Abstract
A hollow hybrid Ni-Fe-O nanomaterial (NiFe2O4) is synthesized using a precursor of metal-organic frameworks through a simple and cost-effective method. The unique hollow nanocage structures shorten the length of Li-ion diffusion. The hollow structure offers a sufficient void space, which sufficiently alleviates the mechanical stress caused by volume change. Besides, the hybrid elements allow the volume change to take place in a stepwise manner during electrochemical cycle. And thus, the hierarchical hollow NiFe2O4 nanocage electrode exhibits extraordinary electrochemical performance. The stable cyclic performance is obtained for all rates from 1 C to 10 C. Even when the current reaches 10 C, the capacity can also arrive at 652 mAhg−1. Subsequently, a specific capacity of ca. 975 mAhg−1 is recovered when the current rate reduces back to 1 C after 200 cycles. This strategy that derived from NMOFs may shed light on a new route for large-scale synthesis of hollow porous hybrid nanocages for energy storage, environmental remediation and other novel applications.
Similar content being viewed by others
Introduction
Currently the efforts in developing advanced materials for energy and environmental applications have become even more intensive driven by the urgency of increasing energy efficiency and environment protection1,2,3,4. In particular, electrode materials with precisely constructed nano-structured architectures have attracted considerable attention due to their potential applications in high-performing electrochemical energy devices such as batteries, fuel cells and supercapacitors. With respect to this, many efforts have been focused on the research to control the size, morphology, composition, crystallinity and building blocks of the materials with hollow structures, which have well-defined interior voids, high specific surface area, low density, accommodate volume change without pulverizing compared with that of solid counterparts of the same sized ones5,6,7,8,9. For instance, TiO2 based hollow materials with different sizes and morphologies could show some enhanced electrochemical properties7,10,11. Our previously prepared hollow cage-bell Ag@TiO2 materials have demonstrated excellent lithium-ion storage capability12. Zhou et al.13 and Wang et al.14 synthesized hollow microcubes of metal sulfides for batteries and the resulted electrodes gave some enhanced lithium storage capability. Most recently, several novel hybrid hollow materials containing multiple layers of shells or multiple compositions were explored and showed desirable and unique properties and also maximized structural advantages when compared to single component hollow structured materials15,16,17,18,19,20. However, most of the current available hollow materials were synthesized by multistep template routes, which could have some challenges such as difficulty in template fabrication, low product yields and multistep and costly operations. Therefore, some new and effective approaches to rationally fabricate hierarchical hollow hybrid nanomaterials are necessary in exploring these materials through a more simple, facile and environment-friendly process.
Regarding the templates used for hollow structured electrode materials, nanostructured metal-organic frameworks (NMOFs)21,22,23, a new class of organic-inorganic hybrid functional materials with high porosity and large surface area, seem to be very attractive, which can allow to be easy tuned for selection of different metal ions and organic bridging ligands10,11. They have been proved to be effective templates for preparing hollow-structured transition metal oxides by thermal decomposition. This is because the porosity and long-range ordering of NMOFs can offer a fast and convenient access for incoming and leaving small molecules and ions in the transformation process11. In this regard, when compared to other templates/precursors, NMOFs can offer distinct advantages due to their unique structure and porosity and/or hollow structures. The advantage of NMFOs as templates gives them a tremendous application opportunity in developing a series of highly tailorable functional nanomaterials. For example, these NMOFs were used to synthesize hollow metal oxides, which exhibited a much enhanced electrochemical performance when evaluated as anode materials for Lithium-ion batteries (LIBs)24. Low et al.25 prepared Fe2O3 microboxes with hierarchically structured shells simply via annealing Prussian blue (PB) microcubes in air. Cho et al.26 reported a spindle-like porous α-Fe2O3 prepared from a typical iron-based NMOF template (MIL-88-Fe). Most recently, some nonspherical hollow-structured porous shell materials were synthesized by our group and others24,27.
In this work, a hybrid nanostructured NiFe2O4 with a hollow nanocage structure is synthesized to validate our proposed strategy in preparing hollow porous nanocages using NMOFs as a template (Fig. 1). The advantages in choosing such a Fe- and Ni- containing material is due to the low cost, non-toxicity and natural abundance of these two transition metal oxides as well as their high capacities when used as anode materials for LIBs24,25,26,27,28. However, although the Ni and Fe oxides-based LIB electrodes can give high capacity, the pulverization of the electrode caused by huge volume change during the process of electrochemical reaction could lead to a rapid capacity degradation and poor cycling stability. When using a hybrid nanostructured NiFe2O4 prepared in this work, this issue could be significantly overcome, allowing the electrochemical reaction to proceed in a hybrid matrix of distinct material systems and resulting in an effective control of the electrode volume changes through facilitating the step-wise manner rather than at a certain fixed potential. Moreover, the coupling of these two metal species could render the NiFe2O4 with rich redox reactions and then improve electronic conductivity. As a result, the ternary NiFe2O4 prepared exhibits a higher electrical conductivity and an improved electrochemical activity when compared to binary metal oxides Fe2O3 and NiO2,24. Furthermore, this hollow nanocage structured NiFe2O4 could allow small-sized Lithium ion (Li+) to fast diffusion for reversible lithium ion storage, resulting in a good toleration to volume change during cycling12,13,14. This paper reports the geometric configuration of hierarchical hollow NiFe2O4 nanocages synthesized using nano metal-organic frameworks and its associated high electrochemical performance when used as the anode materials for LIBs.
Experimental
Synthesis of hollow porous NiFe2O4 nanocages
All chemicals used in this work were analytical grade and used without further purification. For a typical synthetic experiment, Solution A was synthesized by dissolving 0.187 g of Ni(CH3COO)2 and 0.993 g of sodium citrate in 100 mL of distilled water with stirring. Solution B was prepared by adding 1.32 g of K3[Fe(CN)6] into 100 mL of aqueous solution of PVP K30 (4 g) with stirring. Then Solution A and Solution B were mixed together under stirring. After 20 minutes of stirring, an eggplant turbid liquid was formed and then aged for 24 hours for forming a precipitate. Then the precipitate was treated by several centrifuge-wash cycles with distilled water and ethanol and then dried at room temperature for 10 hours. The collected powder of hollow porous NiFe2O4 nanocages was annealed in Air at 350 °C for 2 hours at a heating rate of 1 °C min−1 to obtain the product.
Material characterization
X-ray diffraction (XRD) was used to identity the phase composition of synthesized samples over the 2θ range from 20° to 90° using a Rigaku D/max-A diffractometer with Co Kα radiation. A Fourier transform infrared spectroscope (FTIR, Themo Nicolet 670FT-IR) was used for recording the FTIR spectra of the sample ranged from 500 to 4000 cm−1. The microstructural characteristics of NiFe2O4 nanocages were recorded by high-resolution transmission electron microscope (HR-TEM, JEOL JEM-2010) working at 200 kV accelerating voltage and the lattice structure was identified by selected area electron diffraction (SAED) technique.
Electrochemical characterization
For electrochemical performance evaluation, half-cell measurements were performed. For preparation of working electrode containing NiFe2O4 nanocages, acetylene black powder and polyvinylidene fluoride (PVDF) were used as conductive additive and binder, respectively. In the preparation, the synthesized NiFe2O4 nanocages were mixed with acetylene black and PVDF dissolved in N-methyl-pyrrolidinone in a weight ratio of 85:10:5 to form slurry, which was then painted on a copper foil to form the working electrode. This copper foil was served as both the material support and current collector. After solvent evaporation, the electrode was pressed and dried at 120 oC under vacuum for 48 hours. The electrochemical cells were assembled in a argon filled glove-box. Metallic lithium foil was used as the counter electrode. The electrolyte was 1M LiPF6 in a mixture of ethylene carbonate (EC) and dimethyl carbonate (DMC) (1:1 in vol. ratio). Cycling tests were carried out at different current densities (1c = 914 mAg−1), in the voltage range of 0.01–1.5 V versus Li/Li+ by using a Land 2100A tester.
Results and Discussion
The crystallographic structure and phase purity of the precursor and as-synthesized hollow porous NiFe2O4 nanocages are analyzed by XRD, as shown in Fig. 2a,b. From Fig. 2a and compared the spectrum with standard one (JCPDS card no. 46–0908), it can be seen that the precursor Ni2Fe(CN)6 does not contain impurity. All the diffraction peaks of final products, shown in Fig. 2b, can be indexed to the monoclinic phase of NiFe2O4 (JCPDS card no. 10–0325) without impurity peaks, indicating a complete thermal conversion of the NMOF precursors into NiFe2O4 nanostructures. The FTIR spectrum images of the prepared hollow structured NiFe2O4 nanocage sample and its Ni2Fe(CN)6 precursor are shown in Fig. 3. The broad absorption peaks centered at ca. 3391 to 2357 cm−1 can be assigned to the stretching vibrations of the -OH group of absorbed water molecules and absorption of CO2 in the air. According to the spectrum of Ni2Fe(CN)6, the peaks from 1654 to 1601 cm−1 can be assigned to the bending vibrations of the water molecules; the spike of 2108 cm−1 is assigned to the stretching vibrations of the cyano group of precursor. These peaks are all disappeared in the spectrum of synthesized NiFe2O4 samples, indicating that these groups have decomposed after the calcinations. The strongest broad peaks in the range of 992 to 500 cm−1 are contributed from the bands of metal-oxide29.
Figure 4a,b show the SEM and TEM images of the Ni2Fe(CN)6 precursors. It is clear that the precursors are solid submicro-cubes with an average diameter of ca.100 nm according to Fig. 4a. A smooth surface can be seen on these solid submicro-cubes, as in Fig. 4b. The hollow porous morphology of NiFe2O4 nanocage sample is also characterized by SEM, TEM and HR-TEM, as illustrated in Fig. 4c–f. After calcination of Ni2Fe(CN)6 precursors at 350 °C for 4 hours, a fluffy black powder contains uniformly distributed nanocubes with a shrunk size as in Fig. 4c. It is interesting to find that the NiFe2O4 sample from NMOFs is not a solid box but a visible hollow porous interior structure with an average diameter of ca. 80 nm, as evidenced by the partial broken shell vividly, as shown in Fig. 4d. Particularly, a typical structure with well-defined interior and thin shell can also be detected. The size of as-obtained nanocages is much smaller than the previously reported porous nanostructures derived by NMOFs recently25. It is believed that the hollow porous structure of these particles might be induced by a rapid mass-transport from core to shell during the calcinations. The surface of the synthesized NiFe2O4 powder is made up from nano-sized small particles of ca. 3–9 nm, which is in a good agreement with XRD results. The selected-area electron diffraction (SAED) pattern (Fig. 4e,f) of one typical particle reveals the diffraction rings can be indexed to (2 2 0), (3 1 1) and (4 0 0) diffraction of face-centered cubic NiO, respectively. The lattice fringe with a lattice spacing (0.251 nm) can be seen clearly, agreeing with NiFe2O4 (3 1 1) plane spacing (Fig. 4f).
The N2 adsorption/desorption isotherms and the pore size distribution of obtained hollow porous NiFe2O4 nanocages from NMOFs are shown in Fig. 5. The isotherms are typical Type IV, which are the characteristic isotherm of mesoporous materials. The pore size distribution data indicates that the pore diameter distribution is in the range of 3–8 nm. The BET surface area of the sample is 260.9 m2 g−1. It can be seen that the specific surface area of NiFe2O4 is significantly higher than most of the previous reported TMOs microsphere products24,25,26. The single-point total volume of pores at P/P0 = 0.975 is 0.438 cm3 g−1. These data indicate that the prepared samples have a loose mesoporous structure. This structure is believed to have beneficial effect on buffering the volume changes of hollow porous NiFe2O4 nanocage electrodes during electrochemical reaction.
The formation mechanism can be described as schematically illustrated in Fig. 1 by the following Equation (1). When Ni2Fe(CN)6 is converted into NiFe2O4, the carbon and nitrogen in CN– are oxidized into gases and escaped.
![](http://media.springernature.com/lw403/springer-static/image/art%3A10.1038%2Fsrep13310/MediaObjects/41598_2015_Article_BFsrep13310_Equ1_HTML.gif)
The formation mechanism can be further investigated through a series of experiments as shown in Fig. 6, which presents the TEM images of NiFe2O4 obtained after calcination at 150 °C, 200 °C, 250 °C, 300 °C, 350 °C and 400 °C for 4 hours, respectively. It can be seen that only solid nanocages with a smooth surface can be formed after calcination at 150 °C (Fig. 6a). When the reaction temperature is increased to 200 °C, the sample surface becomes a little coarse and shows a porous structure (Fig. 6b). With continuously increasing the temperature up to 250 °C, the sample surface become even more coarser and the hollow configuration is appearing gradually (Fig. 6c). It can be significantly noticed that the porous nanocage can be transformed into hollow one while the temperature is increased to 300 °C (Fig. 6d). With further increasing the temperature, the interior of the nanocage structure is broken and nanocage becomes a small nano particle with sizes of ca. 4–8 nm, as shown in Fig. 6e,f which are corresponding to those at 350 °C and 400 °C, respectively. According to these observations, it can be speculated that the formation of unique hollow porous NiFe2O4 nanocages go through the transformation from solid to hollow ones, which may be induced by the quick evolution of CO2 and NOx gases during the thermal decomposition process. It can be stated here that our strategy, as shown in Fig. 1, can provide a novel procedure and simple route to prepare hierarchical hollow porous nanocages from NMOFs with higher BET surface and larger quantity.
The electrochemical performance of the prepared hollow NiFe2O4 nanocages as anode material of Li-ion batteries was also tested. As shown in Fig. 7a, the increase in cycling stability and capacity with increasing temperature from 200 °C to 400 °C is mainly attributed to the formation of hollow porous structure. The capacity of the sample at 350 °C remains a stable value as high as 1071 mAhg−1 after 200 cycles. However, its capacity fades drastically from 1242 to 552 mAh g−1 after 200 cycles when the temperature is increased to 400 °C, which is caused by the collapse of hollow structure in the process of calcination at high temperature as evidenced in Fig. 6. The CV and charge/discharge curves of hierarchical hollow NiFe2O4 nanocage (350 °C) electrode are shown in Fig. 7b,c, respectively. In the first scan of CV, two cathodic peaks can be observed at 0.54 and 1.51 V, corresponding to the conversion reactions of Fe3+ and Ni2+ to their metallic states and the formation of Li2O30. The broad anodic peaks can be ascribed to the oxidation reactions of metallic Fe and Ni. The reactions of NiFe2O4 with Li can be written as Equations (2) and (3)31:
Electrochemical performance of prepared hierarchical porous hollow NiFe2O4 nanocage electrode: (a) cycling performance of CoFe2O4 materials at different temperatures from 200 °C to 400 °C at constant current density of 1 C; (b) the cycle of CV curve with a scan rate of 0.05 mVs−1; (c) charge/discharge curves of CoFe2O4 (350 °C) electrode for the 1st, 2nd and 200th cycle at current density of 1 C; (c) the first cycle CV curve with a scan rate of 0.05 mVs−1; (d) rate capability of NiFe2O4 electrode from 1 C to 20 C for 200 cycles. Electrode potential range of 0.01–3.0 V vs. Li/Li+.
![](http://media.springernature.com/lw331/springer-static/image/art%3A10.1038%2Fsrep13310/MediaObjects/41598_2015_Article_BFsrep13310_Equ2_HTML.gif)
![](http://media.springernature.com/lw362/springer-static/image/art%3A10.1038%2Fsrep13310/MediaObjects/41598_2015_Article_BFsrep13310_Equ3_HTML.gif)
Similar to the simple oxide Fe2O3 and NiO, the mixed oxide NiFe2O4 stores Li through reversible formation and decomposition of Li2O. In the second scan, the reduction peaks are shifted to 0.94 and 1.56 V, respectively. The asymmetric nature of the plots suggests that the conversion reactions are only partially reversible and complete structural recovery to NiFe2O4 cannot occur32. As shown in Fig. 7c, the 1st discharge (Li+ insertion) and charge (Li+ extraction) curve at a current density of 1 C in the voltage window of 0.01–3 V (Fig. 7c) shows a wide, steady discharging plateau at ca. 0.65 V, followed by a gradual voltage decrease. The initial discharge and charge capacities are 1245 mAhg−1 and 1152 mAhg−1, respectively. The initial capacity loss should be attributed to the formation of solid electrolyte interphase (SEI) and the reduction of metal oxide to metal with Li2O formation. These results are consistent with CV analysis. From the second cycle onwards, the long potential plateau is replaced by a long slope between 1.2 and 0.73 V. After 200 cycles, the capacity can also be kept at 1071 mAhg−1, showing the excellent reversibility of electrode. To further investigate electrochemical performance, Fig. 7d shows the discharge capacities of NiFe2O4 electrode at different charging rates from 1 C to 10 C with 40 cycles. It can be seen that the stable cyclic performance can be obtained at all rates. Even when the current reaches 10 C, the capacity can also maintain at 652 mAh g−1. Subsequently, a specific capacity of ca. 975 mAhg−1 is recovered when the current rate reduces back to 1 C after 200 cycles. The overall rate performance demonstrates the high capacities in both low and high current rates of the prepared NiFe2O4 nanocage electrode. In Fig. 8, the TEM of NiFe2O4 electrode after 200 cycles at a current rate of 1 C reveals that the structure of this anode material can be retained well without breakage in the process of charge-discharge. Compared with the previously reported TMOs materials24,33,34,35,36, the synthesized NiFe2O4 material in this work exhibits an enhanced electrochemical performance with our novel strategy. The unique hollow nanocage structures can shorten the length of Li-ion diffusion, which is beneficial to the rate performance. Furthermore, the hollow structure can offer a sufficient void space, sufficiently alleviating the mechanical stress caused by the volume change. Besides, the hybrid elements allow the volume change to take place in a stepwise manner during electrochemical cycle. As a result, the hierarchical hollow NiFe2O4 nanocage electrode can exhibit an extraordinary high electrochemical performance.
Conclusions
In summary, material with a structure of hollow porous NiFe2O4 nanocage from NMOFs is successfully synthesized by a facile and fast benign procedure. When it is used as an anode material for Lithium-ion battery, a stable reversible capacity can be retained at 1017 mAhg−1 after 200 cycles with an excellent rate performance. This novel synthetic strategy may shed light on a novel avenue for the effective synthesis of hollow porous hybrid nanocage materials derived from NMOFs for energy storage, sensor, catalyst, environmental remediation and other new applications.
Additional Information
How to cite this article: Guo, H. et al. Self-assembly formation of hollow Ni-Fe-O nanocage architectures by metal-organic frameworks with high-performance lithium storage. Sci. Rep. 5, 13310; doi: 10.1038/srep13310 (2015).
References
Liu, J. et al. Monodisperse yolk–shell nanoparticles with a hierarchical porous structure for delivery vehicles and nanoreactors. Angew. Chem. Int. Ed. 122, 5101–5105 (2010).
Wang, B., Chen, J. S., Wu, H. B., Wang, Z. & Lou, X. W. Quasiemulsion-templated formation of α-Fe2O3 hollow spheres with enhanced lithium storage properties. J. Am. Chem. Soc. 133, 17146–17148 (2011).
Bian, Z. et al. Multitemplates for the hierarchical synthesis of diverse inorganic materials. J. Am. Chem. Soc. 134, 2325–2331 (2012).
Lou, X. W., Li, C. M. & Archer, L. A. Designed synthesis of coaxial SnO2@ carbon hollow nanospheres for highly reversible lithium storage. Adv. Mater. 21, 2536–2539 (2009).
Guo, H. et al. Core-shell TiO2 microsphere with enhanced photocatalytic activity and improved lithium storage. J. Solid State Chem. 201, 137–143 (2013).
Yin, Y. et al. Formation of hollow nanocrystals through the nanoscale Kirkendall effect. Science 304, 711–714 (2004).
Liu, L. et al. Hollow NiO nanotubes synthesized by bio-templates as the high performance anode materials of lithium-ion batteries. Electrochim. Acta 114, 42–47 (2013).
Zhang, Q., Lee, I., Joo, J. B., Zaera, F. & Yin, Y. Core–shell nanostructured catalysts. Acc. Chem. Res. 46, 1816–1824 (2012).
Yao, Y. et al. Interconnected silicon hollow nanospheres for lithium-ion battery anodes with long cycle life. Nano lett. 11, 2949–2954 (2011).
Guo, H. et al. Template-free fabrication of hollow NiO–Carbon hybrid nanoparticle aggregates with improved lithium storage. Part. Part. Syst. Char. 31, 374–381 (2014).
Lai, X. et al. General synthesis and gas-sensing properties of multiple-shell metal oxide hollow microspheres. Angew. Chem. Int. Ed. 123, 2790–2793 (2011).
Guo, H. et al. Shape-controlled synthesis of Ag@ TiO2 cage-bell hybrid structure with enhanced photocatalytic activity and superior lithium storage. Green Chem. 15, 2810–2816 (2013).
Zhou, L., Zhao, D. & Lou, X. W. Double-shelled CoMn2O4 hollow microcubes as high-capacity anodes for lithium-ion batteries. Adv. Mater. 24, 745–748 (2012).
Wang, Z. Wang, Z., Liu, W., Xiao, W. & Lou, X. W. D. Amorphous CoSnO3@C nanoboxes with superior Lithium storage capability. Energy Environ. Sci. 6, 87–91 (2013).
Guo, H. et al. Morphology-controlled synthesis of cage-bell Pd@ CeO2 structured nanoparticle aggregates as catalysts for the low-temperature oxidation of CO. J. Mater. Chem. A 1, 7494–7499 (2013).
Wu, C. et al. Facile strategy for synthesis of silica/polymer hybrid hollow nanoparticles with channels. Langmuir 26, 18503–18507 (2010).
Wang, Y., Su, F., Lee, J. Y. & Zhao, X. S. Crystalline carbon hollow spheres, crystalline carbon-SnO2 hollow spheres and crystalline SnO2 hollow spheres: synthesis and performance in reversible Li-ion storage. Chem. Mater. 18, 1347–1353 (2006).
Deng, J. et al. Sandwich-stacked SnO2/Cu hybrid nanosheets as multichannel anodes for lithium ion batteries. Acs Nano 7, 6948–6954 (2013).
Nelson, K. & Deng, Y. Enhanced light scattering from hollow polycrystalline TiO2 particles in a cellulose matrix. Langmuir 24, 975–982 (2008).
Wang, D. P. & Zeng, H. C. Multifunctional roles of TiO2 nanoparticles for architecture of complex core-shells and hollow spheres of SiO2-TiO2−Polyaniline System. Chemistry of Materials 21, 4811–4823 (2009).
Wu, Y. F., Han, J. Y., Xue, P., Xu, R. & Kang, Y. J. Nano metal-organic framework (NMOF)-based strategies for multiplexed micro RNA detection in solution and living cancer cells. Nanoscale 7, 1753–1759 (2015).
Jana, J. A., Jorge, G. & Freek, K. Metal-organic frameworks as scaffolds for the encapsulation of active species: state of the art and future perspectives. J. Mater. Chem. 22, 10102–10118 (2012).
Falcaro, P. et al. MOF positioning technology and device fabrication. Chem. Soc. Rev. 43, 5513–5560 (2014).
Hu, L. & Chen, Q. Hollow/porous nanostructures derived from nanoscale metal–organic frameworks towards high performance anodes for lithium-ion batteries. Nanoscale 6, 1236–1257 (2014).
Zhang, L., Wu, H. B. & Lou, X. W. Metal–organic-frameworks-derived general formation of hollow structures with high complexity. J. Am. Chem. Soc. 135, 10664–10672 (2013).
Xu, X., Cao, R., Jeong, S. & Cho, J. Spindle-like mesoporous α-Fe2O3 anode material prepared from MOF template for high-rate lithium batteries. Nano lett. 12, 4988–4991 (2012).
Guo, H. et al. Accurate hierarchical control of hollow crossed NiCo2O4 nanocubes for superior lithium storage. Nanoscale 6, 5491–5497 (2014).
Hu, M. et al. Synthesis of superparamagnetic nanoporous iron oxide particles with hollow interiors by using Prussian blue coordination polymers. Chem. Mater. 24, 2698–2707 (2012).
Griffiths, P. R., Haseth, J. A. D. Fourier Transform Infrared Spectrometry, John Wiley & Sons: New York,, 90, 1240–1241(1986).
Vidal-Abarca, C., Lavela, P. & Tirado, J. L. The origin of capacity fading in NiFe2O4 conversion electrodes for lithium ion batteries unfolded by 57Fe Mossbauer spectroscopy. J. Phys. Chem. C 114, 12828–12832 (2010).
Wang, N. et al. A general approach for MFe2O4 (M= Zn, Co, Ni) nanorods and their high performance as anode materials for lithium ion batteries. J. Power Sources. 247, 163–169 (2014).
Cherian, C. T. et al. Morphologically robust NiFe2O4 nanofibers as high capacity Li-ion battery anode material. ACS Appl. Mater. Interfaces. 5, 9957–9963 (2013).
Zhang, G. & Lou, X. W. D. General Solution Growth of Mesoporous NiCo2O4 Nanosheets on Various Conductive Substrates as High-Performance Electrodes for Supercapacitors. Adv. Mater. 25, 976–979 (2013).
Jiang, H., Ma, J. & Li, C. Hierarchical porous NiCo2O4 nanowires for high-rate supercapacitors. Chem. Commun. 48, 4465–4467 (2012).
Yuan, C. et al. X. Facile template-free synthesis of ultralayered mesoporous nickel cobaltite nanowires towards high-performance electrochemical capacitors. J. Mater. Chem. 22, 16084–16090 (2012).
Li, L. et al. Electrospun porous NiCo2O4 nanotubes as advanced electrodes for electrochemical capacitors. Chem.–Eur. J. 19, 5892–5898 (2013).
Acknowledgements
The authors would like to acknowledge financial support provided by the National Natural Science Foundation of China (No. 51474191 and No. 21467030), the Major state basic research development program of China (973 Program, No. 2014CB643406) and the Program for Excellent Young Talents, Yunnan University.
Author information
Authors and Affiliations
Contributions
H.G. and L.X.L. designed the experiment. T.T.L. and W.W.C. carried out the experiment. T.T.L. drawn all figures in this article. J.L.Q. and J.J.Z. carried out data analysis provide the electrochemical techniques for the research on the cycling stability of the electrodes and they have made great work on the modification on the revision.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Guo, H., Li, T., Chen, W. et al. Self-assembly formation of hollow Ni-Fe-O nanocage architectures by metal-organic frameworks with high-performance lithium storage. Sci Rep 5, 13310 (2015). https://doi.org/10.1038/srep13310
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep13310
- Springer Nature Limited
This article is cited by
-
Multi-metal–Organic Frameworks and Their Derived Materials for Li/Na-Ion Batteries
Electrochemical Energy Reviews (2020)
-
Reversible control of the magnetization of spinel ferrites based electrodes by lithium-ion migration
Scientific Reports (2017)
-
Synthesis, characterization and electrical properties of Li2NiFe2O4/NiFe2O4 nanocomposites
Journal of Materials Science: Materials in Electronics (2017)