Abstract
Staphylococci, notably biofilm-forming Staphylococcus epidermidis, have been recognized as global nosocomial pathogens in medical device-related infections. Their potential to attach to and form biofilm on indwelling catheters are significant factors impeding conventional treatment. Due to their extensive antimicrobial and antibiofilm actions, antimicrobial peptides (AMPs) have attracted interest as promising alternative compounds for curing difficult-to-treat, biofilm-forming bacterial infections. Cecropin A-melittin or CM, a well-known hybrid peptide, exhibits broad-spectrum antimicrobial activity, however it also possesses high toxicity. In the current study, a series of hybrid CM derivatives was designed using an amino acid substitution strategy to explore potential antibacterial and antibiofilm peptides with low toxicity. Among the derivatives, CM-10K14K showed the least hemolysis along with potent antibacterial activity against biofilm-forming S. epidermidis (MICs = 3.91 μg/mL) and rapid killing after 15 min exposure (MBCs = 7.81 μg/mL). It can prevent the formation of S. epidermidis biofilm and also exhibited a dose-dependent eradication activity on mature or established S. epidermidis biofilm. In addition, it decreased the development of biofilm by surviving bacteria, and formation of biofilm on the surface of CM-10K14K-impregnated catheters. Released CM-10K14K decreased planktonic bacterial growth and inhibited biofilm formation by S. epidermidis in a dose-dependent manner for 6 and 24 h post-exposure. Impregnation of CM-10K14K prevented bacterial attachment on catheters and thus decreased formation of extensive biofilms. SEM images supported the antibiofilm activity of CM-10K14K. Flow cytometry analysis and TEM images demonstrated a membrane-active mechanism of CM-10K14K, inducing depolarization and permeabilization, and subsequent membrane rupture leading to cell death. The presence of an interaction with bacterial DNA was verified by gel retardation assay. These antibacterial and antibiofilm activities of CM-10K14K suggest its potential application to urinary catheters for prevention of biofilm-forming colonization or for treatment of medical devices infected with S. epidermidis.
Similar content being viewed by others
Introduction
Staphylococcus epidermidis, an opportunistic biofilm former and a common commensal of the human skin, is the most prevalent of coagulase-negative staphylococcus and the major cause of infection of implanted medical devices1,2,3. Staphylococcus epidermidis adhere to the medical devices, then multiply and develop condensed populations covered in a defensive matrix called a biofilm4. This matrix makes difficult the treatment of bacteria within this biomass1.
The Centers for Disease Control and Prevention (CDC) reported that approximately 75% of hospital-acquired, urinary tract infections (UTIs) are associated with catheters placed through the urethra into the bladder to empty urine. Prolonged catheter use is recognized as one of the major risk factors for the development of catheter-associated urinary tract infections (CAUTIs)5, another being immunocompromise of the patient6.
There is presently no commercially available technology to prevent CAUTIs7. Using closed drainage systems, ensuring sterility at the time of insertion, and minimizing the duration of catheterization are considered best practices8,9. More experimental is the incorporation of antimicrobial compounds to release antimicrobial agents, inhibit attachment or kill microbes, and disturbance of the biofilm’s formation in order to prevent or limit UTIs10.
Several antimicrobial agents have been explored, such as impregnating the catheter with antibiotics, silver or antiseptics. Belfield and colleagues demonstrated that rifampicin-, triclosan-, and sparfloxacin-impregnated urinary catheters have a long-term preventive effect against key uropathogens (including methicillin-resistant S. aureus, methicillin-resistant S. epidermidis, extended-spectrum beta-lactamase producing Escherichia coli, and carbapenemase-producing E. coli)7. Johnson and co-workers compared the effectiveness and efficiency of nitrofurazone- and silver-alloy-coated catheters, and found the former is more cost-efficient and effective at preventing the formation of biofilms and planktonic growth11,12. Segev et al. showed that urinary catheters coated with a chlorhexidine sustained-release varnish have a significantly reduced development of biofilms13. Although these catheters demonstrated good antibacterial action in vitro, their limitations include significant cytotoxicity, short duration of drug release, and development of bacterial resistance restricting their long-term use14. Therefore, the search for novel substances is ongoing.
Antimicrobial peptides (AMPs) are short polymers of amino acids with broad-spectrum bactericidal activities and infrequent development of bacterial resistance. In addition, they have been demonstrated to inhibit microbes from colonizing surfaces, kill bacteria in biofilms, and disturb the structure of biofilms15. As such, AMPs have potential in the development of alternative antimicrobial catheters16. Lim and colleagues demonstrated that the potent antimicrobial and anti-biofilm properties of a catheter with a polydopamine-peptide (CWR11) coating are comparable to those of commercial Dover silver-coated catheters14. A polyurethane catheter with a brush coating tethered with AMP E6 reduced bacterial adhesion to the catheter’s surface in a mouse urinary catheter infection model17,18. In addition, the lipopeptide GZ3.27 has potential in the antimicrobial coating of medical implants19.
In this study, the derivative peptides of a parent cecropin A and melittin hybrid were designed and studied for their antimicrobial and antibiofilm properties, and the mechanisms of these actions. Various methods have previously been employed to coat the surfaces of medical devices; impregnation is an effective and simple method and was used in this study. The candidate peptide-impregnated catheters were then evaluated in bactericidal activity against free-floating (planktonic) S. epidermidis and inhibition of biofilm formation adherent to the catheter surface.
Materials and methods
Peptide design and in silico analysis
To further develop the parent Cecropin A-Melittin (or CM) hybrid peptide20 with dual activities as antibacterial and antibiofilm against S. epidermidis biofilm-associated infections on a catheter model, two sets of CM derivatives were designed based on its α-helical secondary structure and helical wheel projection for determining the effect of net charge and hydrophobicity on antibacterial action.
To increase the net positive charge, lysine was substituted in the CM parent peptide. CM-10K was modified by replacing alanine with lysine at position 10, while CM-10K14K was modified by replacing alanine at position 10 and valine at position 14 with two lysine, respectively, resulting in an improved hydrophilic face in helical wheel projection (Fig. 1). To increase the hydrophobicity, CM-1V10K14K was designed by substituting lysine with valine at position 1, where a lysine was embedded on the hydrophobic face in helical wheel projection (Fig. 1), thus improving the amphipathicity. CM-1V14K was created by retaining the original alanine at position 10 to investigate the effect of removing lysine under increasing hydrophobicity conditions. Furthermore, CM-A was designed by adding alanine at the end of the C-terminus where it links the hydrophobic and hydrophilic faces of the CM peptide, resulting in an improved secondary structure and increasing both the charge positivity and hydrophobicity.
The online Antimicrobial Peptide Calculator and Predictor (APD3 Server: https://aps.unmc.edu/prediction) was used to analyze the peptide sequences. The online programs I-TASSER (http://zhanglab.ccmb.med.umich.edu/I-TASSER/) and HeliQuest (https://heliquest.ipmc.cnrs.fr/) were exploited to determine three-dimensional structures and helical wheel projections, respectively.
Peptide synthesis
All peptides were synthesized by China Peptides Co., Ltd. (Shanghai, China) with solid-phase methods using N-(9-fluorenyl) methoxycarbonyl (Fmoc) chemistry. They were amidated at the C-terminus and obtained as trifluoroacetate salts. The purity of peptides was confirmed to be higher than 95% using analytical reverse-phase high-performance liquid chromatography (RP-HPLC). The masses of these peptides were determined using electrospray ionization mass spectrometry (ESI–MS). Lyophilized peptides were dissolved in ultrapure (type 1) water at a concentration of 10 mg/mL and stored at − 20 °C until subsequent testing. For peptide dipping on catheters, lyophilized peptides were dissolved and used immediately.
Bacterial strains and culture conditions
The S. epidermidis ATCC 35984 (biofilm-producer), Staphylococcus aureus ATCC 25923, Enterococcus faecalis ATCC 29219, Acinetobacter baumannii ATCC 19606, Klebsiella pneumoniae ATCC 27736 and Pseudomonas aeruginosa ATCC 27853 were grown overnight on trypticase soy agar (TSA; BD Bacto™), then subcultured in TSB and incubated at 37 °C for 16–18 h before each experiment. Stock bacterial cultures were kept frozen at − 80 °C in trypticase soy broth (TSB; BD Bacto™, USA) containing 20% glycerol.
Antibacterial activity determination
The antimicrobial activity of peptides against S. epidermidis and five strains of both gram-positive and gram-negative bacteria frequently involved in catheter-related infections including S. aureus, E. faecalis, A. baumannii, K. pneumoniae, and P. aeruginosa was compared to that of vancomycin (Vancomycin hydrochloride, BioChemica, UK) using a modified version of the National Committee for Clinical Laboratory Standards (NCCLS) broth microdilution method21. Two-fold serially diluted (0.98–250 µg/mL) aliquots of the peptides were prepared in type 1 water and added to sterile 96-well polypropylene microplates (Nunclon Delta-Treated; Thermo Scientific™, Denmark) in a volume of 50 µL, followed by the addition of 50 µL of bacterial suspensions (2–7 × 105 CFU/mL) in Mueller Hinton Broth (MHB; BD Difco™, USA). Uninoculated MHB and bacterial cultures without peptides were used as negative and positive controls, respectively. After culturing in an incubator shaker for 24 h at 37 °C, the lowest concentration at which the peptide inhibited bacterial growth as observed by visual inspection was taken as the minimal inhibitory concentration (MIC)22. Fifty microliter aliquots from each non-turbid well identified in the MIC experiment were plated on TSA for determination of minimal bactericidal concentration (MBC) by colony count assay21. MBC was defined as the lowest concentration of peptide that showed no bacterial growth on an agar plate. All experiments were performed in triplicate.
Toxicity test
Hemolytic activity
The quantity of hemoglobin released by treatment was used as a measure of a peptide’s hemolytic activity against human red blood cells (hRBCs)23. Venous blood was collected from a healthy volunteer in plastic blood collection tubes with lithium heparin (BD Vacutainer™, USA) and centrifuged at 2000×g for 5 min to separate the plasma and buffy coat. The hRBCs obtained were washed at least three times and diluted to 4% (vol/vol) in phosphate-buffered saline (PBS; Caisson Laboratories, USA). The same volume of the hRBC suspension (50 µL) was incubated with twofold, serially diluted concentrations (0.98–250 μg/mL) of peptide dissolved in PBS for 1 h at 37 °C. The hRBCs incubated in 0.1% Triton X-100 and PBS were used as positive (100% hemolysis) and negative (0% hemolysis) controls, respectively. The release of hemoglobin into the supernatants was monitored by measurement of absorbance at 405 nm using a Multiskan SkyHigh microplate reader (Thermo Scientific™, Singapore). The percentage of hemolysis was calculated as previously described24.
Experiments involving human volunteers were in compliance with ethical standards and received approval from the Ethics Committee of Thammasat University (COA No. 066/2562). All participants voluntarily provided written informed consent.
Cytotoxicity
The cytotoxicity of the candidate peptide on L929 mouse fibroblast cell lines (NCTC clone 929) were evaluated using the 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) assay following the published protocol25. L929 cells (3–5 × 104) in RPMI 1640 medium, supplemented with 10% (vol/vol) heat-inactivated fetal bovine serum, 2 mM l-glutamine, 0.2% (wt/vol) sodium bicarbonate, 100 U/mL penicillin and 100 mg/mL streptomycin were placed into each well of 96-well plates and incubated in 5% CO2 at 37 °C overnight. After removal of media, the two-fold serially diluted peptide was added to achieve final concentrations of 0.98–250 µg/mL. Plates were then incubated at 37 °C under 5% CO2 for 24 h. The RPMI 1640 medium with and without L929 seeded cells were used as positive and negative controls, respectively. After treatment, MTT (Sigma-Aldrich, USA) was added to a final concentration of 0.5 mg/mL and suspensions incubated for 4 h at 37 °C under 5% CO2. Supernatants from each well were then discarded, and 150 µl of dimethyl sulfoxide (DMSO; Fisher BioReagents™, UK) was added and gently mixed to dissolve the crystallized formazan. Absorbance was measured at 570 nm using a Multiskan SkyHigh microplate reader. Cell viability (%) was estimated according to the following formula:
Antibiofilm activity determination
Biofilm cell viability
The assessment of biofilm cell viability of CM-10K14K was conducted by the Calgary Biofilm Device (CBD)26 with some modifications. A suspension of S. epidermidis was exposed to serially diluted peptide concentrations ranging from 0.98 to 250 μg/mL within a 96-well microtiter plate covered with 96-peg lids (NuncTM Immuno TSP Lids, Denmark). After an incubation period of 24 h at 37 °C, the peg lids were rinsed to remove culture media and non-adherent cells. Following this, the peg lids underwent a washing process and were transferred onto new plate containing PBS. For the removal of biofilms from the peg lids, a water bath sonicator (Bandelin SONOREXTM, Germany) was employed. The detached biofilms were then serially diluted and plated on TSA. Following the incubation period, colonies were counted, and the biofilm cell viability was calculated.
Biofilm eradication
The effect of the peptide against established biofilm was evaluated following a previously described method with some modifications26,27. Bacterial suspension was added into 96-well microplates and were subsequently covered with 96-peg lids. After incubation at 37 °C for 24 h, the 96-peg lids underwent a rinsing step to eliminate culture media and non-adherent cells and the established grown biofilms adhering to the 96-peg lids were exposed to various concentration of peptide (ranging from 0.98 to 250 μg/mL) at 37 °C for an additional 24 h. Following this exposure period, the 96-peg lids were washed and transferred onto new plates containing PBS. Biofilm was removed from 96-peg lids by sonicator and the biofilms were serially diluted and cultured on TSA. After incubation at 37 °C for 24 h, the CFUs were counted, and the eradication of preformed biofilm by peptides was calculated according to the equation shown below:
Biostability determination
Proteolysis of peptide by proteinase K was determined using the growth inhibition assay described by Jia et al.28 with some modifications. Staphylococcus epidermidis cell suspensions were prepared as described in MIC determination and incubated with peptide at final concentration ranging from 0.98 to 250 µg/ml in the presence of 0.01 mg/mL (final concentration) proteinase K at 37 °C with continuous shaking at 200 rpm. After 6 and 24 h of incubation, the growth inhibitory effect was determined by measuring the absorbance at 620 nm using a Multiskan SkyHigh microplate reader. The percentage of relative survival rate was calculated as follows:
where \({\text{Abs}}_{\text{Treated}}\) was absorbance value of S. epidermidis cells after incubation with peptide in the presence of proteinase K, \({\text{Abs}}_{\text{Untreated}}\) was that of S. epidermidis cells incubated with ultrapure water in the presence of proteinase K.
Circular dichroism (CD) analysis
The secondary structure of peptide induced by membrane-mimetic surroundings was evaluated on a Jasco-815 spectropolarimeter (Jasco, Japan) at 25 °C, using a 0.1-cm-path-length rectangular quartz cell29. The peptides were dissolved at a final concentration of 0.2 mg/mL in PBS, 30 mM SDS surfactant (Sigma-Aldrich, Japan) or 50% (vol/vol) TFE (Merck, USA) to mimic an aqueous environment, negatively charged bacterial membranes, and hydrophobic parts of microbial membranes, respectively, and conformational changes assessed. Their spectra were recorded in the 190–250 nm range at a scanning speed of 10 nm/min with at least three replicates for each condition. The CD signal spectra were then transformed to mean residue ellipticity using the following equation:
where θM is residue ellipticity (deg. M−1 m−1), θobs is detected ellipticity adjusted for buffer at a given wavelength (mdeg), MRW is residue molecular weight (MW/number of amino acids), c is peptide concentration (mg/mL), and l is path length (cm).
Time-kill kinetics assay
Time-kill curve analyses were assessed by culturing the mid-logarithmic growth phase of S. epidermidis in MHB medium24, in the presence of peptide at MIC or MBC concentrations. After incubation at 37 °C, ten microliters of bacterial suspensions were aliquoted at various time intervals (0.25, 0.5, 1, 2, 4, 6, 8 and 24 h). The aliquots were ten-fold serially diluted in MHB, and 100 µL of each dilution was plated onto TSA. After 24 h of incubation at 37 °C, the number of CFU was determined.
Mode of action
Flow cytometry analysis
Flow cytometry was employed to investigate membrane-lytic mechanisms induced by peptide. Propidium iodide (PI, Sigma-Aldrich, USA), a DNA intercalating dye, was employed to assess the bacterial membrane permeability, while bis-(1,3-dibutylbarbituric acid) trimethine oxonol (BOX; Sigma-Aldrich, USA) was used to monitor changes in the bacterial membrane potential6. Cultured S. epidermidis was washed and the concentration adjusted to an absorbance reading of 0.05 at 620 nm in 1 × PBS. The bacterial suspensions were treated with 1 × MIC of the peptide candidate, then incubated at 37 °C for 5, 15 or 30 min with constant shaking at 140 rpm. The negative control consisted of untreated bacterial cells; the positive control of bacterial cells heated at 70 °C for 30 min. After treatment, bacterial cells were collected by centrifugation at 10,000×g for 10 min and washed with 1 × PBS to remove unbound peptide before adding fluorescent probes. PI and BOX were added to each cell suspension to final concentrations of 1 µg/mL and 0.0625 µM, respectively, for 15 min in the dark before analysis. A flow cytometer (CytoFlex, Beckman Coulter, USA) was used to measure the fluorescent signals at a laser excitation wavelength of 488 nm. Forward scatter (FSC), side scatter (SSC), red fluorescence (585/42 nm) generated by PI and green fluorescence (530/30 nm) from BOX were each collected. 25,000 cells were counted in each sample in accordance with their scatter parameters and the data were investigated using logarithmic scales and Kaluza software version 2.1 (Beckman Coulter, USA).
Scanning electron microscopy
Under scanning electron microscopy (SEM), the surface morphological and biofilm formation of peptide-treated bacteria were evaluated. Staphylococcus epidermidis cultures were washed and adjusted to an OD620 of 0.05 in 300 mL of 1 × PBS. Bacterial suspensions were then incubated with peptide at a final concentration of 1 × MIC at 37 °C for 15 min. After treatment, cells were harvested by centrifugation at 10,000×g for 20 min and washed with 1 × PBS to remove the unbound peptide. As described previously25, the treated bacterial cells were fixed in 2.5% (vol/vol) glutaraldehyde at 4 °C for 12 h. The samples were then washed twice with PBS and dehydrated for 15 min in each of a graded ethanol series (50%, 70%, 90% and 100%), followed by transfer to a mixture (1:1) of ethanol and tertiary butanol for 20 min, and then to pure tertiary butanol for 20 min. After lyophilization and gold coating, the samples were analyzed using a scanning electron microscope (Hitachi SU8020, Tokyo, Japan).
Transmission electron microscopy
Alterations in structural integrity and membrane destruction of bacteria were further observed under transmission electron microscopy (TEM). Bacterial cells were prepared and incubated with peptide as previously described25. After harvesting the bacterial pellets, samples were fixed overnight in glutaraldehyde at a concentration of 2.5% (vol/vol). Afterward, pellets were washed twice with 1 × PBS and post-fixed for 2 h with 1% osmium tetroxide in 1 × PBS. The fixed samples were then washed twice with 1 × PBS, followed by dehydration for 15 min each in a graded ethanol series (50%, 70%, 90%, and 100%). After transfer to a mixture of absolute acetone (1:1) and epoxy resin (1:3) for 1 h, samples were placed in absolute acetone for 20 min, followed by transfer to pure epoxy resin and held for 12 h. A glass knife (ultramicrotome) was used to cut ultrathin slices. After post-staining with lead citrate and uranyl acetate, these slices were examined using a transmission electron microscope (Hitachi HT7700, Japan).
DNA-binding assay
A gel retardation assay was employed to investigate the interaction of peptide candidate with intracellular targets such as DNA30. Overnight S. epidermidis cultures were harvested by centrifugation at 4000×g for 10 min and genomic DNA was extracted using the E.Z.N.A.® Bacterial DNA kit (Omega Bio-Tek, USA). Quantity and purity of the DNA were determined using NanoDrop™ One Microvolume UV–Vis Spectrophotometers (Thermo Scientific™, USA). The serially diluted concentrations (0.98–250 μg/mL) of candidate peptides were suspended in binding buffer [50 µg/mL bovine serum albumin (BSA), 20 mM KCl, 10 mM Tris–HCl (pH 8.0), 1 mM ethylene diamine tetraacetic acid (EDTA), 1 mM dithiothreitol (DTT) and 5% glycerol and then incubated with 143.5 ng of genomic DNA at 37 °C for 1 h. Subsequently, the samples were mixed with 2 µL of 6× loading dye (Vivantis, Malaysia) and 10-μL aliquots were added to 1% agarose gel electrophoresis in 1 × Tris borate-EDTA buffer (89 mM Tris base, 89 mM boric acid and 2 mM EDTA, pH 8.0; Vivantis, Malaysia).
Assessment of prevention of biofilm formation by CM-10K14K-impregnated catheters
Peptide dip-coating of catheters by physical adsorption
A sterilized 14 Fr siliconized latex Foley catheter (Norta®, Malaysia) was cut into 0.5 cm sections and dipped into one of three concentrations (250, 500 and 1000 µg/mL) of CM-10K14K, or into vancomycin freshly prepared in ultrapure water for 1 h at room temperature (Fig. 2), a modified protocol31. The dipped segments were placed in wells of a 24-well plate (1 section per well) and left to dry overnight before testing.
In vitro catheter-associated infection model with biofilm-forming S. epidermidis
The peptide-impregnated catheter segments were placed in the wells of sterile 24-well tissue culture plates (Corning, USA) and 1 mL of TSB containing approximately 107 CFU/mL of S. epidermidis was added to each well (3 catheter segments per concentration). The plates were then incubated at 37 °C for 6 and 24 h. After incubation, the treated segments were transferred to new 24-well plates for future determination of biofilm biomass. Supernatants were collected to determine if viable cells remained; each well containing biofilm, along with its corresponding control media, was fixed and stained with 0.1% CV as described in Supplementary Information (Sect. 1). The percentage of biofilm formation compared to controls was calculated.
Determination of viable planktonic cells by colony count assay
The supernatants were ten-fold serially diluted in 0.85% NaCl, and 10 µL of each dilution (n = 3) was dropped onto TSA. After 24 h of incubation at 37 °C, the CFUs were counted.
Assessment of biofilm biomass on peptide-impregnated catheters by crystal violet staining
The treated catheter segments were washed twice in 0.85% NaCl without disturbing the biofilm, then transferred to tubes containing 1 mL of 0.1% CV stain for 15 min. The stained segments were gently washed, until the supernatants of the negative controls (untreated segments) were clear and left to dry for 1 h. The segments were transferred to tubes containing 600 µL of 95% ethanol for solubilization, followed by sonication for 10 min and vertexing for 30 s three times. The Multiskan SkyHigh microplate reader was used to measure the absorbance at 570 nm.
Statistical Analysis
All experiments were carried out in triplicate and results are presented as mean ± standard deviation (SD). The data were analyzed with GraphPad Prism (version 9.0), using a two-way ANOVA followed by the Tukey's post hoc test. P values of < 0.05 were considered significant.
Results
The designed peptides showed potent antibacterial activity
The newly designed peptides derived from C(1–7)M(2–9) were tested against the biofilm-forming strain of S. epidermidis (Table 1). Among these peptides, the most potent antibacterial activity was demonstrated by the lysine-substituted derivatives with increased net charge, CM-10K and CM-10K14K with MICs (3.91 µg/mL) and MBCs (7.81 µg/mL), comparable to those of vancomycin, a conventional antibiotic. Derivatives with increased hydrophobicity (CM-1V10K14K, CM-1V14K and CM-A) had two-fold higher MBC values than that of the parental peptide.
CM-10K14K exhibited potent antimicrobial activity with low toxicity
The potential toxicity of the peptides was evaluated by their ability to lyse hRBCs and their toxicity against L929 mouse fibroblast cells. The lysis effect of peptides on hRBCs is shown in Fig. 3; HC50 was defined as the concentration of peptide causing 50% lysis of hRBCs (Table 1)32. The results showed that all derivatives, except CM-10K (with less hydrophobicity and higher mean hydrophobic moment than the parental peptide) had improved selectivity as demonstrated by higher HC50 values. Of all peptides, CM-A (an alanine-substituted peptide with the highest hydrophobicity and the lowest mean hydrophobic moment) displayed the strongest hemolytic activity with an HC50 of 42.58 ± 1.98 µg/mL. In contrast, CM-10K14K (a lysine-enriched peptide) showed the least hemolytic activity based on having the highest HC50 (561.90 ± 88.19 µg/mL). At both the MIC and MBC of CM-10K14K, its hemolytic activity was less than 9%.
Hemolytic activity of peptide derivatives against human red blood cells. The experiments were performed in triplicate and the data are expressed as the mean ± SD. P values were determined using a two-way ANOVA with Tukey’s post hoc test. Significant differences are indicated in GP style: > 0.05 (ns), ≤ 0.05 (*), ≤ 0.01 (**), ≤ 0.001 (***), ≤ 0.0001 (****). The horizontal dashed line represented 50% hemolysis.
Given the low degree of hemolytic activity of CM-10K14K, its cytotoxicity was further assessed using L929 mouse fibroblast cells (Fig. 4). The toxicity on these cells was also low, with an IC50 of 56.53 ± 1.84 µg/mL. After peptide treatment, the cell viability was 100% and 92.87 ± 1.82 µg/mL at the MIC and MBC, respectively. Based on its antibacterial and toxicity profile, peptide CM-10K14K was selected for further analysis. CM-10K14K, a candidate peptide, also showed broad-spectrum antibacterial activity against a wide range of gram-positive and gram-negative bacteria were frequently involved in catheter-related infections with MICs ranging from 7.81 to 31.25 µg/mL and MBCs ranging from 7.81 to 62.5 µg/mL as shown in Table 2. Among tested strains, CM-10K14K displayed the strongest antibacterial activity against S. epidermidis with the lowest MIC and MBC values.
The half maximal inhibitory concentration (IC50) of CM-10K14K on L929 mouse fibroblast cells at 24 h. The experiments were performed in triplicate and the data were analyzed by GraphPad Prism 7 Software and are expressed as the mean ± SD. The dashed lines represented the determination of the IC50 value.
CM-10K14K inhibited and eradicated S. epidermidis biofilm
At a concentration of 7.81 µg/mL (MBC) and higher, CM-10K14K killed all S. epidermidis cells grown within the biofilm indicating the bactericidal effect of this peptide and consequently the prevention of biofilm formation (Fig. 5A). These findings are consistent with the reduction in biofilm biomass observed through crystal violet staining (Supplementary Fig. 1). Notably, at a concentration that inhibits the bacterial growth or MIC (3.91 µg/mL), S. epidermidis biofilm cells remained viable. This observation highlights a significant difference in the response of planktonic and biofilm cells to the peptide treatment. In addition to biofilm formation inhibitory activity, CM-10K14K displayed a dose-dependent eradication activity on mature or established S. epidermidis biofilm. More than 90% of mature biofilm was eradicated at a peptide concentration equal to or more than 31.25 μg/ml as shown in Fig. 5B.
Biofilm cells viability (A) and Biofilm eradication activity (B) of S. epidermidis ATCC 35,984 after treated with different concentration of CM-10K14K. The experiments were performed in triplicate and the data were expressed as the mean ± SD. P values were determined using a two-way ANOVA with Tukey’s post hoc test. Significant differences are indicated in GP style: > 0.05 (ns), ≤ 0.05 (*), ≤ 0.01 (**), ≤ 0.001 (***), ≤ 0.0001 (****).
CM-10K14K could inhibit the bacterial growth in the presence of protease enzyme
Most AMPs are susceptible to protease degradation because their amino acid sequence served as excellent substrates for proteolytic cleavage. The biostability of CM-10K14K compared with CM parent peptide was determined in the presence of proteinase K, a broad-spectrum protease. CM-10K14K demonstrated higher tolerance to proteinase K compared to that of CM, as indicated by a reduced survival rate, as illustrated in Fig. 6. After 6 h of incubation, CM-10K14K demonstrated the ability to inhibit bacterial growth ranging from the lowest (0.98 µg/mL) to the highest tested concentration, while at least its MIC was needed for the CM peptide to kill the bacteria. After 24-h incubation, CM-10K14K at 31.25 and 62.5 µg/mL exhibited strong antibacterial activity, but the original CM lost its ability to kill bacteria. The growth inhibition results from the in vitro experiment were consistent with the potential cleavage site predicted by PeptideCutter (https://web.expasy.org/peptide_cutter/). The CM sequence exhibited 9 cleavage site positions, whereas the CM-10K14K sequence had 7 cleavage sites as shown in Supplementary Table 1.
The relative survival rate of S. epidermidis ATCC 35984 after treated with CM and CM-10K14K in the presence of proteinase K for 6 and 24 h. The experiments were performed in triplicate and the data were expressed as the mean ± SD. P values were determined using a two-way ANOVA with Tukey’s post hoc test. Significant differences are indicated in GP style: > 0.05 (ns), ≤ 0.05 (*), ≤ 0.01 (**), ≤ 0.001 (***), ≤ 0.0001 (****).
CM-10K14K adopted an α-helical structure in membrane-mimetic environments
As suggested by I-TASSER and in silico molecular three-dimensional (3D) models using BIOVIA Discovery Studio Visualizer 2020, CM-10K14K and other peptides showed an α-helical structure (Fig. 7). The secondary structures adopted by peptides in membrane-mimic environments were further evaluated using CD spectroscopy (Fig. 8). In aqueous solution, the existence of a significant minimum peak of mean residue ellipticity at 198 nm suggested that CM-10K14K constructed random coil structures. In both 30 mM SDS and 50% TFE solutions, CM-10K14K revealed two negative bands at 222 nm and at 208 nm, and a positive band at 193 nm, characteristics of α-helical structures. These findings indicated that CM-10K14K formed an α-helical structure in membrane-mimicking conditions.
Circular dichroism spectra of CM-10K14K in aqueous solution (red), 30 mM SDS micelles (green) and 50% TFE (blue). The samples were loaded in a rectangular quartz cell (0.1 cm path length); the CD signals were measured at 25 °C using a Jasco-815 spectropolarimeter and recorded at a scanning speed of 10 nm/min in the wavelength range of 190–260 nm.
CM-10K14K rapidly kills S. epidermidis
The killing kinetics of CM-10K14K against S. epidermidis were determined at peptide concentrations of 3.91 μg/mL (MIC) and 7.81 μg/mL (MBC) and compared to those of untreated bacteria (control). As shown in Fig. 9, CM-10K14K at MIC showed a strong inhibitory effect that reduced the concentration of viable S. epidermidis approximately 106 CFU/mL within 15 min, and persisted at least 6 h after treatment. Beyond that time bacterial regrowth was observed. However, CM-10K14K at MBC totally eradicated bacteria within 15 min and no regrowth was observed through 24 h. Therefore, CM-10K14K displayed bactericidal activity which was rapid, and both concentration- and time-dependent.
CM-10K14K disrupted bacterial membranes by depolarization and permeabilization
The mechanisms of antibacterial action of CM-10K14K were investigated using flow cytometry to determine if they were membrane-related. The positive fluorescent signals emitted by PI staining indicated that bacterial membrane integrity was severely compromised or pores had formed, whereas the fluorescent signals from BOX identified the depolarized bacterial cells. In flow cytometric analysis, FSC and SSC gating was used to define the bacteria for study (77.95 ± 0.81%; Fig. 10A). Unstained cells are used to set the negative population (Fig. 10B). Most untreated cells demonstrated negative fluorescent signals (95.34 ± 0.18%) indicating healthy and intact cell membranes (Fig. 10C). Heat treatment of bacterial cells at 70 °C for 30 min, a condition known to kill S. epidermidis within biofilms33, was utilized as a positive control in the experiment34. Heated bacterial cells had high levels (91.51 ± 0.32%) of depolarization and permeabilization (Fig. 10D). The membrane-active mechanism was investigated in a short-time course at the early phase of treatment, based on the rapid bactericidal activity of CM-10K14K observed in the killing kinetics experiments. The results showed that CM-10K14K at 1 × MIC induced time-dependent depolarization and permeabilization of 90.80 ± 0.51%, 91.36 ± 0.74% and 95.71 ± 0.26% of treated bacteria at 5, 15, and 30 min, respectively (Fig. 10E–G). These findings showed that CM-10K14K damaged S. epidermidis membranes in a time-dependent manner through depolarization and permeabilization, and supported their rapidity in the killing kinetics experiment.
Flow cytometry analysis of S. epidermidis treated with CM-10K14K. (A) The tested bacterial population. (B) Untreated S. epidermidis without PI and BOX. (C) Untreated S. epidermidis with PI and BOX stained. The effect on membrane permeability (PI) and membrane depolarization (BOX) of S. epidermidis after treatment with 70 °C for 30 min (D), and CM-10K14K at 1 × MIC for 5, 15 and 30 min (E–G). The percentage of cell populations that fell in each gate are shown in the four corners of each plot. The experiments were performed in triplicate.
CM-10K14K inhibited biofilm formation and altered bacterial membrane structures
Alterations in bacterial morphology and biofilm formation after peptide treatment were evaluated using SEM. Treatment with CM-10K14K at 1 × MIC for 15 min resulted in significant membrane corrugation, distortion and damage of S. epidermidis (Fig. 11C,D), as well as a reduction of extracellular matrix or biofilm when compared with controls. In contrast, the untreated bacterial cells showed more structural and adherent characteristics and became embedded within a biofilm matrix (Fig. 11A,B).
Cell structures at the nanometer scale and intracellular alterations in peptide-treated bacterial cells were investigated by TEM. Untreated bacterial cells were spherical in shape and had smooth cell walls (Fig. 12A–C). In contrast, cells treated with CM-10K14K were structureless, containing empty electron-transparent parts and amorphous clumps of various electron densities (Fig. 12D–F) as described previously35. The red arrows in Fig. 12 indicate cell membrane disintegration and dispersion of intracellular contents after exposure to CM-10K14K at MIC for 15 min. These TEM results agreed with the results from flow cytometry analysis, suggesting that CM-10K14K acted on bacterial membranes as a mechanism of its antibacterial activity.
CM-10K14K interacts with S. epidermidis chromosomal DNA
In addition to disrupting the bacterial membrane, some AMPs kill bacteria by penetrating the cells and interacting with intracellular components36. The DNA-binding ability of CM-10K14K was thus evaluated in a gel retardation assay. Twofold serial concentrations of peptide (0.98–250 µg/mL) were mixed with a fixed amount (143.5 ng) of genomic DNA extracted from S. epidermidis. The complexes were electrophoresed on a 1% agarose gel. When mixed with lower concentrations (0.98–31.25 µg/mL) of peptide, the genomic DNA was able to migrate through the gel (lanes 2–7) in the same manner as non-complexed DNA (lane 1). When the amount of peptide was increased (62.5–250 µg/mL), the genomic DNA was significantly retarded in the gel, indicating that it had become aggregated by CM-10K14K (Fig. 13). This finding suggested that CM-10K14K can bind to bacterial genomic DNA, which could be the intracellular target for bacterial killing mechanisms.
Analysis of the bacterial DNA-binding activity of CM-10K14K using a gel retardation assay. Concentrations of CM-10K14K, ranging from 0.98, 1.95, 3.91, 7.81, 15.63, 31.25, 62.5, 125 to 250 μg/mL (Lanes 2–10, respectively), were mixed with 143.5 ng DNA of S. epidermidis. Lane M and 1 represent the VC 100 bp Plus DNA Ladder (Vivantis, Malaysia) and genomic DNA without peptide treatment, respectively. The original gel is presented in Supplementary Fig. 2.
CM-10K14K impregnated in catheters inhibits biofilm formation by S. epidermidis
The effect of peptide-impregnated catheters was evaluated in three ways: bactericidal activity against free-floating (planktonic) S. epidermidis, suppression of biofilm development by surviving bacteria, and inhibition of biofilm formation adherent to the catheter surface. Figure 14 shows the in vitro antibacterial activity of CM-10K14K-impregnated catheters compared with that of unmodified catheters; the assay allowed S. epidermidis colonization with bacterial cell counts ranging up to 107–108 CFU/mL. CM-10K14K catheters impregnated by dipping in 250, 500 or 1000 µg/mL had reduced bacterial counts of approximately 1 log10CFU/mL, 2 log10CFU/mL and 7 log10CFU/mL, respectively, after exposure to S. epidermidis in vitro for 6 h, and had significantly higher bactericidal activity than vancomycin-coated catheters at 1000 µg/mL dipped condition (Fig. 14). Although some bacterial cells survived and grew, CM-10K14K-impregnated catheters still displayed bactericidal activity 24 h after incubation (Supplementary Fig. 3).
The bactericidal effect of CM-10K14K-impregnated catheters against planktonic S. epidermidis after 6 h of incubation compared to that of vancomycin. P-values were determined using a two-way ANOVA with Tukey’s post hoc test. Significant differences are indicated in GP style: > 0.05 (ns), ≤ 0.05 (*), ≤ 0.01 (**), ≤ 0.001 (***), ≤ 0.0001 (****).
The CM-10K14K-impregnated catheters also inhibited biofilm formation by adherent cells on both 24-well plates and catheters in a dose-dependent manner when exposed to S. epidermidis for 6 and 24 h. On a 24-well plate, the impregnated CM-10K14K on catheters were released and diminished the biomass of S. epidermidis biofilms by more than 50% at 250 µg/mL. It reached to 90% at 500 and 1000 µg/mL dipped conditions after 6 h of incubation, as well as approximately 5%, 35% and 71% of biofilm inhibition after 24 h of treatment (Fig. 15).
Biofilm inhibition on 24-well plate by CM-10K14K-impregnated catheters dipped in 250, 500 or 1000 µg/mL peptide and measured using the crystal violet assay. P values were determined using a two-way ANOVA with Tukey’s post hoc test. Significant differences are indicated in GP style: > 0.05 (ns), ≤ 0.05 (*), ≤ 0.01 (**), ≤ 0.001 (***), ≤ 0.0001 (****).
Biofilm formation on CM-10K14K-impregnated catheters was found to be decreased in a dose-dependent manner. After 6 h of incubation, CM-10K14K on the impregnated catheter reduced the biomass of S. epidermidis biofilms by 74.06 ± 9.51%, 88.17 ± 9.31% and 97.22 ± 5.19% at 250, 500 and 1000 µg/mL dipped conditions, respectively (Fig. 16). This inhibition of biofilm formation was greater than that of vancomycin-impregnated catheters, especially in the 250 µg/mL dipped condition. These results supported the finding of inhibition of S. epidermidis biofilm formation by CM-10K14K-impregnated catheters in vitro.
Inhibition of biofilm on CM-10K14K-impregnated catheters dipped in 250, 500 or 1000 µg/mL of peptide measured using the crystal violet assay. P values were determined using a two-way ANOVA with Tukey’s post hoc test. Significant differences are indicated in GP style: > 0.05 (ns), ≤ 0.05 (*), ≤ 0.01 (**), ≤ 0.001 (***), ≤ 0.0001 (****).
Discussion
One of the most prevalent nosocomial diseases in hospitals is catheter-associated urinary tract infection (CAUTI), mostly caused by cross-contamination from the urinary drainage bag or the skin11, especially by S. epidermidis10,37. CAUTIs are reported in 80% of patients who have indwelling urinary catheters and in 10–50% of patients who have short-term catheterization10. Indwelling catheters are very susceptible to infection as bacteria can adhere, colonize and multiply quickly on their surfaces and subsequently form biofilms11,17. Major consequences such pyelonephritis, bacteremia, septicemia and sepsis can occur if left untreated, contributing significantly to the morbidity and mortality linked to CAUTIs10,38. Antimicrobial peptides (AMPs), with their biocompatible, broad-spectral antibacterial and antibiofilm properties, have significant potential for surface antifouling39. Since they are more effective against drug-resistant pathogens than existing antibiotic treatments, they provide a promising approach for the development of novel antimicrobial catheters to prevent CAUTIs.
Among the promising AMPs, 15-residue CM peptides [hybrids of the first seven amino acids of cecropin A and residues 2–9 of melittin, C(1–7)M(2–9)] in particular have attractive antimicrobial and antibiofilm properties20,40. In this study, the secondary structure and helical wheel projections of the CM parental peptide were exploited to design derivatives by amino acid substitution with potential antibacterial and antibiofilm activity along with low toxicity. The balance between positive charge and hydrophobicity is evidently important for the activity of short AMPs41 and thus in design strategy. Consistent with previous studies, our results indicate that lysine-substituted derivatives with increased net positive charge (CM-10K and CM-10K14K) had improved antibacterial and decreased hemolytic activities40. In contrast, derivatives with increased hydrophobicity (by substituting valine and alanine) did not have enhanced antibacterial activity. When derivatives with the same net charge and hydrophobicity were compared, those with the higher mean hydrophobic moment demonstrated lower hemolytic activity (greater HC50 values), such as CM versus CM-1V14K and CM-10K versus CM-1V10K14K. These results indicated that increased amphipathicity of peptides was associated with reduced toxicity against hRBCs42. Additionally, peptides with a lysine substitution at position 10 had significantly enhanced antibacterial and antibiofilm activity, pointing to the potential impact of increased net charge and a proper hydrophilic part on the polar face of the helical structure41. Antibiofilm activity was correlated with bactericidal activity of CM derivatives.
The capability of CM-10K14K to inhibit biofilm formation was most likely a result of the rapid killing of S. epidermidis bacteria in the initial inoculum through the direct antibacterial activity of the peptide. This suggested that the prevention of biofilm formation by CM-10K14K is primarily a consequence of its ability to promptly eliminate the initial bacterial population, thereby prevent biofilm development. Temporin 1Tb (TB) and its analogs (TB_KKG6A and TB_L1FK) were found to inhibit biofilm formation of P. aeruginosa and S. aureus at concentrations higher to their MIC43. The antibiofilm effect of these peptides is more likely attributed to the direct killing of biofilm-forming bacteria during their planktonic stage, similar to the mechanism observed with CM-10K14K, rather than acting through a biofilm-specific mechanism.
The eradication of mature biofilms presents a significant obstacle in the field of biofilm treatment, since up to 90% of an established biofilm is composed of an extracellular matrix. This matrix surrounds the bacteria and delays or prevents the penetration of antibiofilm agents into the biofilm structure43. Previous studies have emphasized the potential of peptide in combatting biofilms due to their amphipathic property and flexible molecular structure, allowing them to penetrate the extracellular matrix, prevent, and disrupt biofilms44. According to the findings of this study, CM-10K14K exhibited the capability to eliminate established S. epidermidis biofilms. However, a higher concentration of the peptide was necessary for this eradication compared to the concentration required for preventing biofilm formation. This suggested that action of the peptide to eradicate established biofilm may be limited by the presence of extracellular matrix.
CM-10K14K demonstrated more tolerant to proteinase K when compared to that of CM. The replacement of alanine and valine at positions 10 and 14 with two lysine residues enhanced the stability to proteinase K because this enzyme cleaves peptide bonds next to the carboxyl-terminal of aromatic and hydrophobic residues45. However, the antibacterial activity of CM-10K14K might be decreased in the higher concentration and/or other types of proteolytic enzyme, because of their sequence serve as excellent substrates for proteolytic cleavage. D-amino acid replacements might increase the biostability of CM-10K14K without reducing its antimicrobial activity because non-natural amino acids are less likely to degrade and tend to be more stable towards proteolysis28.
CAUTIs are caused by free-floating bacteria or those encrusted in and producing biofilms on the surfaces of medical devices. It thus may be necessary that indwelling catheters possess their own antibacterial and antibiofilm properties14. The impregnation of CM-10K14K onto urinary catheters by physical adsorption, a simple and traditional method of immobilizing AMPs, was developed to shield Foley catheters from colonization by biofilm-forming bacteria and thereby prevent associated infections46. In this study, Foley catheters were dipped in 250, 500 or 1000 µg/mL of CM-10K14K and subsequently released peptide, generating concentrations of approximately 18, 23 and 81 µg/mL, respectively, as tested by a fluorescamine assay (Supplementary Fig. 4). The antibacterial and antibiofilm activities of CM-10K14K-impregnated catheters were further assessed using an in vitro catheter-associated, urinary tract infection model. The release of CM-10K14K from impregnated catheters decreased planktonic growth and inhibited biofilm formation by adherent cells in a dose-dependent manner when challenged with S. epidermidis for 6 and 24 h. The results revealed that impregnation of CM-10K14K prevented bacterial adherence to catheters, hence minimizing the formation of biofilms on them.
Because of inherent differences between the membrane composition and architecture of microbial and mammalian cells allowing selectivity by AMPs47, CM-10K14K with potent antibacterial and antibiofilm activities along with minimal toxicity against mammalian cells (L929 mouse fibroblasts and human red blood cells) was identified as a candidate peptide. The mechanism of action of antibacterial and antibiofilm peptides is traditionally considered to be their disruption of bacterial membranes48. The negatively charged surfaces of S. epidermidis49 attract the positively charged CM-10K14K peptide via electrostatic interactions, and induce secondary structural transformation and interactions with the hydrophobic part of bacterial membranes. Circular dichroism spectroscopy was utilized to evaluate the secondary structure of the peptide. By shifting two negative signals at 222 nm and 208 nm, and a positive signal at 193 nm, the CD spectra of CM-10K14K showed that it formed an α-helical structure under membrane-mimetic conditions as predicted by the in silico 3D model. Following structural alteration, CM-10K14K killed viable S. epidermidis within 15 min in a concentration- and time-dependent manner, suggesting that the bacteria were killed even before they had the ability to divide because the generation times of surface growing S. epidermidis ranged from 17 to 38 min50. This is a crucial mechanism for preventing development of bacterial biofilms after initial attachment, as the survival of all other cells inside a biofilm is dependent on the interactions between the surface and the bacterial cells51.
AMPs typically kill bacteria by breaking their membranes or entering bacterial cells and interacting with internal components52. The membrane disruption mechanism was investigated by flow cytometry, SEM and TEM. Within 5 min, CM-10K14K induced both depolarization and permeabilization at the membrane level; within 15 min there was membrane damage with corrugation and distortion (seen by SEM) and membrane disintegration with dispersion of intracellular contents (seen by TEM). The strong affinity between the cationic peptide and anionic components of microbial pathogens leaded to rapid depolarization and permeabilization53. Most of membrane-lytic AMPs could rapidly destroy the bacterial membrane and some of them can kill bacteria in seconds after the initial contact with cell membrane54. In the opposite, some AMPs exhibited slow bactericidal action by exerting intracellular inhibitory effects via interacting at the molecular level, serving as the supportive mechanisms to achieve efficient killing55. Indolicidin induced increased permeabilization, facilitating continuous peptide entry into the cytosol to inhibit DNA replication and transcription56,57. Buforin II exhibited high nucleic acid binding affinity, implying that it inhibited cellular processes by interrupting DNA55,58. The antibiofilm activity of CM-10K14K was supported by SEM results which demonstrated a decrease in slimy extracellular matrix or biofilm as compared to untreated controls. Beside membrane-active mechanisms, the interaction of CM-10K14K with intracellular targets like DNA was investigated by gel retardation assay. CM-10K14K bound to genomic DNA of S. epidermidis, a possible target after penetration of the bacterial cell membrane and might play a part in the antibacterial activity. Due to its rapid bactericidal activity and multifunction, CM-10K14K might serve as the potential lead peptides for further development as novel antibacterial agents with improved therapeutic profiles.
To continue the clinical application of CM-10K14K as antimicrobial catheter, several factors including toxicity and stability should be concerned. A variety of coating and nanoparticle drug delivery system was optimized for each peptide to control the release, protect the peptide, and eventually overcome these obstacles. For example, functionalization of polyurethane catheters with peptide E6-brush coating can reduce bacterial adhesion on the catheter surface, inhibit planktonic bacterial growth in urine, and are biocompatible with bladder epithelial and fibroblast cells17. Srisang et al. revealed that chlorhexidine-loaded nanoparticles (CHX-NPs) coated catheters demonstrated delayed encrustation and bacterial colonization. Furthermore, in vivo biocompatibility experiments revealed that coated catheters did not induce dermal toxicity59. Further development of the drug delivery or coating strategy as well as the study of underlying antibiofilm mechanism at molecular level and in vivo efficacy could enhance the clinical feasibility of CM-10K14K.
Data availability
All of the data produced throughout the research are contained in this article and its supplementary information file.
References
McCann, M. T., Gilmore, B. F. & Gorman, S. P. Staphylococcus epidermidis device-related infections: Pathogenesis and clinical management. J. Pharm. Pharmacol. 60, 1551–1571 (2008).
Liu, X. et al. Oxidation-sensing regulator AbfR regulates oxidative stress responses, bacterial aggregation, and biofilm formation in Staphylococcus epidermidis. J. Biol. Chem. 288, 3739–3752 (2013).
Severn, M. M. & Horswill, A. R. Staphylococcus epidermidis and its dual lifestyle in skin health and infection. Nat. Rev. Microbiol. 21, 97–111 (2023).
Pietrocola, G. et al. Colonization and infection of indwelling medical devices by Staphylococcus aureus with an emphasis on orthopedic implants. Int. J. Mol. Sci. 23, 5958. https://doi.org/10.3390/ijms23115958 (2022).
CDC. Catheter-associated Urinary Tract Infections (CAUTI), https://www.cdc.gov/hai/ca_uti/uti.html#print (2015).
Rabanal, F. et al. A bioinspired peptide scaffold with high antibiotic activity and low in vivo toxicity. Sci. Rep. 5, 10558. https://doi.org/10.1038/srep10558 (2015).
Belfield, K., Chen, X., Smith, E. F., Ashraf, W. & Bayston, R. An antimicrobial impregnated urinary catheter that reduces mineral encrustation and prevents colonisation by multi-drug resistant organisms for up to 12 weeks. Acta Biomater. 90, 157–168 (2019).
Pratt, R. J. et al. epic2: National evidence-based guidelines for preventing healthcare-associated infections in NHS hospitals in England. J. Hosp. Infect. 65, S1–S59 (2007).
Kai-Larsen, Y. et al. Foley catheter with noble metal alloy coating for preventing catheter-associated urinary tract infections: A large, multi-center clinical trial. Antimicrob. Resist. Infect. Control 10, 40. https://doi.org/10.1186/s13756-021-00907-w (2021).
Al-Qahtani, M., Safan, A., Jassim, G. & Abadla, S. Efficacy of anti-microbial catheters in preventing catheter associated urinary tract infections in hospitalized patients: A review on recent updates. J. Infect. Public Health 12, 760–766 (2019).
Singha, P., Locklin, J. & Handa, H. A review of the recent advances in antimicrobial coatings for urinary catheters. Acta Biomater. 50, 20–40 (2017).
Johnson, J. R., Johnston, B. & Kuskowski, M. A. In vitro comparison of nitrofurazone- and silver alloy-coated Foley catheters for contact-dependent and diffusible inhibition of urinary tract infection-associated microorganisms. Antimicrob. Agents Chemother. 56, 4969–4972 (2012).
Segev, G. et al. Evaluation of urinary catheters coated with sustained-release varnish of chlorhexidine in mitigating biofilm formation on urinary catheters in dogs. J. Vet. Intern. Med. 27, 39–46 (2013).
Lim, K. et al. Development of a catheter functionalized by a polydopamine peptide coating with antimicrobial and antibiofilm properties. Acta Biomater. 15, 127–138 (2015).
Yasir, M., Willcox, M. D. & Dutta, D. Action of antimicrobial peptides against bacterial biofilms. Materials 11, 2468. https://doi.org/10.3390/ma11122468 (2018).
Luong, H. X., Thanh, T. T. & Tran, T. H. Antimicrobial peptides—Advances in development of therapeutic applications. Life Sci. 260, 118407. https://doi.org/10.1016/j.lfs.2020.118407 (2020).
Yu, K. et al. Anti-adhesive antimicrobial peptide coating prevents catheter associated infection in a mouse urinary infection model. Biomaterials 116, 69–81. https://doi.org/10.1016/j.biomaterials.2016.11.047 (2017).
Riool, M., de Breij, A., Drijfhout, J. W., Nibbering, P. H. & Zaat, S. A. J. Antimicrobial peptides in biomedical device manufacturing. Front. Chem. 5, 63. https://doi.org/10.3389/fchem.2017.00063 (2017).
De Zoysa, G. H. & Sarojini, V. Feasibility study exploring the potential of novel battacin lipopeptides as antimicrobial coatings. ACS Appl. Mater. Interfaces 9, 1373–1383 (2017).
Vergis, J. et al. Efficacy of indolicidin, cecropin A (1–7)-melittin (CAMA) and their combination against biofilm-forming multidrug-resistant enteroaggregative Escherichia coli. Probiotics Antimicrob. Proteins. 12, 705–715 (2020).
CLSI. Methods for dilution antimicrobial susceptibility tests for bacteria that grow aerobically; approved standard-Tenth edition. CLSI document M07-A10. Wayne, PA: Clinical and Laboratory Standards Institute (2015).
Andrews, J. M. Determination of minimum inhibitory concentrations. J. Antimicrob. Chemother. 48, 5–16 (2001).
Stark, M., Liu, L.-P. & Deber, C. M. Cationic hydrophobic peptides with antimicrobial activity. Antimicrob. Agents Chemother. 46, 3585–3590 (2002).
Klubthawee, N. & Aunpad, R. A thermostable, modified cathelicidin-derived peptide with enhanced membrane-active activity against Salmonella enterica serovar Typhimurium. Front. Microbiol. 11, 592220. https://doi.org/10.3389/fmicb.2020.592220 (2020).
Klubthawee, N., Adisakwattana, P., Hanpithakpong, W., Somsri, S. & Aunpad, R. A novel, rationally designed, hybrid antimicrobial peptide, inspired by cathelicidin and aurein, exhibits membrane-active mechanisms against Pseudomonas aeruginosa. Sci. Rep. 10, 9117. https://doi.org/10.1038/s41598-020-65688-5 (2020).
Ceri, H. et al. The Calgary Biofilm Device: New technology for rapid determination of antibiotic susceptibilities of bacterial biofilms. J. Clin. Microbiol. 37, 1771–1776 (1999).
Swedan, S., Shubair, Z. & Almaaytah, A. Synergism of cationic antimicrobial peptide WLBU2 with antibacterial agents against biofilms of multi-drug resistant Acinetobacter baumannii and Klebsiella pneumoniae. Infect. Drug Resist. 12, 2019–2030 (2019).
Jia, F. et al. D-amino acid substitution enhances the stability of antimicrobial peptide polybia-CP. Acta Biochim. Biophys. Sin. 49, 916–925 (2017).
Liu, Y., Xia, X., Xu, L. & Wang, Y. Design of hybrid β-hairpin peptides with enhanced cell specificity and potent anti-inflammatory activity. Biomaterials 34, 237–250 (2013).
Wang, J. et al. High specific selectivity and membrane-active mechanism of the synthetic centrosymmetric α-helical peptides with Gly-Gly pairs. Sci. Rep. 5, 15963. https://doi.org/10.1038/srep15963 (2015).
Fisher, L. E. et al. Biomaterial modification of urinary catheters with antimicrobials to give long-term broadspectrum antibiofilm activity. J. Control. Release 202, 57–64 (2015).
Ruiz, J., Calderon, J., Rondón-Villarreal, P. & Torres, R. Analysis of structure and hemolytic activity relationships of antimicrobial peptides (AMPs). Adv. Comput. Biol. 232, 253–258 (2014).
Pijls, B. G., Sanders, I. M. J. G., Kujiper, E. J. & Nelissen, R. G. H. H. Induction heating for eradicating Staphylococcus epidermidis from biofilm. Bone Jt. Res. 9, 192–199 (2020).
Ng, T. W., Chan, W. L. & Lai, K. M. Influence of membrane fatty acid composition and fluidity on airborne survival of Escherichia coli. Appl. Microbiol. Biotechnol. 102, 3327–3336 (2018).
Grigor’eva, A. et al. Changes in the ultrastructure of Staphylococcus aureus treated with cationic peptides and chlorhexidine. Microorganisms 8, 1991. https://doi.org/10.3390/microorganisms8121991 (2020).
Ntwasa, M. Cationic peptide interactions with biological macromolecules. In Binding Protein (ed. Abdelmohsen, K.) (InTech, Singapore, 2012).
Donlan, R. M. Biofilms and device-associated infections. Emerg. Infect. Dis. 7, 277–281 (2001).
Bursle, E. C. et al. Risk factors for urinary catheter associated bloodstream infection. J. Infect. 70, 585–591 (2015).
Yu, K. et al. Rapid assembly of infection-resistant coatings: Screening and identification of antimicrobial peptides works in cooperation with an antifouling background. ACS Appl. Mater. Interfaces 13, 36784–36799 (2021).
Sato, H. & Feix, J. B. Lysine-enriched cecropin-mellitin antimicrobial peptides with enhanced selectivity. Antimicrob. Agents Chemother. 52, 4463–4465 (2008).
Mikut, R. et al. Improving short antimicrobial peptides despite elusive rules for activity. Biochim. Biophys. Acta. 1858, 1024–1033 (2016).
Matthyssen, T. et al. The potential of modified and multimeric antimicrobial peptide materials as superbug killers. Front. Chem. 9, 795433. https://doi.org/10.3389/fchem.2021.795433 (2021).
Grassi, L., Maisetta, G., Maccari, G., Esin, S. & Batoni, G. Analogs of the frog-skin antimicrobial peptide Temporin 1Tb exhibit a wider spectrum of activity and a stronger antibiofilm potential as compared to the parental peptide. Front. Chem. 5, 24. https://doi.org/10.3389/fchem.2017.00024 (2017).
Wang, M. et al. Antibiofilm property and multiple action of peptide PEW300 against Pseudomonas aeruginosa. Front. Microbiol. 13, 963292. https://doi.org/10.3389/fmicb.2022.963292 (2022).
Glibowicka, M., He, S. & Deber, C. M. Enhanced proteolytic resistance of cationic antimicrobial peptides through lysine side chain analogs and cyclization. Biochem. Biophys. Res. Commun. 612, 105–109 (2022).
Nicolas, M. et al. Strategies for antimicrobial peptides immobilization on surfaces to prevent biofilm growth on biomedical devices. Antibiotics 11, 13. https://doi.org/10.3390/antibiotics11010013 (2021).
Ebenhan, T., Gheysens, O., Kruger, H. G., Zeevaart, J. R. & Sathekge, M. M. Antimicrobial peptides: Their role as infection-selective tracers for molecular imaging. Biomed. Res. Int. 2014, 867381. https://doi.org/10.1155/2014/867381 (2014).
Raheem, N. & Straus, S. K. Mechanisms of action for antimicrobial peptides with antibacterial and antibiofilm functions. Front. Microbiol. 10, 2866. https://doi.org/10.3389/fmicb.2019.02866 (2019).
Jones, D. S., Adair, C. G., Mawhinney, W. M. & Gorman, S. P. Standardisation and comparison of methods employed for microbial cell surface hydrophobicity and charge determination. Int. J. Pharm. 131, 83–89 (1996).
Gottenbos, B., van der Mei, H. C. & Busscher, H. J. Initial adhesion and surface growth of Staphylococcus epidermidis and Pseudomonas aeruginosa on biomedical polymers. J. Biomed. Mater. Res. 50, 208–214 (2000).
Palmer, J., Flint, S. & Brooks, J. Bacterial cell attachment, the beginning of a biofilm. J. Ind. Microbiol. Biotechnol. 34, 577–588 (2007).
Benfield, A. H. & Henriques, S. T. Mode-of-action of antimicrobial peptides: Membrane disruption vs. intracellular mechanisms. Front. Med. Technol. 2, 610997. https://doi.org/10.3389/fmedt.2020.610997 (2020).
Zhang, Q.-Y. et al. Antimicrobial peptides: Mechanism of action, activity and clinical potential. Mil. Med. Res. 8, 48. https://doi.org/10.1186/s40779-021-00343-2 (2021).
Bahar, A. A. & Ren, D. Antimicrobial peptides. Pharmaceuticals 6, 1543–1575 (2013).
Le, C.-F., Fang, C.-M. & Sekaran, S. D. Intracellular targeting mechanisms by antimicrobial peptides. Antimicrob. Agents Chemother. 61, e02340-e2416. https://doi.org/10.1128/AAC.02340-16 (2017).
Subbalakshmi, C. & Sitaram, N. Mechanism of antimicrobial action of indolicidin. FEMS Microbiol. Lett. 160, 91–96 (1998).
Ghosh, A. et al. Indolicidin targets duplex DNA: Structural and mechanistic insight through a combination of spectroscopy and microscopy. ChemMedChem 9, 2052–2058 (2014).
Park, C. B., Kim, H. S. & Kim, S. C. Mechanism of action of the antimicrobial peptide Buforin II: Buforin II kills microorganisms by penetrating the cell membrane and inhibiting cellular functions. Biochem. Biophys. Res. Commun. 244, 253–257 (1998).
Srisang, S., Boongird, A., Ungsurungsie, M., Wanasawas, P. & Nasongkla, N. In vivo catheterization study of chlorhexidine-loaded nanoparticle coated Foley urinary catheters in male New Zealand white rabbits. J. Biomed. Mater. Res. Part B Appl. Biomater. 109, 1836–1843 (2021).
Zhang, Y. et al. Incidence rate, pathogens and economic burden of catheter-related bloodstream infection: A single-center, retrospective case-control study. Infect. Drug Resist. 16, 3551–3560 (2023).
Gahlot, R., Nigam, C., Kumar, V., Yadav, G. & Anupurba, S. Catheter-related bloodstream infections. Int. J. Crit. Illn. Inj. Sci. 4, 162–167 (2014).
Surapat, B. et al. Microbial epidemiology and risk factors for relapse in gram-negative bacteria catheter-related bloodstream infection with a pilot prospective study in patients with catheter removal receiving short-duration of antibiotic therapy. BMC Infect. Dis. 20, 604. https://doi.org/10.1186/s12879-020-05312-z (2020).
Acknowledgements
This work was supported by the Thailand Science Research and Innovation Fundamental Fund, and Thammasat University Research Fund (Contract No. TUFT-FF 34/2565). We would like to thank Dr. Arthur Brown, Faculty of Medical Technology, Mahidol University, Thailand, for providing language assistance.
Author information
Authors and Affiliations
Contributions
N.K.: Conceptualization, methodology, investigation, writing—original draft. M.W.: Data curation, methodology, investigation. R.A.: Conceptualization, visualization, investigation, supervision, writing—reviewing and editing, funding acquisition.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Klubthawee, N., Wongchai, M. & Aunpad, R. The bactericidal and antibiofilm effects of a lysine-substituted hybrid peptide, CM-10K14K, on biofilm-forming Staphylococcus epidermidis. Sci Rep 13, 22262 (2023). https://doi.org/10.1038/s41598-023-49302-y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-023-49302-y
- Springer Nature Limited