Abstract
A facile generic template-free strategy is employed to prepare hierarchical hollow hybrid Fe2O3@MIL-101(Fe)/C materials derived from metal-organic frameworks as anode materials for Na-ion batteries. The intrinsic hollow nanostructure can shorten the lengths for both electronic and ionic transport, enlarge the surface areas of electrodes and improve accommodation of the volume change during Na+ insertion/extraction cycling. Therefore, The stable reversible capacity of Fe2O3@MIL-101(Fe)/C electrode is 710 mAhg−1 and can be retained at 662 mAhg−1 after 200 cycles with the retention of 93.2%. Especially, its overall rate performance data confirm again the importance of the hierarchical hollow structures and multi-elements characteristics toward high capacities in both low and high current rates. This general strategy may shed light on a new avenue for fast synthesis of hierarchic hollow functional materials for energy storage, catalyst, sensor and other new applications.
Similar content being viewed by others
Introduction
The sodium-ion batteries (SIBs) recently have attracted great interest for large-scale energy storage in renewable energy and smart grid applications due to the cheap raw materials and its decent energy densities1,2,3,4. However, compared to Li-ion batteries (LIBs), Na ions (0.102 nm in radius) are about 34% larger than that of Li ions (0.076 nm in radius), which makes it difficult to find a suitable host material to allow reversible and rapid ion insertion and extraction5,6,7. And thus, the current SIBs face severe challenges from low energy density and poor cycling stability since sodium intercalation induces anisotropic volume expansion, which triggers large voltage polarization and insufficient contact with the current collector. Therefore, development of good performance electrode materials having high capacities and long term stability is essential to successful commercialization of batteries. The current anode material studies focus on carbonaceous materials8,9,10. However, their reversibility and rate capacity are still limited. In comparison, transition metal oxides based on conversion reactions, such as Fe, Co, Ni, Cu, Mn and Mo, are proposed for the anode materials of SIBs and these oxides can react with Na+ through a one-step conversion reaction11,12,13,14:
![](http://media.springernature.com/lw287/springer-static/image/art%3A10.1038%2Fsrep25556/MediaObjects/41598_2016_Article_BFsrep25556_Equ1_HTML.gif)
Of which, iron oxides attractive anodes due to their high theoretical capacity and low cost. Komaba et al. first testified the nanocrystallized α -Fe2O3 and Fe3O4 in the sodium salt electrolyte, however, the obtained sodium storage capacity was rather low15. Most recently, Fe2O3@GNS exhibited an initial capacity of 535 mAhg−1 and 75% capacity retention after 200 cycles at 100 mAg−1 A full Na ion cell based on the Fe3O4/C anode and Na[Ni0.25Fe0.5Mn0.25]O2 layered cathode delivered a capacity of 130 mAhg−1 and 76.1% capacity retention after 150 cycles16. However, the reversible capacities of most of above metal oxides are not higher than 600 mAhg−1 and the initial coulombic efficiency is low.
To solve this problem, allowing the electrochemical reaction to proceed in a hybrid matrix of distinct material systems, such as metal oxides integrated with carbon, is an effective way to control the volume changes. The coupling of two species could render the iron oxides with rich redox reactions and improve electronic conductivity. As a result, the geometric configuration and cycling stability of electrode are improved. For example, the recent porous γ -Fe2O3@C nanocomposites anode has been characterized by Chen’s group exhibited high sodium storage capacity and outstanding cyclability17. Another popular way to improve the electrochemical performance has been focused on controlling the volumetric change by using small particles with various morphologies including nanotube, nanowall, nanosheet, nanobowl, nanocone and porous solid, of which hollow particles are of particular interest for reversible ion storage because of their short ion diffusion and good toleration for volume change during cycling. This design was former widely used in Li+ batteries18,19,20. In fact, hollow micro/nanoscale metal oxides are of great interest due to well-defined interior voids, high specific surface area, low density, accommodate volume change without pulverizing compared with that of solid counterparts of the same size and thus make them attractive materials for applications such as dye-sensitized solar cells, catalysis, chemical sensors, drug delivery and energy conversion and storage systems. For example, our previous prepared hollow cage-bell Ag@TiO2 exhibit excellent lithium-ion storage, photocatalytic and catalytic performance21. X. W. Lou and co-workers synthesized hollow microcubes of metal sulfides for enhanced lithium storage22. Therefore, a general approach to rationally fabricate hollow hybrid structural materials is still lacking and it is desirable to obtain the materials through more facile, economic and environment-friendly process. Metal–organic frameworks (MOFs), a new class of organic-inorganic hybrid functional materials with high porosity, large surface area and morphology can be easily tuned upon selection of different metal ions and organic bridging ligands23. Recently, MOFs are proved to be an effective template for preparing hollow transition metal oxides by thermal decomposition, because the porosity and long-range ordering of MOFs can offer a fast and convenient access for incoming and leaving small molecules and ions in the transformation process. Though these procedures are effective, each design strategy alone always leads to limited improvement in the electrochemical properties. And thus, the developing of a facile, scalable and controllable fabrication of hierarchic hybrid iron oxides materials with satisfactory cycling ability and high capacity is still highly desirable for SIBs. Besides, to our best knowledge, reports on the fast synthesis of hollow structures derived from MOFs used for Na+ batteries are quite rare and it can be an advantage for chemists to elaborate possible new constructions from all chemical components without any time-restricted conditions.
Herein, we chose Fe-O-C hybrid nanostructure to demonstrate our concept and propose a facile fast strategy to prepare hybrid structures from MOFs. In this work, the advantage of novel hollow structures from MOFs and the virtue of hybrid matrix of distinct material systems are well integrated to solve the problem. Compared with conventional methods produced metal oxides nano electrodes, the hollow nanostructures prepared via MOFs have relatively high surface area and a stable hollow configuration without the destructive effect of template removal on product morphology. The hollow structures can render much contact area between active components and Na ions in the process of electrochemical reaction. Meanwhile, it may help the electrode to accommodate large volume change without pulverizing. Futhermore, the unique structure can shorten ionic/electronic diffusion length and provide efficient channels for mass transport24,25,26. The multi-components allow the electrochemical reaction to proceed in a hybrid matrix of distinct material systems. Moreover, the coupling of carbon could render the Fe2O3 with rich redox reactions and improve electronic conductivity. As a result, the geometric configuration and outstanding electrochemical performance of hierarchical hollow γ -Fe2O3@C structures from MOFs are anticipated to manifest outstanding electrochemical performance.
Results and Discussion
Structure and morphology of hollow Fe2O3@MIL-101(Fe)/C
The crystallographic structure and phase purity of Fe2O3 precursor and hollow Fe2O3@MIL-101(Fe)/C magnetic sample were analyzed by XRD, as shown in Fig. 1a. All the diffraction peaks can be indexed to the γ -Fe2O3 (JCPDS card no. 39–1346). No other impurity peaks are observed, indicating a complete thermal conversion of the MOFs precursors into Fe2O3 nanostructures. Detailed analysis of the peak broadening of the (3 1 1) reflection of Fe2O3@MIL-101(Fe)/C using the Scherrer equation indicates an average crystallite size ca. 5 nm, suggesting that these particles are composed of nanocrystal subunits. Figure 1b presents X-ray diffraction (XRD) patterns of the Fe-MOFs and their simulated results which reveal that the composition of the precursors is MIL-101(Fe). All the diffraction peaks of the formed Fe-btc MOFs in the 2θ range of 1–23° are in agreement with the results.
The FTIR spectrum images of the prepared hollow structured Fe2O3@MIL-101(Fe)/C magnetic sample and its Fe2O3 precursor are shown in Fig. 2a. The broad absorption peaks from 3432 to 2362 cm−1 are associated with the stretching vibrations of the -OH group of absorbed water molecules and absorption of CO2 in the air and the peak of 1626 cm−1 is assigned to the bending vibrations of the water molecules. For the Fe2O3@MIL-101(Fe)/C, the spikes from 1617 to 1000 cm−1 are assigned to the asymmetric and symmetric stretching vibrations of the carbonyl group of organics. The strongest broad peaks in the range of 400–1000 cm−1 are contribution from the face-centered cubic phase Fe-O. The peak intensity of Fe-O bond for final products is different from that of precursor, implying the structure of prepared sample has some discrepancy with its precursor. The SEM and TEM images of the prepared hollow Fe2O3 precursors are shown in Fig. 2b,c. It is obvious that the precursors are hollow sub-microsphere uniformly with average diameter of ca. 300 nm according to Fig. 2b. TEM (Fig. 2c) reveals that these sub-microspheres exhibit hollow structures obviously. Its selected-area electron diffraction (SAED) pattern (Fig. 2c) reveals the diffraction rings 1–3 are indexed to (2 0 0), (3 1 1) and (4 0 0) diffraction of Fe2O3, respectively. This result is in good agreement with XRD analysis. The unique hollow porous morphologies of Fe2O3@MIL-101(Fe)/C are characterized by SEM, TEM and HR-TEM and the results are illustrated in Fig. 3a–d. It is clear that the prepared Fe2O3@MIL-101(Fe) keeps the original morphology of its precursors (Fig. 3a). The TEM image in Fig. 3b shows the hollow structure, which is a visible hollow interior structure obviously. Especially, a typical structure with well-defined interior and shell can also be detected and the thickness of shell of samples is ca. 150–200 nm. Furthermore, the surface of samples exhibits porous frame, which hierarchical structure is resulted from MOFs. Figure 3c is the molecular structure of Fe-MOFs. The lattice fringe is observed obviously and the lattice spacing (0.256 nm) agrees with Fe3O4 (3 1 1) plane spacing from Fig. 3d. The size of as-synthesized Fe2O3@MIL-101(Fe)/C are much smaller than those reported by Zhu very most recently27.
The N2 adsorption/desorption isotherms and the pore size distribution of the obtained hollow porous hollow Fe2O3@MIL-101(Fe)/C are shown in Fig. 4. The isotherms are identified as type IV, which are the characteristic isotherm of mesoporous materials. The pore size distribution data indicates that average pore diameters of the product are in the range of 3–8 nm. The BET surface area of the sample is 123.15 m2 g−1. Remarkably, the specific surface area is far higher than most of the previously reported transition metal oxides microsphere products28,29,30. The single-point total volume of pores at P/P0 = 0.975 is 0.425 cm3g−1. These indicate that the prepared samples have a loose mesoporous structure. This structure can not only keep the nano effect of active components but also help to buffer the volume changes of hollow porous Fe2O3@MIL-101(Fe)/C electrodes during electrochemical reaction.
Electrochemical characterizations of hierarchic hollow Fe2O3@MIL-101(Fe)/C
The electrochemical performance of the hollow Fe2O3 and Fe2O3@MIL-101(Fe)/C hybrid materials used for Na-ion anodic materials is investigated. The cycling performance profiles of Fe2O3 and Fe2O3@MIL-101(Fe)/C electrodes at constant current density of 200 mAg−1 are shown in Fig. 5a. The initial charge capacities are 1040 and 1052 mAhg−1 for bare Fe2O3 and Fe2O3@MIL-101(Fe)/C with corresponding coulombic efficiencies of 87.6% and 87.1%, respectively. The stable charge capacity of Fe2O3@MIL-101(Fe)/C electrode is 710 mAhg−1 and can be retained at 662 mAhg−1 after 200 cycles with the retention of 93.2%. The coulombic efficiencies are always over 99.6% except for the first 4 cycles at 200 mAhg−1. While the bare Fe2O3 samples present only 462 mAhg−1 after 200 cycles. Hence, Fe2O3@MIL-101(Fe)/C exhibits improved reversibility. The charge/discharge curves of hierarchic hollow Fe2O3@MIL-101(Fe)/C electrode for the first two and the 200th cycle at constant current density of 200 mAg−1 are shown in Fig. 5b. It is noticeable that the Na-reaction potential in the Fe2O3 is quite lower than the Li-reaction potential. The electrolyte of Na+ batteries having lower decomposition potential compared with that of Li-ion batteries (LiPF6 system) should be responsible for the performance. In the initial discharge, the potential drops rapidly to a plateau of 1.1 V and then decreases gradually to the plateaus of approximately 0.4 V. The plateau is not so apparently, which is possible due to the presence of small nanoparticles of Fe2O3. The reaction can be described as equation (2) and the conversion of the iron oxide accompanied by the layer formation of solid electrolyte interface (SEI). which results are consistent with other research groups1,7,12.
Electrochemical performance of prepared hierarchical hollow Fe2O3@MIL-101(Fe)/C electrodes: (a) The cycling performance of bare Fe2O3 and Fe2O3@MIL-101(Fe)/C measured at 200 mAg−1. (b) charge/discharge curves of Fe2O3@MIL-101(Fe)/C electrode for the 1st, 2nd and 200th cycle at current density of 200 mAg−1. (c) Cyclic voltammetry plots of Fe2O3@MIL-101(Fe)/C electrode at the scan rate of 0.05 mV s−1. (d) Rate capability of Fe2O3@MIL-101(Fe)/C electrode from 500 mAg−1 to 4000 mAg−1 for 200 cycles. Electrode potential range of 0.05–3.0 V vs. Na/Na+.
![](http://media.springernature.com/lw294/springer-static/image/art%3A10.1038%2Fsrep25556/MediaObjects/41598_2016_Article_BFsrep25556_Equ2_HTML.gif)
After 200 cycles, the capacity can also be kept at ca.660 mAhg−1, showing the excellent reversibility of electrode. The cyclic voltammograms (CVs) within the range of 0.05–3.0 V vs. Na/Na+ at the scan of 0.05 mVs−1 are shown in Fig. 5c. The first CV plot is different from those of the subsequent scans, which is attributed to the irreversible formation of a solid electrolyte interface (SEI). In the subsequent cycles, a broad cathodic peak at 0.67 V is attributed to the insertion-extraction into/from the crystal structure of Fe2O37. These results are consistent with CV analysis above and other reports7,12. Compared with LIBs, the redox peaks is weak because of the large size, heavy mass and poor mobility of Na+31,32.
To investigate electrochemistry performance under the different rate discharge, Fig. 5d exhibits the discharge capacities of Fe2O3@MIL-101(Fe)/C electrode against different current density from 500 mAg−1 to 4000 mAg−1 and each sustained for 40 cycles. The stable cyclic performance is obtained for all densities. Even when the current density reaches 4000 mAg−1, the capacity can also arrive at 421 mAhg−1. Subsequently, a specific capacity of ca. 680 mAhg−1 is recovered when the current density reduces back to 500 mAg−1 after 200 cycles. The overall densities performance demonstrates the high capacities in both low and high current density of the hierarchical hollow Fe2O3@MIL-101(Fe)/C electrode. Figure 6 is the TEM of Fe2O3@MIL-101(Fe)/C electrode after 200 cycles at current density of 500 mAg−1, revealing materials is still kept well without breakage in the process of charge-discharge. SEI layer also can be detected accord to the inset in the Fig. 6, which is resulted from the decomposition of electrolyte. Compared with the previous reported iron oxide materials1,7,11,15,32,33, the material reported here is very attractive due to its facile, fast and improved sodium storage. The nano-scaled characteristics of Fe2O3 particle from MOFs embedded in the aggregates ensure the electrode having a high capacity and the fast Na-ion diffusion in the electrode and the introduction of carbon renders the electrode having a good electronic conductivity. The unique hollow structures can shorten the length of Na-ion diffusion, which is benefit for the rate performance. The hollow structure offers a sufficient void space, which sufficiently alleviates the mechanical stress caused by volume change. Therefore, the hierarchical hollow Fe2O3@MIL-101(Fe)/C electrode exhibits excellent electrochemical performance.
Conclusions
Hierarchical hollow hybrid Fe2O3@MIL-101(Fe)/C materials have been successfully synthesized by a facile template-free procedure combined with a solvothermal synthesis reaction and subsequent calcination. As anode materials used in Na+ batteries, the stable reversible capacity of Fe2O3@MIL-101(Fe)/C electrode is 710 mAhg−1 and can be retained at 662 mAhg−1 after 200 cycles with the retention of 93.2%. This strategy is simple, cheap and suitable for mass-production, which may open a new avenue for fast synthesis of hollow or amorphous structural nano/micro-functional materials for energy storage, sensors, catalysts and other new applications.
Experimental section
Materials and Methods
Synthesis of hollow Fe2O3 precursor
All chemicals were of analytical grade and used without further purification. Typically, FeCl3·6H2O (1.52 g), sodium citrate (3.02 g), urea (0.55 g) were dissolved in 80 mL deionized water and stirred for 30 min to form a homogeneous solution. Then 0.8 g PVP (MW30000) was added to the above solution with a continual stirring for 60 min. Subsequently, the light yellow solution was transfered into a 100 mL Teflon-lined stainless steel autoclave and held at 180 °C for 12 h. Finally, the black products were harvested through several rinse-centrifugation cycles with deionized water and absolute ethanol and then dried at 60 °C under vacuum condition overnight.
Synthesis of Fe2O3@MIL-101(Fe)/C
To synthesis the Fe2O3@MIL-101(Fe)/C, 0.25 g the as-prepared hollow Fe2O3 precursor was dispersed in FeCl3·6H2O ethanol solution (4 mL, 10 mM) for 15 min, then in terephthalic acid ethanol solution (4 mL, 10 mM) for 30 min at 70 °C. The sample was collected by several rinse-precipitation cycles with absolute ethanol and then dried at 120 °C under vacuum condition. The as-prepared Fe2O3@MIL-101(Fe) (0.45 g) was dispersed in 60 ml 0.5 M aqueous glucose solution and then the solution was transferred into 100 mL Teflon cup. The autoclave was heated to 180 °C for 12 h. The resulting product was harvested by several rinse-precipitation cycles with methanol and was dried in vacuum at 60 °C for further characterization. Finally, certain amount of the MOFs precursors corresponding to the condition of hydrothermal treated at180 °C for 12 h were successively annealed in air flowing at 450 °C for 5 h with a slow ramp rate of 1 °C min−1 to make Fe2O3@MIL-101(Fe)/C microspheres.
Characterization
X-ray diffraction (XRD) was carried out to identify the phase composition of synthesized samples over the 2θ range from 20° to 90° using a Rigaku D/max-A diffractometer with Co Kα radiation. A Fourier transform infrared spectroscope (FTIR, Themo Nicolet 670FT-IR) was used for recording the FTIR spectra of the sample ranging from 400 to 4000 cm−1. Morphologies of the synthesized samples were observed with a AMRAY 1000B scanning electron microscope (SEM) and the microstructural characteristics of samples were observed by high-resolution transmission electron microscope (HR-TEM, JEOL JEM-2010) working at 200 kV accelerating voltage and the lattice structure was identified by selected area electron diffraction (SAED) technique. Nitrogen adsorption-desorption measurements were conducted at 77 K on a Micromeritics Tristar apparatus. Specific surface areas were determined following the Brunauer-Emmet-Teller analysis.
Electrochemical Measurements
For electrochemical performance evaluation, half-cell studies were performed. In the experimental electrode, acetylene black powder and polyvinylidene fluoride (PVDF) were used as conductive additive and binder. The working electrodes of sodium-ion batteries were fabricated by blending the active material, acetylene black and polyvinylidene fluoride (PVDF) in N-methyl-2-pyrrolidone with a weight ratio of 80:10:10. The obtained slurry was pasted onto a copper foil as current collector. After solvent evaporation, the electrode was pressed and dried at 120 °C under vacuum for 48 h. The cells were assembled in argon filled glove-box. Na metal and glass fiber were used as counter electrode and separator, respectively. The electrolyte was 1.0 M NaClO4 dissolved in ethylene carbonate/diethyl carbonate (EC/DEC, 1:1 by volume). Cycling tests were carried out at the charge and discharge current density of 100 mAg−1, in the voltage range of 0.05–3.0 V versus Na/Na+ by Land 2100A tester. Cyclic voltammetry was performed between 0.05 and 3.0 V with scan rate of 0.05 mVs−1.
Additional Information
How to cite this article: Li, C. et al. Hierarchical hollow Fe2O3@MIL-101(Fe)/C derived from metal-organic frameworks for superior sodium storage. Sci. Rep. 6, 25556; doi: 10.1038/srep25556 (2016).
References
Kang, H. et al. Update on anode materials for Na-ion batteries. J. Mater. Chem. A 3, 17899–17913 (2015).
Ni, J. F. et al. Strongly Coupled Bi2S3@CNT Hybrids for Robust Lithium Storage. Adv. Energy Mater. 4, 1400798 (2014).
Ni, J. F., Zhao, Y., Li, L. & Mai, L. Q. Ultrathin MoO2 nanosheets for superior lithium storage. Nano Energy. 11, 129–135 (2015).
Luo, C. et al. Graphene oxide wrapped croconic acid disodium salt for sodium ion battery electrodes. J. Power Source. 250, 372–378 (2014).
Yan, Y., Yin, Y. X., Guo, Y. G. & Wan, L. J. A Sandwich-Like Hierarchically Porous Carbon/Graphene Composite as a High-Performance Anode Material for Sodium-Ion Batteries. Adv. Energy Mater. 4, 1301584 (2014).
Liu, J. Z., Ni, J. F., Zhao, Y., Wang, H. B. & Gao, L. J. Grapecluster-like Fe3O4@C/CNT nanostructures with stable Li-storage capability. J. Mater. Chem. A 1, 12879–12884 (2013).
Jian, Z. et al. Fe2O3 nanocrystals anchored onto graphene nanosheets as the anode material for low-cost sodium-ion batteries. Chem. Commun. 50, 1215–1217 (2014).
Stevens, D. A. & Dahn, J. R. High Capacity Anode Materials for Rechargeable Sodium-Ion Batteries. J. Electrochem. Soc. 147, 1271–1273 (2000).
Ding, J. et al. Carbon Nanosheet Frameworks Derived from Peat Moss as High Performance Sodium Ion Battery Anodes. ACS Nano. 7, 11004–11015 (2013).
Cao, Y. et al. Sodium Ion Insertion in Hollow Carbon Nanowires for Battery Applications. Nano Lett. 12, 3783–3787 (2012).
Jian, Z. L. et al. Fe2O3 nanocrystals anchored onto graphene nanosheets as the anode material for low-cost sodium-ion batteries. Chem. Commun. 50, 1215–1217 (2014).
Zhang, N. et al. 3D Porous γ -Fe2O3@C Nanocomposite as High-Performance Anode Material of Na-Ion Batteries. Adv. Energy Mater. 5, 1401123 (2015).
Lu, Y. Y., Zhang, N., Zhao, Q., Liang, J. & Chen, J. Micro-nanostructured CuO/C spheres as high-performance anode materials for Na-ion batteries. Nanoscale 7, 2770–2776 (2015).
Zhao, Y., Feng, Z. X. & Xu, Z. C. J. Yolk–shell Fe2O3@C composites anchored on MWNTs with enhanced lithium and sodium storage. Nanoscale 7, 9520–9525 (2015).
Komaba, S. et al. Electrochemical Insertion of Li and Na Ions into Nanocrystalline Fe3O4 and α -Fe2O3 for Rechargeable Batteries. J. Electrochem. Soc. 157, A60–A65 (2010).
Oh, S. M. et al. Advanced Na[Ni0.25Fe0.5Mn0.25]O2/C− Fe3O4 Sodium-Ion Batteries Using EMS Electrolyte for Energy Storage. Nano Lett. 14, 1620–1626 (2014).
Zhang, N. et al. 3D Porous γ -Fe2O3@C Nanocomposite as High-Performance Anode Material of Na-Ion Batteries. Adv. Energy Mater. 5, 1401123 (2015).
Guo, H. et al. Morphology-controlled synthesis of SnO2/C hollow core–shell nanoparticle aggregates with improved lithium storage. J. Mater. Chem. A 1, 3652–3658 (2013).
Guo, H. et al. Hierarchical synthesis of Mo–Sn oxide cage-bell hybrid structures with superior lithium storage. Chem. Commun. 50, 673–675 (2014).
Chen, W. W., Li, T. T., Hu, Q., Li, C. P. & Guo, H. Hierarchical CoS2@C hollow microspheres constructed by nanosheets with superior lithium storage . J. Power Sources 286, 159–165 (2015).
Guo, H. et al. Shape-controlled synthesis of Ag@TiO2 cage-bell hybrid structure with enhanced photocatalytic activity and superior lithium storage. Green Chem. 15, 2810–2816 (2013).
Yu, X. Y. et al. General Formation of MS (M = Ni, Cu, Mn) Box-in-Box Hollow Structures with Enhanced Pseudocapacitive Properties. Adv. Funct. Mater. 24, 7440–7446 (2014).
Lauren, L. E. et al. Metal-Organic Framework Materials as Chemical Sensors. Chem. Rev. 112, 1105–1125 (2012).
Guo, H. et al. General design of hollow porous CoFe2O4 nanocubes from metal-organic frameworks with extraordinary lithium storage. Nanoscale 6, 15168–15174 (2014).
Guo, H. et al. Core-shell TiO2 microsphere with enhanced photocatalytic activity and improved lithium storage. J. Solid State Chem. 201, 137–143 (2013).
Liu, S., Hu, L., Xu, X., Al-Ghamdi, A. A. & Fang, X. Nickel Cobaltite Nanostructures for Photoelectric and Catalytic Applications. Small 11, 4267–4283 (2015).
Ke, F., Qiu, L. & Zhu, J. Fe3O4@MOF core-shell magnetic microspheres as excellent catalysts for the Claisen–Schmidt condensation reaction. Nanoscale 6, 1596–1601 (2014).
Geng, H. B., Zhou, Q., Pan, Y., Gu, H. W. & Zheng, J. W. Preparation of fluorine-doped, carbonencapsulated hollow Fe3O4 spheres as an efficient anode material for Li-ion batteries. Nanoscale, 6, 3889–3894 (2014).
Ma, Y., Zhang, C., Jia, G. & Lee, J. Y. Nitrogen-doped carbon-encapsulation of Fe3O4 for increased reversibility in Li+ storage by the conversion reaction. J. Mater. Chem. 22, 7845–7850 (2012).
Lei, C. et al. Dopamine as the coating agent and carbon precursor for the fabrication of N-doped carbon coated Fe3O4 composites as superior lithium ion anodes. Nanoscale 5, 1168–1175 (2013).
Wang, B., Chen, J. S., Wu, H. B., Wang, Z. & Lou, X. W. Quasiemulsion-Templated Formation of α -Fe2O3 Hollow Spheres with Enhanced Lithium Storage Properties. J. Am. Chem. Soc. 133, 17146–17148 (2011).
Lin, Y. M., Abel, P. R., Heller, A. & Mullins, C. B. α -Fe2O3 Nanorods as Anode Material for Lithium Ion Batteries. J. Phys. Chem. Lett. 2, 2885–2891 (2011).
Valvo, M., Lindgren, F., Lafont, U., Björefors, F. & Edström, K. Towards more sustainable negative electrodes in Na-ion batteries via nanostructured iron oxide. J. Power Sources 245, 967–978 (2014).
Acknowledgements
The authors would like to acknowledge financial support provided by the National Natural Science Foundation of China (No. 51474191 and No. 21467030), the Major state basic research development program of China (973 Program, No. 2014CB643406) and the Program for Excellent Young Talents, Yunnan University.
Author information
Authors and Affiliations
Contributions
H.G. and L.L. designed the experiment. L.L. provides TG-DTA analysis and have made great work on the modification on the revision. C.L., Q.H., Y.L., H.Z., X.Y. and L.L. carried out data analysis provide the electrochemical techniques for the research on the cycling stability of the electrodes and they have made great work on the modification on the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Li, C., Hu, Q., Li, Y. et al. Hierarchical hollow Fe2O3@MIL-101(Fe)/C derived from metal-organic frameworks for superior sodium storage. Sci Rep 6, 25556 (2016). https://doi.org/10.1038/srep25556
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep25556
- Springer Nature Limited
This article is cited by
-
Zero-valence Fe boosts the activity of Fe–N-C electrocatalyst in oxygen reduction reaction
Ionics (2022)
-
Development of covalent-bonded organic/carbon anode for sodium-ion battery
Journal of Mechanical Science and Technology (2019)
-
A Nanocrystalline Fe2O3 Film Anode Prepared by Pulsed Laser Deposition for Lithium-Ion Batteries
Nanoscale Research Letters (2018)