Abstract
The modeling of charge transport in organic semiconductors usually relies on the treatment of molecular vibrations by assuming a certain limiting case for all vibration modes, such as the dynamic limit in polaron theory or the quasi-static limit in transient localization theory. These opposite limits are each suitable for only a subset of modes. Here, we present a model that combines these different approaches. It is based on a separation of the vibrational spectrum and a quantum-mechanical treatment in which the slow modes generate a disorder landscape, while the fast modes generate polaron band narrowing. We apply the combined method to 20 organic crystals, including prototypical acenes, thiophenes, benzothiophenes, and their derivatives. Their mobilities span several orders of magnitude and we find a close agreement to the experimental mobilities. Further analysis reveals clear correlations to simple mobility predictors and a combination of them can be used to identify high-mobility materials.
Similar content being viewed by others
Introduction
Organic semiconductors are used in various electronic devices, including organic field effect transistors1,2,3,4, organic photovoltaics5,6,7, and organic light emitting diodes8,9,10. Many applications rely on charge-transport processes and the charge-carrier mobility is an important property affecting the device performance. This is a strong motivation to improve the understanding of charge transport in organic semiconductors and a variety of methods have been suggested11,12,13,14,15,16,17,18,19,20,21,22,23,24. The modeling of charge transport, however, remains challenging, because the electrons couple strongly to the molecular vibrations. This coupling, known as electron-phonon coupling (EPC), prevents a straightforward analytical treatment of the electronic and vibrational degrees of freedom. Recent improvements in computational methods allow to model the charge transport numerically while propagating vibrations semiclassically22,25. Although these numerical approaches are generally promising, performing them fully based on ab initio simulations is still expensive for the screening of new materials. Therefore, the number of materials that can be studied and compared simultaneously remain limited. To tackle the complexity, the exploitation of analytical limits can improve the computational efficiency and, more importantly, may push the microscopic understanding of the carrier mobility forward. One of the first classes of analytical models that go beyond a semi-classical treatment of nuclei are polaron theories11,13,26, which describe the formation of the polaron, a charge carrier accompanied by dynamic molecular vibrations. However, the polaronic character is assumed to be weak for the slow, thermally populated vibrations27,28, which often show large EPC. Transient localization theory, initially developed by Troisi, Fratini, Ciuchi, Mayou, and colleages21,29,30, on the other hand focusses on these strongly-coupling low-frequency vibrations, which tend to localize the electronic wave packets in an electronic disorder landscape that is static at small times. At longer times, however, the inevitable motion of the low-frequency modes sets in, presumably lifting this effect – hence the name transient localization (TL). The quasi-static approximation inherent to TL is successful because a strong contribution to the EPC stems from thermally activated low-frequency vibrations. Still, the fast intramolecular high-frequency vibrations, which must not be modeled quasi-statically but generate coherent polaron dressing, also show a large EPC and should not be neglected, which eventually implies a separation of the vibrational mode spectrum31,32,33.
Here, we present an approach to simulate coherent electronic transport, which combines the quasi-static treatment of slow modes in the TL approach with the polaronic treatment of the high-frequency vibrations from polaron approaches (cf. Fig. 1a for a prototypical vibrational spectrum of an OSC material). The EPC of slow low-frequency vibrations generates quasi-static disorder (Fig. 1b, blue), while the EPC of fast high-frequency vibrations generates polaron narrowing (orange). Using the combined model, we calculate the hole mobilities via simulations for extended 3D system utilizing linear-scaling quantum transport methods34,35. To assess the predictive capability of the approach statistically, it is applied to 20 prototypical organic crystals with known experimental mobilities that span two orders of magnitude. We find a close agreement between the mobilities obtained with this approach and the experimental mobility trend. Finally, the validity of simplified mobility predictors like reorganization energies, transfer integrals, and dimensionality is analyzed and a combination of easy-to-compute predictors for fast mobility estimates is found, which is superior to their single predictor components and can be useful in machine-learning schemes to find high-mobility organic semiconductors.
a Mode spectrum of a DNTT crystal. The separating energy (the maximum transfer integral \(\varepsilon _{MN}^{\max }\)) is highlighted as red vertical bar. Modes with lower energy are treated in the quasi-static limit (blue), modes with larger energy in the polaronic limit (orange). As a reference, twice the thermal energy 2kBT at room temperature is highlighted as dashed red bar. b The quasi-static treatment generates static disorder in the transfer integrals εMN and onsite energies εMN. The polaronic treatment generates a narrowing of the electronic transfer integrals εMN.
Results and discussion
Combination of the quasi-static and polaronic treatment
Organic molecules and their crystals show a rich vibrational spectrum. In Fig. 1a, this is illustrated for a DNTT crystal built by a supercell cell with 8 molecules. The vibration frequencies are spread over two orders of magnitude, ranging from ~10 cm−1 to above 1000 cm−1. To account for this wide range, the slow modes are modeled within the quasi-static limit of TL (blue) and enter via their instantaneous configuration, while the faster high-frequency modes enter in the dynamic polaronic limit (yellow), integrating all configurations. Both treatments influence the electronic energies, but in a different fashion as we will elucidate in the following.
The starting point for the calculations and mode separations is the Holstein-Peierls-Hamiltonian11,36, which includes the electronic, vibrational, and EPC contributions
in a mixed representation with the electronic operators aM (\(a_M^{\dagger}\)), the onsite-energies εMM and transfer integrals εMN. The phonon operators bQ (\(b_Q^{\dagger}\)) are used with Q = (λ,q) and λ being the mode index and q the wave vector. The coupling between the phonons and electrons is described by the linear EPC constants \(g_{MN}^Q\), including local coupling (coupling to the onsite-energies) for M = N and nonlocal coupling (coupling to the transfer integrals) for M ≠ N. To calculate the charge-carrier mobility by an electronic quantum-transport approach, the Holstein-Peierls-Hamiltonian in Eq. (1) will be reduced to a completely electronic Hamiltonian. To this end, the impact of the phonon contributions to the electronic energies in the quasi-static and polaronic limit will be analytically pre-evaluated. We briefly summarize the essential steps of the derivation here, while more details can be found in Supplementary Note 1. The slow modes are assumed to generate a (quasi-) static disorder ΔεMN in the electronic energies due to their instantaneously frozen configuration31. With a Gaussian distribution of the disordered energies εMN + ΔεMN around εMN, the variance \(\sigma _{MN}^2\) of ΔεMN can be evaluated to37
with the Bose-Einstein distribution \(N_Q = \left( {e^{{\hslash}\omega _Q/k_{{{\mathrm{B}}}}T} - 1} \right)^{ - 1}\), the Boltzmann constant kB, and absolute temperature T.
In contrast to the slow modes, the fast modes are treated here by a Lang-Firsov-transformation13,38 of Eq. (1). As a result, the transfer integrals εMN are reduced by a narrowing factor fnar and the onsite-energies εMM are shifted by the polaron binding (relaxation) energy \(E_{{{{\mathrm{pol}}}}} = \mathop {\sum}\nolimits_Q^{{{{\mathrm{fast}}}}} {{\hslash}\omega _Q\left| {g_{MM}^Q} \right|^2}\)as 13
In case of equal molecules at each site M (\(g_{MM}^Q = g_{NN}^Q\) for all M and N), Epol is an energetic shift that applies to all sites and can be disregarded.
By combining Eq. (3) and Eq. (2) and Eq. (1), the Holstein-Peierls-Hamiltonian is reduced to the effective electronic Hamiltonian:
and ΔεMN follows a Gaussian distribution according to Eq. (2). Although in real systems there is no sharp transition between slow and fast modes, the separation has to be numerically performed with a distinct cut-off criterion. Here, we chose the maximum between twice the thermal energy32 (red dotted bar in Fig. 1) and the maximum transfer integral \(\varepsilon _{MN}^{{{{\mathrm{max}}}}}\) (red bar in Fig. 1) as a separation criterion, i.e.,
This simultaneously ensures that the thermally activated low-frequency vibrations are treated quasi-statically in the case of small transfer integrals, while only the fast high-frequency vibrations are treated in the polaron limit in the case of large transfer integrals.
Calculation of the charge-carrier mobility
The calculation of the charge-carrier mobility is based on linear-response theory within the Kubo formalism39. This can be evaluated in the presence of disorder \(\bar \varepsilon _{MN}\) (cf. Eq. (4)). Since the disorder landscape changes on the effective time-scale of the slow quasi-static modes τslow, this short-time behavior is lifted at longer times than τslow, which thus acts as a decoherence time. With this in mind, the TL mobility is calculated as30
\(L_{{{{\mathrm{loc}}}}}^2 = \frac{1}{{\tau _{{{{\mathrm{slow}}}}}}}{\int}_0^\infty {e^{ - \frac{t}{{\tau _{{{{\mathrm{slow}}}}}}}}\langle\Delta {X^2}\left( t \right)\rangle {d}t}\) is the squared localization length – it measures the average spread of the wave-packet up to the time τslow and is derived from the thermally averaged, time-resolved quantum spread \(\langle{{\Delta}X^2\left( t \right)\rangle }\). While there exist simplified versions to compute Lloc for 2D systems by a direct diagonalization40 of the disordered Hamiltonian similar to Eq. (4), we calculate the localization length by calculating the time-resolved quantum spread \(\langle{{\Delta}X^2\left( t \right)\rangle }\) via propagation in real-space 3D systems. In this way, we include the effect of possible 3D percolation pathways in the sample. The thermally averaged quantum spread is calculated as
with the Fermi-Dirac distribution \(f\left( E \right) = 1/\left( {e^{\left( {E - \zeta } \right)/k_{{{\mathrm{B}}}}T} + 1} \right)\) and the charge-carrier concentration \(N_0 = {\int} {dE\,f\left( E \right)DOS(E)}\). The chemical potential ζ is chosen such that the charge-carrier concentration equals N0 = 0.001 for all materials. More details on the calculation of the time- and energy-resolved quantum spread ΔX2(E,t) can be found in the methods section. With the chosen system size of approximately 12 million sites, a single transport simulation requires only about 2500 CPUh and can be readily performed in parallel on any computer cluster.
Transport parameters
Regarding EPC parameters, we distinguish between three types of EPC, which are visualized in Fig. 2 for DNTT and briefly introduced here. There are (i) the local terms \(g_{MM}^Q\) (Fig. 2a). It is the coupling of molecular vibrations to the onsite-energy of a single molecule M (top). The local coupling covers the full range of vibration frequencies (bottom), necessitating a separation into quasi-static contributions (blue) and polaronic contributions (orange). The resulting polaronic narrowing factor is, in average over the studied materials, \(\overline f _{{{{\mathrm{nar}}}}} = 0.6\). (ii) The nonlocal EPC \(g_{MN}^Q\) (Fig. 2b) is the coupling to the transfer integrals mediating between sites M and N (top). It is clearly dominated by low-frequency vibrations, leading to a quasi-static disorder landscape in the transfer integrals21,40. (iii) The environmental coupling \(g_{MM}^{Q,CF}\) (Fig. 2c) is the coupling of the crystal vibrations to the electrostatic interaction energy ECF between the charge carrier at site M and the crystal field of the surrounding molecules. Similar to the nonlocal coupling it is dominated by low-frequency vibrations, generating quasi-static disorder in the onsite energies. The environmental coupling is found to contribute only little to the disorder compared to the nonlocal coupling and is included for completeness. Details on the implementation of the three types of couplings and corresponding first principles calculations of the parameters can be found in the methods section. We note here that the calculation of the nonlocal EPC is the step that requires the largest computation time of the approach (~10,000CPUh per material in dependence on the molecular size), but has the advantage of using quantum-chemical methods that are transferable to new materials.
Top: three types of EPC implemented in this approach: a local coupling to the onsite energies, b nonlocal coupling to the transfer integrals between two molecules and c environmental coupling to the electrostatic crystal field. Bottom: mode-resolved squared EPC constant g2 for the three types of coupling of the exemplary molecule DNTT. The energy scale of transport \(\varepsilon _{MN}^{\max }\) is indicated as red vertical bar. The modes that are treated quasi-statically are highlighted in blue, while the ones that are treated with the polaron approach are highlighted in orange. Twice the thermal energy 2kBT at room temperature, which is the separating energy for small transfer integrals, is highlighted as dashed red bar.
The timescale τslow in Eq. (6) is a crucial parameter defining the “lifetime” of the quasi-static disorder landscape. It is usually set to the inverse of the circular frequency \(\tau _{{{{\mathrm{slow}}}}} = \omega _{{{{\mathrm{slow}}}}}^{ - 1}\) of the dominating vibrations, which can be, for example, extracted from molecular dynamics (MD) simulations21. To avoid costly ab initio MD simulations, we follow a different route and extract τslow from the mode-resolved disorder Eq. (2) based on the mode-resolved EPC. The disorder landscape is defined by both the disorder in the onsite-energies (with standard deviation \(\sigma _{MM}^2\)), caused by local and environmental EPC, and disorder in the transfer integrals (with standard deviation \(\sigma _{MN}^2\)), caused by nonlocal EPC. We thus extract ωslow from the collective disorder strength using a weighted average (see methods section). The resulting values of τslow for the 20 crystals range from 60 fs to 270 fs and are summarized in Table 1. The average value over all compounds is about \(\bar \tau _{{{{\mathrm{slow}}}}} = 170\,{{{\mathrm{fs}}}}\), being of the same order of magnitude to the values obtained from MD simulations21,22. We note that their calculation via mode-resolved EPC allows the calculation of the ab initio parameters for new materials for which no force fields are available.
Studied materials and transport simulations
We assess the applicability of the combined approach by calculating the charge-carrier mobility at room temperature (T = 300K) using a set of 20 different organic semiconductor crystals and comparing them to known experimental mobilities. The molecular structures of the studied molecules are shown in Fig. 3. They include different classes of typical organic semiconductors, such as acenes, thiophenes, benzothiophenes, and some of their functionalized derivatives. The materials cover a broad range of ab initio parameters and experimental mobilities, ranging from μPMSB = 0.17 cm2/Vs for PMSB41 to μrubrene = 15.3 cm2/Vs for rubrene42. The mobilities, as well as ab initio parameters are listed in Table 1.
They were chosen to cover a wide range of experimental mobilities. For the TTF molecule, we studied two known crystal structures. References to the studied crystal structures can be found in Supplementary Table 2.
While Eq. (6) enables the calculation of the mobility in any possible direction, here we focus on the maximum intrinsic mobility in transport direction. Figure 4a shows the computed mobilities μsim in comparison to the experimental mobilities μexp. The black dotted diagonal line is a guide for the eye, representing the ideal case μexp = μsim. We find that simulated and experimental mobilities correlate closely. This means that the simulation approach allows identifying low- and high- mobility organic crystals, which suggests that the approach could be used to estimate the charge-carrier mobility of new, unknown materials. We further quantify the correlation between simulation and experiment by calculating the ratio of both \(\mu _{{{{\mathrm{sim}}}}}^i/\mu _{{{{\mathrm{exp}}}}}^i\) for the 20 studied materials, and analyze its average \({\Sigma} = \exp ( {\frac{1}{n}\mathop {\sum}\nolimits_i^n {\ln ( {\mu _{{{{\mathrm{sim}}}}}^i/\mu _{\exp }^i})} })\) and the corresponding spread \({\Delta} = \exp ( {\frac{1}{n}\mathop {\sum}\nolimits_i^n {| {\ln ( {\mu _{{{{\mathrm{sim}}}}}^i/\mu _{\exp }^i} )} |} })\). We obtain ∑ = 0.98 and Δ = 1.54. That is, in average the simulated mobilities deviate by a factor of 1.54 (over- or underestimation) from the experimental mobilities, rendering the approach predictive.
a Highest mobilities simulated in transport direction with the combined approach versus experimental mobilities. The black dotted line represents the case in which both coincide. b Experimental mobility versus the simulated localization length nloc = Lloc/dmol ≤ in transport direction in units of molecular center-of-mass distances dmol. The black dotted line shows the dependency according to TL (Eq. (8)) using the stated averaged \(\bar \tau _{{{{\mathrm{slow}}}}}\) and \(\bar d_{{{{\mathrm{mol}}}}}\) values. c Simulated mobility using the original signs of the transfer integrals (x-axis) versus the simulated mobility by using all positive signs for the transfer integrals (y-axis). Materials that show a large increase of the mobility (of in average a factor of 2.3) due to the sign change are highlighted in red.
Interestingly, we find that the present methodology, which is based on the coherent quantum diffusion, also yields good results for the low-mobility materials with μ ≤ 1 cm2/Vs, although these are more likely in the hopping-transport regime that is driven by molecular vibrations. To explain this observation, we study the localization lengths Lloc from Eq. (6). For convenience, we use the material dependent length unit dmol, which is the center-of-mass distance between neighboring molecules with the largest transfer integral (see Table 1 for the numerical values). We define \(n_{{{{\mathrm{loc}}}}} = L_{{{{\mathrm{loc}}}}}/d_{{{{\mathrm{mol}}}}}\) as a measure for the number of molecules the wave-packet can approximately reach in transport direction during the time τslow. In Fig. 4b we plot this localization length nloc against the experimental mobility for all 20 materials. As intuitively expected, the higher the mobility, the larger is the number of molecules the wave-packet delocalizes over22. As a guide for the eye, we also show the analytical dependency, which is obtained by resolving Eq. (6) for Lloc and use an averaged molecular distance of \(\bar d_{{{{\mathrm{mol}}}}}\) = 5.5 Å and averaged relaxation time \(\bar \tau _{{{{\mathrm{slow}}}}} = 170\,{{{\mathrm{fs}}}}\):
For materials with mobilities below 1 cm2/Vs, nloc is about one to two molecular distances. Thus, in this regime the TL approach can be interpreted to describe a hop of a localized wave-packet from one molecule to the other during the time τslow in analogy to hopping-transport simulations31. It is worth mentioning that, in contrast to hopping approaches, this observed behavior is not an a priori assumption but arises from the inability of the wave-packet to delocalize further than one neighboring molecule in transport direction due to strong disorder potentials. When focusing on the opposite limit, i.e. if one extrapolates Eq. (8) to estimate when a mobility of μ = 100 cm2/Vs could be reached, one would obtain a required delocalization to nloc = 17.
A key proposal in the TL model is the dependency of Lloc (and the resulting charge-carrier mobility μsim) on the relative signs of the transfer integrals that occur between a molecule and its neighbors,21 which is due to changes in the band structure when the sign of the transfer integrals change. This effect is explained in detail in Supplementary Note 2. For holes, a positive product of the signs of non-equivalent neighbors within the high-mobility plane would favor transport, whereas a negative product impedes transport.
To study this effect, we compare the simulated mobility using the original DFT-simulated signs (see methods section) with mobilities using all positive transfer integrals (APT) \(\mu _{{{{\mathrm{sim}}}}}^{{{{\mathrm{APT}}}}}\) for all 20 materials in Fig. 4c (values in Table 1). For most of the materials, the change of the signs has only a minor effect (green circles). The reasons are either already existing ideal sign combinations (e.g. C10-DNBDT and C10-DNTT) or a strong tendency for 1D transport (e.g. BB-PTA and PMSB) in which other transfer integrals but the largest are of minor importance. For seven materials, we see a significant increase in the mobility by an average factor of 2.3 (orange circles). These are indeed materials that show only one transfer integral with negative sign within the high-mobility plane, yielding a negative sign product (e.g. for most of the acenes, DNTT, DBTDT). Consequently, the relative signs of the transfer integrals can have a significant impact on the electronic structure and transport and should be considered when using transfer integrals as a material predictor.
Due to the variety of studied structures, it is also possible to analyze the correlation between simplified predictors and the simulated mobility. The reduction of the complexity of the transport simulation to predictors can improve the understanding of which parameters influence the mobility most. This knowledge is helpful as a guidance for design principles or can be used as a fast measure of transport capabilities in machine learning in the future, where a large number of structures have to be screened efficiently43,44. To analyze for possible dependencies, we graphically compare the dependency of the simulated mobility on different predictors in Fig. 5 and calculate the correlation coefficients r. Since the mobilities cover several orders of magnitude, while the predictors cover only one, we calculate the correlation to both the logarithmized mobility \(\ln \left( \mu \right) \to r_{\log }\) and original mobility \(\mu \to r_{{{{\mathrm{lin}}}}}\). We further present a linear fit of the predictor to In(μ) as black dashed line, which corresponds to the predicted mobility using solely this predictor and assuming an exponential dependency. The corresponding fit parameters can be found in Supplementary Note 3. Finally, the average spread around the prediction Δ (see above for the definition) is also shown. We first study obvious descriptors, like the transfer integral \(\varepsilon _{MN}^{{{{\mathrm{max}}}}}\) and its disorder, which has been studied before by Troisi and coworkers32, and then proceed to more complex descriptors to improve the predictability.
We present the correlation coefficient with respect to the logarithmized mobility (rlog) and the original data (rlin). The black dotted line is a linear fit between the studied material parameter and logarithmized mobility, while Δ is the average deviation from this fit. The fit details and fit parameters can be found in Supplementary Note 3. a shows the dependency of the simulated mobility on the maximum transfer integral \(\varepsilon _{MN}^{\max }\). Here, a second fit is performed by hypothetically neglecting two outliers (gray half circle), leading to the correlation shown in gray. The further studied parameters are b the ratio between the maximum transfer integral \(\varepsilon _{MN}^{\max }\) and its nonlocal disorder σMN, c the molecular center-of-mass distance in the direction of the largest transfer integral dmol, d the ratio between the reorganization energy Λ and transfer integral \(\varepsilon _{MN}^{\max }\), e the ratio between the local disorder \(\sigma _{MM}^2\) and transfer integral \(\varepsilon _{MN}^{\max }\), and f the dimensionality δdim. The last plots show combinations of the previous predictors: the combined predictor \(\zeta ^I\) in g, and fast-to-calculate combined predictor \(\zeta ^{II}\) in h.
A first predictor is the maximum transfer integral \(\varepsilon _{MN}^{{{{\mathrm{max}}}}}\) enabling electronic transport. As suggested by early hopping approaches, where the hopping rate is proportional to \(\varepsilon _{MN}^2\), one might expect a distinct positive correlation between the simulated mobility and \(\varepsilon _{MN}^{{{{\mathrm{max}}}}}\). As shown in Fig. 5a, in contrast to the expectation, we observe a very weak correlation with rlin = 0.0532. When hypothetically excluding the two most outlying data points of the molecules BB-PTA and TTF-α (half gray circles), which show large transfer integrals (\(\varepsilon _{MN}^{{{{\mathrm{max}}}}} \,>\, 100\,{{{\mathrm{meV}}}}\)) but small mobilities (μ ≤ 1 cm2/Vs), we can indeed find a much stronger correlation of rlog = 0.52. Our analysis shows that, besides large transfer integrals, these two materials also show exceptionally large nonlocal and local disorders, which suggests that the mere transfer integral is unsuitable as a general predictor for the mobility. Therefore, we analyze a related one, namely the ratio between the maximum transfer integral \(\varepsilon _{MN}^{{{{\mathrm{max}}}}}\) and the disorder σMN in the same (cf. Fig. 5b). We indeed find a correlation of rlin = 0.62, while for the nonlocal disorder σMN alone we find a weaker correlation of \(r_{{{{\mathrm{log}}}}} = - 0.41\) (not graphically shown). The reason that the combination of both parameters yields a good predictor is quite intuitive: the larger the transfer integral compared to the disorder, the better is the delocalization of the states and the larger are the localization length Lloc and the mobility.
A quantity that is directly connected to the localization length Lloc is the molecular center-of-mass distance dmol. If all other parameters are constant, a larger dmol directly increases Lloc since the charge carriers travel larger distances between molecules. In Fig. 5c, we compare the simulated mobility with dmol in the direction of the largest transfer integral. Indeed, a good correlation of \(r_{{{{\mathrm{log}}}}} = 0.64\) can be found. This suggests that the molecular center-of-mass distance in transport direction is a good predictor for the mobility and should be optimized experimentally, e.g. via functionalization. A prominent example is rubrene where the large center-of-mass distance (dmol = 7.2 Å) is caused by a special crystal packing that is induced by the functionalization of tetracene with phenyl side groups.
A popular transport parameter is the single-molecule reorganization energy Λ, which is a measure of the local EPC. It can be computed easily and enters into fast mobility estimations like Marcus theory45,46. In the present approach, the reorganization energy does not enter the mobility calculation, still we can check for possible correlations. The ratio \({\Lambda}/\varepsilon _{MN}^{\max }\) is compared to the carrier mobility in Fig. 5d and we observe a correlation with \(r_{\log } = - 0.65\). This is further improved in case of the ratio between the local disorder strength \(\sigma _{MM}^2\) and the maximum transfer integral \(\varepsilon _{MN}^{\max }\) (shown in Fig. 5e), exhibiting a strong correlation of \(r_{\log } = - 0.81\). We find the physical reason for this strong correlation of this quantity in the energetic distribution of the band-edge states. When the density-of-states approximately exhibits an exponential Urbach tail47, the predictor \(\sigma _{MM}^2/\varepsilon _{MN}^{\max }\) is closely related to the corresponding exponential steepness parameter, i.e. the Urbach Energy EU48. A steeper exponential tail (low values of \(\sigma _{MM}^2/\varepsilon _{MN}^{\max }\)) means that the Fermi energy is closer to the band center, causing an increased contribution of delocalized states and thus larger charge-carrier mobilities.
The next predictor in our analysis is the dimensionality of transport. Materials showing 1D transport characteristics (e.g. by having only one set of equivalent neighbors with large transfer integrals) are not good transport materials, since they are prone to localization in case of static disorder due to limited percolation pathways21,32. Here, we measure the dimensionality of transport δdim of the studied systems by analyzing the directional distribution of all transfer integrals to all nearest-neighbor molecules of a center molecule. We restricted ourselves to the distribution of transfer integrals within the high-mobility 2D plane (details on the calculation can be found in the methods section). Thus, δdim can take on values between 1 (1D transport, i.e. only one large transfer integral in one direction) and 2 (2D transport, i.e. equally large transfer integrals within a 2D plane). Figure 5f shows the dependency of the simulated mobility on δdim. A correlation of rlog = 0.43 is found, which is weaker than for the previous predictors. Still the dimensionality is worth considering when assessing the transport capability of new materials.
In a final analysis, we study if an even better correlation can be found by combining multiple predictors that correlate well with the simulated mobility. The first combination (shown in Fig. 5g) is \(\sigma _{MM}^2/\varepsilon _{MN}^{\max }\) (the best predictor in Fig. 5e) and the molecular center-of-mass distance dmol (the second-best predictor that does not depend on the local coupling, cf. Fig. 5c). Both predictors are combined via a product: \(\zeta ^I = \sigma _{MM}^2/\left( {\varepsilon _{MN}^{\max } \ast d_{{{{\mathrm{mol}}}}}} \right)\). This combination shows a slightly higher correlation of \(r_{\log } = - 0.84\) compared to the sole predictor \(\sigma _{MM}^2/\varepsilon _{MN}^{\max }\). The second combination focuses on fast-to-calculate, but less reliable predictors. We chose the ratio between reorganization energy and transfer integral \({\Lambda}/\varepsilon _{MN}^{\max }\) (Fig. 5d), the center-of-mass distance dmol (Fig. 5c), and the dimensionality δdim (Fig. 5f). Here, we obtained the best result by combining them via the geometric average \(\zeta ^{II} = \root {3} \of {{\varepsilon _{MN}^{\max } \ast d_{{{{\mathrm{mol}}}}} \ast \delta _{\dim }/{\Lambda}}}\), which is shown in Fig. 5h. Indeed, the correlation of the combined predictor \(\zeta ^{II}\) (\(r_{\log } = 0.81\)) is better than the one of the individual terms. We thus suggest it as an easy-to-compute predictor for the mobility, which is more reliable than its sole components like the reorganization energy Λ or transfer integral \(\varepsilon _{MN}^{\max }\).
The values of all studied predictors (Table 1) can be used to understand differences between the simulated mobilities of the studied materials, whereby we here pick out the most clear-cut cases for the discussion. C10-DNBDT and C10-DNTT for example show the highest simulated mobilities with medium transfer integrals (50–70 meV), whereas BB-PTA shows one of the lowest simulated mobilities despite having the largest transfer integral (180 meV). Therefore, the bare value of the transfer integral alone is no reliable predictor for the mobility. This weak correlation indicates that other factors, like the vibrations and EPC, are very important. For example, more relevant is the ratio between the transfer integral and the electronic disorder due to EPC. This is high for C10-DNBDT and C10-DNTT but low for BB-PTA, leading to stronger localization effects for the latter. For BB-PTA this effect is further enhanced due to the 1D-like transport channel induced by the crystal packing, where there are large transfer integrals to only two nearest-neighbor molecules. This 1D channel makes BB-PTA prone to localization in analogy to the concept of conventional Anderson localization in disordered systems due to the lack of additional percolation pathways49. In contrast, C10-DNBDT and C10-DNTT have 2D high-mobility planes which are enforced by their core-alkyl-side-chain molecular structure, which opens up additional percolation pathways and makes them less susceptible to localization. Finally, the intermolecular distance of BB-PTA is by a factor of 1.5 smaller than for C10-DNBDT and C10-DNTT, directly reducing the distance the charge carriers can diffuse over. All these effects sum up in the simulation, leading to mobilities of BB-PTA that are factor of 50 smaller than for C10-DNBDT and C10-DNTT despite more-than-doubled transfer integrals. On top, the latter two molecules show ideal sign combinations of the transfer integrals (all positive transfer integrals), which maximizes the total bandwidth and producing the highest simulated mobilities.
In conclusion, we presented a framework to calculate the charge-carrier mobility of organic semiconductors by combining the quasi-static treatment of slow molecular vibrations (transient localization model) with the treatment of fast molecular vibrations from polaron theory. It is required, since the wide vibrational spectrum of organic molecules does not allow for a collective description of all modes in a single analytical treatment. The agreement between simulated and experimental mobilities for the full range of studied materials (quantified to an expected ratio of 1.54) suggests a good predictability for novel compounds. Using purely quantum-chemical methods to calculate the material parameters, the total computational expense is quite modest with about 15,000CPUh per material, where most of the computation time is required for the calculation of the nonlocal EPC. All simulations can be performed in parallel on high-performance computing clusters.
Finally, the correlation between the simulated mobility and simple predictors potentially allows estimating μ without performing all ab initio calculations. Since multiple parameters enter the transport simulation, there are also several predictors that correlate with the mobility. While the maximum transfer integral \(\varepsilon _{MN}^{{{{\mathrm{max}}}}}\) was shown to fail as a predictor for certain materials, there are several alternatives that work well such as the dimensionality of transport δdim or the center-of-mass distance to the neighboring molecule with the largest transfer integral dmol. The tightest correlations among all predictors showed r values between 0.64 and 0.81. The best predictor was the ratio \(\sigma _{MM}^2/\varepsilon _{MN}^{{{{\mathrm{max}}}}}\) between the local disorder strength and largest transfer integral, which requires only low computational resources due the absence of nonlocal EPC. To further increase the predictability, not a single but a set of predictors can be used. From our analysis, we suggest the geometric average of an easy-to-calculate set of predictors: (i) the ratio between reorganization energy Λ and the maximum transfer integral \(\varepsilon _{MN}^{{{{\mathrm{max}}}}}\) (ii) the dimensionality δdim and (iii) the center-of-mass distance dmol. While these predictors cannot reach the predictability of the full mobility simulations with ab initio parameters, they are fast to calculate and can be applied to estimate the mobility for a much larger set of systems in the future.
Methods
Transfer integrals
The transfer integrals were calculated within the fragment-orbital approach50,51 for molecular dimer pairs in a 3D nearest-neighbor shell of a given central molecule. Including Löwdin orthogonalization52, they are defined as
The matrix F, overlap matrix S and molecular Kohn-Sham orbitals ϕM (corresponding to the highest occupied molecular HOMO orbital in case of hole transport) were calculated with density functional theory (DFT). To this end, the B3LYP exchange-correlation functional53,54 and 6–311 G** basis set55,56 were used within the Gaussian 16 program package57.
The signs of the transfer integrals were obtained via comparison to the signs between maximally localized Wannier functions58 that were obtained with the Wannier90 code59,60 in combination with the VASP package61,62 using a plane-wave basis set. The calculations were based on the projector augmented-wave method63,64 and PBE functional65,66. Depending on the number of molecules in the unit cell, two or four valence bands were used for the wannierization to obtain the sign.
Vibrational analysis
The local coupling was calculated with DFT using the vibrational modes of a single, isolated gas-phase molecule. The mode energy and displacement patterns were obtained using the normal mode analysis as implemented in Gaussian 1657 using the B3LYP exchange-correlation functional53,54 and 6–311 G** basis set55,56.
The nonlocal and environmental coupling is based on the vibrational crystal modes. Due to the increased system size, the calculation was performed with density functional tight binding (DFTB)67 instead of DFT. It has been shown that, while DFTB is not perfectly suited for the calculation of electronic properties, it describes vibrational properties sufficiently well68. The normal mode analysis was performed for unit cells consisting of, in general, 8 molecules and periodic boundary conditions. The specific choice of the supercell size ensures, that the supercell includes one of the two equivalent nearest neighbor molecules of the 3D shell for which we calculated the transfer integrals. Thus, we include symmetric (q = 0, phase between adjacent molecules is eiqa = 1) and anti-symmetric (\(q = \frac{\pi }{a}\), phase between adjacent molecules is eiqa = −1) vibrations. More q points could in principle be sampled by further increasing the unit cell size68,69, but drastically increases the computational load.
For four molecules (rubrene, C10-DNBDT, C10-DNTT, and TIPS-pentacene) we included only 4 molecules in the unit cell due to the large molecular and unit cell size. We included the nearest-neighbor molecules, corresponding to two sampled q-points, within the high-mobility plane. Consequently, in the third low-mobility direction, we included only the symmetric vibrations (q = 0, eiqa = 1).
The crystal mode analysis was performed with third order DFTB70 implemented in the DFTB+ program package70,71 using the 3ob parameter sets70. For TIPS-Pentacene, the pbc72 parameter sets, which include silicon, were used. Additionally, Grimme’s dispersion correction GD373 was included in every calculation.
To compensate numerical errors in the mode frequencies occurring during normal mode analysis, which are most impactful for the low-frequency modes, the frequencies obtained from the normal analysis were re-computed. This is done by calculating the second derivative of the DFTB crystal energy \(E_{{{{\mathrm{DFTB}}}}}^{{{{\mathrm{Crystal}}}}}\left( {X_Q} \right)\) in dependence on the deflection XQ. The new frequencies are obtained as:
If negative frequencies were obtained for (non-translational) crystal modes, the crystal was shuffled according to these modes, followed by a second relaxation and frequency calculation. In rare cases, very small but non-negative mode frequencies (<5 cm−1) remained. These modes fully contributed to the disorder potential in Eq. (2) but were suppressed in the calculation of τslow in Eq. (15).
Calculation of electron–phonon coupling
The local coupling \(g_{MM}^Q\), nonlocal coupling \(g_{MN}^Q\) and environmental coupling \(g_{MM}^{Q,CF}\), collectively notated as GQ, were calculated using the deflection of the normal modes XQ and mode energies ωQ according to:
The derivative is calculated in the frozen-phonon approach74 and the energy E in Eq. (11) stands for the onsite energy εM (local coupling), the transfer integral εMN (nonlocal coupling) and the electrostatic interaction energy of the charge carrier with the surrounding molecules \(E_{CF}^M\). The calculations of the respective energies are performed in real-space to ensure scalability to larger molecules, since the required DFT simulations can then be performed for smaller subsystems.
Onsite energies and local coupling
The onsite energies, corresponding to the binding energy of the charge carrier in the HOMO orbital in case of hole transport, is calculated as75:
where \(E_{{{{\mathrm{DFT}}}}}^ {0/+}\) is the total DFT energy for the neutral or positively charged molecule, respectively. The energies are calculated with the B3LYP functional53,54 and the 6–311 G** basis set55,56 in Gaussian 1657.
In gas phase, the molecules TTF, DT-TTF, and HM-TTF show very large local coupling constants for low-frequency bending modes (and consequently large reorganization energies), which are not present to that extent in a crystalline environment. To account for the constraints within the crystal, we calculated the reorganization energy in a cluster environment using the well-established 4-point method76. The cluster included all nearest-neighbor molecules of a central molecule that is allowed to relax. The atomic positions of the neighbor molecules were kept constant, while the charging states of the central molecule were controlled via charge constraints. These calculations were performed with the NWchem package77 on the level of theory presented above. The mode-resolved electron-phonon couplings of these molecules were scaled down, so that twice the total polaron binding energy (relaxation energy) \(E_{{{{\mathrm{pol}}}}} = \mathop {\sum}\nolimits_Q {{\hslash}\omega _Q\left| {g_{MM}^Q} \right|} ^2\) is equal to the reorganization energy obtained within the cluster environment.
Nonlocal coupling
The transfer integrals εMN used to calculate the nonlocal coupling according to Eq. (11) have been calculated similar to Eq. (9), however the DFT calculations were performed using the smaller 6–31 G* basis set instead of 6–311 G** to reduce the computational load. Further, we used a method proposed by Landi et al.78 to calculate the derivatives \(\frac{{\partial \varepsilon _{MN}\left( {X_Q} \right)}}{{\partial X_Q}}\) more efficiently. For a unit cell consisting of \(N = n_{\frac{{{{{\mathrm{mol}}}}}}{{{{{\mathrm{unit}}}}}}} \ast n_{\frac{{{{{\mathrm{atom}}}}}}{{{{{\mathrm{mol}}}}}}}\) there are 3N normal modes, for which the derivative in Eq. (11) has to be performed. However, only \(2^\ast n_{\frac{{{{{\mathrm{atom}}}}}}{{{{{\mathrm{mol}}}}}}}\) atoms contribute to the transfer integral εMN. Thus, the derivative with respect to the full displacement pattern is replaced by a derivative with respect to only the displacement s of the atoms l in direction α contributing to the transfer integral weighted with the displacement pattern \(e_{{{{\mathrm{Q}}}}}^ {\alpha}\). of mode Q:
As a consequence, only \(3 \ast 2 \ast n_{\frac{{{{{\mathrm{atom}}}}}}{{{{{\mathrm{mol}}}}}}}\) derivatives have to be computed. In our case, this treatment saves computational time of a factor of \({n_{\frac{{{{{\mathrm{mol}}}}}}{{{{{\mathrm{unit}}}}}}}}/2 = 4\).
Electrostatic interaction energy and environmental coupling
The final type of electron-phonon coupling is the environmental coupling arising due to changes in the electrostatic interaction energy between the charge carrier and the crystal field generated by the surrounding molecules ECF. Although the surrounding molecules are neutral, the interaction energy is nonzero due to non-vanishing quadrupole moments, and, for some molecules, non-vanishing dipole moments. For the calculation, the charge carrier is approximately localized on a single molecule M76. The interaction energy of the electronic charge distribution is modeled by atomic point charges q75,76 obtained by an electrostatic potential fit (ESP)79,80 and reads
The sum over i goes over all atomic point charges of the excess charge carrier \({{{\mathrm{{\Delta}}}}}q_i = q_i^ + - q_i^0\) localized on site M and the sum over j goes over all atomic point charges of the neutral molecular environment. \(\left| {{{\mathbf{R}}}} \right| = \left| {{{{\mathbf{r}}}}_{{{i}}} - {{{\mathbf{r}}}}_{{{j}}}} \right|\) is the distance between both charges. \(\epsilon_{0}\) is the vacuum permittivity and \(\epsilon\) is the relative (isotropic) permittivity of the medium. It is set to \(\epsilon\) = 3.6 for all materials, which is a common (average) value for organic semiconductors. We note that the environmental coupling is the smallest disorder contribution compared to the nonlocal coupling and is included in this approximated fashion for numerical efficiency and completeness.
Relaxation time
In the TL approach, the relaxation time is set to the timescale of the slow quasi-static modes τslow on which the quasi-static disorder landscape changes. It is set to the inverse of the circular frequency of a dominating low-frequency mode \(\tau _{{{{\mathrm{slow}}}}} = \omega _{{{{\mathrm{slow}}}}}^{ - 1}\). Here, the disorder landscape consists of two contributions: the local disorder σMM and nonlocal disorder σMN. Thus, we extract the dominating frequency from the combined disorder \(\sigma _{MM}^2 + \mathop {\sum}\nolimits_{MN} {\sigma _{MN}^2}\) (for a given center molecule M and nearest-neighbors N) in a weighted average:
Charge transport simulations
The charge-carrier mobilities are calculated according to Eq. (6) of the main text and are based on the time- and energy-resolved quantum spread of Eq. (7) of the main text:
with |Φ′RP(t)〉 = [X,U(t)]|ΦRP〉, U(t) = e−iHt/ℏ. The energy-projection and time-evolution is performed with respect to the purely electronic Hamiltonian in Eq. (4) of the main text. To this end, we build a 3D model Hamiltonian consisting of 12,288,000 sites for each material. The system is initialized in a random-phase state81 \(\left| {{\Phi}_{{{{\mathrm{RP}}}}}} \right\rangle = N_{{{{\mathrm{sites}}}}}^{-1/2}\mathop {\sum}\nolimits_j^{{{{\mathrm{sites}}}}} {e^{i\theta _j}} \left| {{{{\mathrm{{\Phi}}}}}_j} \right\rangle\), i.e. a state having a different random phase θj for each site j. This allows us to simulate the quantum spread in Eq. (7) of the main text as an average over different disorder landscapes in different parts of the 3D sample in a single run since the wave-packet localizes in only a small region of the full 3D sample. The energy projection in Eq. (16) is performed using the Lanczos algorithm82, while the time-evolution is performed using the Chebyshev-polynomial expansion83.
Estimation of the dimensionality
The dimensionality is studied by analyzing the directional distribution of all transfer integrals to all nearest-neighbor molecules of a given center molecule. We therefore establish a standardized, orthonormal frame: the vector ex points in the direction of the largest transfer integral, ey lies in the plane spanned by the vectors in direction of the two largest transfer integrals and is chosen to be perpendicular to ex, and ez is perpendicular to both ex and ey. We now calculate the averaged nearest-neighbor transfer integral \(\bar \varepsilon _{OP}^\alpha\) (for a given center molecule O) in direction α in a weighted average, whereby the weight is the projection of the center-of-mass distance vector dOP onto ea:
the sum runs over all nearest-neighbor molecules P. To study the two-dimensionality as done in the main manuscript, we take the sum \(\bar \varepsilon _{OP}^x\) and \(\bar \varepsilon _{OP}^y\), which is the sum of the averaged transfer integrals within the high-mobility plane, and normalize it to the maximum transfer integral:
This choice ensures that \(\delta _{\dim }^{2D}\) equals to one if there are strong contributions of transfer integrals in only one direction (i.e. 1D transport), while it is two if there are equal contributions into two orthogonal directions within the high-mobility plane (i.e. 2D transport).
Data availability
The data that support the findings of the study are available from the corresponding author upon reasonable request.
References
Brown, A. R., Pomp, A., Hart, C. M. & De Leeuw, D. M. Logic gates made from polymer transistors and their use in ring oscillators. Science 270, 972–974 (1995).
Gershenson, M. E., Podzorov, V. & Morpurgo, A. F. Colloquium: electronic transport in single-crystal organic transistors. Rev. Mod. Phys. 78, 973–989 (2006).
Briseno, A. L. et al. Patterning organic single-crystal transistor arrays. Nature 444, 913–917 (2006).
Mei, J., Diao, Y., Appleton, A. L. & Bao, Z. Integrated materials design of organic semiconductors for field-effect transistors. J. Am. Chem. Soc. 135, 6724–6746 (2013).
Kippelen, B. & Brédas, J. L. Organic photovoltaics. Energy Environ. Sci. 2, 251–261 (2009).
Cao, W. & Xue, J. Recent progress in organic photovoltaics: device architecture and optical design. Energy Environ. Sci. 7, 2123–2144 (2014).
Meng, L. et al. Organic and solution-processed tandem solar cells with 17.3% efficiency. Science 361, 1094–1098 (2018).
Berggren, M. et al. Light-emitting diodes with variable colours from polymer blends. Nature 372, 444–446 (1994).
Forrest, S. R. The road to high efficiency organic light emitting devices. Org. Electron. 4, 45–48 (2003).
Reineke, S., Thomschke, M., Lüssem, B. & Leo, K. White organic light-emitting diodes: status and perspective. Rev. Mod. Phys. 85, 1245–1293 (2013).
Holstein, T. Studies of polaron motion part I. The molecular-crystal model. Ann. Phys. 8, 325–342 (1959).
Holstein, T. Studies of polaron motion: Part II. The “small” polaron. Ann. Phys. 8, 343–389 (1959).
Hannewald, K. et al. Theory of polaron bandwidth narrowing in organic molecular crystals. Phys. Rev. B 69, 075211 (2004).
Troisi, A. & Orlandi, G. Charge-transport regime of crystalline organic semiconductors: diffusion limited by thermal off-diagonal electronic disorder. Phys. Rev. Lett. 96, 086601 (2006).
Ortmann, F., Bechstedt, F. & Hannewald, K. Charge transport in organic crystals: theory and modelling. Phys. Status Solidi Basic Res. 248, 511–525 (2011).
Ishii, H., Honma, K., Kobayashi, N. & Hirose, K. Wave-packet approach to transport properties of carrier coupled with intermolecular and intramolecular vibrations of organic semiconductors. Phys. Rev. B 85, 245206 (2012).
Heiber, M. C., Baumbach, C., Dyakonov, V. & Deibel, C. Encounter-limited charge-carrier recombination in phase-separated organic semiconductor blends. Phys. Rev. Lett. 114, 136602 (2015).
Spencer, J., Gajdos, F. & Blumberger, J. FOB-SH: fragment orbital-based surface hopping for charge carrier transport in organic and biological molecules and materials. J. Chem. Phys. 145, 064102 (2016).
Massé, A. et al. Ab initio charge-carrier mobility model for amorphous molecular semiconductors. Phys. Rev. B 93, 195209 (2016).
Yi, H. T., Gartstein, Y. N. & Podzorov, V. Charge carrier coherence and Hall effect in organic semiconductors. Sci. Rep. 6, 23650 (2016).
Fratini, S., Ciuchi, S., Mayou, D., Trambly de Laissardière, G. & Troisi, A. A map of high-mobility molecular semiconductors. Nat. Mater. 16, 998–1002 (2017).
Giannini, S. et al. Quantum localization and delocalization of charge carriers in organic semiconducting crystals. Nat. Commun. 10, 3843 (2019).
Roosta, S., Ghalami, F., Elstner, M. & Xie, W. Efficient surface hopping approach for modeling charge transport in organic semiconductors. J. Chem. Theory Comput. 18, 1264 (2022).
Chang, B. K., Zhou, J. J., Lee, N. E. & Bernardi, M. Intermediate polaronic charge transport in organic crystals from a many-body first-principles approach. npj Comput. Mater. 8, 63 (2022).
Carof, A., Giannini, S. & Blumberger, J. How to calculate charge mobility in molecular materials from surface hopping non-adiabatic molecular dynamics-beyond the hopping/band paradigm. Phys. Chem. Chem. Phys. 21, 26368–26386 (2019).
Ortmann, F., Bechstedt, F. & Hannewald, K. Theory of charge transport in organic crystals: Beyond Holstein’s small-polaron model. Phys. Rev. B 79, 235206 (2009).
Troisi, A. & Orlandi, G. Dynamics of the intermolecular transfer integral in crystalline organic semiconductors. J. Phys. Chem. A 110, 4065–4070 (2006).
Vukmirović, N., Bruder, C. & Stojanović, V. M. Electron-phonon coupling in crystalline organic semiconductors: Microscopic evidence for nonpolaronic charge carriers. Phys. Rev. Lett. 109, 126407 (2012).
Troisi, A. Quantum dynamic localization in the Holstein Hamiltonian at finite temperatures. Phys. Rev. B - Condens. Matter Mater. Phys. 82, 245202 (2010).
Fratini, S., Mayou, D. & Ciuchi, S. The transient localization scenario for charge transport in crystalline organic materials. Adv. Funct. Mater. 26, 2292–2315 (2016).
Hutsch, S., Panhans, M. & Ortmann, F. Time-consistent hopping transport with vibration-mode-resolved electron-phonon couplings. Phys. Rev. B 104, 054306 (2021).
Nematiaram, T., Padula, D., Landi, A. & Troisi, A. On the largest possible mobility of molecular semiconductors and how to achieve it. Adv. Funct. Mater. 30, 2001906 (2020).
Fetherolf, J. H., GoleŽ, D. & Berkelbach, T. C. A unification of the holstein polaron and dynamic disorder pictures of charge transport in organic crystals. Phys. Rev. X 10, 021062 (2020).
Fan, Z. et al. Linear scaling quantum transport methodologies. Phys. Rep. 903, 1–69 (2021).
Panhans, M. & Ortmann, F. Efficient time-domain approach for linear response functions. Phys. Rev. Lett. 127, 016601 (2021).
Mahan, G. D. Many-Particle Physics (Kluwer Academic/Plenum Publishers, 2000).
Sánchez-Carrera, R. S., Paramonov, P., Day, G. M., Coropceanu, V. & Brédas, J. L. Interaction of charge carriers with lattice vibrations in oligoacene crystals from naphthalene to pentacene. J. Am. Chem. Soc. 132, 14437–14446 (2010).
Lang, I. G. & Firsov, Y. A. Kinetic theory of semiconductors with low mobility. Sov. Phys. JETP 16, 1301 (1963).
Kubo, R. Statistical-mechanical theory of irreversible processes. i. general theory and simple applications to magnetic and conduction problems. J. Phys. Soc. Jpn 12, 570–586 (1957).
Nematiaram, T., Ciuchi, S., Xie, X., Fratini, S. & Troisi, A. Practical computation of the charge mobility in molecular semiconductors using transient localization theory. J. Phys. Chem. C 123, 6989–6997 (2019).
Nakanotani, H., Saito, M., Nakamura, H. & Adachi, C. Highly balanced ambipolar mobilities with intense electroluminescence in field-effect transistors based on organic single crystal oligo(p -phenylenevinylene) derivatives. Appl. Phys. Lett. 95, 033308 (2009).
Sundar, V. C. et al. Elastomeric transistor stamps: reversible probing of charge transport in organic crystals. Science 303, 1644–1646 (2004).
Kunkel, C., Schober, C., Margraf, J. T., Reuter, K. & Oberhofer, H. Finding the right bricks for molecular legos: a data mining approach to organic semiconductor design. Chem. Mater. 31, 969–978 (2019).
Kunkel, C., Margraf, J. T., Chen, K., Oberhofer, H. & Reuter, K. Active discovery of organic semiconductors. Nat. Commun. 12, 2422 (2021).
Marcus, R. A. On the theory of oxidation‐reduction reactions involving electron transfer. I. J. Chem. Phys. 24, 966–978 (1956).
Marcus, R. A. & Sutin, N. Electron transfers in chemistry and biology. Biochim. Biophys. Acta 811, 265–322 (1985).
Urbach, F. The long-wavelength edge of photographic sensitivity and of the electronic absorption of solids. Phys. Rev. 92, 1324–1324 (1953).
Cohen, M. H. & Economou, E. N. Theory of electron band tails and the urbach optical-absorption edge. Phys. Rev. Lett. 57, 1777–1780 (1986).
Anderson, P. W. Absence of diffusion in certain random lattices. Phys. Rev. 109, 1492 (1958).
Valeev, E. F., Coropceanu, V., Da Silva Filho, D. A., Salman, S. & Brédas, J. L. Effect of electronic polarization on charge-transport parameters in molecular organic semiconductors. J. Am. Chem. Soc. 128, 9882–9886 (2006).
Kirkpatrick, J. An approximate method for calculating transfer integrals based on the ZINDO Hamiltonian. Int. J. Quant. Chem. 108, 51–56 (2008).
Löwdin, P. O. On the non-orthogonality problem connected with the use of atomic wave functions in the theory of molecules and crystals. J. Chem. Phys. 18, 365–375 (1950).
Becke, A. D. Density-functional exchange-energy approximation with correct asymptotic behavior. Phys. Rev. A 38, 3098–3100 (1988).
Lee, C., Yang, W. & Parr, R. G. Development of the Colle-Salvetti correlation-energy formula into a functional of the electron density. Phys. Rev. B 37, 785–789 (1988).
Krishnan, R., Binkley, J. S., Seeger, R. & Pople, J. A. Self-consistent molecular orbital methods. XX. A basis set for correlated wave functions. J. Chem. Phys. 72, 650–654 (1980).
McLean, A. D. & Chandler, G. S. Contracted Gaussian basis sets for molecular calculations. I. Second row atoms, Z=11-18. J. Chem. Phys. 72, 5639–5648 (1980).
Frisch, M. J. et al. G16_C01. Gaussian 16, Revision C.01 (Gaussian, Inc., Wallin, 2016).
Marzari, N., Mostofi, A. A., Yates, J. R., Souza, I. & Vanderbilt, D. Maximally localized Wannier functions: theory and applications. Rev. Mod. Phys. 84, 1419 (2012).
Pizzi, G. et al. Wannier90 as a community code: new features and applications. J. Phys. Condens. Matter 32, 165902 (2020).
Mostofi, A. A. et al. An updated version of wannier90: a tool for obtaining maximally-localised Wannier functions. Comput. Phys. Commun. 185, 2309–2310 (2014).
Kresse, G. & Hafner, J. Ab initio molecular dynamics for liquid metals. Phys. Rev. B 47, 558 (1993).
Kresse, G. & Furthmüller, J. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys. Rev. B 54, 11169–11186 (1996).
Blöchl, P. E. Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994).
Kresse, G. & Joubert, D. From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758–1775 (1999).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Perdew, J. P., Burke, K. & Ernzerhof, M. Erratum: generalized gradient approximation made simple. Phys. Rev. Lett. 78, 1396 (1997).
Elstner, M. & Seifert, G. Density functional tight binding. Philos. Trans. R. Soc. A Math. Phys. Eng. Sci. 372, 20120483 (2014).
Xie, X., Santana-Bonilla, A. & Troisi, A. Nonlocal electron-phonon coupling in prototypical molecular semiconductors from first principles. J. Chem. Theory Comput. 14, 3752–3762 (2018).
Yi, Y., Coropceanu, V. & Brédas, J. L. Nonlocal electron-phonon coupling in the pentacene crystal: Beyond the Γ-point approximation. J. Chem. Phys. 137, 164303 (2012).
Gaus, M., Goez, A. & Elstner, M. Parametrization and benchmark of DFTB3 for organic molecules. J. Chem. Theory Comput. 9, 338–354 (2013).
Hourahine, B. et al. DFTB+, a software package for efficient approximate density functional theory based atomistic simulations. J. Chem. Phys. 152, 124101 (2020).
Rauls, E., Elsner, J., Gutierrez, R. & Frauenheim, T. Stoichiometric and non-stoichiometric (101̄0) and (112̄0) surfaces in 2H-SiC: a theoretical study. Solid State Commun 111, 459–464 (1999).
Grimme, S., Antony, J., Ehrlich, S. & Krieg, H. A consistent and accurate ab initio parametrization of density functional dispersion correction (DFT-D) for the 94 elements H-Pu. J. Chem. Phys. 132, 154104 (2010).
Giustino, F. Electron-phonon interactions from first principles. Rev. Mod. Phys. 89, 015003 (2017).
D’Avino, G. et al. Electrostatic phenomena in organic semiconductors: fundamentals and implications for photovoltaics. J. Phys. Condens. Matter 28, 433002 (2016).
Rühle, V. et al. Microscopic simulations of charge transport in disordered organic semiconductors. J. Chem. Theory Comput. 7, 3335–3345 (2011).
Valiev, M. et al. NWChem: a comprehensive and scalable open-source solution for large scalemolecular simulations. Comput. Phys. Commun 181, 1477–1489 (2010).
Landi, A. & Troisi, A. Rapid evaluation of dynamic electronic disorder in molecular semiconductors. J. Phys. Chem. C 122, 18336–18345 (2018).
Singh, U. C. & Kollman, P. A. An approach to computing electrostatic charges for molecules. J. Comput. Chem. 5, 129–145 (1984).
Besler, B. H., Merz, K. M. & Kollman, P. A. Atomic charges derived from semiempirical methods. J. Comput. Chem. 11, 431–439 (1990).
Iitaka, T. & Ebisuzaki, T. Random phase vector for calculating the trace of a large matrix. Phys. Rev. E 69, 4 (2004).
Lanczos, C. An iteration method for the solution of the eigenvalue problem of linear differential and integral operators 1. J. Res. Natl. Bur. Stand. 45, 2133 (1950).
Weiße, A., Wellein, G., Alvermann, A. & Fehske, H. The kernel polynomial method. Rev. Mod. Phys. 78, 275–306 (2006).
Acknowledgements
We would like to thank the Deutsche Forschungsgemeinschaft for financial support [Projects No. OR 349/3 and the Cluster of Excellence e-conversion (grant no. EXC2089)]. Grants for computer time from the Zentrum für Informationsdienste und Hochleistungsrechnen of TU Dresden and the Leibniz Supercomputing Centre in Garching (SuperMUC-NG) are gratefully acknowledged.
Funding
Open Access funding enabled and organized by Projekt DEAL.
Author information
Authors and Affiliations
Contributions
S.H. and M.P. developed the theoretical model. S.H. performed the ab-initio calculations and transport simulations. F.O. supervised the project. The manuscript was written by all co-authors.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Hutsch, S., Panhans, M. & Ortmann, F. Charge carrier mobilities of organic semiconductors: ab initio simulations with mode-specific treatment of molecular vibrations. npj Comput Mater 8, 228 (2022). https://doi.org/10.1038/s41524-022-00915-3
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41524-022-00915-3
- Springer Nature Limited
This article is cited by
-
Insight on charge-transfer regimes in electron-phonon coupled molecular systems via numerically exact simulations
Communications Physics (2023)
-
Directed exciton transport highways in organic semiconductors
Nature Communications (2023)