a gas-circulated pump. The water-reduction gaseous products at different reaction time were analyzed on an online gas chromatograph (GC-9790II, FULI Corp., China) equipped with a flame ionization detector (FID) and a thermal conductivity detector (TCD). The PEC performance under illumination of concentrated solar light was also estimated. It was need to be noted that the concentrated solar light was filtered through cycling cool water, coated on the outer surface of PEC cells, before it reached the PEC setup to maintain the experimental temperature at 25 °C.
DFT calculation
The DFT calculation were performed with the CP2K quantum chemistry software package, using Perdew–Burke–Ernzerhof (PBE) parametrization of generalized gradient approximation (GGA) to describe the exchange-correlation part in Hamiltonian36. We use GTH potential and Molopt basis set (DZVP-MOLOPT-SR-GTH) with an energy cutoff of 400 Ry43. Van der Waals (vdW) interaction was taken into account at the DFT-D3 level as proposed by Grimme44. Both atomic position and cell parameters were relaxed until the max force is <4.5 × 10−4 Ha/bohr.
Data availability
All data are available from the corresponding author upon reasonable request.
References
Khaselev, O. & Turner, J. A. A monolithic photovoltaic-photoelectrochemical device for hydrogen production via water splitting. Science 280, 425–427 (1998).
Zeng, G. et al. Development of a photoelectrochemically self-improving Si/GaN photocathode for efficient and durable H2 production. Nat. Mater. 20, 1130–1135 (2021).
Ye, S. et al. Unassisted photoelectrochemical cell with multimediator modulation for solar water splitting exceeding 4% solar-to-hydrogen efficiency. J. Am. Chem. Soc. 143, 12499–12508 (2021).
Vijselaar, W. et al. Spatial decoupling of light absorption and catalytic activity of Ni–Mo-loaded high-aspect-ratio silicon microwire photocathodes. Nat. Energy 3, 185–192 (2018).
Yu, Y. et al. Enhanced photoelectrochemical efficiency and stability using a conformal TiO2 film on a black silicon photoanode. Nat. Energy 2, 17045 (2017).
Ding, Q. et al. Designing efficient solar-driven hydrogen evolution photocathodes using semitransparent MoQxCly (Q = S, Se) catalysts on Si micropyramids. Adv. Mater. 27, 6511–6518 (2015).
Yang, Y. et al. Progress in developing metal oxide nanomaterials for photoelectrochemical water splitting. Adv. Energy Mater. 7, 1700555 (2017).
Kecsenovity, E. et al. Enhanced photoelectrochemical performance of cuprous oxide/graphene nanohybrids. J. Am. Chem. Soc. 139, 6682–6692 (2017).
Gu, J. et al. A graded catalytic–protective layer for an e-cient and stable water-splitting photocathode. Nat. Energy 2, 16192 (2017).
Huang, D. et al. Wittichenite semiconductor of Cu3BiS3 films for efficient hydrogen evolution from solar driven photoelectrochemical water splitting. Nat. Commun. 12, 3795 (2021).
Liu, M. et al. Modulation of morphology and electronic structure on MoS2-based electrocatalysts for water splitting. Nano Res. 15, 6862–6887 (2022).
Paracchino, A., Laporte, V., Sivula, K., Grätzel, M. & Thimsen, E. Highly active oxide photocathode for photoelectrochemical water reduction. Nat. Mater. 10, 456–461 (2011).
Pan, L. et al. Boosting the performance of Cu2O photocathodes for unassisted solar water splitting devices. Nat. Catal. 1, 412–420 (2018).
Niu, W. et al. Extended light harvesting with dual Cu2O-based photocathodes for high efficiency water splitting. Adv. Energy Mater. 8, 1702323 (2018).
Niu, W. et al. Crystal orientation-dependent etching and trapping in thermally-oxidised Cu2O photocathodes for water splitting. Energy Environ. Sci. 15, 2002–2010 (2022).
Paracchino, A. et al. Ultrathin films on copper(I) oxide water splitting photocathodes: a study on performance and stability. Energy Environ. Sci. 5, 8673–8681 (2012).
Zhu, Q. et al. Electron transfer in Cu/Cu2O generated by disproportionation promoting efficient CO2 photoreduction. Nano Res. 15, 7099–7106 (2022).
Zhang, Y. et al. Stable unbiased photo-electrochemical overall water splitting exceeding 3% efficiency via covalent triazine framework/metal oxide hybrid photoelectrodes. Adv. Mater. 33, 2008264 (2021).
Morales-Guio, C. G., Tilley, S. D., Vrubel, H., Grätzel, M. & Hu, X. Hydrogen evolution from a copper(I) oxide photocathode coated with an amorphous molybdenum sulphide catalyst. Nat. Commun. 5, 3059 (2014).
Zhang, Z. et al. Carbon-layer-protected cuprous oxide nanowire arrays for efficient water reduction. ACS Nano 7, 1709–1717 (2013).
Zhang, Z. & Wang, P. Highly stable copper oxide composite as an effective photocathode for water splitting via a facile electrochemical synthesis strategy. J. Mater. Chem. 22, 2456–2464 (2012).
Li, Z., Xin, Y. & Zhang, Z. New photocathodic analysis platform with quasi-core/shell-structured TiO2@Cu2O for sensitive detection of H2O2 release from living cells. Anal. Chem. 87, 10491–10497 (2015).
Li, Z. & Zhang, Z. Tetrafunctional Cu2S thin layers on Cu2O nanowires for efficient photoelectrochemical water splitting. Nano Res. 11, 1530–1540 (2018).
He, J. et al. Hydrogen substituted graphdiyne as carbon-rich flexible electrode for lithium and sodium ion batteries. Nat. Commun. 8, 1172 (2017).
Zhang, T. et al. Copper-surface-mediated synthesis of acetylenic carbon-rich nanofibers for active metal-free photocathodes. Nat. Commun. 9, 1140 (2018).
Sun, H. et al. Molecular engineering of conjugated acetylenic polymers for efficient cocatalyst-free photoelectrochemical water reduction. Angew. Chem. Int. Ed. 58, 10368–10374 (2019).
Zhou, X., Yang, J. & Zhang, Z. Acetylenic carbon-rich frameworks on copper foam as conjugated polymer photocathodes for efficient and stable water reduction. Chem. Commun. 55, 10396–10399 (2019).
Zhuo, S. et al. Dual-template engineering of triple-layered nanoarray electrode of metal chalcogenides sandwiched with hydrogen-substituted graphdiyne. Nat. Commun. 9, 3132 (2018).
Li, J. et al. Tuning the electronic bandgap of graphdiyne by H-substitution to promote interfacial charge carrier separation for enhanced photocatalytic hydrogen production. Adv. Funct. Mater. 31, 2100994 (2021).
Zhang, T. et al. Solvent-mediated engineering of coppermetalated acetylenic polymer scaffolds with enhanced photoelectrochemical performance. J. Mater. Chem. A 9, 9729–9734 (2021).
Connor, P., Schuch, J., Kaiser, B. & Jaegermann, W. The determination of electrochemical active surface area and specific capacity revisited for the system MnOx as an oxygen evolution catalyst. Z. Phys. Chem. 234, 979–994 (2020).
Walter, M. G. et al. Solar water splitting cells. Chem. Rev. 110, 6446–6473 (2010).
Wang, Y., Cheng, Y., Wu, N. & Zhang, Z. Graphitic carbon nitride/poly(3-hexylthiophene) nanocomposites for the photoelectrochemical detection of H2O2 in living cells. ACS Appl. Nano Mater. 3, 8598–8603 (2020).
Borrelli, M. et al. Thiophene-based conjugated acetylenic polymers with dual active sites for efficient co-catalyst-free photoelectrochemical water reduction in alkaline medium. Angew. Chem. Int. Ed. 60, 18876–18881 (2021).
Lu, Y. et al. sp-carbon incorporated conductive metal-organic framework as photocathode for photoelectrochemical hydrogen generation. Angew. Chem. Int. Ed. https://doi.org/10.1002/anie.202208163 (2022).
Kühne, T. D. et al. CP2K: an electronic structure and molecular dynamics software package-Quickstep: Efficient and accurate electronic structure calculations. J. Chem. Phys. 152, 194103 (2020).
Li, X., Feng, J., Mao, W., Yin, F. & Jiang, J. Emerging uniform Cu2O nanocubes for 251st harmonic ultrashort pulse generation. J. Mater. Chem. C 8, 14386–14392 (2020).
Rahimi, M. G., Wang, A., Ma, G., Han, N. & Chen, Y. A one-pot synthesis of a monolithic Cu2O/Cu catalyst for efficient ozone decomposition. RSC Adv. 10, 40916–40922 (2020).
Platzman, I., Brener, R., Haick, H. & Tannenbaum, R. Oxidation of polycrystalline copper thin films at ambient conditions. J. Phys. Chem. C 112, 1101–1108 (2008).
Balasubramanian, P., Balamurugan, T. S. T., Chen, S. M., Chen, T. W. & Sathesh, T. Rational design of Cu@Cu2O nanospheres anchored B, N Co-doped mesoporous carbon: a sustainable electrocatalyst to assay eminent neurotransmitters acetylcholine and dopamine. ACS Sustain. Chem. Eng. 7, 5669–5680 (2019).
Zhao, Y., Qiu, B. & Zhang, Z. Concentrated solar light for rapid crystallization of nanomaterials and extreme enhancement of photoelectrochemical performance. Chem. Commun. 54, 2373 (2018).
Wu, Z., Wang, L., Fu, B. & Zhang, Z. A “green” concentrated solar light doping strategy for significantly improved photoelectrochemical performance. ACS Appl. Energy Mater. 3, 8164–8170 (2020).
VandeVondele, J. & Hutter, J. Gaussian basis sets for accurate calculations on molecular systems in gas and condensed phases. J. Chem. Phys. 127, 114105 (2007).
Grimme, S., Antony, J., Ehrlich, S. & Krieg, H. A consistent and accurate ab initio parametrization of density functional dispersion correction (DFT-D) for the 94 elements H-Pu. J. Chem. Phys. 132, 154104 (2010).
Acknowledgements
This research was supported by National Natural Science Foundation of China (No. 22174045, 21822403, 21775045).
Author information
Authors and Affiliations
Contributions
X.Z., B.F., and Z.Z. designed the experiments. X.Z., J.Y., L.L., and Z.W. carried out the experiments of photocathodes fabrication and PEC measurements. Z.T. and X.X. conducted the characterizations. All authors wrote the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks Néstor Guijarro, Hyunwoong Park and the other anonymous reviewer(s) for their contribution to the peer review of this work.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Zhou, X., Fu, B., Li, L. et al. Hydrogen-substituted graphdiyne encapsulated cuprous oxide photocathode for efficient and stable photoelectrochemical water reduction. Nat Commun 13, 5770 (2022). https://doi.org/10.1038/s41467-022-33445-z
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-022-33445-z
- Springer Nature Limited
This article is cited by
-
Accelerating Oxygen Electrocatalysis Kinetics on Metal–Organic Frameworks via Bond Length Optimization
Nano-Micro Letters (2024)